CN102241910A - 溶剂型涂料油墨用具有流平功能的超分散剂及制备方法 - Google Patents
溶剂型涂料油墨用具有流平功能的超分散剂及制备方法 Download PDFInfo
- Publication number
- CN102241910A CN102241910A CN2011101366736A CN201110136673A CN102241910A CN 102241910 A CN102241910 A CN 102241910A CN 2011101366736 A CN2011101366736 A CN 2011101366736A CN 201110136673 A CN201110136673 A CN 201110136673A CN 102241910 A CN102241910 A CN 102241910A
- Authority
- CN
- China
- Prior art keywords
- solvent
- hyper
- dispersant
- weight percent
- based coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种溶剂型涂料油墨用具有流平功能的超分散剂及制备方法,由丙烯酸酯单体、引发剂、含氟单体、溶剂、胺组成。本发明生产的产品既有分散作用又有流平作用。
Description
技术领域
本发明涉及一种溶剂型涂料油墨用具有流平功能的超分散剂及生产方法。
背景技术
在涂料油墨生产中,一般的分散剂只具有分散作用,没有流平作用。
发明内容:
本发明的目的在于提供一种既有分散作用又有流平作用的溶剂型涂料油墨用具有流平功能的超分散剂及制备方法。
本发明的技术解决方案是:
一种溶剂型涂料油墨用具有流平功能的超分散剂,其特征是:由下列重量百分比的原料制成:
所述丙烯酸酯单体为丙烯酸甲酯、甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸异辛酯或丙烯酸丁酯。
引发剂为偶氮二异丁腈或过氧化苯甲酰。
含氟单体为丙烯酸三氟乙酯、甲基丙烯酸十二氟庚酯、丙烯酸六氟丁酯或丙烯酸十二氟庚酯。
溶剂为二甲苯、醋酸丁酯或丙二醇甲醚醋酸酯。
胺为二甲基氨基丙胺、三乙烯四胺或二乙二醇胺。
一种溶剂型涂料油墨用具有流平功能的超分散剂的制备方法,其特征是:首先将1-15%重量百分比的溶剂倒入反应釜内,升温至80-145℃;同时将10-40%重量百分比的丙烯酸酯单体、0.08-0.90%重量百分比的引发剂、15-50%重量百分比的含氟单体混合,在80-145℃的温度下,3-5小时内加入到反应釜内,进行聚合反应,保温2-3小时;补加0.3-5%重量百分比的溶剂和0.01-0.05%重量百分比的引发剂;保温2-3小时;加入剩余的引发剂和0.5~25%重量百分比的溶剂;保温1~2小时;最后加入剩余的溶剂和5-10%胺;保温1~2小时,冷却后得产品。
本发明生产的产品既有分散作用又有流平作用。试验数据:
一、分散实验对比资料
1、配方
组成 | 1# | 2# | 3# | 4# | 5# | 6# |
丙烯酸树脂 | 65 | 65 | 65 | 65 | 65 | 65 |
碳黑C311 | 6 | 6 | 6 | 6 | 6 | 6 |
分散剂1 | 3 | |||||
分散剂2 | 3 | |||||
分散剂3 | 3 | |||||
分散剂4 | 3 | |||||
分散剂5 | 3 | |||||
本发明产品 | 3 | |||||
混合溶剂 | 26 | 26 | 26 | 26 | 26 | 26 |
合计 | 100 | 100 | 100 | 100 | 100 | 100 |
注:①混合溶剂的配比:
二甲苯∶醋酸丁酯∶PMA=2∶1∶1
2、测细度按GB/T1724-79(89)中规定执行
时间 | 1 | 2 | 3 | 3 | 4 | 5 |
30分钟 | 13 | 15 | 15 | 13 | 15 | 12 |
1小时 | 11 | 13 | 14 | 11 | 14 | 10 |
2小时 | 10 | 12 | 11 | 10 | 12 | 9 |
3小时 | 10 | 10 | 10 | 9 | 10 | 8 |
二、无分散助剂、普通分散剂和含氟类分散剂桔皮仪测试数据(表1:采集数据统计表;图1:采集数据曲线图)
表1:
图1说明本发明含氟类分散剂具有很好的长波流平性。
下面结合附图和实施例对本发明作进一步说明。
图1是本发明桔皮仪测试数据图。
图中1为无助剂时的曲线,2为普通分散剂曲线,3为本发明产品曲线。
具体实施方式
一种溶剂型涂料油墨用具有流平功能的超分散剂的制备方法,其特征是:首先将1-15%(例1%、8%、15%)重量百分比的溶剂倒入反应釜内,升温至80-145℃(例80℃、120℃、145℃);同时将10-40%重量百分比的丙烯酸酯单体、0.08-0.90%(例0.08%、0.5%、0.9%)重量百分比的引发剂、15-50%(例15%、25%、50%)重量百分比的含氟单体混合,在80-145℃(例80℃、120℃、145℃)的温度下,3-5小时内加入到反应釜内,进行聚合反应,保温2-3小时;补加0.3-5%(例0.3%、3%、5%)重量百分比的溶剂和0.01-0.05%(例0.01%、0.03%、0.05%)重量百分比的引发剂;保温2-3小时;加入剩余的引发剂和0.5~25%(例0.5%、15%、25%)重量百分比的溶剂;保温1~2小时;最后加入剩余的溶剂和5-10%(例5%、7%、10%)重量百分比的胺;保温1~2小时,冷却后得产品。
所得产品为溶剂型涂料油墨用具有流平功能的超分散剂,由下列重量百分比的原料制成:
上述各组分用量之和为100%。
所述丙烯酸酯单体为丙烯酸甲酯(或甲基丙烯酸甲酯或丙烯酸乙酯或丙烯酸异辛酯或丙烯酸丁酯)。
引发剂为偶氮二异丁腈或过氧化苯甲酰。
含氟单体为丙烯酸三氟乙酯(或甲基丙烯酸十二氟庚酯或丙烯酸六氟丁酯或丙烯酸十二氟庚酯)。
溶剂为二甲苯(或醋酸丁酯或丙二醇甲醚醋酸酯)。
胺为二甲基氨基丙胺(或三乙烯四胺或二乙二醇胺)。
Claims (7)
1. 一种溶剂型涂料油墨用具有流平功能的超分散剂,其特征是:由下列重量百分比的原料制成:
丙烯酸酯单体 10~40%
引发剂 0.1~1%
含氟单体 15~50%
溶剂 1~50%
胺 5-10%。
2. 根据权利要求1所述的溶剂型涂料油墨用具有流平功能的超分散剂,其特征是:所述丙烯酸酯单体为丙烯酸甲酯、甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸异辛酯或丙烯酸丁酯。
3. 根据权利要求1或2所述的溶剂型涂料油墨用具有流平功能的超分散剂,其特征是:引发剂为偶氮二异丁腈或过氧化苯甲酰。
4. 根据权利要求1或2所述的溶剂型涂料油墨用具有流平功能的超分散剂,其特征是:含氟单体为丙烯酸三氟乙酯、甲基丙烯酸十二氟庚酯、丙烯酸六氟丁酯或丙烯酸十二氟庚酯。
5. 根据权利要求1或2所述的溶剂型涂料油墨用具有流平功能的超分散剂,其特征是:溶剂为二甲苯、醋酸丁酯或丙二醇甲醚醋酸酯。
6. 根据权利要求1或2所述的溶剂型涂料油墨用具有流平功能的超分散剂,其特征是:胺为二甲基氨基丙胺、三乙烯四胺或二乙二醇胺。
7. 一种权利要求1所述的溶剂型涂料油墨用具有流平功能的超分散剂的制备方法,其特征是:首先将1-15%重量百分比的溶剂倒入反应釜内,升温至80-145℃;同时将10-40%重量百分比的丙烯酸酯单体、0.08-0.90%重量百分比的引发剂、15-50%重量百分比的含氟单体混合,在80-145℃的温度下,3-5小时内加入到反应釜内,进行聚合反应,保温2-3小时;补加0.3-5%重量百分比的溶剂和0.01-0.05%重量百分比的引发剂;保温2-3小时;加入剩余的引发剂和0.5~25%重量百分比的溶剂;保温1~2小时;最后加入剩余的溶剂和5-10%胺;保温1~2小时,冷却后得产品。