CN101349008A - 毛衫面料茶多酚抗菌整理的工艺 - Google Patents
毛衫面料茶多酚抗菌整理的工艺 Download PDFInfo
- Publication number
- CN101349008A CN101349008A CNA2008101468973A CN200810146897A CN101349008A CN 101349008 A CN101349008 A CN 101349008A CN A2008101468973 A CNA2008101468973 A CN A2008101468973A CN 200810146897 A CN200810146897 A CN 200810146897A CN 101349008 A CN101349008 A CN 101349008A
- Authority
- CN
- China
- Prior art keywords
- antibiotic finish
- sweater fabric
- tea polyphenols
- tea
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种毛衫面料茶多酚抗菌整理的工艺。该工艺先将毛衫面料在40～50℃温水中恒温7～10分钟，取出后在35～40℃温度下干燥；再采用二浸二轧法，将干燥后的毛衫面料置于50～55℃恒温的茶多酚抗菌整理剂中，浸渍8～10小时，用轧车轧一遍后再次放入50～55℃恒温的茶多酚整理剂中，浸渍8～10小时，再用轧车轧一遍；最后水洗浸渍后的毛衫面料，烘干后即得成品。该工艺采用绿色环保的天然抗菌剂茶多酚对毛衫面料进行抗菌整理，不但保证使毛衫面料具有抗菌效果，同时具有健康环保的优点。
Description
技术领域
本发明涉及一种毛衫面料的抗菌整理工艺，尤其涉及一种通过茶多酚对毛衫面料进行抗菌整理的工艺。
背景技术
毛织物因其独特的性能如弹性好、保暖性好、手感柔和等优点而倍受消费者的欢迎，然而毛织物在穿洗过程中易发生虫蛀、霉变、滋养细菌等现象，从而严重影响了毛织物的外观、寿命和卫生性。由于传统的纯毛产品的抗菌整理均采用大量的化学试剂，易产生大量的可吸收性有机卤素，不但严重污染环境，也对人体健康构成威胁，因此，在毛衫面料中采用绿色环保的天然抗菌剂进行抗菌整理的研究不但具有理论价值，更具有极大的社会效益。
发明内容
本发明的目的是提供一种毛衫面料茶多酚抗菌整理的工艺，该工艺采用绿色环保的天然抗菌剂茶多酚对毛衫面料进行抗菌整理，不但保证使毛衫面料具有抗菌效果，同时具有健康环保的优点。
为了达到上述目的，本发明申请人在研究中发现，茶多酚能特异性地凝固细菌蛋白、破坏细菌细胞膜结构、与细菌遗传物质CDE结合，从而改变细菌生理抑制生长；另外茶多酚受潮后容易发生氧化，在环境中与细菌争夺氧，不利于需氧菌生长。而且，茶多酚的抗菌特点主要有：抗菌谱广，对有细胞壁和无细胞壁的革兰氏阳性、阴性菌均有明显抑制作用；抗菌作用强，用药浓度低，以酯型儿茶素的抗菌效果最好；在体内外均有抗菌及抗细菌毒素的作用；保护和促进有益菌生长，调节菌群平衡；具有除臭功效；不易使细菌产生耐药性等。
本发明技术方案包括：
一种毛衫面料茶多酚抗菌整理的工艺，包括抗菌整理、水洗和烘干，所述抗菌整理包括：
(1)将毛衫面料在40～50℃温水中恒温7～10分钟，取出后在35～40℃温度下干燥；
(2)采用二浸二轧法，将干燥后的毛衫面料置于50～55℃恒温的茶多酚抗菌整理剂中，浸渍8～10小时，用轧车轧一遍后再次放入50～55℃恒温的茶多酚整理剂中，浸渍8～10小时，再用轧车轧一遍。
其中，所述茶多酚抗菌整理剂是将茶多酚、NaCl、环保粘结剂投入温度为50-55℃的水中，搅拌溶解即可，其中，茶多酚浓度为8～10g/L，NaCl浓度为20～25g/L，环保粘结剂浓度为1～2g/L。
其中，所述工艺还包括在抗菌整理前先将毛衫面料进行超声波水浴预处理，其中超声频率为59KHz，超声功率为120～150W，超声时间为20～40分钟，超声水浴比为1∶15～1∶20。
其中，所述的水洗是指将抗菌整理后的毛衫面料进行清水冲洗。
其中，所述的烘干是将水洗后的毛衫面料在30-35℃温度下烘干。
本发明工艺所处理的毛衫面料，抗菌性得到了明显的改善，并且耐洗涤性良好，与其他抗菌整理剂及整理工艺相比，由于采用天然抗菌材料，处理工艺无污染，符合健康环保的要求。同时测试抗菌整理后样品的尺寸稳定性、色牢度等指标与整理前样品比较，均在±5％以内，起球性等级未有变化。
具体实施方式
下面结合实施例对本发明作进一步描述，旨在帮助阅读者更好理解本发明的技术方案，并不对本发明技术方案的实施范围构成任何限定。
本发明申请人在研究中发现，茶多酚能特异性地凝固细菌蛋白、破坏细菌细胞膜结构、与细菌遗传物质CDE结合，从而改变细菌生理抑制生长；另外茶多酚受潮后容易发生氧化，在环境中与细菌争夺氧，不利于需氧菌生长。而且，茶多酚的抗菌特点主要有：抗菌谱广，对有细胞壁和无细胞壁的革兰氏阳性、阴性菌均有明显抑制作用；抗菌作用强，用药浓度低，以酯型儿茶素的抗菌效果最好；在体内外均有抗菌及抗细菌毒素的作用；保护和促进有益菌生长，调节菌群平衡；具有除臭功效；不易使细菌产生耐药性等。同时，在配置茶多酚抗菌整理剂时，由于单独茶多酚液体无粘度，因此加入NaCl，有利于提高整理剂的粘度，从而提高整理效果；加入环保粘结剂，有利于提高整理剂与毛衫面料之间的结合效果，增加毛衫面料的耐洗次数，且对环境、人体无害。
并且，本发明还可在采用茶多酚对毛衫面料进行抗菌整理前，先将毛衫面料通过超声波预处理，增加抗菌整理处理中毛衫面料对茶多酚的吸附，从而提高抗菌效果。
同时，本发明申请人对该工艺中几个关键技术进行了如下研究：
(1)茶多酚浓度的设定。
茶多酚浓度并非浓度越大越好，根据不同茶多酚浓度抗菌处理效果的对比，在8-10g/L范围内，抑菌率达到95％以上。
(2)超声波预处理频率的设定。
根据不同频率的超声波预处理实验比较，在频率为59KHz时，在纤维表面的机械振荡效应相对强烈一些，对茶多酚的吸附能力大大增强，从而处理效果表现的更为显著。
实施例1
(1)将毛衫面料在40℃温水中恒温10分钟，取出后在35℃温度下干燥；
(2)将8g茶多酚、25gNaCl以及1g环保粘结剂投入1L温度为55℃的水中，搅拌溶解即得茶多酚抗菌整理剂；
(3)采用二浸二轧法，将干燥后的毛衫面料置于55℃恒温的茶多酚抗菌整理剂中，浸渍8小时，用轧车轧一遍后再次放入55℃恒温的茶多酚整理剂中，浸渍8小时，再用轧车轧一遍；
(4)水洗浸渍后的毛衫面料；
(5)将水洗后的毛衫面料在30℃温度下烘干。
实施例2
(1)将毛衫面料进行超声波水浴预处理，其中超声频率为59KHz，超声功率为135W，超声时间为30分钟，超声水浴比为1∶15；
(2)将毛衫面料在50℃温水中恒温7分钟，取出后在40℃温度下干燥；
(3)将9g茶多酚、20gNaCl以及2g环保粘结剂投入1L温度为50℃的水中，搅拌溶解即得茶多酚抗菌整理剂；
(4)采用二浸二轧法，将干燥后的毛衫面料置于50℃恒温的茶多酚抗菌整理剂中，浸渍10小时，用轧车轧一遍后再次放入50℃恒温的茶多酚整理剂中，浸渍10小时，再用轧车轧一遍；
(5)水洗浸渍后的毛衫面料；
(6)将水洗后的毛衫面料在35℃温度下烘干。
实施例3
(1)将毛衫面料进行超声波水浴预处理，其中超声频率为59KHz，超声功率为120W，超声时间为40分钟，超声水浴比为1∶20；
(2)将毛衫面料在45℃温水中恒温8分钟，取出后在37℃温度下干燥；
(3)将10g茶多酚、22gNaCl以及1.5g环保粘结剂投入1L温度为52℃的水中，搅拌溶解即得茶多酚抗菌整理剂；
(4)采用二浸二轧法，将干燥后的毛衫面料置于52℃恒温的茶多酚抗菌整理剂中，浸渍9小时，用轧车轧一遍后再次放入52℃恒温的茶多酚整理剂中，浸渍9小时，再用轧车轧一遍；
(5)水洗浸渍后的毛衫面料；
(6)将水洗后的毛衫面料在32℃温度下烘干。
实施例4
(1)将毛衫面料进行超声波水浴预处理，其中超声频率为59KHz，超声功率为150W，超声时间为20分钟，超声水浴比为1∶18；
(2)将毛衫面料在48℃温水中恒温9分钟，取出后在39℃温度下干燥；
(3)将9g茶多酚、23gNaCl以及1.8g环保粘结剂投入1L温度为52.5℃的水中，搅拌溶解即得茶多酚抗菌整理剂；
(4)采用二浸二轧法，将干燥后的毛衫面料置于52.5℃恒温的茶多酚抗菌整理剂中，浸渍9小时，用轧车轧一遍后再次放入52.5℃恒温的茶多酚整理剂中，浸渍9小时，再用轧车轧一遍；
(5)水洗浸渍后的毛衫面料；
(6)将水洗后的毛衫面料在32.5℃温度下烘干。
对实施例1至实施例4所得的成品进行振荡烧瓶法大肠杆菌性能测试，结果如下表：
1#：茶多酚抗菌整理后清水洗过0次，烘干；
2#：茶多酚抗菌整理后清水洗过1次，烘干；
3#：茶多酚抗菌整理后清水洗过5次，烘干。
通过对上述表格数据的分析可知：本发明工艺所处理的毛衫面料，抗菌性得到了明显的改善，并且耐洗涤性良好，与其他抗菌整理剂及整理工艺相比，由于采用天然抗菌材料，处理工艺无污染，符合健康环保的要求。同时测试抗菌整理后样品的尺寸稳定性、色牢度等指标与整理前样品比较，均在±5％以内，起球性等级未有变化。
Claims (5)
1.一种毛衫面料茶多酚抗菌整理的工艺，包括抗菌整理、水洗和烘干，其特征在于，所述抗菌整理包括：
(1)将毛衫面料在40～50℃温水中恒温7～10分钟，取出后在35～40℃温度下干燥；
(2)采用二浸二轧法，将干燥后的毛衫面料置于50～55℃恒温的茶多酚抗菌整理剂中，浸渍8～10小时，用轧车轧一遍后再次放入50～55℃恒温的茶多酚整理剂中，浸渍8～10小时，再用轧车轧一遍。
2.根据权利要求1所述的一种毛衫面料茶多酚抗菌整理的工艺，其特征在于，所述茶多酚抗菌整理剂是将茶多酚、NaCl、环保粘结剂投入温度为50-55℃的水中，搅拌溶解即可，其中，茶多酚浓度为8～10g/L，NaCl浓度为20～25g/L，环保粘结剂浓度为1～2g/L。
3.根据权利要求1所述的一种毛衫面料茶多酚抗菌整理的工艺，其特征在于，所述工艺还包括在抗菌整理前先将毛衫面料进行超声波水浴预处理，其中超声频率为59KHz，超声功率为120～150W，超声时间为20～40分钟，超声水浴比为1∶15～1∶20。
4.根据权利要求1所述的一种毛衫面料茶多酚抗菌整理的工艺，其特征在于，所述的水洗是指将抗菌整理后的毛衫面料进行清水冲洗。
5.根据权利要求1所述的一种毛衫面料茶多酚抗菌整理的工艺，其特征在于，所述的烘干是将水洗后的毛衫面料在30-35℃温度下烘干。