CN102092981B - 一种节能增强型水泥液体助磨剂及其制备方法 - Google Patents

一种节能增强型水泥液体助磨剂及其制备方法 Download PDF

Info

Publication number
CN102092981B
CN102092981B CN2010105907267A CN201010590726A CN102092981B CN 102092981 B CN102092981 B CN 102092981B CN 2010105907267 A CN2010105907267 A CN 2010105907267A CN 201010590726 A CN201010590726 A CN 201010590726A CN 102092981 B CN102092981 B CN 102092981B
Authority
CN
China
Prior art keywords
cement
grinding aid
sodium
energy
type liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2010105907267A
Other languages
English (en)
Other versions
CN102092981A (zh
Inventor
邵继新
司双龙
李文斌
杨映塘
景国
孟渊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lanzhou Acer Square New Building Materials Technology Co., Ltd.
Original Assignee
GANSU PROV BUILDING MATERIAL RESEARCH AND DESIGN INST
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GANSU PROV BUILDING MATERIAL RESEARCH AND DESIGN INST filed Critical GANSU PROV BUILDING MATERIAL RESEARCH AND DESIGN INST
Priority to CN2010105907267A priority Critical patent/CN102092981B/zh
Publication of CN102092981A publication Critical patent/CN102092981A/zh
Application granted granted Critical
Publication of CN102092981B publication Critical patent/CN102092981B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种节能增强型水泥液体助磨剂，该助磨剂由下述质量百分比的原料组成：三乙醇胺5～15％、三聚磷酸钠1～10％、硫酸铝溶液5～10％、十二烷基苯磺酸钠3～10％、二乙二醇5～10％、醋酸钠5～10％，余量为水。本发明既可提高水泥的生产效率和水泥比表面积，又能提高水泥抗压强度，增加混合材的添加量。同时本发明还公开了该助磨剂的制备方法。

Description

一种节能增强型水泥液体助磨剂及其制备方法
技术领域
本发明涉及水泥生产领域，尤其涉及一种节能增强型水泥液体助磨剂及其制备方法。
背景技术
节能降耗是当前水泥生产企业的紧迫工作，而与水泥生产过程中其它节能减排的途径相比，水泥助磨剂的使用几乎不需要增加任何固定资产投资，还可以提高磨机的研磨效率、降低水泥电耗、增加混合材掺加量、节约水泥成本，增强水泥生产企业的市场竞争力。目前，市场上生产的有些水泥助磨剂虽然能增加混合材的掺加量，但影响水泥后期强度的增长；还有一些水泥助磨剂虽能同时满足混合材掺加量和水泥强度的提高要求，但生产成本过高。
发明内容
本发明所要解决的技术问题是提供一种有效提高产量、强度的节能增强型水泥液体助磨剂。
本发明所要解决的另一个技术问题是提供一种工艺简单、有效降低生产成本的节能增强型水泥液体助磨剂的制备方法。
为解决上述问题，本发明所述的一种节能增强型水泥液体助磨剂，其特征在于：该助磨剂由下述质量百分比的原料组成：三乙醇胺5～15％、三聚磷酸钠1～10％、硫酸铝溶液5～10％、十二烷基苯磺酸钠3～10％、二乙二醇5～10％、醋酸钠5～10％，余量为水。
如上所述的一种节能增强型水泥液体助磨剂的制备方法，其特征在于：将各原料按配比称量后，首先在反应釜中注水，并将其加热至70～80℃；然后加入三聚磷酸钠、硫酸铝溶液，经搅拌20分钟后加入十二烷基苯磺酸钠和醋酸钠，再搅拌10分钟；接着加入二乙二醇搅拌10分钟后，加入三乙醇胺，最后再搅拌20分钟后即得。
本发明与现有技术相比具有以下优点：
1、由于本发明中添加有硫酸铝溶液，因此，可有效提高水泥强度，三天强度提高2～5Mpa，28天强度可提高2～6Mpa。
2、由于本发明中添加有三聚磷酸钠，因此，可有效帮助熟料研磨，消除静电吸附，提高混合材的添加量和水泥的比表面积，从而达到提产和增强的效果。
3、经实际测试，本发明既可提高水泥的生产效率(在加入0.1～0.3％本发明的情况下能显著改善磨内工况，提高水泥磨机台时产量10％～20％。)和水泥比表面积，又能提高水泥抗压强度，增加混合材的添加量；同时，水泥标准稠度用水量和凝结时间在添加此助磨剂前后变化不大(参见表1)。
表1本发明使用前后主要性能指数对比表
某水泥生产企业
4、本发明既可适用于闭路粉磨系统，而且也适用于开路粉磨系统。
5、由于本发明采用简单混合的方式进行制备，因此，不但工艺简单，而且有效地降低了生产成本。
具体实施方式
实施例1一种节能增强型水泥液体助磨剂，由下述质量百分比的原料组成：三乙醇胺5％、三聚磷酸钠2％、硫酸铝溶液6％、十二烷基苯磺酸钠3％、二乙二醇7％、醋酸钠10％，余量为水。
该助磨剂的制备方法：将各原料按配比称量后，首先在反应釜中注水，并将其加热至70～80℃；然后加入三聚磷酸钠、硫酸铝溶液，经搅拌20分钟后加入十二烷基苯磺酸钠和醋酸钠，再搅拌10分钟；接着加入二乙二醇搅拌10分钟后，加入三乙醇胺，最后再搅拌20分钟后即得。
实施例2一种节能增强型水泥液体助磨剂，由下述质量百分比的原料组成：三乙醇胺10％、三聚磷酸钠5％、硫酸铝溶液8％、十二烷基苯磺酸钠9％、二乙二醇10％、醋酸钠7％，余量为水。
该助磨剂的制备方法同实施例1。
实施例3一种节能增强型水泥液体助磨剂，由下述质量百分比的原料组成：三乙醇胺15％、三聚磷酸钠1％、硫酸铝溶液7％、十二烷基苯磺酸钠5％、二乙二醇5％、醋酸钠8％，余量为水。
该助磨剂的制备方法同实施例1。
实施例4一种节能增强型水泥液体助磨剂，由下述质量百分比的原料组成：三乙醇胺5％、三聚磷酸钠1％、硫酸铝溶液5％、十二烷基苯磺酸钠3％、二乙二醇5％、醋酸钠5％，余量为水。
该助磨剂的制备方法同实施例1。
实施例5一种节能增强型水泥液体助磨剂，由下述质量百分比的原料组成：三乙醇胺6％、三聚磷酸钠10％、硫酸铝溶液9％、十二烷基苯磺酸钠6％、二乙二醇8％、醋酸钠6％，余量为水。
该助磨剂的制备方法同实施例1。
实施例6一种节能增强型水泥液体助磨剂，由下述质量百分比的原料组成：三乙醇胺13％、三聚磷酸钠4％、硫酸铝溶液10％、十二烷基苯磺酸钠10％、二乙二醇6％、醋酸钠7％，余量为水。
该助磨剂的制备方法同实施例1。
实施例7一种节能增强型水泥液体助磨剂，由下述质量百分比的原料组成：三乙醇胺15％、三聚磷酸钠10％、硫酸铝溶液10％、十二烷基苯磺酸钠10％、二乙二醇10％、醋酸钠10％，余量为水。
该助磨剂的制备方法同实施例1。

Claims (1)

1.一种节能增强型水泥液体助磨剂，其特征在于：该助磨剂由下述质量百分比的原料组成：三乙醇胺15％、三聚磷酸钠10％、硫酸铝溶液10％、十二烷基苯磺酸钠10％、二乙二醇10％、醋酸钠10％，余量为水；
其制备方法如下：将各原料按配比称量后，首先在反应釜中注水，并将其加热至70～80℃；然后加入三聚磷酸钠、硫酸铝溶液，经搅拌20分钟后加入十二烷基苯磺酸钠和醋酸钠，再搅拌10分钟；接着加入二乙二醇搅拌10分钟后，加入三乙醇胺，最后再搅拌20分钟后即得。
CN2010105907267A 2010-12-10 2010-12-10 一种节能增强型水泥液体助磨剂及其制备方法 Expired - Fee Related CN102092981B (zh)