CN101239856A - Multi-nutrition release-controllable special-purpose fertilizer for clivia and preparation method thereof - Google Patents
Multi-nutrition release-controllable special-purpose fertilizer for clivia and preparation method thereof Download PDFInfo
- Publication number
- CN101239856A CN101239856A CNA2008100143654A CN200810014365A CN101239856A CN 101239856 A CN101239856 A CN 101239856A CN A2008100143654 A CNA2008100143654 A CN A2008100143654A CN 200810014365 A CN200810014365 A CN 200810014365A CN 101239856 A CN101239856 A CN 101239856A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- modified epoxy
- parts
- fertilizer
- resin integument
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a clivia minata specialized controlled releasing fertilizer and the preparing method thereof. The fertilizer is obtained by recompounding the compounds of modified epoxy resin coated ammonium phosphate, modified epoxy resin coated ammonium phosphate, modified epoxy resin coated sulphate-potassium magnesium fertilizer, modified epoxy resin coated ammonium phosphate, potassium muriate complex fertilizer and the like for different coating amounts. The clivia minata specialized controlled releasing agent of the invention is one-time applied when the clivia minata is changed with the port or is replanted and the injury to the root system of the clivia minata is avoided in multi-time fertilizing, and the fertilizer has the advantages of saving labor and force, increasing the utilization efficiency of the fertilizer, stable nutrition providing and facilitating the holding of the excellent strain type of the clivia minata.
Description
Technical field
The present invention relates to a kind of modified epoxy resin integument kafir lily special-purpose control-release fertilizer and preparation method thereof, belong to slow/controlled release fertilizer technology field.
Background technology
Kafir lily is the perennial evergreen plant, is one of famous flower of China.Its both considerable leaf, also considerable flower.Blade is generous dark green, and is dignified, generous, and corolla is dazzling brilliant, liked by people.The kafir lily plant type is of moderate size, and is to support the desirable flower variety of planting at home.
Kafir lily is the meat root system, and respiration is strong, and hobby is loose, the soil of many soil ulmin, is afraid of soil ponding.Present potted plant kafir lily is many to be cultivation matrix with septic pine needle, dry branches and fallen leaves.These materials do not have adsorption to the nutrient ion, and the quick acting fertilizer of using is very fast with watering and run off, and fertilization effect is not obvious.The kafir lily happiness is fertile, but the not anti-again fertilizer of meat root system.Even application of organic fertilizers, ampoule can not be too many, because also contain more quick-acting nutrient in the fertilizer that becomes thoroughly decomposed.According to cultivation practices for many years, execute fertilizer general every month one time, but frequent shoveling fertilising very easily injures root system, is unfavorable for that kafir lily grows.Present a kind of fertilizer efficiency period length, the slow such technical barrier of fertilizer variety solution that can satisfy kafir lily absorption requirement again of nutrient release of also lacking.
Summary of the invention
At the deficiencies in the prior art, the invention provides a kind of modified epoxy resin integument kafir lily special-purpose control-release fertilizer and preparation method thereof, utilize the Nutrient Release of modified epoxy resin integument fertilizer, the law of nutritive absorption according to kafir lily carries out the composite kafir lily special-purpose control-release fertilizer that gets simultaneously.
Technical scheme of the present invention is as follows:
Kafir lily special-purpose control-release fertilizer of the present invention, feed composition is as follows, is weight part:
130～210 parts in 3% modified epoxy resin integument ammonium phosphate
140～200 parts in 5% modified epoxy resin integument ammonium phosphate
80～140 parts in 4% modified epoxy resin integument saltpetre
140～200 parts of 3% modified epoxy resin integument potassium magnesium sulfates
60～110 parts in 3% modified epoxy resin integument ammonium nitrate
40～90 parts in 4% modified epoxy resin integument ammonium nitrate
70～130 parts in 5% modified epoxy resin integument ammonium nitrate
30～80 parts in 6% modified epoxy resin integument ammonium nitrate
40～100 parts of Repone K composite fertilizers
0～6 part of chelating iron fertilizer
0～6 part in zinc sulfate.
Above-mentioned raw materials is the commercially available prod, and wherein the fertile Shandong Kingenta Bio-engineering Stock Co., Ltd. of modified epoxy resin integument produces and sells, and 3% modified epoxy resin integument ammonium phosphate is meant that the resin molding quality is 3% of a total mass, and model is KTS02 (16-43-0); 5% modified epoxy resin integument ammonium phosphate is meant that the resin molding quality is 5% of a total mass, and model is KTS04 (16-43-0); 4% modified epoxy resin integument saltpetre is meant that the resin molding quality is 4% of a total mass, and model is KTS03 (14-0-40); 3% modified epoxy resin integument potassium magnesium sulfate is meant that the resin molding quality is 3% of a total mass, and model is KTS02 (2-0-21); 3% modified epoxy resin integument ammonium nitrate is meant that the resin molding quality is 3% of a total mass, and model is KTS02 (34-0-0); 4% modified epoxy resin integument ammonium nitrate is meant that the resin molding quality is 4% of a total mass, and model is KTS03 (34-0-0); 5% modified epoxy resin integument ammonium nitrate is meant that the resin molding quality is 5% of a total mass, and model is KTS04 (34-0-0); 6% modified epoxy resin integument ammonium nitrate is meant that the resin molding quality is 6% of a total mass, and model is KTS05 (34-0-0); Numerical value in the product type bracket is the mass percentage content of N, P, K, and being that this area is conventional indicates.
Above raw material also can for example can prepare by the method for CN1569773 (200410024049.7) by prior art for preparing.
In the Repone K composite fertilizer, nitrogen, Vanadium Pentoxide in FLAKES, potassium oxide content be respectively 18%, 18%, 18% or nitrogen, Vanadium Pentoxide in FLAKES, potassium oxide content be respectively 15%, 15%, 15%; Be mass percent.
The particle diameter of above-mentioned all raw materials is good in 2～4 millimeters scopes all.
Above-mentioned chelating iron fertilizer is Dutch Akzo Nobel N.V. product, and marque " No. 2, auspicious grace " belongs to a kind of chelated microelement fertilizer, and zinc sulfate is common agricultural zinc sulfate, these two kinds of raw materials with Powdered be good.
Further preferred, the kafir lily special-purpose control-release fertilizer, feed composition is as follows, is weight part:
195～205 parts in 3% modified epoxy resin integument ammonium phosphate
145～155 parts in 5% modified epoxy resin integument ammonium phosphate
130～140 parts in 4% modified epoxy resin integument saltpetre
175～185 parts of 3% modified epoxy resin integument potassium magnesium sulfates
95～105 parts in 3% modified epoxy resin integument ammonium nitrate
45～55 parts in 4% modified epoxy resin integument ammonium nitrate
85～95 parts in 5% modified epoxy resin integument ammonium nitrate
35～45 parts in 6% modified epoxy resin integument ammonium nitrate
45～55 parts of Repone K composite fertilizers
4～6 parts of chelating iron fertilizers
4～6 parts in zinc sulfate.
The preparation method of kafir lily special-purpose control-release fertilizer of the present invention puts into stirrer with above-mentioned each raw material together by proportioning and stirred 5～10 minutes, and fully mixing promptly.Then the fertilizer that mixes is sent into metering, wrapping machine measures, packs.
The application of kafir lily special-purpose control-release fertilizer of the present invention, this fertilizer are disposable applying when kafir lily is changed basin or transplants.Preferred fertilizing method is first with fertilizer and the abundant mixing of soil, in the basin of packing into, waters sufficient water behind the kafir lily of planting again.
The technical characterstic of kafir lily special-purpose control-release fertilizer of the present invention is that the single fertile controlled release fertilizer of modified epoxy resin integument of planting that difference is discharged the period carries out composite, be equipped with part quick-acting fertilizer and trace element fertilizer again, can better accurately control nitrogen, phosphorus, potassium by kafir lily growth nutrient absorbing rule requirement release, help the good growth of kafir lily.The nutrient of modified epoxy resin integument fertilizer discharges the variation of temperature sensitivity, and temperature raises, and nutrient releasing speed is accelerated.Kafir lily is based on potted plant, and it is more obvious than field soil that the interior soil moisture of basin is influenced by temperature, and temperature raises, and the kafir lily speed of growth is accelerated, and the nutrient of absorption increases.
Excellent results of the present invention is as follows:
1. nutrient element releasing rule is consistent with the kafir lily dietetic alimentation
In 1 year, enter kafir lily growth in autumn and accelerate, at this moment be grown to the master with leaf, need more nitrogen.In winter, under the suitable condition of temperature, kafir lily begins breeding of flower.Generally speaking, be 3～April flowering period, also has bloom for 2～March.At this moment kafir lily absorbs more phosphorus element so that a type of flower is big, color and luster is gorgeous.Florescence enters summer later, the kafir lily decreased growth, and the nutrient of absorption obviously reduces.The nutrient release of special-purpose control-release fertilizer designs according to the nutritional needs rule of kafir lily just.Simultaneously, special-purpose control-release fertilizer also utilizes modified epoxy resin integument ammonium nitrate and modified epoxy resin integument potassium magnesium sulfate as material composition, added the chelating iron fertilizer, these compositions all help the intensification of the plumpness and the green color of blade, and the Rangooncreeper Fruit orchid has more ornamental value.
2. nutrient supply is stable, helps the maintenance of the good plant type of kafir lily
Growing that kafir lily is good needs stable and competent nutrient supply.Practice shows, the nutrient particularly fluctuation supplied with of nitrogen all has in various degree influence to length, thickness and the width etc. of kafir lily blade too greatly.The quick-acting chemical fertilizer is subjected to the restriction of fertilizer application frequency owing to use the back dissolving soon, is difficult to accomplish that nutrient supply is steady.Special-purpose control-release fertilizer is that their nutrient release profiles is through repeatedly stack by fertile composite the forming of single kind controlled release of multiple different release periods, and nutrition supply is steady, helps keeping the good plant type of kafir lily.
3. avoid repeatedly applying fertilizer injury to the kafir lily root system
Kafir lily is executed disposable fertilizer in autumn, winter, in three seasons of spring each moon of general requirement, and each fertilising need be pushed basin soil aside, and fertilizer is executed 2～3 centimetres depths, if careless, is easy to hurt root system.Special-purpose control-release fertilizer is to use when changing basin annual, is convenient to operation, and needn't go more later on and topdress, so can obviously reduce injury to the kafir lily root system.
4. reduce the fertile cost of controlled release, easy to utilize
The kafir lily special-purpose control-release fertilizer adopts " different grain speed change " principle, different release characteristics single is planted controlled release fertilizer carry out compositely, has both satisfied the requirement of kafir lily dietetic alimentation, has avoided again that special-purpose control-release fertilizer brought was expensive with a kind of coated fertilizer production.Studies show that this special-purpose control-release fertilizer reduces cost 1 to 3 times than import controlled release fertilizer, this just lays a good foundation for applying.
Embodiment
The present invention will be further described below in conjunction with embodiment, but be not limited thereto.
Modified epoxy resin integument fertilizer is Shandong Kingenta Bio-engineering Stock Co., Ltd. and produces and to sell among the embodiment, and product type as previously mentioned.In the Repone K composite fertilizer, nitrogen, Vanadium Pentoxide in FLAKES, potassium oxide content are respectively 18%, 18%, 18%, are mass percent.The particle diameter of above-mentioned all raw materials is all in 2～4 millimeters scopes.Above-mentioned chelating iron fertilizer is Dutch Akzo Nobel N.V. product, marque " No. 2, auspicious grace ", and zinc sulfate is common agricultural zinc sulfate, these two kinds of raw materials are Powdered, can be buied by market.
Embodiment 1: the kafir lily special-purpose control-release fertilizer, total nutrient: nitrogen, Vanadium Pentoxide in FLAKES, potassium oxide content are respectively 20%, 16%, 8% mass percents.Feed composition is as follows:
3% modified epoxy resin integument ammonium phosphate 130kg
5% modified epoxy resin integument ammonium phosphate 200kg
4% modified epoxy resin integument saltpetre 80kg
3% modified epoxy resin integument potassium magnesium sulfate 140kg
3% modified epoxy resin integument ammonium nitrate 60kg
4% modified epoxy resin integument ammonium nitrate 75kg
5% modified epoxy resin integument ammonium nitrate 125kg
6% modified epoxy resin integument ammonium nitrate 80kg
Repone K composite fertilizer 100kg
Chelating iron fertilizer 5kg
Zinc sulfate 5kg.
The preparation method puts into stirrer with above-mentioned each raw material together by proportioning and stirred 5～10 minutes, and fully mixing promptly.
Embodiment 2: the kafir lily special-purpose control-release fertilizer, total nutrient: nitrogen, Vanadium Pentoxide in FLAKES, potassium oxide content are respectively 18%, 17%, 9% mass percents.Feed composition is as follows:
3% modified epoxy resin integument ammonium phosphate 200kg
5% modified epoxy resin integument ammonium phosphate 150kg
4% modified epoxy resin integument saltpetre 80kg
3% modified epoxy resin integument potassium magnesium sulfate 180kg
3% modified epoxy resin integument ammonium nitrate 100kg
4% modified epoxy resin integument ammonium nitrate 50kg
5% modified epoxy resin integument ammonium nitrate 90kg
6% modified epoxy resin integument ammonium nitrate 40kg
Repone K composite fertilizer 100kg
Chelating iron fertilizer 5kg
Zinc sulfate 5kg.
Embodiment 3: the kafir lily special-purpose control-release fertilizer, total nutrient: nitrogen, Vanadium Pentoxide in FLAKES, potassium oxide content are respectively 18%, 16%, 10% mass percents.Feed composition is as follows:
3% modified epoxy resin integument ammonium phosphate 200kg
5% modified epoxy resin integument ammonium phosphate 150kg
4% modified epoxy resin integument saltpetre 135kg
3% modified epoxy resin integument potassium magnesium sulfate 180kg
3% modified epoxy resin integument ammonium nitrate 100kg
4% modified epoxy resin integument ammonium nitrate 50kg
5% modified epoxy resin integument ammonium nitrate 90kg
6% modified epoxy resin integument ammonium nitrate 40kg
Repone K composite fertilizer 50kg
Zinc sulfate 5kg.
Embodiment 4: the kafir lily special-purpose control-release fertilizer, total nutrient: nitrogen, Vanadium Pentoxide in FLAKES, potassium oxide content are respectively 18%, 15%, 10% mass percents.Feed composition is as follows:
3% modified epoxy resin integument ammonium phosphate 170kg
5% modified epoxy resin integument ammonium phosphate 140kg
4% modified epoxy resin integument saltpetre 100kg
3% modified epoxy resin integument potassium magnesium sulfate 200kg
3% modified epoxy resin integument ammonium nitrate 80kg
4% modified epoxy resin integument ammonium nitrate 90kg
5% modified epoxy resin integument ammonium nitrate 75kg
6% modified epoxy resin integument ammonium nitrate 50kg
Repone K composite fertilizer 90kg
Chelating iron fertilizer 5kg.
Comparative Examples: common Repone K composite fertilizer (total nutrient content 45%)
The effect of above embodiment 1～4 and Comparative Examples is as follows:
For examination kafir lily kind is that Japan is blue, and cultivation matrix is septic willow leaf, and planting type is potted plant, and basin alms bowl volume is 30 centimetres of 25 centimetres of (internal diameter) * (highly).Select kafir lily seedling of the same size.Restrain Repone K composite fertilizers by every basin 8 in the Comparative Examples, plant 8 basins altogether; The fertilizer amount of special-purpose control-release fertilizer is every basin 7 grams, and each embodiment plants 10 basins.Whole kafir lily special-purpose control-release fertilizers are once to apply before planting among the embodiment; 20% of Repone K composite fertilizer is to apply before planting in the Comparative Examples, and fertilizing method is identical with special-purpose control-release fertilizer, promptly earlier with fertilizer and the abundant mixing of cultivation matrix, in the basin of packing into, waters sufficient water behind the kafir lily of planting again.Remaining fertilizer divides and whenever asks every 1 month and use once that each consumption is identical for 6 times in the Comparative Examples.Fertilizing method is to push a circle basin soil aside apart from kafir lily 6～7 centimeters, and fertilizer is executed depths at 2～3 centimetres.This test was done 2 years continuously.
| Biomass increases) (%) | Utilization rate of nitrogen fertilizer improves (%) | Estimate | |
| Embodiment 1 | 9.3 | 12.9 | The blade plumpness, plant type is better, and saving of labor, laborsaving can promote. |
| Embodiment 2 | 11.5 | 13.4 | The blade plumpness, plant type is better, and the leaf look dark green, and saving of labor, laborsaving is worthy to be popularized. |
| Embodiment 3 | 14.6 | 18.5 | The blade plumpness, plant type is better, and the leaf look dark green, and saving of labor, laborsaving is worthy to be popularized. |
| Embodiment 4 | 8.4 | 13.1 | Blade is plump, and the leaf look better, and saving of labor, laborsaving can promote. |
| Comparative Examples | - | - | Fertilizer application frequency is many, and the effort of taking a lot of work should not be promoted. |
Claims (6)
1. the kafir lily special-purpose control-release fertilizer is characterized in that feed composition is as follows, is weight part:
130～210 parts in 3% modified epoxy resin integument ammonium phosphate
140～200 parts in 5% modified epoxy resin integument ammonium phosphate
80～140 parts in 4% modified epoxy resin integument saltpetre
140～200 parts of 3% modified epoxy resin integument potassium magnesium sulfates
60～110 parts in 3% modified epoxy resin integument ammonium nitrate
40～90 parts in 4% modified epoxy resin integument ammonium nitrate
70～130 parts in 5% modified epoxy resin integument ammonium nitrate
30～80 parts in 6% modified epoxy resin integument ammonium nitrate
40～100 parts of Repone K composite fertilizers
0～6 part of chelating iron fertilizer
0～6 part in zinc sulfate.
2. kafir lily special-purpose control-release fertilizer as claimed in claim 1 is characterized in that, the particle diameter of all raw materials is all at 2～4 millimeters.
3. kafir lily special-purpose control-release fertilizer as claimed in claim 1 is characterized in that feed composition is as follows, is weight part:
195～205 parts in 3% modified epoxy resin integument ammonium phosphate
145～155 parts in 5% modified epoxy resin integument ammonium phosphate
130～140 parts in 4% modified epoxy resin integument saltpetre
175～185 parts of 3% modified epoxy resin integument potassium magnesium sulfates
95～105 parts in 3% modified epoxy resin integument ammonium nitrate
45～55 parts in 4% modified epoxy resin integument ammonium nitrate
85～95 parts in 5% modified epoxy resin integument ammonium nitrate
35～45 parts in 6% modified epoxy resin integument ammonium nitrate
45～55 parts of Repone K composite fertilizers
4～6 parts of chelating iron fertilizers
4～6 parts in zinc sulfate.
4. the preparation method of the described kafir lily special-purpose control-release fertilizer of claim 1 puts into stirrer with described each raw material together by proportioning and stirred 5～10 minutes, and fully mixing promptly.
5. the application of the described kafir lily special-purpose control-release fertilizer of claim 1, this fertilizer are disposable applying when kafir lily is changed basin or transplants.
6. the application of kafir lily special-purpose control-release fertilizer as claimed in claim 5 is characterized in that, fertilizing method is first with fertilizer and the abundant mixing of soil, in the basin of packing into, waters sufficient water behind the kafir lily of planting again.