CN100519460C - 一种水泥助磨剂及其制备方法 - Google Patents

一种水泥助磨剂及其制备方法 Download PDF

Info

Publication number
CN100519460C
CN100519460C CNB2007100550270A CN200710055027A CN100519460C CN 100519460 C CN100519460 C CN 100519460C CN B2007100550270 A CNB2007100550270 A CN B2007100550270A CN 200710055027 A CN200710055027 A CN 200710055027A CN 100519460 C CN100519460 C CN 100519460C
Authority
CN
China
Prior art keywords
grinding aid
cement
stirred
cement grinding
percent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2007100550270A
Other languages
English (en)
Other versions
CN101125742A (zh
Inventor
白文利
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LYOYANG WANSHUN BUILDING MATERIALS CO Ltd
Original Assignee
LYOYANG WANSHUN BUILDING MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LYOYANG WANSHUN BUILDING MATERIALS CO Ltd filed Critical LYOYANG WANSHUN BUILDING MATERIALS CO Ltd
Priority to CNB2007100550270A priority Critical patent/CN100519460C/zh
Publication of CN101125742A publication Critical patent/CN101125742A/zh
Application granted granted Critical
Publication of CN100519460C publication Critical patent/CN100519460C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种水泥助磨剂及其制备方法,其原料由10%~30%三乙醇胺、12%~30%三异丙醇胺、5%~20%乙二醇、3%~10%丙二醇、15%~40%水、1%~5%十二烷基苯磺酸钠、3%~10%木质素、2%~5%无水硫酸钠组成;在反应釜中注水,加热至40~50℃备用;将十二烷基苯磺酸钠加入,搅拌15分钟;加入无水硫酸钠搅拌10分钟,再加入木质素搅拌30分钟;将反应釜中的材料用150目筛网过滤;加入乙二醇、丙二醇搅拌20分钟;加入三乙醇胺、三异丙醇胺搅拌30分钟,即得到助磨剂产品。该水泥助磨剂能够提高粉磨效率,提高水泥早期和后期强度,减少水泥成本。

Description

一种水泥助磨剂及其制备方法
技术领域
本发明属于水泥添加剂技术领域,尤其是涉及一种水泥助磨剂及其制备方法。
背景技术
目前,在水泥工业领域,水泥助磨剂在世界各国已被广泛的应用。在水泥生产过程中,破碎和粉磨环节是整个生产环节中消耗能源最高的,也是能源利用率最低的,粉磨工序中易产生饱磨、粘球、挂壁而影响粉磨效率,因此在粉磨过程中添加助磨剂,能够提高水泥的粉磨效率,降低粉磨功耗和粉磨成本,增加水泥的流动性,提高水泥的质量;而目前市场上的大多数水泥助磨剂,有些虽然能够提高水泥产量,但在水泥质量和性能方面不够理想。
发明内容
为了克服现有技术中存在的缺陷,本发明的目的是提供一种水泥助磨剂及其制备方法,其不仅能够提高水泥的台时产量,而且提高水泥的强度,节能降耗,降低成本。
为实现上述发明目的,本发明采用如下技术方案:
所述的水泥助磨剂,其原料由三乙醇胺、三异丙醇胺、乙二醇、丙二醇、水、十二烷基苯磺酸钠、木质素、无水硫酸钠组成,各组分的重量百分比为:三乙醇胺10%~30%,三异丙醇胺12%~30%,乙二醇5%~20%,丙二醇3%~10%,水15%~40%,十二烷基苯磺酸钠1%~5%,木质素3%~10%,无水硫酸钠2%~5%。
所述的水泥助磨剂,其原料组分及重量百分比为:三乙醇胺20%,三异丙醇胺10%,乙二醇15%,丙二醇5%,水35%,十二烷基苯磺酸钠3%,木质素9%,无水硫酸钠3%。
所述的水泥助磨剂,其原料组分及重量百分比为:三乙醇胺15%,三异丙醇胺25%,乙二醇10%,丙二醇6%,水30%,十二烷基苯磺酸钠1%,木质素8%,无水硫酸钠5%。
所述的水泥助磨剂的制备方法,其步骤如下:
1)在反应釜中注水,加热至40~50℃备用;
2)将十二烷基苯磺酸钠加入,搅拌15分钟;
3)加入无水硫酸钠搅拌10分钟,再加入木质素搅拌30分钟;
4)将反应釜中的材料用150目筛网过滤;
5)加入乙二醇、丙二醇搅拌20分钟;
6)加入三乙醇胺、三异丙醇胺搅拌30分钟,即得到产品。
由于采用了如上所述的技术方案,本发明具有如下优越性:
一、本发明水泥助磨剂及其制备方法,显著提高粉磨效率,提产幅度达10~30%,减少单位粉磨电耗和粉磨成本;
二、本发明水泥助磨剂及其制备方法,增加水泥的流动性,减少水泥结块现象,降低输送成本,减少浪费;
三、本发明水泥助磨剂及其制备方法,提高水泥早期和后期强度,三天强度提高2~3MPa,28天强度提高3~5MPa;
四、本发明水泥助磨剂及其制备方法,减少水泥成本,用非活混合材代替熟料,节约熟料3%~8%。
水泥助磨剂的添加对水泥产量和性能的影响,如表1、表2
表1  2.4×13m开路高细磨(普通水泥P.042.5)
Figure C200710055027D00051
表2  2.4×8m开路高细磨(矿渣水泥P.S32.5)
具体实施方式
实施方式一
按重量百分比选取原料:三乙醇胺20%、三异丙醇胺10%、乙二醇15%、丙二醇5%、水35%、十二烷基苯磺酸钠3%、木质素9%、无水硫酸钠3%;
在反应釜中注35%水,加热至40~50℃备用;将3%十二烷基苯磺酸钠加入,搅拌15分钟;加入3%无水硫酸钠搅拌10分钟,再加入9%木质素搅拌30分钟;将反应釜中的材料用150目筛网过滤;加入15%乙二醇、5%丙二醇搅拌20分钟;加入20%三乙醇胺、10%三异丙醇胺搅拌30分钟,即得到产品水泥助磨剂。
实施方式二
按重量百分比选取原料:三乙醇胺15%、三异丙醇胺25%、乙二醇10%、丙二醇6%、水30%、十二烷基苯磺酸钠1%、木质素8%、无水硫酸钠5%;
在反应釜中注30%水,加热至40~50℃备用;将1%十二烷基苯磺酸钠加入,搅拌15分钟;加入5%无水硫酸钠搅拌10分钟,再加入8%木质素搅拌30分钟;将反应釜中的材料用150目筛网过滤;加入10%乙二醇、6%丙二醇搅拌20分钟;加入15%三乙醇胺、25%三异丙醇胺搅拌30分钟,即得到产品水泥助磨剂。

Claims (4)

1、一种水泥助磨剂,其特征在于:其原料由三乙醇胺、三异丙醇胺、乙二醇、丙二醇、水、十二烷基苯磺酸钠、木质素、无水硫酸钠组成,各组分的重量百分比为:
三乙醇胺                     10%~30%
三异丙醇胺                   12%~30%
乙二醇                       5%~20%
丙二醇                       3%~10%
水                           15%~40%
十二烷基苯磺酸钠             1%~5%
木质素                       3%~10%
无水硫酸钠                   2%~5%。
2、如权利要求1所述的水泥助磨剂,其特征在于:所述的水泥助磨剂,其原料组分及重量百分比为:三乙醇胺20%,三异丙醇胺10%,乙二醇15%,丙二醇5%,水35%,十二烷基苯磺酸钠3%,木质素9%,无水硫酸钠3%。
3、如权利要求1所述的水泥助磨剂,其特征在于:所述的水泥助磨剂,其原料组分及重量百分比为:三乙醇胺15%,三异丙醇胺25%,乙二醇10%,丙二醇6%,水30%,十二烷基苯磺酸钠1%,木质素8%,无水硫酸钠5%。
4、如权利要求1所述的水泥助磨剂的制备方法,其特征在于:其步骤如下:
1)在反应釜中注水,加热至40~50℃备用;
2)将十二烷基苯磺酸钠加入,搅拌15分钟;
3)加入无水硫酸钠搅拌10分钟,再加入木质素搅拌30分钟;
4)将反应釜中的材料用150目筛网过滤;
5)加入乙二醇、丙二醇搅拌20分钟;
6)加入三乙醇胺、三异丙醇胺搅拌30分钟,即得到产品。
CNB2007100550270A 2007-08-18 2007-08-18 一种水泥助磨剂及其制备方法 Expired - Fee Related CN100519460C (zh)