CN103030335A - Colored rock paint and preparation method thereof - Google Patents

Colored rock paint and preparation method thereof Download PDF

Info

Publication number
CN103030335A
CN103030335A CN2012105771694A CN201210577169A CN103030335A CN 103030335 A CN103030335 A CN 103030335A CN 2012105771694 A CN2012105771694 A CN 2012105771694A CN 201210577169 A CN201210577169 A CN 201210577169A CN 103030335 A CN103030335 A CN 103030335A
Authority
CN
China
Prior art keywords
colored stone
lacquer
colored
stone lacquer
thickening
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012105771694A
Other languages
Chinese (zh)
Other versions
CN103030335B (en
Inventor
王�义
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Baochen joint Polytron Technologies Inc
Original Assignee
BEIJING TIANWEI BAOCHEN CHEMICAL PRODUCT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BEIJING TIANWEI BAOCHEN CHEMICAL PRODUCT Co Ltd filed Critical BEIJING TIANWEI BAOCHEN CHEMICAL PRODUCT Co Ltd
Priority to CN201210577169.4A priority Critical patent/CN103030335B/en
Publication of CN103030335A publication Critical patent/CN103030335A/en
Application granted granted Critical
Publication of CN103030335B publication Critical patent/CN103030335B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses colored rock paint which comprises the following components in mass percentage: 90-93% of colored sand and 6-9% of acrylic based emulsion powder. The invention further discloses a preparation method of the colored rock paint, which comprises the steps of putting the colored sand, the acrylic based emulsion powder, and a thickening agent into a double-screw dry-mixed mortar mixer according to the mass percentage in the colored rock paint, and stirring and obtaining the powder-shaped colored rock paint. The colored rock paint and the preparation method thereof have the advantages that the acrylic based emulsion powder is added into the colored rock paint to serve as a binding material of the powder-shaped colored rock paint, and provides the colored rock paint with high cohesiveness, low water-absorbing property, good crack resistance, efflorescence resistance and long-term durability; and as the prepared colored rock paint is powder-shaped, compared with the traditional pasty colored rock paint, the colored rock paint is convenient and quick to use in a construction process, convenient to package, low in transportation cost, low-toxic, safe, and environment-friendly, and is a good wall material and an indoor decorating material.

Description

A kind of colored stone lacquer and preparation method thereof
Technical field
The invention belongs to building material technical field, be specifically related to a kind of colored stone lacquer.
Background technology
Existing material of construction is along with people are developed for the house quality requirements, and particularly as this material of construction for decorated wall surface of colored stone lacquer, people require more and more higher and diversified for architecture inside and outside decoration.Tradition colored stone lacquer is to mix into paste by emulsion, sand, pigment and auxiliary agent in factory, is divided in the plastic tank, then transports the working-yard to and uses.Paste colored stone lacquer exists that the packed and transported cost is high, large, storage in the winter difficulty of smell when using, summer the shortcoming such as anticorrosion difficulty, be very limited so that paste uses at cold district, and use the paste colored stone to paint Ben Taigao in distance emulsion grown place than the territory, far field.
In addition, also has a kind of facing mortar, take cement as main raw material(s) more in addition inorganic coagulation material and pigment as wall decoration, but, the color of this mortar does not have rich and variedization of colored stone lacquer, moulding is few, without stereoscopic sensation, and this facing mortar is because main material is cement, very easily the accumulation of salt in the surface soil and produce aberration.
Summary of the invention
For addressing the above problem, the invention discloses a kind of colored stone lacquer, the working-yard is stirred convenient to use, and colored stone lacquer of the present invention is Powdered packaged convenience, transportation cost is low, do not contain toxic substance, volatility is extremely low, to construction workman and user's toxicological harmless side effect, high-adhesion, good splitting resistance, the inhibition accumulation of salt in the surface soil, the long durability of low water absorbable, thereby the decorative effect of assurance colored stone lacquer can not be subjected to the impact of the gentle time of moisture lastingly, reaches color and texture nature, vision is soft, expressive force is abundant, the strong texts of stereoscopic sensation.
For achieving the above object, the technical solution adopted in the present invention is: a kind of colored stone lacquer provided by the invention, and this colored stone enamel-cover is drawn together color sand and acrylic latex powder, and each composition is respectively in the mass percent of colored stone lacquer, color sand 90~93%, acrylic latex powder 6~9%.The used acrylic latex powder of the present invention is the product that our company's (being sky, Beijing Wellable occasion chemical products company limited) produces, its trade name is that TIONES board colored stone coats with lacquer special-purpose acrylic latex powder 6021A, acrylic latex powder is added in the colored stone lacquer, mix with color sand, can realize the dry powder of colored stone lacquer.And acrylic latex powder has the incomparable advantage of the true mineral varnish of emulsion-type in production, packing, transportation, storage and use.In addition, the free formaldehyde content of this latex powder is zero, environmental protection.And in production formula, needn't add mould inhibitor, sanitas and frostproofer.Production formula is simple, and production control is easy.The pure acrylic acid redispersable latex powder provides high-adhesion, low water absorbable, good splitting resistance, suppresses the accumulation of salt in the surface soil, long durability for colored stone lacquer, thereby the decorative effect of assurance colored stone lacquer can not be subjected to the impact of the gentle time of moisture lastingly, reaches color and texture nature, vision is soft, expressive force is abundant, the strong texts of stereoscopic sensation.
Above-mentioned colored stone lacquer also comprises thickening material, and thickening material is 0.05~0.1% in the mass percent of colored stone lacquer.
Colored stone lacquer of the present invention also comprises mineral dye, and mineral dye is 0~1% in the mass percent of colored stone lacquer.
Color grain fineness number in the prescription of above-mentioned colored stone lacquer is 10~140 orders.Color sand is as the filler of colored stone lacquer, and selection and the collocation of color sand grains footpath size, color are determining the texture effect that the single-component colored stone coats with lacquer, and the size of color sand total amount is determining acrylic latex powder amount size, and then is determining colored stone lacquer over-all properties.
Thickening material in the colored stone paint formula of the present invention, what select is that viscosity is the hydroxypropyl methyl cellulose ether of 20000~150000mpa ﹒ s under 20~30 ° of C of temperature.Ether of cellulose is the thickening material of colored stone lacquer, and its consumption is adjusted according to application property, when proportioning, determines its consumption according to viscosity measurement.
Also can add mineral dye in the above-mentioned colored stone lacquer, mineral dye comprises a kind of, two or more mixing in red iron oxide, iron oxide yellow, the blue or green orchid of phthalein, the cobalt blue.Can adjust and enrich changeable color for decorating needs, and and the acrylic latex powder bond strength high, can not produce aberration, for a long time can the accumulation of salt in the surface soil yet, generation yellowing phenomenon.
The invention also discloses the method for preparing the colored stone lacquer, this production method for the color sand of 10~140 purposes, acrylic latex powder, thickening material according to the mass percent of each composition in the colored stone lacquer: color sand 90~93%, acrylic latex powder 6~9%, thickening material 0.05~0.1% drop in the double-screw type dry-mix mixer and stir, temperature is 20~30 ° of C, stir 15min, packing namely obtains the colored stone lacquer of powder shaped.The present invention is made into powder shaped with the colored stone lacquer, and common paper bag or woven bag get final product packed and transported, and the scene adds water can use, and is convenient succinct.And traditional paste colored stone lacquer needs special little plastic tank packing, and packing and transportation cost are far above powder-like product of the present invention, and patent of the present invention can be avoided the shortcomings such as traditional paste colored stone lacquer smell is large, VOC content height.
Selected thickening material is that viscosity is the hydroxypropyl methyl cellulose ether of 20000~150000mpa ﹒ s under 20~30 ° of C of temperature among the above-mentioned preparation method.
The present invention produces the method for colored stone lacquer, in the colored stone paint formula, also can add by in blue or green blue, the cobalt blue of red iron oxide, iron oxide yellow, phthalein a kind of, two or more mixes the mineral dye that forms, and mineral dye is 0~1% in the mass percent of colored stone lacquer, makes to form the diversified powder shaped colored stone lacquer of color.
To sum up, useful technique effect of the present invention, added the gelling material of acrylic latex powder as powdery single-component colored stone lacquer in the colored stone lacquer of the present invention, redispersable latex powder plays decisive role to the over-all properties of powder shaped colored stone lacquer, the pure acrylic acid latex powder considers latex powder second-order transition temperature, minimum film-forming temperature, unit elongation, burst size of methanal, water tolerance, weathering resistance to be selected on the basis, and the volume of acrylic latex powder is determined according to experiment.Redispersable latex powder is mainly ethene-vinyl acetate copolymerization rubber powder, vinyl acetate between to for plastic-tertiary monocarboxylic acid ethylene copolymer rubber powder, pure acrylate emulsion copolymer powder etc. on the domestic market, we find in the situation of identical volume by a large amount of experiments, the water tolerance of acrylic latex powder, weathering resistance significantly are better than the other types rubber powder, auxiliary inorganic film-forming components consumption can reduce comparatively speaking, and this is very beneficial for improving the over-all properties of colored stone lacquer.
The colored stone lacquer that the present invention makes is powder shaped, the paste colored stone lacquer of comparing traditional, easy to use during construction, quick, the water that only needs to add colored stone lacquer powder 14~20% mixes and gets final product, and packaged convenience, transportation cost are low, safety low-poison environmental protection, powder shaped color easily are in harmonious proportion, color is enriched changeable, and water-intake rate is low, also can not produce for a long time the accumulation of salt in the surface soil, yellowing phenomenon, stereoscopic sensation is strong, is good body of wall, indoor hardware fitting.
Embodiment
Below in conjunction with specific embodiment summary of the invention is described further.
Embodiment one: colored stone lacquer disclosed by the invention, this colored stone enamel-cover is drawn together color sand and acrylic latex powder, and each composition is respectively color sand 90%, acrylic latex powder 9% in the mass percent of colored stone lacquer.
Also comprise thickening material in the above-mentioned colored stone paint formula, and thickening material is 0.05~0.1% in the mass percent of colored stone lacquer, selected thickening material is that viscosity is the hydroxypropyl methyl cellulose ether of 20000~150000mpa ﹒ s under 20~30 ° of C of temperature.
Color grain fineness number in the above-mentioned colored stone paint formula is 10~140 orders.
The present invention produces the method for colored stone lacquer, this production method for the color sand of 10~140 purposes, acrylic latex powder, thickening material according to the mass percent of each composition in the colored stone lacquer: color sand 90%, acrylic latex powder 9%, thickening material 0.05~0.1% drop in the double-screw type dry-mix mixer and stir, temperature is 20~30 ° of C, stir 15min, packing namely obtains the colored stone lacquer of powder shaped.
Used thickening material is that viscosity is the hydroxypropyl methyl cellulose ether of 20000~150000mpa ﹒ s under 20~30 ° of C of temperature in the production method.
Embodiment two: the prescription of colored stone lacquer of the present invention is color sand 93%, and acrylic latex powder 6%, thickening material 0.05%, mineral dye 1%, above-mentioned percentage ratio are the mass percent of each composition in the colored stone lacquer.
Color grain fineness number in the above-mentioned colored stone paint formula is 10~140 orders, and what thickening material was selected is that viscosity is the hydroxypropyl methyl cellulose ether of 20000~150000mpa ﹒ s under 20~30 ° of C of temperature.
The mineral dye that adds in the colored stone lacquer comprises a kind of, two or more mixing in red iron oxide, iron oxide yellow, the blue or green orchid of phthalein, the cobalt blue.
Produce the method for present embodiment colored stone lacquer, this production method stirs for the color sand of 10~140 purposes, acrylic latex powder, thickening material, mineral dye are dropped in the double-screw type dry-mix mixer according to above-mentioned mass percent, temperature is 20~30 ° of C, stir 15min, packing namely obtains the colored stone lacquer of powder shaped.The thickening material of using in the production method and mineral dye are all the same.
Embodiment three: the prescription of colored stone lacquer of the present invention is color sand 92%, and acrylic latex powder 7%, thickening material 0.08%, mineral dye 0.06%, above-mentioned percentage ratio are the mass percent of each composition in the colored stone lacquer.
Color grain fineness number in the above-mentioned colored stone paint formula is 10~140 orders, and what thickening material was selected is that viscosity is the hydroxypropyl methyl cellulose ether of 20000~150000mpa ﹒ s under 20~30 ° of C of temperature.
The mineral dye that adds in the colored stone lacquer comprises a kind of, two or more mixing in red iron oxide, iron oxide yellow, the blue or green orchid of phthalein, the cobalt blue.
Production method is with embodiment two.
Embodiment four: the prescription of colored stone lacquer of the present invention is color sand 91%, and acrylic latex powder 8%, thickening material 0.06%, mineral dye 0.04%, above-mentioned percentage ratio are the mass percent of each composition in the colored stone lacquer.
Color grain fineness number in the above-mentioned colored stone paint formula is 10~140 orders, and what thickening material was selected is that viscosity is the hydroxypropyl methyl cellulose ether of 20000~150000mpa ﹒ s under 20~30 ° of C of temperature.
The mineral dye that adds in the colored stone lacquer comprises a kind of, two or more mixing in red iron oxide, iron oxide yellow, the blue or green orchid of phthalein, the cobalt blue.
Production method is with embodiment two.
The powder shaped colored stone lacquer that four embodiment of the present invention obtain is checked product performance according to " synthetic resin emulsion sandy paint " (JG/T 24-2000).
Can find out that according to test-results time of drying is fast, alkali resistance is strong, and water tolerance is good, and alkali resistance is excellent, and cohesive strength is high, and artificial ageing resistance can reach paste colored stone lacquer performance index fully.Because its single-component, high low temperature stability in storage are much better than paste colored stone lacquer.
Present embodiment is not any restriction that invention is made only for further specifying the present invention, all the present invention in fact the simple modification made of content and improving all still belong within the protection domain of technical solution of the present invention.

Claims (9)

1. a colored stone lacquer is characterized in that this colored stone enamel-cover is drawn together color sand and acrylic latex powder, and each composition is respectively color sand 90~93%, acrylic latex powder 6~9% in the mass percent of colored stone lacquer.
2. colored stone lacquer according to claim 1 is characterized in that, this colored stone lacquer also comprises thickening material, and thickening material is 0.05~0.1% in the mass percent of colored stone lacquer.
3. colored stone lacquer according to claim 1 is characterized in that, this colored stone lacquer also comprises mineral dye, and mineral dye is 0~1% in the mass percent of colored stone lacquer.
4. colored stone lacquer according to claim 1 is characterized in that the fineness of described color sand is 10~140 orders.
5. colored stone lacquer according to claim 2 is characterized in that described thickening material is that viscosity is the hydroxypropyl methyl cellulose ether of 20000~150000mpa ﹒ s under 20~30 ° of C of temperature.
6. colored stone lacquer according to claim 3 is characterized in that, described mineral dye comprises a kind of, two or more mixing in red iron oxide, iron oxide yellow, the blue or green orchid of phthalein, the cobalt blue.
7. one kind prepares the method that the described colored stone of claim 1 coats with lacquer, it is characterized in that, this production method for the color sand of 10~140 purposes, acrylic latex powder, thickening material according to the mass percent of each composition in the colored stone lacquer: color sand 90~93%, acrylic latex powder 6~9%, thickening material 0.05~0.1% drop in the double-screw type dry-mix mixer and stir, temperature is 20~30 ° of C, stir 15min, packing namely obtains the colored stone lacquer of powder shaped.
8. a kind of method for preparing the colored stone lacquer according to claim 7 is characterized in that described thickening material is that viscosity is the hydroxypropyl methyl cellulose ether of 20000~150000mpa ﹒ s under 20~30 ° of C of temperature.
9. a kind of method for preparing colored stone lacquer according to claim 7, it is characterized in that, in the colored stone paint formula, also can add by in blue or green blue, the cobalt blue of red iron oxide, iron oxide yellow, phthalein a kind of, two or more mixes the mineral dye that forms, and mineral dye is 0~1% in the mass percent that colored stone coats with lacquer.
CN201210577169.4A 2012-12-27 2012-12-27 Colored rock paint and preparation method thereof Active CN103030335B (en)