CN101220241B - 一种双组份高强度聚氨酯防水涂料 - Google Patents

一种双组份高强度聚氨酯防水涂料 Download PDF

Info

Publication number
CN101220241B
CN101220241B CN2007101725643A CN200710172564A CN101220241B CN 101220241 B CN101220241 B CN 101220241B CN 2007101725643 A CN2007101725643 A CN 2007101725643A CN 200710172564 A CN200710172564 A CN 200710172564A CN 101220241 B CN101220241 B CN 101220241B
Authority
CN
China
Prior art keywords
agent
parts
polyether glycol
double
coating material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2007101725643A
Other languages
English (en)
Other versions
CN101220241A (zh
Inventor
程雪峰
何家旭
程业武
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Beixin Yuehuang New Material Group Co ltd
Original Assignee
SHANGHAI TAI'AN ENGINEERING INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI TAI'AN ENGINEERING INDUSTRY Co Ltd filed Critical SHANGHAI TAI'AN ENGINEERING INDUSTRY Co Ltd
Priority to CN2007101725643A priority Critical patent/CN101220241B/zh
Publication of CN101220241A publication Critical patent/CN101220241A/zh
Application granted granted Critical
Publication of CN101220241B publication Critical patent/CN101220241B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种双组份高强度聚氨酯防水涂料,由主剂A和固化剂B两个组份组成,主剂A的配方为:聚醚多元醇30-35份、硫化促进剂20-22份、稀释剂38-40份、补强4-5份、消泡剂0.3-0.5份;固化剂B的配方为:聚醚多元醇58-63份、增塑剂8-10份、二苯基甲烷二异氰酸酯(MDI)30-35份。由于主剂A和固化剂B中都包含有内含活泼氢的聚醚多元醇,可与固化剂B组份中的-NCO基起化学反应,交联成的涂膜的强度、耐磨性都优于现有技术中的用TDI制备的涂料,涂膜拉伸强度≥15MPa、伸长率≥500%,特别适于长期工作于振动环境中的建筑物墙面上使用。

Description

一种双组份高强度聚氨酯防水涂料
技术领域
本发明涉及化工涂料技术领域,特别是一种能适应基层一定形变和承受一定压力、粘贴性能优良、一般情况下不会发生从基层上自动剥离、防水性能可靠和耐老化性突出的双组份高强度聚氨酯防水涂料。
背景技术
目前市场上销售的防水涂料基本上均按国家II型防水涂料标准生产,当用于无振动性干扰环境中的建筑物上时具有良好的防水效果和较长的工作寿命,但如果用于车辆往来频繁、且伴随着比较剧烈振动影响环境中的铁道、隧道、桥梁、高速公路之类及其附属建筑物上时,很容易发生涂膜开裂和剥离的情况,实际有效工作寿命很短。事实证明,对于长期处于振动环境中建筑物上所用的防水涂料有其独特的苛刻要求。经大量试验证明,可以胜任这类建筑物上使用的防水涂料,其涂膜拉伸强度至少应当大于15MPa、伸长率至少应当大于500%。这种高强度要求的涂料的开发和研制的难度较大、成本较高,目前国内尚处研制阶段。
发明内容
本发明的目的是要提供一种拉伸强度等于或大于15MPa、伸长率等于或大于500%、适宜长期工作于振动环境中建筑物上使用的双组份高强度聚氨酯防水涂料。
本发明的双组份高强度聚氨酯防水涂料由主剂A和固化剂B两个组份组成,其中:
主剂A的配方(以100份为重量配制单位)如下:
聚醚多元醇    30-35份
硫化促进剂    20-22份
稀释剂        38-40份
补强剂        4-5份
消泡剂        0.3-0.5份
固化剂B的配方(以100份为重量配制单位)如下:
聚醚多元醇                    58-63份
增塑剂                        8-10份
二苯基甲烷二异氰酸酯(MDI)     30-35份
生产工艺如下:
主剂A:先将聚醚多元醇加热至120℃搅拌脱水,然后加入硫化促进剂,使之充分溶解,再降温至20-30℃,加入稀释剂、补强剂和消泡剂,最后高速分散或研磨出料。
固化剂B:先将聚醚多元醇和增塑剂加热至120℃搅拌脱水,然后降至室温,再加入二苯基甲烷二异氰酸酯(MDI)自然反应半小时,再升温至75-85℃,于恒温状态下搅拌2-3小时,最后降温30℃出料。
其中:A组中硫化促进剂是促进双组份涂料混合后的反应,使A组中的羟基与B组份的异氰酸基充分交联固化、反应完全,使反应后的涂膜无残留、无污染,提高延伸率;补强剂是采用法国翰尔公司悬浮法提取的补强超细白碳黑,以提高产品的最终反应强度;稀释剂主要是参与体系反应,降低涂料粘度,提高施工性能等作用而不影响使用效果;所述的消泡剂主要作用是消除搅拌和施工过程中所产生的机械气泡以及双组份混合反应过程中产生CO2所带来的气泡,以增强产品的防水性能,提高产品的拉伸强度和伸长率,可以按照涂料的粘度选择使用,例如日本的P-420型消泡剂适用于高粘度涂料,韩国的AC-301型消泡剂适用于低粘度涂料。此外,对于用于建筑物外墙上的涂料,还可在A组份中加入各种颜料和适量具有防止产品老化和抗紫外线功能的抗氧剂和防老剂,以使涂膜保持长期的鲜艳色彩而不因阳光的照射而老化。
B组份中的增塑剂,具有贮存稳定、相溶性好和明显增塑作用,以增加聚合物的柔韧性和耐冲击性。
施工前按主剂A和固化剂B1∶1的重量配比混合、充分搅拌均匀即可使用。
使用时,可按施工时的要求厚度及施工面积按需备料配制,通常按厚度要求为1mm的涂层,每平方米为1.2kg的总用量备料,在加料混合过程中宜高速分散、搅拌均匀,可以刮涂或喷涂的方法施涂。
基于上述构思的本发明双组份高强度聚氨酯防水涂料,由于主剂A和固化剂B中都包含有内含活泼氢的聚醚多元醇,可与固化剂B组份中的-NCO基起化学反应,交联成膜,对涂膜性能起关键作用;固化剂中的二苯基甲烷二异氰酸酯,简称MDI,是生产聚氨酯预聚体的主要原料,具有挥发性小,蒸气压低,对人体毒性小的特点,是一种极其重要的异氰酸酯单体,由二苯基甲烷二异氰酸酯(MDI)制备的聚氨酯涂料,其强度、耐磨性都优于现有技术中的用TDI制备的涂料;此外,为了使产品得到最佳的技术效果和性能,添加了多种助剂,以达到相应的目的。所以,本发明的双组份高强度聚氨酯防水涂料能确保其涂膜达到拉伸强度≥15MPa、伸长率≥500%,固化时间可以按需调节控制,表干≤2小时,实干≤4小时。由于其涂膜的拉伸强度和伸长率均高,即使在长期工作于振动环境中的建筑物表面上使用,也可确保涂膜不会轻易开裂、不会自动剥离和正常情况下可有与建筑物相同寿命的防水效果。

Claims (3)

1.一种双组份高强度聚氨酯防水涂料,由主剂A和固化剂B两个组份组成,其特征在于:
a.主剂A的配方(以100份为重量配制单位)如下:
聚醚多元醇        30-35份
硫化促进剂        20-22份
稀释剂            38-40份
补强剂            4-5份
消泡剂            0.3-0.5份
固化剂B的配方(以100份为重量配制单位)如下:
聚醚多元醇                   58-63份
增塑剂                       8-10份
二苯基甲烷二异氰酸酯(MDI)    30-35份
b.生产工艺如下:
主剂A:先将聚醚多元醇加热120℃搅拌脱水,然后加入硫化促进剂,使之充分溶解,再降温至20-30℃,加入稀释剂、补强剂和消泡剂,最后高速分散或研磨出料;
固化剂B:先将聚醚多元醇和增塑剂加热至120℃搅拌脱水,然后降至室温,再加入二苯基甲烷二异氰酸酯(MDI)自然反应半小时,再升温至75-85℃,于恒温状态下搅拌2-3小时,最后降温至30℃出料;
c.主剂A和固化剂B使用时的重量配比:1∶1;
d.固化时间按需调节控制:表干≤2小时、实干≤24小时;
e.涂膜能达到的技术指标:拉伸强度≥15MPa、伸长率≥500%。
2.根据权利要求1所述的双组份高强度聚氨酯防水涂料,其特征在于所述的消泡剂按照涂料的粘度要求优选适用于高粘度涂料的日本P-420型消泡剂和适用于低粘度涂料的韩国AC-301型消泡剂。
3.根据权利要求1所述的双组份高强度聚氨酯防水涂料,其特征在于所述的补强剂优选法国翰尔公司悬浮法提取的补强超细白碳黑。
CN2007101725643A 2007-12-19 2007-12-19 一种双组份高强度聚氨酯防水涂料 Active CN101220241B (zh)