CN101417820A - 多形貌纳米二氧化锰的制备方法 - Google Patents
多形貌纳米二氧化锰的制备方法 Download PDFInfo
- Publication number
- CN101417820A CN101417820A CNA2008102002877A CN200810200287A CN101417820A CN 101417820 A CN101417820 A CN 101417820A CN A2008102002877 A CNA2008102002877 A CN A2008102002877A CN 200810200287 A CN200810200287 A CN 200810200287A CN 101417820 A CN101417820 A CN 101417820A
- Authority
- CN
- China
- Prior art keywords
- manganese dioxide
- mixed solution
- solution
- product
- mno
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (1)