CN101248197B - 具有抗失延裂纹的药皮焊条及由此产生的堆焊 - Google Patents
具有抗失延裂纹的药皮焊条及由此产生的堆焊 Download PDFInfo
- Publication number
- CN101248197B CN101248197B CN2006800031802A CN200680003180A CN101248197B CN 101248197 B CN101248197 B CN 101248197B CN 2006800031802 A CN2006800031802 A CN 2006800031802A CN 200680003180 A CN200680003180 A CN 200680003180A CN 101248197 B CN101248197 B CN 101248197B
- Authority
- CN
- China
- Prior art keywords
- welding
- built
- alloy
- crack
- crackle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
使用Ni-Cr-Fe合金的Ni-Cr-Fe合金形式的堆焊、焊条和焊剂以及焊接方法。所述合金按重量百分比包含:27-31 Cr、6-11 Fe、0.01-0.04 C、1.5-4 Mn、1-3 Nb、高达3 Ta、1-3(Nb+Ta)、0.01-0.50 Ti、0.0003-0.02 Zr、0.0005-0.004 B、<0.50 Si、至多0.50 Al、<0.50 Cu、<1.0 W、<1.0 Mo、<0.12 Co、<0.015 S、<0.015 P、至多0.01 Mg、余量的Ni和附带的添加物和杂质。所述焊接方法包括使用短弧的焊接,其中焊条端至堆焊的距离保持在小于0.125英寸。
Description
相关申请的交叉引用
本申请要求2005年1月25日提交的第60/647,179号,题为“具有抗失延裂纹的药皮焊条”的美国临时申请的权益,本文引入其全部内容。
发明背景
发明领域
本发明总体涉及镍、铬、铁的焊接合金,由其制造的用于生产焊件的物件,以及焊接件和生产这些焊件的方法。本发明还涉及焊条、焊丝、焊药涂剂(fluxchemical coating)组合物以及焊接方法,以获得堆焊组合物,该堆焊组合物在原子能发电环境中尤其具有抗失延裂纹性能,以及具有抗一次水(primary water)应力腐蚀裂纹性能。
相关技术描述
在包括用于原子能发电设备在内的各种焊接应用中,需要提供抵抗各种裂纹现象的焊件。所述裂纹现象不但包括应力腐蚀裂纹,而且还包括热裂纹、冷裂纹以及根部裂纹。
自20世纪的后半叶就已存在商用和军用的原子能发电。在这期间,该工业用含有约30%的更高铬含量的合金取代了含有14%至15%铬的第一代NiCrFe合金。该变化是以发现能用包含该含量铬的这种类型的合金来避免核纯水(pure water)中的应力腐蚀裂纹为基础的。含约30%铬含量的NiCrFe合金现已使用了约20至25年。
在核电站里需要大量焊接和被焊接产品的原子能发电设备的具体应用是核蒸汽发生器的装配。该设备基本上是一个大的管-壳式热交换器,该热交换器可从来自一次核反应堆冷却剂的二次水(secondary water)产生蒸汽。该蒸汽发生器的关键部件是管板。该管板有时直径为15至20英寸,厚度大于一英寸,通常由高强度的低合金钢铸造而成,所述合金钢必须用具有优良的可成型性并具有抗核纯水应力腐蚀裂纹性能的NiCrFe合金进行堆焊。由于管板的尺寸,在堆焊期间所述堆焊要承受相当大的残余应力。此外,在焊接金属堆焊层(overlay)中钻孔后,其必须能够被重新焊接,所述孔接受数千个小蒸汽发生器管。这些管子必须被焊封到堆焊层的堆焊上,以构成氦气密封的焊接。这些焊接必须具有非常高的质量并且必须提供30至50年的可预测的寿命。另外,在堆焊层的堆焊和被焊接的蒸汽发生器管中,必须提供极好的抗裂性。关于对抗热裂性,也称为抗“硬化裂纹”性以及抗应力腐蚀裂纹性能的需求已通过大部分含30%铬的焊件得到解决。
除了抗热裂性和抗应力腐蚀裂纹性能以外,管子与管板的焊接需要抗根部裂纹性能。通过熔化管端和管周围的一圈堆焊层材料进行管子与管板的焊接(使用或不使用额外的焊料),从而密封管壁和管板的孔之间的空间。这些焊接在管子与管板界面处的焊接底部有开裂倾向。由于其发生在焊接的根部,因此这种类型的裂纹被称为“根部裂纹”。含30%铬的焊接合金不具有抗根部裂纹性能。
可能遇到的第三种类型的裂纹是冷裂纹,也称为“失延裂纹”或“DDC”。该裂纹仅发生在完成焊接凝固后的固化状态。在凝固发生后,由于在较低温度下焊接合金体积的减少,收缩应力开始出现。同时,一旦凝固完成,对于几百度延展性复原迅速发生,然后延展性急剧暂时丧失,接着延展性再进一步逐步连续恢复直至到达室温。如果当合金显示出这种急剧的延展性丧失时,冷却的残余应力足够大,那么可以发生固态裂纹(DDC)。这是由于在通常温度下,不具有足以抵抗应力的强度或延展性的部分微观结构造成的。目前可商购的含有30%铬的焊接合金不能充分抵抗DDC。
在过去十年间,在用于核工业的单相奥氏体镍-铬-铁合金和焊接产品中,失延裂纹(DDC)/冷裂纹已成为引起人们关注的主题。科学界已经意识到含约30%Cr的NiCrFe合金具有抗核环境中的一次水应力腐蚀裂纹(PWSCC)的性能。然而,较高的Cr水平,以及减少的Nb,趋于得到沿长直的树枝状结晶边界取向附生凝固的堆焊。当经受较高应变和升高的温度时,这些边界尤其易于产生DDC。这些现象在含30%铬的镍合金中似乎更为普遍,所述镍合金例如因科内尔合金690和AWS级NiCrFe-7的焊接产品。因科内尔焊料52M和焊带52M(AWS级NiCrFe-7A-UNS3N06054)的发明已经解决了DDC裂纹的倾向性。美国专利第6,242,113号公开的本发明人的发明包括了这些产品,在此将其全部内容引入作为参考。本申请具体解决了在药皮焊条中的DDC/冷裂纹。
美国焊接学会(“AWS”)和美国国家标准协会(“ANSI”)的各种规范是令人关注的背景信息,即ANSI/AWS规范A5.11/A5.11M:2005,题为“用于屏蔽金属弧焊的镍和镍合金焊条的规范”(“Specification for Nickel andNickel-Alloy Welding Electrodesfor Shielded Metal Arc Welding”)和ANSI/AWS规范A5.14/A5.14M:2005,题为“镍和镍合金的裸焊条和焊棒的规范”(“Specification for Nickel and Nickel-Alloy Bare Welding Electrodesand Rods”)。在此将这两篇规范的全部内容引入作为参考。
发明概述
本发明的目的是提供镍、铬、铁的焊接合金,由此制得的焊件,以及焊接方法,该焊接方法除了提供抗热裂纹、抗DDC/冷裂纹、抗根部裂纹以及抗应力腐蚀裂纹的性能以外,还提供期望的强度和耐蚀性。
本发明的另一目的是提供具有焊剂涂层的镍、铬、铁型焊接合金,该焊接合金尤其适用于装配原子能发电所使用的设备。
根据本发明,提供了用于产生堆焊的镍、铬、铁合金。按照重量百分比,所述合金包含约27%至31%的铬;约6%至11%的铁;约0.01%至0.04%的碳;约1.5%至4%的锰;约1%至3%的铌和钽;低于0.75%的硅;约0.01%至0.50%的钛;至多0.50%的铝;低于0.50的铜;低于1.0%的钨;低于1.0%的钼;低于0.12%的钴;约0.0003%至0.02%的锆;低于约0.015%的硫;约0.0005%至0.004%的硼;低于约0.02%的磷;高达约0.02的镁;以及余量的镍(优选最少48%Ni)和附带的杂质。
以铬含量来说,所述合金具有足够的抗应力腐蚀裂纹性能。所述合金的形式可以是堆焊、药皮焊条、具有药皮的焊丝形式的焊条、具有焊剂芯的鞘形式的焊条、堆焊层或包含合金基体的焊件,例如带有本发明合金堆焊层的钢。其可用于产生堆焊或焊件的方法,该焊件的形式是用于产生堆焊的药皮焊条。产生堆焊的方法可包括生产镍、铬焊丝或镍、铬、铁焊丝的药皮焊条,以及使用“短弧”熔化焊条以产生堆焊,同时由于焊剂涂层和堆焊的相互作用,保持期望水平的硼、锆和镁。短弧被定义为从焊条端到堆焊的距离,并且该距离小于0.125英寸并优选为约0.020至0.040英寸。为了堆焊的优良抗裂纹性能,期望将堆焊中Nb:Si之比维持在5:1至7:1。本领域技术人员公知焊条药皮的生产,因此无需在此详细描述。本发明的焊剂涂层包含氟化物、氧化物、碳酸盐以及本文提及的所选金属间化合物的混合物。
简言之,本发明涉及Ni-Cr-Fe合金,按重量百分比,其包含:27-31Cr、6-11Fe、0.01-0.04C、1.5-4Mn、1-3Nb、高达3Ta、1-3(Nb+Ta)、0.10-0.50Ti、0.0003-0.02Zr、0.0005-0.004B、<0.50Si、至多0.20Al、<0.20Cu、<1.0W、<1.0Mo、<0.12Co、<0.015S、<0.015P、至多0.01Mg、余量的Ni和附带的添加物和杂质。优选地,该合金至少包含48%的Ni。更优选地,该合金包含29-31Cr、6.5-9Fe、0.0007-0.004B、2.5-3.5Mn、0.003-0.01Zr和至少50Ni。
本发明还包括不掺杂的Ni-Cr-Fe合金堆焊,按重量百分比,其包含:27-31Cr、6-11Fe、0.01-0.04C、1.5-4Mn、1-3Nb、高达3Ta、1-3(Nb+Ta)、0.10-0.50Ti、0.0003-0.02Zr、0.0005-0.004B、<0.50Si、至多0.20Al、<0.20Cu、<1.0W、<1.0Mo、<0.12Co、<0.015S、<0.015P、0.004-0.01Mg、余量的Ni和附带的添加物和杂质。优选地,该堆焊至少包含50Ni。优选地,该堆焊还包含0.0007-0.003B、0.001-0.01Zr和至少50Ni。更进一步优选,该堆焊包含0.0005-0.002B、0.001-0.01Zr和至少50Ni。
根据本发明,目前优选的用于产生堆焊的方法包括以下步骤:提供具有与之相关焊剂的Ni-Cr-Fe或Ni-Cr-Fe焊丝的药皮焊条以及用短弧技术在焊接步骤中熔化所述焊条或焊丝,其中焊条或钢丝端与堆焊的间隔小于0.125英寸,以产生堆焊,按重量百分比,该堆焊包含:27-31Cr、6-11Fe、0.01-0.04C、1.5-4Mn、1-3Nb、高达3Ta、1-3(Nb+Ta)、0.01-0.50Ti、0.0003-0.02Zr、0.0005-0.004B、<0.50Si、至多0.50Al、<0.50Cu、<1.0W、<1.0Mo、<0.12Co、<0.015S、<0.015P、0.004-0.01Mg、余量的Ni和附带的添加物和杂质。焊条或焊丝端至堆焊的间隔优选为0.02至0.04英寸。优选使用屏蔽金属电弧法进行本发明的焊接步骤。在本方法中,焊剂优选包含一种或多种Ni、Mg和Si的混合物并产生堆焊,其中Nb和Si的重量比为5:1至7:1。
发明详细描述
本发明的NiCrFe焊接合金含有足量的镍和铬,并且相当严格地控制次要化学组分以及痕量元素,以便于除了提供极好的抗应力腐蚀裂纹性能以外,还提供适当的耐蚀性。另外,该合金在重新加热的条件下必须具有抗硬化裂纹性能、抗根部裂纹性能以及抗冷裂纹性能。
为了赋予抗硬化裂纹性能,对于其合金元素,所述合金应具有足够的溶解性以及窄的液相线-固相线温度范围。同样,该合金应具有低水平的硫、磷和其它低熔点的元素,并且该合金应含有最低水平的在合金中形成低熔点相的元素。
通过提高晶界的热稳性和延展性来控制抗冷裂纹性能。根据本发明的范围,其通过铌、锆和硼的仔细组合得以实现。需要限制铌含量来避免二次相(secondary phases)的形成,同时有助于固态的晶界强度。对于抗应力腐蚀裂纹性能也需要铌。硼有助于晶界强度并且改善热延展性,但是高于本发明的水平时,对抗热裂纹性能是不利的。锆改善了晶界的固态强度和延展性,并改善了晶界的抗氧化性。当高于本发明的水平时,锆导致热裂纹。当硼和锆的水平低于本发明时,具有相对较低的抗冷裂纹性能。当单独加入硼时,显示出对抗冷裂纹性能非常微小的改进,但是使用本发明水平的硼和锆时,基本上消除冷裂纹。
镍合金焊接领域的技术人员很容易理解,指定用于核设施(nuclearservice)的焊接的质量要求包括抗热裂纹性能、抗冷裂纹性能、抗弯曲裂纹性能、抗根部裂纹性能以及抗弧坑裂纹性能。现有的NiCrFe-7分类产品通常对大部分这些类型的裂纹提供不同程度的抵抗性能,但是倾向于DDC。对本发明进行设计以提供对DDC的补救以及改善的抗弧坑裂纹性能,从而使用屏蔽金属弧焊法(SMAW)能够进行焊接。失延裂纹是一种现象,其特征在于,在远低于单相奥氏体NiCrFe合金和焊缝的固相线温度下,固态中发生的晶界裂纹。这被认为与高温蠕变现象有关,并且例如加入少量的硼和锆以改善晶界强度和延展性。以下试验用于评价上述类型的裂纹:
(1)通过堆焊层堆焊的渗液探伤试验来评价热裂纹和弧坑裂纹;
(2)对具有模拟管子和管板焊接和修补的堆焊层中的一系列钻孔进行切割、蚀刻,并在60倍的放大倍数下评价以检查DDC和任何其它的热裂纹迹象;
(3)为了评价根部裂纹,使用端面焊缝,将因科内尔合金690的固定板(solid plate)沿着焊接堆焊层的一侧进行焊接,以模拟管子和管板的焊缝。对该接缝进行切割、磨光,并在60倍的放大倍数下,在沿其长度的不同位置进行观察以检查根部裂纹趋势;
(4)还将标准3/8英寸厚的横向侧弯从焊接堆焊层上切下,并绕2T心轴弯曲180°。然后使用每次弯曲所记录的裂缝数和裂缝尺寸来研究被拉长约20%的弯曲外表面的弯曲裂纹或“裂缝”。
一系列堆焊的化学性质如以下表1所示。每种堆焊的化学组成包含约30%Cr、58%Ni、8%Fe和不同含量的Nb、Mn以及其它微量元素。在表中每一组分之下将上述试验的简要报告制成表格。表格和结果是显而易见的,但是对硼和锆与DDC或冷裂纹的检验表明,当不含两者之一或不含两者时,规律性出现冷裂纹;而在硼含量为约0.0005%至0.004%,且锆含量为约0.0003%至0.02%时,可避免冷裂纹。还应指出,当具有足够水平的Nb和Mn,并适当控制其它微量元素时,可避免热裂纹。硼和锆的添加以及改善的Nb和Mn水平的另一优点是可以降低Al的水平,这改善抗弧坑裂纹性能。指定批号83F8短弧和76F9HTG的表1的试验显示,用于得到最高质量堆焊的焊条堆焊的最佳化学组分。根据本发明,通过SMAW法堆焊的不掺杂的化学组成如下所示:优选地,最少48%Ni;27%至31%Cr;6%至11%Fe;1%至3%Nb;1.5%至4%Mn;0.01至0.04%C;0.005至0.01Mg;低于0.015%S;低于0.015%P;0.0005%至0.004%B;0.0003%至0.02%Zr;0.01%至0.50%Ti;以及至多0.50%Al。在其它功能中,Nb和Ta形成一次碳化物(源自熔融物),该碳化物在凝固过程中趋于控制晶粒大小和针状(pin)晶界,并且趋于冷却,以使得在晶界产生更大的迂曲度。弯曲的晶界有利于在焊接过程中减少产生DDC(失延裂纹)的趋势。本文引用的AWS规范包括题为Nb+Ta的专栏。在历史上,这些元素被列在一起,这是因为它们一起天然地出现在地壳中,并且在电子学应用出现之前,人们没有花费过多的精力将全部的Ta从Nb中提取出来。由于它们一起出现并且行为相似,所以将它们列在一起。这两种元素都具有非常高的熔化温度,但是铌的密度约是钽的一半。这两种元素都具有体心立方晶体结构并都具有同样的晶格参数(最接近原子)。因此,这些观测的实践结果为,由于钽的成本极高,通常它不作为添加物与铌一同使用。铌的密度约是钽的一半。这导致Ta在作为碳化物形成元素(carbide former)时所起的作用是铌的一半。虽然Ta可以是更活泼的碳化物形成元素,但是需要两倍的铌的重量百分比,以提供与铌相同的原子数。
使用本发明的这种堆焊材料(指定为“152M”)所获得的通常机械性能为:
表1
表1-续
简言之,通过使用本发明,镍和30%Cr可以获得抗应力腐蚀裂纹性能而没有遭受DDC损伤。使合金组合物平衡以将孔隙率和所有类型的裂纹最小化,并应操作人员最大限度的请求以及3/32和1/8英寸直径焊条的不当性能而设计药皮组合物。
由于在焊条涂料中使用了焊剂化学药品和硅酸盐粘合剂,所述焊条的生产与本发明人的在先美国专利第6,242,113号(因科内尔合金WE52M)中的焊条生产不同。使用硅酸钠粘合剂以及有时使用硅酸钾粘合剂通常增加堆焊中的硅含量,这趋于增加裂纹趋向。对抗硅的措施是添加铌。对于镍铬型合金,为了具有优良的抗裂纹性能,优选使用Nb和Si之比约为5:1至7:1。表1的倒数第二行所报导的数据计算了不同候选合金的Nb和Si之比。倒数第六行是不同的质量测试结果:SB=侧弯,SB1和SB2是实际弯曲的样品,并使用裂缝数并且有时使用各自的裂缝长度进行评价。SB总数以英寸为单位并且是两个边带裂缝长度的总和。TS=管板。如下所示进行模拟管板焊接:首先,堆焊待测材料的焊接金属堆焊层,在模拟管板上钻孔(但是没有管子),然后围绕孔的顶端进行GTAW焊接以模拟管子与管板的焊接。随后,沿孔的中心线将板切割,以暴露模拟焊接的横截面。将样品磨光、蚀刻并在60倍的放大倍数下检测以寻找裂纹。TS裂纹被认为是DDC/冷裂纹(失延裂纹)。虽然并非全部的裂纹均具有典型的DDC迹象时,但是大部分裂纹具有典型的DDC迹象并且在最低可能造成DDC的应变下被认为是DDC。RC1和RC2是对管子与管板焊接的根部裂纹趋向的尺度。
表1再向上的十六行是对不同药皮焊条堆焊样品的化学分析。由于通常进行药皮焊条(SMAW)焊接中升高的硅含量高,所以以实现上述Nb和Si之比为目的开始研究。在研究初期,测试将B和Zr引入堆焊的不同方法并明确了事实上不可能通过使用药皮添加物控制达到有效所必需的少量。因此,本研究起始时使用焊条芯中含有B(0.004%)和Zr(0.006%)的裸焊条芯(表1中指定为Y9570)。通过生产药皮焊条,然后评价裂纹趋向开始基础研究。指定为1005、1008、1011以及1018的样品是早期的药皮焊条样品,其在堆焊中不包含B、Zr或Mg。经验认为,在焊接过程中,通过简单的氧化发生焊条芯中的B和Zr添加物从堆焊中剥离。对于样品1018,将镍镁添加物制成药皮,对于样品1022、1023以及1024,评价镍锆添加物。虽然不存在镁时,但是样品1023偶尔也没有出现TS裂纹。由于镁和锆都是公知的非常强的脱氧剂,所以样品1018至1024中的药皮存在镍镁和镍锆。将它们加入成为镍合金,以便在使用过程中保持它们的脱氧能力。虽然向样品1018中加入NiMg,但是在堆焊分析中没有发现Mg。这可能是由于未使用“短弧”长度技术(后文可获悉)。对于样品1022、1023以及1024,注意到Zr堆焊适度增加至高达约0.009%至0.01%;然而,裂纹仍继续存在于TS(DDC)范畴中。在样品1038中将镍镁焊剂的含量增加至5%,以及在样品1040中将其增加至7.5%,这通过在堆焊中保留0.003%得以实现。对于这些样品,发现仅B=0.0015%且Zr=0.01%的样品1023和B=0.0014%且Zr=0.013%的样品1038对TS产生良好的结果(分别为0和3)。基于这些结果,决定进行若干直径的“实验性”生产运行。最初,使用7.5%NiMg焊剂制造76F9,当在堆焊中保持Mg=0.006%、Zr=0.003%以及B=0.001%时,没有TS裂纹,这是有利的结果。然后制造其它的批号为83F5、83F6、83F7以及83F8的样品,它们都具有含7.5%NiMg的相同的焊剂湿混合物。挤压和烘焙药皮焊条后,进行测试,并且令人吃惊的是,在83F7中发现9条TS裂纹以及在83F8中发现23条TS裂纹。在测定化学分析后,更令人意想不到的是,堆焊中不含B、Zr或Mg。再次评估试车并且发现在焊接过程中维持短弧长度的重要性。结论是这种短弧技术有助于保护产品中的脱氧剂并在堆焊中保持Mg、B以及Zr。观察使用短弧的83F8与使用长弧的83F8,并进行比较使用长弧的23条TS裂纹和使用短弧的1条TS裂纹。同样地,对使用长弧的83F7与使用短弧的83F7进行比较,并发现长弧的TS裂纹为9条而短弧的TS裂纹为2条。还注意到,堆焊中保留的B、Zr以及Mg在期望的范围内。
“短弧”被定义为焊条端至堆焊的距离并且其小于0.125英寸并优选为约0.020至0.040英寸。“长弧”大于0.125英寸。
因此,通过将堆焊中优选的Nb和Si之比控制在约5:1至7:1并通过使用短弧焊接技术,实现堆焊中期望的B、Zr以及Mg分析。
虽然已详细描述本发明的具体实施方案,但是本领域技术人员应理解,按照本公开的整体教导可对这些细节进行多种修改和选择。目前本文所描述的优选实施方案仅仅是示例性的,并不限制本发明的范围,所述范围由所附权利要求以其任意和所有等同替代的全部范围所给定的。
Claims (7)
1.Ni-Cr-Fe焊接合金,按重量百分比,其包含:27-31Cr、6-11Fe、0.01-0.04C、1.5-4Mn、1-3Nb、高达3Ta、1-3(Nb+Ta)、0.01-0.50Ti、0.0003-0.02Zr、0.0005-0.004B、<0.50Si、至多0.50Al、<0.50Cu、<1.0W、<1.0Mo、<0.12Co、<0.015S、<0.015P、至多0.01Mg、余量的Ni和附带的添加物和杂质。
2.如权利要求1所述的焊接合金,其中存在至少48%的Ni。
3.如权利要求1所述的焊接合金,其包含29-31Cr、6.5-9Fe、0.0005-0.004B、2.5-3.5Mn、0.0005-0.01Zr和至少50Ni。
4.不掺杂的Ni-Cr-Fe合金堆焊,按重量百分比,其包含:27-31Cr、6-11Fe、0.01-0.04C、1.5-4Mn、1-3Nb、高达3Ta、1-3(Nb+Ta)、0.01-0.50Ti、0.0003-0.02Zr、0.0005-0.004B、<0.50Si、至多0.50Al、<0.50Cu、<1.0W、<1.0Mo、<0.12Co、<0.015S、<0.015P、0.004-0.01Mg、余量的Ni和附带的添加物和杂质。
5.如权利要求4所述的堆焊,其中存在至少50Ni。
6.如权利要求5所述的堆焊,其包含0.0007-0.003B和0.001-0.01Zr。
7.如权利要求6所述的堆焊,其包含0.0005-0.002B、0.001-0.01Zr和至少50Ni。