CN101115601A - 用于形成现场固化的衬垫的注塑工艺、装置和材料 - Google Patents
用于形成现场固化的衬垫的注塑工艺、装置和材料 Download PDFInfo
- Publication number
- CN101115601A CN101115601A CNA2006800042417A CN200680004241A CN101115601A CN 101115601 A CN101115601 A CN 101115601A CN A2006800042417 A CNA2006800042417 A CN A2006800042417A CN 200680004241 A CN200680004241 A CN 200680004241A CN 101115601 A CN101115601 A CN 101115601A
- Authority
- CN
- China
- Prior art keywords
- composition
- actinic radiation
- liner
- methyl
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
组分 | 样品号/数量(wt%) | |||||
种类 | 具体物 | 1 | 2 | 3 | 4 | 5 |
弹性体 | KANEKA RC220C1 | 90 | 70 | -- | -- | -- |
聚异戊二烯二丙烯酸酯 | -- | -- | 70 | -- | -- | |
BOMAR BR-7432 GHL2 | -- | -- | -- | 70 | -- | |
RAHN GENOMER 42153 | -- | -- | -- | -- | 70 | |
橡胶增韧剂 | VAMAC DP4 | -- | 6.5 | 6.6 | 6.5 | 6.5 |
抗氧剂 | IRGANOX 10105 | -- | 0.3 | -- | 0.3 | 0.3 |
活性稀释剂 | 丙烯酸异冰片酯 | -- | 13.2 | -- | 13.2 | 13.2 |
SARTOMER SR3956 | -- | -- | 13.4 | -- | -- | |
二氧化硅填料 | CABOSIL TS-5307 | 8 | 8 | 8 | 8 | 8 |
光引发剂 | DAROCUR 4265 | 2 | 2 | 2 | 2 | 2 |
物理性能 | 样品号 | ||||
1 | 2 | 3 | 4 | 5 | |
Shore A | 29 | 43 | 50 | 75 | 95 |
拉伸,psi | 176 | 364 | 117 | 2080 | 2484 |
100%模量,psi | 114 | 177 | -- | 679 | -- |
伸长率,% | 127 | 190 | 34 | 191 | 41 |
初始CSR力,N(S-W) | 124 | 147 | -- | 292 | -- |
CSR,%残留力(S-W)70小时@150℃ | 16 | 21 | -- | 0 | -- |
组分 | 样品号/数量(wt%) | |||||
种类 | 具体物 | 1 | 2 | 6 | 7 | 8 |
弹性体 | BOMAR BR-7432GHL | -- | -- | -- | 78 | 78 |
KANEKA RC220C | 90 | 70 | 70 | -- | -- | |
橡胶增韧剂 | VAMAC DP | -- | 6.5 | 6.6 | 6.5 | 6.6 |
抗氧剂 | IRGANOX 1010 | -- | 0.3 | -- | 0.3 | -- |
活性稀释剂 | 丙烯酸异冰片酯 | -- | 13.2 | -- | 13.2 | -- |
SARTOMER SR4951 | -- | -- | 13.4 | -- | 13.4 | |
二氧化硅填料 | CABOSIL TS-530 | 8 | 8 | 8 | -- | -- |
光引发剂 | DAROCUR 4265 | 2 | 2 | 2 | 2 | 2 |
物理性能 | 样品号 | ||||
1 | 2 | 6 | 7 | 8 | |
Shore A | 29 | 43 | 28 | 67 | 58 |
拉伸,psi | 176 | 364 | 163 | 890 | 393 |
100%模量,psi | 114 | 177 | 55 | 489 | -- |
伸长率,% | 127 | 190 | 239 | 155 | 86 |
压缩形变,%70小时@150℃ | 27 | 12 | 21 | 97 | 101 |
初始CSR力,N(S-W) | 124 | 147 | 97 | 251 | -- |
CSR,%残留力(S-W)70小时@150℃ | 16 | 21 | 24 | 0 | -- |
组分 | 样品号/数量(wt%) | |||||
种类 | 具体物 | 9 | 10 | 11 | 12 | 13 |
弹性体 | KANEKA RC220C | 70 | 70 | 70 | 71.5 | 71.5 |
橡胶增韧剂 | HYCAR VTB1 | 6.6 | 6.6 | 6.6 | -- | -- |
抗氧剂 | IRGANOX 1010 | -- | -- | -- | 2.5 | 2.5 |
活性稀释剂 | 丙烯酸异冰片酯 | 13.4 | -- | 6 | 8 | -- |
SARTOMER SR395 | -- | 13.4 | 7.4 | 8 | 8 | |
SARTOMER SR5312 | -- | -- | -- | -- | 8 | |
二氧化硅填料 | CABOSIL TS-530 | 8 | -- | -- | -- | -- |
HDK-2000 | -- | 8 | 8 | 8 | 8 | |
光引发剂 | DAROCUR 4265 | 2 | 2 | 2 | -- | -- |
IRGACURE 819 | -- | -- | -- | 2 | 2 |
物理性能 | 样品号 | ||||
9 | 10 | 11 | 12 | 13 | |
Shore A | 42 | 26 | 28 | 25 | 21 |
拉伸,psi | 476 | 198 | 163 | 157 | 98 |
100%模量,psi | 215 | -- | 72 | 60 | 55 |
伸长率,% | 196 | 150 | 181 | 210 | 158 |
粘度,cPs@0.5sec- | -- | 178300 | 204020 | 126500 | 115100 |
粘度,cPs@5sec- | -- | 118100 | 136000 | 90550 | 86900 |
压缩形变,%70小时@150℃ | 27 | 27 | 34 | 34 | 13 |
初始CSR力,N(S-W) | 20 | 195 | 196 | 52 | 95 |
CSR,%残留力(S-W)70时@150℃ | 120 | 5 | 6 | 8 | 28 |
组分 | 样品号/数量(wt%) | ||||
种类 | 具体物 | 14 | 15 | 16 | 17 |
弹性体 | KANEKA RC220C | 42.4 | 42.4 | 50 | 42.9 |
KANEKA RC100C | 21.1 | 21.1 | 25 | 21.6 | |
橡胶增韧剂 | HYCAR VTB | 2.5 | 2.5 | 2.5 | 2.5 |
抗氧剂 | IRGANOX HP2225 FF | 1 | 1 | 1 | 1 |
活性稀释剂 | DMAA | 20 | 20 | 15 | 20 |
丙烯酸异冰片酯 | 5 | 5 | -- | 5 | |
SARTOMER PRO66221 | -- | 5 | -- | -- | |
SARTOMER SR 395 | 5 | 5 | -- | 5 | |
SARTOMER SR531 | -- | -- | 1.5 | -- | |
丙烯酸2-乙基己酯 | -- | -- | 3 | -- | |
二氧化硅填料 | HDK-2000 | 2 | 2 | -- | -- |
光引发剂 | IRGACURE 20222 | 1 | 1 | -- | 2 |
IRGACURE 819 | -- | -- | 2 | -- |
物理性能 | 样品号 | |||
14 | 15 | 16 | 17 | |
Shore A | 52 | 50 | 31 | 36 |
拉伸,psi | 397 | 403 | 247 | 403 |
100%模量,psi | 126 | 145 | 74 | 92 |
伸长率,% | 258 | 231 | 249 | 318 |
撕裂强度,Die C,1bs.-in. | 44.6 | 50.6 | -- | 41.4 |
粘度,cPs@0.5sec- | 5784 | 4893 | 9601 | 8295 |
粘度,cPs@5sec- | 3317 | 2916 | 7511 | 7504 |
固化穿透深度,mm | 10+ | 7.7 | -- | 7.2 |
压缩形变,%70小时@150℃ | 11 | 11 | 16 | 26 |
100小时@150℃ | -- | -- | 20.5 | -- |
初始CSR力,N(S-W) | 102 | 82 | 187 | 68 |
CSR,%残留力(S-W)70小时@150℃ | 42 | 34 | 5 | 6 |
初始CSR力,N(J-O) | 107 | -- | -- | 98 |
CSR,%残留力(J-O)70小时@150℃ | 46 | -- | -- | 55 |
初始CSR力,N,Dyneon夹具 | 3 | -- | -- | -- |
组分 | 样品号/数量wt%) | |||||
种类 | 具体物 | 1 | 2 | 18 | 19 | 20 |
弹性体 | KANEKA RC220C | 90 | 70 | 70 | 70 | 70 |
橡胶增韧剂 | VAMAC DP | -- | 6.5 | -- | -- | - |
HYPALON 202 | -- | -- | 6.6 | -- | - | |
NEOPRENE AD-102 | -- | -- | -- | 6.6 | - | |
NIPOL IR2200L3 | -- | -- | -- | -- | 6.6 | |
活性稀释剂 | 丙烯酸异冰片酯 | -- | 13.2 | -- | -- | - |
SARTOMER SR395 | -- | -- | 13.4 | 13.4 | 13.4 | |
二氧化硅填料 | CABOSIL TS-530 | 8 | 8 | 8 | 8 | 8 |
光引发剂 | DAROCUR 4265 | 2 | 2 | 2 | 2 | 2 |
物理性能 | 样品号 | ||||
1 | 2 | 18 | 19 | 20 | |
Shore A | 29 | 43 | 26 | 29 | 27 |
拉伸,psi | 176 | 364 | 178 | 175 | 81 |
100%模量,psi | 114 | 177 | 62 | 69 | 55 |
伸长率,% | 127 | 190 | 210 | 205 | 123 |
压缩形变,%70小时@150℃ | 27 | 12 | 29 | 27 | 不可识别 |
初始CSR力,N(S-W) | 124 | 147 | 20 | 20 | -- |
CSR,%残留力(S-W)70小时@150℃ | 16 | 21 | 15 | 10 | -- |
组分 | 样品号/数量(wt%) | |||||
种类 | 具体物 | 21 | 22 | 23 | 10 | 24 |
弹性体 | KANEKA RC220C | 70 | 70 | 70 | 70 | 70 |
橡胶增韧剂 | RICACRYL 31001 | 6.6 | -- | -- | -- | -- |
VAMAC DP | -- | -- | 6.6 | -- | -- | |
HYCAR VTB | -- | 6.6 | -- | 6.6 | 6.6 | |
活性稀释剂 | 丙烯酸异冰片酯 | 13.4 | 13.4 | -- | -- | 13.4 |
SARTOMER SR395 | -- | -- | 13.4 | 13.4 | -- | |
二氧化硅填料 | CABOSIL TS-530 | 8 | 8 | -- | -- | -- |
HDK-2000 | -- | -- | 8 | 8 | 8 | |
光引发剂 | DAROCUR 4265 | 2 | 2 | 2 | 2 | 2 |
物理性能 | 样品号 | ||||
21 | 22 | 23 | 10 | 24 | |
Shore A | 34 | 42 | 20 | 26 | 42 |
拉伸,psi | 504 | 476 | 130 | 198 | 476 |
100%模量,psi | 197 | 215 | 47 | -- | 215 |
伸长率,% | 209 | 196 | 219 | 150 | 196 |
粘度,cPs@0.5sec- | -- | -- | 188500 | 178300 | -- |
粘度,cPs@5sec- | -- | -- | 113260 | 118100 | -- |
压缩形变,%70小时@150℃ | 43 | 27 | 21 | 27 | 27 |
初始CSR力,N(S-W) | 115 | 20 | 136 | 159 | 20 |
CSR,%残留力(S-W)70小时@150℃ | 2 | 120 | 18 | 5 | 120 |
组分 | 样品号/数量(wt%) | |||
种类 | 具体物 | 11 | 25 | 26 |
弹性体 | KANEKA RC220C | 70 | 74.1 | 71.6 |
橡胶增韧剂 | HYCAR VTB | 6.6 | 2.5 | 5 |
活性稀释剂 | 丙烯酸异冰片酯 | 6 | 6 | 6 |
SARTOMER SR395 | 7.4 | 7.4 | 7.4 | |
二氧化硅填料 | HDK-2000 | 8 | 8 | 8 |
光引发剂 | IRGACURE 819 | 2 | 2 | 2 |
物理性能 | 样品号 | ||
11 | 25 | 26 | |
Shore A | 26 | 26 | 26 |
拉伸,psi | 163 | 156 | 180 |
100%模量,psi | 72 | 82 | 94 |
伸长率,% | 181 | 169 | 163 |
撕裂强度,Die C,lbs.-in. | -- | 18.3 | 17.4 |
粘度,cPs@0.5sec- | 204020 | 172800 | 191200 |
粘度,cPs@5sec- | 136000 | 126900 | 145200 |
压缩形变,%70小时@150℃ | 34 | 22 | 38 |
初始CSR力,N(S-W) | 196 | 170 | 178 |
CSR,%残留力(S-W)70小时@150℃ | 6 | 19 | 11 |
组分 | 样品号/数重(wt%) | ||||||
种类 | 具体物 | 1 | 27 | 8 | 28 | 6 | 23 |
弹性体 | KANEKA RC220C | 90 | 70 | 78 | 78 | 70 | 70 |
橡胶增韧剂 | VAMAC DP | -- | 6.6 | 6.6 | 6.6 | 6.6 | 6.6 |
活性稀释剂 | SARTOMER SR395 | -- | -- | -- | 13.4 | 13.4 | 13.4 |
SARTOMER SR495 | -- | 13.4 | 13.4 | -- | -- | -- | |
二氧化硅填料 | CABOSIL TS-530 | 8 | 8 | -- | -- | 8 | -- |
HDK-2000 | -- | -- | -- | -- | -- | 8 | |
光引发剂 | DAROCUR 4265 | 2 | 2 | 2 | 2 | 2 | 2 |
物理性能 | 样品号 | |||||
1 | 27 | 8 | 28 | 6 | 23 | |
Shore A | 29 | 26 | 58 | 21 | 28 | 20 |
拉伸,psi | 176 | 160 | 393 | 134 | 163 | 130 |
100%模量,psi | 114 | 107 | -- | 40 | 55 | 47 |
伸长率,% | 127 | 137 | 86 | 405 | 239 | 219 |
粘度,cPs@0.5sec- | -- | -- | -- | -- | -- | 188500 |
粘度,cPs@5sec- | -- | -- | -- | -- | -- | 113260 |
压缩形变,%70小时@150℃ | 27 | 77 | 101 | 21 | 21 | 21 |
初始CSR力,N(S-W) | 124 | -- | -- | 128 | 97 | 136 |
CSR,%残留力(S-W)70小时@150℃ | 16 | -- | -- | 24 | 24 | 18 |
组分 | 样品号/数量(wt%) | ||||
种类 | 具体物 | 1 | 2 | 29 | 6 |
弹性体 | KANEKA RC220C | 90 | 70 | 68 | 70 |
橡胶增韧剂 | 分散于丙烯酸异冰片酯中的32.5份VAMAC DP | -- | -- | 20 | -- |
VAMAC DP | -- | 6.5 | -- | 6.6 | |
活性稀释剂 | 丙烯酸异冰片酯 | -- | 13.2 | -- | -- |
抗氧剂 | IRGANOX 1010 | -- | 0.3 | 2 | -- |
二氧化硅填料 | CABOSIL TS-530 | 8 | 8 | 8 | 8 |
光引发剂 | DAROCUR 4265 | 2 | 2 | 2 | 2 |
物理性能 | 样品 | |||
1 | 2 | 29 | 6 | |
Shore A | 29 | 43 | 40 | 28 |
拉伸,psi | 176 | 364 | 363 | 163 |
100%模量,psi | 114 | 177 | 160 | 55 |
伸长率,% | 127 | 190 | 208 | 239 |
压缩形变,%70小时@150℃ | 27 | 12 | -- | 21 |
初始CSR力,N(S-W) | 124 | 147 | -- | 97 |
CSR,%残留力(S-W) | 16 | 21 | -- | 24 |
组分 | 样品号/数量(wt%) | ||
种类 | 具体物 | 27 | 23 |
弹性体 | KANEKA RC220C | 70 | 70 |
橡胶增韧剂 | 分散于丙烯酸异冰片酯中的32.5份VAMAC DP | 20 | -- |
VAMAC DP | -- | 6.6 | |
活性稀释剂 | SARTOMER SR395 | -- | 13.4 |
二氧化硅填料 | CABOSIL TS-530 | 8 | -- |
HDK-2000 | -- | 8 | |
光引发剂 | DAROCUR 4265 | 2 | 2 |
物理性能 | 样品 | |
27 | 23 | |
Shore A | 26 | 20 |
拉伸,psi | 160 | 130 |
100%模量,psi | 107 | 47 |
伸长率,% | 137 | 219 |
粘度,cPs@0.5sec- | -- | 188500 |
粘度,cPs@5sec- | -- | 113260 |
压缩形变,%70小时@150℃ | 77 | 21 |
初始CSR力,N(S-W) | -- | 136 |
CSR,%残留力(S-W) | -- | 18% |
组分 | 样品号/数量(wt%) | |||
种类 | 具体物 | 13 | 16 | 39 |
弹性体 | KANEKA RC220C | 71.5 | 50 | 47.5 |
KANEKA RC100C | -- | 25 | 22 | |
橡胶增韧剂 | NOVEON VTB | 2.5 | 2.5 | 2.5 |
抗氧剂 | IRGANOX HP2225 FF | -- | 1 | 1 |
活性稀释剂 | DMAA | -- | 15 | 15 |
丙烯酸异冰片酯 | -- | -- | 5 | |
SARTOMER SR395 | 8 | -- | -- | |
SARTOMER SR531 | 8 | 1.5 | -- | |
丙烯酸2-乙基己酯 | -- | 3 | -- | |
丙烯酸 | -- | -- | 5 | |
二氧化硅填料 | HDK-2000 | 8 | -- | -- |
光引发剂 | IRGACURE 2022 | -- | -- | 2 |
IRGACURE 819 | 2 | 2 | -- |
物理性能 | 样品号 | ||
13 | 16 | 39 | |
Shore A | 21 | 31 | 62 |
拉伸,psi | 98 | 247 | 965 |
100%模量,psi | 55 | 74 | 384 |
伸长率,% | 158 | 249 | 199 |
粘度,cPs@0.5sec- | 115100 | 9601 | 9240 |
粘度,cPs@5sec- | 86900 | 7511 | 6361 |
固化穿透深度,mm | -- | -- | 0.226 |
压缩形变,%70小时@150℃ | 13 | 16 | 65 |
初始CSR力,N(S-W) | 95 | 187 | 100 |
70小时@150℃ | 28 | 5 | 0 |
组分 | 样品号/数量(wt%) | ||||
种类 | 具体物 | 17 | 41 | 14 | 42 |
弹性体 | KANEKA RC220C | 42.9 | 49.8 | 42.4 | -- |
KANEKA RC200C | -- | -- | -- | 63.5 | |
KANEKA RC100C | 21.6 | 25 | 21.1 | -- | |
橡胶增韧剂 | NOVEON VTB | 2.5 | 2.5 | 2.5 | 2.5 |
抗氧剂 | IRGANOX HP2225 FF | 1 | 1 | 1 | 1 |
活性稀释剂 | DMAA | 20 | 4 | 20 | 20 |
丙烯酸异冰片酯 | 5 | 3.5 | 5 | 5 | |
SARTOMER SR395 | 5 | 3.5 | 5 | 5 | |
丙烯酸 | -- | 0.7 | -- | -- | |
二氧化硅填料 | HDK-2000 | -- | 8 | 2 | 2 |
光引发剂 | IRGACURE 2022 | 2 | 2 | 1 | 1 |
物理性能 | 样品号 | |||
17 | 41 | 14 | 42 | |
Shore A | 36 | 29 | 52 | -- |
拉伸,psi | 403 | 259 | 397 | 566 |
100%模量,psi | 92 | 74 | 126 | 100 |
伸长率,% | 318 | 249 | 258 | 295 |
撕裂强度,Die C,lbs.-in. | 41.4 | 22.8 | 44.6 | -- |
粘度,cPs@0.5sec- | 8295 | 299300 | 5784 | -- |
粘度,cPs@5sec- | 7504 | 198100 | 3317 | -- |
固化穿透深度,mm | 7.2 | 6.1 | 10 | -- |
压缩形变,%70小时@150℃ | 26 | 13 | 11 | -- |
初始CSR力,N(S-W) | 68 | 83 | 102 | -- |
70小时@150℃ | 6 | 28 | 42 | -- |
初始CSR力,N(J-O) | 98 | 167 | 107 | 182 |
CSR,%残留力(J-O) | 55 | 46 | 46 | 67 |
初始力,N Dyneon | -- | -- | 3 | 3 |
%保持24小时150℃ | -- | -- | -- | 95.7 |
%保持70小时150℃ | -- | -- | -- | 43.5 |
组分 | 样品号/数量(wt%) | ||||
种类 | 具体物 | 15 | 43 | 44 | 45 |
弹性体 | KANEKA RC220C | 42.4 | 47 | -- | -- |
KANEKA RC210C | -- | -- | 68 | 45.3 | |
KANEKA RC200C | -- | -- | -- | 22.7 | |
KANEKA RC100C | 21.1 | 18 | -- | -- | |
橡胶增韧剂 | NOVEON VTB | 2.5 | -- | -- | -- |
抗氧剂 | IRGANOX HP2225 FF | 1 | 1 | 1 | 1 |
活性稀释剂 | DMAA | 20 | 20 | 15 | 15 |
SARTOMER PRO6622 | 5 | -- | -- | -- | |
SARTOMER SR395 | 5 | -- | -- | -- | |
二氧化硅填料 | HDK-2000 | 2 | 10 | 15 | 15 |
光引发剂 | IRGACURE 2022 | 1 | 4 | 1 | 1 |
物理性能 | 样品号 | |||
15 | 43 | 44 | 45 | |
Shore A | 50 | 60 | 60 | 74 |
拉伸,psi | 403 | 662 | 626 | 944 |
100%模量,psi | 145 | 274 | 441 | 487 |
伸长率,% | 231 | 232 | 125 | 172 |
撕裂强度,Die C,lbs.-in. | 50.6 | -- | -- | -- |
粘度,cPs@0.5sec- | 4893 | -- | 272200 | 579010 |
粘度,cPs@5sec- | 2916 | -- | 68700 | 116250 |
固化穿透深度,mm | 7.7 | -- | -- | -- |
压缩形变,%70小时@150℃ | 11 | -- | 13 | -- |
初始CSR力,N(S-W) | 82 | -- | -- | -- |
70小时@150℃ | 34 | -- | -- | -- |
初始力,N Dyneon | -- | -- | 91 | -- |
%保持24小时150℃ | -- | -- | 49 | -- |
%保持70小时150℃ | -- | -- | 44.1 | -- |
硬度计,Shore A1 | 85+/-5 | 50+/-5 | 60+/-5 | 50-70 |
撕裂强度,Mpa,min2 | 8.3 | 9.0 | 9.0 | 7.5 |
伸长率,%,min3 | 75 | 250 | 180 | 175 |
100%模量,Mpa,min4 | 3.4 | 3.0 | 3.0 | 2.5 |
压缩形变-70小时@150℃,%max | 60 | 25 | 25 | 40 |
Claims (16)