CN102464962A - 一种白乳胶的生产工艺 - Google Patents

一种白乳胶的生产工艺 Download PDF

Info

Publication number
CN102464962A
CN102464962A CN2010105384067A CN201010538406A CN102464962A CN 102464962 A CN102464962 A CN 102464962A CN 2010105384067 A CN2010105384067 A CN 2010105384067A CN 201010538406 A CN201010538406 A CN 201010538406A CN 102464962 A CN102464962 A CN 102464962A
Authority
CN
China
Prior art keywords
mixture
weight
multipolymer
temperature
vinyl acetate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010105384067A
Other languages
English (en)
Inventor
吕继学
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2010105384067A priority Critical patent/CN102464962A/zh
Publication of CN102464962A publication Critical patent/CN102464962A/zh
Pending legal-status Critical Current

Abstract

本发明是一种白乳胶的生产工艺，其特征在于，其步骤如下：取聚乙烯醇加水于93-95℃溶解，得混合物，其中水占混合物重量的60-70%；向混合物中滴加醋酸乙烯，于83-85℃下发生共聚反应，得共聚物，其中醋酸乙烯占混合物重量的30-40%；向共聚物中加入共聚物重量的0.04-0.05‰ 苯甲酸钠、0.04-0.05‰ 的抗氧剂1010和14-15%沙素蜡进行反应，反应温度为97-98℃，所述的沙素蜡在加入前先于195-205℃下溶解；反应结束即得成品。本发明生产工艺简单，可操作性强。用本发明工艺制备出的白乳胶的胶体均匀，使用时不会有气泡产生，而且粘接性能高，使用效果好，可适用范围广。

Description

一种白乳胶的生产工艺
技术领域
 本发明涉及一种胶，特别是一种白乳胶的生产工艺。
背景技术
现有技术中的白乳胶的生产工艺大多比较复杂，且制备出的白乳胶存在胶体不均匀，使用时容易产生气泡，而且粘接性能不强，影响了其使用效果及范围。
发明内容
本发明所要解决的技术问题是针对现有技术的不足，提供一种新的、工艺简单、可操作性强的白乳胶的生产工艺。
本发明所要解决的技术问题是通过以下的技术方案来实现的。本发明是一种白乳胶的生产工艺，其特点是，其步骤如下：
（1）取聚乙烯醇加水于93-95℃溶解，得混合物，其中水占混合物重量的60-70%；
（2）向混合物中滴加醋酸乙烯，于83-85℃下发生共聚反应，得共聚物，其中醋酸乙烯占混合物重量的30-40%；
（3）向共聚物中加入共聚物重量的0.04-0.05‰ 苯甲酸钠、0.04-0.05‰ 的抗氧剂1010和14-15%沙素蜡进行反应，反应温度为97-98℃，所述的沙素蜡在加入前先于195-205℃下溶解；反应结束即得成品。
本发明所要解决的技术问题还可以通过以下的技术方案来进一步实现。以上所述的白乳胶的生产工艺，其特点是，其步骤如下：
（1）取聚乙烯醇加水于94℃溶解，得混合物，其中水占混合物重量的65%；
（2）向混合物中滴加醋酸乙烯，于84℃下发生共聚反应，得共聚物，其中醋酸乙烯占混合物重量的35%；
（3）向共聚物中加入共聚物重量的0.045‰ 苯甲酸钠、0.045‰ 的抗氧剂1010和14.5%沙素蜡进行反应，反应温度为97.5℃，所述的沙素蜡在加入前先于198℃下溶解；反应结束即得成品。
与现有技术相比，本发明生产工艺简单，可操作性强。用本发明工艺制备出的白乳胶的胶体均匀，使用时不会有气泡产生，而且粘接性能高，使用效果好，可适用范围广。
具体实施方式
以下进一步描述本发明的具体技术方案，以便于本领域的技术人员进一步地理解本发明，而不构成对其权利的限制。
实施例1。一种白乳胶的生产工艺，其步骤如下：
（1）取聚乙烯醇加水于93℃溶解，得混合物，其中水占混合物重量的60%；
（2）向混合物中滴加醋酸乙烯，于83℃下发生共聚反应，得共聚物，其中醋酸乙烯占混合物重量的30%；
（3）向共聚物中加入共聚物重量的0.04‰ 苯甲酸钠、0.04‰ 的抗氧剂1010和14%沙素蜡进行反应，反应温度为97℃，所述的沙素蜡在加入前先于195℃下溶解；反应结束即得成品。
实施例2。一种白乳胶的生产工艺，其步骤如下：
（1）取聚乙烯醇加水于95℃溶解，得混合物，其中水占混合物重量的70%；
（2）向混合物中滴加醋酸乙烯，于85℃下发生共聚反应，得共聚物，其中醋酸乙烯占混合物重量的40%；
（3）向共聚物中加入共聚物重量的0.05‰ 苯甲酸钠、0.05‰ 的抗氧剂1010和15%沙素蜡进行反应，反应温度为98℃，所述的沙素蜡在加入前先于205℃下溶解；反应结束即得成品。
实施例3。一种白乳胶的生产工艺，其步骤如下：
（1）取聚乙烯醇加水于94℃溶解，得混合物，其中水占混合物重量的65%；
（2）向混合物中滴加醋酸乙烯，于84℃下发生共聚反应，得共聚物，其中醋酸乙烯占混合物重量的35%；
（3）向共聚物中加入共聚物重量的0.045‰ 苯甲酸钠、0.045‰ 的抗氧剂1010和14.5%沙素蜡进行反应，反应温度为97.5℃，所述的沙素蜡在加入前先于198℃下溶解；反应结束即得成品。

Claims (2)

1.一种白乳胶的生产工艺，其特征在于，其步骤如下：
（1）取聚乙烯醇加水于93-95℃溶解，得混合物，其中水占混合物重量的60-70%；
（2）向混合物中滴加醋酸乙烯，于83-85℃下发生共聚反应，得共聚物，其中醋酸乙烯占混合物重量的30-40%；
（3）向共聚物中加入共聚物重量的0.04-0.05‰ 苯甲酸钠、0.04-0.05‰ 的抗氧剂1010和14-15%沙素蜡进行反应，反应温度为97-98℃，所述的沙素蜡在加入前先于195-205℃下溶解；反应结束即得成品。
2.根据权利要求1所述的白乳胶的生产工艺，其特征在于，其步骤如下：
（1）取聚乙烯醇加水于94℃溶解，得混合物，其中水占混合物重量的65%；
（2）向混合物中滴加醋酸乙烯，于84℃下发生共聚反应，得共聚物，其中醋酸乙烯占混合物重量的35%；
（3）向共聚物中加入共聚物重量的0.045‰ 苯甲酸钠、0.045‰ 的抗氧剂1010和14.5%沙素蜡进行反应，反应温度为97.5℃，所述的沙素蜡在加入前先于198℃下溶解；反应结束即得成品。
CN2010105384067A 2010-11-10 2010-11-10 一种白乳胶的生产工艺 Pending CN102464962A (zh)