CN100569814C - 共聚白乳胶 - Google Patents

共聚白乳胶 Download PDF

Info

Publication number
CN100569814C
CN100569814C CNB2007100305067A CN200710030506A CN100569814C CN 100569814 C CN100569814 C CN 100569814C CN B2007100305067 A CNB2007100305067 A CN B2007100305067A CN 200710030506 A CN200710030506 A CN 200710030506A CN 100569814 C CN100569814 C CN 100569814C
Authority
CN
China
Prior art keywords
agent
white latex
defoamer
value conditioning
conditioning agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2007100305067A
Other languages
English (en)
Other versions
CN101130586A (zh
Inventor
林玉珠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2007100305067A priority Critical patent/CN100569814C/zh
Publication of CN101130586A publication Critical patent/CN101130586A/zh
Application granted granted Critical
Publication of CN100569814C publication Critical patent/CN100569814C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及粘合剂技术领域，具体是一种新型共聚白乳胶，其配料包括：聚乙烯醇、去离子水、碳酸氢钠、醋酸乙烯、丙烯酸丁酯、叔碳酸乙烯酯、分散剂、消泡剂、过硫酸铵、增塑剂、PH值调节剂，聚合反应在搪玻璃反应釜中进行，首先将聚乙烯醇、去离子水投入反应釜中，升温使其溶解；降温后加入分散剂、消泡剂；再加入反应单体在常压、温度为72-80℃、搅拌状态下，进行聚合反应；然后加入适量PH值调节剂，使PH在6.0-7.0之间；最后加入增塑剂DBP，构成本产品。具有粘接性能好、胶膜透明、安全环保和节约资源等优点。

Description

共聚白乳胶
技术领域：
本发明涉及粘合剂技术领域，具体是一种新型共聚白乳胶。
背景技术：
现有的白乳胶，大多以聚乙烯醇、醋酸乙烯、甲醛、盐酸等为原料，经聚合反应而制得，具有工艺成熟、成本较低等特点。但其不足之处是：1、产品中含有大量有毒的游离甲醛，对人身健康有较大的危害性；2、产品固含量低、冻融稳定性能差、耐热性能不高、抗蠕变性能差、干燥速度慢、耐水性能较差。
随着人民生活质量的不断提高和科技进步，人们对胶粘剂产品的需要和选择越来越苛刻，那些性能好、质量高、环保安全和节能产品将会倍受人们青睐，乳液的发展趋高性能化，多功能化和环保节能化，通过共聚、共混、保护胶体改性来获得各种高性能产品，以满足不同领域的需求。共聚改性复合型、高含量乳液将成为新的发展方向。
发明内容：
本发明的目的在于克服现有白乳胶的不足，提供一种不含游离甲醛的且性能优异的新型共聚白乳胶。
本发明目的的实现，是在配方中加入改性单体，使改性单体与醋酸乙烯在催化剂作用下发生共聚，同时，采用聚乙烯醇作保护胶体，制得新型共聚白乳胶。
本发明，其配料重量比为：聚乙烯醇：4.0-6.0％；去离子水：32.0-45.0％；碳酸氢钠：0.3-0.5％；醋酸乙烯35.0-50.0％；丙烯酸丁酯：5.0-6.0％；叔碳酸乙烯酯(VeoVa)：1.5-2.0％；分散剂0.1-0.2％；消泡剂：2.5-3.5％；过硫酸铵0.2-0.6％；增塑剂DBP 2.5-5.0％；PH值调节剂适量，其合成工艺为：
A、将聚乙烯醇、去离子水投入搪玻璃反应釜中，升温至95℃溶解完全；
B、降温至68-72℃时，加入碳酸氢钠、分散剂、消泡剂，搅拌0.5h；
C、加入醋酸乙烯、丙烯酸丁酯、叔碳酸乙烯酯(VeoVa)和过硫酸铵，在常压、温度为72-80℃、搅拌状态下，进行聚合反应8-10h；
D、加入适量PH值调节剂，使PH在6.0-7.0之间；
E、加入增塑剂DBP，搅拌均匀，降温至45℃以下；
F、成品包装。
本发明，所述分散剂可以选用5040分散剂；所述消泡剂可以选用有机硅消泡剂；所述PH值调节剂可以选用AMP-95添加剂。
本发明，具有如下特点：
1、配方中加入改性单体——丙烯酸丁酯及叔碳酸乙烯酯(VeoVa)，实现多元化共聚，提高乳液的稳定性，获得优良性能共聚乳液；
2、通过改性单体的加入，有效降低乳液玻璃化温度；
3、固含量高，结晶干燥速度快；
4、粘接强度高，增加了极性基团，提高化学和吸附能力，耐水性能优异；
5、具有优良的耐老化性能。
本发明与传统白乳胶比较，其主要技术指标如下表所示：
  序号   传统白乳胶   本发明
  1   固含量低，一般为25-40％   固含量达60％
  2   固化速度较慢   固化速度快
  3   耐水性差，尤其不耐沸水，易吸潮，潮湿环境易开胶   耐水性能优异，在潮湿环境保持优良粘接性能，被粘物在沸水连续煮4小时不开胶
  4   耐热性差，软化点低(40-80℃)  耐热性能好，软化点高(100-120℃)
  5  冻融稳定性差，5℃以下容易冻结   冻融稳定性好，-5℃连续冻融48小时无变化
具体实施方式：
一种新型共聚白乳胶，其配料为：聚乙烯醇：5kg；去离子水：40kg；碳酸氢钠：0.4kg；醋酸乙烯40kg；丙烯酸丁酯：5.5kg；叔碳酸乙烯酯(VeoVa)：2.0kg；5040分散剂0.2kg；有机硅消泡剂：2.8kg；过硫酸铵0.4kg；增塑剂DBP 3.7kg；AMP-95添加剂适量，其合成工艺为：
A、将聚乙烯醇、去离子水投入搪玻璃反应釜中，升温至95℃使聚乙烯醇溶解；
B、降温至68-72℃时，加入碳酸氢钠、5040分散剂、有机硅消泡剂，搅拌0.5h；
C、加入醋酸乙烯、丙烯酸丁酯、叔碳酸乙烯酯(VeoVa)和过硫酸铵，在常压、温度为72-80℃、搅拌状态下，进行聚合反应8-10h；
D、加入适量AMP-95添加剂(AMP-95为2-氨基-2甲基-1-丙醇，作为PH值调节剂)，使PH值为6.5；
E、加入增塑剂DBP(DBP为邻苯二甲酸二丁酯)，搅拌均匀，降温至45℃以下；
F、成品包装。
本新型共聚白乳胶具有粘接性能好、胶膜透明、安全环保和节约资源等许多优点，它克服了传统聚醋酸乙烯乳液固含量低、冻融稳定性能差、耐热性能不高、抗蠕变性能差、干燥速度慢、耐水性不好等方面的缺陷。另外传统聚醋酸乙烯乳液还含有游离甲醛或/和有机溶剂等有害物质，给人们的生活及环境带来负面影响。新型共聚白乳胶在聚合过程加入一些具有特定功能的共聚单体，使用之后与醋酸乙烯酯共聚，得到共聚乳液，共聚改性可在聚合物主链上引入反应性官能团，实现“内增塑”和“外亲和”；改性单体非常活泼，与醋酸乙烯反应后，耐水性优越，同时采用性能伏越的聚乙烯醇(PVA)作保护胶体，使其具有良好的水溶性，乳化效果好，形成的乳液稳定性好，对乳液的干湿强度明显提高，同时也大大提高其化学吸附能力，改善其粘接综合性能。

Claims (5)

1、一种共聚白乳胶，其配料重量比为：聚乙烯醇：4.0-6.0％；去离子水：32.0-45.0％；碳酸氢钠：0.3-0.5％；醋酸乙烯35.0-50.0％；丙烯酸丁酯：5.0-6.0％；叔碳酸乙烯酯：1.5-2.0％；分散剂0.1-0.2％；消泡剂：2.5-3.5％；过硫酸铵0.2-0.6％；增塑剂邻苯二甲酸二丁酯2.5-5.0％；PH值调节剂适量，其合成工艺为：
A、将聚乙烯醇、去离子水投入搪玻璃反应釜中，升温至95℃溶解完全；
B、降温至68-72℃时，加入分散剂、消泡剂，搅拌0.5h；
C、加入碳酸氢钠、醋酸乙烯、丙烯酸丁酯、叔碳酸乙烯酯和过硫酸铵，在常压、温度为72-80℃、搅拌状态下，进行聚合反应8-10h；
D、加入适量PH值调节剂，使PH在6.0-7.0之间；
E、加入增塑剂邻苯二甲酸二丁酯，搅拌均匀，降温至45℃以下；
F、成品包装。
2、根据权利要求1所述的共聚白乳胶，其特征为：所述分散剂为5040分散剂。
3、根据权利要求1或2所述的共聚白乳胶，其特征为：所述消泡剂为有机硅消泡剂。
4、根据权利要求1或2所述的共聚白乳胶，其特征为：所述PH值调节剂为AMP-95添加剂。
5、根据权利要求3所述的共聚白乳胶，其特征为：所述PH值调节剂为AMP-95添加剂。
CNB2007100305067A 2007-09-18 2007-09-18 共聚白乳胶 Expired - Fee Related CN100569814C (zh)