CN100585510C - 导电性环带以及使用其的图像形成装置 - Google Patents
导电性环带以及使用其的图像形成装置 Download PDFInfo
- Publication number
- CN100585510C CN100585510C CN200680028503A CN200680028503A CN100585510C CN 100585510 C CN100585510 C CN 100585510C CN 200680028503 A CN200680028503 A CN 200680028503A CN 200680028503 A CN200680028503 A CN 200680028503A CN 100585510 C CN100585510 C CN 100585510C
- Authority
- CN
- China
- Prior art keywords
- resin
- endless belt
- conductive endless
- thermoplastic
- ester bond
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种导电性环带以及使用其的图像形成装置，其中，该导电性环带在结构方面具有可耐受反复连续使用的物性、特别是耐安装性，且具有光泽度和导电性也稳定的特性。一种导电性环带以及使用其的图像形成装置，其中，该导电性环带是对由热塑性聚萘二甲酸烷二醇酯树脂和除热塑性聚萘二甲酸烷二醇酯树脂以外的2种以上具有酯键的热塑性树脂形成的基材添加导电性填料而成的，热塑性聚萘二甲酸烷二醇酯树脂与2种以上具有酯键的热塑性树脂的重量比在95/5～55/45的范围内，且2种以上具有酯键的热塑性树脂包含各至少1种非结晶性树脂和结晶性树脂。
Description
技术领域
本发明涉及在复印机、打印机等电子照相装置、静电记录装置等中的静电记录过程中，将调色剂像转印到纸等记录介质上时所使用的导电性环带(以下简单称为“皮带”)以及使用其的图像形成装置，其中，该调色剂像是将显影剂供给至在表面上保持有静电潜像的潜像保持体等图像形成体表面而形成的。
背景技术
一直以来，在复印机、打印机等中的静电记录过程中，采用如下方法：首先，使感光体(潜像保持体)的表面均匀带电，由光学系统向该感光体投射影像，除去光照射部分所带的电，从而形成静电潜像，接着，将调色剂供给至该静电潜像，通过调色剂的静电吸附形成调色剂像，将其转印到纸、OHP、印相纸等记录介质上，由此打印。
此时，在彩色打印机或彩色复印机中，基本上也按照上述过程进行打印，但在彩色印刷时，使用品红色、黄色、青色、黑色4种颜色的调色剂重现色调，因此必须要有以规定比例叠加这些调色剂得到所需色调的工序，为了进行该工序而提出了几种方式。
首先，第1，有如下的多重显影方式：与进行单色印刷的情况同样，在将调色剂供给至感光体上使静电潜像可视化时，依次叠加上述品红色、黄色、青色、黑色4种颜色的调色剂，从而进行显影，在感光体上形成彩色的调色剂像。通过该方式，能够比较小型地构成装置，但该方式中存在非常难以控制灰度、无法得到高画质的问题。
第2，有如下的串联方式：设置4个感光鼓，分别利用品红色、黄色、青色、黑色的调色剂将各鼓的潜像显影，由此形成品红色产生的调色剂像、黄色产生的调色剂像、青色产生的调色剂像以及黑色产生的调色剂像这4个调色剂像，将形成有这些调色剂像的感光鼓排成1列，将各调色剂像依次转印到纸等记录介质上，在记录介质上叠加，由此重现彩色图像。该方式虽然可以得到良好的图像，但4个感光鼓和设于每个感光鼓上的带电机构和显影机构成为排成1列的状态，装置大型化且变得昂贵。
图2显示了串联方式的图像形成装置的打印部的构成实例。将由感光体鼓1、带电辊2、显影辊3、显影刮板4、调色剂供给辊5以及清洁刮板6构成的打印单元与黄色Y、品红色M、青色C、黑色B的各调色剂相对应排列4个，被驱动辊(驱动部件)9循环驱动，而将调色剂依次转印到通过转印输送皮带10输送的用纸上，形成彩色图像。转印输送皮带的带电和除电分别由带电辊7和除电辊8进行。另外，在用于将用纸吸附到皮带上的用纸带电中使用吸附辊(未图示)。通过这些对策，可以抑制臭氧的发生。在吸附辊中，在将用纸从输送通路乘载到转印输送皮带上的同时，进行向转印输送皮带的静电吸附。另外，转印后的用纸分离是通过降低转印电压而减弱用纸与转印输送皮带的吸附力，可以仅通过曲率分离进行用纸分离。
转印输送皮带10的材料有电阻体和电介体，各有优点和缺点。电阻体皮带保持电荷的时间短，因此在用于串联型的转印时，在转印中的电荷注入少，即便在4色连续的转印中电压的上升也比较小。另外，在接下来的用纸的转印中重复使用时电荷已被释放，不需要电复位。但是，由于电阻值因环境的变化而发生改变，因此存在影响转印效率、易受到用纸厚度和宽度的影响等缺点。
另一方面，在电介体皮带的情况下，所注入的电荷不会自然释放，电荷的注入、释放都必须电控制。但是，由于电荷被稳定地保持，所以用纸的吸附牢靠，可进行高精度的纸输送。由于介电常数对温度湿度的依赖性也小，所以是对环境也比较稳定的转印过程。缺点是，每重复一次转印，都在皮带上积蓄了电荷，因此转印电压变高。
第3，还有如下的转印鼓方式：将纸等记录介质卷绕在转印鼓上，将其旋转4次，每旋转1次依次将感光体上的品红色、黄色、青色、黑色转印到记录介质上，重现彩色图像。通过该方式，可以得到较高的画质，但当记录介质为明信片等厚纸的情况下，难以将其卷绕在上述转印鼓上，存在记录介质种类受到限制的问题。
相对于上述多重显影方式、串联方式以及转印鼓方式，作为可得到良好的画质，且装置不会特别大型化，而且也不特别受记录介质种类限定的方式，提出了中间转印方式。
即，该中间转印方式为：设置由暂时转印保持感光体上的调色剂像的鼓、皮带构成的中间转印部件，在该中间转印部件的周围配置形成了品红色产生的调色剂像、黄色产生的调色剂像、青色产生的调色剂像以及黑色产生的调色剂像的4个感光体，依次将4种颜色的调色剂像转印到中间转印部件上，由此在该中间转印部件上形成彩色图像，将该彩色图像转印到纸等记录介质上。从而，通过叠加4种颜色的调色剂像调整灰度，因此可以得到高画质，且由于不需要像串联方式那样将感光体排成1列，所以装置不会特别大型化，而且也不需要将记录介质卷绕在鼓上，因此记录介质种类也不受限制。
作为通过中间转印方式形成彩色图像的装置，在图3中例示出将无接头带状的中间转印部件用作中间转印部件的图像形成装置。
图3中，11为鼓状的感光体，按照图中箭头方向旋转。该感光体11通过一次带电器12带电，接着，通过图像曝光13消除曝光部分的带电，相应于第1颜色成分的静电潜像形成于该感光体11上，进而静电潜像通过显影器41由第1颜色品红色调色剂M显影，第1颜色品红色调色剂图像形成于感光体11上。接着，该调色剂图像被转印到被驱动辊(驱动部件)30循环驱动而边与感光体11接触边循环旋转的中间转印部件20上。此时，从感光体11向中间转印部件20的转印是在感光体11和中间转印部件20的咬合部通过由电源61施加到中间转印部件20的一次转印偏压进行。在第1颜色品红色调色剂图像被转印到该中间转印部件20上之后，上述感光体11的表面被清洁装置14清扫，感光体11的第1旋转的显影转印操作完成。之后，感光体旋转3次，每旋转一次依次使用显影器42～44，在感光体11上依次形成第2颜色青色调色剂图像、第3颜色黄色调色剂图像、第4颜色黑色调色剂图像，这些调色剂图像每旋转一次被叠加转印到中间转印部件20上，在中间转印部件20上形成对应于目标彩色图像的合成彩色调色剂图像。另外，在图3的装置中，感光体11每旋转一次显影器41～44也依次交替，依次进行品红色调色剂M、青色调色剂C、黄色调色剂Y、黑色调色剂B的显影。
接着，在形成了上述合成彩色调色剂图像的中间转印部件20上抵接转印辊25，从给纸盒19将纸等记录介质26送给到其咬合部。与此同时，由电源29将二次转印偏压施加到转印辊25，将合成彩色调色剂图像从中间转印部件20转印到记录介质26上，加热定影，成为最终图像。将合成彩色调色剂图像转印到记录介质26后的中间转印部件20，通过清洁装置35除去表面的转印残留调色剂，返回到初始状态，准备下次的图像形成。
另外，还有组合了串联方式和中间转印方式的串联中间转印方式。图4中例示出使用无接头带状的串联中间转印部件形成彩色图像的串联中间转印方式的图像形成装置。
在图示的装置中，沿着串联中间转印部件50，依次配置有分别通过黄色、品红色、青色、黑色将感光体鼓52a～52d上的静电潜像显影的第1显影部54a～第4显影部54d，将该串联中间转印部件50按照图中的箭头方向循环驱动，依次转印形成在各显影部54a～54d的感光体鼓52a～52d上的4种颜色的调色剂像，由此在该串联中间转印部件50上形成彩色的调色剂像，将该调色剂像转印到纸等记录介质53上，由此打印出来。
另外，在图中，符号55表示用于循环驱动串联中间转印部件50的驱动辊或张力辊，符号56表示记录介质传送辊，符号57表示记录介质传送装置，符号58表示通过加热等将记录介质上的图像定影的定影装置。另外，符号59表示向串联中间转印部件50施加电压的电源装置(电压施加装置)，该电源装置59在将调色剂像从感光鼓52a～52d转印到上述串联中间转移部件50的情形中和从串联中间转移部件50转印到记录介质53上的情形中，可以反转所施加的电压的正负。
在上述各种图像形成装置中，作为转印输送皮带10、中间转印部件20、串联中间转印部件50等所使用的导电性环带，目前主要使用半导电性的树脂薄膜皮带和具有纤维补强体的橡胶皮带。其中，作为树脂薄膜皮带，例如，在专利文献1中公开了将热塑性聚萘二甲酸烷二醇酯或其与其它热塑性树脂的聚合物合金或共混聚合物用作基材的导电性环带。
此外，在专利文献2中记载有制作无缝皮带的技术，其中，为了得到耐弯曲性等优异并抑制熔融混合时反应导致的物性劣化的无缝皮带，对具有羟基、羧酸和酯键中至少1种的结晶性树脂、和具有羟基、羧酸和酯键中至少1种的非结晶性树脂、以及聚合催化剂加热混合并成形而制成无缝皮带。
专利文献1：日本特开2002-132053号公报(权利要求书等)
专利文献2：日本特开2001-247677号公报(权利要求书等)
发明内容
发明要解决的问题
在上述各种图像形成装置中使用的导电性环带中，要求耐折性、耐安装性优异、在结构方面具有可耐受反复连续使用的高机械强度，并且作为表面光学特性具有高光泽度、且具备良好的导电性及其稳定性。根据上述专利文献1记载的技术，可得到兼具规定的良好的强度、特别是弯曲耐久性和耐蠕变性以及尺寸稳定性的导电性环带，但在该文献中没有考虑光泽度。此外，伴随近年来的图像形成装置的高性能化，期望实现耐久性更优异的导电性环带。
于是，本发明的目的在于提供一种导电性环带以及使用其的图像形成装置，其中，该导电性环带在结构方面具有可耐受反复连续使用的物性、特别是耐安装性，且具有光泽度和导电性也稳定的特性。
解决问题的方法
本发明人进行了深入研究，结果发现通过下述技术方案可解决上述问题，直至完成了本发明。
即，本发明的导电性环带，其为被驱动部件循环驱动，而将通过静电吸附保持的记录介质输送到4种图像形成体上，并将各调色剂像依次转印到该记录介质上的串联方式的转印、输送用导电性环带，其特征在于，
该导电性环带包含由热塑性聚萘二甲酸烷二醇酯树脂和除热塑性聚萘二甲酸烷二醇酯树脂以外的2种以上具有酯键的热塑性树脂形成的基材、和导电性填料，前述热塑性聚萘二甲酸烷二醇酯树脂与2种以上具有酯键的热塑性树脂的重量比在95/5～55/45的范围内，且该2种以上具有酯键的热塑性树脂由包含各至少1种非结晶性树脂和结晶性树脂的树脂组合物组成。
此外，本发明的其它的导电性环带，其为被设置在图像形成体和记录介质之间，并被驱动部件循环驱动，而将形成在前述图像形成体表面的调色剂像暂时转印保持在自身的表面上，并将其转印到记录介质上的中间转印部件用的导电性环带，其特征在于，
该导电性环带包含由热塑性聚萘二甲酸烷二醇酯树脂和除热塑性聚萘二甲酸烷二醇酯树脂以外的2种以上具有酯键的热塑性树脂形成的基材、和导电性填料，前述热塑性聚萘二甲酸烷二醇酯树脂与2种以上具有酯键的热塑性树脂的重量比在95/5～55/45的范围内，且该2种以上具有酯键的热塑性树脂由包含各至少1种非结晶性树脂和结晶性树脂的树脂组合物组成。
此外，本发明的另一导电性环带，其为被设置在4种图像形成体和记录介质之间，并被驱动部件循环驱动，而将形成在前述4种图像形成体表面的调色剂像暂时依次转印保持在自身的表面上，并将其转印到记录介质上的串联中间转印部件用的导电性环带，其特征在于，
该导电性环带包含由热塑性聚萘二甲酸烷二醇酯树脂和除热塑性聚萘二甲酸烷二醇酯树脂以外的2种以上具有酯键的热塑性树脂形成的基材、和导电性填料，前述热塑性聚萘二甲酸烷二醇酯树脂与2种以上具有酯键的热塑性树脂的重量比在95/5～55/45的范围内，且该2种以上具有酯键的热塑性树脂由包含各至少1种非结晶性树脂和结晶性树脂的树脂组合物组成。
本发明中，作为前述热塑性聚萘二甲酸烷二醇酯树脂，适合为聚萘二甲酸丁二醇酯树脂。此外，作为前述具有酯键的结晶性热塑性树脂，优选为聚对苯二甲酸丁二醇酯树脂或聚对苯二甲酸乙二醇酯树脂，作为前述具有酯键的非结晶性热塑性树脂，优选包括二醇改性聚对苯二甲酸烷二醇酯树脂或聚酯系弹性体。进而优选为：前述导电性填料为炭黑，相对于100重量份前述基材添加5～30重量份该填料。导电性环带的体积电阻率适合为102Ω·cm～1013Ω·cm。
此外，本发明的图像形成装置，其特征在于，使用上述本发明的导电性环带。
发明效果
根据本发明，通过采用上述技术方案，可提供一种导电性环带以及使用其的图像形成装置，其中，该导电性环带在结构方面具有可耐受反复连续使用的物性、特别是耐安装性、耐弯曲性，且具有光泽度和导电性也适当的特性。
附图说明
图1为本发明的一具体实施方式的导电性环带的宽度方向截面图。
图2为显示作为本发明图像形成装置的一例的使用转印输送皮带的串联方式的图像形成装置的概略图。
图3为显示作为本发明图像形成装置的其它例的使用中间转印部件的中间转印装置的概略图。
图4为显示作为本发明图像形成装置的其它例的使用串联中间转印部件的串联中间转印装置的概略图。
符号说明：
1、11、52a-52d：感光体鼓
2、7：带电辊
3：显影辊
4：显影刮板
5：调色剂供给辊
6：清洁刮板
8：除电辊
9、30、55：驱动辊(驱动部件)
10：转印输送皮带
12：一次带电器
13：图像曝光
14、35：清洁装置
19：给纸盒
20：中间转印部件
25：转印辊
26、53：记录介质
29、61：电源
41、42、43、44：显影器
50：串联中间转印部件
54a～54d：第1显影部～第4显影部
56：记录介质传送辊
57：记录介质传送装置
58：定影装置
59：电源装置(电压施加装置)
具体实施方式
以下对本发明适合的实施方式进行详细说明。
在导电性环带中，通常存在有接缝的导电性环带和无接缝的导电性环带(所谓的无缝皮带)，在本发明中可以是任何一种。优选无缝皮带。如前所述，本发明的导电性环带可以作为串联方式、中间转印方式和串联中间转印方式的转印部件等使用。
本发明的导电性环带例如为图2中参照符号10所示的转印输送皮带时，通过驱动辊9等驱动部件被驱动，调色剂被依次转印到随之被输送的记录介质上，形成彩色图像。
此外，本发明的导电性环带例如为图3中参照符号20所示的中间转印部件时，使其被驱动辊30等驱动部件循环驱动，并且配置在感光体鼓(潜像保持体)11和纸等记录介质26之间，由此暂时转印保持形成在前述感光体鼓11表面的调色剂像，接着将其转印到记录介质26上。另外，图3的装置，如上所述，是通过中间转印方式进行彩色印刷的。
进而，本发明的导电性环带例如为图4中参照符号50所示的串联中间转印部件时，配置在具备感光体鼓52a～52d的显影部54a～54d和纸等记录介质53之间，被驱动辊55等驱动部件循环驱动，暂时转印保持形成在各感光体鼓52a～52d表面的4色调色剂像，接着将其转印到记录介质53上，从而形成彩色图像。
本发明的导电性环带在如下方面具有特征，即，其包括由(a)热塑性聚萘二甲酸烷二醇酯树脂和除此以外的2种以上的(b)具有酯键的热塑性树脂形成的基材、和导电性填料，(a)热塑性聚萘二甲酸烷二醇酯树脂与2种以上的(b)具有酯键的热塑性树脂的重量比在95/5～55/45的范围内，且2种以上的(b)具有酯键的热塑性树脂由包含各至少1种非结晶性树脂和结晶性树脂的树脂组合物组成。
选择其它的(b)具有酯键的热塑性树脂来作为在基材中与(a)热塑性聚萘二甲酸烷二醇酯树脂一起使用的树脂的理由在于：通过使用同样是酯系的树脂，可提高与(a)热塑性聚萘二甲酸烷二醇酯树脂的相容性，由此可实现皮带表面的高光泽。此外，通过将这些(a)/(b)的重量比规定在上述范围，可维持表面性、耐弯曲性和耐蠕变性能，且通过限定结晶性酯树脂的配合，进一步可实现耐弯曲性的提高，而且，通过配合非结晶性酯树脂，可控制表面电阻、提高耐安装性。本发明中，发现通过将(a)热塑性聚萘二甲酸烷二醇酯树脂与2种以上(b)具有酯键的热塑性树脂组合使用、并将这些的重量比限定为规定值、进而使作为(b)具有酯键的热塑性树脂包含结晶性的树脂和非结晶性的树脂这两者，从而可飞跃性且平衡良好地提高皮带物性。
本发明中，在基材所使用的(a)热塑性聚萘二甲酸烷二醇酯树脂，具体地说，可列举聚萘二甲酸丁二醇酯(PBN)树脂、聚萘二甲酸乙二醇酯(PEN)树脂等，优选为PBN树脂。这些树脂可从市场上买到，例如，作为PBN树脂，可使用帝人化成(株)制造的TQB-OT等。
此外，作为(b)具有酯键的热塑性树脂之中，作为结晶性热塑性树脂，具体地说，可优选列举例如聚对苯二甲酸丁二醇酯(PBT)树脂和聚对苯二甲酸乙二醇酯(PET)树脂，作为非结晶性热塑性树脂，可适合使用二醇改性聚对苯二甲酸烷二醇酯树脂、例如二醇改性聚对苯二甲酸乙二醇酯(PET-G)树脂、二醇改性聚对苯二甲酸环己二甲醇酯(PCT-G)树脂等、以及聚酯系弹性体。作为聚酯系弹性体，可适合使用在硬链段和软链段中使用聚酯得到的聚酯-聚酯型弹性体，以及在硬链段中使用聚酯、在软链段中使用聚醚得到的聚酯-聚醚型弹性体这两者。另外，聚酯系弹性体的硬链段通常使用PBT或PBN作为主成份，本发明中可使用任意一种。这些树脂还可从市场上买到，作为PBT树脂，可列举例如TORAY(株)制造的TORAYCON 1401，作为二醇改性聚对苯二甲酸烷二醇酯树脂，可列举例如EASTMAN CHEMICAL COMPANY制造的6763等。此外，作为聚酯系弹性体，可列举帝人化成(株)制造的nubelanP4110、nubelan B4063、东洋纺(株)制造的PELPRENE S-1001、PELPRENE EN-1000等。
此外，作为导电性填料，可无特别限制地使用电子导电剂、离子导电剂等。其中，作为电子导电剂，具体地说可列举例如科琴黑、乙炔黑等导电性炭，SAF、ISAF、HAF、FEF、GPF、SRF、FT、MT等橡胶用炭，实施了氧化处理等的彩色(墨水)用炭、热解炭、天然石墨、人造石墨、掺杂有锑的氧化锡、氧化钛、氧化锌、镍、铜、银、锗等的金属和金属氧化物，聚苯胺、聚吡咯、聚乙炔等导电性聚合物，炭须晶、石墨须晶、碳化钛须晶、导电性钛酸钾须晶、导电性钛酸钡须晶、导电性氧化钛须晶、导电性氧化锌须晶等导电性须晶等。此外，作为离子导电剂，具体地说可列举例如四乙基铵、四丁基铵、十二烷基三甲基铵、十六烷基三甲基铵、苄基三甲基铵、改性脂肪酸二甲基乙基铵等的高氯酸盐，氯酸盐、盐酸盐、溴酸盐、碘酸盐、氢氟硼酸盐、硫酸盐、乙基硫酸盐、羧酸盐、磺酸盐等的铵盐，锂、钠、钾、钙、镁等碱金属、碱土类金属的高氯酸盐、氯酸盐、盐酸盐、溴酸盐、碘酸盐、氢氟硼酸盐、硫酸盐、三氟甲基硫酸盐、磺酸盐等。
这些导电性填料可单独使用1种，也可适当组合2种以上使用，例如还可将电子导电剂与离子导电剂组合使用，此时，对被施加电压的变化和环境变化也可稳定地表现导电性。
电子导电剂的配合量相对于100重量份基材通常为100重量份以下，例如1～100重量份、特别是1～80重量份、尤其是10～50重量份。此外，离子导电剂的配合量相对于100重量份树脂通常为0.01～10重量份、特别为0.05～5重量份的范围。本发明中，特别优选使用炭黑作为导电性填料，并相对于100重量份基材添加5～30重量份炭墨。
在不损害本发明效果的范围内，在本发明的导电性环带中除了上述导电性填料以外还可以适当添加其它功能性成分，例如，可以适当混合各种填充材料、偶联剂、抗氧化剂、润滑剂、表面处理剂、颜料、紫外线吸收剂、防静电剂、分散剂、中和剂、发泡剂、交联剂等。此外，还可以添加着色剂进行着色。
本发明的导电性环带的厚度是根据转印输送皮带或中间转印部件等的形态适当选定的，优选为50～200μm的范围内。另外，作为其表面粗糙度，优选JIS 10点平均粗糙度Rz为10μm以下，特别优选为6μm以下，进一步优选为3μm以下。此外，体积电阻率优选调整为102Ω·cm～1013Ω·cm的范围内左右。
进而，如图1的虚线所示，本发明的导电性环带中，还可以在与图2的图像形成装置的驱动辊9或图3的驱动辊30等驱动部件相接触一侧的面上形成与形成于该驱动部件的嵌合部(未图示)相嵌合的嵌合部，本发明的导电性环带通过设置这样的嵌合部并使其与设置于驱动部件的嵌合部(未图示)嵌合运行，能够防止皮带在其宽度方向上的偏移。
该情况下，前述嵌合部没有特别限定，优选如图1所示那样，优选为制成沿皮带的圆周方向(旋转方向)连续的凸条，使其与在驱动辊等驱动部件的圆周面上沿着圆周方向形成的沟槽相嵌合。
另外，图1(a)中显示出设置1根连续的凸条作为嵌合部的例子，但该嵌合部也可以将多个凸部沿皮带圆周方向(旋转方向)排成一列突出设置，或者设置2根以上嵌合部(图1(b))，还可以在皮带的宽度方向中央部位设置嵌合部。另外，嵌合部还可以不是图1所示的凸条，而是沿着皮带的圆周方向(旋转方向)设置沟槽，使其与在前述驱动辊等驱动部件的圆周面上沿着圆周方向形成的凸条相嵌合。
另外，作为使用本发明导电性环带的本发明的图像形成装置，可以例示如图2所示的串联方式的装置、如图3所示的中间转印方式的装置或者如图4所示的串联中间转印方式的装置，但并不限定于这些装置。另外，如图3所示的装置的情形中，可以由电源61向使本发明中间转印部件20旋转的驱动辊或驱动齿轮适当施加电压，此时的电压可以适当选择施加条件，如仅施加直流或在直流中叠加交流施加等。
实施例
以下，使用实施例更加详细地说明本发明。
实施例1-11和比较例1、2
使用双螺杆混炼机分别熔融混炼下述表1、2中所示的各配合成分，再使用环状模具将所得混炼物挤出成型，从而制得具有内径220mm、厚100μm、宽250mm尺寸的各实施例和比较例的导电性环带。按照以下顺序对所得各皮带进行各测定，进行综合评价，耐实际使用的记为“○”、不耐实际使用的记为“×”。
<体积电阻率的测定>
在温度23℃、相对湿度50％下，测定装置使用ADVANTEST公司制造的在电阻计R8340A上连接有样品室R12704A的装置，对测定电压500V下的皮带的体积电阻率和测定电压1000V下的皮带的表面电阻进行测定。
<耐安装性>
在温度30℃、相对湿度85％的环境下，在对各皮带拉伸负荷的状态下放置24小时，然后，安装到实际装置上使其运行，通过此时的运行性来评价耐安装性。运行性没有变化的情形记为“○”、产生强烈蜿蜒或空转的情形记为“×”。
<耐折次数>
使用东洋精机(株)的MIT耐揉疲劳试验机测定耐折弯次数，该结果用将比较例1作为250的指数来示出。数值越大，结果越良好。
<光泽度>
使用堀场制作所制作的便携光泽计IG-320型进行测定。
以上的各测定结果示于下述表1、2中。
表1
1)热塑性聚萘二甲酸烷二醇酯树脂A：PBN(帝人化成(株)制造)、TQB-OT
2)含有酯键的热塑性树脂B：PBT(TORAY(株)制造)、TORAYCON 1401(结晶性)
3)含有酯键的热塑性树脂C：PET-G、EASTMANCHEMICAL COMPANY制造、6763(非结晶性)
4)含有酯键的热塑性树脂D：PCT-G、EASTMANCHEMICAL COMPANY制造(非结晶性)
5)炭黑：电气化学工业(株)制造、DENKA BLACK
表2
6)含有酯键的热塑性树脂E：聚酯系弹性体(聚酯-聚酯型)：帝人化成(株)制造、商品名NUBELAN P4110(非结晶性)
7)含有酯键的热塑性树脂F：聚酯系弹性体(聚酯-聚酯型)：东洋纺(株)制造、商品名PELPRENE S-1001(非结晶性)
8)含有酯键的热塑性树脂G：聚酯系弹性体(聚酯-聚醚型)：帝人化成(株)制造、商品名NUBELAN B 4063(非结晶性)
9)含有酯键的热塑性树脂H：聚酯系弹性体(聚酯-聚醚型)：东洋纺(株)制造、商品名PELPRENE EN-1000等(非结晶性)
由上述表1、2的结果可确认，作为基材，以规定重量比使用热塑性聚萘二甲酸烷二醇酯树脂以及具有酯键的非结晶性热塑性树脂和结晶性热塑性树脂并对其添加导电性填料，由此得到的各实施例的皮带中，得到导电性、耐安装性、耐折性和光泽度均良好的性能。与此相对，不满足规定重量比的比较例1和不含有非结晶性热塑性树脂的比较例2中，得到各评价项目与实施例相比均不充分的结果。
Claims (21)
1.串联方式的转印、输送用导电性环带，其被驱动部件循环驱动，而将通过静电吸附保持的记录介质输送到4种图像形成体上，并将各调色剂像依次转印到该记录介质上，其特征在于，
该导电性环带包含由热塑性聚萘二甲酸烷二醇酯树脂和除热塑性聚萘二甲酸烷二醇酯树脂以外的2种以上具有酯键的热塑性树脂形成的基材、和导电性填料，所述热塑性聚萘二甲酸烷二醇酯树脂和2种以上具有酯键的热塑性树脂的重量比在95/5～55/45的范围内，且该2种以上具有酯键的热塑性树脂由包含各至少1种非结晶性树脂和结晶性树脂的树脂组合物组成，其中，作为所述热塑性聚萘二甲酸烷二醇酯树脂，包括聚萘二甲酸丁二醇酯树脂。
2.根据权利要求1所述的导电性环带，其中，作为所述具有酯键的结晶性热塑性树脂，包括聚对苯二甲酸丁二醇酯树脂或聚对苯二甲酸乙二醇酯树脂。
3.根据权利要求1所述的导电性环带，其中，作为所述具有酯键的非结晶性热塑性树脂，包括二醇改性聚对苯二甲酸烷二醇酯树脂。
4.根据权利要求1所述的导电性环带，其中，作为所述具有酯键的非结晶性热塑性树脂，包括聚酯系弹性体。
5.根据权利要求1所述的导电性环带，其中，所述导电性填料为炭黑，相对于100重量份所述基材添加5～30重量份该填料。
6.根据权利要求1所述的导电性环带，其体积电阻率为102Ω·cm～1013Ω·cm。
7.图像形成装置，其特征在于，使用权利要求1所述的导电性环带。
8.中间转印部件用的导电性环带，其被设置在图像形成体和记录介质之间，并被驱动部件循环驱动，而将形成在所述图像形成体表面的调色剂像暂时转印保持在自身的表面上，并将其转印到记录介质上，其特征在于，
该导电性环带包含由热塑性聚萘二甲酸烷二醇酯树脂和除热塑性聚萘二甲酸烷二醇酯树脂以外的2种以上具有酯键的热塑性树脂形成的基材、和导电性填料，所述热塑性聚萘二甲酸烷二醇酯树脂和2种以上具有酯键的热塑性树脂的重量比在95/5～55/45的范围内，且该2种以上具有酯键的热塑性树脂由包含各至少1种非结晶性树脂和结晶性树脂的树脂组合物组成，其中，作为所述热塑性聚萘二甲酸烷二醇酯树脂，包括聚萘二甲酸丁二醇酯树脂。
9.根据权利要求8所述的导电性环带，其中，作为所述具有酯键的结晶性热塑性树脂，包括聚对苯二甲酸丁二醇酯树脂或聚对苯二甲酸乙二醇酯树脂。
10.根据权利要求8所述的导电性环带，其中，作为所述具有酯键的非结晶性热塑性树脂，包括二醇改性聚对苯二甲酸烷二醇酯树脂。
11.根据权利要求8所述的导电性环带，其中，作为所述具有酯键的非结晶性热塑性树脂，包括聚酯系弹性体。
12.根据权利要求8所述的导电性环带，其中，所述导电性填料为炭黑，相对于100重量份所述基材添加5～30重量份该填料。
13.根据权利要求8所述的导电性环带，其体积电阻率为102Ω·cm～1013Ω·cm。
14.图像形成装置，其特征在于，使用权利要求8所述的导电性环带。
15.串联中间转印部件用的导电性环带，其被设置在4种图像形成体和记录介质之间，并被驱动部件循环驱动，而将形成在所述4种图像形成体表面的调色剂像暂时依次转印保持在自身的表面上，并将其转印到记录介质上，其特征在于，
该导电性环带包含由热塑性聚萘二甲酸烷二醇酯树脂和除热塑性聚萘二甲酸烷二醇酯树脂以外的2种以上具有酯键的热塑性树脂形成的基材、和导电性填料，所述热塑性聚萘二甲酸烷二醇酯树脂与2种以上具有酯键的热塑性树脂的重量比在95/5～55/45的范围内，且该2种以上具有酯键的热塑性树脂由包含各至少1种非结晶性树脂和结晶性树脂的树脂组合物组成，其中，作为所述热塑性聚萘二甲酸烷二醇酯树脂，包括聚萘二甲酸丁二醇酯树脂。
16.根据权利要求15所述的导电性环带，其中，作为所述具有酯键的结晶性热塑性树脂，包括聚对苯二甲酸丁二醇酯树脂或聚对苯二甲酸乙二醇酯树脂。
17.根据权利要求15所述的导电性环带，其中，作为所述具有酯键的非结晶性热塑性树脂，包括二醇改性聚对苯二甲酸烷二醇酯树脂。
18.根据权利要求15所述的导电性环带，其中，作为所述具有酯键的非结晶性热塑性树脂，包括聚酯系弹性体。
19.根据权利要求15所述的导电性环带，其中，所述导电性填料为炭黑，相对于100重量份所述基材添加5～30重量份该填料。
20.根据权利要求15所述的导电性环带，其体积电阻率为102Ω·cm～1013Ω·cm。
21.图像形成装置，其特征在于，使用权利要求15所述的导电性环带。