CN101548202A - 用于显示面板的滤光片和制备该滤光片的方法 - Google Patents
用于显示面板的滤光片和制备该滤光片的方法 Download PDFInfo
- Publication number
- CN101548202A CN101548202A CNA200780041585XA CN200780041585A CN101548202A CN 101548202 A CN101548202 A CN 101548202A CN A200780041585X A CNA200780041585X A CN A200780041585XA CN 200780041585 A CN200780041585 A CN 200780041585A CN 101548202 A CN101548202 A CN 101548202A
- Authority
- CN
- China
- Prior art keywords
- acrylate
- optical filter
- layer
- electromagnetic radiation
- radiation shielding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
通过印刷法形成一种包括在滤光片中的电磁辐射屏蔽层,从而可以使用简单的方法制备具有良好性能的滤光片。
Description
技术领域
本发明涉及一种用于显示面板的滤光片和制备该滤光片的方法。更具体而言,本发明涉及一种用于等离子体显示面板(PDP)的滤光片,其中,电磁辐射屏蔽层通过凹版胶印法(gravure offset method)直接形成在玻璃基板上。
背景技术
除其它组件外,显示面板通常装备有能够阻挡对人体健康造成不利影响和导致电子设备故障的电磁辐射和近红外线(NIR)的滤光片。
目前可用于等离子体显示面板(PDP)的用于阻挡有害电磁辐射的滤光片通常可被分为三类:i)通过将铜膜附着在聚酯(例如,聚对苯二甲酸乙二酯)的基板膜上并通过刻蚀法图形化该铜膜而制备的金属网状膜,ii)通过在基板膜上加工金属纤维或带金属涂层的有机纤维并图形化该纤维而制备的纤维网状膜,以及iii)通过使用例如溅射的干法涂覆法交替层叠金属(Ag)层和电介质层而制备的多层导电膜。
然而,由于其复杂的制备过程和对材料的低效率使用,这种电磁辐射屏蔽滤光片的制备成本较高。而且,当使用单独的基板膜制备包括电磁辐射屏蔽层的滤光片时,需要粘合剂层将电磁辐射屏蔽层粘附在基板膜上。特别是,使用如图1所示的常规的网状电磁辐射屏蔽滤光片,由于十分模糊而难以实现栩栩如生的图像。因此,为了将网状电磁辐射屏蔽层用作改善的滤光片,必须单独形成透明的树脂作为粘合剂层而使可见光透过该滤光片。
因此,对能够易于以低成本生产的PDP滤光片的开发需求日益增加,该滤光片展示出优异的电磁辐射屏蔽性和光学特性。
发明内容
因此,本发明的一个目的是提供一种制备用于显示面板的滤光片的改进方法。
根据本发明的一个实施方案,其提供了一种制备用于显示面板的滤光片的方法,该滤光片包括透明玻璃基板和电磁辐射屏蔽层,该方法包括通过在玻璃基板上通过直接印刷组合物来形成电磁辐射屏蔽层的步骤,该组合物包含:(a)5~30wt%的丙烯酸酯聚合物树脂、(b)5~30wt%的可交联低聚物、(c)0.1~5wt%的光聚合引发剂和(d)50~85wt%的金属粉末。
附图说明
当结合附图时,从本发明的下述说明中,本发明的上述和其它目的和特征将变得显而易见,附图分别显示:
图1为说明常规的滤光片结构的剖视图;
图2为说明根据本发明的一个实施方式的滤光片结构的剖视图;以及
图3为说明根据本发明的另一个实施方式的滤光片结构的剖视图。
<附图中附图标记的简要说明>
100:减反射层
110:基板膜
120:粘合剂层
130:玻璃基板
140:粘合剂层
150:基板膜
160:电磁辐射屏蔽层
170:粘合剂层
180:近红外线阻挡和选择性光吸收层
190:基板膜
200:减反射层
210:基板膜
220:粘合剂层
230:基板膜
240:近红外线阻挡和选择性光吸收层
250:粘合剂层
260:玻璃基板
270:电磁辐射屏蔽层
300:减反射层
310:基板膜
320:粘合剂层
330:玻璃基板
340:电磁辐射屏蔽层
350:粘合剂层
360:近红外线阻挡和选择性光吸收层
370:基板膜
具体实施方式
根据本发明,通过直接在玻璃基板上形成导电网状图形,例如采用凹版胶印法,来形成电磁辐射屏蔽层。这样形成的电磁辐射屏蔽层具有优异的机械特性(例如,膜粘附性)和导电性。
用于形成根据本发明的电磁辐射屏蔽层的组合物包含:(a)5~30wt%的丙烯酸酯聚合物树脂、(b)5~30wt%的可交联低聚物、(c)0.1~5wt%的光聚合引发剂和(d)50~85wt%的金属粉末。
组分(a),丙烯酸酯聚合物树脂,可以选自本领域公知的丙烯酸酯聚合物树脂。优选地,通过聚合不饱和羧酸单体、芳香族单体以及除不饱和羧酸单体和芳香族单体外的单体可以制备丙烯酸酯聚合物树脂。
将不饱和羧酸单体通过增加氢键用于增加丙烯酸酯聚合物树脂的弹性。具体而言,不饱和羧酸单体可以为丙烯酸、甲基丙烯酸、衣康酸、马来酸、富马酸、乙烯基乙酸或其酸酐。基于在制备丙烯酸酯聚合物树脂中的所使用的单体的总量,可以使用20~50wt%量的不饱和羧酸单体。当不饱和羧酸单体的含量在上述范围内时,可以得到聚合物树脂所需的弹性特性和所需的聚合度,并且也可以防止聚合过程中的凝胶化。
芳香族单体是一种丙烯酸系单体,其提供对玻璃基板良好的粘合性(adhesibility)以允许进行稳定图形化,例如,苯乙烯、苄基甲基丙烯酸酯、苄基丙烯酸酯、苯基丙烯酸酯、苯基甲基丙烯酸酯、2-硝基苯基丙烯酸酯、4-硝基苯基丙烯酸酯、2-硝基苯基甲基丙烯酸酯、4-硝基苯基甲基丙烯酸酯、4-氯苯基丙烯酸酯等。基于在制备丙烯酸酯聚合物树脂中所使用的单体的总量,可以使用10~30wt%,优选为15~20wt%量的芳香族单体。当芳香族单体的含量在上述范围内时,可以满足如下所有的要求:图形对基板良好的粘附性、图形良好的方向性、稳定的图形化和通过烧结容易除去有机材料。
在制备丙烯酸酯聚合物树脂中使用的除了不饱和羧酸单体和芳香族单体之外的单体(在下文中,称作“其它单体”)起到调节丙烯酸酯聚合物的玻璃化转变温度和极性的作用。其它单体可以为丙烯酸系单体,例如,(甲基)丙烯酸-2-羟乙酯、(甲基)丙烯酸-2-羟辛酯、(甲基)丙烯酸甲酯、(甲基)丙烯酸乙酯或丙烯酸正丁酯。基于在制备丙烯酸酯聚合物树脂中所使用的单体的总量,可以使用20~60wt%量的其它单体,该其它单体影响丙烯酸酯聚合物树脂的玻璃化转变温度、所得图形的耐热性和图形与基板的紧密接触。
为了防止这些单体凝胶化并在胶版印刷过程中提供合适的蒸发速率,在溶剂存在下通过聚合不饱和羧酸单体、芳香族单体和其它单体可以制备丙烯酸酯聚合物树脂。该溶剂可以为丙二醇单甲醚、二丙二醇单甲醚、丙二醇单甲醚丙酸酯、乙醚丙酸酯(ethylether propionate)、松油醇、丙二醇单甲醚乙酸酯、二甲氨基甲醛、甲乙酮、丁基卡必醇、丁基卡必醇乙酸酯、γ-丁内酯、乳酸乙酯或其混合物。
在溶剂存在下通过聚合不饱和羧酸单体、芳香族单体和其它单体得到的丙烯酸酯聚合物树脂的重均分子量可以为10,000~100,000,更优选为20,000~50,000。当丙烯酸酯聚合物树脂的重均分子量在上述范围内时,丙烯酸酯聚合物树脂的玻璃化转变温度降低,因此,丙烯酸酯聚合物树脂的流动性变得符合在胶印法中将在凹版凹槽中的图形转移至覆盖层(blanket)上的要求,并且由于丙烯酸酯聚合物树脂良好的弹性特性,也使得将组合物传送至凹版凹槽中变得令人满意。
在根据本发明的组合物中使用的丙烯酸酯聚合物树脂的量为5~30wt%。如果丙烯酸酯聚合物树脂的含量小于5wt%时,由于组合物降低的弹性,而不能高效地实施胶印法。另一方面,如果丙烯酸酯聚合物树脂的含量大于30wt%,所得图形的电阻率可能增加。
组分(b),可交联低聚物,可以为含有至少两个烯双键的丙烯酸酯化合物。具体而言,可交联低聚物可以为1,4-丁二醇二丙烯酸酯、1,3-丁二醇二丙烯酸酯、乙二醇二丙烯酸酯、季戊四醇四丙烯酸酯、三甘醇二丙烯酸酯、双酚A二丙烯酸酯衍生物、包含尿烷键的二丙烯酸酯衍生物、三甲基丙烷三丙烯酸酯、二季戊四醇多丙烯酸酯、其甲基丙烯酸酯或其混合物。
在本发明的组合物中,使用5~30wt%,优选为5~15wt%量的可交联低聚物。如果可交联低聚物的含量小于5wt%,由于组合物增加的粘度,图形化可能变得难以进行。另一方面,如果可交联低聚物的含量大于30wt%,由于聚合物降低的弹性,所得图形的分离特性(off characteristic)和方向性可能变差。
组分(c),光聚合引发剂,可以为一种选自如三嗪类、苯偶姻乙酰苯类和咪唑类的化合物中的至少一种。
光聚合物引发剂以0.1~5wt%的量包含在本发明的组合物中。如果光聚合引发剂的含量小于0.1wt%,所得图形的粘附性可能变得不令人满意。另一方面,如果光聚合引发剂的含量大于5wt%,光聚合物引发剂可能仍然未溶解。
组分(d),金属粉末,没有特别限制且其可以为在形成用于显示器的电极中使用的金属粉末或者可以为用于阻挡电磁辐射的金属粉末。优选地,金属粉末为银、铜、镍、ATO(氧化锑锡)或其合金的金属粉末。
在本发明的组合物中使用50~85wt%量的金属粉末。如果金属粉末的含量小于50wt%,难以实现所需的电磁辐射屏蔽性能。另一方面,如果金属粉末的含量超过85wt%,则由于组合物增加的粘度可能产生差的分散性。
如有必要,本发明的组合物可以进一步包含选自用于分散金属粉末的分散剂、用于调节对比度的炭黑、用于通过烧结增加对玻璃基板的粘附性的玻璃粉等中的添加剂。在本发明的组合物中可以使用0.01~10wt%,更优选为0.1~3wt%量的添加剂。
由根据本发明的组合物形成的电磁辐射屏蔽层具有大约为0.2~1.2Ω/□的表面电阻率。
除了电磁辐射屏蔽层之外,根据本发明的滤光片可以包括本领域公知的功能层,即,减反射层以及近红外线(NIR)阻挡和选择性光吸收层。
NIR阻挡和选择性光吸收层包含NIR阻挡材料和选择性光吸收材料。该NIR-阻挡材料可以为基于镍配合物的化合物和基于二铵的化合物的混合物、包含铜和锌离子的颜料化合物、有机颜料等,以及选择性光吸收材料可以为含有位于八苯基四氮杂卟啉(octaphenyltetraazaporphyrin)或四氮杂卟啉环中心的金属元素的金属配合物衍生物颜料,以及选自与金属元素配位的铵、水和卤素中的材料。可以通过在溶剂中将上述用于NIR-阻挡材料和选择性光吸收材料的颜料与透明塑料树脂混合以制备溶液混合物,并将该溶液混合物涂覆在透明基板上形成1~20μm的厚度来制备该NIR-阻挡和选择性光吸收层。在此,该透明塑料树脂可以为聚(甲基丙烯酸甲酯)(PMMA)、聚乙烯醇(PVA)、聚碳酸酯(PC)、乙烯乙酸乙烯酯(EVA)、聚(乙烯醇缩丁醛)(PVB)、聚对苯二甲酸乙二酯(PET)等,并且溶剂可以为甲苯、二甲苯、丙酮、甲乙酮(MEK)、丙醇、异丙醇、甲基溶纤剂、乙基溶纤剂、二甲基甲酰胺(DMF)等。
对于减反射层,通过对基板膜进行耐划痕处理,然后用亚克力树脂(acrylresin)进行硬性涂覆(hard coating)可以形成单层的低折射率膜,或者,其可以为通过交替层叠高折射率透明膜和低折射率透明膜得到的层。使用包含上述材料的溶液通过真空沉积法或通过湿法涂覆(例如,辊涂法或模压涂覆法)可以形成减反射层。
可以在不同的基板上形成减反射层以及NIR-阻挡和选择性光吸收层,或者,可以分别形成在基板的前面和后面。NIR-阻挡和选择性光吸收层也可以由通过使粘合剂与NIR-阻挡颜料和选择性光吸收颜料混合得到的混合物来形成。
在图2和3中显示了根据本发明的滤光片的优选实施方式。参照图2,将用于防止外部光线反射的减反射层200通过透明粘合剂层220设置在NIR-阻挡和选择性光吸收层240上并使其朝向外部,通过上述方法,直接在玻璃基板260上形成电磁辐射屏蔽层270,以及将NIR-阻挡和选择性光吸收层240通过透明粘合剂层250层叠在玻璃基板260的正面以使其与电磁辐射屏蔽层270相对,从而得到用于显示面板的滤光片。参照图3,将用于防止外部光线反射的减反射层300设置成朝向外部,通过上述方法,直接在玻璃基板330上形成电磁辐射屏蔽层340,以及将NIR-阻挡和选择性光吸收层360通过透明粘合剂层350层叠在玻璃基板330的背面以使其与电磁辐射屏蔽层340相对,从而得到用于显示面板的滤光片。尽管没有显示,通过直接在基板膜的前面和后面分别形成减反射层和NIR-阻挡和选择性光吸收层也可以形成用于显示面板的滤光片。在一些情形下,电磁辐射屏蔽层和减反射层可以设置在基板膜的表面。另外,粘合剂层可以具有NIR-阻挡功能和选择性光吸收光功能。
根据本发明的滤光片在380~780nm的波长范围内具有30~60%的透光率。该滤光片展示出1~6%非常低的雾度值,该雾度值是在没有透明片材粘附至各层的情况下测量的。
通过固定夹具可以将如上述制备的滤光片与电视机连接。
与包括通过常规刻蚀法形成的电磁辐射屏蔽网状膜的常规滤光片不同,根据本发明的方法制备的用于显示面板的滤光片采用了电磁辐射屏蔽层,该电磁辐射屏蔽层是通过将适合于凹版胶印的浆料直接涂覆在玻璃基板上来形成的。因此,本发明的方法不需要使用聚酯膜和粘合剂层,其明显简化了滤光片结构并提高了光的透光度。而且,根据本发明的滤光片能够被应用至普通的家庭用PDP电视机,因为由于其简单的制备方法而使其具有低电阻率,这也显著降低了制备成本。
在下文中,通过实施例将更加详细地描述本发明。然而,提供如下的实施例仅用于说明,因此本发明不限于此或不被其限定。
实施例1
如下所述制备浆料组合物:
将由甲基丙烯酸(MA)、苄基甲基丙烯酸酯(BM)、(甲基)丙烯酸-2-羟乙酯(2-HEMA)与(甲基)丙烯酸甲酯(MMA)按30:20:10:40的重量比组成的15wt%的丙烯酸酯聚合物树脂(其中重均分子量为25,000);由M310(MiwonCo.,韩国)、DPHA(日本Chemical Co.,Ltd.)和U 108 A(Shin-NakamuraChemical,Co.,L td,)按1:2:1的重量比组成的10wt%的可交联低聚物;2wt%的作为光聚合引发剂的I-107(Ciba Specialty Chemicals);71wt%的作为金属粉末的银粉;与2wt%的包含胺基的有机分散剂:DS-101(San Nopco韩国,Ltd.)混合并在室温下搅拌,接着在3-辊碾磨机中碾磨以得到所需的用于印刷的浆料组合物,其中,wt%为基于组合物的总重量。
将浆料组合物凹版胶印在玻璃基板的表面上形成电磁辐射屏蔽层。具体而言,将上述制备的浆料组合物涂覆在凹版平板上并使用刮刀均匀地涂覆至预定的厚度,然后转移至覆盖层上(“分离”步骤(“off”process))。然后,使用UV灯使转移至覆盖层上的图形进行第一次固化步骤,接着将所得的图形转移至玻璃基板上(“固定”步骤)。使用UV灯对转移至玻璃基板上的图形进行第二次固化步骤并进行热处理以除去杂质,得到电磁辐射屏蔽层。
实施例2
基于组合物的总重量,除了分别使用10和15wt%量的丙烯酸酯聚合物和可交联低聚物之外,使用与实施例1相同的步骤形成电磁辐射屏蔽层。
比较实施例1
基于组合物的总重量,除了不使用丙烯酸酯聚合物以及使用25wt%量的可交联低聚物之外,使用与实施例1相同的步骤形成电磁辐射屏蔽层。
实施例3
如下所述制备在图2中示意性显示的滤光片。
首先,硬涂层,将具有高折射率的基于氧化锆的膜与低折射率的基于氟代硅氧烷的膜通过湿法涂覆法依次层叠在聚酯膜上以得到减反射层。另一方面,将300g的聚(甲基丙烯酸甲酯)完全溶解在1,000ml的甲乙酮(MEK)中,并将100mg的八苯基四氮杂卟啉和150mg的IFG022(日本ChemicalCo.,Ltd.)溶解在其中。然后,将在50ml的异丙醇中的120mg的吖啶橙(Aldrich Chemical Co.,Ltd.)溶液逐渐加入到其中,接着将所得的溶液通过湿法涂覆法涂覆在双轴拉伸的膜上,得到NIR-阻挡和选择性光吸收层(干厚:大约5μm)。
接着,使用普通涂覆法将丙烯酸系透明粘合剂连续涂覆在剥离膜中的硅酮剥离层上(silicone release layer),并进行热风干燥。然后,将另一剥离膜粘附在粘合剂层的另一个表面上得到辊筒形式的经双面剥离处理的透明粘合剂层。
当将透明粘合剂层的剥离膜分层时,在3kgf/m2的压力下将减反射层以及NIR-阻挡和选择性光吸收层粘附至玻璃基板上,在该玻璃基板上具有在实施例1中形成的电磁辐射屏蔽膜。
实施例4
除了使用在实施例2中得到的电磁辐射屏蔽层之外,通过实施例3的步骤制备用于显示面板的滤光片。
比较实施例2
除了使用在比较实施例1中得到的电磁辐射屏蔽层之外,通过实施例3的步骤制备用于显示面板的滤光片。
比较实施例3
除了将透明粘合剂涂覆在线宽为10μm、线节距(line pitch)为300μm且开口率(aperture ratio)约为93%的刻蚀型网状膜(Nippon Filcoii Co.,Ltd.)上之外,通过实施例3的步骤形成减反射层、粘合剂层以及NIR-阻挡和选择性光吸收层,然后干燥,并将剥离膜层叠在粘合剂层的表面上,得到电磁辐射屏蔽层。
在将剥离膜分层时,在3kgf/m2的压力下将这样得到的电磁辐射屏蔽层粘附至玻璃基板上,得到如图1所示的用于显示面板的滤光片。
特性的评价
对于在实施例3和4与比较实施例2和3中制备的滤光片,根据ASTMD257标准,使用以相同间隔设置的四个探针组成的四点探针测量表面电阻率,并使用分光计(型号:NDH,Nippon Denshoku Kogyo K.K.)测量透光率和雾度值。此外,使用光学显微镜测量电磁辐射屏蔽层的网状图形的最小线宽。也使用相同的光学显微镜观察网状图形的形状。结果概括在表1中。
表1
实施例3 | 实施例4 | 比较实施例2 | 比较实施例3 | |
表面电阻率(Ω/□) | 0.5 | 0.3 | - | 0.05 |
透光率(%) | 45.93 | 45.3 | 35.5 | 44.2 |
雾度(%) | 3.2 | 3.7 | 5.3 | 18 |
网状图形的形状 | 好 | 好 | 差 | 好 |
网状图形的线宽 | 15μm | 20μm | 100μm | 10μm |
如表1所示,在实施例3和4中制备的滤光片,即,包括通过使用凹版胶印法在玻璃基板上直接形成根据本发明的浆料组合物得到的电磁辐射屏蔽层的滤光片,其展示出约为3%的雾度值,这表明在实施例3和4中制备的滤光片的透明度优于在比较实施例2和3中制备的滤光片的透明度。
至于网状图形的形状,在实施例3和4中制备的滤光片展示出均匀的15~20μm的线宽。另一方面,在比较实施例2中制备的滤光片展示出较差的外观,例如宽图形的线宽为100μm以及较差的图形方向性。至于光的透射,在比较实施2中制备滤光片展示出宽的网状线宽且具有35%的非常低的透光率,其图形方向性差,这一透光率低于本发明的NIR-阻挡和选择性光吸收层的滤光片的透光率。
在比较实施例3中制备的包括本领域常用的刻蚀型网状膜的滤光片由于网状膜的存在展示出非常高的雾度值。
至于通常用作电磁屏蔽效果的指示特征的表面电阻率,在实施例3和4中制备的滤光片的电磁屏蔽辐射层展示出0.4~0.7Ω/□的表面电阻率,其稍高于在常规滤光片(比较实施例3)中使用的刻蚀型网状膜的表面电阻率(0.05Ω/□)。然而,考虑到目前用于家庭用PDP电视上的作为多层溅射型导电膜形成的电磁辐射屏蔽层的表面电阻率为0.8~1.2Ω/□的事实,可以看出在实施例3和4中制备的滤光片具有更好的电磁屏蔽效果。
尽管参照上述具体实施例描述了本发明,但应该认识到本领域的技术人员可以对本发明进行多种修改和变化,而这些修改和变化仍落在如所附权利要求限定的本发明的范围内。
Claims (17)
1、一种制备用于显示面板的滤光片的方法,该滤光片包括透明玻璃基板和电磁辐射屏蔽层,该方法包括在透明玻璃基板上通过直接印刷组合物来形成电磁辐射屏蔽层的步骤,该组合物包含:(a)5~30wt%的丙烯酸酯聚合物树脂、(b)5~30wt%的可交联低聚物、(c)0.1~5wt%的光聚合引发剂和(d)50~85wt%的金属粉末。
2、根据权利要求1所述的方法,其中,所述滤光片进一步包括选自减反射层以及近红外线阻挡和选择性光吸收层中的至少一种。
3、根据权利要求1所述的方法,其中,所述电磁辐射屏蔽层的表面电阻率为0.2~1.2Ω/□。
4、根据权利要求1所述的方法,其中,所述组合物是通过凹版胶印法印刷的。
5、根据权利要求2所述的方法,其中,所述滤光片的雾度值为1~6%,该雾度值是在没有透明片材粘附至各电磁辐射屏蔽层、减反射层以及近红外线阻挡和选择性光吸收层上的情况下测量的。
6、根据权利要求1所述的方法,其中,所述丙烯酸酯聚合物树脂组分(a)是通过使i)20~50wt%的不饱和羧酸单体、ii)10~30wt%的芳香族单体和iii)20~60wt%的选自(甲基)丙烯酸-2-羟乙酯、(甲基)丙烯酸-2-羟辛酯、(甲基)丙烯酸甲酯、(甲基)丙烯酸乙酯和丙烯酸正丁酯中的至少一种单体在溶剂的存在下聚合而制备的,wt%为基于聚合物的总重量。
7、根据权利要求6所述的方法,其中,所述不饱和羧酸单体选自丙烯酸、甲基丙烯酸、衣康酸、马来酸、富马酸、乙烯基乙酸、其酸酐及其混合物中。
8、根据权利要求6所述的方法,其中,所述芳香族单体选自苯乙烯、苄基甲基丙烯酸酯、苄基丙烯酸酯、苯基丙烯酸酯、苯基甲基丙烯酸酯、2-硝基苯基丙烯酸酯、4-硝基苯基丙烯酸酯、2-硝基苯基甲基丙烯酸酯、4-硝基苯基甲基丙烯酸酯、2-硝基苄基甲基丙烯酸酯、4-硝基苄基甲基丙烯酸酯、2-氯苯基甲基丙烯酸酯、4-氯苯基丙烯酸酯、2-氯苯基甲基丙烯酸酯、4-氯苯基甲基丙烯酸酯及其混合物中。
9、根据权利要求1所述的方法,其中,所述丙烯酸酯聚合物树脂组分(a)的重均分子量为10,000~100,000。
10、根据权利要求1所述的方法,其中,所述可交联低聚物组分(b)为含有至少两个烯双键的基于丙烯酸酯的化合物。
11、根据权利要求1所述的方法,其中,所述金属粉末组分(d)为选自银、铜、镍及其合金中的至少一种。
12、根据权利要求1所述的方法,其中,所述组合物进一步包含0.01~10wt%的选自分散剂、炭黑和玻璃粉中的添加剂。
13、根据权利要求2所述的方法,其中,所述减反射层形成在最外层上。
14、根据权利要求2所述的方法,其中,所述近红外线阻挡和选择性光吸收层以及减反射层分别形成在所述透明玻璃基板的任一面上。
15、根据权利要求2所述的方法,其中,所述近红外线阻挡和选择性光吸收层是由近红外线阻挡颜料和选择性光吸收颜料的混合物与粘合剂形成的。
16、一种用于显示面板的滤光片,其通过权利要求1~15中任意一项所述的方法制备。
17、根据权利要求16所述的滤光片,其在380~780nm的波长范围内的透光率为30~60%。