CN101215087B - 一种防红外线玻璃的制作方法 - Google Patents

一种防红外线玻璃的制作方法 Download PDF

Info

Publication number
CN101215087B
CN101215087B CN2008100100112A CN200810010011A CN101215087B CN 101215087 B CN101215087 B CN 101215087B CN 2008100100112 A CN2008100100112 A CN 2008100100112A CN 200810010011 A CN200810010011 A CN 200810010011A CN 101215087 B CN101215087 B CN 101215087B
Authority
CN
China
Prior art keywords
oxide
calcium
plumbous
chromic
glass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008100100112A
Other languages
English (en)
Other versions
CN101215087A (zh
Inventor
陈默
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenyang Jianzhu University
Original Assignee
Shenyang Jianzhu University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang Jianzhu University filed Critical Shenyang Jianzhu University
Priority to CN2008100100112A priority Critical patent/CN101215087B/zh
Publication of CN101215087A publication Critical patent/CN101215087A/zh
Application granted granted Critical
Publication of CN101215087B publication Critical patent/CN101215087B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种防红外线玻璃的制作方法，涉及一种光学玻璃的制作方法，该制作方法包括如下步骤：(1)分别称取氧化硅、氧化钙、氧化铝、氧化铬和氧化铅，其质量比为氧化硅∶氧化钙∶氧化铝∶氧化铬∶氧化铅＝1∶0.05∶0.74∶0.11～0.15∶0.05～0.20；(2)将氧化硅和氧化钙的混合物加热至完全熔化，在熔融物中依次加入氧化铝、氧化铬、氧化铅，加温至全部物料完全熔化；(3)将熔融的物料倒入指定形状的容器或用浮法对物料进行降温；(4)将降温后已固化成型的物料表面的白色析出物打磨剔除，即可得到防红外线玻璃。该方法生产工艺简单，原料易得，成本低廉。生产的玻璃可有效防止红外线通过。

Description

一种防红外线玻璃的制作方法
技术领域
本发明涉及一种光学玻璃的制作方法，特别是涉及一种防红外线光学玻璃的制作方法。
背景技术
紫外线与红外线是诱发人眼白内障的主要诱因，强烈的阳光或者特殊的生产环境中都存在着高强度的紫外线、红外线。目前，人们采用在玻璃表面镀膜的方法隔断防紫外线，但这种方法对红外线的防护作用很微弱，并且影响玻璃的强度，防紫外线性较差，通光率较低。
发明内容
本发明的目的在于克服现有普通玻璃和镀膜玻璃不能有效防止红外线的缺点，通过试验改进，提供一种以氧化硅、氧化铝、氧化铬和氧化铅为主要原料，氧化钙为添加剂的光学玻璃，该方法采用普通光学玻璃的生产方法生产，生产的光学玻璃可有效防止红外线的通过，同时还不影响玻璃的强度、防紫外线性和通光率。
本发明的目的是通过以下技术方案实现的：
一种防红外线玻璃的制作方法，该制作方法包括如下步骤：
(1)分别称取氧化硅、氧化钙、氧化铝、氧化铬和氧化铅，其质量比为氧化硅∶氧化钙∶氧化铝∶氧化铬∶氧化铅＝1∶0.05∶0.74∶0.11～0.15∶0.05～0.20；
(2)将氧化硅和氧化钙的混合物加热至完全熔化，在熔融物中依次加入氧化铝、氧化铬、氧化铅，加温至全部物料完全熔化；
(3)将熔融的物料倒入指定形状的容器或用浮法对物料进行降温；
(4)将降温后已固化成型的物料表面的白色析出物打磨剔除，即可得到防红外线玻璃。
如上所述的一种防红外线玻璃的制作方法，所述的氧化硅、氧化钙、氧化铝、氧化铬、氧化铅均为工业纯粉末原料。
本发明的优点与效果是：
1.本发明以氧化硅、氧化铝、氧化铬和氧化铅为主要原料，以氧化钙为添加剂，可有效防止红外线通过。
2.本发明采用普通光学玻璃的生产方法生产，其生产工艺简单，原料易得，成本低廉。
具体实施方式
实施例1
分别称取氧化硅、氧化钙、氧化铝、氧化铬和氧化铅，其质量比为氧化硅∶氧化钙∶氧化铝∶氧化铬∶氧化铅＝1∶0.05∶0.74∶0.11∶0.05，将氧化硅和氧化钙的混合物加热至完全熔化，在熔融物中依次加入氧化铝、氧化铬、氧化铅，加温至全部物料完全熔化。将熔融的物料倒入指定形状的容器或用浮法对物料进行降温。将降温后已固化成型的物料表面的白色析出物打磨剔除，即可得到红外线通过率在5％的防红外线玻璃。
实施例2
分别称取氧化硅、氧化钙、氧化铝、氧化铬和氧化铅，其质量比为氧化硅∶氧化钙∶氧化铝∶氧化铬∶氧化铅＝1∶0.05∶0.74∶0.15∶0.20，将氧化硅和氧化钙的混合物加热至完全熔化，在熔融物中依次加入氧化铝、氧化铬、氧化铅，加温至全部物料完全熔化。将熔融的物料倒入指定形状的容器或用浮法对物料进行降温。将降温后已固化成型的物料表面的白色析出物打磨剔除，即可得到红外线通过率在7％的防红外线玻璃。
实施例3
分别称取氧化硅、氧化钙、氧化铝、氧化铬和氧化铅，其质量比为氧化硅∶氧化钙∶氧化铝∶氧化铬∶氧化铅＝1∶0.05∶0.74∶0.125∶0.125，将氧化硅和氧化钙的混合物加热至完全熔化，在熔融物中依次加入氧化铝、氧化铬、氧化铅，加温至全部物料完全熔化。将熔融的物料倒入指定形状的容器或用浮法对物料进行降温。将降温后已固化成型的物料表面的白色析出物打磨剔除，即可得到红外线通过率在3％的防红外线玻璃。

Claims (2)

1.一种防红外线玻璃的制作方法，其特征在于，该制作方法包括如下步骤：
(1)分别称取氧化硅、氧化钙、氧化铝、氧化铬和氧化铅，其质量比为氧化硅∶氧化钙∶氧化铝∶氧化铬∶氧化铅＝1∶0.05∶0.74∶0.11～0.15∶0.05～0.20；
(2)将氧化硅和氧化钙的混合物加热至完全熔化，在熔融物中依次加入氧化铝、氧化铬、氧化铅，加温至全部物料完全熔化；
(3)将熔融的物料倒入指定形状的容器或用浮法对物料进行降温；
(4)将降温后已固化成型的物料表面的白色析出物打磨剔除，即可得到防红外线玻璃。
2.根据权利要求1所述的一种防红外线玻璃的制作方法，其特征在于，所述的氧化硅、氧化钙、氧化铝、氧化铬、氧化铅均为工业纯粉末原料。
CN2008100100112A 2008-01-02 2008-01-02 一种防红外线玻璃的制作方法 Expired - Fee Related CN101215087B (zh)