CN102430580A - 一种采用普通冷轧机对纯钛带卷进行干平整的方法 - Google Patents

一种采用普通冷轧机对纯钛带卷进行干平整的方法 Download PDF

Info

Publication number
CN102430580A
CN102430580A CN2011103635332A CN201110363533A CN102430580A CN 102430580 A CN102430580 A CN 102430580A CN 2011103635332 A CN2011103635332 A CN 2011103635332A CN 201110363533 A CN201110363533 A CN 201110363533A CN 102430580 A CN102430580 A CN 102430580A
Authority
CN
China
Prior art keywords
pure titanium
common cold
titanium strip
strip coil
roll
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103635332A
Other languages
English (en)
Inventor
顾新盛
包淑娟
刘茵琪
王非
石洪轻
王卫超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Luoyang Sunrui Titanium Precision Casting Co Ltd
Original Assignee
Luoyang Sunrui Titanium Precision Casting Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Luoyang Sunrui Titanium Precision Casting Co Ltd filed Critical Luoyang Sunrui Titanium Precision Casting Co Ltd
Priority to CN2011103635332A priority Critical patent/CN102430580A/zh
Publication of CN102430580A publication Critical patent/CN102430580A/zh
Pending legal-status Critical Current

Abstract

本发明介绍了一种采用普通冷轧机对纯钛带卷进行干平整的方法，将经过退火处理的纯钛带卷送入普通冷轧机，在轧制速度15～50m/min，开卷单位张力1～10kg/mm2，收卷单位张力1.5～15kg/mm2，轧制力为100～400吨的条件下，通过恒轧制力控制模式，采用普通冷轧机上的工作辊直接对纯钛带卷进行干平整。本发明可使冷轧退火后的纯钛带卷经普通冷轧机干平整后，消除应力的影响，矫平板面，干平整后的纯钛带卷板面不平度≤3mm/m，各项力学性能指标和表面质量均能满足中国、美国的相关标准要求及客户使用要求。

Description

一种采用普通冷轧机对纯钛带卷进行干平整的方法
技术领域
本发明涉及一种材料加工技术，特别是一种采用普通冷轧机对纯钛带卷进行干平整的方法。
背景技术
冷轧纯钛带卷具有弹性模量低、屈强比高，变形回弹大，变形强化率高等特点，因此退火后的冷轧纯钛带卷需要通过平整来消除应力影响，矫平板面，获得良好的板形质量和力学性能及表面质量（出自专利，公开号CN 101486051A）。但目前纯钛带卷的板形矫正均需通过专门的拉矫机或平整机实现，设备投入较大，因此，有必要研究如何采用普通冷轧机实现纯钛带卷的平整。
发明内容
本发明所要解决的技术问题是提供一种采用普通冷轧机对纯钛带卷进行干平整的方法，借助普通冷轧机，可使冷轧退火后的纯钛带卷经普通冷轧机干平整后，获得良好的板形质量、力学性能和表面质量，且上述各项指标均能满足中国、美国的相关标准要求及客户使用要求。
为了实现解决上述技术问题的目的，本发明采用了如下技术方案：
本发明的一种采用普通冷轧机对纯钛带卷进行干平整的方法，将经过退火处理的纯钛带卷送入普通冷轧机，在轧制速度15～50m/min，开卷单位张力1～10kg/mm2，收卷单位张力1.5～15 kg/mm2，轧制力为100～400吨的条件下，通过恒轧制力控制模式，采用普通冷轧机上的工作辊直接对纯钛带卷进行干平整。
所述的普通冷轧机为现有技术的冷轧机。
所述普通冷轧机上的工作辊采用平辊或凸度辊，其中凸度辊的辊面设为以中部为凸点并向两端延伸的正弦曲线，凸度值为0.01～0.03mm，表面粗糙度为0.2～0.4um。
通过采用上述技术方案，本发明具有以下的有益效果：
本发明可使冷轧退火后的纯钛带卷经普通冷轧机干平整后，消除应力的影响，矫平板面，干平整后的纯钛带卷板面不平度≤3mm/m，粗糙度为0.15～0.40um，TA1（GR1）材质的屈服强度为180～250MPa，抗拉强度为280～340MPa，断后伸长率A20可达到60%以上，TA2（GR2）材质的屈服强度为280～350MPa，抗拉强度为400～450MPa，断后伸长率A50可达到30%以上，上述技术指标均能满足GB/T 3621-2007、GB/T 14845-2007和ASTM B265-2006标准要求。 
具体实施方式
实施例1
将经过退火处理的规格为1.22*1250*mm的GR2纯钛带卷送入普通冷轧机，在轧制速度为45m/min，开卷单位张力2.0 kg/mm2，收卷单位张力5.0 kg/mm2，轧制力为320吨的条件下，通过恒轧制力控制模式，采用平辊进行干平整，平整后该带卷的板面不平度≤2mm/m，表面粗糙度为0.28～0.38um，屈服强度为300～330 MPa，抗拉强度为410～430MPa，断后伸长率A50为31～35%。
实施例2
将经过完全再结晶退火处理的规格为1.02*1250mm的GR2纯钛带卷送入普通冷轧机，在轧制速度为35m/min，开卷单位张力2.5 kg/mm2，收卷单位张力6.0 kg/mm2，轧制力为240吨的条件下，通过恒轧制力控制模式，采用平辊进行干平整，平整后该带卷的板面不平度≤2.5mm/m，表面粗糙度为0.22～0.32um，屈服强度为300～330 MPa，抗拉强度为415～435MPa，断后伸长率A50为32～35%。
实施例3
将经过完全再结晶退火处理的规格为0.6*1250mm的TA1纯钛带卷送入普通冷轧机，在轧制速度为25m/min，开卷单位张力3.0 kg/mm2，收卷单位张力7.0kg/mm2，轧制力为110吨的条件下，通过恒轧制力控制模式，采用凸度为0.01mm的凸度辊进行干平整，该带卷平整后的板面不平度≤3.0mm/m，表面粗糙度为0.15～0.25um，屈服强度为220～245MPa，抗拉强度为305～325MPa，断后伸长率A20为65～72%。
实施例4
将经过完全再结晶退火处理的规格为0.51*1250mm的GR2纯钛带卷送入普通冷轧机，在轧制速度为25m/min，开卷单位张力3.0 kg/mm2，收卷单位张力7.5 kg/mm2，轧制力为180吨的条件下，通过恒轧制力控制模式，采用凸度为0.01mm的凸度辊进行干平整，平整后该带卷的板面不平度≤3mm/m，表面粗糙度为0.15～0.25um，屈服强度为280～310MPa，抗拉强度为405～425MPa，断后伸长率A50为33～37%。

Claims (2)

1.一种采用普通冷轧机对纯钛带卷进行干平整的方法，其特征是：将经过退火处理的纯钛带卷送入普通冷轧机，在轧制速度15～50m/min，开卷单位张力1～10kg/mm2，收卷单位张力1.5～15 kg/mm2，轧制力为100～400吨的条件下，通过恒轧制力控制模式，采用普通冷轧机上的工作辊直接对纯钛带卷进行干平整。
2.根据权利要求1所述采用普通冷轧机对纯钛带卷进行干平整的方法，其特征是：所述的普通冷轧机上的工作辊采用平辊或凸度辊，其中凸度辊的辊面设为以中部为凸点并向两端延伸的正弦曲线，凸度值为0.01～0.03mm，表面粗糙度为0.2～0.4um。
CN2011103635332A 2011-11-16 2011-11-16 一种采用普通冷轧机对纯钛带卷进行干平整的方法 Pending CN102430580A (zh)