CN101435004A - 皮革制品创伤的修补方法 - Google Patents
皮革制品创伤的修补方法 Download PDFInfo
- Publication number
- CN101435004A CN101435004A CNA2008101542844A CN200810154284A CN101435004A CN 101435004 A CN101435004 A CN 101435004A CN A2008101542844 A CNA2008101542844 A CN A2008101542844A CN 200810154284 A CN200810154284 A CN 200810154284A CN 101435004 A CN101435004 A CN 101435004A
- Authority
- CN
- China
- Prior art keywords
- breach
- leatherware
- repairing
- polishing
- scar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种皮革制品创伤的修补方法,用细砂纸打磨皮革制品裂口,于裂口处涂胶对接后,在其背面垫有衬布并用软胶粘牢,以增加裂口处的抗拉强度,再用调好颜色的补伤膏修复裂口痕迹,晾干;继续用细砂纸打磨不平处;反复涂抹补伤膏→晾干→用细砂纸打磨→找平,直至裂口完全平齐光滑;用毛刷将常规的液态皮纤维均匀的涂在裂口表面,经晾干后,再根据皮革制品的颜色进行配色上色,晾干;最后,喷皮革亮光剂,如仍可见疤痕再在疤痕上面铺上真丝布用 50℃-60℃低温熨斗在平面桌上熨一下,熨出纹路使之与原皮革制品的纹路相似。裂口平齐,消除裂口痕迹,美观又结实,裂口处柔软如初,穿着舒服,延长了皮革制品的使用寿命,节约开支和原材料。
Description
技术领域
本发明涉及一种皮革制品的修补方法,特别是涉及一种修补方法简单、完全消除裂口创伤和擦伤痕迹和皮革制品外表更加美观的皮革制品创伤的修补方法。
背景技术
众所周知,在生活水平不断提高和追求舒适的今天,都想买名牌高档的正宗皮革制品,如皮衣、皮裤、皮鞋、真皮沙发和皮具制品等,但它们因被磨损、被刀割和遇硬物被钩挂破的现象经常发生,产生的裂口创伤均需要修补,而目前的修补方法主要是在创伤的背面垫上与原皮革制品的皮革相同的皮子或用胶粘或用胶粘后再用线缝制,再涂皮革油磨光,裂口创伤的痕迹依然可见,极不美观且不结实,遇雪或雨容易开胶,修补处的皮质变硬,穿着不舒服,缩短了皮革制品的使用寿命。
发明内容:
本发明的主要目的在于克服以上不足而提供一种修补方法简单、完全消除裂口创伤痕迹和皮革制品外表更加美观的皮革制品创伤的修补方法。
本发明解决其技术问题所采用的技术方案是:它包括皮革制品裂口创伤、垫衬布和胶粘合,其特征在于:
①.首先,用细砂纸打磨皮革制品裂口,于裂口处涂胶对接后,在其裂口的背面垫有大于裂口创伤尺寸的细软衬布用软胶粘好,在常温下晾一天;
②.再用外购的补伤膏调色后,修复裂口痕迹,在常温下晾干;
③.用细砂纸打磨不平处;
④.反复涂抹补伤膏、晾干、用细砂纸打磨找平,直至裂口完全平齐光滑;
⑤.用细毛刷将外购的液态皮纤维均匀的刷涂在裂口表面,经晾干后,再根据皮革制品的颜色进行配色上色,常温下晾干;
⑥.最后,喷上皮革亮光剂,如仍可见疤痕再在疤痕上面铺上真丝布用50℃--60℃低温熨斗在平面桌上熨一下,熨出纹路,直至看不出疤痕。
本发明还可以采用如下技术措施:
所述的皮革制品裂口背面用的衬布是棉布或丝绸。
本发明具有的优点和积极效果是:反复涂抹补伤膏、晾干、用细砂纸打磨找平,裂口完全平齐光滑,完全消除裂口创伤痕迹,既美观又结实,修补后的裂口创伤处柔软如初,穿着舒服,遇雪或雨不易开胶,延长了皮革制品的使用寿命,为家庭节约了开支,为国家节约了原材料,应用范围广,可广泛用于皮衣、皮裤、皮鞋、真皮沙发和皮具制品等。
具体实施方式
为能进一步了解本发明的发明内容特点及功效兹举例以下实施例,详细说明如下。
实施例1:以修补皮衣裂口创伤为例加以说明
首先,用细砂纸打磨皮衣裂口,打磨出新茬更利于牢固的粘合,于裂口处涂胶对接后,在其裂口的背面垫有大于裂口创伤尺寸的衬布或丝绸并用软胶粘牢,以增加裂口处的抗拉强度,然后,常温下晾一天;再用外购的经调色后补伤膏修复裂口痕迹,在常温下晾干;继续用细砂纸打磨不平处;反复涂抹补伤膏→晾干→用细砂纸打磨→找平,直至裂口完全平齐;用毛刷将常规的液态皮纤维均匀的刷涂在裂口表面,经晾干后,再根据皮衣的颜色进行配色上色,在常温下晾干;最后,喷上皮革亮光剂,如仍可见疤痕再在疤痕上面铺上与皮革纹路相应的真丝布用50℃--60℃低温熨斗在平面桌上熨一下,熨出纹路使之与原皮衣的纹路相似,且可进一步修复裂口,直至看不出疤痕,皮衣裂口创伤修补完毕。
其优点是:裂口平齐光滑,完全消除裂口创伤痕迹,既美观又结实,修补后的裂口创伤处柔软如初,穿着舒服,遇雪或雨不易开胶,延长了皮革制品的使用寿命,为家庭节约了开支,为国家节约了原材料,应用范围广,可广泛用于皮衣、皮裤、皮鞋、真皮沙发和皮具制品等。
实施例2:皮革制品创伤的修补方法用于改制皮鞋时,以修补皮鞋鞋面裂口为例加以说明
当高档皮鞋需要放大、改小时,除了鞋底鞋跟采用常规的方法连接外,其鞋面接口均采用皮革制品创伤的修补方法。
皮鞋需要放大时,其主要步骤如下:
①.首先,用吹风机在200℃—300℃的温度下均匀加热鞋面和鞋底的四周,将鞋面和鞋底间的粘胶变软熔化,使鞋面和鞋底分离;
②.把鞋面切开后,套在规定的大号鞋楦上,根据皮子缺口的大小准备与原皮料相同的植皮;
③.采用皮革制品创伤及裂口的修补方法修补鞋面植皮后形成的的裂口:首先,用细砂纸打磨皮鞋裂口,打磨出新茬更利于牢固的粘合,于裂口处涂胶对接后,在其裂口的背面垫有大于裂口创伤尺寸的衬布或丝绸并用软胶粘牢,以增加裂口处的抗拉强度,然后,常温下晾一天;再用外购的补伤膏修复裂口痕迹,在常温下晾干;继续用细砂纸打磨不平处;反复涂抹补伤膏→晾干→用细砂纸打磨→找平,直至裂口完全平齐光滑;用细毛刷将常规的液态皮纤维均匀的刷涂在裂口表面,经晾干后,再根据皮鞋的颜色进行配色上色,在常温下晾干;最后,喷上皮革亮光剂,如仍可见疤痕再在疤痕上面铺上与皮革纹路相应的真丝布用50℃--60℃低温熨斗将鞋套在鞋楦上熨一下,熨出纹路使之与原皮鞋的纹路相似,且可进一步修复裂口,直至看不出疤痕;
④.将鞋底后跟处呈斜面切开,用与原鞋底的材质相同的鞋底料,剪出大于鞋面的鞋底料,其一端也切成带斜面的切口,然后,用常规的砂轮机进行打磨,使两个切口具有相同角度的坡面,并用强力软胶粘合,最后,用砂轮机修饰平滑;
⑤.最后,将修饰好的鞋面和鞋底结合在一起,鞋面和鞋底用强力软胶粘合或用线缝合。
皮鞋改小的改制工艺步骤
①.首先,用吹风机在200℃—300℃的温度下均匀加热皮鞋的后跟部将鞋面和鞋底间的粘胶变软熔化,使鞋面和鞋底分离;
②.把鞋面后跟部切开后再进行剪切,然后,套在规定缩小的鞋楦上;
③.采用皮革制品焊接裂口方法修补鞋面形成的的裂口:首先,用细砂纸打磨皮鞋裂口,打磨出新茬更利于牢固的粘合,于裂口处涂胶对接后,在其裂口的背面垫有大于裂口创伤尺寸的衬布或丝绸并用软胶粘牢,以增加裂口处的抗拉强度,然后,常温下晾一天;再用外购的补伤膏经调色后,修复裂口痕迹,在常温下晾干;继续用细砂纸打磨不平处;反复涂抹补伤膏→晒干→用细砂纸打磨→找平,直至裂口完全平齐;用毛刷将常规的液态皮纤维均匀的刷涂在裂口表面,经晒干后,再根据皮鞋的颜色进行配色上色,在常温下晒干;最后,喷上皮革亮光剂,如仍可见疤痕再在疤痕上面铺上真丝布用50℃--60℃低温熨斗将鞋套在鞋楦上熨一下,熨出纹路使之与原皮鞋的纹路相似,且可进一步修复裂口,直至看不出疤痕;
④.将鞋底按照鞋面尺寸剪去多余部分,用常规的砂轮机将鞋底打磨平滑,使两个切口具有相同角度的坡面,并用强力软胶粘合,最后,用砂轮机修饰平滑;
⑤.最后,将修饰好的鞋面和鞋底结合在一起,鞋面和鞋底用强力软胶粘合或用线缝合。
其优点是:裂口平齐光滑,完全消除裂口创伤痕迹,既美观又结实,修补后的裂口处柔软如初,穿着舒服,遇雪或雨不易开胶,延长了皮鞋的使用寿命,节约了开支和原材料。
Claims (2)
1.一种皮革制品创伤的修补方法,它包括皮革制品裂口创伤、垫衬布和胶粘合,其特征在于:
①.首先,用细砂纸打磨皮革制品裂口,于裂口处涂胶对接后,在其裂口的背面垫有大于裂口创伤尺寸的衬布用软胶粘好,在常温下晾一天;
②.再用外购的补伤膏经调色后,修复裂口痕迹,在常温下晾干;
③.用细砂纸打磨不平处;
④.反复涂抹补伤膏、晾干、用细砂纸打磨找平,直至裂口完全平齐光滑;
⑤.用细毛刷将外购的液态皮纤维均匀的刷涂在裂口表面,经晾干后,再根据皮革制品的颜色进行配色上色,在常温下晾干;
⑥.最后,喷上皮革亮光剂,如仍可见疤痕再在疤痕上面铺上真丝布用50℃--60℃低温熨斗在平面桌上熨一下,熨出纹路,直至看不出疤痕。
2.根据权利要求1所述的皮革制品创伤的修补方法,其特征在于:所述的皮革制品裂口背面用的衬布是棉布或丝绸。