CN106495591A - A kind of fire proofing material - Google Patents
A kind of fire proofing material Download PDFInfo
- Publication number
- CN106495591A CN106495591A CN201610969092.3A CN201610969092A CN106495591A CN 106495591 A CN106495591 A CN 106495591A CN 201610969092 A CN201610969092 A CN 201610969092A CN 106495591 A CN106495591 A CN 106495591A
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- black mud
- slag
- zirconium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of fire proofing material, including the following raw material of parts by weight：The mixture of black mud powder or black mud particle and pulverized slag or slag granules, red beach powder or 55 65 parts of white afrodite powder, aquamaine stone flour or andalusite powder or 11 13 parts of 30 35 parts of sillimanite powder, zirconium silicate powder or yttrium stable zirconium oxide powder, 25 29 parts of cement, 9 11 parts of fiber, Alumina gel or yttrium colloidal sol or zirconium colloidal sol or 3.5 4 parts of silicon-aluminum sol.The invention has the advantages and positive effects of：The fire proofing material refractory temperature of the present invention is high, low cost of manufacture, and preparation method is simple, it is easy to produce, fire resistance period is long, and refractory temperature is high, low production cost, steady quality.
Description
Technical field
The invention is related to a kind of fire proofing material, belongs to fireproof material technology field.
Background technology
Fire proofing material is used for building, and form is various to play critical effect, conventional fire prevention to modern fire prevention
Material includes PLASTIC LAMINATED, fire resistant doorsets, flame resistant glass, fireproof coating fire prevention bag etc..With development in science and technology, people are to fire proofing material
Require more and more higher, can cost increasing, therefore, we research and develop the high fire proofing material of a kind of low cost, fire protecting performance.
Content of the invention
The invention problem to be solved is to research and develop the high fire proofing material of a kind of low cost, fire protecting performance.
For solving above-mentioned technical problem, the technical scheme that the invention is adopted is：A kind of fire proofing material, its feature exist
In：Following raw material including parts by weight：Black mud powder or black mud particle and pulverized slag or mixture, the red beach of slag granules
Powder or white afrodite powder 55-65 parts, aquamaine stone flour or andalusite powder or sillimanite powder 30-35 part, zirconium silicate powder or yttrium are stablized
Zirconia powder 11-13 parts, cement 25-29 parts, fiber 9-11 parts, Alumina gel or yttrium colloidal sol or zirconium colloidal sol or silicon-aluminum sol
3.5-4 part；Also include water and animal composite foamable agent；The amount of the water meet can make black mud powder or black mud particle or pulverized slag or
The mixture of slag granules or black mud powder or black mud particle and pulverized slag or slag granules, red beach powder or white afrodite powder, indigo plant
Spar powder or andalusite powder or sillimanite powder, zirconium silicate powder or yttrium stable zirconium oxide powder, cement, calgon and fiber
Mixture forms thick；The animal composite foamable agent is configured to the aqueous solution, and its concentration is 5%-12%, then by the water
Solution makes foam slurry in foaming machine, and foam diameter is：0.5mm-2mm, the volume of the foam slurry and other all materials
The volume ratio of summation is 5-10: 1.
The invention has the advantages and positive effects of：The fire proofing material refractory temperature of the present invention is high, manufacturing cost
Low, preparation method is simple, it is easy to produce, and fire resistance period is long, and refractory temperature is high, low production cost, steady quality.
Specific embodiment
A kind of fire proofing material, it is characterised in that：Following raw material including parts by weight：Black mud powder or black mud particle and stove
The mixture of ground-slag or slag granules, red beach powder or white afrodite powder 55-65 parts, aquamaine stone flour or andalusite powder or silicon line
Stone flour 30-35 parts, zirconium silicate powder or yttrium stable zirconium oxide powder 11-13 parts, cement 25-29 parts, fiber 9-11 parts, Alumina gel or
Yttrium colloidal sol or zirconium colloidal sol or silicon-aluminum sol 3.5-4 parts；Also include water and animal composite foamable agent；The amount of the water meets energy
Make the mixed of black mud powder or black mud particle or pulverized slag or slag granules or black mud powder or black mud particle and pulverized slag or slag granules
Compound, red beach powder or white afrodite powder, aquamaine stone flour or andalusite powder or sillimanite powder, zirconium silicate powder or yttrium are stably aoxidized
The mixture of zirconium powder, cement, calgon and fiber forms thick；The animal composite foamable agent is configured to the aqueous solution,
Its concentration is 5%-12%, and the aqueous solution is made in foaming machine foam slurry then, and foam diameter is：0.5mm-2mm, described
The volume of foam slurry is 5-10: 1 with the volume ratio of other all material summations.
Above the embodiment of the invention is described in detail, but the content has been only the preferable of the invention
Embodiment, it is impossible to be considered as limit the present invention practical range.All impartial changes that is made according to the invention scope with
Improve etc., still all should belong within this patent covering scope.
Claims (1)
1. a kind of fire proofing material, it is characterised in that：Following raw material including parts by weight：Black mud powder or black mud particle and slag
The mixture of powder or slag granules, red beach powder or white afrodite powder 55-65 parts, aquamaine stone flour or andalusite powder or sillimanite
Powder 30-35 parts, zirconium silicate powder or yttrium stable zirconium oxide powder 11-13 parts, cement 25-29 parts, fiber 9-11 parts, Alumina gel or yttrium
Colloidal sol or zirconium colloidal sol or silicon-aluminum sol 3.5-4 parts；Also include water and animal composite foamable agent；The amount of the water meets can be made
Black mud powder or the mixing of black mud particle or pulverized slag or slag granules or black mud powder or black mud particle and pulverized slag or slag granules
Thing, red beach powder or white afrodite powder, aquamaine stone flour or andalusite powder or sillimanite powder, zirconium silicate powder or yttrium stable zirconium oxide
The mixture of powder, cement, calgon and fiber forms thick；The animal composite foamable agent is configured to the aqueous solution, its
Concentration is 5%-12%, and the aqueous solution is made in foaming machine foam slurry then, and foam diameter is：0.5mm-2mm, the bubble
The volume of foam slurry is 5-10: 1 with the volume ratio of other all material summations.