CN109913125A - A kind of heat insulation type Environment-friendlyexterior exterior wall paint - Google Patents
A kind of heat insulation type Environment-friendlyexterior exterior wall paint Download PDFInfo
- Publication number
- CN109913125A CN109913125A CN201910126708.4A CN201910126708A CN109913125A CN 109913125 A CN109913125 A CN 109913125A CN 201910126708 A CN201910126708 A CN 201910126708A CN 109913125 A CN109913125 A CN 109913125A
- Authority
- CN
- China
- Prior art keywords
- mixing
- parts
- agent
- stirred
- heat insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat insulation type Environment-friendlyexterior exterior wall paints, it is related to technical field of coatings, specially coating proportioning contains: mixing A, mixed material B, mixing C, reinforcing agent, modifying agent, stabilizer, outer lubrication prescription, defoaming agent, pigment, aluminium powder and modifying agent, the mixing A, 100 parts of assembly of mixed material B and mixing C, 15-70 parts of reinforcing agent, 1-1.5 parts of modifying agent, 0.7-2 parts of stabilizer, outer lubrication prescription 0.2-0.25 parts, 0.15-0.8 parts of defoaming agent, 2-2.8 parts of pigment, 1.5-2.8 parts of aluminium powder, 0.3-0.8 parts of modifying agent, according to weight ratio meter, the mixing A: mixed material B: mixing C=10:6:6.The heat insulation type Environment-friendlyexterior exterior wall paint, process flow is simple and efficient, it is mutually merged using multiple material, interaction, and it mutually assists, synthesis improves the properties of product such as heat insulating ability, the barrier property of entire exterior coating, and the beautiful color for making exterior coating have metallic luster simultaneously, also has good viscosity, attachment degree, good forming curing performance and excellent environmental-protecting performance with building body.
Description
Technical field
The present invention relates to technical field of coatings, specially a kind of heat insulation type Environment-friendlyexterior exterior wall paint.
Background technique
Coating, in the entitled paint of Chinese tradition, so-called coating be coated in the body surface being protected or decorated, and
The continuous film of firm attachment can be formed with coated article, usually based on resin or oil or lotion, add or do not add face
Material, filler, add corresponding additive, the thick liquid being formulated with organic solvent or water, coating in terms of building using non-
Often extensively, fit up build during, coating using ubiquitous, and play a very important role.
Existing coating material have in performance in terms of heat preservation it is to be strengthened, although present coating type is a variety of
Multiplicity, the function of coating and effect are also more and more complete, and the range of coating application is also more and more roomy, but coating itself is in property
Still there are biggish development space, the production technology of coating also should more develop toward summary direction for the improvement of energy aspect.
A kind of silica aerogel reflective insulation disclosed in Chinese invention patent application prospectus CN107163855A
Exterior coating and preparation method thereof, the silica aerogel reflective insulation exterior wall paint and preparation method thereof, although and traditional reflective every
Hot exterior coating is compared, and the reflective insulation performance of the silica aerogel reflective insulation exterior wall paint is very excellent, and is had and be produced into
This low and environmentally friendly advantage, still, silica aerogel reflective insulation exterior wall paint and preparation method thereof, in the raw material system to coating
It is standby upper, still have the development space that can be improved and progress greatly.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of heat insulation type Environment-friendlyexterior exterior wall paint, above-mentioned background is solved
The problem of being proposed in technology.
In order to achieve the above object, the present invention is achieved by the following technical programs: a kind of heat insulation type Environment-friendlyexterior exterior wall paint,
Coating proportioning contains: mixing A, mixed material B, mixing C, reinforcing agent, modifying agent, stabilizer, outer lubrication prescription, defoaming agent, pigment, aluminium powder with
And modifying agent, 100 parts of the assembly of the mixing A, mixed material B and mixing C, 1-1.5 parts of modifying agent, are stablized by 15-70 parts of reinforcing agent
0.7-2 parts of agent, outer lubrication prescription 0.2-0.25 parts, 0.15-0.8 parts of defoaming agent, 2-2.8 parts of pigment, 1.5-2.8 parts of aluminium powder, modifying agent
0.3-0.8 parts, according to weight ratio meter, the mixing A: mixed material B: mixing C=10:6:6.
Optionally, the mixing A includes PVC resin powder and vegetable oil, according to weight ratio meter, the PVC resin powder: plant
Oil=8:10.
Optionally, the preparation method of the mixing A is that side annular adds PVC resin powder into vegetable oil, and Bian Jinhang is stirred
Mix, agitator shaft speed 450r/min, in whipping process, agitating shaft up and down pull and push, and intromission frequency be 1.5-2 seconds/move up (under
Drop) once, mixing time 30-45min.
Optionally, the mixed material B includes Nylon Nanocomposite aegisox, pamxd6/ nano clay composite material m9
With polyvinyl alcohol (pva) membrane material, according to weight ratio meter, described Nylon Nanocomposite aegisox:pamxd6/ nanometers viscous
Soil composite material m9: polyvinyl alcohol (pva) membrane material=1:1:1.
Optionally, the preparation method of the mixed material B is, using flour mill to Nylon Nanocomposite aegisox,
Pamxd6/ nano clay composite material m9 and polyvinyl alcohol (pva) membrane material carry out milling processing respectively, and particulate matter diameter exists
100 mesh, by Nylon Nanocomposite aegisox, pamxd6/ nano clay composite material m9 and polyvinyl alcohol of powdered form
(pva) membrane material is added sequentially in agitator tank, and the speed with speed for 300-450r/min is stirred mixing, mixing time
For 30min.
Optionally, the mixing C includes distilled water, polyethylene, polyurethane, inorfil cotton and inorganic mineral earth surface insulating
Mortar, according to weight ratio meter, the distilled water: polyethylene: polyurethane: inorfil cotton: inorganic mineral earth surface insulating mortar=
10:3:3:3:4, wherein inorfil cotton is made of one or more of rock wool, mineral wool, mineral wool, aluminium silicate wool.
Optionally, the distilled water is that pure water is heated to 280-300 DEG C, is formed after distillation, when preparing mixing C,
After water temperature is reduced to 25-30 DEG C, polyethylene, polyurethane and inorfil cotton are successively added, is stirred with the speed of 150r/min
Mixing is mixed, mixing time 15-18min finally adds inorganic mineral earth surface insulating mortar, and with the speed of 280-300r/min
It is stirred mixing, mixing time 30min.
Optionally, the inorganic mineral earth surface insulating mortar includes Inorganic nonmetal mineral material (specially silica
Aeroge), pitchstone glass bead, anti-cracking impervious material (specially FMA-H impermeability and erosion resistance agent) and inorganic coagulation material it is (specific
For portland cement), according to weight ratio meter, the Inorganic nonmetal mineral material: pitchstone glass bead: anti-cracking impervious material
Material: inorganic coagulation material=1:0.8:0.5:0.5.
Optionally, the modifying agent is in thickener, coalescing agent, toughener, PH regulator, fire retardant and antistatic agent
Two or three of composition described above.
Optionally, the preparation of the heat insulation type Environment-friendlyexterior exterior wall paint includes following processing steps:
A) mixing A is previously heated to 60-75 DEG C, and water-bath is kept the temperature, and is stirred with the speed of 500-800r/min, it is stirred
Reinforcing agent, modifying agent, stabilizer, outer lubrication prescription, defoaming agent and modifying agent are added in journey, stir duration 30-40min；
B) mixed material B is added in mixing A mixture, is stirred with the speed of 800-850r/min, stir duration 45min；
C) mixing C is added in mixing A and the mixture of mixed material B, is stirred with the speed of 750-800r/min, when stirring
Long 30min；
D) pigment is added in the mixture of mixing A, mixed material B and mixing C, is stirred with the speed of 750-800r/min,
Duration 8-10min is stirred, then aluminium powder is even added in the mixture of mixing A, mixed material B and mixing C, with 550-650r/min
Speed be stirred, stir duration 10min；
E) screening is filtered to the mixture of mixing A, mixed material B and mixing C, filters out air entrapment；
F) heat-preserving equipment is removed, is stirred with the speed of 300-450r/min, when being cooled to room temperature 20-25 DEG C, stops stirring；
G) it after mixture anaerobic stands 3-4h, examines, packaging, storage.
The present invention provides a kind of heat insulation type Environment-friendlyexterior exterior wall paints, have following the utility model has the advantages that the heat insulation type environmental protection exterior wall
Coating, process flow are simple and efficient, and are mutually merged using multiple material, interaction, and are mutually assisted, comprehensive to improve entirely
The properties of product such as heat insulating ability, the barrier property of exterior coating, the beautiful color for making exterior coating have metallic luster simultaneously, also have
Good viscosity, attachment degree, good thermal insulation property, good barrier property, good forming curability with building body
Energy and excellent environmental-protecting performance, after being coated in building body outside, be formed by level itself has well the exterior coating
Toughness, waterproofness and moisture resistance be also equipped with excellent water hardening ability other than the exclusive flexibility of cotton fibre, make
When carrying out exterior wall coating, more preferably, faster, be less susceptible to such environmental effects and rapid condensation solidifies.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.
In the description of the present invention, unless otherwise indicated, the meaning of " plurality " is two or more；Term " the
One ", " second ", " third " etc. are used for descriptive purposes only and cannot be understood as indicating or suggesting relative importance.
In the description of the present invention, it should be noted that unless otherwise clearly defined and limited, term " connected " " connects
Connect " it shall be understood in a broad sense, for example, it may be being fixedly connected, it may be a detachable connection, or be integrally connected；It can be machine
Tool connection, is also possible to be electrically connected；It can be directly connected, it can also be indirectly connected through an intermediary.For this field
For those of ordinary skill, the concrete meaning of above-mentioned term in the present invention can be understood with concrete condition.
The present invention provides a kind of technical solution: a kind of heat insulation type Environment-friendlyexterior exterior wall paint, coating proportioning contain: mixing A, mixing
B, mixing C, reinforcing agent, modifying agent, stabilizer, outer lubrication prescription, defoaming agent, pigment, aluminium powder and modifying agent, the mixing A, mixing
100 parts of the assembly of B and mixing C, 15-70 parts of reinforcing agent, 1-1.5 parts of modifying agent, 0.7-2 parts of stabilizer, outer lubrication prescription 0.2-
0.25 part, 0.15-0.8 parts of defoaming agent, 2-2.8 parts of pigment, 1.5-2.8 parts of aluminium powder, 0.3-0.8 parts of modifying agent, according to weight ratio
Meter, the mixing A: mixed material B: mixing C=10:6:6.
Mixing A includes PVC resin powder and vegetable oil, according to weight ratio meter, the PVC resin powder: vegetable oil=8:10.
The preparation method of mixing A is that into vegetable oil, side annular adds PVC resin powder, while being stirred, agitator shaft speed
For 450r/min, in whipping process, agitating shaft pulls and pushes up and down, and intromission frequency be 1.5-2 second/move up (decline) once, stirring
Time is 30-45min.
Mixed material B includes Nylon Nanocomposite aegisox, pamxd6/ nano clay composite material m9 and polyvinyl alcohol
(pva) membrane material, according to weight ratio meter, the Nylon Nanocomposite aegisox:pamxd6/ nano clay composite material
M9: polyvinyl alcohol (pva) membrane material=1:1:1.
The preparation method of mixed material B is, using flour mill to Nylon Nanocomposite aegisox, pamxd6/ nanoclay
Composite material m9 and polyvinyl alcohol (pva) membrane material carry out milling processing respectively, and particulate matter diameter is in 100 mesh, by powdered form
Nylon Nanocomposite aegisox, pamxd6/ nano clay composite material m9 and polyvinyl alcohol (pva) membrane material successively add
Enter into agitator tank, the speed with speed for 300-450r/min is stirred mixing, mixing time 30min.
Mixing C includes distilled water, polyethylene, polyurethane, inorfil cotton and inorganic mineral earth surface insulating mortar, according to weight
Amount is than counting, the distilled water: polyethylene: polyurethane: inorfil cotton: inorganic mineral earth surface insulating mortar=10:3:3:3:4,
Middle inorfil cotton is made of one or more of rock wool, mineral wool, mineral wool, aluminium silicate wool.
Distilled water is that pure water is heated to 280-300 DEG C, is formed after distillation, when preparing mixing C, water temperature is reduced to
After 25-30 DEG C, polyethylene, polyurethane and inorfil cotton are successively added, mixing is stirred with the speed of 150r/min, stirred
Time is 15-18min, finally adds inorganic mineral earth surface insulating mortar, and is stirred with the speed of 280-300r/min mixed
It closes, mixing time 30min.
Inorganic mineral earth surface insulating mortar includes Inorganic nonmetal mineral material (specially aerosil), rosin
Rock glass bead, anti-cracking impervious material (specially FMA-H impermeability and erosion resistance agent) and inorganic coagulation material (specially silicate cement
Mud), according to weight ratio meter, the Inorganic nonmetal mineral material: pitchstone glass bead: anti-cracking impervious material: inorganic gel
Material=1:0.8:0.5:0.5.
Modifying agent is two kinds or three in thickener, coalescing agent, toughener, PH regulator, fire retardant and antistatic agent
Kind composition described above.
The preparation of heat insulation type Environment-friendlyexterior exterior wall paint includes following processing steps:
A) mixing A is previously heated to 60-75 DEG C, and water-bath is kept the temperature, and is stirred with the speed of 500-800r/min, it is stirred
Reinforcing agent, modifying agent, stabilizer, outer lubrication prescription, defoaming agent and modifying agent are added in journey, stir duration 30-40min；
B) mixed material B is added in mixing A mixture, is stirred with the speed of 800-850r/min, stir duration 45min；
C) mixing C is added in mixing A and the mixture of mixed material B, is stirred with the speed of 750-800r/min, when stirring
Long 30min；
D) pigment is added in the mixture of mixing A, mixed material B and mixing C, is stirred with the speed of 750-800r/min,
Duration 8-10min is stirred, then aluminium powder is even added in the mixture of mixing A, mixed material B and mixing C, with 550-650r/min
Speed be stirred, stir duration 10min；
E) screening is filtered to the mixture of mixing A, mixed material B and mixing C, filters out air entrapment；
F) heat-preserving equipment is removed, is stirred with the speed of 300-450r/min, when being cooled to room temperature 20-25 DEG C, stops stirring；
G) it after mixture anaerobic stands 3-4h, examines, packaging, storage
In conclusion the heat insulation type Environment-friendlyexterior exterior wall paint, process flow are simple and efficient, mutually merged using multiple material, mutually
Effect, and mutually assist, synthesis improves the properties of product such as heat insulating ability, the barrier property of entire exterior coating, has exterior coating
The beautiful color of standby metallic luster simultaneously, also with good viscosity, with the attachment degree of building body, good thermal insulation property,
Good barrier property, good forming curing performance and excellent environmental-protecting performance, the exterior coating are being coated in building body
Behind outside, being formed by level itself has good toughness, waterproofness and moisture resistance, with the exclusive flexibility of cotton fibre
In addition, be also equipped with excellent water hardening ability, make when carrying out exterior wall coating, more preferably, faster, be less susceptible to such environmental effects
And rapid condensation solidifies.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (10)
1. a kind of heat insulation type Environment-friendlyexterior exterior wall paint, it is characterised in that: coating proportioning contains: mixing A, mixed material B, mixing C, enhancing
Agent, modifying agent, stabilizer, outer lubrication prescription, defoaming agent, pigment, aluminium powder and modifying agent, the group of the mixing A, mixed material B and mixing C
It is 100 parts fit, 15-70 parts of reinforcing agent, 1-1.5 parts of modifying agent, 0.7-2 parts of stabilizer, outer lubrication prescription 0.2-0.25 parts, defoaming agent
0.15-0.8 parts, 2-2.8 parts of pigment, 1.5-2.8 parts of aluminium powder, 0.3-0.8 parts of modifying agent, according to weight ratio meter, the mixing A:
Mixed material B: mixing C=10:6:6.
2. a kind of heat insulation type Environment-friendlyexterior exterior wall paint according to claim 1, it is characterised in that: the mixing A includes PVC tree
Cosmetics and vegetable oil, according to weight ratio meter, the PVC resin powder: vegetable oil=8:10.
3. a kind of heat insulation type Environment-friendlyexterior exterior wall paint according to claim 2, it is characterised in that: the preparation side of the mixing A
Method is that into vegetable oil, side annular adds PVC resin powder, while being stirred, agitator shaft speed 450r/min, whipping process
In, agitating shaft up and down pull and push, and intromission frequency be 1.5-2 seconds/move up (decline) once, mixing time 30-45min.
4. a kind of heat insulation type Environment-friendlyexterior exterior wall paint according to claim 1, it is characterised in that: the mixed material B includes nylon
Nanocomposite aegisox, pamxd6/ nano clay composite material m9 and polyvinyl alcohol (pva) membrane material, according to weight ratio
Meter, the Nylon Nanocomposite aegisox:pamxd6/ nano clay composite material m9: polyvinyl alcohol (pva) membrane material=
1:1:1。
5. a kind of heat insulation type Environment-friendlyexterior exterior wall paint according to claim 4, it is characterised in that: the preparation side of the mixed material B
Method is, using flour mill to Nylon Nanocomposite aegisox, pamxd6/ nano clay composite material m9 and polyvinyl alcohol
(pva) membrane material carries out milling processing respectively, and particulate matter diameter is in 100 mesh, by the Nylon Nanocomposite of powdered form
Aegisox, pamxd6/ nano clay composite material m9 and polyvinyl alcohol (pva) membrane material are added sequentially in agitator tank, with speed
Degree is that the speed of 300-450r/min is stirred mixing, mixing time 30min.
6. a kind of heat insulation type Environment-friendlyexterior exterior wall paint according to claim 1, it is characterised in that: the mixing C includes distillation
Water, polyethylene, polyurethane, inorfil cotton and inorganic mineral earth surface insulating mortar, according to weight ratio meter, the distilled water: poly-
Ethylene: polyurethane: inorfil cotton: inorganic mineral earth surface insulating mortar=10:3:3:3:4, wherein inorfil cotton by rock wool,
One or more of mineral wool, mineral wool, aluminium silicate wool composition.
7. a kind of heat insulation type Environment-friendlyexterior exterior wall paint according to claim 6, it is characterised in that: the distilled water is pure water
It is heated to 280-300 DEG C, is formed after distillation, when preparing mixing C, after water temperature is reduced to 25-30 DEG C, successively adds poly- second
Alkene, polyurethane and inorfil cotton are stirred mixing with the speed of 150r/min, and mixing time 15-18min finally adds
Add inorganic mineral earth surface insulating mortar, and mixing, mixing time 30min are stirred with the speed of 280-300r/min.
8. a kind of heat insulation type Environment-friendlyexterior exterior wall paint according to claim 6, it is characterised in that: the heat-insulated guarantor of inorganic mineral
Warm mortar includes Inorganic nonmetal mineral material (specially aerosil), pitchstone glass bead, anti-cracking impervious material
Expect (specially FMA-H impermeability and erosion resistance agent) and inorganic coagulation material (specially portland cement), according to weight ratio meter, the nothing
Machine nonmetallic mineral material: pitchstone glass bead: anti-cracking impervious material: inorganic coagulation material=1:0.8:0.5:0.5.
9. a kind of heat insulation type Environment-friendlyexterior exterior wall paint according to claim 1, it is characterised in that: the modifying agent is thickening
Two or three of composition described above in agent, coalescing agent, toughener, PH regulator, fire retardant and antistatic agent.
10. a kind of heat insulation type Environment-friendlyexterior exterior wall paint according to claim 1, it is characterised in that: the heat insulation type environmental protection is outer
The preparation of wall coating includes following processing steps:
A) mixing A is previously heated to 60-75 DEG C, and water-bath is kept the temperature, and is stirred with the speed of 500-800r/min, it is stirred
Reinforcing agent, modifying agent, stabilizer, outer lubrication prescription, defoaming agent and modifying agent are added in journey, stir duration 30-40min；
B) mixed material B is added in mixing A mixture, is stirred with the speed of 800-850r/min, stir duration 45min；
C) mixing C is added in mixing A and the mixture of mixed material B, is stirred with the speed of 750-800r/min, when stirring
Long 30min；
D) pigment is added in the mixture of mixing A, mixed material B and mixing C, is stirred with the speed of 750-800r/min,
Duration 8-10min is stirred, then aluminium powder is even added in the mixture of mixing A, mixed material B and mixing C, with 550-650r/min
Speed be stirred, stir duration 10min；
E) screening is filtered to the mixture of mixing A, mixed material B and mixing C, filters out air entrapment；
F) heat-preserving equipment is removed, is stirred with the speed of 300-450r/min, when being cooled to room temperature 20-25 DEG C, stops stirring；
G) it after mixture anaerobic stands 3-4h, examines, packaging, storage.