CN100393764C - 一种发泡型酚醛树脂及其合成工艺 - Google Patents

一种发泡型酚醛树脂及其合成工艺 Download PDF

Info

Publication number
CN100393764C
CN100393764C CNB031295703A CN03129570A CN100393764C CN 100393764 C CN100393764 C CN 100393764C CN B031295703 A CNB031295703 A CN B031295703A CN 03129570 A CN03129570 A CN 03129570A CN 100393764 C CN100393764 C CN 100393764C
Authority
CN
China
Prior art keywords
expansion type
paraformaldehyde
type resol
raw material
foam type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB031295703A
Other languages
English (en)
Other versions
CN1566172A (zh
Inventor
杨金平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Meiks Technology Development Co., Ltd.
Original Assignee
SHANGHAI ADVANCED ENGINEERING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI ADVANCED ENGINEERING MATERIALS Co Ltd filed Critical SHANGHAI ADVANCED ENGINEERING MATERIALS Co Ltd
Priority to CNB031295703A priority Critical patent/CN100393764C/zh
Publication of CN1566172A publication Critical patent/CN1566172A/zh
Application granted granted Critical
Publication of CN100393764C publication Critical patent/CN100393764C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种发泡型酚醛树脂及其合成工艺，该树脂采用以下组分(摩尔份数)为原料：苯酚100份、多聚甲醛120～170份、催化剂0.5～6份，该方法是将以上原料在常压下，温度控制在60～130℃之间，加成反应3～7小时，制得所需发泡型酚醛树脂。与现有技术相比，本发明由于采用了多聚甲醛代替甲醛水溶液为原料，因此可以采用电加热的方式进行加成反应，从而使生产易于控制，树脂质量稳定，有利于环境保护。

Description

一种发泡型酚醛树脂及其合成工艺
技术领域
本发明涉及一种合成树脂材料，尤其涉及一种发泡型酚醛树脂及其合成工艺。
背景技术
目前，发泡型酚醛树脂的合成采用的是热固性酚醛树脂的合成方法，通过采用苯酚和过量的甲醛水溶液(37％的水溶液)在NH3·H2O、NaOH、Ba(OH)2等碱性物质催化下，通过加成反应制得。该方法采用蒸汽加热，生产不易控制，造成产品质量不稳定，同时，合成的产品中水份较多，需配制脱水设备进行真空脱水，从而产生废液排放，造成环境污染。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种生产易于控制、树脂质量稳定、有利于环境保护的发泡型酚醛树脂及其合成工艺。
本发明的目的可以通过以下技术方案来实现：
一种发泡型酚醛树脂，其特征在于，该树脂采用以下组分(摩尔份数)为原料：
苯酚        100份，
多聚甲醛    120～170份，
催化剂      0.5～6份。
所述的多聚甲醛的结构式为：
Figure C0312957000031
其中，n＝3～20。
所述的催化剂选自以下弱碱物质中的一种或几种：醋酸锌、氨水、碳酸钠。
一种发泡型酚醛树脂的合成工艺，其特征在于，该工艺采用以下组分(摩尔份数)为原料：苯酚100份、多聚甲醛120～170份、催化剂0.5～6份，以上原料在常压下，温度控制在60～130℃之间，加成反应3～7小时，制得所需发泡型酚醛树脂。
所述的工艺中，加热方法采用电加热方式。
所述的多聚甲醛的结构式为：
Figure C0312957000041
其中，n＝3～20。
所述的催化剂选自以下弱碱物质中的一种或几种：醋酸锌、氨水、碳酸钠。
本发明由于采用了多聚甲醛代替甲醛水溶液为原料，因此可以采用电加热的方式进行加成反应，从而使生产易控制，树脂质量稳定；又因原料中没有水份，合成工艺中无需真空脱水和排污设备，故本发明不但可以减少设备投资，提高企业的经济效益，而且可以大大降低环境污染。
具体实施方式
下面结合具体实施例，对本发明作进一步说明。
实施例1
一种发泡型酚醛树脂的合成工艺，该工艺采用以下组分(摩尔份数)为原料：苯酚100份、聚甲醛(聚合度为14)140份、催化剂醋酸锌3份，以上原料在常压下，采用电加热的方式将温度控制在100℃，加成反应5小时，制得所需发泡型酚醛树脂。
实施例2
一种发泡型酚醛树脂的合成工艺，该工艺采用以下组分(摩尔份数)为原料：苯酚100份、聚甲醛(聚合度为8)120份、催化剂氨水0.5份，以上原料在常压下，采用电加热的方式将温度控制在60℃，加成反应7小时，制得所需发泡型酚醛树脂。
实施例3
一种发泡型酚醛树脂的合成工艺，该工艺采用以下组分(摩尔份数)为原料：苯酚100份、聚甲醛(聚合度为3)170份、催化剂碳酸钠6份，以上原料在常压下，采用电加热的方式将温度控制在130℃，加成反应3小时，制得所需发泡型酚醛树脂。

Claims (3)

1.一种发泡型酚醛树脂的合成工艺，其特征在于，该工艺采用以下组分摩尔份数为原料：苯酚100份、多聚甲醛120～170份、催化剂0.5～6份，以上原料在常压下，温度控制在60～130℃之间，加成反应3～7小时，制得所需发泡型酚醛树脂；所述的催化剂选自以下弱碱物质中的一种或几种：醋酸锌、氨水、碳酸钠。
2.根据权利要求1所述的发泡型酚醛树脂的合成工艺，其特征在于，所述的工艺中，加热方法采用电加热方式。
3.根据权利要求1所述的发泡型酚醛树脂的合成工艺，其特征在于，所述的多聚甲醛的结构式为：
H[CH2O]nOH
其中，n＝3～20。
CNB031295703A 2003-06-27 2003-06-27 一种发泡型酚醛树脂及其合成工艺 Expired - Fee Related CN100393764C (zh)