CN102372453B - 一种水泥复合助磨剂 - Google Patents

一种水泥复合助磨剂 Download PDF

Info

Publication number
CN102372453B
CN102372453B CN201010254797.XA CN201010254797A CN102372453B CN 102372453 B CN102372453 B CN 102372453B CN 201010254797 A CN201010254797 A CN 201010254797A CN 102372453 B CN102372453 B CN 102372453B
Authority
CN
China
Prior art keywords
cement
cement composite
molasses
composite grinding
anhydrous sodium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201010254797.XA
Other languages
English (en)
Other versions
CN102372453A (zh
Inventor
胡鉴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Jiye Changqing New Materials Co ltd
Original Assignee
Guangzhou Built To Last Energy Saving Industrial Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Built To Last Energy Saving Industrial Co ltd filed Critical Guangzhou Built To Last Energy Saving Industrial Co ltd
Priority to CN201010254797.XA priority Critical patent/CN102372453B/zh
Publication of CN102372453A publication Critical patent/CN102372453A/zh
Application granted granted Critical
Publication of CN102372453B publication Critical patent/CN102372453B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种水泥复合助磨剂，包括以下组份：多元醇胺，糖蜜，无水硫酸钠，磁化水。所述组份的重量百分比分别为：多元醇胺25～40％，糖蜜5～10％，无水硫酸钠5～10％，磁化水40～65％。本发明可有效提高水泥强度，助磨效果较好。

Description

一种水泥复合助磨剂
技术领域
本发明涉及一种水泥复合助磨剂。
背景技术
在水泥的制作过程中，当各种物料喂入磨机后粉磨，此时物料与物料、物料与研磨体之间会发生剧烈、频繁的摩擦和撞击，使得物料产生静电，这些带有电荷的物料会吸附在钢球及研磨体的表面，使得水泥磨机出现严重的包球包锻现象；当喂入的附加材料的湿度大于5％时，还会在磨机中大量水蒸气，增加了研磨料的湿度，也会产生上述的包球包锻现象。为了解决静电问题，大多数厂家采用加入水泥复合助磨剂的方法。目前，水泥复合助磨剂有粉体和液体两大类，液体助磨剂使用比较方便，因此应用比较普遍。大多数液体助磨剂配方存在一定的缺陷：助磨效果不甚理想，对水泥强度的提高不大。
发明内容
本发明的目的提供一种水泥复合助磨剂，可有效提高水泥强度，助磨效果较好。
本发明的目的是这样实现的：
一种水泥复合助磨剂，包括以下组份：多元醇胺，糖蜜，无水硫酸钠，磁化水。
优选地，本发明所述组份的重量百分比分别为：多元醇胺25～40％，糖蜜5～10％，无水硫酸钠5～10％，磁化水40～65％。
优选地，本发明所述的多元醇胺为三乙醇胺、三异丙醇胺的其中一种或几种，所述三乙醇胺、三异丙醇胺的重量百分比分别为10～20％、15～20％。
其中，三乙醇胺分子中有N原子，有一对未共用电子，很容易与金属离子形成共价键发生络合，与金属离子形成比较稳定的络合物，这些络合物在溶液中形成许多可溶区，从而提高水化产物的扩散塑料，提高水泥的早期强度；此外三乙醇胺还可提高比表面积，降低细度，加快流速。
三异丙醇胺可通过与难水化的矿物C4AF发生络合反应，促进其持续水化，提高水泥的后期强度，同时三异丙醇胺还具有良好的分散作用，有利于磨机产量的提高。
糖蜜是制糖工业废渣，含有羟基、羧基、羰基等极性较强的基团，属于阴离子表面活性剂，有较强的吸附作用，可被吸附于水泥水化物的晶核，阻碍结晶继续生长，可对水泥中C3A水化物进行延缓和推迟，同时有利于其他水化物的晶体发育，可有效调节水泥凝结时间和中后期的强度。
无水硫酸钠，又可称为元明粉或无水芒硝，主要成份为Na2SO4，其与水泥水化时产生的氢氧化钙反应，生产硫酸钙以及氢氧化钠，硫酸钙与水泥中的C3A、C4AF发生反应，迅速生成水化硫铝酸钙、水化硫铁酸钙以及它们的固溶体，很快结晶形成晶核，促进了水泥其他成份的水化结晶，有效提高了水泥的早期强度，生成的氢氧化钠提高了碱度，有利于水泥中活性混合材水化反应，可起到早强作用。
由上可见，与现有技术相比，本发明有如下有益效果：
本发明可提水泥早、后期强度2～5Mpa，或在保持相同的水泥强度等级条件下可以降低水泥中的熟料用量4％～10％，助磨效果较好。
具体实施方式
下面将结合具体实施例来详细说明本发明，在此本发明的示意性实施例以及说明用来解释本发明，但并不作为对本发明的限定。
实施例一
水泥复合助磨剂，包括以下重量百分比的组份：
三乙醇胺10％，三异丙醇胺15％，糖蜜5％，无水硫酸钠5％，磁化水65％。
实施例二
水泥复合助磨剂，包括以下重量百分比的组份：
三乙醇胺20％，三异丙醇胺20％，糖蜜10％，无水硫酸钠10％，磁化水40％。
实施例三
水泥复合助磨剂，包括以下重量百分比的组份：
三乙醇胺15％，三异丙醇胺16％，糖蜜8％，无水硫酸钠8％，磁化水49％。
实施例四
水泥复合助磨剂，包括以下重量百分比的组份：
三乙醇胺14％，三异丙醇胺18％，糖蜜6％，无水硫酸钠9％，磁化水53％。
实施例五
水泥复合助磨剂，包括以下重量百分比的组份：
三乙醇胺16％，三异丙醇胺17％，糖蜜7％，无水硫酸钠6％，磁化水54％。
以上对本发明实施例所提供的技术方案进行了详细介绍，本文中应用了具体个例对本发明实施例的原理以及实施方式进行了阐述，以上实施例的说明只适用于帮助理解本发明实施例的原理；同时，对于本领域的一般技术人员，依据本发明实施例，在具体实施方式以及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。

Claims (2)

1.一种水泥复合助磨剂，其特征在于包括以下组份： 
多元醇胺，糖蜜，无水硫酸钠，磁化水；多元醇胺25～40％，糖蜜5～10％，无水硫酸钠5～10％，磁化水40～65％；所述的多元醇胺为三乙醇胺、三异丙醇胺的其中一种或几种。 
2.根据权利要求1所述的水泥复合助磨剂，其特征是：所述三乙醇胺、三异丙醇胺的重量百分比分别为10～20％、15～20％。 
CN201010254797.XA 2010-08-16 2010-08-16 一种水泥复合助磨剂 Active CN102372453B (zh)