CN101486051A - 钛板卷的平整方法 - Google Patents

钛板卷的平整方法 Download PDF

Info

Publication number
CN101486051A
CN101486051A CNA2009100941254A CN200910094125A CN101486051A CN 101486051 A CN101486051 A CN 101486051A CN A2009100941254 A CNA2009100941254 A CN A2009100941254A CN 200910094125 A CN200910094125 A CN 200910094125A CN 101486051 A CN101486051 A CN 101486051A
Authority
CN
China
Prior art keywords
smooth
coiled sheet
levelling
titanium
planisher
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2009100941254A
Other languages
English (en)
Inventor
王均洪
熊鉴
张宝柱
陈育生
聂志文
蒋进华
杜磊
薛鹂昆
曹占元
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yunnan Titanium Industry Co Ltd
Original Assignee
Wuhan Iron and Steel Group Kunming Iron and Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan Iron and Steel Group Kunming Iron and Steel Co Ltd filed Critical Wuhan Iron and Steel Group Kunming Iron and Steel Co Ltd
Priority to CNA2009100941254A priority Critical patent/CN101486051A/zh
Publication of CN101486051A publication Critical patent/CN101486051A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种钛板卷的平整方法，它将经过退火处理的钛板卷送入平整机上，在轧制速度为50～200m/min，开卷张力为0.5～4.0吨，卷曲张力为3.0～5.0吨，延伸率为0.80～2.0％的条件下，经平整机上的平整辊直接对钛板卷进行平整延伸或者进行用平整辊进行湿平整。本发明可使冷轧退火后的钛板卷，经平整机上的平整辊进行平整延伸后，消除应力及其影响，矫平板面，获得较好的表面质量，平整后的钛板卷的板形、尺寸、表面质量、力学性能等均达到国家标准要求，完全满足了市场需求。

Description

钛板卷的平整方法
技术领域
本发明涉及一种钛板卷的平整方法，尤其是冷轧工业纯钛板卷的平整工艺方法，属于金属材料加工技术领域。
背景技术
冷轧钛板既是一种强度高，重量轻，表面质量好，耐强酸强碱腐蚀的新材料。但同时冷轧钛板又具有弹性模量低、屈强比高，变形回弹大，变形强化率高等特点，正是这些特点增加了钛板的生产难度。此外退火后的冷轧钛板卷需要通过平整工艺来消除应力影响，矫平板面，获得较好的表面质量，使力学性能完全达到国家标准要求。但目前使用普通钢板卷的平整方法来处理钛板卷时，无法对钛板卷进行平整加工，因此，必须对冷轧钛板卷的平整工艺方法进行创新。
发明内容
为克服冷轧钛板卷存在的钛带平坦度和表面质量较差，力学性能不稳定等缺点，本发明提供一种工业纯钛板卷的平整方法，通过该方法可消除应力影响，矫平板面，获得较好的表面质量，使力学性能完全达到国家标准要求。
本发明通过下列技术方案实现：一种钛板卷的平整方法，其特征在于：将经过退火处理的钛板卷送入平整机上，在轧制速度为50～200m/min，开卷张力为0.5～4.0吨，卷曲张力为3.0～5.0吨，延伸率为0.80～2.0％的条件下，经平整机上的平整辊直接对钛板卷进行平整延伸；
或者
将经过退火处理的钛板卷送入平整机上，在轧制速度50～200m/min，开卷张力为0.5～4.0吨，卷曲张力为3.0～5.0吨，延伸率为0.80～2.0％的条件下，经平整机上的平整辊对钛板卷进行湿平整延伸，其中，湿平整延伸是在平整液质量浓度为2.0～5.0％，平整液温度为25～45℃，钛板卷温度为30～70℃的条件下进行平整延伸的，之后采用0.5～0.6MPa的压缩空气吹扫钛板表面至无残留的平整液，以提高平整后钛板卷的平坦度、表面质量和力学性能。
所述平整机为现有技术中的常规平整机。
所述平整机上的平整辊采用普通平整辊或者凹度平整辊，其中凹度平整辊的辊面设为以中部为凹点并向两端延伸的曲线凹面，且曲线凹面的最低凹点与辊面水平面的高度(也称凹度或负凸度)为0.01～0.03mm，表面粗糙度为0.4～0.8μm。
所述湿平整用的平整液为市购的平整液产品。
所述轧制速度、开卷张力、卷曲张力的设定以避免引起散卷，使钛板表面不产生划伤为限，采用较慢的轧制速度，即小于200m/min的速度为佳，以防止散卷而划伤钛板表面。
所述湿平整方法是针对钛板冷板形加工硬化逐渐加强的特点，采用在喷射平整液后，用空气吹扫板面至无残留的平整液的方法进行平整，以提高表面质量。
采用较低的辊面表面粗糙度较为适宜。
本发明与现有技术相比具有下列优点和效果：采用上述方案，可使冷轧退火后的钛板卷，经平整机上的平整辊进行平整延伸后，消除应力及其影响，矫平板面，获得较好的表面质量，平整后的钛板卷的板形、尺寸、表面质量、力学性能等均达到国家标准要求，完全满足了市场需求。
具体实施方式
下面结合实施例对本发明做进一步描述。
实施例1
将经过退火处理的规格为1.53×1060mm钛板卷送入现有技术的常规平整机上，在轧制速度为100m/min，开卷张力为0.5吨，卷曲张力为3.0吨，延伸率为0.8％的条件下，经平整机上的普通平整辊直接对钛板卷进行平整延伸，确保平整后钛板的力学性能。
实施例2
将经过退火处理的规格为1.53×1060mm钛板卷送入现有技术的常规平整机上，在轧制速度为200m/min，开卷张力为4.0吨，卷曲张力为5.0吨，延伸率为2％的条件下，经平整机上的普通平整辊直接对钛板卷进行平整延伸，确保平整后钛板的力学性能。
实施例3
将经过退火处理的规格为1.53×1060mm钛板卷送入现有技术的常规平整机上，在轧制速度为50m/min，开卷张力为2.0吨，卷曲张力为4.0吨，延伸率为1.8％的条件下，经平整机上的普通平整辊直接对钛板卷进行平整延伸，确保平整后钛板的力学性能。
实施例4
将经过退火处理的规格为1.53×1060mm的钛板卷送入现有技术的平整机上，在轧制速度150m/min，开卷张力为0.5吨，卷曲张力为3.0吨，延伸率为0.80％的条件下，经平整机上的凹面平整辊对钛板卷进行湿平整延伸，平整延伸时，先喷射平整液，之后用0.5MPa的压缩空气吹扫板面至无残留的平整液，其中，湿平整延伸是在市购平整液质量浓度为2.0％，平整液温度为25℃，钛板卷温度为30℃的条件下进行的；所述凹面平整辊的辊面设为以中部为凹点并向两端延伸的曲线凹面，且曲线凹面的最低凹点与辊面水平面的高度(也称凹度或负凸度)为0.01mm，表面粗糙度为0.4μm。
实施例5
将经过退火处理的规格为1.53×1060mm的钛板卷送入现有技术的平整机上，在轧制速度200m/min，开卷张力为3.5吨，卷曲张力为4.0吨，延伸率为1.8％的条件下，经平整机上的凹面平整辊对钛板卷进行湿平整延伸，平整延伸时，先喷射平整液，之后用0.6MPa的压缩空气吹扫板面至无残留的平整液，其中，湿平整延伸是在市购平整液质量浓度为5.0％，平整液温度为45℃，钛板卷温度为70℃的条件下进行的；所述凹面平整辊的辊面设为以中部为凹点并向两端延伸的曲线凹面，且曲线凹面的最低凹点与辊面水平面的高度(也称凹度或负凸度)为0.03mm，表面粗糙度为0.8μm。

Claims (5)

1、一种钛板卷的平整方法，其特征在于：将经过退火处理的钛板卷送入平整机上，在轧制速度为50～200m/min，开卷张力为0.5～4.0吨，卷曲张力为3.0～5.0吨，延伸率为0.80～2.0％的条件下，经平整机上的平整辊直接对钛板卷进行平整延伸。
2、一种钛板卷的平整方法，其特征在于：将经过退火处理的钛板卷送入平整机上，在轧制速度50～200m/min，开卷张力为0.5～4.0吨，卷曲张力为3.0～5.0吨，延伸率为0.80～2.0％的条件下，经平整机上的平整辊对钛板卷进行湿平整延伸，其中，湿平整延伸是在平整液质量浓度为2.0～5.0％，平整液温度为25～45℃，钛板卷温度为30～70℃的条件下进行平整延伸的，之后采用0.5～0.6MPa的压力空气吹扫钛板表面至无残留的平整液，以提高平整后钛板卷的平坦度、表面质量和力学性能。
3、根据权利要求1或2所述的钛板卷的平整方法，其特征在于所述平整机为现有技术中的常规平整机。
4、根据权利要求1或2所述的钛板卷的平整方法，其特征在于所述平整机上的平整辊采用普通平整辊或者凹度平整辊，其中凹度平整辊的辊面设为以中部为凹点并向两端延伸的曲线凹面，且曲线凹面的最低凹点与辊面水平面的高度为0.01～0.03mm，表面粗糙度为0.4～0.8μm。
5、根据权利要求2所述的钛板卷的平整方法，其特征在于所述湿平整用的平整液为市购的平整液产品。
CNA2009100941254A 2009-02-24 2009-02-24 钛板卷的平整方法 Pending CN101486051A (zh)