BR112019004943A2 - chapa de aço revestida, método para fabricação de chapa de aço galvanizada por imersão a quente e método para fabricação de chapa de aço galvanizada por imersão a quente com liga - Google Patents

chapa de aço revestida, método para fabricação de chapa de aço galvanizada por imersão a quente e método para fabricação de chapa de aço galvanizada por imersão a quente com liga

Info

Publication number
BR112019004943A2
BR112019004943A2 BR112019004943A BR112019004943A BR112019004943A2 BR 112019004943 A2 BR112019004943 A2 BR 112019004943A2 BR 112019004943 A BR112019004943 A BR 112019004943A BR 112019004943 A BR112019004943 A BR 112019004943A BR 112019004943 A2 BR112019004943 A2 BR 112019004943A2
Authority
BR
Brazil
Prior art keywords
dip galvanized
hot dip
steel
manufacturing hot
galvanized sheet
Prior art date
Application number
BR112019004943A
Other languages
English (en)
Inventor
Uenishi Akihiro
Kawata Hiroyuki
Haga Jun
Sano Kohichi
Hayashi Koutarou
Hayashi Kunio
Kameda Masaharu
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of BR112019004943A2 publication Critical patent/BR112019004943A2/pt

Abstract

a presente invenção refere-se a uma chapa de aço revestida tendo uma composição química incluindo, em termos de % em massa, pelo menos 0,03 % a 0,70% de c, 0,25% a 2,50% de si, 1,00% a 5,00% de mn, 0,100% ou menos de p, 0,010% ou menos de s, 0,001% a 2,500% de al sol. e 0,020% ou menos de n, e o restante consistindo em ferro e impurezas, onde a composição de metal da mesma inclui mais de 5,0% em vol. de austenita residual e mais de 5,0% em vol. de martensita temperada, e a austenita residual tem um teor de c de 0,85% em massa ou mais.
BR112019004943A 2016-10-19 2016-10-19 chapa de aço revestida, método para fabricação de chapa de aço galvanizada por imersão a quente e método para fabricação de chapa de aço galvanizada por imersão a quente com liga BR112019004943A2 (pt)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2016/081018 WO2018073919A1 (ja) 2016-10-19 2016-10-19 めっき鋼板、溶融亜鉛めっき鋼板の製造方法及び合金化溶融亜鉛めっき鋼板の製造方法

Publications (1)

Publication Number Publication Date
BR112019004943A2 true BR112019004943A2 (pt) 2019-06-25

Family

ID=62018949

Family Applications (1)

Application Number Title Priority Date Filing Date
BR112019004943A BR112019004943A2 (pt) 2016-10-19 2016-10-19 chapa de aço revestida, método para fabricação de chapa de aço galvanizada por imersão a quente e método para fabricação de chapa de aço galvanizada por imersão a quente com liga

Country Status (8)

Country Link
US (1) US11732341B2 (pt)
EP (1) EP3530768B9 (pt)
JP (1) JP6809532B2 (pt)
KR (1) KR102276055B1 (pt)
CN (1) CN109790606B (pt)
BR (1) BR112019004943A2 (pt)
MX (1) MX2019004000A (pt)
WO (1) WO2018073919A1 (pt)

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6690793B1 (ja) * 2018-06-29 2020-04-28 日本製鉄株式会社 高強度鋼板およびその製造方法
EP3822382A4 (en) * 2018-10-10 2021-09-15 JFE Steel Corporation HIGH STRENGTH STEEL SHEET AND METHOD OF MANUFACTURING ITEM
WO2020128574A1 (en) 2018-12-18 2020-06-25 Arcelormittal Cold rolled and heat-treated steel sheet and method of manufacturing the same
US11643701B2 (en) 2019-01-29 2023-05-09 Jfe Steel Corporation High-strength hot-dip galvanized steel sheet and manufacturing method therefor
MX2021015578A (es) 2019-06-28 2022-01-24 Nippon Steel Corp Lamina de acero.
JP7364963B2 (ja) * 2020-04-03 2023-10-19 日本製鉄株式会社 鋼板およびその製造方法
CN113802051A (zh) * 2020-06-11 2021-12-17 宝山钢铁股份有限公司 一种塑性优异的超高强度钢及其制造方法
CN114606446B (zh) * 2020-12-08 2023-03-24 清华大学 一种高强度韧性钢及其制备方法、以及热浸镀锌钢的制备方法
CN114875336A (zh) * 2022-05-31 2022-08-09 山东钢铁集团日照有限公司 一种增塑性热镀锌复相钢的生产调控方法
WO2024190415A1 (ja) * 2023-03-10 2024-09-19 日本製鉄株式会社 鋼板

Family Cites Families (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS61157625A (ja) 1984-12-29 1986-07-17 Nippon Steel Corp 高強度鋼板の製造方法
JPS61217529A (ja) 1985-03-22 1986-09-27 Nippon Steel Corp 延性のすぐれた高強度鋼板の製造方法
JP3527092B2 (ja) 1998-03-27 2004-05-17 新日本製鐵株式会社 加工性の良い高強度合金化溶融亜鉛めっき鋼板とその製造方法
JP3840864B2 (ja) 1999-11-02 2006-11-01 Ｊｆｅスチール株式会社 高張力溶融亜鉛めっき鋼板およびその製造方法
CA2387322C (en) * 2001-06-06 2008-09-30 Kawasaki Steel Corporation High-ductility steel sheet excellent in press formability and strain age hardenability, and method for manufacturing the same
CN102242306B (zh) * 2005-08-03 2013-03-27 住友金属工业株式会社 热轧钢板及冷轧钢板及它们的制造方法
JP5223360B2 (ja) * 2007-03-22 2013-06-26 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5369663B2 (ja) 2008-01-31 2013-12-18 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5092858B2 (ja) * 2008-04-11 2012-12-05 新日本製鐵株式会社 溶融亜鉛めっき用鋼板及び合金化溶融亜鉛めっき鋼板
JP5136609B2 (ja) 2010-07-29 2013-02-06 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
EP2439290B1 (de) 2010-10-05 2013-11-27 ThyssenKrupp Steel Europe AG Mehrphasenstahl, aus einem solchen Mehrphasenstahl hergestelltes kaltgewalztes Flachprodukt und Verfahren zu dessen Herstellung
JP5141811B2 (ja) 2010-11-12 2013-02-13 Ｊｆｅスチール株式会社 均一伸びとめっき性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
KR101646857B1 (ko) * 2011-07-06 2016-08-08 신닛테츠스미킨 카부시키카이샤 용융 도금 냉연 강판 및 그 제조 방법
WO2013018741A1 (ja) * 2011-07-29 2013-02-07 新日鐵住金株式会社 形状凍結性に優れた高強度鋼板、高強度亜鉛めっき鋼板およびそれらの製造方法
BR112014002023B1 (pt) 2011-07-29 2019-03-26 Nippon Steel & Sumitomo Metal Corporation Chapa de aço de alta resistência excelente em resistência ao impacto e seu método de produção.
WO2013047739A1 (ja) * 2011-09-30 2013-04-04 新日鐵住金株式会社 機械切断特性に優れた高強度溶融亜鉛めっき鋼板、高強度合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
BR112014007498B1 (pt) 2011-09-30 2019-04-30 Nippon Steel & Sumitomo Metal Corporation Chapa de aço galvanizado a quente de alta resistência e método de produção da mesma
JP2013241636A (ja) * 2012-05-18 2013-12-05 Jfe Steel Corp 低降伏比型高強度溶融亜鉛めっき鋼板、低降伏比型高強度合金化溶融亜鉛めっき鋼板、低降伏比型高強度溶融亜鉛めっき鋼板の製造方法、および低降伏比型高強度合金化溶融亜鉛めっき鋼板の製造方法
RU2605404C2 (ru) 2012-08-06 2016-12-20 Ниппон Стил Энд Сумитомо Метал Корпорейшн Холоднокатаный стальной лист и способ его изготовления, и сформованное горячей штамповкой изделие
JP5857909B2 (ja) * 2012-08-09 2016-02-10 新日鐵住金株式会社 鋼板およびその製造方法
EP3219822B1 (en) * 2015-01-15 2018-08-22 Jfe Steel Corporation High-strength hot-dip galvanized steel sheet and production method thereof
JP6348436B2 (ja) 2015-02-27 2018-06-27 株式会社神戸製鋼所 高強度高延性鋼板
BR112018076347A2 (pt) * 2016-09-21 2019-04-02 Nippon Steel & Sumitomo Metal Corporation chapa de aço

Also Published As

Publication number Publication date
JPWO2018073919A1 (ja) 2019-06-24
CN109790606A (zh) 2019-05-21
KR20190040018A (ko) 2019-04-16
KR102276055B1 (ko) 2021-07-13
EP3530768B9 (en) 2024-07-10
US11732341B2 (en) 2023-08-22
US20190218652A1 (en) 2019-07-18
MX2019004000A (es) 2019-08-14
EP3530768B1 (en) 2021-08-04
WO2018073919A1 (ja) 2018-04-26
EP3530768A4 (en) 2020-03-11
CN109790606B (zh) 2021-08-06
EP3530768A1 (en) 2019-08-28
JP6809532B2 (ja) 2021-01-06

Similar Documents

Publication Publication Date Title
BR112019004943A2 (pt) chapa de aço revestida, método para fabricação de chapa de aço galvanizada por imersão a quente e método para fabricação de chapa de aço galvanizada por imersão a quente com liga
BR112019003791A2 (pt) chapa de aço laminada a frio e tratada termicamente, junta soldada por pontos de resistência, método para a fabricação de uma chapa de aço laminada a frio e tratada termicamente e processo para a produção de uma junta soldada por pontos de resistência
BR112018013375A2 (pt) ?chapa de aço e método de fabricação de uma chapa de aço?
MX2019007165A (es) Lamina de acero templada y recubierta que tiene excelente conformabilidad y metodo para fabricar la misma.
BR112017000405A2 (pt) folha de aço laminada e método para a fabricação de uma folha de aço
BR112017017134A2 (pt) chapa de aço laminada a frio e método de fabricação da mesma
UA124354C2 (uk) Відпущена листова сталь з покриттям, яка характеризується чудовою деформованістю, і спосіб її виготовлення
BR112017007999A2 (pt) ?processo para fabricar chapas de aço para endurecimento por prensagem e peças obtidas por esse processo?
BR112014007432A2 (pt) folha de aço galvanizada e método de fabricação da mesma
BR112019006995A2 (pt) chapa de aço
BR112016013130A2 (pt) Folha de aço e método para fabricar uma folha de aço
BR112017000005A2 (pt) método para produzir uma chapa de aço revestida e chapa de aço revestida
BR112019004843A2 (pt) chapa de aço
HK1141841A1 (en) Pretreatment compositions and methods for coating a metal substrate
MX2016011156A (es) Material laminado para resorte de alta resistencia y cable para resorte de alta resistencia.
UA124949C2 (uk) Дуплексна нержавіюча сталь та її застосування
BR112016015486A2 (pt) Cano de ferro e aço que contém cromo à base de martensita para poço de óleo
BR112016029379A2 (pt) chapa de aço laminada a quente
BR112017002189A2 (pt) método para produzir uma folha de aço, folha de aço e uso de uma folha de aço
BR112022005230A2 (pt) Substrato de aço inoxidável revestido, método para a fabricação de um substrato de aço inoxidável revestido, processo de revestimento por imersão a quente de uma tira de aço e instalação de revestimento por imersão a quente
BR112018071994A2 (pt) tecnologia de soldagem de metal dissimilar em campo para aço com alto teor de manganês resistente ao desgaste realçado
MX2022003433A (es) Lamina de acero laminada en caliente.
BR112015030003A2 (pt) chapa de aço laminada a frio, chapa de aço laminada a frio galvanizada e método de produção da mesma
MX366127B (es) Composiciones de pretratamiento de zirconio que contienen molibdeno, metodos asociados para tratar sustratos metalicos, y sustratos metalicos revestidos relacionados.
BR112016029457A2 (pt) ?método para produzir uma chapa de aço revestida com alta resistência e chapa de aço revestida?

Legal Events

Date Code Title Description
B25D Requested change of name of applicant approved

Owner name: NIPPON STEEL CORPORATION (JP)

B06U Preliminary requirement: requests with searches performed by other patent offices: procedure suspended [chapter 6.21 patent gazette]
B07A Application suspended after technical examination (opinion) [chapter 7.1 patent gazette]
B08F Application dismissed because of non-payment of annual fees [chapter 8.6 patent gazette]

Free format text: REFERENTE A 5A ANUIDADE.

B350 Update of information on the portal [chapter 15.35 patent gazette]
B08K Patent lapsed as no evidence of payment of the annual fee has been furnished to inpi [chapter 8.11 patent gazette]

Free format text: EM VIRTUDE DO ARQUIVAMENTO PUBLICADO NA RPI 2640 DE 10-08-2021 E CONSIDERANDO AUSENCIA DE MANIFESTACAO DENTRO DOS PRAZOS LEGAIS, INFORMO QUE CABE SER MANTIDO O ARQUIVAMENTO DO PEDIDO DE PATENTE, CONFORME O DISPOSTO NO ARTIGO 12, DA RESOLUCAO 113/2013.