CN101450993A - 一种无卤阻燃尼龙6的制备方法 - Google Patents
一种无卤阻燃尼龙6的制备方法 Download PDFInfo
- Publication number
- CN101450993A CN101450993A CNA200710192571XA CN200710192571A CN101450993A CN 101450993 A CN101450993 A CN 101450993A CN A200710192571X A CNA200710192571X A CN A200710192571XA CN 200710192571 A CN200710192571 A CN 200710192571A CN 101450993 A CN101450993 A CN 101450993A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- retardant
- mass fraction
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种无卤阻燃尼龙6的制备方法，在反应器中加入二羧酸的三聚氰胺盐、有机二胺的三聚氰酸盐或者三聚氰胺、三聚氰酸、酰胺盐，成碳剂、炭化促进剂、己内酰胺、水，进行分散混合，升温至230℃～265℃、在压力0.2MPa～0.8MPa下，搅拌聚合反应5小时～8小时，然后卸压、减压抽真空去除低分子得到无卤阻燃尼龙6。该方法制备得到材料的稳定性好、毒性小、力学性能得到大幅提高、阻燃性持久，可直接用于阻燃纺丝或工程塑料。
Description
技术领域
本发明涉及一种无卤阻燃尼龙6的制备方法
背景技术
尼龙6的阻燃改性不仅是工程塑料研究的重点，同时也一直是纺织领域研究的前沿学科。在众多研究中，虽然PA6纤维能够实现阻燃，但大多数使用含卤或含磷阻燃剂与PA6基体树脂共混纺丝或在织物后整理工序中通过表面处理来达到阻燃目的；无卤阻燃PA6塑料的研究及生产也仅限于螺杆共混。
上述阻燃尼龙6工程塑料的制备采用的方法均是螺杆共混；由于加入的阻燃剂量大，微细阻燃剂在加工过程中易团聚形成应力集中点，同时加上尼龙6肌体树脂经过螺杆的二次加工受热降解，阻燃尼龙6的力学性能较纯尼龙6下降大，只能用于塑料行业。
近年来，随着低毒性、低烟尘、低添加量、低成本和抗滴落的阻燃剂的开发，以及适合于制造阻燃锦纶工艺的推出，锦纶纤维阻燃化将日趋普及。日本宇部兴产在PA中加人至少一种有机磷化合物作阻燃剂开发出阻燃锦纶，阻燃效果好且不影响纤维的物性；三光开发科研所研制的阻燃锦纶选用的含磷阻燃剂对PA具有特别的亲和力，由于添加量小，耐热性好，也不影响纤维物性；这两种制备技术虽然是在聚合过程中加入的阻燃剂，但由于磷系阻燃剂与尼龙6的相容性有一定限度，织物在使用过程中阻燃剂易析出而影响阻燃的持久性，同时，这类阻燃剂燃烧时生成具有强烈腐蚀性的磷酸或五氧化二磷等，产生烟雾密度大，易使现场人员中毒。
国内山西省化学纤维研究所所研制的锦纶阻燃剂NF一8702还比较理想。但需采用后整理法：即在尼龙6纺丝成织物后，织物经过加热的阻燃剂溶液进行热处理而成，这类处理方法仍存在一些不尽人意的问题，如阻燃的持久性，阻燃锦纶的毒性，发烟性，阻燃处理后很能保持锦纶纤维原有的优良特征等。
目前尼龙6的阻燃主要是通过两种途径实现。(1)使用添加型阻燃剂，即通过机械共混方法，将阻燃剂加入到聚酰胺中，使其获得阻燃性；采用此类方法无论制备阻燃PA6纤维还是阻燃工程塑料，对阻燃PA6树脂的应用都带来了一定的影响。(2)使用反应型阻燃剂，即阻燃剂是作为一种反应单体参加反应，并结合到聚酰胺的主链或侧链上去，使聚酰胺本身含有阻燃成分；本发明采用第二种途径：即在己内酰胺聚合过程中加入阻燃单体及其它阻燃协效剂一步原位法聚合阻燃尼龙6。
专利技术2005100220464是以三聚氰胺(MEL)和氰尿酸(CA)为原料，聚酰胺高分子为基体树脂，以水为分散介质，在分子复合剂及缚水增塑剂的作用下，通过螺杆在挤出加工过程中原位合成MCA并制备了阻燃聚酰胺纳米复合材料；该发明方法制备阻燃尼龙6时，增加了螺杆挤出工序，一方面是导致生产成本增加，另一方面是增加了尼龙6肌体树脂的二次热降解几率，难于保证阻燃剂与尼龙充分混合均匀，使基础树脂力学性能损失较大，加快了阻燃尼龙6材料的老化步伐。
文献Preparation，properties and characterizationsof.halogen-free..nitrogen-phosphorous..flame-retarded glass fiberreinforced polyamide 6 composite[Polymer Degradation and Stability，91(9)，2003-2013]采用原位聚合的方法合成了含磷-氮系阻燃剂，该阻燃剂也是通过螺杆与尼龙共混来制备玻璃纤维阻燃增强尼龙6，所制备的材料只能用于玻璃纤维增强尼龙6组合物，仅适用于工程塑料。
其它文献报道的阻燃尼龙6材料也较多是采用填加型。即通过填加各种阻燃填加剂来实现。
现有技术制备阻燃尼龙6时，由于加入的阻燃剂量大，微细阻燃剂在加工过程中易团聚形成应力集中点，有加上尼龙6肌体树脂经过螺杆的二次加工受热，因此，材料的力学性能较纯尼龙6下降幅度大，只能用于塑料行业；同时，由于增加了后续螺杆工序，阻燃尼龙6制造成本也有一定提高，因而也直接增加了用户原材料成本。
发明内容
为了克服现有制备阻燃尼龙6技术上的不足，拟采用本发明方法来制备无卤阻燃尼龙6。
本发明技术按以下方法实施：在反应器中加入二羧酸的三聚氰胺盐、有机二胺的三聚氰酸盐、成碳剂、炭化促进剂、己内酰胺、水或者三聚氰胺、三聚氰酸、酰胺盐、成碳剂、炭化促进剂、己内酰胺、水；二羧酸的三聚氰胺盐、有机二胺的三聚氰酸盐、成碳剂、炭化促进剂、己内酰胺、水的配比为：二羧酸的三聚氰酸盐的质量份数为：5.37份～29.87份，有机二胺的三聚氰酸盐的质量份数为：2.47份～9.87份，成碳剂的质量份数为：1份～5份，炭化促进剂的质量份数为：0.01份～1份，己内酰胺的质量份数为：88.79份～38.02份，水的质量份数为：0.3份～5份；三聚氰胺、三聚氰酸、酰胺盐、成碳剂、炭化促进剂、己内酰胺、水的配比为：三聚氰胺的质量份数为：2.47份～9.87份，三聚氰酸的质量份数为：2.53份～10.11份，酰胺盐的质量份数为：5.2份～36份，成碳剂的质量份数为：1份～5份，炭化促进剂的质量份数为：0.01份～1份，己内酰胺的质量份数为：88.79份～38.02份，水的质量份数为：0.3份～5份；进行分散混合，升温至230℃～265℃、在压力0.2MPa～0.8MPa下，搅拌聚合反应5小时～8小时，然后卸压、减压抽真空去除低分子得到无卤阻燃尼龙6。
本发明的二羧酸的三聚氰胺盐，通过等摩尔的三聚氰胺与二羧酸分散在去离子水中，在50℃～120℃下搅拌反应0.5小时～3小时，然后离心过滤，干燥制备得到；所用的二羧酸可以是长碳链的二元羧酸或芳香族二羧酸，长碳链的二元羧酸如：己二酸、癸二酸、十一烷二羧酸，芳香族二羧酸如：对苯二甲酸、间苯二甲酸。
本发明的有机二胺的三聚氰酸盐，通过等摩尔的三聚氰酸与有机二胺分散在去离子水中，在30℃～80℃下搅拌反应0.5小时～2小时，然后离心过滤，干燥制备得到；所用的有机二胺可以是长碳链二胺或芳香族二胺，长碳链的二胺如：己二胺、癸二胺、十一烷二胺，芳香族二胺如：对苯二甲胺、间苯二甲胺。
本发明的酰胺盐有上述二羧酸和有机二胺反应得到的。
本发明的成碳剂为多羟基有机化合物，如：季戊四醇、双季戊四醇。
本发明的炭化促进剂为杂多酸，如：钨酸、磷钨酸。
为保证二羧酸的三聚氰胺盐、有机二胺的三聚氰酸盐或者三聚氰胺、三聚氰酸、酰胺盐能在熔融的己内酰胺、水中达到纳米级分散，分散混合可在胶体磨或高压均质机或球磨机中进行。
为保证制备的阻燃尼龙具有一定的聚合度，以适合阻燃纤维及工程塑料用，二羧酸的三聚氰胺与有机二胺的三聚氰酸盐的摩尔比为1:1；或三聚氰胺、三聚氰酸、酰胺盐三者的摩尔比为1:1:1。
本发明具有如下的技术效果：
1、本发明使用了在己内酰胺熔体中有一定溶解度的阻燃单体盐，这种阻燃单体盐一方面可参与己内酰胺的聚合，在尼龙6分子链上引入阻燃元素；另一方面，阻燃单体的盐自身相互反应形成无卤阻燃剂以纳米或分子级尺度分散在聚合的尼龙肌体中；与目前普遍采用的共混法制备的阻燃尼龙6相比，材料的稳定性好、毒性小、力学性能得到大幅提高、阻燃性持久，可直接用于阻燃纺丝或工程塑料。
2、采用本发明方法制备的阻燃尼龙6的阻燃性达到UL94-V-0级，阻燃剂在材料中达到了纳米或分子级分散；本发明的阻燃尼龙6颗粒与共混无卤无磷阻燃尼龙6颗粒的场发射环扫电镜形貌图以及聚合级阻燃PA6丝束与尼龙6工业消光丝束的场发射环扫电镜形貌图分别见附图1～8，从附图1～4可以看出：聚合制备的阻燃尼龙6与共混阻燃尼龙6相比，聚合级阻燃尼龙6中分布的阻燃剂粒径远远小于后者，阻燃剂分布更均匀；从附图5～8可以看出：从丝束表面分布的小白斑点颗粒来看，消光丝所含颗粒稍多而且还粗大些，由于尼龙6工业消光丝中加有0.3％的钛白粉，聚合级阻燃尼龙6丝束中含有7.5％的阻燃剂，从而说明阻燃剂在尼龙6聚合体中达到了纳米级分散或直接参与了PA6的聚合，否则，阻燃剂添加量是钛白粉量的25倍后，阻燃尼龙丝束表面应该可以看到更多的颗粒。
3、阻燃尼龙6织物的氧指数达到35％，大于难燃材料所要求的氧指数标准(30％)。
4、本发明制备的阻燃尼龙6与纯尼龙6的可纺丝性相当。
附图及附图说明
图1：共混级阻燃PA6颗粒在0.5万倍的场发射环扫电镜形貌图
图2：共混级阻燃PA6颗粒在5万倍的场发射环扫电镜形貌图
图3：聚合级阻燃PA6颗粒在1万倍的场发射环扫电镜形貌图
图4：聚合级阻燃PA6颗粒在5万倍的场发射环扫电镜形貌图
图5：尼龙6工业消光丝束在500倍的场发射环扫电镜形貌图
图6：尼龙6工业消光丝束在5万倍的场发射环扫电镜形貌图
图7：聚合级阻燃PA6丝束在500倍的场发射环扫电镜形貌图
图8：聚合级阻燃PA6丝束在5万倍的场发射环扫电镜形貌图
具体实施方式
实施例1：在10升聚合釜中，投入由2.9份己二酸和2.47份三聚氰胺在50℃下搅拌反应3小时，然后离心过滤，干燥制备得到的己二酸三聚氰胺盐、2.3份己二胺和2.53份三聚氰酸在80℃下搅拌反应0.5小时，然后离心过滤，干燥制备得到的己二胺三聚氰酸盐的两种阻燃单体、1份季戊四醇、0.01份钨酸，上述物质先用高剪切乳化机和88.79份熔融的己内酰胺、0.3份水进行预分散混合，然后升温至230～265℃、压力0.2～0.8MPa下搅拌聚合反应5小时，再卸压、减压抽真空去除低分子、出料铸带切粒，得到无卤阻燃尼龙6颗粒经过萃取、干燥，得到样品进行阻燃、力学性能检测。结果见表1。
实施例2：在10升聚合釜中，投入2.47份三聚氰胺、2.53份三聚氰酸、5.2份尼龙66盐、1份季戊四醇、0.01份钨酸，上述物质先用高剪切乳化机和88.79份熔融的己内酰胺、0.3份水进行预分散混合，然后升温至230～265℃、压力0.2～0.8MPa下搅拌聚合反应8小时，再卸压、减压抽真空去除低分子、出料铸带切粒，得到无卤阻燃尼龙6颗粒经过萃取、干燥，得到样品进行阻燃、力学性能检测。结果见表1。
实施例3：先在胶体磨中，投入由2.9份己二酸和2.47份三聚氰胺在95℃下搅拌反应1.5小时，然后离心过滤，干燥制备得到的己二酸三聚氰胺盐、2.3份己二胺和2.53份三聚氰酸在50℃下搅拌反应2小时，然后离心过滤，干燥制备得到己二胺三聚氰酸盐组成的两种阻燃单体，1份季戊四醇、0.01份钨酸和88.79份熔融的己内酰胺、0.3份水进行预分散混合；然后将已预分散好的混合溶液泵入聚合釜中，升温至230～265℃、压力0.2～0.8MPa下搅拌聚合反应5～8小时，再卸压、减压抽真空去除低分子、出料铸带切粒，得到无卤阻燃尼龙6颗粒经过萃取、干燥，得到样品进行阻燃、力学性能检测。结果见表1。
实施例4：在10升聚合釜中，投入由11.44份己二酸和9.87份三聚氰胺在120℃下搅拌反应0.5小时，然后离心过滤，干燥制备得到的反应的己二酸三聚氰胺盐、9.10份己二胺和10.11份三聚氰酸反应在30℃下搅拌反应2小时，然后离心过滤，干燥制备得到的己二胺三聚氰酸盐组成的两种阻燃单体、1季戊四醇、0.01份钨酸，上述物质先用高剪切乳化机和53.48份熔融的己内酰胺、0.3～5份水进行预分散混合，然后升温至230～265℃、压力0.2～0.8MPa下搅拌聚合反应5～8小时，再卸压、减压抽真空去除低分子、出料铸带切粒，得到无卤阻燃尼龙6颗粒经过萃取、干燥，得到样品进行阻燃、力学性能检测。结果见表1。
实施例5：在10升聚合釜中，投入9.87份三聚氰胺、10.11份三聚氰酸、20.54份尼龙66盐、1～5份成碳剂、0.01～1份炭化促进剂，上述物质先用高剪切乳化机和53.48份熔融的己内酰胺、0.3～5份水进行预分散混合，然后升温至230～265℃、压力0.2～0.8MPa下搅拌聚合反应5～8小时，再卸压、减压抽真空去除低分子、出料铸带切粒，得到无卤阻燃尼龙6颗粒经过萃取、干燥，得到样品进行阻燃、力学性能检测。结果见表1。
实施例6：在10升聚合釜中，投入由3.96份癸二酸和2.47份三聚氰胺在80℃下搅拌反应1.5小时，然后离心过滤，干燥制备得到的癸二酸三聚氰胺盐、2.3份己二胺和2.53份三聚氰酸在50℃下搅拌反应1小时，然后离心过滤，干燥制备得到的己二胺三聚氰酸盐组成的两种阻燃单体、1份季戊四醇、0.01份磷钨酸，上述物质先用高剪切乳化机和87.73份熔融的己内酰胺、0.3份水进行预分散混合，然后升温至230～265℃、压力0.2～0.8MPa下搅拌聚合反应5～8小时，再卸压、减压抽真空去除低分子、出料铸带切粒，得到无卤阻燃尼龙6颗粒经过萃取、干燥，得到样品进行阻燃、力学性能检测。结果见表1
实施例7：在10升聚合釜中，投入由3.25份对苯二甲酸和2.47份三聚氰胺在65℃下搅拌反应2.5小时，然后离心过滤，干燥制备得到的苯二甲酸三聚氰胺盐、2.3份己二胺和2.53份三聚氰酸在60℃下搅拌反应1.5小时，然后离心过滤，干燥制备得到的己二胺三聚氰酸盐组成的两种阻燃单体、1份季戊四醇、0.01份钨酸，上述物质先用高剪切乳化机和88.44份熔融的己内酰胺、0.3份水进行预分散混合，然后升温至230～265℃、压力0.2～0.8MPa下搅拌聚合反应5～8小时，再卸压、减压抽真空去除低分子、出料铸带切粒，得到无卤阻燃尼龙6颗粒经过萃取、干燥，得到样品进行阻燃、力学性能检测。结果见表1
实施例8：在10升聚合釜中，投入由2.9份己二酸和2.47份三聚氰胺在75℃下搅拌反应2小时，然后离心过滤，干燥制备得到己二酸三聚氰胺盐、3.37份癸二胺和2.53份三聚氰酸在70℃下搅拌反应1小时，然后离心过滤，干燥制备得到的癸二胺三聚氰酸盐组成的两种阻燃单体、1份季戊四醇、0.01份钨酸，上述物质先用高剪切乳化机和87.72份熔融的己内酰胺、0.3份水进行预分散混合，然后升温至230～265℃、压力0.2～0.8MPa下搅拌聚合反应5～8小时，再卸压、减压抽真空去除低分子、出料铸带切粒，得到无卤阻燃尼龙6颗粒经过萃取、干燥，得到样品进行阻燃、力学性能检测。结果见表1。
实施例9：在10升聚合釜中，投入由2.9份己二酸和2.47份三聚氰胺在75℃下搅拌反应2小时，然后离心过滤，干燥制备得到己二酸三聚氰胺盐、3.37份癸二胺和2.53份三聚氰酸在65℃下搅拌反应1小时，然后离心过滤，干燥制备得到的癸二胺三聚氰酸盐组成的两种阻燃单体、1份双季戊四醇、0.01份钨酸，上述物质先用高剪切乳化机和87.72份熔融的己内酰胺、0.3份水进行预分散混合，然后升温至230～265℃、压力0.2～0.8MPa下搅拌聚合反应5～8小时，再卸压、减压抽真空去除低分子、出料铸带切粒，得到无卤阻燃尼龙6颗粒经过萃取、干燥，得到样品进行阻燃、力学性能检测。结果见表1
对比实例1：5份由三聚氰胺和三聚氰酸合成的无卤阻燃剂MCA、1.01份阻燃协效剂与88.79份相对粘度为3.45的纯尼龙6，在双螺杆上进行共混挤出切粒、干燥，然后铸塑制样检测，结果见表1。
对比实例2：20.0份由三聚氰胺和三聚氰酸合成的无卤阻燃剂MCA、1.01份阻燃协效剂与53.48份相对粘度为3.45的纯尼龙6，在双螺杆上进行共混挤出切粒、干燥，然后铸塑制样检测，结果见表1。
对比实例3：在10升聚合釜中，投入2.47份三聚氰胺、2.53份三聚氰酸、1份季戊四醇、0.01份钨酸、93.99份熔融的己内酰胺和0.3份水，升温至230～265℃、压力0.2～0.8MPa下搅拌聚合反应5～8小时，再卸压、减压抽真空去除低分子、出料铸带切粒，得到无卤阻燃尼龙6颗粒经过萃取、干燥，得到样品进行阻燃、力学性能检测。结果见表1。
表1、共聚合、共混阻燃以及纯尼龙阻燃、力学性能检测数据
| 实验编号 | 结晶度 | 结晶速率 | 冲击强度 | 弯曲强度 | 弯曲模量 | 拉伸强度 | 断裂伸长率 | 热变形温温 | 燃烧性 |
| 测试方法 | DSC | DSC | GB1043-93 | GB8341 | GB9341 | GB/T1040 | GB/T1040 | GB1634 | UL94 |
| 单位 | ％ | 1/min | kJ/m2 | MPa | MPa | MPa | ％ | 0.46MPa | 垂直 |
| 实施例1 | 27.3 | 0.063 | 8.7 | 99.1 | 2689 | 61.1 | 11.2 | 199.8 | V-0 |
| 实施例2 | 27.9 | 0.062 | 8.2 | 94.9 | 2756 | 58.6 | 12.5 | 202.2 | V-0 |
| 实施例3 | 27.6 | 0.062 | 8.6 | 96.3 | 2721 | 60.3 | 11.5 | 203.2 | V-0 |
| 实施例4 | 26.2 | 0.061 | 7.5 | 91.6 | 2883 | 57.9 | 10.9 | 206.8 | V-0 |
| 实验编号 | 结晶度 | 结晶速率 | 冲击强度 | 弯曲强度 | 弯曲模量 | 拉伸强度 | 断裂伸长率 | 热变形温温 | 燃烧性 |
| 测试方法 | DSC | DSC | GB1043-93 | GB8341 | GB9341 | GB/T1040 | GB/T1040 | GB1634 | UL94 |
| 单位 | ％ | 1/min | kJ/m2 | MPa | MPa | MPa | ％ | 0.46MPa | 垂直 |
| 实施例5 | 26.7 | 0.066 | 7.8 | 92.3 | 2901 | 564 | 10.3 | 207.4 | V-0 |
| 实施例6 | 25.6 | 0.071 | 9.1 | 88.5 | 2156 | 68.9 | 18.9 | 193.2 | V-0 |
| 实施例7 | 28.3 | 0.063 | 8.3 | 99.8 | 2732 | 56.9 | 9.8 | 209.5 | V-0 |
| 实施例8 | 26.8 | 0.070 | 9.2 | 89.1 | 2253 | 67.8 | 19.1 | 192.8 | V-0 |
| 实施例9 | 27.2 | 0.067 | 8.9 | 91.1 | 2453 | 71.8 | 12.1 | 201.8 | V-0 |
| 对比例1 | 31.7 | 0.055 | 6.2 | 106.5 | 2878 | 59.0 | 6.8 | 209.6 | V-2 |
| 对比例2 | 33.1 | 0.057 | 4.9 | 105.1 | 3118 | 62.2 | 4.2 | 215.9 | V-2 |
| 对比例3 | 37.0 | 0.056 | 5.3 | 66.2 | 2511 | 62.6 | 1.9 | 208.2 | V-2 |
| 纯尼龙6 | 47.5 | 0.055 | 13.6 | 91.7 | 2080 | 66.6 | 18.6 | 189.4 | V-2 |
Claims (6)
1、一种无卤阻燃尼龙6的制备方法，其特征在于：在反应器中加入二羧酸的三聚氰胺盐、有机二胺的三聚氰酸盐、成碳剂、炭化促进剂、己内酰胺、水或者三聚氰胺、三聚氰酸、酰胺盐、成碳剂、炭化促进剂、己内酰胺、水；二羧酸的三聚氰胺盐、有机二胺的三聚氰酸盐、成碳剂、炭化促进剂、己内酰胺、水的配比为：二羧酸的三聚氰酸盐的质量份数为：5.37份～29.87份，有机二胺的三聚氰酸盐的质量份数为：2.47份～9.87份，成碳剂的质量份数为：1份～5份，炭化促进剂的质量份数为：0.01份～1份，己内酰胺的质量份数为：88.79份～38.02份，水的质量份数为：0.3份～5份；三聚氰胺、三聚氰酸、酰胺盐、成碳剂、炭化促进剂、己内酰胺、水的配比为：三聚氰胺的质量份数为：2.47份～9.87份，三聚氰酸的质量份数为：2.53份～10.11份，酰胺盐的质量份数为：5.2份～36份，成碳剂的质量份数为：1份～5份，炭化促进剂的质量份数为：0.01份～1份，己内酰胺的质量份数为：88.79份～38.02份，水的质量份数为：0.3份～5份；进行分散混合，升温至230℃～265℃、在压力0.2MPa～0.8MPa下，搅拌聚合反应5小时～8小时，然后卸压、减压抽真空去除低分子得到无卤阻燃尼龙6。
2、根据权利要求1所述的方法，其特征在于：二羧酸的三聚氰胺盐，通过等摩尔的三聚氰胺与二羧酸分散在去离子水中，在50℃～120℃下搅拌反应0.5小时～3小时，然后离心过滤，干燥制备得到，所用的二羧酸可以是长碳链的二元羧酸或芳香族二羧酸；有机二胺的三聚氰酸盐，通过等摩尔的三聚氰酸与有机二胺分散在去离子水中，在30℃～80℃下搅拌反应0.5小时～2小时，然后离心过滤，干燥制备得到；所用的有机二胺可以是长碳链二胺或芳香族二胺；酰胺盐有上述二羧酸和有机二胺反应得到的，成碳剂为多羟基有机化合物；炭化促进剂为杂多酸。
3、根据权利要求2所述的方法，其特征在于：长碳链的二元羧酸可以是己二酸或癸二酸或十一烷二羧酸，芳香族二羧酸可以是对苯二甲酸或间苯二甲酸；长碳链的二胺可以是己二胺或癸二胺或十一烷二胺，芳香族二胺可以是对苯二甲胺或间苯二甲胺；多羟基有机化合物可以是季戊四醇或双季戊四醇；杂多酸可以是钨酸或磷钨酸。
4、根据权利要求1或2或3所述的方法，其特征在于：为保证二羧酸的三聚氰胺盐、有机二胺的三聚氰酸盐或者三聚氰胺、三聚氰酸、酰胺盐能在熔融的己内酰胺、水中达到纳米级分散，分散混合可在胶体磨或高压均质机或球磨机中进行。
5、根据权利要求1或2或3所述的方法，其特征在于：为保证制备的阻燃尼龙具有一定的聚合度，以适合阻燃纤维及工程塑料用，二羧酸的三聚氰胺与有机二胺的三聚氰酸盐的摩尔比为1:1；或三聚氰胺、三聚氰酸、酰胺盐三者的摩尔比为1:1:1。
6、根据权利要求4所述的方法，其特征在于：为保证制备的阻燃尼龙具有一定的聚合度，以适合阻燃纤维及工程塑料用，二羧酸的三聚氰胺与有机二胺的三聚氰酸盐的摩尔比为1:1；或三聚氰胺、三聚氰酸、酰胺盐三者的摩尔比为1:1:1。