CN102038286A - Toxin-reducing cigarette additive and preparation method and use thereof - Google Patents

Toxin-reducing cigarette additive and preparation method and use thereof Download PDF

Info

Publication number
CN102038286A
CN102038286A CN2010105701885A CN201010570188A CN102038286A CN 102038286 A CN102038286 A CN 102038286A CN 2010105701885 A CN2010105701885 A CN 2010105701885A CN 201010570188 A CN201010570188 A CN 201010570188A CN 102038286 A CN102038286 A CN 102038286A
Authority
CN
China
Prior art keywords
cigarette
additive
tobacco
mesh
added
Prior art date
Application number
CN2010105701885A
Other languages
Chinese (zh)
Inventor
秦亮生
赵立红
郭小义
金勇�
银董红
陈潜
Original Assignee
湖南中烟工业有限责任公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 湖南中烟工业有限责任公司 filed Critical 湖南中烟工业有限责任公司
Priority to CN2010105701885A priority Critical patent/CN102038286A/en
Publication of CN102038286A publication Critical patent/CN102038286A/en

Abstract

The invention discloses a toxin-reducing cigarette additive, and a preparation method and use thereof. In the toxin-reducing cigarette additive, cores are made of an inorganic particulate matter such as silica gel and active carbon, shells are made of waste tobacco powder fibers, and granulation forming is performed under the action of an adhesive, and according to needs, an alkaline functional material can be added in the forming process for reducing HCN content in smoke. The preparation method of the cigarette tip particle additive is simple, the cost of the cigarette tip particle additive is low, and when the prepared additive is added into the tips, the HCN content in the smoke of cigarettes can be reduced effectively without influencing the smoke flavor of the cigarettes.

Description

一种具有减害作用的卷烟添加剂及其制备和应用技术领域[0001] 本发明属于卷烟制造领域,具体涉及具有减害作用的卷烟嘴棒添加剂及其制备方法和在卷烟减害中的应用。 Cigarette additives and their preparation and use Field of desensitization having harmful [0001] The present invention belongs to the field of cigarette manufacturing, particularly relates to a cigarette filter rod having harmful additives and preparation method and application in desensitization of the cigarette harm reduction. 背景技术[0002] 降焦减害是关系到吸烟者身体健康的重要问题,多年以来,各烟草研究机构一直致力于该工作的研究,并且取得了大量研究成果,烟气中有害成分相对有了较大幅度降低。 [0002] tar harm reduction is an important issue related to the health of smokers, over the years, each tobacco research institutions have been working on the job and made a lot of research, flue gas harmful ingredients have relatively a more significant reduction. 一方面在这种多减害手段中,大量添加剂得到了应用,由于这些添加剂并不是烟草本身所具有的,它可能引入外来风险,同时部分地影响到了卷烟原有风格口味。 In this multi-hand harm reduction approach, a number of additives has been applied, since these additives are not the tobacco itself has, it may introduce external risks, while partially affected the style of the original taste of cigarettes. 另一方面,烟草生产过程中部分原材料没有得到很好的利用,产生了大量的浪费。 On the other hand, part of the tobacco material in the production process is not well utilized to produce a lot of waste. 因此很多烟草企业也在这方面做了不少工作。 So many tobacco companies are doing a lot of work in this area. [0003] HCN是烟气中的主要有害物质之一,同时也是重要的环境污染源之一,在严重情况下它可能使人在数分钟内死亡,危害极大。 [0003] HCN is one of the main harmful substances in the flue gas, but also an important source of environmental pollution, in severe cases it may make people die within a few minutes, it is lethal. 因此,烟气中HCN的选择性降低也成为烟草行业必须解决的重要问题。 Therefore, the flue gas HCN selectivity to reduce tobacco industry has become an important issue that must be addressed. [0004] 在过去几十年中大量机构对如何有效降低烟气中HCN及醛类做了大量研究,如采用离子交换树脂作为嘴棒添加剂、无机盐处理嘴棒、活性炭嘴棒等,但这些手段要么由于价格因素,要么因为可能引入的新的危害源或者影响卷烟吸味,因此很少有工业化的应用。 [0004] In the last decades a lot of research on the mechanism of how large to effectively reduce smoke HCN and aldehydes, such as ion-exchange resin as a filter tip additive, inorganic processing filter tip, the activated carbon filter tip, but these means either due to price factors, or because of new sources of hazards that may be introduced or affect cigarette smoke flavor, there are few applications of industrialization. [0005] 在专利申请2009103104069中述及了一种烟末颗粒的制备及其在卷烟减害中的应用,所述的方法制备的烟末颗粒是烟末的松散粘结,得到的颗粒颗粒度均勻性较差,强度不好,在作为添加剂应用到卷烟过滤嘴的后续工艺中很容易出现再次破碎,对机器造成较大磨损和污染,与此同时,制备出的颗粒复合嘴棒吸阻急剧增大,使得其实用性不强,应用前景非常暗淡。 [0005] In the mentioned patent application 2009103104069 Preparation and application of the end of a smoking cigarette harm reduction in particles in the smoke particles produced at the end of the method of bonding is loose end of tobacco, the particles of the particle obtained poor uniformity, poor strength, it is prone to break again, resulting in greater wear and contamination of the cigarette filter machine to use as an additive in a subsequent process, at the same time, the composite particles prepared filter tip sharp increase resistance to draw large, so its usefulness is not strong, the prospects are very bleak. 针对专利申请2009103104069中所用方法的缺点,本发明能够很好地弥补其缺陷的同时保证降害效果也很好。 Application for Patent 2009103104069 disadvantages of the method, the present invention can well compensate for its shortcomings harm reduction while ensuring also very effective. 发明内容[0006] 本发明的第一个目的是提供一种制备且添加方便,适合于工业化生产的要求,成本低,可很好地选择性降低卷烟烟气中HCN含量的添加剂。 SUMMARY [0006] A first object of the present invention is to provide a process and to add convenient, suitable for industrial production requirements, low cost, very selectively reducing additive content of HCN in cigarette smoke. [0007] 本发明的另一目的在于提供上述添加剂的一种制备方法。 [0007] Another object of the present invention is to provide a method for preparing the above-described additives. [0008] 本发明的第三个目的在于提供上述添加剂的一种较佳的应用方法。 [0008] A third object of the present invention to provide a preferred method of application of the above additives. [0009] 本发明是通过下述方式实现的:[0010] 一种具有减害作用的卷烟添加剂,是由硅胶、分子筛、氧化铝、活性炭中的一种或多种为内核;然后将烟末采用胶黏剂水溶液粘接在内核表面,烘干而成的颗粒。 [0009] The present invention is achieved by the following manner: [0010] A cigarette having a reduced harmful effect of additives is silica gel, molecular sieves, alumina, activated carbon or more of one kind to the core; and the tobacco powder an aqueous adhesive using the adhesive surface of the core, granules obtained by drying. [0011] 所述的硅胶、分子筛、氧化铝、活性炭颗粒大小为60-80目。 [0011] The silica gel, molecular sieves, alumina, activated carbon particle size of 60-80 mesh. [0012] 所述的烟末颗粒大小为150-200目。 [0012] The tobacco dust of particle size of 150-200 mesh. [0013] 所述的烟末来源于经过粉碎的烟梗、烟末、碎烟片或梗签中的一种或几种。 [0013] After the end of the smoke from pulverized tobacco stems, tobacco dust, shredded tobacco sheet or to check one or more of the stems. [0014] 所述的胶黏剂为羧甲基纤维素钠、瓜豆胶、硅酸钠、硅酸钾中的一种或多种。 [0014] The adhesive of sodium carboxymethyl cellulose, guar gum, sodium silicate, potassium silicate, one or more. [0015] 所述的添加剂颗粒大小为10-100目。 Additive particle size [0015] of the 10 to 100 mesh. [0016] 上述卷烟添加剂的制备方法:将硅胶、分子筛、氧化铝或活性炭中的一种或几种在不断搅拌状态下缓慢加入含有胶黏剂的水溶液,使之湿润,然后加入烟末并不断搅拌,同时再缓慢加入含有胶黏剂的水溶液使之牢固粘结在固体颗粒物表面,之后烘干、自然冷却,取10-100目粒径的颗粒即得。 [0016] The preparation method of the cigarette additives: one kind of the silica gel, molecular sieve, alumina or activated carbon or several state under continuous stirring is slowly added an aqueous solution containing adhesive, moistening, tobacco dust and then added continuously stirred while added slowly so that the aqueous solution containing adhesive is firmly adhered to the surface of the solid particles, after drying, natural cooling, taking 10-100 mesh to obtain sized particles. [0017] 所述的胶黏剂的浓度为-50%。 The concentration of the adhesive [0017] -50%. [0018] 所述的卷烟添加剂应用于添加到卷烟嘴棒或烟丝中。 Cigarette Additives [0018] The applied or added to the tobacco in a cigarette filter rod. 添加剂颗粒粒径优选为40-60 目。 Additives preferably 40-60 mesh particle size. [0019] 添加剂添加到卷烟嘴棒时添加量为10-60mg/支卷烟,优选为20_50mg/支卷烟。 Addition amount of 10-60mg / cigarette while [0019] additive to cigarette filter rod, preferably 20_50mg / cigarettes. [0020] 本发明的应用方法也可将发明的添加剂颗粒直接添加到烟丝中或者经过处理后添加到烟丝中,其添加量可以根据需要调节。 [0020] Application of the method according to the present invention the additive particles may also be added directly to the shredded tobacco to the invention or added to the tobacco after treatment, it may be added in an amount adjusted according to need. [0021] 本发明提供的添加剂颗粒可以根据卷烟降焦减害的需要在成型过程中添加其它具有减害作用的无害添加剂,如氢氧化钠或碳酸钠。 [0021] The additive particles of the present invention may provide a cigarette tar harm reduction additive has a need to add additional harm reduction sound effect during the molding process in accordance with such as sodium hydroxide or sodium carbonate. [0022] 本发明提供的添加剂颗粒由于在成型过程中使用的胶黏剂具有一定的碱性,它具有很好的选择性降低烟气中HCN的作用。 [0022] The present invention provides additive particles used in the adhesive due to the molding process has certain basic, it has good selectivity to HCN smoke reducing effect. 由于该颗粒表面基本全部被烟末所覆盖,与其它类似嘴棒添加剂相比具有先天优势,基本不会引起卷烟吸味的改变,本发明的创新性在相关领域也未见报道。 Since the surface of the particles to be substantially all of the tobacco dust covered filter rod as compared with other similar additives have inherent advantages, does not substantially cause a change in cigarette smoke flavor, the innovation of the present invention is also not been reported in the related art. [0023] 由于本发明的添加剂主要组分为内核为无机组分、外层为烟草植物纤维组成的固体颗粒,难溶于大部分有机试剂,且具有足够强度,适合制备复合嘴棒;添加量小且可以根据需要任意调节;能够显著地选择性降低烟气中HCN含量且对卷烟吸味影响小;由于该技术的操作性很强,具有很强的现实意义。 [0023] Since additives of the invention into the main component is an inorganic component core, the outer layer of solid particles of tobacco plant fibers, insoluble in most organic reagent, and has sufficient strength, suitable for producing a composite filter rod; amount added small and can be adjusted according to need; can be significantly reduced in flue gas HCN selectivity and little influence on the content of the cigarette smoke flavor; operably since this technique is very strong, it has a great practical significance. [0024] 本发明最大的优点是制备得到的颗粒颗粒度均勻性很好,同时具有很好的强度, 在制备颗粒复合棒的后续过程中不会再次破碎,扬尘少,对机器磨损和污染较少,制备出的颗粒复合棒吸阻也不会显著性增大,基本能够满足卷烟复合嘴棒的生产工艺要求。 [0024] The greatest advantage of the invention is a particle prepared particle uniformity is good, while having good strength, will not be broken again in the preparation of the particles of the composite rod subsequent process, less dust, machine wear and polluted less, the composite particles prepared rod resistance to draw is not significantly increased, to meet the basic filter tip cigarette of the composite production process. [0025] 本发明与已有技术相比具有显著优点:[0026] A.该技术能显著地选择性降低烟气中HCN含量。 [0025] The prior art and the present invention has significant advantages as compared to: [0026] A. This technique can significantly reduce the selectivity of HCN content in the flue gas. [0027] B.该技术物质来源于烟草,使得烟草利用率得到提高,同时基本不改变卷烟吸味, 生产可行性大。 [0027] B. The material from the tobacco art, so that improved utilization of tobacco, while not substantially changing the cigarette smoke flavor, the feasibility of producing. [0028] C.该技术物质可作为一种很好的降焦减害载体,根据不同的减害需求进行不同的处理。 [0028] C. This technique can be used as a good material harm reduction tar vector for different processing according to different needs of harm reduction. [0029] D.该技术物质具有足够强度,在制备颗粒复合棒的后续过程中不会再次破碎,扬尘少,对机器磨损和污染较少,制备出的颗粒复合棒吸阻也不会增大,基本能够满足卷烟复合嘴棒的生产工艺要求。 [0029] D. The technical material having sufficient strength, in the preparation of the particles composite rod will not break during subsequent again, little dust, machine wear and less polluting particles prepared composite rod resistance to draw is not increased can basically meet the filter tip cigarette of the composite production process. [0030] E.该技术成本低廉,制备简单,操作方便。 [0030] E. low cost of the technology, the preparation of simple to operate. [0031] 综上所述,本发明的添加剂制备且添加方便,适合于工业化生产的要求,可很好地选择性降低烟气中HCN含量,可大大地减少对吸烟的者的危害的同时保持口味的稳定。 [0031] In summary, the present invention is conveniently prepared and the additive is added, adapted to the requirements of industrial production, may well be selectively reducing HCN content in the flue gas, can greatly reduce the hazards of smoking persons while maintaining the stability of taste. 具体实施方式[0032] 以下实施例旨在说明本发明而不是对本发明进一步限定。 DETAILED DESCRIPTION [0032] The following examples are intended to further illustrate the invention and not to limit the present invention. 4[0033] 实施例1[0034] 称取60-80目硅胶30g置于玻璃杯中,配制IOOg 10%水玻璃溶液,硅胶在搅拌状态下缓慢加入水玻璃溶液,使硅胶表面变得潮润有粘性,再将20g烟末(烟末颗粒大小为150-200目)缓慢加入潮润的硅胶颗粒中,搅拌混合均勻并使烟末粘结在硅胶表面,继续加入少量水玻璃溶液使得烟末粘结更牢固;将制备所得颗粒物转移至烘箱中,在100°C烘8小时左右至干,自然冷却;将烘干的烟末颗粒过筛,筛去部分较细小烟末,得到添加剂颗粒大小为40-60目。 4 [0033] Example 1 [0034] 30g weighed 60-80 mesh silica gel was placed in a glass, prepared IOOg 10% water-glass solution, silica gel was slowly added waterglass solution under stirring, the silica gel has a surface becomes moist viscosity, and then tobacco powder 20g silica particles (tobacco powder particle size 150-200 mesh) was slowly added to the moist, and mixing evenly tobacco powder bonded silica surface, so that the water glass solution further added a small amount of tobacco dust adhesion more firmly; the resulting granules prepared was transferred to an oven at 100 ° C bake to dryness to 8 hours, allowed to cool; the dried tobacco dust granules are screened, to the end portion of the finer mesh cigarette, the additive particle size of 40 to give -60 mesh. [0035] 将制备得到的颗粒添加剂以40mg/支添加到烟支嘴棒中,用SM400型吸烟机按照标准烟气检测方法进行烟气检测,烟气检测结果显示该颗粒添加剂具有较好的选择性降低卷烟烟气中HCN含量的效果,结果见下表1 :[0036] 表1降害效果[0037] [0035] The particulate additive prepared at 40mg / support added to the cigarette filter rod, for detecting smoke SM400 smoking machine according to standard method of gas detection, gas detection results show that the particulate additive has a better choice the effect of reducing the content of HCN in cigarette smoke, the results in table 1 below: [0036] tABLE 1 effect harm reduction [0037]

Figure CN102038286AD00051

[0038] 实施例2[0039] 称取60-80目活性炭40g置于玻璃杯中,配制IOOg 10%水玻璃溶液,活性炭在搅拌状态下缓慢加入水玻璃溶液,使活性炭表面变得潮润有粘性,再将20g烟末缓慢加入潮润的活性炭颗粒中,搅拌混合均勻并使烟末粘结在活性炭表面,继续加入少量水玻璃溶液使得烟末粘结更牢固;将制备所得颗粒物转移至烘箱中,在100°C烘8小时左右至干,自然冷却;将烘干的烟末颗粒过筛,筛去部分较细小烟末,得到添加剂颗粒大小为40-60目。 [0038] Example 2 [0039] 40g of activated carbon weighed 60-80 mesh placed in the glass, prepared IOOg 10% water-glass solution, stirring the activated carbon was slowly added waterglass solution state, activated carbon becomes moist tacky surface , activated carbon particles and then 20g of moist tobacco powder was slowly added, followed by stirring and mixing uniformly the surface of the activated carbon adhered to tobacco powder, further added a small amount of water glass solution that tobacco powder bonded more firmly; the resulting granules prepared was transferred to an oven, to dryness and baked at about 100 ° C for 8 hours and allowed to cool; the end of the drying of smoke particles with a sieve tobacco dust to a finer part, to give a particle size of 40-60 mesh additive. [0040] 将制备得到的颗粒添加剂以40mg/支添加到烟支嘴棒中,用SM400型吸烟机按照标准烟气检测方法进行烟气检测,烟气检测结果显示该颗粒添加剂具有较好的选择性降低卷烟烟气中HCN含量的效果,结果见下表2 :[0041] 表2降害效果[0042] [0040] The particulate additive prepared at 40mg / support added to the cigarette filter rod, for detecting smoke SM400 smoking machine according to standard method of gas detection, gas detection results show that the particulate additive has a better choice reducing effect of the HCN content in cigarette smoke, results in table 2 below: [0041] table 2 effect harm reduction [0042]

Figure CN102038286AD00052

[0043] 实施例3[0044] 称取60-80目硅胶30g置于玻璃杯中,配制IOOg 15%的羧甲基纤维素钠和碳酸钠(质量比1 : 1)混合溶液,硅胶在搅拌状态下缓慢加入混合溶液,使硅胶表面变得潮润有粘性,再将20g烟末(烟末颗粒大小为150-200目)缓慢加入潮润的硅胶颗粒中,搅拌混合均勻并使烟末粘结在硅胶表面,继续加入少量混合溶液使得烟末粘结更牢固;将制备所得颗粒物转移至烘箱中,在100°C烘8小时左右至干,自然冷却;将烘干的烟末颗粒过筛,筛去部分较细小烟末,得到添加剂颗粒大小为40-60目。 [0043] Example 3 [0044] Weigh 30g silica gel 60-80 mesh placed in the glass, is formulated IOOg 15% of sodium carboxymethylcellulose and sodium carbonate (mass ratio 1: 1) mixed solution, silica gel was stirred in was slowly added to the mixed solution in the state, the silica gel surface becomes moist sticky, the end of the cigarette and then 20g (tobacco powder of 150-200 mesh particle size) was slowly added to moist silica particles stirred and mixed tobacco dust adhered silica surface, so that the mixed solution was further added a small amount of tobacco powder bonded more firmly; the resulting granules prepared was transferred to an oven at 100 ° C bake to dryness to 8 hours, allowed to cool; the dried tobacco dust particles with a sieve tobacco to a finer part of the end, to give a particle size of 40-60 mesh additive. [0045] 将制备得到的颗粒添加剂以40mg/支添加到烟支嘴棒中,用SM400型吸烟机按照标准烟气检测方法进行烟气检测,烟气检测结果显示该颗粒添加剂具有较好的选择性降低卷烟烟气中HCN含量的效果,结果见下表3 :[0046] 表3降害效果[0047] [0045] The particulate additive prepared at 40mg / support added to the cigarette filter rod, for detecting smoke SM400 smoking machine according to standard method of gas detection, gas detection results show that the particulate additive has a better choice the effect of reducing the content of HCN in cigarette smoke, results in table 3 below: [0046] table 3 effect harm reduction [0047]

Figure CN102038286AD00061

[0048][0049] 实施例4[0050] 称取60-80目硅胶30g置于玻璃杯中,配制IOOg 1 %的羧甲基纤维素钠和氢氧化钠(质量比1 : 1)混合溶液,硅胶在搅拌状态下缓慢加入混合溶液,使硅胶表面变得潮润有粘性,再将20g烟末(烟末颗粒大小为150-200目)缓慢加入潮润的硅胶颗粒中,搅拌混合均勻并使烟末粘结在硅胶表面,继续加入少量混合溶液使得烟末粘结更牢固;将制备所得颗粒物转移至烘箱中,在100°C烘8小时左右至干,自然冷却;将烘干的烟末颗粒过筛,筛去部分较细小烟末,得到添加剂颗粒大小为40-60目。 [0048] [0049] Example 4 [0050] 30g weighed 60-80 mesh silica glass was placed in formulated IOOg 1% of sodium carboxymethylcellulose and sodium hydroxide (mass ratio 1: 1) mixed solution of , silica gel was added slowly under stirring the mixed solution, the silica gel has a tacky surface becomes moist, then the end 20g smoke (tobacco powder of 150-200 mesh particle size) was slowly added to moist silica particles and stirred uniformly mixed and smoke bonding the end surface of silica gel, further added a small amount of the mixed solution such that the tobacco powder bonded more firmly; the resulting granules prepared was transferred to an oven at 100 ° C bake to dryness to 8 hours, allowed to cool; the dried tobacco dust particles a sieve finer end portion to smoke, additives to give a particle size of 40-60 mesh. [0051] 将制备得到的颗粒添加剂以40mg/支添加到烟支嘴棒中,用SM400型吸烟机按照标准烟气检测方法进行烟气检测,烟气检测结果显示该颗粒添加剂具有较好的选择性降低卷烟烟气中HCN含量的效果,结果见下表4 :[0052] 表4降害效果[0053] [0051] The particulate additive prepared at 40mg / support added to the cigarette filter rod, for detecting smoke SM400 smoking machine according to standard method of gas detection, gas detection results show that the particulate additive has a better choice reducing effect of the HCN content in cigarette smoke, the results in table 4 below: [0052] tABLE 4 effect harm reduction [0053]

Figure CN102038286AD00062

[0054] 实施例5[0055] 称取60-80目硅胶30g置于玻璃杯中,配制IOOg 15%的羧甲基纤维素钠和氢氧化钠(质量比1 : 4)混合溶液,硅胶在搅拌状态下缓慢加入混合溶液,使硅胶表面变得潮润有粘性,再将20g烟末(烟末颗粒大小为150-200目)缓慢加入潮润的硅胶颗粒中,搅拌混合均勻并使烟末粘结在硅胶表面,继续加入少量混合溶液使得烟末粘结更牢固;将制备所得颗粒物转移至烘箱中,在100°C烘8小时左右至干,自然冷却;将烘干的烟末颗粒过筛,筛去部分较细小烟末,得到添加剂颗粒大小为40-60目。 [0054] Example 5 [0055] 30g weighed 60-80 mesh silica glass was placed in formulated IOOg 15% of sodium carboxymethylcellulose and sodium hydroxide (mass ratio 1: 4) mixed solution, silica gel was slowly added under stirring the mixed solution, the silica gel surface becomes moist sticky, then the tobacco powder 20g silica particles (tobacco powder 150-200 mesh particle size) was slowly added to the moist, homogeneous mixing tobacco dust and binder the silica surface, so that the mixed solution was further added a small amount of tobacco powder bonded more firmly; the resulting granules prepared was transferred to an oven at 100 ° C bake to dryness to 8 hours, allowed to cool; the dried tobacco dust granules are screened, end portion finer sieve to smoke, additives to give a particle size of 40-60 mesh. [0056] 将制备得到的颗粒添加剂以40mg/支添加到烟支嘴棒中,用SM400型吸烟机按照标准烟气检测方法进行烟气检测,烟气检测结果显示该颗粒添加剂具有较好的选择性降低卷烟烟气中HCN含量的效果,结果见下表5 :[0057] 表5降害效果[0058] [0056] The particulate additive prepared at 40mg / support added to the cigarette filter rod, for detecting smoke SM400 smoking machine according to standard method of gas detection, gas detection results show that the particulate additive has a better choice the effect of reducing the content of HCN in cigarette smoke, the results in table 5 below: [0057] table 5 effect harm reduction [0058]

Figure CN102038286AD00071

Claims (16)

1. 一种具有减害作用的卷烟添加剂,其特征在于,是由硅胶、分子筛、氧化铝、活性炭中的一种或多种为内核;然后将烟末采用胶黏剂水溶液粘接在内核表面,烘干而成的颗粒。 An additive having a cigarette harm reduction effect, characterized in that is made from a silica gel, molecular sieves, alumina, activated carbon or more of the kernel; tobacco dust is then employed in the aqueous adhesive surface of the adhesive core drying formed granules.
2.根据权利要求1所述的卷烟添加剂,其特征在于,所述的硅胶、分子筛、氧化铝、活性炭颗粒大小为60-80目。 2. The cigarette additive according to claim 1, wherein said silica gel, molecular sieves, alumina, activated carbon particle size of 60-80 mesh.
3.根据权利要求1所述的卷烟添加剂,其特征在于,所述的烟末颗粒大小为150-200目。 3. The cigarette additive in claim 1, wherein said tobacco dust particle size of 150-200 mesh.
4.根据权利要求1所述的卷烟添加剂,其特征在于,所述的烟末来源于经过粉碎的烟梗、烟末、碎烟片或梗签中的一种或几种。 4. The cigarette additive in claim 1, characterized in that, after the end of the smoke from pulverized tobacco stems, tobacco dust, shredded tobacco stems or sheet of one or more check.
5.根据权利要求1所述的卷烟添加剂,其特征在于,所述的胶黏剂为羧甲基纤维素钠、 瓜豆胶、硅酸钠、硅酸钾中的一种或多种。 The cigarette additive according to claim 1, wherein said adhesive is sodium carboxymethylcellulose, guar gum, sodium silicate, potassium silicate, one or more.
6.根据权利要求1所述的卷烟添加剂,其特征在于,所述的添加剂颗粒大小为10-100目。 6. The cigarette additive according to claim 1, wherein said additive particle size of 10-100 mesh.
7. 一种卷烟添加剂的制备方法,其特征在于,将硅胶、分子筛、氧化铝或活性炭中的一种或几种在不断搅拌状态下缓慢加入含有胶黏剂的水溶液,使之湿润,然后加入烟末并不断搅拌,同时再缓慢加入含有胶黏剂的水溶液使之牢固粘结在固体颗粒物表面,之后烘干、 自然冷却,取10-100目粒径的颗粒即得。 A method of preparing a cigarette additives, wherein the silica gel, molecular sieves, activated alumina, or one or several state under continuous stirring is slowly added an aqueous solution containing adhesive, moistening, and then added tobacco powder and continue stirring while an aqueous solution added slowly to contain adhesive firmly adhered to the surface of the solid particles, after drying, natural cooling, taking 10-100 mesh to obtain sized particles.
8.根据权利要求7所述的制备方法,其特征在于,所述的硅胶、分子筛、氧化铝、活性炭颗粒大小为60-80目。 8. The production method according to claim 7, wherein said silica gel, molecular sieves, alumina, activated carbon particle size of 60-80 mesh.
9.根据权利要求7所述的制备方法,其特征在于,所述的烟末颗粒大小为150-200目。 9. A method of preparation according to claim 7, wherein said tobacco dust of particle size of 150-200 mesh.
10.根据权利要求7或9所述的卷烟添加剂,其特征在于,所述的烟末来源于经过粉碎的烟梗、烟末、碎烟片或梗签中的一种或几种。 Additive cigarette according to claim 7 or 9, characterized in that, after the end of the smoke from pulverized tobacco stems, tobacco dust, shredded tobacco stems or sheet of one or more check.
11.根据权利要求7所述的制备方法,其特征在于,所述的胶黏剂为羧甲基纤维素钠、 瓜豆胶、硅酸钠、硅酸钾中的一种或多种。 The production method according to claim 7, wherein said adhesive is sodium carboxymethylcellulose, guar gum, sodium silicate, potassium silicate, one or more.
12.根据权利要求7或11所述的制备方法,其特征在于,所述的胶黏剂的浓度为1% -50%。 7 or 12. The preparation process as claimed in claim 11, wherein said adhesive is a concentration of 1% to 50%.
13.权利要求1所述的卷烟添加剂应用于添加到卷烟嘴棒或烟丝中。 13. The cigarette as claimed in claim 1, the additive is applied or added to the tobacco in a cigarette filter rod.
14.根据权利要求13所述的应用方法,其特征在于,添加剂颗粒粒径为40-60目。 14. The application of the method according to claim 13, wherein the additive particle size is 40-60 mesh.
15.根据权利要求13或14所述的应用方法,其特征在于,添加到卷烟嘴棒时添加量为10-60mg/支卷烟。 Addition amount of 10-60mg / cigarette 15. The application of the method of claim 13 or claim 14, characterized in that, when added to a cigarette filter tip.
16.根据权利要求15所述的应用方法,其特征在于,添加到卷烟嘴棒时添加量为20-50mg/支卷烟。 16. The application of the method according to claim 15, characterized in that, added to the addition amount of 20-50mg / cigarette when the cigarette filter tip.
CN2010105701885A 2010-12-02 2010-12-02 Toxin-reducing cigarette additive and preparation method and use thereof CN102038286A (en)