CN101002628A - Application of turnary porous granule in cigarette production - Google Patents
Application of turnary porous granule in cigarette production Download PDFInfo
- Publication number
- CN101002628A CN101002628A CN 200710065612 CN200710065612A CN101002628A CN 101002628 A CN101002628 A CN 101002628A CN 200710065612 CN200710065612 CN 200710065612 CN 200710065612 A CN200710065612 A CN 200710065612A CN 101002628 A CN101002628 A CN 101002628A
- Authority
- CN
- China
- Prior art keywords
- turnary
- tobacco
- expanded cut
- porous granule
- cigarette
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An application of the porous ternary particles in preparing cigarettes for decreasing the content of tar and improving the quality of smoking is disclosed. Said porous ternary particles are mixed with tobacco shreds in ratio of (2-50):100.
Description
Technical field
The invention belongs to the production of cigarettes technical field, relate to the application of cigarette new material, particularly relate to the online application of a kind of turnary porous granule in production of cigarettes.
Background technology
Under the influence of the World Health Organization and anti-smoking campaign, smoking and health problem have become the main challenge that current tobacco business development is faced.How under the prerequisite that guarantees suction quality, to reduce the tar content in the cigarette as far as possible, become the common difficulty of pendulum in face of world's tobacco enterprise.In the prior art, in cigarette composition, use the pipe tobacco substitution material usually, by reducing the consumption of pipe tobacco, reach the purpose of falling Jiao.Pipe tobacco substitution material commonly used at present mainly contains expanded cut tobacco, expanded cabo and reconstituted tobacco etc.Though the use of these substitution material can reduce releasing content of coke tar to a certain extent, also can produce adverse influence simultaneously to the suction quality of cigarette, for example bring wooden assorted gas into, influence harmony etc.
Recently the turnary porous granule of Chu Xianing, for example Chinese patent CN200510021139.5 disclosed " a kind of expanded cabo particle " might find approach for solving this technical barrier.Such material be with offal, thin stalk, stalk sign, stalk piece is raw material, after the special process processing, the particle diameter of formation between 2～5mm, be the expanded cabo of irregular particle state.Its filling value 〉=7.5, inside are distributed with the aperture of many aperture 100～400 μ m.This type of material has the high and high characteristic of filling value of dilation, has good burning performance, and the tar and the carbon monoxide that discharge during burning are low, and do not have wooden assorted gas in the flue gas, have a good application prospect.But for how to use, particularly how it is cooperated with pipe tobacco or other pipe tobacco substitute in the prior art, online production goes out high-quality cigarette, does not see relevant report as yet.
Summary of the invention
The objective of the invention is at the deficiencies in the prior art, the online application process of a kind of turnary porous granule in production of cigarettes is provided, new material is converted into actual production power, satisfy the active demand of enterprise.
Purpose of the present invention is achieved by the following technical programs.
The application of turnary porous granule in production of cigarettes, its specific practice is as follows: adopt the side line feeding manner that turnary porous granule and pipe tobacco and other pipe tobacco substitution material are mixed and join evenly, pack through mixing perfuming, wire distribution storage silk and cigarette, make finished cigarettes.
Described side line feeding manner adopts the quantitative feed system that disposes the groove belt.
Described pipe tobacco substitution material is a kind of in expanded cut tobacco, expanded cut stem or the reconstituted tobacco, or their mixture.
Turnary porous granule and pipe tobacco are mixed by following weight portion and are joined: add 2～50 parts of turnary porous granules in per 100 parts of pipe tobaccos.
Turnary porous granule and pipe tobacco and pipe tobacco substitution material are mixed by following weight portion and are joined: add 0～25 part of expanded cut tobacco, 0～20 part of expanded cut stem, 0～20 part of reconstituted tobacco, 2～50 parts of turnary porous granules in per 100 parts of pipe tobaccos.
In the wire distribution storage silk stage, the control temperature is 28 ± 2.0 ℃, relative humidity 65.0 ± 5.0%, period of storage 2～6 hours.
Compared with prior art, the present invention has the following advantages:
1. the present invention has taken the lead in realizing the practical application of turnary porous granule on cigarette production line, can significantly reduce tar content and carbon monoxide content in the cigarette, improves suction quality, and can reduce production costs, and reduces loss;
2. this technology can be connected well with existing cigarette process and equipment, only needs existing equipment is done simple the adjustment, can realize producing;
3. the good characteristic of turnary porous granule has been given full play in the utilization of this technology, not only can directly add in the existing cigarette composition, and make the existing pipe tobacco substitution material of part or all of replacement become possibility;
4. technology is reasonable, easy and simple to handle, with low cost, has good promotion prospect.
Description of drawings
Fig. 1 is the online application technology flow chart of turnary porous granule of the present invention.
The specific embodiment
Below in conjunction with specific embodiment, the present invention is done further clearly explanation, but they are not the qualification to protection domain of the present invention.
Except as otherwise noted, percentage of the present invention is percetage by weight.
Embodiment 1～4
Conventional side line feeding manner adopts nail and rake type belt convey materials.Because the profile of turnary porous granule is irregular, easy landing during conveying can't effectively be carried, and therefore, changes into the groove belt and carrying.Turnary porous granule and pipe tobacco mixed join evenly, mix mixing ratio and be respectively 2%, 4%, 6% and 8%, mix that to join precision be 1.0%.Mix the prescription silk for preparing and send in the perfuming cylinder by the charging groove that shakes, during rollers running, the finger on the inner wall of rotary drum drives the prescription silk and rolls and travel forward.Essence in the essence bucket, it is vaporific with compressed air to be that power is formed by the essence nozzle, is sprayed on the prescription silk that rolls.The prescription silk enters in the storeroom of Temperature and Humidity Control, and design temperature is 28 ± 2.0 ℃, relative humidity 65.0 ± 5.0%, period of storage 4 hours.Store good prescription silk and be delivered to cigarette machine, roll packing according to conventional cigarette technology of the package from storeroom.The finished cigarettes that makes is carried out flue gas analysis and the aesthetic quality smokes panel test, relatively more differently mixes of the influence of the turnary porous granule of mixing ratio, the results are shown in Table 1 and table 2 cigarette smoke quality and organoleptic quality.
Table 1 cigarette smoke detects table
| Mix mixing ratio | Average weight (g) | Average resistance to suction (Pa) | TPM (mg) | Moisture (mg) | Nicotine content in smoke (mg) | Tar content (mg) | Puff number (mouthful /) | Carbon monoxide (mg) |
| 0 2％ 4％ 6％ 8％ | 0.95 0.95 0.94 0.95 0.95 | 1150 1160 1170 1230 1210 | 18.0 17.4 16.9 16.1 16.0 | 2.7 2.7 2.6 2.5 2.5 | 1.3 1.3 1.3 1.2 1.2 | 14.0 13.4 13.0 12.4 12.3 | 8.3 8.3 8.3 8.3 8.4 | 14.2 13.6 12.9 12.3 12.4 |
The table 2 cigarette organoleptic quality table of smokeing panel test
| Mix mixing ratio | Gloss | Fragrance | Harmony | Assorted gas | Excitant | Pleasant impression | Add up to |
| 0 2％ | 5.0 5.0 | 29.15 29.35 | 5.23 5.14 | 11.00 11.00 | 17.46 17.59 | 22.34 22.50 | 90.2 90.6 |
| 4％ 6％ 8％ | 5.0 5.0 5.0 | 29.43 28.95 29.15 | 5.18 5.20 5.21 | 10.95 11.06 11.14 | 17.55 17.63 17.65 | 22.05 22.38 22.19 | 90.2 90.2 90.3 |
Test result analysis:
Mix mixing ratio 0: pipe tobacco gloss is glossy, and fragrance abundance, coarse is slightly coordinated, and little have assorted gas, slightly stimulate, pleasant impression more only, more comfortable.
Mix mixing ratio 2%: pipe tobacco gloss is glossy, fragrance matter better, fine and smooth sufficient, still coordinate, little have assorted gas, stimulates for a short time, pleasant impression is clean, comfortable.
Mix mixing ratio 4%: pipe tobacco gloss is glossy, and fine and smooth abundance of fragrance, richness, concentration are still outstanding, still coordinate, the gas of slightly mixing, stimulate little, pleasant impression still only, still comfortable.
Mix mixing ratio 6%: pipe tobacco gloss is glossy, and fragrance is still sufficient, coarse slightly, coordinates, and little have assorted gas, stimulate little, pleasant impression more only, more comfortable.
Mix mixing ratio 8%: pipe tobacco gloss is glossy, and fragrance abundance, coarse is slightly coordinated, and base does not have assorted gas, slightly stimulate, pleasant impression still only, still comfortable.
The above results shows that along with the increase that turnary porous granule is mixed mixing ratio, the tar content of cigarette and carbon monoxide content all are tangible reduction trend, and the suction quality of cigarette then slightly improves or be constant substantially.
Embodiment 5～6
Repeat embodiment 1, difference is: the mixing ratio of mixing of turnary porous granule is respectively and accounts for 20%, 50% of pipe tobacco.Testing result sees Table 3 and table 4.
Table 3 cigarette smoke detects table
| Mix mixing ratio | Average weight (g) | Average resistance to suction (Pa) | TPM (mg) | Moisture (mg) | Nicotine content in smoke (mg) | Tar content (mg) | Puff number (mouthful /) | Carbon monoxide (mg) |
| 0 20％ 50％ | 0.94 0.85 0.83 | 1100 1130 1150 | 17.7 15.0 11.4 | 2.3 2.1 2.6 | 1.5 1.3 0.8 | 13.9 11.6 8.0 | 9.6 8.7 8.0 | 13.2 11.5 9.3 |
The table 4 cigarette organoleptic quality table of smokeing panel test
| Mix mixing ratio | Gloss | Fragrance | Harmony | Assorted gas | Excitant | Pleasant impression | Add up to |
| 0 20％ 50％ | 5.00 5.00 5.00 | 27.85 27.79 27.70 | 4.85 4.80 4.80 | 10.10 10.15 9.90 | 16.75 16.80 16.70 | 21.05 21.17 21.15 | 85.6 85.7 85.3 |
Test result analysis:
Mix mixing ratio 0: pipe tobacco gloss is glossy, and fragrance is still sufficient, coarse slightly, harmony still, and slightly assorted gas, excitant is bigger, and pleasant impression is poor slightly, comfortableness is poor slightly.
Mix mixing ratio 20%: pipe tobacco gloss is glossy, and fragrance is still sufficient, coarse slightly, harmony still, slightly assorted gas, excitant is bigger, pleasant impression still only, still comfortable.
Mix mixing ratio 50%: pipe tobacco gloss is glossy, and fragrance is thin, more coarse, and harmony still has assorted gas, and excitant is bigger, pleasant impression still only, still comfortable.
Result of the test shows, use technology of the present invention, turnary porous granule is mixed under the mixing ratio condition at height, not only can significantly reduce tar content and carbon monoxide content in the cigarette, cigarette smoke quality and organoleptic quality also tool are improved significantly, simultaneously the every physical index of cigarette is all had no effect, can replace existing pipe tobacco substitution material fully.
Embodiment 7～8
Repeat embodiment 1, difference is: turnary porous granule and pipe tobacco, expanded cut stem and expanded cut tobacco are mixed joined, the mixing ratio of mixing of expanded cut stem and expanded cut tobacco is 6%, and turnary porous granule is mixed mixing ratio and is respectively 6%, 10%, mixes that to join precision be 1.0%.Testing result sees Table 5 and table 6.
Table 5 cigarette smoke detects table
| Mix mixing ratio | ||||||||||
| Expanded cut stem | Expanded cut tobacco | Turnary porous granule | Average weight (g) | Average resistance to suction (Pa) | TPM (mg) | Moisture (mg) | Nicotine content in smoke (mg) | Tar content (mg) | Puff number (mouthful /) | Carbon monoxide (mg) |
| 6％ 6％ 6％ | 6％ 6％ 6％ | 0 6％ 10％ | 0.93 0.92 0.92 | 1170 1190 1190 | 17.1 16.2 15.9 | 3.0 2.9 2.8 | 1.3 1.2 1.2 | 12.8 12.1 11.9 | 8.1 7.9 8.1 | 13.4 12.0 12.2 |
The table 6 cigarette organoleptic quality table of smokeing panel test
| Mix mixing ratio | |||||||||
| Expanded cut stem | Expanded cut tobacco | Turnary porous granule | Gloss | Fragrance | Harmony | Assorted gas | Excitant | Pleasant impression | Add up to |
| 6％ 6％ 6％ | 6％ 6％ 6％ | 0 6％ 10％ | 5.0 5.0 5.0 | 28.20 28.06 28.13 | 5.06 5.18 5.18 | 11.33 11.48 11.59 | 16.16 16.27 16.45 | 21.43 21.50 21.47 | 87.2 87.5 87.8 |
Test result analysis:
Mix and join expanded cut stem 6%, expanded cut tobacco 6%: pipe tobacco gloss is glossy, the fragrance abundance, shows slightly dull, coordinates, and does not have obviously assorted gas, slightly stimulates, and palate has spine slightly, pleasant impression more only, more comfortable.
Mix and join expanded cut stem 6%, expanded cut tobacco 6%, turnary porous granule 6%: pipe tobacco gloss is glossy, it is flat that fragrance shows slightly, coarse slightly, coordinates, and do not have obviously assorted gas, slightly stimulate, pleasant impression more only, more comfortable.
Mix and join expanded cut stem 6%, expanded cut tobacco 6%, turnary porous granule 10%: pipe tobacco gloss is glossy, fragrance abundance, concentration are still outstanding, coordinate, and do not have assorted gas, slightly stimulate, pleasant impression more only, more comfortable.
Result of the test shows that turnary porous granule and expanded cut tobacco, expanded cut stem mix and match are applied in the cigarette, can effectively improve the effect that reduces tar content in cigarette, carbon monoxide content, to the suction quality effect of having clear improvement of cigarette.
Embodiment 9～10
Repeat embodiment 1, difference is: turnary porous granule and pipe tobacco, expanded cut tobacco and reconstituted tobacco are mixed joined, the mixing ratio of mixing of expanded cut tobacco and reconstituted tobacco is respectively 6% and 4%, and turnary porous granule is mixed mixing ratio and is respectively 4%, 10%, mixes that to join precision be 1.0%.Testing result sees Table 7 and table 8.
Table 7 cigarette smoke detects table
| Mix mixing ratio | ||||||||||
| Expanded cut tobacco | Reconstituted tobacco | Turnary porous granule | Average weight (g) | Average resistance to suction (Pa) | TPM (mg) | Moisture (mg) | Nicotine content in smoke (mg) | Tar content (mg) | Puff number (mouthful /) | Carbon monoxide (mg) |
| 6％ 6％ 6％ | 4％ 4％ 4％ | 0 4％ 10％ | 0.94 0.96 0.97 | 1191 1249 1275 | 17.0 15.9 14.8 | 2.8 2.6 2.5 | 1.4 1.3 1.2 | 12.8 12.0 11.1 | 8.1 8.5 8.1 | 13.9 12.6 12.2 |
The table 8 cigarette organoleptic quality table of smokeing panel test
| Mix mixing ratio | |||||||||
| Expanded cut tobacco | Reconstituted tobacco | Turnary porous granule | Gloss | Fragrance | Harmony | Assorted gas | Excitant | Pleasant impression | Add up to |
| 6％ 6％ 6％ | 4％ 4％ 4％ | 0 4％ 10％ | 5.0 5.0 5.0 | 29.28 29.63 29.35 | 5.00 5.21 5.20 | 10.80 11.06 11.10 | 17.86 18.23 18.54 | 21.85 22.00 22.21 | 89.8 91.1 91.4 |
Test result analysis:
Mix and join expanded cut tobacco 6%, reconstituted tobacco 4%: pipe tobacco gloss is glossy, and fragrance matter is good, and fragrance is plentiful, fine and smooth, coordinates, and little have assorted gas, slightly stimulate, pleasant impression more only, more comfortable.
Mix and join expanded cut tobacco 6%, reconstituted tobacco 4%, turnary porous granule 4%: pipe tobacco gloss is glossy, fragrance matter better, fine and smooth sufficient, the property sent out is better thoroughly, coordinates, and does not have assorted gas, stimulates for a short time, pleasant impression is clean, comfortable.
Mix and join expanded cut tobacco 6%, reconstituted tobacco 4%, turnary porous granule 10%: pipe tobacco gloss is glossy, fragrance is fine and smooth sufficient, richness outstanding, coordinates, and does not have assorted gas, stimulate little, noresidue, pleasant impression is clean, comfortable.
The above results shows that turnary porous granule and expanded cut tobacco, reconstituted tobacco mix and match are applied in the cigarette, along with the increase of turnary porous granule adding proportion, can reduce tar content in cigarette 6%, 13%, reduces cigarette carbon monoxide 9%, 12%.And can reduce the dried thorn sense of cigarette, improve pleasant impression, improve the cigarette comfortableness, obviously improve the cigarette smoking quality.
Embodiment 11～12
Repeat embodiment 1, following difference is arranged: period of storage was respectively 2 hours, 6 hours.
Embodiment 13
Repeat embodiment 1, following difference is arranged: also mix in the prescription silk and be furnished with 25% expanded cut tobacco.Testing result sees Table 9 and table 10.
Table 9 cigarette smoke detects table
| Mix mixing ratio | |||||||||
| Expanded cut tobacco | Turnary porous granule | Average weight (g) | Average resistance to suction (Pa) | TPM (mg) | Moisture (mg) | Nicotine content in smoke (mg) | Tar content (mg) | Puff number (mouthful /) | Carbon monoxide (mg) |
| 25％ 25％ | 0 8％ | 0.94 0.94 | 1153 1131 | 18.7 18.4 | 3.1 3.0 | 1.4 1.4 | 14.2 14.0 | 9.6 9.4 | 14.1 13.8 |
The table 10 cigarette organoleptic quality table of smokeing panel test
| Mix mixing ratio | ||||||||
| Expanded cut tobacco | Turnary porous granule | Gloss | Fragrance | Harmony | Assorted gas | Excitant | Pleasant impression | Add up to |
| 25％ | 0 | 5.0 | 26.16 | 5.00 | 10.35 | 16.77 | 20.74 | 84.0 |
| 25％ | 8％ | 5.0 | 26.21 | 4.96 | 10.45 | 16.83 | 20.78 | 84.2 |
Test result analysis:
Mix and join expanded cut tobacco 25%: pipe tobacco gloss is glossy, and fragrance abundance, fragrance matter are poor slightly, coordinates, and assorted gas is arranged, and nasal cavity, throat stimulate obviously, pleasant impression still only, still comfortable.
Mix and join expanded cut tobacco 25%, turnary porous granule 8%: pipe tobacco gloss is glossy, and fragrance abundance, coarse is slightly coordinated, and little have assorted gas, stimulate little, pleasant impression still totally, still comfortable.
The above results shows that turnary porous granule and expanded cut tobacco mix and match are applied in the cigarette, compare the cigarette that only uses expanded cut tobacco, and it all has the improvement effect at aspects such as excitant, the assorted gas of reduction.
Embodiment 14
Repeat embodiment 1, following difference is arranged: also mix in the prescription silk and be furnished with 20% expanded cut stem.Testing result sees Table 11 and table 12.
Table 11 cigarette smoke detects table
| Mix mixing ratio | |||||||||
| Expanded cut stem | Turnary porous granule | Average weight (g) | Average resistance to suction (Pa) | TPM (mg) | Moisture (mg) | Nicotine content in smoke (mg) | Tar content (mg) | Puff number (mouthful /) | Carbon monoxide (mg) |
| 20％ 20％ | 0 8％ | 0.96 0.96 | 1012 985 | 14.5 14.0 | 1.8 1.7 | 1.2 1.1 | 11.5 11.2 | 8.8 8.8 | 11.9 11.4 |
The table 12 cigarette organoleptic quality table of smokeing panel test
| Mix mixing ratio | ||||||||
| Expanded cut stem | Turnary porous granule | Gloss | Fragrance | Harmony | Assorted gas | Excitant | Pleasant impression | Add up to |
| 20％ 20％ | 0 8％ | 5.0 5.0 | 26.33 26.30 | 4.85 4.87 | 10.03 10.04 | 16.16 16.22 | 19.92 20.04 | 82.3 82.5 |
Test result analysis:
Mix and join expanded cut stem 20%: pipe tobacco gloss is glossy, and fragrance abundance, coarse is slightly still coordinated, and significantly wooden assorted gas is arranged, slightly stimulate, pleasant impression still only, still comfortable.
Mix and join expanded cut stem 20%, turnary porous granule 8%: pipe tobacco gloss is glossy, and fragrance matter is better but concentration is not enough, coordinates, and slightly assorted gas slightly stimulates, and pleasant impression is clean, comfortable.
The above results shows that turnary porous granule and expanded cut stem mix and match are applied in the cigarette, compare the cigarette that only uses expanded cut stem, and it all has the improvement effect at aspects such as excitant, pleasant impressions.
Embodiment 15
Repeat embodiment 1, following difference is arranged: also mix in the prescription silk and be furnished with 20% reconstituted tobacco.Testing result sees Table 13 and table 14.
Table 13 cigarette smoke detects table
| Mix mixing ratio | |||||||||
| Reconstituted tobacco | Turnary porous granule | Average weight (g) | Average resistance to suction (Pa) | TPM (mg) | Moisture (mg) | Nicotine content in smoke (mg) | Tar content (mg) | Puff number (mouthful /) | Carbon monoxide (mg) |
| 20％ 20％ | 0 8％ | 0.92 0.91 | 917 919 | 13.9 13.3 | 2.1 2.0 | 1.0 1.0 | 10.8 10.3 | 7.6 7.6 | 11.4 10.9 |
The table 14 cigarette organoleptic quality table of smokeing panel test
| Mix mixing ratio | ||||||||
| Reconstituted tobacco | Turnary porous granule | Gloss | Fragrance | Harmony | Assorted gas | Excitant | Pleasant impression | Add up to |
| 20％ 20％ | 0 8％ | 5.0 5.0 | 25.88 25.85 | 4.90 4.84 | 11.56 11.61 | 17.66 17.7 3 | 20.11 20.19 | 85.1 85.2 |
Test result analysis:
Mix and join reconstituted tobacco 20%: pipe tobacco gloss is glossy, and fragrance is thin, fragrance matter is better, still coordinates, and little have assorted gas, stimulate little, pleasant impression still only, still comfortable.
Mix and join reconstituted tobacco 20%, turnary porous granule 8%: pipe tobacco gloss is glossy, and fragrance is thin, coarse slightly, still coordinates, and does not have obviously assorted gas, stimulate little, pleasant impression more only, more comfortable.
The above results shows that turnary porous granule and reconstituted tobacco mix and match are applied in the cigarette, compare the cigarette that only uses reconstituted tobacco, its reduce excitant, alleviate assorted gas, change on aspect such as pleasant impression effect is all arranged.
Embodiment 16
Repeat embodiment 1, following difference is arranged: the prescription silk is made up of the raw material of following weight parts: 100 parts of pipe tobaccos, 2 parts of turnary porous granules, 15 parts of expanded cut tobaccos, 10 parts of expanded cut stems and 10 parts of reconstituted tobaccos.Testing result sees Table 13 and table 14.
Table 13 cigarette smoke detects table
| Mix mixing ratio | |||||||||||
| Expanded cut tobacco | Expanded cut stem | Reconstituted tobacco | Turnary porous granule | Average weight (g) | Average resistance to suction (Pa) | TPM (mg) | Moisture (mg) | Nicotine content in smoke (mg) | Tar content (mg) | Puff number (mouthful /) | Carbon monoxide (mg) |
| 15％ 15％ | 10％ 10％ | 10％ 10％ | 0 2％ | 0.93 0.93 | 1106 1111 | 15.9 15.8 | 2.3 2.3 | 1.4 1.4 | 12.2 12.1 | 9.2 9.3 | 13.4 13.3 |
The table 14 cigarette organoleptic quality table of smokeing panel test
| Mix mixing ratio | ||||||||||
| Expanded cut tobacco | Expanded cut stem | Reconstituted tobacco | Turnary porous granule | Gloss | Fragrance | Harmony | Assorted gas | Excitant | Pleasant impression | Add up to |
| 15％ 15％ | 10％ 10％ | 10％ 10％ | 0 2％ | 5.0 5.0 | 27.09 27.06 | 4.92 4.93 | 11.11 11.11 | 17.26 17.32 | 20.57 20.61 | 86.0 86.0 |
Test result analysis:
Mix and join expanded cut tobacco 15%, expanded cut stem 10%, reconstituted tobacco 10%: pipe tobacco gloss is glossy, fragrance concentration is good, matter is good slightly, still coordinates, little have assorted gas, slightly stimulate, pleasant impression still only, still comfortable.
Mix and join expanded cut tobacco 15%, expanded cut stem 10%, reconstituted tobacco 10%, turnary porous granule 2%: pipe tobacco gloss is glossy, fragrance matter is good slightly, fragrance concentration slightly reduces, and still coordinates, little have assorted gas, slightly stimulate, pleasant impression more only, more comfortable.
The above results shows that turnary porous granule and expanded cut tobacco, expanded cut stem, reconstituted tobacco mix and match are applied in the cigarette, under the situation of mixing the dosage minimum, still can slightly change the effect of going up to cigarette excitant, pleasant impression.
Claims (6)
1. the application of turnary porous granule in production of cigarettes, its specific practice is as follows: adopt the side line feeding manner with turnary porous granule and pipe tobacco and other pipe tobacco substitution material mix join even, through mixing perfuming, wire distribution storage silk and cigarette packing, make finished cigarettes.
2. application process according to claim 1 is characterized in that: described side line feeding manner adopts the quantitative feed system that disposes the groove belt.
3. application process according to claim 1 is characterized in that: turnary porous granule and pipe tobacco are mixed by following weight portion and are joined: add 2～50 parts of turnary porous granules in per 100 parts of pipe tobaccos.
4. application process according to claim 1 is characterized in that: described pipe tobacco substitution material is a kind of in expanded cut tobacco, expanded cut stem or the reconstituted tobacco, or their mixture.
5. application process according to claim 4, it is characterized in that: described turnary porous granule and pipe tobacco and other pipe tobacco substitution material are mixed by following weight portion and are joined: add 0～25 part of expanded cut tobacco in per 100 parts of pipe tobaccos, 0～20 part of expanded cut stem, 0～20 part of reconstituted tobacco, 2～50 parts of turnary porous granules.
6. application process according to claim 1 is characterized in that: in the wire distribution storage silk stage, the control temperature is 28 ± 2.0 ℃, relative humidity 65.0 ± 5.0%, period of storage 2～6 hours.