CN101613929A - 一种无机纳米抗菌棉纤维的制备方法及其在家纺产品中的应用 - Google Patents

一种无机纳米抗菌棉纤维的制备方法及其在家纺产品中的应用 Download PDF

Info

Publication number
CN101613929A
CN101613929A CN200910054870A CN200910054870A CN101613929A CN 101613929 A CN101613929 A CN 101613929A CN 200910054870 A CN200910054870 A CN 200910054870A CN 200910054870 A CN200910054870 A CN 200910054870A CN 101613929 A CN101613929 A CN 101613929A
Authority
CN
China
Prior art keywords
cotton fiber
silver ion
nano
finishing agent
antibacterial finishing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200910054870A
Other languages
English (en)
Inventor
李裕杰
周忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHUIXING DOMESTIC TEXTILE PRODUCTS CO Ltd SHANGHAI
Shanghai Shuixing Home Textile Co Ltd
Original Assignee
SHUIXING DOMESTIC TEXTILE PRODUCTS CO Ltd SHANGHAI
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHUIXING DOMESTIC TEXTILE PRODUCTS CO Ltd SHANGHAI filed Critical SHUIXING DOMESTIC TEXTILE PRODUCTS CO Ltd SHANGHAI
Priority to CN200910054870A priority Critical patent/CN101613929A/zh
Publication of CN101613929A publication Critical patent/CN101613929A/zh
Pending legal-status Critical Current

Abstract

一种无机纳米抗菌棉纤维的制备方法，包括浸轧抗菌整理剂和烘干，所述抗菌整理剂包括银离子抗菌剂，该银离子抗菌剂的载体为纳米TiO2，该银离子抗菌剂的pH值为4－5。本发明的有益效果：本发明通过采用纳米TiO2为银离子抗菌剂的载体，在湿状态下(如排汗)，释放出具有抗菌效果的银离子。由于以纳米TiO2为载体的银离子抗菌剂有很大的表面活性，1g纳米级的抗菌整理剂大概有600000cm2的表面积，少量即可达到很好的效果。

Description

一种无机纳米抗菌棉纤维的制备方法及其在家纺产品中的应用
技术领域
本发明涉及纺织技术领域，具体涉及一种无机纳米抗菌棉纤维的制备方法及其在家纺产品中的应用。
背景技术
天然棉纤维因其舒适性等而深受消费者欢迎，但是它们存在着一些缺点，如棉纤维受霉菌和真菌的侵袭比合成纤维敏感得多，而且在适宜的条件下，一些病原菌如金黄色葡萄球菌、大肠杆菌、白色念珠球菌和伤寒沙门氏菌等在棉纤维上存在时间延长，并以人体的新陈代谢产物-汗水、脂肪质和皮屑等为营养物质迅速繁殖，分解出各种低级脂肪酸和胺类等有臭味的挥发性化合物，加上细菌本身的分泌物和其死骸腐烂的气味，纺织品释放出令人恶心的臭味。这不仅使纤维制品变色、发霉、脆化降解，而且还会对人体皮肤产生异常的刺激，诱发各种皮肤疾病，危害人体健康，所以要求纺织品具有抗菌防臭功能。
因此，出现了很多具有抗菌功能的棉纤维，但是这些棉纤维经过几次洗涤后其抗菌就由明显的下降，实用性不高。
发明内容
本发明所解决的技术问题在于，提供一种无机纳米抗菌棉纤维的制备方法，通过该方法处理的棉纤维可经多次洗涤，且其抗菌效率仍能达到99.9％。
本发明所需要解决的技术问题，可以通过以下技术方案来实现：
一种无机纳米抗菌棉纤维的制备方法，包括以下步骤：
a、将棉纤维放置到抗菌整理剂中浸渍4-6min，该抗菌整理剂的载体为纳米TiO2；抗菌整理剂的PH值4-5；
b、将在抗菌整理剂中浸渍过的棉纤维轧压；反复浸轧步骤两到三次，每次轧压的压力为40～50kn。
c、将轧压后的棉纤维在150～170℃中的温度下烘培，烘培时间为120s。
该无机纳米抗菌棉纤维在家纺产品中的应用，其特征在于，该无机纳米抗菌棉纤维可以用来制备四件套、六件套。
本发明的有益效果：本发明通过采用纳米TiO2为银离子抗菌剂的载体，在湿状态下(如排汗)，释放出具有抗菌效果的银离子。由于以纳米TiO2为载体的银离子抗菌剂有很大的表面活性，1g纳米级的抗菌整理剂大概有600000cm2的表面积，少量即可达到很好的效果。且通过该方法处理的棉纤维可经多次洗涤，其抗菌效率仍能达到99.9％。
具体实施方式
为了使本发明的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1：
一种无机纳米抗菌棉纤维的制备方法，包括以下步骤：
a、将棉纤维放置到抗菌整理剂中浸渍5min，要指出的是：该抗菌整理剂的载体为纳米TiO2；抗菌整理剂的PH值4-5；
b、将在抗菌整理剂中浸渍过的棉纤维轧压。重复上述浸轧步骤两到三次，并且浸轧过程中棉纤维的带液率为70％～80％，保证良好的浸轧效果。每次轧压的压力为45kn。
c、将轧压后的棉纤维在150～170℃中的温度下烘培，烘培时间为120s。
整理后的棉纤维抗菌率高达99.9％，抑菌圈为17mm。经10次洗涤后的抗菌效果仍无变化；耐水洗次数达到50次；整理后织物上的银含量可达到367.3mg/kg；经过10次洗涤后，银和钦的保留率均在50％左右，抗菌效率仍然可达99.9％。
实施例2：
在对棉纤维进行轧压时，每次轧压的压力为40kn。其余同实施例1。
实施例3：
在对棉纤维进行轧压时，每次轧压的压力为50kn。其余同实施例1。
本发明通过采用纳米TiO2为银离子抗菌剂的载体，在湿状态下(如排汗)，释放出具有抗菌效果的银离子。由于以纳米TiO2为载体的银离子抗菌剂有很大的表面活性，1g纳米级的抗菌整理剂大概有600000cm2的表面积，少量即可达到很好的效果。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等同物界定。

Claims (2)

1、一种无机纳米抗菌棉纤维的制备方法，包括以下步骤：
a、将棉纤维放置到抗菌整理剂中浸渍4-6min，该抗菌整理剂的载体为纳米TiO2；抗菌整理剂的PH值4-5；
b、将在抗菌整理剂中浸渍过的棉纤维轧压；反复浸轧步骤两到三次，每次轧压的压力为40～50kn。
c、将轧压后的棉纤维在150～170℃中的温度下烘培，烘培时间为120s。
2、如权利要求1所述的无机纳米抗菌棉纤维在家纺产品中的应用，其特征在于，该无机纳米抗菌棉纤维可以用来制备四件套、六件套。
CN200910054870A 2009-07-16 2009-07-16 一种无机纳米抗菌棉纤维的制备方法及其在家纺产品中的应用 Pending CN101613929A (zh)