CN101250362A - 一种紫外光固化灯罩镀膜底漆 - Google Patents
一种紫外光固化灯罩镀膜底漆 Download PDFInfo
- Publication number
- CN101250362A CN101250362A CNA2008100272532A CN200810027253A CN101250362A CN 101250362 A CN101250362 A CN 101250362A CN A2008100272532 A CNA2008100272532 A CN A2008100272532A CN 200810027253 A CN200810027253 A CN 200810027253A CN 101250362 A CN101250362 A CN 101250362A
- Authority
- CN
- China
- Prior art keywords
- resin
- lampshade
- priming paint
- acrylate
- ultraviolet light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种紫外光固化灯罩镀膜底漆，它的重量百分组成为酚醛环氧丙烯酸酯10～40wt％、二官能脂肪族聚氨酯丙烯酸酯5～20wt％、大分子的纯丙树脂20～40wt％、高官能丙烯酸酯5～30wt％、单官能丙烯酸酯5～30wt％、附着力促进树脂5～10wt％、光引发剂1～5wt％、稀释剂20～60wt％、助剂0.01～1wt％，本发明选用酚醛环氧树脂提高产品的耐高温，大分子纯丙树脂可填充表面孔粒结构，解决了在不饱和聚酯玻璃纤维增强模塑料BMC基材上真空镀膜附着力差的问题。
Description
技术领域
本发明涉及一种紫外光固化涂料，尤其涉及灯罩真空镀膜配套使用的涂料。
背景技术
车灯反射灯罩大多用不饱和聚酯玻璃纤维增强模塑料BMC注塑成型，内表面有很多孔粒结构，不够光滑，缺乏光泽，如果直接气相沉积一层铝膜，仍然得不到光滑表面，难以形成有效的反射镜面，北美BMC车灯反射灯罩100％采用了紫外光固化UV涂装工艺，国内两年前开始引进该工艺涂装试验，目前已有好几条线可以正常生产，但紫外光固化UV涂料都是100％进口，且价格昂贵。
中国专利CN1294162是一种灯罩镀膜底漆，由成膜树脂、稀释剂、光引发剂、助剂组成，按一定的重量百分比配比后，混合搅拌均匀，制成。
发明内容
本发明需解决在不饱和聚酯玻璃纤维增强模塑料BMC基材镀膜附着力差的问题。
本发明所采用的技术方案是：一种紫外光固化灯罩镀膜底漆，其其重量百分组成为：酚醛环氧丙烯酸酯10～40wt％，二官能脂肪族聚氨酯丙烯酸酯5～20wt％，大分子的纯丙树脂20～40wt％，高官能丙烯酸酯5～30wt％，单官能丙烯酸酯5～30wt％，附着力促进树脂5～10wt％，光引发剂1～5wt％，稀释剂20～60wt％、助剂0.01～1wt％，本发明选用酚醛环氧树脂提高产品的耐高温，大分子纯丙树脂可填充表面孔粒结构。
进一步：上述的底漆中，所述的附着力促进树脂是乙烯-醋酸乙烯共聚物、丙烯-醋酸乙烯共聚物、苯氧基二甲基硅烷化合物中的一种或两种；所述的光引发剂是苯基亚膦酸二乙酯、二苯甲酮、α一羟基异丙基苯甲酮、α一羟基环己基苯甲酮中的一种或几种，这些光引发剂具有较高的光敏性和热稳定性；所述的稀释剂是己二醇二丙烯酸酯、新戊二醇二丙烯酸酶、三羟甲基丙烷三丙烯酸酯中的一种或几种；常用的助剂有阻聚剂、消泡剂、流平剂和颜填料等助剂，它们的主要作用是改善涂料性能，增加紫外光敏感性，降低施工难度。
上述配方中优选的配方是酚醛环氧丙烯酸酯15～30wt％、二官能脂肪族聚氨酯丙烯酸酯8～18wt％、大分子的纯丙树脂10～30wt％、高官能丙烯酸酯10～20wt％、单官能丙烯酸酯10～20wt％、附着力促进树脂6～9wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.08～0.8wt％。
将上述紫外光固化UV灯罩镀膜底漆应用在不饱和聚酯玻璃纤维增强模塑料BMC车灯反射灯罩气相镀铝的底层，即先在灯罩内表面喷涂一层紫外光固化UV灯罩镀膜底漆，固化后非常光滑的表层再镀铝膜，形成高度平滑的反射镜面。本发明选用酚醛环氧树脂提高产品的耐高温，大分子纯丙树脂可填充表面孔粒结构，特殊的附着力促进树脂解决了在BMC基材上附着力的问题。
用上述紫外光固化UV灯罩镀膜底漆处理过的BMC反射灯罩再气相镀铝，使灯罩表面的镀层具有以下优点：
1、涂层与BMC塑料之间的附着力强；
2、通过了180℃高温烘烤测试；
3、表面高度平滑
具体实施方式
以下实施例是紫外光固化UV灯罩镀膜底漆优选的配方，这些配方为非限定性实施方式，其只是用于具体说明本发明，本领域的技术人员完全可以根据本发明的思路和选料配比筛选出的配方均为本发明的保护范围。
实施例1
一种紫外光固化灯罩镀膜底漆，其组成为酚醛环氧丙烯酸酯15wt％、二官能脂肪族聚氨酯丙烯酸酯15wt％、大分子的纯丙树脂10wt％、高官能丙烯酸酯10wt％、单官能丙烯酸酯10wt％、附着力促进树脂6wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.08～0.8wt％，附着力促进树脂是乙烯-醋酸乙烯共聚物，光引发剂是苯基亚膦酸二乙酯，稀释剂是己二醇二丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化UV灯罩镀膜底漆处理过的BMC反射灯罩再气相镀铝，使灯罩表面的镀层具有以下优点：
1、涂层与BMC塑料之间的附着力强；
2、通过了180℃高温烘烤测试；
3、表面高度平滑。
实施例2
一种紫外光固化灯罩镀膜底漆，其组成为酚醛环氧丙烯酸酯16wt％、二官能脂肪族聚氨酯丙烯酸酯8wt％、大分子的纯丙树脂12wt％、高官能丙烯酸酯10wt％、单官能丙烯酸酯12wt％、附着力促进树脂9wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.08～0.8wt％，其中附着力促进树脂是丙烯-醋酸乙烯共聚物，光引发剂是二苯甲酮，稀释剂是新戊二醇二丙烯酸酶，再加上常用助剂。
用上述配方的紫外光固化UV灯罩镀膜底漆处理过的BMC反射灯罩再气相镀铝，使灯罩表面的镀层具有以下优点：
1、涂层与BMC塑料之间的附着力强；
2、通过了180℃高温烘烤测试；
3、表面高度平滑。
实施例3
一种紫外光固化灯罩镀膜底漆，其组成为酚醛环氧丙烯酸酯18wt％、二官能脂肪族聚氨酯丙烯酸酯10wt％、大分子的纯丙树脂10wt％、高官能丙烯酸酯11wt％、单官能丙烯酸酯11wt％、附着力促进树脂7wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.08～0.8wt％，其中附着力促进树脂是苯氧基二甲基硅烷化合物，光引发剂是α一羟基异丙基苯甲酮，稀释剂是三羟甲基丙烷三丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化UV灯罩镀膜底漆处理过的BMC反射灯罩再气相镀铝，使灯罩表面的镀层具有以下优点：
1、涂层与BMC塑料之间的附着力强；
2、通过了180℃高温烘烤测试；
3、表面高度平滑。
实施例4
一种紫外光固化灯罩镀膜底漆，其成份为酚醛环氧丙烯酸酯18wt％、二官能脂肪族聚氨酯丙烯酸酯11wt％、大分子的纯丙树脂10wt％、高官能丙烯酸酯10wt％、单官能丙烯酸酯10wt％、附着力促进树脂6wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.08～0.8wt％，其中附着力促进树脂是乙烯-醋酸乙烯共聚物、丙烯-醋酸乙烯共聚物两种混合物、光引发剂是苯基亚膦酸，稀释剂是己二醇二丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化UV灯罩镀膜底漆处理过的BMC反射灯罩再气相镀铝，使灯罩表面的镀层具有以下优点：
1、涂层与BMC塑料之间的附着力强；
2、通过了180℃高温烘烤测试；
3、表面高度平滑。
实施例5
一种紫外光固化灯罩镀膜底漆，其组成为酚醛环氧丙烯酸酯22wt％、二官能脂肪族聚氨酯丙烯酸酯8wt％、大分子的纯丙树脂10wt％、高官能丙烯酸酯10wt％、单官能丙烯酸酯10wt％、附着力促进树脂7wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.08～0.8wt％，其中附着力促进树脂是丙烯-醋酸乙烯共聚物、苯氧基二甲基硅烷化合物中的混合物，光引发剂是苯基亚膦酸二乙酯，稀释剂是己二醇二丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化UV灯罩镀膜底漆处理过的BMC反射灯罩再气相镀铝，使灯罩表面的镀层具有以下优点：
1、涂层与BMC塑料之间的附着力强；
2、通过了180℃高温烘烤测试；
3、表面高度平滑。
实施例6
一种紫外光固化灯罩镀膜底漆，其组成为酚醛环氧丙烯酸酯16wt％、二官能脂肪族聚氨酯丙烯酸酯8wt％、大分子的纯丙树脂10wt％、高官能丙烯酸酯11wt％、单官能丙烯酸酯12wt％、附着力促进树脂8wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.08～0.8wt％，其中附着力促进树脂是乙烯-醋酸乙烯共聚物，光引发剂是苯基亚膦酸二乙酯，稀释剂是己二醇二丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化UV灯罩镀膜底漆处理过的BMC反射灯罩再气相镀铝，使灯罩表面的镀层具有以下优点：
1、涂层与BMC塑料之间的附着力强；
2、通过了180℃高温烘烤测试；
3、表面高度平滑。
实施例7
一种紫外光固化灯罩镀膜底漆，其组成为酚醛环氧丙烯酸酯15wt％、二官能脂肪族聚氨酯丙烯酸酯8wt％、大分子的纯丙树脂13wt％、高官能丙烯酸酯10wt％、单官能丙烯酸酯10wt％、附着力促进树脂6wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.08～0.8wt％，其中附着力促进树脂是乙烯-醋酸乙烯共聚物，光引发剂是苯基亚膦酸二乙酯，稀释剂是己二醇二丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化UV灯罩镀膜底漆处理过的BMC反射灯罩再气相镀铝，使灯罩表面的镀层具有以下优点：
1、涂层与BMC塑料之间的附着力强；
2、通过了180℃高温烘烤测试；
3、表面高度平滑。
实施例8
一种紫外光固化灯罩镀膜底漆，其组成为酚醛环氧丙烯酸酯15wt％、二官能脂肪族聚氨酯丙烯酸酯8wt％、大分子的纯丙树脂10wt％、高官能丙烯酸酯10wt％、单官能丙烯酸酯12wt％、附着力促进树脂8wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.08～0.8wt％，其中附着力促进树脂是乙烯-醋酸乙烯共聚物，光引发剂是苯基亚膦酸二乙酯，稀释剂是己二醇二丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化UV灯罩镀膜底漆处理过的BMC反射灯罩再气相镀铝，使灯罩表面的镀层具有以下优点：
1、涂层与BMC塑料之间的附着力强；
2、通过了180℃高温烘烤测试；
3、表面高度平滑。
Claims (3)
1、一种紫外光固化灯罩镀膜底漆，其特征在于其重量百分组成为：酚醛环氧丙烯酸酯10～40wt％、二官能脂肪族聚氨酯丙烯酸酯5～20wt％、大分子的纯丙树脂20～40wt％、高官能丙烯酸酯5～30wt％、单官能丙烯酸酯5～30wt％、附着力促进树脂5～10wt％、光引发剂1～5wt％、稀释剂20～60wt％、助剂0.01～1wt％。
2、如权利要求1所述的紫外光固化灯罩镀膜底漆，其特征在于：所述的附着力促进树脂是乙烯-醋酸乙烯共聚物、丙烯-醋酸乙烯共聚物、苯氧基二甲基硅烷化合物中的一种或两种；
所述的光引发剂是苯基亚膦酸二乙酯、二苯甲酮、α一羟基异丙基苯甲酮、α一羟基环己基苯甲酮中的一种或几种；
所述的稀释剂是己二醇二丙烯酸酯、新戊二醇二丙烯酸酶、三羟甲基丙烷三丙烯酸酯中的一种或几种。
3、如权利要求2所述的紫外光固化灯罩镀膜底漆，其特征在于：酚醛环氧丙烯酸酯15～30wt％、二官能脂肪族聚氨酯丙烯酸酯8～18wt％、大分子的纯丙树脂10～30wt％、高官能丙烯酸酯10～20wt％、单官能丙烯酸酯10～20wt％、附着力促进树脂6～9wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.08～0.8wt％。