BR112018013375A2 - ?chapa de aço e método de fabricação de uma chapa de aço? - Google Patents

?chapa de aço e método de fabricação de uma chapa de aço?

Info

Publication number
BR112018013375A2
BR112018013375A2 BR112018013375-2A BR112018013375A BR112018013375A2 BR 112018013375 A2 BR112018013375 A2 BR 112018013375A2 BR 112018013375 A BR112018013375 A BR 112018013375A BR 112018013375 A2 BR112018013375 A2 BR 112018013375A2
Authority
BR
Brazil
Prior art keywords
less
steel sheet
iron
equal
unavoidable impurities
Prior art date
Application number
BR112018013375-2A
Other languages
English (en)
Other versions
BR112018013375B1 (pt
Inventor
Uta Elena
Hebert Véronique
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of BR112018013375A2 publication Critical patent/BR112018013375A2/pt
Publication of BR112018013375B1 publication Critical patent/BR112018013375B1/pt

Abstract

uma chapa de aço laminada a frio e tratada a quente que tem uma composição que compreende de 0,17% inferior ao carbono inferior a 0,24%, 1,9% inferior ao manganês inferior a 2,2%, 0,5% inferior ao alumínio inferior a 1,2%, 0,5% inferior ao silício inferior a 1%, 0,05% inferior ao cromo menor ou igual a 0,2%, 0,015% inferior ao nióbio inferior a 0,03%, enxofre inferior a 0,003%, fósforo inferior a 0,03% e opcionalmente contém 0,005% inferior ao titânio inferior a 0,05%, 0,001% inferior ao molibdênio inferior a 0,05%, a composição restante sendo composta por ferro e impurezas inevitáveis causadas pelo processamento, em que si + al maior ou igual 1,3%, o restante consistindo em ferro e impurezas inevitáveis que resultam da microestrutura da chapa de aço revestida que compreendem, em fração de área, 10 a 20% de austenita residual, a dita fase de austenita tendo um teor de carbono entre 0,9 a 1,1%, 40 a 55% de ferrita poligonal, 15 a 40% de bainita granular e pelo menos 5% de martensita temperada, a soma de martensita temperada e austenita residual estando compreendida entre 20 a 30%.
BR112018013375-2A 2016-01-18 2017-01-17 Chapa de aço e método de fabricação de uma chapa de aço BR112018013375B1 (pt)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
IBPCT/IB2016/000024 2016-01-18
PCT/IB2016/000024 WO2017125773A1 (en) 2016-01-18 2016-01-18 High strength steel sheet having excellent formability and a method of manufacturing the same
PCT/IB2017/000018 WO2017125809A1 (en) 2016-01-18 2017-01-17 High strength steel sheet having excellent formability and a method of manufacturing the same

Publications (2)

Publication Number Publication Date
BR112018013375A2 true BR112018013375A2 (pt) 2018-12-04
BR112018013375B1 BR112018013375B1 (pt) 2022-08-09

Family

ID=55300730

Family Applications (1)

Application Number Title Priority Date Filing Date
BR112018013375-2A BR112018013375B1 (pt) 2016-01-18 2017-01-17 Chapa de aço e método de fabricação de uma chapa de aço

Country Status (13)

Country Link
US (1) US11466335B2 (pt)
EP (1) EP3405340A1 (pt)
JP (1) JP6751766B2 (pt)
KR (1) KR102230103B1 (pt)
CN (1) CN108463340B (pt)
BR (1) BR112018013375B1 (pt)
CA (1) CA3009117C (pt)
MA (1) MA43659A (pt)
MX (1) MX2018008561A (pt)
RU (1) RU2712591C1 (pt)
UA (1) UA119838C2 (pt)
WO (2) WO2017125773A1 (pt)
ZA (1) ZA201804092B (pt)

Families Citing this family (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6749818B2 (ja) * 2016-02-29 2020-09-02 株式会社神戸製鋼所 高強度鋼板およびその製造方法
WO2019122978A1 (en) * 2017-12-21 2019-06-27 Arcelormittal Welded steel part used as motor vehicle part, hot pressed steel part, and method of manufacturing said welded steel part
CN108950405B (zh) * 2018-08-14 2020-02-18 武汉钢铁有限公司 一种具有良好翻边性能的800MPa级多相钢及生产方法
WO2020058748A1 (en) * 2018-09-20 2020-03-26 Arcelormittal Cold rolled and coated steel sheet and a method of manufacturing thereof
US20220056543A1 (en) * 2018-09-20 2022-02-24 Arcelormittal Hot rolled steel sheet with high hole expansion ratio and manufacturing process thereof
MX2021005866A (es) * 2018-11-30 2021-07-16 Arcelormittal Hoja de acero recocido laminado en frio con una alta proporcion de expansion de agujero y proceso de fabricacion de la misma.
SE542893C2 (en) * 2018-11-30 2020-08-18 Voestalpine Stahl Gmbh A resistance spot welded joint comprising a zinc coated ahss steel sheet
KR20210127922A (ko) * 2019-02-18 2021-10-25 타타 스틸 이즈무이덴 베.뷔. 기계적 특성이 개선된 고강도 강
WO2020229877A1 (en) * 2019-05-15 2020-11-19 Arcelormittal A cold rolled martensitic steel and a method for it's manufacture
WO2020245626A1 (en) * 2019-06-03 2020-12-10 Arcelormittal Cold rolled and coated steel sheet and a method of manufacturing thereof
WO2020245627A1 (en) * 2019-06-03 2020-12-10 Arcelormittal Cold rolled and coated steel sheet and a method of manufacturing thereof
WO2020250009A1 (en) * 2019-06-12 2020-12-17 Arcelormittal A cold rolled martensitic steel and a method of martensitic steel thereof
ES2911656T3 (es) * 2019-06-17 2022-05-20 Tata Steel Ijmuiden Bv Método de tratamiento térmico de un fleje de acero laminado en frío
PT3754037T (pt) * 2019-06-17 2022-04-19 Tata Steel Ijmuiden Bv Método de tratamento térmico de uma tira de aço laminada a frio de alta resistência
EP3754036B1 (en) * 2019-06-17 2022-03-02 Tata Steel IJmuiden B.V. Heat treatment of high strength cold rolled steel strip
ES2911655T3 (es) * 2019-06-17 2022-05-20 Tata Steel Ijmuiden Bv Tratamiento térmico de un fleje de acero laminado en frío
WO2021116741A1 (en) * 2019-12-13 2021-06-17 Arcelormittal Heat treated cold rolled steel sheet and a method of manufacturing thereof
WO2021176249A1 (en) * 2020-03-02 2021-09-10 Arcelormittal High strength cold rolled and galvannealed steel sheet and manufacturing process thereof
CN111893379B (zh) * 2020-07-13 2022-01-18 首钢集团有限公司 一种780MPa级增强成形性热镀锌双相钢及其制造方法
WO2022018501A1 (en) * 2020-07-24 2022-01-27 Arcelormittal Cold rolled and annealed steel sheet and method of manufacturing the same
CN111996467B (zh) * 2020-09-28 2022-05-20 首钢集团有限公司 一种980MPa级镀锌高强钢及其制备方法
CN114763595B (zh) * 2021-01-15 2023-07-07 宝山钢铁股份有限公司 一种冷轧钢板以及冷轧钢板的制造方法
CN114807736A (zh) * 2021-01-21 2022-07-29 宝山钢铁股份有限公司 一种抗lme钢及抗lme钢板的制造方法
CN113416887B (zh) * 2021-05-21 2022-07-19 鞍钢股份有限公司 汽车超高成形性980MPa级镀锌钢板及制备方法
CN114032452A (zh) * 2021-10-11 2022-02-11 鞍钢集团北京研究院有限公司 一种高强塑积冷轧trip钢板及其制备方法
CN116987974B (zh) * 2023-08-14 2024-04-09 东北大学 一种高强度高韧性的低磁导率中锰钢及其制造方法

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3924108B2 (ja) 2000-03-13 2007-06-06 新日本製鐵株式会社 予加工後のハイドロフォーム成形性の優れた高強度鋼板の製造方法
JP4716359B2 (ja) 2005-03-30 2011-07-06 株式会社神戸製鋼所 均一伸びに優れた高強度冷延鋼板およびその製造方法
WO2007114261A1 (ja) * 2006-03-31 2007-10-11 Kabushiki Kaisha Kobe Seiko Sho 化成処理性に優れた高強度冷延鋼板
US7979194B2 (en) 2007-07-16 2011-07-12 Cummins Inc. System and method for controlling fuel injection
JP5167487B2 (ja) 2008-02-19 2013-03-21 Ｊｆｅスチール株式会社 延性に優れる高強度鋼板およびその製造方法
JP5332981B2 (ja) 2009-07-08 2013-11-06 新日鐵住金株式会社 延性及び耐食性に優れた合金化溶融亜鉛めっき鋼板及びその製造方法
CN102712980B (zh) 2010-01-26 2014-07-02 新日铁住金株式会社 高强度冷轧钢板及其制造方法
JP5719545B2 (ja) 2010-08-13 2015-05-20 新日鐵住金株式会社 伸びとプレス成形安定性に優れた高強度薄鋼板
JP5640898B2 (ja) * 2011-06-02 2014-12-17 新日鐵住金株式会社 熱延鋼板
CN105648311B (zh) 2011-08-09 2018-03-30 新日铁住金株式会社 在低温下的冲击能吸收特性和耐haz软化特性优异的高屈服比热轧钢板
BR112014007530B1 (pt) 2011-09-30 2018-12-11 Nippon Steel & Sumitomo Metal Corporation chapa de aço galvanizada por imersão a quente de alta resistência e processo para produção da mesma
EP2765212B1 (en) * 2011-10-04 2017-05-17 JFE Steel Corporation High-strength steel sheet and method for manufacturing same
JP6290168B2 (ja) * 2012-03-30 2018-03-07 フォエスタルピネ スタール ゲゼルシャフト ミット ベシュレンクテル ハフツングＶｏｅｓｔａｌｐｉｎｅ Ｓｔａｈｌ Ｇｍｂｈ 高強度冷間圧延鋼板およびそのような鋼板を作製する方法
JP6232045B2 (ja) * 2012-03-30 2017-11-15 フォエスタルピネ スタール ゲゼルシャフト ミット ベシュレンクテル ハフツングＶｏｅｓｔａｌｐｉｎｅ Ｓｔａｈｌ Ｇｍｂｈ 高強度冷間圧延鋼板およびそのような鋼板を作製する方法
US20150152533A1 (en) 2012-06-05 2015-06-04 Thyssenkrupp Steel Europe Ag Steel, Sheet Steel Product and Process for Producing a Sheet Steel Product
JP6221424B2 (ja) * 2013-07-04 2017-11-01 新日鐵住金株式会社 冷延鋼板およびその製造方法
MX2016006777A (es) * 2013-11-29 2016-09-07 Nippon Steel & Sumitomo Metal Corp Componente de lamina de acero formada en caliente y metodo para producir el mismo asi como la lamina de acero para formacion en caliente.
US10435763B2 (en) 2014-04-15 2019-10-08 Thyssenkrupp Steel Europe Ag Method for producing a cold-rolled flat steel product with high yield strength and flat cold-rolled steel product

Also Published As

Publication number Publication date
US20210040576A1 (en) 2021-02-11
US11466335B2 (en) 2022-10-11
KR102230103B1 (ko) 2021-03-19
KR20180095671A (ko) 2018-08-27
RU2712591C1 (ru) 2020-01-29
JP6751766B2 (ja) 2020-09-09
UA119838C2 (uk) 2019-08-12
BR112018013375B1 (pt) 2022-08-09
CA3009117A1 (en) 2017-07-27
CN108463340A (zh) 2018-08-28
WO2017125773A1 (en) 2017-07-27
EP3405340A1 (en) 2018-11-28
JP2019506530A (ja) 2019-03-07
WO2017125809A1 (en) 2017-07-27
CA3009117C (en) 2020-10-27
MA43659A (fr) 2018-11-28
CN108463340B (zh) 2021-07-06
MX2018008561A (es) 2018-11-09
ZA201804092B (en) 2019-03-27

Similar Documents

Publication Publication Date Title
BR112018013375A2 (pt) ?chapa de aço e método de fabricação de uma chapa de aço?
MX2019007165A (es) Lamina de acero templada y recubierta que tiene excelente conformabilidad y metodo para fabricar la misma.
UA124354C2 (uk) Відпущена листова сталь з покриттям, яка характеризується чудовою деформованістю, і спосіб її виготовлення
MX2019007170A (es) Hoja de acero enrollada en frio, de alta resistencia con alta capacidad de formacion y un metodo para fabricar la misma.
MX2020004769A (es) Hoja de acero laminada en frio y un metodo para la fabricacion de la misma.
BR112016013130A2 (pt) Folha de aço e método para fabricar uma folha de aço
MA47998B1 (fr) Acier pour une trempe à la presse et pièce trempée à la presse fabriquée à partir d'un tel acier
MX2020004787A (es) Hoja de acero tratada termicamente laminada en frio y un metodo de fabricacion de la misma.
MX2019003282A (es) Lamina de acero de alta resistencia y alta conformabilidad laminada en frio y tratada termicamente y metodo de fabricacion.
BR112017000405A2 (pt) folha de aço laminada e método para a fabricação de uma folha de aço
MX2018007347A (es) Amina de acero galvanizada por inmersion en caliente de alta resistencia que tiene excelente calidad de superficie y soldabilidad por puntos, y metodo de manufactura para la misma.
BR112017007999A2 (pt) ?processo para fabricar chapas de aço para endurecimento por prensagem e peças obtidas por esse processo?
MX2020004784A (es) Hoja de acero laminada en frio y tratada termicamente y un metodo de fabricacion de la misma.
MX2017015841A (es) Acero de alta resistencia y metodo de fabricacion.
BR112019025042A2 (pt) Vergalhão laminado para aço para mola
BR112019004943A2 (pt) chapa de aço revestida, método para fabricação de chapa de aço galvanizada por imersão a quente e método para fabricação de chapa de aço galvanizada por imersão a quente com liga
MX2020006338A (es) Hoja de acero laminada en frio y tratada termicamente y un metodo para la fabricacion de la misma.
MX2020006340A (es) Hoja de acero laminada en frio y recubierta y un metodo de fabricacion de la misma.
BR112022010056A2 (pt) Chapa de aço laminada a quente, método de produção de uma chapa de aço laminada a quente, uso de uma chapa de aço e máquina industrial
ZA202212135B (en) Cold rolled and heat-treated steel sheet and a method of manufacturing thereof
MX2021003290A (es) Hoja de acero laminada en frio y recubierta y un metodo de fabricacion de la misma.
MX2021007122A (es) Acero laminado en caliente y un metodo de fabricacion del mismo.
BR112022014638A2 (pt) Chapa de aço laminada a frio e galvanizada e processo para fabricação de uma chapa de aço laminada a frio e galvanizada
BR112017003147A2 (pt) aço de baixa liga e alta resistência laminado a frio
BR112021021482A2 (pt) Chapa de aço laminada a frio e revestida, método de produção de uma chapa de aço laminada a frio e revestida, uso de uma chapa de aço e veículo

Legal Events

Date Code Title Description
B06W Patent application suspended after preliminary examination (for patents with searches from other patent authorities) chapter 6.23 patent gazette]
B09A Decision: intention to grant [chapter 9.1 patent gazette]
B16A Patent or certificate of addition of invention granted [chapter 16.1 patent gazette]

Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 17/01/2017, OBSERVADAS AS CONDICOES LEGAIS