CN101191244A - 碱性锌酸盐镀锌添加剂生产工艺 - Google Patents
碱性锌酸盐镀锌添加剂生产工艺 Download PDFInfo
- Publication number
- CN101191244A CN101191244A CN 200610129547 CN200610129547A CN101191244A CN 101191244 A CN101191244 A CN 101191244A CN 200610129547 CN200610129547 CN 200610129547 CN 200610129547 A CN200610129547 A CN 200610129547A CN 101191244 A CN101191244 A CN 101191244A
- Authority
- CN
- China
- Prior art keywords
- technique
- producing alkaline
- alkaline zincate
- gram
- mixed liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种碱性锌酸盐镀锌添加剂生产工艺，取乙二胺加2－硫醇基间(二)氮茚，在混合液中，加入12％的甲醛水溶液搅拌加热，滴入环氧氯丙烷，搅拌待反应完全后，回流。本发明具有以下优点：简化镀液成分，便于镀液调控降低成本，适于低铬钝化，有利于环保。
Description
技术领域
本发明涉及一种碱性锌酸盐镀锌添加剂生产工艺。
背景技术
目前，碱性锌酸盐镀锌的关键在于选择好恰当的添加剂，加入电镀液中的有机添加剂，在镀锌生产中须同时加入极化型、光亮型两种添加剂。成份复杂，成本高，有污染产生，不利于环保。
发明内容
本发明的目的在于克服上述的缺陷，提供一种碱性锌酸盐镀锌添加剂生产工艺。
本发明的技术方案是：一种碱性锌酸盐镀锌添加剂生产工艺，其特征在于：取40克乙二胺加0.5-8克2-硫醇基间(二)氮茚，在混合液中，加入60ml 12％的甲醛水溶液搅拌30-35分钟加热至60℃，滴入环氧氯丙烷60-70克，搅拌待反应完全后，回流1小时。
本发明具有以下优点：简化镀液成分，便于镀液调控降低成本，适于低铬钝化，有利于环保。
具体实施方式
实施例：一种碱性锌酸盐镀锌添加剂生产工艺，取40克乙二胺加0.5-8克2-硫醇基间(二)氮茚，在混合液中，加入60ml 12％的甲醛水溶液搅拌30-35分钟加热至60℃，滴入环氧氯丙烷60-70克，搅拌待反应完全后，回流1小时。
Claims (1)
1.一种碱性锌酸盐镀锌添加剂生产工艺，其特征在于：取40克乙二胺加0.5-8克2-硫醇基间(二)氮茚，在混合液中，加入60ml 12％的甲醛水溶液搅拌30-35分钟加热至60℃，滴入环氧氯丙烷60-70克，搅拌待反应完全后，回流1小时。