CN101251723A - 一种负性彩色光刻胶脱胶剂及其制备方法 - Google Patents
一种负性彩色光刻胶脱胶剂及其制备方法 Download PDFInfo
- Publication number
- CN101251723A CN101251723A CNA2008100198587A CN200810019858A CN101251723A CN 101251723 A CN101251723 A CN 101251723A CN A2008100198587 A CNA2008100198587 A CN A2008100198587A CN 200810019858 A CN200810019858 A CN 200810019858A CN 101251723 A CN101251723 A CN 101251723A
- Authority
- CN
- China
- Prior art keywords
- percent
- stirring
- add
- degumming agent
- emulsion tank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种负性彩色光刻胶脱胶剂,它是由如下重量份数的组分组成:五水偏硅酸钠0.5~1%,对甲基苯磺酸钠2~5%,单乙醇胺3~5%,三乙醇胺25~35%,脂肪醇聚氧乙烯醚0.5~1%,乙二醇苯醚25~35%,环己酮4~8%,乙二醇丁醚1~5%,其余为水。将上述原料按顺序加入乳化罐,经混合、均质、冷却、排气和过滤后,即可制得。本发明的负性彩色光刻胶脱胶剂pH值低,使用时微泡或无泡,水溶性强,清洗后玻璃表面无残留、无颗粒物质,洁净度好,无毒、无刺激性,易生物降解,易进行废液排放处理。其制备方法简单,产率高,只有少量的沉淀残渣,能耗低,加工操作简便,易于自动化,无环境污染,经济效益高。
Description
技术领域
本发明涉及一种脱胶剂及其制备方法,尤其涉及一种专用于电子通讯材料——负性彩色光刻胶的脱胶剂及其制备方法。
背景技术
负性彩色光刻胶脱胶剂目前国内空白,需从国外进口,进口原液pH值接近14,使用浓度为20%,价格昂贵,由于碱性较强,因此对设备有一定的腐蚀,能耗较高。
发明内容
本发明所要解决的技术问题是提供一种高效、无毒、无腐蚀的负性彩色光刻胶脱胶剂。
本发明所要解决的另一技术问题是提供上述负性彩色光刻胶脱胶剂的制备方法。
为解决上述技术问题,本发明所采用的技术方案如下:
一种负性彩色光刻胶脱胶剂,以水为溶剂,三乙醇胺、乙二醇苯醚、环己酮作为助溶剂,五水偏硅酸钠、单乙醇胺作为pH值调节剂,脂肪醇聚氧乙烯醚作为渗透剂、乳化剂,乙二醇丁醚作为消泡剂,均匀混合。具体组份和重量百分比为:五水偏硅酸钠0.5~1%,对甲基苯磺酸钠2~5%,单乙醇胺3~5%,三乙醇胺25~35%,脂肪醇聚氧乙烯醚0.5~1%,乙二醇苯醚25~35%,环己酮4~8%,乙二醇丁醚1~5%,其余为水。
上述负性彩色光刻胶脱胶剂的制备方法,包括如下步骤:
1、向乳化罐内加入去离子水,先后加入五水偏硅酸钠和对甲基苯磺酸钠,搅拌混匀;
2、向乳化罐内加入单乙醇胺,搅拌混匀;
3、向乳化罐内加入三乙醇胺,搅拌混匀;
4、向乳化罐内加入脂肪醇聚氧乙烯醚,搅拌混匀;
5、向乳化罐内加入乙二醇苯醚,搅拌混匀;
6、向乳化罐内加入环己酮,搅拌混匀;
7、向乳化罐内加入乙二醇丁醚,搅拌混匀;
8、把制得的均相透明的混合溶液送入均质机,经过均质处理,使乳液中分散相的颗粒更细小,更均匀,得到高度稳定的产品;
9、均质液经冷却、排气和过滤后包装;将液体中的气泡排出、陈放(老化),可使体系更稳定;过滤可除去机械杂质和絮状物。
有益效果:本发明的负性彩色光刻胶脱胶剂pH值低(pH值为8.2~8.7),使用时微泡或无泡,水溶性强,清洗后玻璃表面无残留、无颗粒物质,洁净度好,无毒、无刺激性,易生物降解,易进行废液排放处理。本发明的负性彩色光刻胶脱胶剂的制备方法工艺简单,产率高,只有少量的沉淀残渣,能耗低,加工操作简便,易于自动化,无环境污染,经济效益高。
附图说明
图1为本发明负性彩色光刻胶脱胶剂制备方法的工艺流程和设备示意图。其中1为贮料罐(实际6个,图中只画了1个示意),2为加料计量罐(实际6个,图中只画了2个,即2-1、2-2),3为乳化罐(即混合罐),4为冷却罐,5为成品贮罐,6为均质机,7为过滤器。
具体实施方式:
实施例1:
在乳化罐内加入去离子水,再加入五水偏硅酸钠搅拌,取计量罐2-1内的单乙醇胺加入乳化罐,搅拌;取计量罐2-2内的三乙醇胺加入乳化罐,搅拌;取计量罐2-3内的脂肪醇聚氧乙烯醚加入乳化罐,搅拌;再取计量罐2-4内的乙二醇苯醚加入乳化罐,搅拌;取计量罐2-5内的环己酮加入乳化罐,搅拌;取计量罐2-6内的乙二醇丁醚加入乳化罐,搅拌;制成均相透明的混合溶液。再进入均质机,经过均质处理,使乳液中分散相的颗粒更细小,更均匀,得到高度稳定的产品。将均质液打入冷却罐冷却、排气,将液体中的气泡排出、陈放(老化),使体系更稳定,再打入成品贮罐存放,送入过滤器过滤,除去机械杂质和絮状物,进行包装、入库,以上所有成分的加入量见表1。
表1实施例1中原料一览表
将制备得到的负性彩色光刻胶脱胶剂按照10∶90进行稀释,在常温下滴到涂有负性彩色光刻胶的玻璃上并立即用水冲洗,负性彩色光刻胶被剥离。
实施例2:
和实施例1的操作方法相同,所不同的是各组份含量不同,具体见表2。
表2实施例2中原料一览表
实施例3:
和实施例1的操作方法相同,所不同的是各组份含量不同,具体见表3。
表3实施例3中原料一览表
Claims (2)
1、一种负性彩色光刻胶脱胶剂,其特征在于它是由如下重量份数的组分组成:五水偏硅酸钠0.5~1%,对甲基苯磺酸钠2~5%,单乙醇胺3~5%,三乙醇胺25~35%,脂肪醇聚氧乙烯醚0.5~1%,乙二醇苯醚25~35%,环己酮4~8%,乙二醇丁醚1~5%,其余为水。
2、权利要求1所述的负性彩色光刻胶脱胶剂的制备方法,其特征在于它包括如下步骤:
(1)向乳化罐内加入去离子水,先后加入五水偏硅酸钠和对甲基苯磺酸钠,搅拌混匀;
(2)向乳化罐内加入单乙醇胺,搅拌混匀;
(3)向乳化罐内加入三乙醇胺,搅拌混匀;
(4)向乳化罐内加入脂肪醇聚氧乙烯醚,搅拌混匀;
(5)向乳化罐内加入乙二醇苯醚,搅拌混匀;
(6)向乳化罐内加入环己酮,搅拌混匀;
(7)向乳化罐内加入乙二醇丁醚,搅拌混匀;
(8)把制得的均相透明的混合溶液送入均质机,经过均质处理;
(9)均质液经冷却、排气和过滤后包装。