CN101225262B - 涂料油墨用氟碳化合物改性聚丙烯酸酯流平剂及生产方法 - Google Patents
涂料油墨用氟碳化合物改性聚丙烯酸酯流平剂及生产方法 Download PDFInfo
- Publication number
- CN101225262B CN101225262B CN2008100205059A CN200810020505A CN101225262B CN 101225262 B CN101225262 B CN 101225262B CN 2008100205059 A CN2008100205059 A CN 2008100205059A CN 200810020505 A CN200810020505 A CN 200810020505A CN 101225262 B CN101225262 B CN 101225262B
- Authority
- CN
- China
- Prior art keywords
- flow agent
- modified polyacrylate
- compound modified
- fluorocarbon compound
- polyacrylate flow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种涂料油墨用氟碳化合物改性聚丙烯酸酯流平剂及生产方法，由丙烯酸酯单体、引发剂、丙烯酸氟单体、二甲苯、甲苯、丙二醇甲醚反应制成。本发明原料易得、生产成本低、生产方法简便。并具有使用方便，增加涂料油墨表面光泽等优点。
Description
技术领域：
本发明涉及一种涂料油墨用流平剂及生产方法。
背景技术：
现有的涂料油墨用流平剂，原料复杂，成本高，生产工艺复杂，工作效果不理想。
发明内容：
本发明的目的在于提供一种原料易得、生产成本低、生产方法简便的涂料油墨用氟碳化合物改性聚丙烯酸酯流平剂及生产方法。
本发明的技术解决方案是：
一种涂料油墨用氟碳化合物改性聚丙烯酸酯流平剂，其特征是：由下列重量百分比的原料反应制成：
丙稀酸酯单体 30～70％
引发剂 1～10％
丙稀酸氟单体 1～20％
二甲苯 1～10％
甲苯 1～10％
丙二醇甲醚 1～20％。
丙稀酸酯单体是甲基丙烯酸甲酯或丙稀酸丁酯。
丙稀酸氟单体是丙稀酸全氟烷基酯、丙稀酸十九氟庚酯、甲基丙烯酸十二氟庚酯或丙烯酸六氟丁酯。引发剂是过氧化二苯甲醚或偶氮二异丁腈等。
一种涂料油墨用氟碳化合物改性聚丙烯酸酯流平剂的生产方法，其特征是：包括下列步骤：
(1)将二甲苯、甲苯、丙二醇甲醚放入反应釜内，升温至80～120℃；
(2)将丙稀酸酯单体、引发剂、丙稀酸氟单体1～20％在80～150℃下，3～5小时内加入上述反应釜中，80～150℃下保温2～5小时。
步骤(2)后还补加入二甲苯、甲苯、丙二醇甲醚及引发剂，80～150℃下保温2～5小时。
本发明原料易得、生产成本低、生产方法简便。并具有使用方便，增加涂料油墨表面光泽等优点。
具体实施方式：
下面结合实施例对本发明作进一步说明。
具体实施方式：
实施例1：
(1)将二甲苯1～10％(例1％、5％、10％)、甲苯1～10％(例1％、5％、10％)、丙二醇甲醚1～20％(例1％、19％、20％)放入反应釜内，升温至80～120℃(例80℃、100℃、120℃)；
(2)将丙稀酸酯单体30～70％(例30％、50％、70％)、引发剂过氧化二苯甲醚(或偶氮二异丁腈)1～10％(例1％、5％、10％)、丙稀酸氟单体1～20％(例1％、10％、20％)在80～150℃(例80℃、110℃、150℃)下，3～5小时内加入上述反应釜中，80～150℃(例80℃、110℃、150℃)下保温2～5小时，得产品。
上述用量百分比均为重量百分比。
其中丙稀酸酯单体是甲基丙烯酸甲酯(或丙稀酸丁酯等)。丙稀酸氟单体是丙稀酸全氟烷基酯(或丙稀酸十九氟庚酯、甲基丙烯酸十二氟庚酯、丙烯酸六氟丁酯等)。
实施例2：
(1)将二甲苯、甲苯、丙二醇甲醚放入反应釜内，升温至80～120℃(例80℃、100℃、120℃)；
(2)将丙稀酸酯单体30～70％(例30％、50％、70％)、引发剂过氧化二苯甲醚(或偶氮二异丁腈)、丙稀酸氟单体1～20％(例1％、10％、20％)在80～150℃(例80℃、110℃、150℃)下，3～5小时内加入上述反应釜中，80～150℃(例80℃、110℃、150℃)下保温2～5小时，得产品。
然后再补加入二甲苯至1～10％(例1％、5％、10％)、甲苯至1～10％(例1％、5％、10％)、丙二醇甲醚至1～20％(例1％、19％、20％)及引发剂过氧化二苯甲醚(或偶氮二异丁腈)至1～10％(例1％、5％、10％)，80～150℃下保温2～5小时。
上述用量百分比均为重量百分比。
其中丙稀酸酯单体是甲基丙烯酸甲酯(或丙稀酸丁酯等)。丙稀酸氟单体是丙稀酸全氟烷基酯(或丙稀酸十九氟庚酯、甲基丙烯酸十二氟庚酯、丙烯酸六氟丁酯等)。
Claims (4)
1.一种涂料油墨用氟碳化合物改性聚丙烯酸酯流平剂，其特征是：由下列重量百分比的原料反应制成：
丙烯酸酯单体 30～70％
引发剂 1～10％
丙烯酸氟单体 1～20％
二甲苯 1～10％
甲苯 1～10％
丙二醇甲醚 1～20％；
丙烯酸氟单体是丙烯酸全氟烷基酯、丙烯酸十九氟庚酯或丙烯酸六氟丁酯。
2.根据权利要求1所述的涂料油墨用氟碳化合物改性聚丙烯酸酯流平剂，其特征是：丙烯酸酯单体是甲基丙烯酸甲酯或丙烯酸丁酯。
3.一种权利要求1所述的涂料油墨用氟碳化合物改性聚丙烯酸酯流平剂的生产方法，其特征是：包括下列步骤：
(1)将二甲苯、甲苯、丙二醇甲醚放入反应釜内，升温至80～120℃；
(2)将丙烯酸酯单体、引发剂、丙烯酸氟单体在80～150℃下，3～5小时内加入上述反应釜中，80～150℃下保温2～5小时。
4.根据权利要求3所述的涂料油墨用氟碳化合物改性聚丙烯酸酯流平剂的生产方法，其特征是：步骤(2)后还补加入二甲苯、甲苯、丙二醇甲醚及引发剂，80～150℃下保温2～5小时。