AU605234B2 - High temperature epoxy resin tooling composition - Google Patents

High temperature epoxy resin tooling composition Download PDF

Info

Publication number
AU605234B2
AU605234B2 AU10964/88A AU1096488A AU605234B2 AU 605234 B2 AU605234 B2 AU 605234B2 AU 10964/88 A AU10964/88 A AU 10964/88A AU 1096488 A AU1096488 A AU 1096488A AU 605234 B2 AU605234 B2 AU 605234B2
Authority
AU
Australia
Prior art keywords
parts
weight
epoxy resin
composition
micrometres
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
AU10964/88A
Other languages
English (en)
Other versions
AU1096488A (en
Inventor
Richard P. Atkins
Chen-Shih Wang
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Motors Liquidation Co
Original Assignee
General Motors Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by General Motors Corp filed Critical General Motors Corp
Publication of AU1096488A publication Critical patent/AU1096488A/en
Application granted granted Critical
Publication of AU605234B2 publication Critical patent/AU605234B2/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
    • C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
    • C08G59/68—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the catalysts used
    • C08G59/686—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the catalysts used containing nitrogen
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
    • C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
    • C08G59/20—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the epoxy compounds used
    • C08G59/32—Epoxy compounds containing three or more epoxy groups
    • C08G59/38—Epoxy compounds containing three or more epoxy groups together with di-epoxy compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
    • C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
    • C08G59/40—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the curing agents used
    • C08G59/42—Polycarboxylic acids; Anhydrides, halides or low molecular weight esters thereof

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Epoxy Resins (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
AU10964/88A 1987-02-18 1988-01-29 High temperature epoxy resin tooling composition Ceased AU605234B2 (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US015997 1987-02-18
US07/015,997 US4732962A (en) 1987-02-18 1987-02-18 High temperature epoxy tooling composition of bisphenol-A epoxy, trifunctional epoxy, anhydride curing agent and an imidazole catalyst

Publications (2)

Publication Number Publication Date
AU1096488A AU1096488A (en) 1988-08-25
AU605234B2 true AU605234B2 (en) 1991-01-10

Family

ID=21774790

Family Applications (1)

Application Number Title Priority Date Filing Date
AU10964/88A Ceased AU605234B2 (en) 1987-02-18 1988-01-29 High temperature epoxy resin tooling composition

Country Status (6)

Country Link
US (1) US4732962A (enExample)
EP (1) EP0279516B1 (enExample)
JP (1) JPS63223028A (enExample)
AU (1) AU605234B2 (enExample)
CA (1) CA1301984C (enExample)
DE (1) DE3882056T2 (enExample)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
AU618608B2 (en) * 1988-06-24 1992-01-02 Gm Global Technology Operations, Inc. High strength epoxy tooling compositions

Families Citing this family (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0668012B2 (ja) * 1987-09-15 1994-08-31 インターナショナル・ビジネス・マシーンズ・コーポレーション 封止用組成物及び前記組成物を用いた電子装置
US4925886A (en) * 1989-01-23 1990-05-15 General Motors Corporation High temperature epoxy tooling composition of bifunctional epoxy, trifunctional epoxy, anhydride, imidazole and interstitially matched filler
US4931528A (en) * 1989-05-08 1990-06-05 Texaco Chemical Company 1-isopropyl-2-methyl imidazole as an epoxy resin curative
EP0466950B1 (en) * 1990-07-16 1998-10-07 Nitto Denko Corporation Method for producing an epoxy resin composition for use in molding photosemiconductor
US5189118A (en) * 1991-02-28 1993-02-23 Texaco Chemical Company Mixtures of 1-isopropyl-2-aryl imidazole and 1-isopropyl-2-aryl imidazoline as epoxy resin curatives
US5260014A (en) * 1991-06-13 1993-11-09 Automotive Plastic Technologies Method of making a multilayer injection mold
JPH05214214A (ja) * 1992-02-06 1993-08-24 Mitsubishi Petrochem Co Ltd エポキシ樹脂組成物及びその硬化物
DE4211250A1 (de) * 1992-04-03 1993-10-07 Siemens Ag Reaktionsharze zum Vergießen von druckempfindlichen elektronischen Bauelementen
US5427676A (en) * 1993-08-10 1995-06-27 General Motors Corporation Method of making a cast-to-size mold for molding finished plastic parts
EP0888394B1 (en) * 1996-03-22 2001-07-25 Vantico AG One-component epoxy resin tooling material
US5691402A (en) * 1996-09-13 1997-11-25 Composite Technology Group, Llc Composite tooling material having vinyl ester resins and fillers
CN1197893C (zh) * 1997-07-24 2005-04-20 洛克泰特公司 用作充填密封材料的热固性树脂组合物
US6060540A (en) * 1998-02-13 2000-05-09 Landec Corporation Modeling pastes
US6632893B2 (en) 1999-05-28 2003-10-14 Henkel Loctite Corporation Composition of epoxy resin, cyanate ester, imidazole and polysulfide tougheners
US6309587B1 (en) 1999-08-13 2001-10-30 Jeffrey L. Gniatczyk Composite molding tools and parts and processes of forming molding tools
KR100417067B1 (ko) * 2000-12-05 2004-02-05 주식회사 엘지화학 에폭시 수지 조성물 및 이를 이용한 저유전율 동박 적층판
DE10144871A1 (de) * 2001-09-12 2003-03-27 Bosch Gmbh Robert Vergußmasse mit hoher thermischer Stabilität
US20040249044A1 (en) * 2003-02-18 2004-12-09 Tuan Nguyenquang High temperature resistant coating composition
EP1817148B1 (en) * 2004-11-17 2015-07-22 Huntsman Advanced Materials (Switzerland) GmbH Method of making high temperature resistant models or tools and compositon therefor
CN116018710B (zh) 2020-08-24 2024-05-03 绿色锂离子私人有限公司 用于锂离子电池回收中去除杂质的方法
FR3126335B1 (fr) * 2021-08-27 2024-03-22 Safran Aircraft Engines Procede de fabrication d’une piece composite, en particulier aeronautique et installation associee

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
AU4670885A (en) * 1984-07-17 1986-02-10 Dow Chemical Company, The Partially advanced epoxy resin compositions and products resulting from reacting and curing said compositions
AU6074886A (en) * 1985-07-31 1987-02-05 Dow Chemical Company, The Resin composition and a process for preparing laminates therefrom
AU3727889A (en) * 1988-06-24 1991-01-03 Gm Global Technology Operations, Inc. High strength epoxy tooling compositions

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3265647A (en) * 1962-01-29 1966-08-09 Armstrong Cork Co Trowelable epoxy-polyamide composition with graded filler
US3313007A (en) * 1963-08-22 1967-04-11 Gen Motors Corp Method of making sheet metal forming dies
US3329652A (en) * 1965-02-15 1967-07-04 Shell Oil Co Process for curing polyepoxides with anhydrides and activators therefor
DE1956066A1 (de) * 1968-12-10 1971-04-08 Pumpen & Verdichter Veb K Verfahren zum Herstellen von haertbaren Giessharzen fuer verschleissfeste,korrosionsbestaendige selbsttragende Bauteile
US3658750A (en) * 1969-02-13 1972-04-25 Hitachi Ltd Thermosetting resin composition and electrical appliances using the same
JPS5124399B2 (enExample) * 1973-03-19 1976-07-23
US4031059A (en) * 1974-01-21 1977-06-21 Martin Marietta Corporation Low density ablator compositions
US4002599A (en) * 1975-11-06 1977-01-11 Lord Corporation Epoxy resin compositions from glycidyl derivatives of aminophenols cured with tetracarboxylic dianhydrides
JPS559626A (en) * 1978-07-07 1980-01-23 Ube Ind Ltd Epoxy resin composition
US4346207A (en) * 1980-08-11 1982-08-24 Ciba-Geigy Corporation Flowable, curable epoxy resin mixture
US4374076A (en) * 1981-10-09 1983-02-15 Coors Porcelain Company Method for making cast epoxy resin bodies and epoxy formulation therefor
US4423094A (en) * 1982-11-12 1983-12-27 General Motors Corporation Durable cast epoxy tooling composition

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
AU4670885A (en) * 1984-07-17 1986-02-10 Dow Chemical Company, The Partially advanced epoxy resin compositions and products resulting from reacting and curing said compositions
AU6074886A (en) * 1985-07-31 1987-02-05 Dow Chemical Company, The Resin composition and a process for preparing laminates therefrom
AU3727889A (en) * 1988-06-24 1991-01-03 Gm Global Technology Operations, Inc. High strength epoxy tooling compositions

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
AU618608B2 (en) * 1988-06-24 1992-01-02 Gm Global Technology Operations, Inc. High strength epoxy tooling compositions

Also Published As

Publication number Publication date
JPH0577690B2 (enExample) 1993-10-27
US4732962A (en) 1988-03-22
EP0279516A3 (en) 1990-09-05
DE3882056D1 (de) 1993-08-05
AU1096488A (en) 1988-08-25
CA1301984C (en) 1992-05-26
EP0279516A2 (en) 1988-08-24
DE3882056T2 (de) 1993-10-07
JPS63223028A (ja) 1988-09-16
EP0279516B1 (en) 1993-06-30

Similar Documents

Publication Publication Date Title
EP0279516B1 (en) High temperature epoxy resin tooling composition
US4925886A (en) High temperature epoxy tooling composition of bifunctional epoxy, trifunctional epoxy, anhydride, imidazole and interstitially matched filler
US6379799B1 (en) Low moisture absorption epoxy resin systems with alkylated diamine hardeners
AU2001266730A1 (en) Low moisture absorption epoxy resin systems
US6602936B1 (en) Casting resin and process for the fabrication of resin molds
US5280053A (en) Machinable, high strength epoxy tooling compositions
US5322864A (en) Epoxy resin composition and cured product thereof
EP0199180B1 (en) Epoxy resin composition
AU618608B2 (en) High strength epoxy tooling compositions
US5045575A (en) Method of reducing voids in thermoset resin products
US8586654B2 (en) Anisotropic composite
EP3320013B1 (en) Stable high glass transition temperature epoxy resin system for making composites
JPS58138729A (ja) 熱硬化性成形組成物
JPH09137044A (ja) エポキシ樹脂組成物
JPS62241915A (ja) １２時間で硬化する工具用エポキシ樹脂組成物
JPH07330896A (ja) 架橋樹脂原液及び該架橋樹脂原液を用いる架橋樹脂の製造法
JP2025153516A (ja) エポキシ樹脂組成物、樹脂硬化物、繊維強化複合材料およびその製造方法
JPH02103223A (ja) エポキシ樹脂組成物
JPH0126326B2 (enExample)
JPH0656967A (ja) 注型用樹脂
CA2253622A1 (en) Cationic catalysts for epoxy resin formulations in pultrusion molding systems
JPH04178421A (ja) エポキシ樹脂組成物
JP2025059327A (ja) エポキシ樹脂組成物、成形品、繊維強化複合材料用成形材料および繊維強化複合材料
JPH02103222A (ja) エポキシ樹脂組成物
JPH06256464A (ja) 注型用樹脂