CN102093796A - Stone paint coating - Google Patents

Stone paint coating Download PDF

Info

Publication number
CN102093796A
CN102093796A CN 201110036403 CN201110036403A CN102093796A CN 102093796 A CN102093796 A CN 102093796A CN 201110036403 CN201110036403 CN 201110036403 CN 201110036403 A CN201110036403 A CN 201110036403A CN 102093796 A CN102093796 A CN 102093796A
Authority
CN
Grant status
Application
Patent type
Prior art keywords
parts
stone
sense
lacquer coating
color
Prior art date
Application number
CN 201110036403
Other languages
Chinese (zh)
Other versions
CN102093796B (en )
Inventor
康跃金
Original Assignee
康跃金
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

The invention relates to a coating of paint for a wall, in particular to a stone-like paint coating used for decorative industry. The stone paint coating is prepared by proportioning the following raw materials in parts by mass: 100 parts-120 parts of water, 6 parts-8 parts of cellulose, 6 parts-8 parts of dispersing wetting agent, 5 parts-7 parts of defoaming agent, 2 parts-3 parts of preservative, 5 parts-7 parts of mildew preventive, 14 parts-17 parts of freeze proof agent, 15 parts-17 parts of film-forming auxiliary, 145 parts-165 parts of pigment and filler, 360 parts-380 parts of organic silicon acrylic acid polymer, 320 parts-340 parts of color protective colloidal particle and 4 parts-6 parts of thickener. Thus, the paint coating can completely replace dry-hang marble to be used for wall decoration because of emulational appearance decorative effect, and has the advantages that other wall decorative materials do not have.

Description

石感漆涂料 Paint stone sense of paint

技术领域 FIELD

[0001] 本发明涉及墙体面涂装涂料,尤其涉及可以应用于装饰行业的仿石材质感的漆涂料。 [0001] The present invention relates to a wall paint coating surface, it can be applied particularly to the decoration imitation stone texture lacquer coating.

背景技术 Background technique

[0002] 墙体面装饰对于居家环境是十分重要的。 [0002] wall surface decoration for the home environment is very important. 目前建筑市场上普遍使用的墙体面装饰材料为:内外墙涂料(内外墙乳胶漆、氟碳漆)、干挂石材、瓷砖等。 Currently wall surface decoration materials commonly used in the construction market are: interior and exterior paint (interior and exterior latex paint, fluorocarbon), hanging stone, tiles and so on.

[0003] 其中,内外墙涂料施工处理存在如下问题:1、产品不配套:施工后出现产品排斥现象,表现为裂缝、返碱、退色、起皮、脱粉、渗水、耐候性差等;2、施工成本控制导致产品施工质量低劣,易出现产品后期施工质量问题;3、产品施工后出现色差严重、透底等质量问题;4、美观性较差。 [0003] wherein the presence of the external coating construction addresses the following questions: 1, the product is not complete: product exclusion, manifested as cracks, back to base, fading, peeling, from powder, seepage, weather resistance and poor after construction; 2, construction cost control lead to poor product quality construction, prone to post-construction product quality problems; 3, the product of serious color after construction, through the end of other quality problems; 4, poor aesthetics.

[0004] 虽然干挂石材,如干挂大理石材作为高档墙体装饰材料得到市场和消费者的认可,但是由于石材为自然不可再生资源,以干挂石材用作墙体装饰存在如下问题:1、环境破坏严重:采石场环境破坏、石材加工厂环境污染严重;石材在干挂时要用到油性固化剂、其中的甲苯、二甲苯及其它有毒溶剂的挥发,严重的造成了环境污染;2、能源消耗大:石材资源有限,不可再生。 [0004] Although the hanging stone, such as marble sheets hanging by the market as high-end consumer recognition and wall decoration materials, but since the stone is a natural non-renewable resources, to be used as decorative wall hanging stone following problems: 1 , serious environmental damage: quarry environmental damage, environmental pollution stone processing; stone to use a curing agent at the time of hanging oil, wherein the volatile toluene, xylene, and other toxic solvents, causing serious environmental pollution; 2, energy consumption: stone limited resources, non-renewable. 从采石到石材加工、墙体装饰严重耗费自然资源、电力资源、人力、钢材构件等;3、石材因材质较重,大面积使用会大大增加建筑物体的承载重量,在高层建筑物中禁止使用;4、石材易产生辐射,石材毛细孔粗,致密性差,易吸水,很容易造成建筑物体渗水、泛白吐碱等常见问题;5、石材外墙施工装饰成本造价高、施工安全性较差、工期长、施工技术要求高;6、不可再利用,干挂石材的旧物体翻新使用较为困难;墙体翻新难度增加。 From quarrying to stone processing, wall decoration serious consumes natural resources, power resources, manpower, and other steel components; 3, stone materials due to heavy, large-scale use will greatly increase the weight-bearing architectural objects prohibited in high-rise buildings use; 4, easy to produce radiation stone, stone pores coarse, dense and poor, easy to absorb water easily lead to water seepage FAQ architectural objects, such as whitening spit base; 5, decorative stone facades construction costs high cost, construction safety than difference, long duration, high technical requirements construction; 6, can not be reused, refurbishment of old objects hanging stone more difficult to use; refurbished to increase the difficulty of the wall.

[0005] 采用瓷砖用作墙体装饰也存在如下常见问题:1、环境破坏严重:对自然资源、环境破坏严重;2、能源消耗大:瓷砖成品制造过程耗能、耗费自然资源;3、施工安性较差、易脱落,不宜外墙高层施工,不耐污、不美观。 [0005] The decorative wall tiles as there are common problems as follows: 1, serious environmental damage: natural resources, serious environmental damage; 2, energy consumption: finished tile manufacturing process energy consuming natural resources; 3, construction security is poor, easy to fall off, not the external walls of high-rise construction, not tolerance, not pretty.

发明内容 SUMMARY

[0006] 因此,针对上述的各种墙体面装饰材料存在的一些不足之处,发明提出一种新式的墙体面装饰材料,即仿石材质感的漆涂料。 [0006] Thus, for some of the shortcomings present in a variety of wall surface decoration materials, the invention proposes a new type of wall surface decoration materials, i.e. imitation stone textured lacquer coating. 本发明的石感漆涂料因其极具仿真的外观装饰效果完全可以取代大理石材的干挂石材而用作墙体装饰,且具有其他墙体面装饰材料所不具备的优点。 Stone sense lacquer coating of the present invention because of its highly aesthetic performance simulation substituted hanging stone marble can be used as a decorative wall material, and having a wall surface decoration materials other advantages not available.

[0007] 本发明采用的技术方案是: [0007] aspect of the present invention is that:

[0008] 一种石感漆涂料,是按照如下质量份数进行配比: [0008] A sense stone lacquer coating, is parts by mass ratio as follows:

[0009] 1、水 100 份-120 份 [0009] 1, 100 parts of water -120 parts

[0010] 2、纤维素 6份-8份 [0010] 2, 6 parts of cellulose parts -8

[0011] 3、分散湿润剂 6份-8份 [0011] 3, 6 parts dispersing agent, wetting parts -8

[0012] 4、消泡剂 5份-7份 [0012] 4, 5 parts of defoamer parts -7

[0013] 5、防腐剂 2份-3份6、防霉剂 5份-7份 [0013] 5, preservatives parts 2 -3 parts 6, -7 fungicide parts 5 parts

7、防冻剂 14份-17份 7, parts 14 -17 parts antifreeze

8、成膜助剂 15份-17份 8, -17 coalescent parts 15 parts

9、颜填料 145份-165份 9, 145 parts -165 parts pigment

10、有机硅丙烯酸聚合物360份-380份 10, a silicone acrylate polymer 360 parts -380 parts

11、色彩保护胶粒 320份-340份 11, the color protective rubber 320 parts -340 parts

12、增稠剂 4份-6份 12, 4 parts of a thickener -6 parts

优选的,为了获得更佳的效果,是按照如下更佳的质量份数进行配比 Preferably, in order to obtain better results, according to the following ratio is better quality parts

[0014] [0014]

[0015] [0015]

[0016] [0016]

[0017] [0017]

[0018] [0018]

[0019] [0019]

[0020] [0021] [0022] [0020] [0021] [0022]

[0023] [0023]

[0024] [0024]

[0025] [0025]

[0026] [0026]

[0027] [0027]

[0028] [0028]

[0029] [0029]

[0030] [0030]

[0031] [0031]

[0032] [0032]

[0033] [0033]

[0034] 进一步的,为了获得更佳的涂料质量效果和质感效果,所述的颜填料由耐候型金红石钛白粉、煅烧高岭土、重钙粉混合组成。 [0034] Further, in order to obtain better coating quality results and texture effects, said weather resistant pigment calcined kaolin, heavy calcium rutile titanium dioxide were mixed, composed.

[0035] 优选的混合比例是,所述的耐候型金红石钛白粉、煅烧高岭土、重钙粉的混合比例;^; 3 1 . 2 ο [0035] The preferable mixing proportion of the rutile titanium dioxide weather, calcined kaolin, heavy calcium powder mixing ratio; ^;. 3 1 2 ο

[0036] 进一步的,所述的有机硅丙烯酸聚合物是由有机硅氧烷与丙烯酸丁酯(BA)、丙烯酸甲酯、(MA)、丙烯酸(MAA)及催化剂反应复合而成。 [0036] Further, the acrylic silicone polymer is a polyorganosiloxane with butyl acrylate (BA), methyl acrylate, (MA), acrylic acid (MAA) and the catalyst composite.

[0037] 进一步的,如上所述的有机硅丙烯酸聚合物中含有有机硅氧烷基团R-Si (OR' )3。 [0037] Further, silicone-containing acrylic polymers described above organosiloxane group R-Si (OR ') 3.

[0038] 进一步的,所述的色彩保护胶粒是经过活化的阳离子胶体与色浆复配后经筛网造粒而成。 [0038] Further, the color of the protective colloid is activated after colloid and the cationic compound granulation from the paste by the screen. 所述的色彩保护胶粒的颜色为多种色彩的粒子组成。 The color of the color of the protective colloid is composed of particles of various colors.

[0039] 本发明的石感漆涂料涂装于墙体面,可以在墙体面产生高度仿真大理石干挂的外观效果,并且不会有背景技术所言的普通内外墙涂料的褪色、起皮、色差、不够美观等不足, 更不会有背景技术所言的干挂石材的污染、不环保、对建筑承重不利、施工不便等不足,也不会有背景技术所言的瓷砖的不环保、不易施工、不够美观等不足。 [0039] Coating lacquer sense stone in the wall face of the present invention can be produced highly simulated marble appearance in the hanging wall surface, and there will fade ordinary external coating of said background art, peeling , color, appearance and other issues is not enough, there will be no more pollution hanging stone bACKGROUND said, and not environmentally friendly, adverse bearing on the building, such as lack of inconvenient construction, there will be no environmental protection tiles background of said, construction is not easy, not beautiful and so inadequate. 本发明的漆涂料具有如下优点: Lacquer coating according to the present invention has the following advantages:

[0040] 1、纯水性配方,完全符合环保要求。 [0040] 1, pure formula, in full compliance with environmental requirements.

[0041] 2、色彩完全可以仿干挂大理石材做墙体装饰,效果可以效真。 [0041] 2, the color can imitation marble material as wall hanging decorative effect can be really effective.

[0042] 3、耐候性能优,使用寿命达10年以上,经人工老化试验600小时以上。 [0042] 3, excellent weather resistance, service life of 10 years, artificial aging test over 600 hours.

[0043] 4、通用型强、无任何负重,施工后漆膜厚度在100-120um左右,大大减轻了建筑物体的承载负荷。 [0043] 4, strong general, no load, after construction film thickness of approximately 100-120um, greatly reducing the load-bearing construction of the object.

1、水 100份2、纤维素 7份3、分散湿润剂 6份4、消泡剂 5份5、防腐剂 2份6、防霉剂 5份7、防冻剂 15份8、成膜助剂 16份9、颜填料 150份10、有机硅丙烯酸聚合物 360份11、色彩保护胶粒 330份12、增稠剂 4份[0044] 5、施工简便,一次喷涂即可实现预期装饰效果。 1, 2 100 parts of water, 7 parts of a cellulose 3, 4 6 parts dispersing wetting agent, a defoaming agent 5 parts 5, 6 parts of 2 antiseptic, an antifungal agent 5 parts 7, 8 antifreeze 15 parts coalescents 9 16 parts, 10 parts of fillers 150, a silicone acrylate polymer 360 parts 11, 12 color protective rubber 330 parts, 4 parts of a thickener [0044] 5, the construction is simple, a spray can achieve the desired decorative effect.

[0045] 6、防水、抗龟裂,彻底解决了干挂石材渗水、泛碱等异常现象。 [0045] 6, waterproof, anti-cracking, solve the hanging stone water seepage, efflorescence and other anomalies.

[0046] 7、不存在安全隐患,可再利用建筑物体再次翻新装修。 [0046] 7, there is no security risk, can be reused again refurbishment architectural objects.

[0047] 8、自洁性强,耐污性< 5%,高强度、耐洗刷达2万次以上。 [0047] 8, strong self-cleaning, stain resistance <5%, high strength, abrasion of more than 20,000.

具体实施方式 [0048] 现结合具体实施方式对本发明进一步说明。 DETAILED DESCRIPTION [0048] Now with reference to specific embodiments of the present invention is further described. [0049] 实施例1 : [0050] 本实施例的石感漆涂料,是按照如下质量份_ 女进行配比[0051] 1、水 100份 [0052] 2、纤维素 8份 [0053] 3、分散湿润剂 6份 [0054] 4、消泡剂 7份 [0055] 5、防腐剂 2份 [0056] 6、防霉剂 7份 [0057] 7、防冻剂 14份 [0058] 8、成膜助剂 15份 [0059] 9、颜填料 165份 [0060] 10、有机硅丙烯酸聚合物 360份 [0061] 11、色彩保护胶粒 340份 [0062] 12、增稠剂 4份 [0063] 实施例2 : [0064] 本实施例的石感漆涂料,是按照如下质量份_ 女进行配比[0065] 1、水 120份 [0066] 2、纤维素 6份 [0067] 3、分散湿润剂 8份 [0068] 4、消泡剂 5份 [0069] 5、防腐剂 3份 [0070] 6、防霉剂 5份 [0071] 7、防冻剂 17份 [0072] 8、成膜助剂 15份 [0073] 9、颜填料 165份 [0074] 10、有机硅丙烯酸聚合物 360份 [0075] 11、色彩保护胶粒 340份 [0076] 12、增稠剂 4份 [0077] 实施例3 : [0078] 本实施例的石感漆涂料,是按照如下质量 [0049] Example 1: [0050] sense stone lacquer coating according to the present embodiment, parts by mass is as follows for the ratio M _ [0051] 1, 100 parts of water [0052] 2, cellulose 8 parts [0053] 3 , 6 parts dispersing wetting agent [0054] 4, 7 parts of a defoaming agent [0055] 5, 2 parts of a preservative [0056] 6, 7 parts of a fungicide [0057] 7, 14 parts of an antifreeze [0058] 8, as 15 parts adjuvants film [0059] 9, 165 parts pigment [0060] 10, 360 parts of a silicone acrylic polymer [0061] 11, 340 parts of colloidal color protection [0062] 12, 4 parts of a thickener [0063] Example 2: [0064] sense stone lacquer coating according to the present embodiment, parts by mass is as follows for the ratio M _ [0065] 1, 120 parts of water, [0066] 2, 6 parts of cellulose [0067] 3, wet dispersion agent 8 parts [0068] 4, 5 parts of defoamer [0069] 5, 3 parts of a preservative [0070] 6, 5 parts of a fungicide [0071] 7, 17 parts of an antifreeze [0072] 8, coalescents 15 parts [0073] 9, 165 parts pigment [0074] 10, 360 parts of a silicone acrylic polymer [0075] 11, 340 parts of colloidal color protection [0076] 12, 4 parts of a thickener [0077] Example 3 : [0078] sense stone lacquer coating according to the present embodiment, the mass is as follows _ 女进行配比[0079] 1、水 110份 [0080] 2、纤维素 6份份0081] 3、分散湿润剂 8份0082] 4、消泡剂 6份0083] 5、防腐剂 2份份0084] 6、防霉剂 6份0085] 7、防冻剂 16份0086] 8、成膜助剂 16份0087] 9、颜填料 155份0088] 10、有机硅丙烯酸聚合物 375份0089] 11、色彩保护胶粒 325份0090] 12、增稠剂 5份0091] 实施例4 : 0092] 本实施例的石感漆涂料,是按照如下质量份数进行配比: 0093] 1、水 100份0094] 2、纤维素 7份0095] 3、分散湿润剂 6份0096] 4、消泡剂 5份0097] 5、防腐剂 2份0098] 6、防霉剂 5份0099] 7、防冻剂 15份0100] 8、成膜助剂 16份0101] 9、颜填料 150份0102] 10、有机硅丙烯酸聚合物360份 0103] 11、色彩保护胶粒 330份0104] 12、增稠剂 4份0105] 上述4个实施例的各物质的不同质量份数配比均能获得不错的涂料质量效果和 _ F ratio for [0079] 1, 110 parts of water, [0080] 2, 6 parts by cellulose 0081] 3, wetting agents dispersing 8 parts 0082] 4, 6 parts of defoamer 0083] 5, preservatives parts 2 parts 0084] 6, 6 parts of a fungicide 0085] 7, 16 parts of an antifreeze 0086] 8, 16 parts coalescent 0087] 9, 155 parts of pigments 0088] 10, a silicone acrylate polymer 375 parts by 0089] 11, color protective rubber 325 parts by 0090] 12, 5 parts of a thickener 0091] Example 4: 0092] stone sense lacquer coating according to the present embodiment, the ratio is as follows parts by mass: 0093] 1, 100 parts of water, 0094 ] 2, 7 parts of cellulose 0095] 3, 6 parts dispersing wetting agent 0096] 4, 5 parts of defoamer 0097] 5, 2 parts of a preservative 0098] 6, 5 parts of a fungicide 0099] 7, 15 parts of an antifreeze 0100] 8, 16 parts coalescent 0101] 9, 150 parts pigment 0102] 10, a silicone acrylate polymer 360 parts by 0103] 11, 330 parts of a color protective colloid 0104] 12, 4 parts of a thickener 0105] parts of the four different mass ratio of each substance embodiments can get a good quality paint and effects

质感效果的实感漆涂料。 Real sense of the texture of paint coating effect. 尤其是实施例4的质量份数配比,效果最佳。 Particularly, in Example 4 parts by mass ratio, the best results.

[0106] 上述的配方原材料使用说明: [0106] The formulation of raw materials for use:

[0107] 1、颜填料:为了获得更佳的涂料质量效果和质感效果,颜填料是由特级耐候型金红石钛白粉、煅烧高岭土、重钙粉组成。 [0107] 1, pigment: For better effect the quality and texture of the coating effect, a pigment is rutile titanium dioxide super weather resistant, calcined kaolin, heavy calcium composition. 优选的混合比例是,所述的耐候型金红石钛白粉、煅烧高岭土、重钙粉的混合比例是3 : 1 : 2。 Preferred mixing proportion of the rutile titanium dioxide weather, calcined kaolin, heavy calcium mixing ratio is 3: 1: 2.

[0108] 2、有机硅丙烯酸聚合物:是由有机硅氧烷与丙烯酸丁酯(BA)、丙烯酸甲酯、(MA)、 丙烯酸(MAA)及催化剂在一定的温度条件下反应复合而成。 [0108] 2, a silicone acrylic polymer: is an organosiloxane with butyl acrylate (BA), methyl acrylate, (MA), acrylic acid (MAA) and a catalyst under certain conditions the reaction temperature composite. 有机硅丙烯酸聚合物在常温下无异常,较稳定。 No abnormality silicone acrylic polymer at room temperature, more stable. 所述的有机硅丙烯酸聚合物中含有有机硅氧烷基团R-Si (OR' )3。 The silicone-containing acrylic polymer organosiloxane group R-Si (OR ') 3. 因聚合物体中含有有机硅氧烷基团R-Si (OR' )3,其基团具有优异的耐候性、憎水性和防水性。 Because polymer precursor containing organosiloxane group R-Si (OR ') 3, a group which has excellent weather resistance, water repellency and water resistance.

[0109] 3、色彩保护胶粒:是经过特级活化的阳离子胶体与色浆复配后经筛网造粒而成, 根据不同的仿真石面图案,可配置多种色彩的粒子。 [0109] 3, color protection rubber: is activated after the super colloid and a cationic compound paste by the screen from granulated, depending on the pattern simulated stone surface, the particles may be arranged in a variety of colors.

[0110] 4、其他原材料:均可以选用一般的仿真石涂漆的材料,即可实现。 [0110] 4, other raw materials: the selection of materials can be painted stone general simulation can be realized.

[0111] 本发明的石感漆涂料相对于普通内外墙涂料、干挂石、瓷砖等均具有独特的优点。 [0111] Stone sense lacquer coating of the present invention with respect to the common interior and exterior paints, hanging stone, tiles etc. has unique advantages. 相比于已有的仿真石涂料,通过更佳不同的配方原材料及合理的配比,亦具有环保无污染、仿真度更高、耐候性能优、防水、抗龟裂等更优的性能和美观度。 Compared to the existing simulation stone paint, through better raw materials and different formulations reasonable ratio, also has environmental pollution, a higher degree of simulation, excellent weather resistance, waterproof, anti-cracking, and other superior performance and aesthetics degree.

[0112] 尽管结合优选实施方案具体展示和介绍了本发明,但所属领域的技术人员应该明白,在不脱离所附权利要求书所限定的本发明的精神和范围内,在形式上和细节上可以对本发明做出各种变化,均为本发明的保护范围。 [0112] While the preferred embodiment in conjunction with the specific embodiment shown and described the present invention, those skilled in the art will appreciate that within the spirit and scope of the invention without departing from the appended claims as defined by the form and details various changes may be made to the present invention, the scope of the present invention are.

Claims (8)

  1. 1. 一种石感漆涂料,其特征在于,按照如下质量份数进行配比:1、水 100 份-120 份2、纤维素 6份-8份3、分散湿润剂 6份-8份4、消泡剂 5份-7份5、防腐剂 2份-3份6、防霉剂 5份-7份7、防冻剂 14份-17份8、成膜助剂 15份-17份9、颜填料 145 份-165 份10、有机硅丙烯酸聚合物 360 份-380 份11、色彩保护胶粒 320 份-340 份12、增稠剂 4份-6份。 A sense stone lacquer coating, characterized in that the parts by mass ratio performed as follows: 1, 100 parts of water 2 parts -120, 6 parts -8 cellulose 3 parts, 6 parts dispersing agent, wetting -8 4 parts , 5 parts of defoamer -7 5 parts, 2 parts of a preservative -3 parts 6, -7 antifungal agent 5 parts of 7 parts, 14 parts of an antifreeze parts 8 -17, -17 coalescent parts 15 parts 9, -165 145 parts pigment 10 parts, 360 parts of a silicone acrylate polymer 11 parts -380, -340 color protective rubber 320 parts 12 parts, 4 parts of a thickener -6 parts.
  2. 2.如权利要求1所述的石感漆涂料,其特征在于,按照如下更佳的质量份数进行配比:1、水 100份2、纤维素 7份3、分散湿润剂 6份4、消泡剂 5份5、防腐剂 2份6、防霉剂 5份7、防冻剂 15份8、成膜助剂 16份9、颜填料 150份10、有机硅丙烯酸聚合物 360份11、色彩保护胶粒 330份12、增稠剂 4份。 2. Stone sense lacquer coating according to claim 1, characterized in that, for better quality ratio according to the following parts: 1, 2 100 parts of water, 7 parts of a cellulose 3, 4 6 parts dispersing wetting agent, 5 5 parts of defoamer, 6 parts of 2 antiseptic, an antifungal agent 5 parts 7, 8 antifreeze 15 parts, 16 parts coalescent 9, 10 parts of fillers 150, a silicone acrylate polymer 360 parts 11, color 12 parts protective colloid 330, 4 parts of a thickener.
  3. 3.如权利要求1所述的石感漆涂料,其特征在于:所述的颜填料由耐候型金红石钛白粉、煅烧高岭土、重钙粉混合组成。 Stone sense lacquer coating according to claim 1, wherein: said weather resistant rutile titanium dioxide pigment calcined kaolin, heavy calcium mixed, composed.
  4. 4.如权利要求3所述的石感漆涂料,其特征在于:所述的耐候型金红石钛白粉、煅烧高岭土、重钙粉的混合比例是3 : 1 : 2。 4. The sense stone lacquer coating according to claim 3, wherein: said weather rutile titanium dioxide, calcined kaolin, heavy calcium mixing ratio is 3: 1: 2.
  5. 5.如权利要求1所述的石感漆涂料,其特征在于:所述的有机硅丙烯酸聚合物是由有机硅氧烷与丙烯酸丁酯(BA)、丙烯酸甲酯、(MA)、丙烯酸(MAA)及催化剂反应复合而成。 5. The sense stone lacquer coating according to claim 1, wherein: the acrylic silicone polymer is a polyorganosiloxane with butyl acrylate (BA), methyl acrylate, (MA), acrylic acid ( MAA) and the catalyst composite.
  6. 6.如权利要求1或5所述的石感漆涂料,其特征在于:所述的有机硅丙烯酸聚合物中含有有机硅氧烷基团R-Si (OR' )3。 Stone sense lacquer coating of claim 1 or 5 as claimed in claim 6, wherein: said silicone acrylic polymer containing an organosiloxane group R-Si (OR ') 3.
  7. 7.如权利要求1所述的石感漆涂料,其特征在于:所述的色彩保护胶粒是经过活化的阳离子胶体与色浆复配后经筛网造粒而成。 7. Stone sense lacquer coating according to claim 1, wherein: said protective colloid is a color after activation with colloidal cationic complex granulation from the paste by the screen.
  8. 8.如权利要求1或7所述的石感漆涂料,其特征在于:所述的色彩保护胶粒的颜色为多种色彩的粒子组成。 Sensing the stone or lacquer coating as claimed in claim 17, wherein: the color of the color of the protective colloid is composed of particles of various colors.
CN 201110036403 2011-01-31 2011-01-31 Stone paint coating CN102093796B (en)