ATE222145T1 - Verfahren zum becshichten,verfahren zur herstellung von keramik-metall-strukturen, verfahren zum verbinden und so gebildete strukturen. - Google Patents

Verfahren zum becshichten,verfahren zur herstellung von keramik-metall-strukturen, verfahren zum verbinden und so gebildete strukturen.

Info

Publication number
ATE222145T1
ATE222145T1 AT96923296T AT96923296T ATE222145T1 AT E222145 T1 ATE222145 T1 AT E222145T1 AT 96923296 T AT96923296 T AT 96923296T AT 96923296 T AT96923296 T AT 96923296T AT E222145 T1 ATE222145 T1 AT E222145T1
Authority
AT
Austria
Prior art keywords
substrate
fluidizable material
powder particles
structures
wettable
Prior art date
Application number
AT96923296T
Other languages
English (en)
Inventor
Aleksander J Pyzik
Harold E Rossow
Jack J Ott
Uday V Deshmukh
Original Assignee
Dow Chemical Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Chemical Co filed Critical Dow Chemical Co
Application granted granted Critical
Publication of ATE222145T1 publication Critical patent/ATE222145T1/de

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D1/00—Processes for applying liquids or other fluent materials
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/45—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements
    • C04B41/4505—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements characterised by the method of application
    • C04B41/4507—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements characterised by the method of application using keying elements, e.g. particulate material, to facilitate the adherence of coating layers
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/006—Surface treatment of glass, not in the form of fibres or filaments, by coating with materials of composite character
    • C03C17/007—Surface treatment of glass, not in the form of fibres or filaments, by coating with materials of composite character containing a dispersed phase, e.g. particles, fibres or flakes, in a continuous phase
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B37/00—Joining burned ceramic articles with other burned ceramic articles or other articles by heating
    • C04B37/003—Joining burned ceramic articles with other burned ceramic articles or other articles by heating by means of an interlayer consisting of a combination of materials selected from glass, or ceramic material with metals, metal oxides or metal salts
    • C04B37/006—Joining burned ceramic articles with other burned ceramic articles or other articles by heating by means of an interlayer consisting of a combination of materials selected from glass, or ceramic material with metals, metal oxides or metal salts consisting of metals or metal salts
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/45—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/45—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements
    • C04B41/52—Multiple coating or impregnating multiple coating or impregnating with the same composition or with compositions only differing in the concentration of the constituents, is classified as single coating or impregnation
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C24/00—Coating starting from inorganic powder
    • C23C24/08—Coating starting from inorganic powder by application of heat or pressure and heat
    • C23C24/10—Coating starting from inorganic powder by application of heat or pressure and heat with intermediate formation of a liquid phase in the layer
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C26/00—Coating not provided for in groups C23C2/00 - C23C24/00
    • C23C26/02—Coating not provided for in groups C23C2/00 - C23C24/00 applying molten material to the substrate
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2217/00—Coatings on glass
    • C03C2217/40—Coatings comprising at least one inhomogeneous layer
    • C03C2217/42—Coatings comprising at least one inhomogeneous layer consisting of particles only
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2217/00—Coatings on glass
    • C03C2217/40—Coatings comprising at least one inhomogeneous layer
    • C03C2217/43—Coatings comprising at least one inhomogeneous layer consisting of a dispersed phase in a continuous phase
    • C03C2217/44—Coatings comprising at least one inhomogeneous layer consisting of a dispersed phase in a continuous phase characterized by the composition of the continuous phase
    • C03C2217/45—Inorganic continuous phases
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2217/00—Coatings on glass
    • C03C2217/40—Coatings comprising at least one inhomogeneous layer
    • C03C2217/43—Coatings comprising at least one inhomogeneous layer consisting of a dispersed phase in a continuous phase
    • C03C2217/46—Coatings comprising at least one inhomogeneous layer consisting of a dispersed phase in a continuous phase characterized by the dispersed phase
    • C03C2217/47—Coatings comprising at least one inhomogeneous layer consisting of a dispersed phase in a continuous phase characterized by the dispersed phase consisting of a specific material
    • C03C2217/475—Inorganic materials
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C04B2235/5418—Particle size related information expressed by the size of the particles or aggregates thereof
    • C04B2235/5436—Particle size related information expressed by the size of the particles or aggregates thereof micrometer sized, i.e. from 1 to 100 micron
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C04B2235/5418—Particle size related information expressed by the size of the particles or aggregates thereof
    • C04B2235/5445—Particle size related information expressed by the size of the particles or aggregates thereof submicron sized, i.e. from 0,1 to 1 micron
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/65—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes
    • C04B2235/658—Atmosphere during thermal treatment
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/65—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes
    • C04B2235/658—Atmosphere during thermal treatment
    • C04B2235/6581—Total pressure below 1 atmosphere, e.g. vacuum
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/02—Aspects relating to interlayers, e.g. used to join ceramic articles with other articles by heating
    • C04B2237/12—Metallic interlayers
    • C04B2237/121—Metallic interlayers based on aluminium
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/36—Non-oxidic
    • C04B2237/366—Aluminium nitride
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/58—Forming a gradient in composition or in properties across the laminate or the joined articles
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/59—Aspects relating to the structure of the interlayer
    • C04B2237/597—Aspects relating to the structure of the interlayer whereby the interlayer is continuous but porous, e.g. containing hollow or porous particles, macro- or micropores or cracks
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/61—Joining two substrates of which at least one is porous by infiltrating the porous substrate with a liquid, such as a molten metal, causing bonding of the two substrates, e.g. joining two porous carbon substrates by infiltrating with molten silicon
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/70—Forming laminates or joined articles comprising layers of a specific, unusual thickness
    • C04B2237/708—Forming laminates or joined articles comprising layers of a specific, unusual thickness of one or more of the interlayers
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T156/00—Adhesive bonding and miscellaneous chemical manufacture
    • Y10T156/10—Methods of surface bonding and/or assembly therefor
    • Y10T156/1002—Methods of surface bonding and/or assembly therefor with permanent bending or reshaping or surface deformation of self sustaining lamina
    • Y10T156/1036—Bending of one piece blank and joining edges to form article
    • Y10T156/1038—Hollow cylinder article

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Ceramic Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Structural Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Composite Materials (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • General Chemical & Material Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Dispersion Chemistry (AREA)
  • Laminated Bodies (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
  • Ceramic Products (AREA)
  • Chemically Coating (AREA)
AT96923296T 1995-06-23 1996-06-24 Verfahren zum becshichten,verfahren zur herstellung von keramik-metall-strukturen, verfahren zum verbinden und so gebildete strukturen. ATE222145T1 (de)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US08/494,125 US6123797A (en) 1995-06-23 1995-06-23 Method for coating a non-wetting fluidizable and material onto a substrate
PCT/US1996/010180 WO1997000734A1 (en) 1995-06-23 1996-06-24 Method of coating, method for making ceramic-metal structures, method for bonding, and structures formed thereby

Publications (1)

Publication Number Publication Date
ATE222145T1 true ATE222145T1 (de) 2002-08-15

Family

ID=23963145

Family Applications (1)

Application Number Title Priority Date Filing Date
AT96923296T ATE222145T1 (de) 1995-06-23 1996-06-24 Verfahren zum becshichten,verfahren zur herstellung von keramik-metall-strukturen, verfahren zum verbinden und so gebildete strukturen.

Country Status (9)

Country Link
US (1) US6123797A (de)
EP (1) EP0833698B1 (de)
JP (3) JP4115521B2 (de)
KR (1) KR100432075B1 (de)
AT (1) ATE222145T1 (de)
DE (1) DE69623020T2 (de)
MY (1) MY132223A (de)
TW (1) TW408092B (de)
WO (1) WO1997000734A1 (de)

Families Citing this family (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7163713B2 (en) 1999-07-31 2007-01-16 The Regents Of The University Of California Method for making dense crack free thin films
US6682842B1 (en) 1999-07-31 2004-01-27 The Regents Of The University Of California Composite electrode/electrolyte structure
US6605316B1 (en) 1999-07-31 2003-08-12 The Regents Of The University Of California Structures and fabrication techniques for solid state electrochemical devices
US7553573B2 (en) 1999-07-31 2009-06-30 The Regents Of The University Of California Solid state electrochemical composite
US6887361B1 (en) 2001-03-22 2005-05-03 The Regents Of The University Of California Method for making thin-film ceramic membrane on non-shrinking continuous or porous substrates by electrophoretic deposition
DE10114306B4 (de) 2001-03-23 2005-06-16 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Kompositschicht, Verfahren zur Herstellung einer Kompositschicht und deren Verwendung
ATE508488T1 (de) 2001-12-18 2011-05-15 Univ California Verfahren zur herstellung dichter dünnfilme
US6740441B2 (en) 2001-12-18 2004-05-25 The Regents Of The University Of California Metal current collect protected by oxide film
AU2003256251A1 (en) 2002-04-24 2003-11-10 The Regents Of The University Of California Planar electrochemical device assembly
WO2004033061A2 (en) * 2002-10-04 2004-04-22 The Regents Of The University Of California Fluorine separation and generation device
US8637127B2 (en) 2005-06-27 2014-01-28 Kennametal Inc. Composite article with coolant channels and tool fabrication method
US8186565B1 (en) 2006-10-18 2012-05-29 Dow Global Technologies Llc Method of bonding aluminum-boron-carbon composites
WO2008051588A2 (en) 2006-10-25 2008-05-02 Tdy Industries, Inc. Articles having improved resistance to thermal cracking
EP2285752A1 (de) * 2008-05-01 2011-02-23 Maxim Seleznev Kontinuierliche oder diskrete metallisierungsschicht auf einem keramiksubstrat
US8790439B2 (en) 2008-06-02 2014-07-29 Kennametal Inc. Composite sintered powder metal articles
US8030234B2 (en) * 2008-10-27 2011-10-04 Dow Global Technologies Llc Aluminum boron carbide composite and method to form said composite
JP4936261B2 (ja) * 2010-08-31 2012-05-23 美濃窯業株式会社 炭化ホウ素含有セラミックス接合体及び該接合体の製造方法
TWI466650B (zh) * 2010-11-08 2015-01-01 Ind Tech Res Inst 鍋具及其製造方法
US20140299781A1 (en) * 2011-06-30 2014-10-09 Lars Hultman Method for producing a neutron detector component comprising a boron carbide layer for use in a neutron detecting device
US8800848B2 (en) 2011-08-31 2014-08-12 Kennametal Inc. Methods of forming wear resistant layers on metallic surfaces
US9016406B2 (en) 2011-09-22 2015-04-28 Kennametal Inc. Cutting inserts for earth-boring bits
KR101493642B1 (ko) * 2012-02-28 2015-02-13 미노요교 가부시키가이샤 충격 흡수 부재 및 그 제조 방법
EP3210956B1 (de) * 2016-02-26 2018-04-11 Heraeus Deutschland GmbH & Co. KG Kupfer-keramik-verbund
DE102016203030B4 (de) 2016-02-26 2025-05-08 Heraeus Electronics Gmbh & Co. Kg Kupfer-Keramik-Verbund und ein diesen Verbund enthaltendes Modul
DE102017200945B3 (de) 2017-01-20 2018-05-09 Ford Global Technologies, Llc Verfahren zur Herstellung von Hybrid- Leichtbau- Bremsscheiben
EP3539887B1 (de) * 2018-03-16 2021-05-26 Schott AG Hohlkörper, insbesondere zum verpacken einer pharmazeutischen zusammensetzung, mit einer schicht aus glas und einem oberflächenbereich mit einem kontaktwinkel zum benetzen mit wasser
KR102414881B1 (ko) * 2020-01-31 2022-06-30 한양대학교 산학협력단 광 소결용 세라믹 페이스트 및 세라믹의 광 소결 방법
CN113774377B (zh) * 2021-09-15 2024-02-06 广西斯达奔材料科技有限公司 一种提高截齿耐磨性能的等离子熔覆焊涂层配方及工艺

Family Cites Families (34)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2264152A (en) * 1938-04-27 1941-11-25 Locke Insulator Corp Method of forming a metallic surface on ceramic bodies
US2902756A (en) * 1955-10-18 1959-09-08 Rca Corp Method and material for metallizing ceramics
US3291578A (en) * 1963-11-04 1966-12-13 Gen Electric Metallized semiconductor support and mounting structure
US4163736A (en) * 1971-06-16 1979-08-07 Johnson, Matthey & Co., Limited Method of producing platinum-clad articles
US4108822A (en) * 1973-01-16 1978-08-22 Albright & Wilson Ltd. Curable resin compositions
US3854332A (en) * 1973-09-24 1974-12-17 Us Navy Incendiary capture device
US4197104A (en) * 1978-09-21 1980-04-08 General Electric Company Magnetic tag process
US4657794A (en) * 1980-01-16 1987-04-14 Vereinigte Aluminium-Werke Aktiengeselschaft Binderless ceramic or ceramic oxide hollow body and method for its manufacture
US4521496A (en) * 1980-07-24 1985-06-04 Sara Raymond V Stress relieved metal/ceramic abradable seals
IL68291A (en) * 1983-04-05 1986-12-31 Yeheskel Twina Imprinter of credit card
JPS59194836A (ja) * 1983-04-19 1984-11-05 日本特殊陶業株式会社 セラミツクと金属の複合体
US4487157A (en) * 1983-11-07 1984-12-11 Hazelett Strip-Casting Corporation Machine for producing insulative and protective coatings on endless flexible metallic belts of continuous casting machines
US4588021A (en) * 1983-11-07 1986-05-13 Hazelett Strip-Casting Corporation Matrix coatings on endless flexible metallic belts for continuous casting machines method of forming such coatings and the coated belts
WO1985003436A1 (en) * 1984-02-10 1985-08-15 A/S Alfred Benzon Diffusion coated multiple-units dosage form
DK62184D0 (da) * 1984-02-10 1984-02-10 Benzon As Alfred Diffusionsovertrukket polydepotpraeparat
JPS60170287A (ja) * 1984-02-14 1985-09-03 信越化学工業株式会社 銅張積層基板
US4610320A (en) * 1984-09-19 1986-09-09 Directional Enterprises, Inc. Stabilizer blade
US5165983A (en) * 1984-09-30 1992-11-24 Kabushiki Kaisha Toshiba Method for production of aluminum nitride ceramic plate
US4915902A (en) * 1984-10-19 1990-04-10 Martin Marietta Corporation Complex ceramic whisker formation in metal-ceramic composites
JPS61268439A (ja) * 1985-05-22 1986-11-27 三菱油化株式会社 制振用複合鋼板
US4695517A (en) * 1985-05-31 1987-09-22 Ngk Spark Plug Co., Ltd. Composite layer aluminum nitride base sintered body
GB2185437B (en) * 1985-12-26 1989-12-06 Hitachi Chemical Co Ltd Ceramic coated laminate and process for producing the same
JPS6379777A (ja) * 1986-09-24 1988-04-09 科学技術庁金属材料技術研究所長 セラミツクス基板上への被覆体の製造法
US4789563A (en) * 1986-09-26 1988-12-06 Advanced Technology Materials, Inc. Sol gel formation of polysilicate, titania, and alumina interlayers for enhanced adhesion of metal films on substrates
DE3725455A1 (de) * 1987-07-31 1989-02-09 Siemens Ag Elektrisches vielschichtbauelement mit einem gesinterten, monolithischen keramikkoerper und verfahren zur herstellung des elektrischen vielschichtbauelementes
JP2544398B2 (ja) * 1987-08-27 1996-10-16 富士通株式会社 Ａ１ｎセラミックスのメタライズ方法
JPH0230689A (ja) * 1988-07-20 1990-02-01 Nippon Steel Corp アルミナセラミックスのメタライズ方法
US5020584A (en) * 1988-11-10 1991-06-04 Lanxide Technology Company, Lp Method for forming metal matrix composites having variable filler loadings and products produced thereby
JPH03146487A (ja) * 1989-10-30 1991-06-21 Sumitomo Electric Ind Ltd 金属化層を有する窒化アルミニウム焼結体の製造方法
US5133594A (en) * 1990-07-19 1992-07-28 Tufts University Transparent ion-blocking layer for electrochromic windows
JPH04342479A (ja) * 1991-05-16 1992-11-27 Nippon Cement Co Ltd セラミックスと金属との接合方法
JPH04342488A (ja) * 1991-05-20 1992-11-27 Isuzu Ceramics Kenkyusho:Kk 金属とセラミックスの複合体とその製造方法
JPH04342481A (ja) * 1991-05-21 1992-11-27 Isuzu Ceramics Kenkyusho:Kk セラミックスと金属の複合体構造とその製造方法
US5217589A (en) * 1991-10-03 1993-06-08 Motorola, Inc. Method of adherent metal coating for aluminum nitride surfaces

Also Published As

Publication number Publication date
JP2008024589A (ja) 2008-02-07
TW408092B (en) 2000-10-11
JP2008012922A (ja) 2008-01-24
JP4115521B2 (ja) 2008-07-09
KR100432075B1 (ko) 2004-08-16
DE69623020D1 (de) 2002-09-19
DE69623020T2 (de) 2003-04-17
JPH11508201A (ja) 1999-07-21
KR19990028330A (ko) 1999-04-15
US6123797A (en) 2000-09-26
EP0833698A1 (de) 1998-04-08
WO1997000734A1 (en) 1997-01-09
EP0833698B1 (de) 2002-08-14
MY132223A (en) 2007-09-28

Similar Documents

Publication Publication Date Title
DE69623020D1 (de) Verfahren zum becshichten,verfahren zur herstellung von keramik-metall-strukturen, verfahren zum verbinden und so gebildete strukturen.
SE8205274L (sv) Sker samt metod for tillverkning av detsamma
IE45250L (en) Coating glass or ceramic surfaces
DK0941078T3 (da) Fremgangsmåde og apparatur til coating af substrater til farmaceutisk anvendelse
ATE117438T1 (de) Verfahren zur herstellung einer kunststofflinse.
FI875153A7 (fi) Menetelmä kerrosten, kuten alustoilla olevien pintakerrosten paksuuden säätämiseksi ja/tai mittaamiseksi.
ATE148720T1 (de) Verfahren zur herstellung einer linse aus kunststoff
DE69129857D1 (de) Cvd- und pvd-beschichtete schneidwerkzeuge
DK0474369T3 (da) Diamantlignende kulstofbelægninger
NL184845C (nl) Werkwijze voor het bekleden van een substraat met een poreus oppervlak of een voorwerp.
CA2152769A1 (en) Synthesizing diamond film
ATE103806T1 (de) Verfahren zur herstellung einer nichtkohaesiven ueberzugsschicht.
DE69902449D1 (de) Verfahren zur herstellung einer gleitlagerbeschichtung
AU619980B2 (en) Ceramic material and method for producing the same
EP0856399A3 (de) Verbundstoff und uniaxial orientierter Verbundwerkstoff
AU5973199A (en) Method for the production of optical layers having uniform layer thickness
ATE111068T1 (de) Verfahren zur herstellung eines starren isolierenden feuerfesten materials, und verfahrensgemäss hergestelltes material.
DE3872498D1 (de) Verfahren zur herstellung korrosions-, verschleiss- und pressfester schichten.
ATE93763T1 (de) Strukturierung einer form-oberflaeche.
DE68921253D1 (de) Verfahren zur Abscheidung einer dünnen Supraleiterschicht.
WO1992019567A3 (en) Coatings for composite articles
ES2039271T3 (es) Procedimiento para la elaboracion de un revestimiento protector y/o decorativo de varias capas y compuestos de recubrimiento diluibles en agua.
NO891630L (no) Fremgangsmaate og anordning for fremstilling av diafragmer.
EP0873821A3 (de) Läppband
JPS5223136A (en) Removal of oil stain

Legal Events

Date Code Title Description
RER Ceased as to paragraph 5 lit. 3 law introducing patent treaties