CN101058956A - 一种高透气吸附衬纸的制造方法 - Google Patents

一种高透气吸附衬纸的制造方法 Download PDF

Info

Publication number
CN101058956A
CN101058956A CN 200710015620 CN200710015620A CN101058956A CN 101058956 A CN101058956 A CN 101058956A CN 200710015620 CN200710015620 CN 200710015620 CN 200710015620 A CN200710015620 A CN 200710015620A CN 101058956 A CN101058956 A CN 101058956A
Authority
CN
China
Prior art keywords
paper
pulp
slurry
adsorption
lining paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200710015620
Other languages
English (en)
Inventor
刘相友
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANDONG HENGLIAN INVESTMENT CO Ltd
Original Assignee
SHANDONG HENGLIAN INVESTMENT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANDONG HENGLIAN INVESTMENT CO Ltd filed Critical SHANDONG HENGLIAN INVESTMENT CO Ltd
Priority to CN 200710015620 priority Critical patent/CN101058956A/zh
Publication of CN101058956A publication Critical patent/CN101058956A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高透气吸附衬纸的制造方法,以天然木浆为原料,包括碎浆、除砂、疏解、抄纸等步骤,其特点是所说的木浆是由针叶浆和阔叶浆混合组成,其中针叶浆所占重量比例为80-90%,阔叶浆所占重量比例为10-20%,打浆电流为320-340A,抄造上网浓度为0.05%。应用本发明方法制成的吸附衬纸透气性能好,高分子材料吸附均匀,湿强度高,特别适合用于生产妇女卫生巾、婴儿纸尿裤、宠物垫等一次性吸附用品。

Description

一种高透气吸附衬纸的制造方法
技术领域
本发明涉及纸张的制造方法,特别是涉及一种用于生产妇女卫生巾、婴儿纸尿裤、宠物垫等高透气吸附衬纸的制造方法。
背景技术
高透气吸附衬纸是用于生产妇女卫生巾、婴儿纸尿裤、宠物垫等的一次性生活用纸。上述产品都是以吸附衬纸为底层,上敷高分子吸水材料、无纺布等复合制成。因此吸附衬纸作为承载体,要求具有高的透气性能和相应的湿强度。目前,国内市场上所使用的吸附衬纸大多为进口产品,虽然质量交好,但成本较高。而国产产品大都透气性较差,用其制作卫生巾、纸尿裤,高分子材料吸附不均匀,往往会导致局部温度升高,形成潮湿环境,易诱发多种病症,并且湿强度低,使用时容易撕裂。
发明内容
本发明的目的就是针对上述现有技术的不足,提供一种吸附衬纸的制造方法,用该方法生产的吸附衬纸透气性能好,湿强度高,特别适合用于生产妇女卫生巾、婴儿纸尿裤、宠物垫等一次性吸附用品。
为实现上述目的,本发明采用的技术方案是:一种高透气吸附衬纸的制造方法,以天然木浆为原料,包括碎浆、除砂、疏解、抄纸等步骤,所说的木浆是由针叶浆和阔叶浆混合组成,其中针叶浆所占重量比例为80-90%,阔叶浆所占重量比例为10-20%,打浆电流为320-340A;浆料在水力碎浆机中碎解15分钟,稀释到3~5%的浓度,泵入未叩浆罐除砂,然后进入疏解机疏解,疏解后的木浆再进入双盘磨,对纤维进行切断和帚化后,进入浓白水槽,用白水冲稀,同时加入湿强剂,浆料经浓白水槽到压力筛,除去体积较大杂质,最后进入流浆箱上网抄造,抄造上网浓度为0.05%。
如上所述高透气吸附衬纸的制造方法,在纸浆中还添加有湿强剂,湿强剂用量为吨纸25-40kg。
如上所述高透气吸附衬纸的制造方法,在纸浆中还添加有干强剂CMC,干强剂CMC用量为吨纸0.5-2kg。
如上所述高透气吸附衬纸的制造方法,其剥离剂和贴缸剂用量的重量比为剥离剂∶贴缸剂=4∶6。
应用本发明方法制备吸附衬纸,由于采用的木浆是由一定比例的针叶浆和阔叶浆混合组成,制成的吸附衬纸透气性能好,高分子材料吸附均匀,并且湿强度高,特别适合用于生产妇女卫生巾、婴儿纸尿裤、宠物垫等一次性吸附用品。经检测,用本发明方法制备的定量为16g/m2吸附衬纸,成品纵拉力2850mN/15mm,横拉力945mN/15mm;湿拉力纵向855mN/15mm;透气度1.?20。透气度比现有国产同类产品提高近6倍。
附图说明
图1为本发明高透气吸附衬纸制造方法的工艺流程图。
具体实施方式
实施例1:
一种高透气吸附衬纸的制造方法,以天然木浆为原料,包括碎浆、除砂、疏解、抄纸等步骤,所说的木浆是由针叶浆和阔叶浆混合组成,其中针叶浆所占重量比例为80%,阔叶浆所占重量比例为20%,打浆电流为320-340A;浆料在水力碎浆机中碎解15分钟,稀释到3~5%的浓度,泵入未叩浆罐除砂,然后进入疏解机疏解,疏解后的木浆再进入双盘磨,对纤维进行切断和帚化后,进入浓白水槽,用白水冲稀,同时加入湿强剂,浆料经浓白水槽到压力筛,除去体积较大的杂质,最后进入流浆箱上网抄造,抄造上网浓度为0.05%。在纸浆中添加有湿强剂和干强剂,湿强剂用量为吨纸25kg,干强剂CMC用量为吨纸2kg,剥离剂和贴缸剂用量的重量比为剥离剂∶贴缸剂=4∶6。具体生产工艺流程见图1。
实施例2:
本发明是以漂白木浆为生产原料,按照90%针叶浆∶20%阔叶浆的重量比例投入到水力碎浆机内,进行碎浆(水力碎浆机容积为8m3),在碎浆的同时加入消泡剂,按吨纸250ml加入,CMC使用量按1.5kg/吨纸加入;在水力碎浆机中碎解15分钟后,稀释到3~5%的浓度,用泵泵送到中间浆罐(32m3),然后再用中间泵,泵送到未叩浆罐(32m3),通过高浓除砂器除砂,除去原料中的砂粒、铁块等比重较大的杂质;浆料从未叩浆进入疏解机,对纤维进行充分疏解,使纤维充分的分丝帚化;疏解后的木浆再进入¢550mm双盘磨,对纤维进行切断和帚化;叩后浆进入到混合槽,准备抄纸,同时取样检测打浆质量;浆料到达浓白水槽,用白水冲稀,同时在线加入湿强剂,湿强剂采用PAE造纸湿强剂,用量为吨纸40kg;浆料经浓白水槽到压力筛,除去体积较大的杂质,最后进入流浆箱上网抄造。调整流浆箱压力至8~9m H2O柱,通过调整纤维的纵横向排列,达到纵横拉力比为2-5∶1;稳定纸机的车速在650m/min;。烘缸的压力在5公斤左右;烘缸罩的温度在170摄氏度左右;为了更好的提高纸页的质量,调整剥离剂和贴缸剂的用量比例,由常规生产的6∶4调整为4∶6,加大贴缸剂用量,提高涂层硬度,使纸页的粘缸效果更好,从而进一步提高纸页的透气性,并且有利于卷取得到平整的纸页。定量16g/m2;抄造上网浓度0.05%;PH值6.7-7.6。

Claims (4)

1、一种高透气吸附衬纸的制造方法,以天然木浆为原料,包括碎浆、除砂、疏解、抄纸等步骤,其特征在于:所说的木浆是由针叶浆和阔叶浆混合组成,其中针叶浆所占重量比例为80-90%,阔叶浆所占重量比例为10-20%,打浆电流为320-340A;浆料在水力碎浆机中碎解15分钟,稀释到3~5%的浓度,泵入未叩浆罐除砂,然后进入疏解机疏解,疏解后的木浆再进入双盘磨,对纤维进行切断和帚化后,进入浓白水槽,用白水冲稀,同时加入湿强剂,浆料经浓白水槽到压力筛,除去体积较大的杂质,最后进入流浆箱上网抄造,抄造上网浓度为0.05%。
2、根据权利要求1所述的高透气吸附衬纸的制造方法,其特征是在纸浆中还添加有湿强剂,湿强剂用量为吨纸25-40kg。
3、根据权利要求1所述的高透气吸附衬纸的制造方法,其特征是在纸浆中还添加有干强剂CMC,干强剂CMC用量为吨纸0.5-2kg。
4、根据权利要求1所述的高透气吸附衬纸的制造方法,其特征是剥离剂和贴缸剂用量的重量比为剥离剂∶贴缸剂=4∶6。
CN 200710015620 2007-05-21 2007-05-21 一种高透气吸附衬纸的制造方法 Pending CN101058956A (zh)