WO2024084858A1 - 二次電池用電解液および二次電池 - Google Patents

二次電池用電解液および二次電池 Download PDF

Info

Publication number
WO2024084858A1
WO2024084858A1 PCT/JP2023/032776 JP2023032776W WO2024084858A1 WO 2024084858 A1 WO2024084858 A1 WO 2024084858A1 JP 2023032776 W JP2023032776 W JP 2023032776W WO 2024084858 A1 WO2024084858 A1 WO 2024084858A1
Authority
WO
WIPO (PCT)
Prior art keywords
negative electrode
secondary battery
group
electrolyte
positive electrode
Prior art date
Application number
PCT/JP2023/032776
Other languages
English (en)
French (fr)
Inventor
謙太郎 吉村
Original Assignee
株式会社村田製作所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社村田製作所 filed Critical 株式会社村田製作所
Publication of WO2024084858A1 publication Critical patent/WO2024084858A1/ja

Abstract

二次電池は、正極と、負極と、式（１）により表されるベンゾチアゾリン型化合物を含む電解液とを備える。

Description

二次電池用電解液および二次電池
　本技術は、二次電池用電解液および二次電池に関する。
　携帯電話機などの多様な電子機器が普及しているため、小型かつ軽量であると共に高エネルギー密度が得られる電源として二次電池の開発が進められている。この二次電池は、正極および負極と共に電解液（二次電池用電解液）を備えており、その二次電池の構成に関しては、様々な検討がなされている。
　具体的には、特定の構造を有するベンゾトリアゾール誘導体が電解液に含有されている（例えば、特許文献１，２参照。）。また、特定の構造を有するベンゾチアゾール誘導体が電解液に含有されている（例えば、特許文献３，４参照。）。
特開２００１－２７３９２７号公報 特表２０１３－５１３９２３号公報 特許第６０５６７２１号明細書 国際公開第２０１９／１８１２７８号パンフレット
　二次電池の構成に関する様々な検討がなされているが、その二次電池の電池特性は未だ十分でないため、改善の余地がある。
　優れた電池特性を得ることが可能である二次電池用電解液および二次電池が望まれている。
　本技術の一実施形態の二次電池用電解液は、式（１）により表されるベンゾチアゾリン型化合物を含むものである。
Figure JPOXMLDOC01-appb-C000003
 （Ｒ１～Ｒ１２のそれぞれは、水素、フッ素、アミノ基、アルキル基、シクロアルキル基、アリール基、アルコキシ基、フッ素化アルキル基、フッ素化シクロアルキル基、フッ素化アリール基、フッ素化アルコキシ基およびそれらの２種類以上が互いに結合された１価の結合基のうちのいずれかである。）
　本技術の一実施形態の二次電池は、正極と負極と電解液とを備え、その電解液が上記した本技術の一実施形態の二次電池用電解液の構成と同様の構成を有するものである。
　本技術の一実施形態の二次電池用電解液または二次電池によれば、その二次電池用電解液が式（１）に示したベンゾチアゾリン型化合物を含んでいるので、優れた電池特性を得ることができる。
　なお、本技術の効果は、必ずしもここで説明された効果に限定されるわけではなく、後述する本技術に関連する一連の効果のうちのいずれの効果でもよい。
本技術の一実施形態における二次電池の構成を表す断面図である。 図１に示した電池素子の構成を表す断面図である。 二次電池の適用例の構成を表すブロック図である。
　以下、本技術の一実施形態に関して、図面を参照しながら詳細に説明する。なお、説明する順序は、下記の通りである。

　１．二次電池用電解液
　　１－１．構成
　　１－２．製造方法
　　１－３．作用および効果
　２．二次電池
　　２－１．構成
　　２－２．動作
　　２－３．製造方法
　　２－４．作用および効果
　３．変形例
　４．二次電池の用途
＜１．二次電池用電解液＞
　まず、本技術の一実施形態の二次電池用電解液（以下、単に「電解液」と呼称する。）に関して説明する。
＜１－１．構成＞
　ここで説明する電解液は、電気化学デバイスである二次電池に用いられる液状の電解質である。ただし、電解液は、二次電池以外の他の電気化学デバイスに用いられてもよい。他の電気化学デバイスの具体例は、一次電池およびキャパシタなどである。
［ベンゾチアゾリン型化合物］
　電解液は、式（１）により表されるベンゾチアゾリン型化合物のうちのいずれか１種類または２種類以上を含んでいる。このベンゾチアゾリン型化合物は、式（１）から明らかなように、ベンゾチアゾリンでもよいし、そのベンゾチアゾリン型化合物の誘導体でもよい。
Figure JPOXMLDOC01-appb-C000004
 （Ｒ１～Ｒ１２のそれぞれは、水素、フッ素、アミノ基、アルキル基、シクロアルキル基、アリール基、アルコキシ基、フッ素化アルキル基、フッ素化シクロアルキル基、フッ素化アリール基、フッ素化アルコキシ基およびそれらの２種類以上が互いに結合された１価の結合基のうちのいずれかである。）
　電解液がベンゾチアゾリン型化合物を含んでいるのは、その電解液を用いた二次電池の充放電時において、そのベンゾチアゾリン型化合物に由来する良好な被膜が負極の表面に形成されるからである。この被膜は、緻密な膜構造を有していると共に、電気化学的に安定である。これにより、被膜を用いて負極の表面が電気化学的に保護されるため、その負極の表面における電解液の分解反応が抑制される。よって、充放電が繰り返されても、放電容量の減少が抑制される。
（構成）
　Ｒ１～Ｒ１２のそれぞれは、上記したように、水素（－Ｈ）、フッ素（－Ｆ）、アミノ基（－ＮＨ2 ）、アルキル基、シクロアルキル基、アリール基、アルコキシ基、フッ素化アルキル基、フッ素化シクロアルキル基、フッ素化アリール基、フッ素化アルコキシ基および結合基のうちのいずれかであれば、特に限定されない。
　アルキル基の炭素数は、特に限定されないため、そのアルキル基の具体例は、メチル基、エチル基、プロピル基およびブチル基などである。ただし、アルキル基は、鎖状でもよいし、分岐状でもよい。
　シクロアルキル基の炭素数は、特に限定されないため、そのシクロアルキル基の具体例は、シクロプロピル基、シクロブチル基、シクロペンチル基およびシクロヘキシル基などである。
　アリール基の炭素数は、特に限定されないため、そのアリール基の具体例は、フェニレン基およびナフチレン基などである。
　アルコキシ基の炭素数は、特に限定されないため、そのアルコキシ基の具体例は、メトキシ基、エトキシ基およびプロポキシ基などである。ただし、アルコキシ基は、鎖状でもよいし、分岐状でもよい。
　フッ素化アルキル基は、アルキル基に含まれている１個以上の水素がフッ素により置換された基である。フッ素化シクロアルキル基は、シクロアルキル基に含まれている１個以上の水素がフッ素により置換された基である。フッ素化アリール基は、アリール基に含まれている１個以上の水素がフッ素により置換された基である。フッ素化アルコキシ基は、アルコキシ基に含まれている１個以上の水素がフッ素により置換された基である。
　結合基は、水素、フッ素、アミノ基、アルキル基、シクロアルキル基、アリール基、アルコキシ基、フッ素化アルキル基、フッ素化シクロアルキル基、フッ素化アリール基およびフッ素化アルコキシ基のうちの２種類以上が互いに結合された１価の基である。結合基の種類は、特に限定されないが、具体的には、アルキル基とアミノ基とが互いに結合された基（アルキレン基とアミノ基とが互いに結合された基）などである。
（具体例）
　ベンゾチアゾリン型化合物の具体例は、式（１－１）～式（１－９）のそれぞれにより表される化合物などである。
Figure JPOXMLDOC01-appb-C000005
Figure JPOXMLDOC01-appb-C000006
（含有量）
　電解液におけるベンゾチアゾリン型化合物の含有量は、特に限定されないが、中でも、０．００１重量％～５重量％であることが好ましい。十分に良好な被膜が形成されるため、電解液の分解反応が十分に抑制されるからである。
　なお、ベンゾチアゾリン型化合物の含有量を測定する場合には、二次電池を解体することにより、電解液を回収したのち、その電解液を分析することにより、そのベンゾチアゾリン型化合物の含有量を算出する。電解液の分析方法は、特に限定されないが、具体的には、高周波誘導結合プラズマ（ＩＣＰ）発光分光分析法、核磁気共鳴分光法（ＮＭＲ）およびガスクロマトグラフ質量分析法（ＧＣ－ＭＳ）などのうちのいずれか１種類または２種類以上である。
［溶媒］
　なお、電解液は、さらに、溶媒を含んでいてもよい。この溶媒は、非水溶媒（有機溶剤）のうちのいずれか１種類または２種類以上を含んでおり、その非水溶媒を含んでいる電解液は、いわゆる非水電解液である。
　非水溶媒は、エステル類およびエーテル類などであり、より具体的には、炭酸エステル系化合物、カルボン酸エステル系化合物およびラクトン系化合物などである。
　炭酸エステル系化合物は、環状炭酸エステルおよび鎖状炭酸エステルなどである。環状炭酸エステルの具体例は、炭酸エチレンおよび炭酸プロピレンなどである。鎖状炭酸エステルの具体例は、炭酸ジメチル、炭酸ジエチルおよび炭酸エチルメチルなどである。
　カルボン酸エステル系化合物は、鎖状カルボン酸エステルなどである。鎖状カルボン酸エステルの具体例は、酢酸メチル、酢酸エチル、プロピオン酸メチル、プロピオン酸エチル、プロピオン酸プロピル、トリメチル酢酸エチル、酪酸メチルおよび酪酸エチルなどである。
　ラクトン系化合物は、ラクトンなどである。ラクトンの具体例は、γ－ブチロラクトンおよびγ－バレロラクトンなどである。
　なお、エーテル類は、１，２－ジメトキシエタン、テトラヒドロフラン、１，３－ジオキソランおよび１，４－ジオキサンなどでもよい。
（電解質塩）
　また、電解液は、さらに、電解質塩を含んでいてもよい。この電解質塩は、リチウム塩などの軽金属塩である。
　リチウム塩の具体例は、六フッ化リン酸リチウム（ＬｉＰＦ6 ）、四フッ化ホウ酸リチウム（ＬｉＢＦ4 ）、トリフルオロメタンスルホン酸リチウム（ＬｉＣＦ3 ＳＯ3 ）、ビス（フルオロスルホニル）イミドリチウム（ＬｉＮ（ＦＳＯ2 ）2 ）、ビス（トリフルオロメタンスルホニル）イミドリチウム（ＬｉＮ（ＣＦ3 ＳＯ2 ）2 ）、リチウムトリス（トリフルオロメタンスルホニル）メチド（ＬｉＣ（ＣＦ3 ＳＯ2 ）3 ）、ビス（オキサラト）ホウ酸リチウム（ＬｉＢ（Ｃ2 Ｏ4 ）2 ）、ジフルオロオキサラトホウ酸リチウム（ＬｉＢＦ2 （Ｃ2 Ｏ4 ））、ジフルオロジ（オキサラト）ホウ酸リチウム（ＬｉＰＦ2 （Ｃ2 Ｏ4 ）2 ）、テトラフルオロオキサラトリン酸リチウム（ＬｉＰＦ4 （Ｃ2 Ｏ4 ））、モノフルオロリン酸リチウム（Ｌｉ2 ＰＦＯ3 ）およびジフルオロリン酸リチウム（ＬｉＰＦ2 Ｏ2 ）などである。
　電解質塩の含有量は、特に限定されないが、具体的には、溶媒に対して０．３ｍｏｌ／ｋｇ～３．０ｍｏｌ／ｋｇである。高いイオン伝導性が得られるからである。
（添加剤）
　なお、電解液は、さらに、添加剤のうちのいずれか１種類または２種類以上を含んでいてもよい。
（不飽和環状炭酸エステル、フッ素化環状炭酸エステルおよびシアノ化環状炭酸エステル）
　具体的には、添加剤は、不飽和環状炭酸エステル、フッ素化環状炭酸エステルおよびシアノ化環状炭酸エステルのうちのいずれか１種類または２種類以上である。電解液の電気化学的安定性が向上するからである。これにより、二次電池の充放電時において電解液の分解反応がより抑制されるため、充放電が繰り返されても放電容量の減少がより抑制される。
　不飽和環状炭酸エステルは、不飽和炭素結合（炭素間二重結合）を含む環状炭酸エステルである。不飽和炭素結合の数は、特に限定されないため、１個だけでもよいし、２個以上でもよい。
　この不飽和環状炭酸エステルは、炭酸ビニレン系化合物、炭酸ビニルエチレン系化合物および炭酸メチレンエチレン系化合物のうちのいずれか１種類または２種類以上を含んでいる。
　炭酸ビニレン系化合物は、炭酸ビニレン型の構造を有する不飽和環状炭酸エステルである。炭酸ビニレン系化合物の具体例は、炭酸ビニレン（１，３－ジオキソール－２－オン）、炭酸メチルビニレン（４－メチル－１，３－ジオキソール－２－オン）、炭酸エチルビニレン（４－エチル－１，３－ジオキソール－２－オン）、４，５－ジメチル－１，３－ジオキソール－２－オン、４，５－ジエチル－１，３－ジオキソール－２－オン、４－フルオロ－１，３－ジオキソール－２－オンおよび４－トリフルオロメチル－１，３－ジオキソール－２－オンなどである。
　炭酸ビニルエチレン系化合物は、炭酸ビニルエチレン型の構造を有する不飽和環状炭酸エステルである。炭酸ビニルエチレン系化合物の具体例は、炭酸ビニルエチレン（４－ビニル－１，３－ジオキソラン－２－オン）、４－メチル－４－ビニル－１，３－ジオキソラン－２－オン、４－エチル－４－ビニル－１，３－ジオキソラン－２－オン、４－ｎ－プロピル－４－ビニル－１，３－ジオキソラン－２－オン、５－メチル－４－ビニル－１，３－ジオキソラン－２－オン、４，４－ジビニル－１，３－ジオキソラン－２－オンおよび４，５－ジビニル－１，３－ジオキソラン－２－オンなどである。
　炭酸メチレンエチレン系化合物は、炭酸メチレンエチレン型の構造を有する不飽和環状炭酸エステルである。炭酸メチレンエチレン系化合物の具体例は、炭酸メチレンエチレン（４－メチレン－１，３－ジオキソラン－２－オン）、４，４－ジメチル－５－メチレン－１，３－ジオキソラン－２－オンおよび４，４－ジエチル－５－メチレン－１，３－ジオキソラン－２－オンなどである。ここでは、炭酸メチレンエチレン系化合物として、１個のメチレン基だけを有する化合物を例示したが、その炭酸メチレンエチレン系化合物は、２個以上のメチレン基を有していてもよい。
　なお、不飽和炭素結合を含む環状炭酸エステルは、フッ素化環状炭酸エステルおよびシアノ化環状炭酸エステルのいずれかには該当せずに、不飽和環状炭酸エステルに該当することとする。
　フッ素化環状炭酸エステルは、フッ素を構成元素として含む環状炭酸エステルである。フッ素の数は、特に限定されないため、１個だけでもよいし、２個以上でもよい。すなわち、フッ素化環状炭酸エステルは、環状炭酸エステルのうちの１個または２個以上の水素がフッ素により置換された化合物である。
　フッ素化環状炭酸エステルの具体例は、フルオロ炭酸エチレン（４－フルオロ－１，３－ジオキソラン－２－オン）およびジフルオロ炭酸エチレン（４，５－ジフルオロ－１，３－ジオキソラン－２－オン）などである。
　なお、フッ素を構成元素として含む環状炭酸エステルは、不飽和環状炭酸エステルおよびシアノ化環状炭酸エステルのいずれかには該当せずに、フッ素化環状炭酸エステルに該当することとする。
　シアノ化環状炭酸エステルは、シアノ基を含む環状炭酸エステルである。シアノ基の数は、特に限定されないため、１個だけでもよいし、２個以上でもよい。すなわち、シアノ化環状炭酸エステルは、環状炭酸エステルのうちの１個または２個以上の水素がシアノ基により置換された化合物である。
　シアノ化環状炭酸エステルの具体例は、シアノ炭酸エチレン（４－シアノ－１，３－ジオキソラン－２－オン）およびジシアノ炭酸エチレン（４，５－ジシアノ－１，３－ジオキソラン－２－オン）などである。
　なお、シアノ基を含む環状炭酸エステルは、不飽和環状炭酸エステルおよびフッ素化環状炭酸エステルのいずれかには該当せずに、シアノ化環状炭酸エステルに該当することとする。
（スルホン酸エステル、硫酸エステル、亜硫酸エステル、ジカルボン酸無水物、ジスルホン酸無水物、スルホン酸カルボン酸無水物およびスルホ安息香酸イミド）
　また、添加剤は、スルホン酸エステル、硫酸エステル、亜硫酸エステル、ジカルボン酸無水物、ジスルホン酸無水物、スルホン酸カルボン酸無水物およびスルホ安息香酸イミドのうちのいずれか１種類または２種類以上である。電解液の電気化学的安定性が向上するからである。これにより、二次電池の充放電時において電解液の分解反応がより抑制されるため、充放電が繰り返されても放電容量の減少がより抑制される。
　スルホン酸エステルの具体例は、１，３－プロパンスルトン、１－プロペン－１，３－スルトン、１，４－ブタンスルトン、２，４－ブタンスルトンおよびメタンスルホン酸プロパルギルエステルなどである。
　硫酸エステルの具体例は、１，３，２－ジオキサチオラン２，２－ジオキシド、１，３，２－ジオキサチアン２，２－ジオキシド、４－メチルスルホニルオキシメチル－２，２－ジオキソ－１，３，２－ジオキサチオランなどである。
　亜硫酸エステルの具体例は、１，３－プロパンスルトン、１－プロペン－１，３－スルトン、１，４－ブタンスルトン、２，４－ブタンスルトンおよびメタンスルホン酸プロパルギルエステルなどである。亜硫酸エステルの具体例は、１，３，２－ジオキサチオラン２－オキシドおよび４－メチル－１，３，２－ジオキサチオラン２－オキシドなどである。
　ジカルボン酸無水物の具体例は、１，４－ジオキサン－２，６－ジオン、コハク酸無水物およびグルタル酸無水物などである。
　ジスルホン酸無水物の具体例は、１，２－エタンジスルホン酸無水物、１，３－プロパンジジスルホン酸無水物およびヘキサフルオロ１，３－プロパンジスルホン酸無水物などである。
　スルホン酸カルボン酸無水物の具体例は、２－スルホ安息香酸無水物および２，２－ジオキソオキサチオラン－５－オンなどである。
　スルホ安息香酸イミドの具体例は、ｏ－スルホベンズイミドおよびＮ－メチルサッカリンなどである。
（ニトリル化合物）
　また、添加剤は、ニトリル化合物である。電解液の電気化学的安定性が向上するからである。これにより、充放電時において電解液の分解反応がより抑制されるため、充放電が繰り返されても放電容量の減少がより抑制される。この場合には、電解液の分解反応に起因するガスの発生も抑制される。
　このニトリル化合物は、１個または２個以上のシアノ基（－ＣＮ）を含む化合物である。ニトリル化合物の具体例は、オクタンニトリル、ベンゾニトリル、フタロニトリル、スクシノニトリル、グルタロニトリル、アジポニトリル、セバコニトリル、１，３，６－ヘキサントリカルボニトリル、３，３’－オキシジプロピオニトリル、３－ブトキシプロピオニトリル、エチレングリコールビスプロピオニトリルエーテル、１，２，２，３－テトラシアノプロパン、テトラシアノプロパン、フマロニトリル、７，７，８，８－テトラシアノキノジメタン、シクロペンタンカルボニトリル、１，３，５－シクロヘキサントリカルボニトリルおよび１，３－ビス（ジシアノメチリデン）インダンなどである。
　ただし、上記したシアノ化環状炭酸エステルは、ここで説明したニトリル化合物から除かれる。
＜１－２．製造方法＞
　電解液を製造する場合には、溶媒に電解質塩を添加したのち、その溶媒にベンゾチアゾリン型化合物を添加する。これにより、溶媒中において電解質塩およびベンゾチアゾリン型化合物のそれぞれが溶解または分散されるため、電解液が調製される。
＜１－３．作用および効果＞
　この電解液によれば、その電解液がベンゾチアゾリン型化合物を含んでいる。
　この場合には、上記したように、電解液を用いた二次電池の充放電時において、ベンゾチアゾリン型化合物に由来する良好な被膜が負極の表面に形成されるため、その被膜を用いて負極の表面が電気化学的に保護される。これにより、負極の表面における電解液の分解反応が抑制されるため、充放電が繰り返されても放電容量の減少が抑制される。よって、優れた電池特性を有する二次電池を実現することができる。
ができる。
　特に、電解液におけるベンゾチアゾリン型化合物の含有量が０．００１重量％～５重量％であれば、十分に良好な被膜が形成される。よって、電解液の分解反応が十分に抑制されるため、より高い効果を得ることができる。
　また、電解液が不飽和環状炭酸エステル、フッ素化環状炭酸エステルおよびシアノ化環状炭酸エステルのうちのいずれか１種類または２種類以上を含んでいれば、電解液の分解反応がより抑制されるため、より高い効果を得ることができる。
　また、電解液がスルホン酸エステル、硫酸エステル、亜硫酸エステル、ジカルボン酸無水物、ジスルホン酸無水物、スルホン酸カルボン酸無水物およびスルホ安息香酸イミドのうちのいずれか１種類または２種類以上を含んでいれば、電解液の分解反応がより抑制されるため、より高い効果を得ることができる。
＜２．二次電池＞
　次に、上記した電解液を用いた本技術の一実施形態の二次電池に関して説明する。
　ここで説明する二次電池は、電極反応物質の吸蔵放出を利用して電池容量が得られる二次電池であり、正極および負極と共に電解液を備えている。
　負極の充電容量は、正極の放電容量よりも大きいことが好ましい。すなわち、負極の単位面積当たりの電気化学容量は、正極の単位面積当たりの電気化学容量よりも大きいことが好ましい。充電途中において負極の表面に電極反応物質が析出することを防止するためである。
　電極反応物質の種類は、特に限定されないが、具体的には、アルカリ金属およびアルカリ土類金属などの軽金属である。アルカリ金属は、リチウム、ナトリウムおよびカリウムなどであると共に、アルカリ土類金属は、ベリリウム、マグネシウムおよびカルシウムなどである。
　以下では、電極反応物質がリチウムである場合を例に挙げる。リチウムの吸蔵放出を利用して電池容量が得られる二次電池は、いわゆるリチウムイオン二次電池である。このリチウムイオン二次電池では、リチウムがイオン状態で吸蔵放出される。
＜２－１．構成＞
　図１は、二次電池の断面構成を表していると共に、図２は、図１に示した電池素子２０の断面構成を表している。
　この二次電池は、図１および図２に示したように、主に、電池缶１１と、一対の絶縁板１２，１３と、電池素子２０と、正極リード２５と、負極リード２６とを備えている。ここで説明する二次電池は、円筒状の電池缶１１の内部に電池素子２０が収納されている円筒型の二次電池である。
［電池缶］
　電池缶１１は、図１に示したように、電池素子２０などを収納する収納部材である。この電池缶１１は、開放された一端部および閉塞された他端部を有しているため、中空の構造を有している。また、電池缶１１は、鉄、アルミニウム、鉄合金およびアルミニウム合金などの金属材料のうちのいずれか１種類または２種類以上を含んでいる。なお、電池缶１１の表面には、ニッケルなどの金属材料が鍍金されていてもよい。
　電池缶１１の開放された一端部には、電池蓋１４、安全弁機構１５および熱感抵抗素子（ＰＴＣ素子）１６がガスケット１７を介して加締められている。これにより、電池缶１１は、電池蓋１４により密閉されている。ここでは、電池蓋１４は、電池缶１１の形成材料と同様の材料を含んでいる。安全弁機構１５およびＰＴＣ素子１６のそれぞれは、電池蓋１４の内側に設けられており、その安全弁機構１５は、ＰＴＣ素子１６を介して電池蓋１４と電気的に接続されている。ガスケット１７は、絶縁性材料を含んでおり、そのガスケット１７の表面には、アスファルトなどが塗布されていてもよい。
　この安全弁機構１５では、内部短絡および外部加熱などに起因して電池缶１１の内圧が一定以上に到達すると、ディスク板１５Ａが反転するため、電池蓋１４と電池素子２０との電気的接続が切断される。大電流に起因する異常な発熱を防止するために、ＰＴＣ素子１６の電気抵抗は、温度の上昇に応じて増加する。
［絶縁板］
　絶縁板１２，１３は、図１に示したように、電池素子２０を介して互いに対向するように配置されている。これにより、電池素子２０は、絶縁板１２，１３により挟まれている。
［電池素子］
　電池素子２０は、図１および図２に示したように、正極２１と、負極２２と、セパレータ２３と、電解液（図示せず）とを含む発電素子である。
　この電池素子２０は、いわゆる巻回電極体である。すなわち、正極２１および負極２２は、セパレータ２３を介して互いに積層されていると共に、そのセパレータ２３を介して互いに対向しながら巻回されている。電池素子２０の巻回中心に設けられている空間２０Ｓには、センターピン２４が挿入されている。ただし、センターピン２４は省略されてもよい。
（正極）
　正極２１は、図２に示したように、正極集電体２１Ａおよび正極活物質層２１Ｂを含んでいる。
　正極集電体２１Ａは、正極活物質層２１Ｂが設けられる一対の面を有している。この正極集電体２１Ａは、金属材料などの導電性材料を含んでおり、その導電性材料の具体例は、アルミニウムなどである。
　正極活物質層２１Ｂは、リチウムを吸蔵放出する正極活物質のうちのいずれか１種類または２種類以上を含んでいる。ただし、正極活物質層２１Ｂは、さらに、正極結着剤および正極導電剤などの他の材料のうちのいずれか１種類または２種類以上を含んでいてもよい。正極活物質層２１Ｂの形成方法は、特に限定されないが、具体的には、塗布法などである。
　ここでは、正極活物質層２１Ｂは、正極集電体２１Ａの両面に設けられているため、正極２１は、２個の正極活物質層２１Ｂを含んでいる。ただし、正極活物質層２１Ｂは、正極２１が負極２２に対向する側において正極集電体２１Ａの片面だけに設けられているため、正極２１は、１個の正極活物質層２１Ｂだけを含んでいてもよい。
　正極活物質の種類は、特に限定されないが、具体的には、リチウム含有化合物などである。このリチウム含有化合物は、リチウムと共に１種類または２種類以上の遷移金属元素を構成元素として含む化合物であり、さらに、１種類または２種類以上の他元素を構成元素として含んでいてもよい。他元素の種類は、リチウムおよび遷移金属元素のそれぞれ以外の元素であれば、特に限定されないが、具体的には、長周期型周期表中の２族～１５族に属する元素である。リチウム含有化合物の種類は、特に限定されないが、具体的には、酸化物、リン酸化合物、ケイ酸化合物およびホウ酸化合物などである。
　酸化物の具体例は、ＬｉＮｉＯ2 、ＬｉＣｏＯ2 、ＬｉＣｏ0.98Ａｌ0.01Ｍｇ0.01Ｏ2 、ＬｉＮｉ0.5 Ｃｏ0.2 Ｍｎ0.3 Ｏ2 およびＬｉＭｎ2 Ｏ4 などである。リン酸化合物の具体例は、ＬｉＦｅＰＯ4 、ＬｉＭｎＰＯ4 およびＬｉＦｅ0.5 Ｍｎ0.5 ＰＯ4 などである。
　正極結着剤は、合成ゴムおよび高分子化合物などの材料のうちのいずれか１種類または２種類以上を含んでいる。合成ゴムの具体例は、スチレンブタジエン系ゴム、フッ素系ゴムおよびエチレンプロピレンジエンなどである。高分子化合物の具体例は、ポリフッ化ビニリデン、ポリイミドおよびカルボキシメチルセルロースなどである。
　正極導電剤は、炭素材料、金属材料および導電性高分子化合物などの導電性材料のうちのいずれか１種類または２種類以上を含んでおり、その炭素材料の具体例は、黒鉛、カーボンブラック、アセチレンブラックおよびケッチェンブラックなどである。
（負極）
　負極２２は、図２に示したように、負極集電体２２Ａおよび負極活物質層２２Ｂを含んでいる。
　負極集電体２２Ａは、負極活物質層２２Ｂが設けられる一対の面を有している。この負極集電体２２Ａは、金属材料などの導電性材料を含んでおり、その導電性材料の具体例は、銅などである。
　負極活物質層２２Ｂは、リチウムを吸蔵放出する負極活物質のうちのいずれか１種類または２種類以上を含んでいる。ただし、負極活物質層２２Ｂは、さらに、負極結着剤および負極導電剤などの他の材料のうちのいずれか１種類または２種類以上を含んでいてもよい。負極活物質層２２Ｂの形成方法は、特に限定されないが、具体的には、塗布法、気相法、液相法、溶射法および焼成法（焼結法）などのうちのいずれか１種類または２種類以上である。
　ここでは、負極活物質層２２Ｂは、負極集電体２２Ａの両面に設けられているため、負極２２は、２個の負極活物質層２２Ｂを含んでいる。ただし、負極活物質層２２Ｂは、負極２２が正極２１に対向する側において負極集電体２２Ａの片面だけに設けられているため、負極２２は、１個の負極活物質層２２Ｂだけを含んでいてもよい。
　負極活物質の種類は、特に限定されないが、具体的には、炭素材料および金属系材料などである。高いエネルギー密度が得られるからである。
　炭素材料の具体例は、易黒鉛化性炭素、難黒鉛化性炭素および黒鉛（天然黒鉛および人造黒鉛）などである。
　金属系材料は、リチウムと合金を形成可能である金属元素および半金属元素のうちのいずれか１種類または２種類以上を構成元素として含む材料であり、その金属元素および半金属元素の具体例は、ケイ素およびスズなどである。この金属系材料は、単体でもよいし、合金でもよいし、化合物でもよいし、それらの２種類以上の混合物でもよいし、それらの２種類以上の相を含む材料でもよい。金属系材料の具体例は、ＴｉＳｉ2 およびＳｉＯx （０＜ｘ≦２または０．２＜ｘ＜１．４）などである。
　ここで説明した「単体」は、あくまで一般的な単体を意味しているため、微量の不純物を含んでいてもよい。すなわち、単体の純度は、必ずしも１００％に限られない。また、ここで説明した「合金」には、２種類以上の金属元素を構成元素として含む材料だけでなく、１種類または２種類以上の金属元素と１種類または２種類以上の半金属元素とを構成元素として含む材料も含まれる。また、「合金」は、１種類または２種類以上の非金属元素を構成元素として含んでいてもよい。
　中でも、負極材料は、金属系材料を含んでいることが好ましく、ケイ素含有材料を含んでいることがより好ましい。十分に高いエネルギー密度が得られると共に、ベンゾチアゾリン型化合物を利用して電解液の分解反応が十分に抑制されるからである。このケイ素含有材料は、ケイ素を構成元素として含む材料である。上記したように、ケイ素含有材料は、ケイ素の単体でもよいし、ケイ素の合金でもよいし、ケイ素の化合物でもよいし、それらの２種類以上の混合物でもよいし、それらの２種類以上の相を含む材料でもよい。
　ケイ素の合金は、ケイ素以外の構成元素として、スズ、ニッケル、銅、鉄、コバルト、マンガン、亜鉛、インジウム、銀、チタン、ゲルマニウム、ビスマス、アンチモンおよびクロムなどの金属元素のうちのいずれか１種類または２種類以上を含んでいる。ケイ素の化合物は、ケイ素以外の構成元素として、炭素および酸素などの非金属元素のうちのいずれか１種類または２種類以上を含んでいる。ただし、ケイ素の化合物は、ケイ素以外の構成元素として、さらに、ケイ素の合金に関して説明した一連の金属元素のうちのいずれか１種類または２種類以上を含んでいてもよい。
　ケイ素の合金の具体例は、上記したＴｉＳｉ2 の他、ＳｉＢ4 、ＳｉＢ6 、Ｍｇ2 Ｓｉ、Ｎｉ2 Ｓｉ、ＭｏＳｉ2 、ＣｏＳｉ2 、ＮｉＳｉ2 、ＣａＳｉ2 、ＣｒＳｉ2 、Ｃｕ5 Ｓｉ、ＦｅＳｉ2 、ＭｎＳｉ2 、ＮｂＳｉ2 、ＴａＳｉ2 、ＶＳｉ2 、ＷＳｉ2 、ＺｎＳｉ2 およびＳｉＣなどである。ただし、ケイ素の合金の組成（ケイ素と金属元素との混合比）は、任意に変更可能である。
　ケイ素の化合物の具体例は、上記したＳｉＯx 他、Ｓｉ3 Ｎ4 、Ｓｉ2 Ｎ2 ＯおよびＬｉＳｉＯなどである。
　特に、負極活物質は、炭素材料およびケイ素含有材料の双方を含んでいることが好ましい。充放電時において、電池容量が担保されながら、負極活物質層２２Ｂの破損および脱落などが防止されるからである。
　詳細には、金属系材料であるケイ素含有材料は、理論容量が高いという利点を有している反面、充放電時において激しく膨張収縮しやすいという懸念点を有している。一方、炭素材料は、理論容量が低いという懸念点を有している反面、充放電時において膨張収縮しにくいという利点を有している。よって、炭素材料とケイ素含有材料とを併用することにより、高い理論容量が得られながら、充放電時において負極活物質層２２Ｂの膨張収縮が抑制される。これにより、上記したように、電池容量が担保されながら、負極活物質層２２Ｂの破損および脱落などが防止される。
　負極結着剤に関する詳細は、正極結着剤に関する詳細と同様であると共に、負極導電剤に関する詳細は、正極導電剤に関する詳細と同様である。
（セパレータ）
　セパレータ２３は、図２に示したように、正極２１と負極２２との間に介在している絶縁性の多孔質膜であり、その正極２１と負極２２との接触（短絡）を防止しながらリチウムイオンを通過させる。このセパレータ２３は、ポリエチレンなどの高分子化合物を含んでいる。
（電解液）
　電解液は、正極２１、負極２２およびセパレータ２３のそれぞれに含浸されており、上記した構成を有している。すなわち、電解液は、ベンゾチアゾリン型化合物を含んでいる。
［正極リードおよび負極リード］
　正極リード２５は、図１および図２に示したように、正極２１の正極集電体２１Ａに接続されており、アルミニウムなどの導電性材料を含んでいる。この正極リード２５は、安全弁機構１５を介して電池蓋１４と電気的に接続されている。
　負極リード２６は、図１および図２に示したように、負極２２の負極集電体２２Ａに接続されており、ニッケルなどの導電性材料を含んでいる。この負極リード２６は、電池缶１１と電気的に接続されている。
＜２－２．動作＞
　二次電池は、充放電時において、以下のように動作する。
　充電時には、電池素子２０において、正極２１からリチウムが放出されると共に、そのリチウムが電解液を介して負極２２に吸蔵される。一方、放電時には、電池素子２０において、負極２２からリチウムが放出されると共に、そのリチウムが電解液を介して正極２１に吸蔵される。これらの充電時および放電時には、リチウムがイオン状態で吸蔵および放出される。
＜２－３．製造方法＞
　二次電池を製造する場合には、以下で説明する一例の手順により、正極２１および負極２２を作製すると共に、その正極２１および負極２２と共に電解液を用いて二次電池を組み立てたのち、その組み立て後の二次電池の安定化処理を行う。なお、電解液を調製する手順は、上記した通りである。
［正極の作製］
　最初に、正極活物質、正極結着剤および正極導電剤を互いに混合させることにより、正極合剤とする、続いて、溶媒に正極合剤を投入することにより、ペースト状の正極合剤スラリーを調製する。この溶媒は、水性溶媒でもよいし、有機溶剤でもよい。続いて、正極集電体２１Ａの両面に正極合剤スラリーを塗布することにより、正極活物質層２１Ｂを形成する。最後に、ロールプレス機などを用いて正極活物質層２１Ｂを圧縮成型してもよい。この場合には、正極活物質層２１Ｂを加熱してもよいし、圧縮成型を複数回繰り返してもよい。これにより、正極集電体２１Ａの両面に正極活物質層２１Ｂが形成されるため、正極２１が作製される。
［負極の作製］
　上記した正極２１の作製手順と同様の手順により、負極２２を形成する。具体的には、最初に、負極活物質、負極結着剤および負極導電剤が互いに混合された混合物（負極合剤）を溶媒に投入することにより、ペースト状の負極合剤スラリーを調製する。続いて、負極集電体２２Ａの両面に負極合剤スラリーを塗布することにより、負極活物質層２２Ｂを形成する。最後に、負極活物質層２２Ｂを圧縮成型してもよい。これにより、負極集電体２２Ａの両面に負極活物質層２２Ｂが形成されるため、負極２２が作製される。
［二次電池の組み立て］
　最初に、溶接法などの接合法を用いて、正極２１の正極集電体２１Ａに正極リード２５を接続させると共に、溶接法などの接合法を用いて、負極２２の負極集電体２２Ａに負極リード２６を接続させる。続いて、セパレータ２３を介して正極２１および負極２２を互いに積層させたのち、その正極２１、負極２２およびセパレータ２３を巻回させることにより、空間２０Ｓを有する巻回体（図示せず）を作製する。この巻回体は、正極２１、負極２２およびセパレータ２３のそれぞれに電解液が含浸されていないことを除いて、電池素子２０の構成と同様の構成を有している。続いて、巻回体の空間２０Ｓにセンターピン２４を挿入する。
　続いて、絶縁板１２，１３により巻回体が挟まれた状態において、電池缶１１の内部に巻回体および絶縁板１２，１３を収納する。この場合には、溶接法などの接合法を用いて、正極リード２５を安全弁機構１５に接続させると共に、溶接法などの接合法を用いて、負極リード２６を電池缶１１に接続させる。続いて、電池缶１１の内部に電解液を注入することにより、その電解液を巻回体に含浸させる。これにより、正極２１、負極２２およびセパレータ２３のそれぞれに電解液が含浸されるため、電池素子２０が作製される。
　最後に、電池缶１１の内部に電池蓋１４、安全弁機構１５およびＰＴＣ素子１６を収納したのち、ガスケット１７を介して電池缶１１を加締める。これにより、電池缶１１に電池蓋１４、安全弁機構１５およびＰＴＣ素子１６が固定されると共に、その電池缶１１の内部に電池素子２０が封入されるため、二次電池が組み立てられる。
［二次電池の安定化］
　組み立て後の二次電池を充放電させる。環境温度、充放電回数（サイクル数）および充放電条件などの各種条件は、任意に設定可能である。これにより、正極２１および負極２２のそれぞれの表面に被膜が形成されるため、電池素子２０の状態が電気化学的に安定化する。よって、二次電池が完成する。
＜２－４．作用および効果＞
　この二次電池によれば、電解液が上記した構成を有している。この場合には、上記した理由により、充放電が繰り返されても、負極２２の表面における電解液の分解反応が抑制されるため、放電容量の減少が抑制される。よって、優れた電池特性を得ることができる。
　特に、負極２２が負極活物質としてケイ素含有材料を含んでいれば、十分に高いエネルギー密度が得られると共に、ベンゾチアゾリン型化合物を利用して電解液の分解反応が十分に抑制されるため、より高い効果を得ることができる。
　また、二次電池がリチウムイオン二次電池であれば、リチウムの吸蔵放出を利用して十分な電池容量が安定に得られるため、より高い効果を得ることができる。
　この二次電池に関する他の作用および効果は、上記した電解液に関する他の作用および効果と同様である。
＜３．変形例＞
　上記した二次電池の構成は、以下で説明するように、適宜、変更可能である。ただし、以下で説明する一連の変形例のうちの任意の２種類以上は、互いに組み合わされてもよい。
［変形例１］
　二次電池の電池構造が円筒型である場合に関して説明した。しかしながら、ここでは具体的に図示しないが、電池構造の種類は、特に限定されないため、ラミネートフィルム型、角型、コイン型およびボタン型などでもよい。
［変形例２］
　多孔質膜であるセパレータ２３を用いた。しかしながら、ここでは具体的に図示しないが、高分子化合物層を含む積層型のセパレータを用いてもよい。
　具体的には、積層型のセパレータは、一対の面を有する多孔質膜と、その多孔質膜の片面または両面に設けられた高分子化合物層とを含んでいる。正極２１および負極２２のそれぞれに対するセパレータの密着性が向上するため、電池素子２０の位置ずれ（巻きずれ）が抑制されるからである。これにより、電解液の分解反応などが発生しても、二次電池の膨れが抑制される。高分子化合物層は、ポリフッ化ビニリデンなどの高分子化合物を含んでいる。ポリフッ化ビニリデンなどの高分子化合物は、物理的強度に優れていると共に、電気化学的に安定だからである。
　なお、多孔質膜および高分子化合物層のうちの一方または双方は、複数の絶縁性粒子のうちのいずれか１種類または２種類以上を含んでいてもよい。二次電池の発熱時において複数の絶縁性粒子が放熱を促進させるため、その二次電池の安全性（耐熱性）が向上するからである。複数の絶縁性粒子は、無機材料および樹脂材料のうちの一方または双方を含んでいる。無機材料の具体例は、酸化アルミニウム、窒化アルミニウム、ベーマイト、酸化ケイ素、酸化チタン、酸化マグネシウムおよび酸化ジルコニウムなどである。樹脂材料の具体例は、アクリル樹脂およびスチレン樹脂などである。
　積層型のセパレータを作製する場合には、高分子化合物および溶媒などを含む前駆溶液を調製したのち、多孔質膜の片面または両面に前駆溶液を塗布する。この場合には、必要に応じて、前駆溶液に複数の絶縁性粒子を添加してもよい。
　この積層型のセパレータを用いた場合においても、正極２１と負極２２との間においてリチウムが移動可能になるため、同様の効果を得ることができる。この場合には、特に、上記したように、二次電池の安全性が向上するため、より高い効果を得ることができる。
［変形例３］
　液状の電解質である電解液を用いた。しかしながら、ここでは具体的に図示しないが、ゲル状の電解質である電解質層を用いてもよい。
　電解質層を用いた電池素子２０では、セパレータ２３および電解質層を介して正極２１および負極２２が互いに積層されていると共に、その正極２１、負極２２、セパレータ２３および電解質層が巻回されている。この電解質層は、正極２１とセパレータ２３との間に介在していると共に、負極２２とセパレータ２３との間に介在している。
　具体的には、電解質層は、電解液と共に高分子化合物を含んでおり、その電解液は、高分子化合物により保持されている。電解液の漏液が防止されるからである。電解液の構成は、上記した通りである。高分子化合物は、ポリフッ化ビニリデンなどを含んでいる。電解質層を形成する場合には、電解液、高分子化合物および溶媒などを含む前駆溶液を調製したのち、正極２１および負極２２のそれぞれの片面または両面に前駆溶液を塗布する。
　この電解質層を用いた場合においても、正極２１と負極２２との間において電解質層を介してリチウムが移動可能になるため、同様の効果を得ることができる。この場合には、特に、上記したように、電解液の漏液が防止されるため、より高い効果を得ることができる。
＜３．二次電池の用途＞
　二次電池の用途（適用例）は、特に限定されない。電源として用いられる二次電池は、電子機器および電動車両などにおいて、主電源でもよいし、補助電源でもよい。主電源とは、他の電源の有無に関係なく、優先的に用いられる電源である。補助電源は、主電源の代わりに用いられる電源でもよいし、主電源から切り替えられる電源である。
　二次電池の用途の具体例は、以下の通りである。ビデオカメラ、デジタルスチルカメラ、携帯電話機、ノート型パソコン、ヘッドホンステレオ、携帯用ラジオおよび携帯用情報端末などの電子機器である。バックアップ電源およびメモリーカードなどの記憶用装置である。電動ドリルおよび電動鋸などの電動工具である。電子機器などに搭載される電池パックである。ペースメーカおよび補聴器などの医療用電子機器である。電気自動車（ハイブリッド自動車を含む。）などの電動車両である。非常時などに備えて電力を蓄積しておく家庭用または産業用のバッテリシステムなどの電力貯蔵システムである。これらの用途では、１個の二次電池が用いられてもよいし、複数個の二次電池が用いられてもよい。
　電池パックは、単電池を用いてもよいし、組電池を用いてもよい。電動車両は、駆動用電源として二次電池を用いて作動（走行）する車両であり、その二次電池以外の他の駆動源を併せて備えたハイブリッド自動車でもよい。家庭用の電力貯蔵システムでは、電力貯蔵源である二次電池に蓄積された電力を利用して、家庭用の電気製品などを使用可能である。
　ここで、二次電池の適用例の一例に関して具体的に説明する。以下で説明する適用例の構成は、あくまで一例であるため、適宜、変更可能である。
　図３は、電池パックのブロック構成を表している。ここで説明する電池パックは、１個の二次電池を用いた電池パック（いわゆるソフトパック）であり、スマートフォンに代表される電子機器などに搭載される。
　この電池パックは、図３に示したように、電源５１と、回路基板５２とを備えている。この回路基板５２は、電源５１に接続されていると共に、正極端子５３、負極端子５４および温度検出端子５５を含んでいる。
　電源５１は、１個の二次電池を含んでいる。この二次電池では、正極リードが正極端子５３に接続されていると共に、負極リードが負極端子５４に接続されている。この電源５１は、正極端子５３および負極端子５４を介して外部と接続可能であるため、充放電可能である。回路基板５２は、制御部５６と、スイッチ５７と、ＰＴＣ素子５８と、温度検出部５９とを含んでいる。ただし、ＰＴＣ素子５８は、省略されてもよい。
　制御部５６は、中央演算処理装置（ＣＰＵ）およびメモリなどを含んでおり、電池パック全体の動作を制御する。この制御部５６は、必要に応じて電源５１の使用状態の検出および制御を行う。
　なお、制御部５６は、電源５１（二次電池）の電圧が過充電検出電圧または過放電検出電圧に到達すると、スイッチ５７を切断することにより、電源５１の電流経路に充電電流が流れないようにする。過充電検出電圧は、特に限定されないが、具体的には、４．２０Ｖ±０．０５Ｖであると共に、過放電検出電圧は、特に限定されないが、具体的には、２．４０Ｖ±０．１Ｖである。
　スイッチ５７は、充電制御スイッチ、放電制御スイッチ、充電用ダイオードおよび放電用ダイオードなどを含んでおり、制御部５６の指示に応じて電源５１と外部機器との接続の有無を切り換える。このスイッチ５７は、金属酸化物半導体を用いた電界効果トランジスタ（ＭＯＳＦＥＴ）などを含んでおり、充放電電流は、スイッチ５７のＯＮ抵抗に基づいて検出される。
　温度検出部５９は、サーミスタなどの温度検出素子を含んでいる。この温度検出部５９は、温度検出端子５５を用いて電源５１の温度を測定すると共に、その温度の測定結果を制御部５６に出力する。温度検出部５９により測定される温度の測定結果は、異常発熱時において制御部５６が充放電制御を行う場合および残容量の算出時において制御部５６が補正処理を行う場合などに用いられる。
　本技術の実施例に関して説明する。
＜実施例１～１３および比較例１，２＞
　以下で説明するように、二次電池を製造したのち、その二次電池の電池特性を評価した。
［二次電池の製造］
　以下で説明する手順により、図１および図２に示した円筒型のリチウムイオン二次電池を製造した。
（正極の作製）
　最初に、正極活物質（リチウム含有化合物（酸化物）であるコバルト酸リチウム（ＬｉＣｏＯ2 ））９４質量部と、正極結着剤（ポリフッ化ビニリデン）３質量部と、正極導電剤（アセチレンブラック）３質量部とを互いに混合させることにより、正極合剤とした。続いて、溶媒（有機溶剤であるＮ－メチル－２－ピロリドン）に正極合剤を投入したのち、その溶媒を撹拌することにより、ペースト状の正極合剤スラリーを調製した。続いて、コーティング装置を用いて正極集電体２１Ａ（厚さ＝１２μｍである帯状のアルミニウム箔）の両面に正極合剤スラリーを塗布したのち、その正極合剤スラリーを乾燥させることにより、正極活物質層２１Ｂを形成した。最後に、ロールプレス機を用いて正極活物質層２１Ｂを圧縮成型した。これにより、正極２１が作製された。
（負極の作製）
　ここでは、２種類の負極２２を作製した。
　１種類目の負極２２を作製する場合には、最初に、負極活物質９３質量部（炭素材料である人造黒鉛６３質量部および金属系材料（ケイ素含有材料）である酸化ケイ素３０質量部）と、負極結着剤（ポリフッ化ビニリデン）７質量部とを互いに混合させることにより、負極合剤とした。続いて、溶媒（有機溶剤であるＮ－メチル－２－ピロリドン）に負極合剤を投入したのち、その溶媒を撹拌することにより、ペースト状の負極合剤スラリーを調製した。続いて、コーティング装置を用いて負極集電体２２Ａ（厚さ＝１５μｍである帯状の銅箔）の両面に負極合剤スラリーを塗布したのち、その負極合剤スラリーを乾燥させることにより、負極活物質層２２Ｂを形成した。最後に、ロールプレス機を用いて負極活物質層２２Ｂを圧縮成型した。これにより、負極２２が作製された。
　２種類目の負極２２を作製する場合には、負極合剤を得るために負極活物質（炭素材料である人造黒鉛）９３質量部と負極結着剤（ポリフッ化ビニリデン）７質量部とを互いに混合させたことを除いて、１種類目の負極２２の作製手順と同様の手順を用いた。
（電解液の調製）
　溶媒（環状炭酸エステルである炭酸エチレンおよび鎖状炭酸エステルである炭酸ジメチル）を準備した。溶媒の混合比（重量比）は、炭酸エチレン：炭酸ジメチル＝２０：８０とした。続いて、溶媒に電解質塩（リチウム塩であるＬｉＰＦ6 ）を添加したのち、その溶媒を撹拌した。電解質塩の含有量は、溶媒に対して１．２ｍｏｌ／ｋｇとした。最後に、電解質塩が添加された溶媒にベンゾチアゾリン型化合物を添加したのち、その溶媒を撹拌した。ベンゾチアゾリン型化合物の種類は、表１に示した通りである。これにより、電解液が調製された。
　なお、比較のために、ベンゾチアゾリン型化合物を用いなかったことを除いて同様の手順により、電解液を調製した。
（二次電池の組み立て）
　最初に、正極２１の正極集電体２１Ａに正極リード２５（アルミニウム箔）を溶接したと共に、負極２２の負極集電体２２Ａに負極リード２６（銅箔）を溶接した。
　続いて、セパレータ２３（厚さ＝１５μｍである微多孔性ポリエチレンフィルム）を介して正極２１および負極２２を互いに積層させたのち、その正極２１、負極２２およびセパレータ２３を巻回させることにより、空間２０Ｓを有する巻回体を作製した。続いて、巻回体の空間２０Ｓにセンターピン２４を挿入した。
　続いて、電池缶１１の内部に巻回体と共に絶縁板１２，１３を収納した。この場合には、安全弁機構１５に正極リード２５を溶接したと共に、電池缶１１に負極リード２６を溶接した。続いて、電池缶１１の内部に電解液を注入した。これにより、巻回体に電解液が含浸されたため、電池素子２０が作製された。
　最後に、電池缶１１の内部に電池蓋１４、安全弁機構１５およびＰＴＣ素子１６を収納したのち、ガスケット１７を介して電池缶１１を加締めた。これにより、電池缶１１が封止されたため、二次電池が組み立てられた。
（二次電池の安定化）
　常温環境中（温度＝２３℃）において二次電池を１サイクル充放電させた。充電時には、０．１Ｃの電流で電圧が４．２Ｖに到達するまで定電流充電したのち、その４．２Ｖの電圧で電流が０．０５Ｃに到達するまで定電圧充電した。放電時には、０．１Ｃの電流で電圧が３．０Ｖに到達するまで定電流放電した。０．１Ｃとは、電池容量（理論容量）を１０時間で放電しきる電流値であると共に、０．０５Ｃとは、その電池容量を２０時間で放電しきる電流値である。
　これにより、正極２１および負極２２のそれぞれの表面に被膜が形成されたため、電池素子２０の状態が電気化学的に安定化した。よって、二次電池が完成した。
　なお、二次電池の完成後、ＩＣＰ発光分光分析法を用いて、電解液におけるベンゾチアゾリン型化合物の含有量（重量％）を測定した結果は、表１に示した通りである。
［電池特性の評価］
　以下で説明する手順により、電池特性としてサイクル特性を評価したところ、表１に示した結果が得られた。
　最初に、高温環境中（温度＝５０℃）において二次電池を充電させたのち、同環境中において充電状態の二次電池を静置（静置時間＝５時間）した。充電時には、１Ｃの電流で電圧が４．２Ｖに到達するまで定電流充電したのち、その４．２Ｖの電圧で電流が０．０５Ｃに到達するまで定電圧充電した。１Ｃとは、電池容量を１時間で放電しきる電流値である。
　続いて、同環境中において二次電池を放電させることにより、放電容量（１サイクル目の放電容量）を測定した。放電時には、３Ｃの電流で電圧が３．０Ｖに到達するまで定電流放電した。３Ｃとは、電池容量を１／３時間で放電しきる電流値である。
　続いて、同環境中においてサイクル数が１００サイクルに到達するまで二次電池を繰り返して充放電させることにより、放電容量（１００サイクル目の放電容量）を測定した。２サイクル目以降の充放電条件は、１サイクル目の充放電条件と同様にした。
　最後に、容量維持率（％）＝（１００サイクル目の放電容量／１サイクル目の放電容量）×１００という計算式に基づいて、サイクル特性を評価するための指標である容量維持率を算出した。
Figure JPOXMLDOC01-appb-T000007
［考察］
　表１に示したように、容量維持率は、電解液の構成に応じて変動した。
　具体的には、電解液がベンゾチアゾリン型化合物を含んでいる場合（実施例１～１３）には、電解液がベンゾチアゾリン型化合物を含んでいない場合（比較例１，２）と比較して、容量維持率が増加した。
　特に、電解液がベンゾチアゾリン型化合物を含んでいる場合には、以下で説明する傾向が得られた。
　第１に、電解液におけるベンゾチアゾリン型化合物の含有量が０．００１重量％～５重量％であると、容量維持率がより増加した。
　第２に、負極活物質がケイ素含有材料を含んでいる場合には、負極活物質がケイ素含有材料を含んでいない場合（負極活物質が炭素材料を含んでいる場合）と比較して、容量維持率の増加割合が増加した。具体的には、負極活物質がケイ素含有材料を含んでいない場合における容量維持率の増加割合は、約１７％であったのに対して、負極活物質がケイ素含有材料を含んでいる場合における容量維持率の増加割合は、６５％であった。
＜実施例１４～１９＞
　表２に示したように、電解液に添加剤（不飽和環状炭酸エステル、フッ素化環状炭酸エステルまたはシアノ化環状炭酸エステル）を含有させたことを除いて実施例４と同様の手順により、二次電池を作製したのち、電池特性を評価した。添加剤の分類、種類および含有量（重量％）は、表２に示した通りである。
　具体的には、不飽和環状炭酸エステルとして、炭酸ビニレン（ＶＣ）を用いた。フッ素化環状炭酸エステルとして、フルオロ炭酸エチレン（ＦＥＣ）を用いた。シアノ化環状炭酸エステルとしては、シアノ炭酸エチレン（ＣＥＣ）を用いた。
Figure JPOXMLDOC01-appb-T000008
　表２に示したように、電解液が添加剤（不飽和環状炭酸エステル、フッ素化環状炭酸エステルまたはシアノ化環状炭酸エステル）を含んでいる場合（実施例１４～１９）には、電解液が添加剤を含んでいない場合（実施例４）と比較して、容量維持率がより増加した。
＜実施例２０～３９＞
　表３および表４に示したように、電解液に添加剤（スルホン酸エステル、硫酸エステル、亜硫酸エステル、ジカルボン酸無水物、ジスルホン酸無水物、スルホン酸カルボン酸無水物またはスルホ安息香酸イミド）を含有させたことを除いて実施例４と同様の手順により、二次電池を作製したのち、電池特性を評価した。添加剤の分類、種類および含有量（重量％）は、表３および表４に示した通りである。
　具体的には、スルホン酸エステルとして、１，３－プロパンスルトン（ＰＳ）、１－プロペン－１，３－スルトン（ＰＲＳ）、１，４－ブタンスルトン（ＢＳ１）、２，４－ブタンスルトン（ＢＳ２）およびメタンスルホン酸プロパルギルエステル（ＭＳＰ）を用いた。
　硫酸エステルとして、１，３，２－ジオキサチオラン２，２－ジオキシド（ＯＴＯ）、１，３，２－ジオキサチアン２，２－ジオキシド（ＯＴＡ）および４－メチルスルホニルオキシメチル－２，２－ジオキソ－１，３，２－ジオキサチオラン（ＳＯＴＯ）を用いた。
　亜硫酸エステルとして、１，３，２－ジオキサチオラン２－オキシド（ＤＴＯ）および４－メチル－１，３，２－ジオキサチオラン２－オキシド（ＭＤＴＯ）を用いた。
　ジカルボン酸無水物として、１，４－ジオキサン－２，６－ジオン（ＤＯＤ）、コハク酸無水物（ＳＡ）およびグルタル酸無水物（ＧＡ）を用いた。
　ジスルホン酸無水物として、１，２－エタンジスルホン酸無水物（ＥＳＡ）、１，３－プロパンジジスルホン酸無水物（ＰＳＡ）およびヘキサフルオロ１，３－プロパンジスルホン酸無水物（ＦＰＳＡ）を用いた。
　スルホン酸カルボン酸無水物として、２－スルホ安息香酸無水物（ＳＢＡ）および２，２－ジオキソオキサチオラン－５－オン（ＤＯＴＯ）を用いた。
　スルホ安息香酸イミドとして、ｏ－スルホベンズイミド（ＳＢＩ）およびＮ－メチルサッカリン（ＮＭＳ）を用いた。
Figure JPOXMLDOC01-appb-T000009
Figure JPOXMLDOC01-appb-T000010
　表３および表４に示したように、電解液が添加剤（スルホン酸エステル、硫酸エステル、亜硫酸エステル、ジカルボン酸無水物、ジスルホン酸無水物、スルホン酸カルボン酸無水物またはスルホ安息香酸イミド）を含んでいる場合（実施例２０～３９）には、電解液が添加剤を含んでいない場合（実施例４）と比較して、容量維持率がより増加した。
［まとめ］
　表１～表４に示した結果から、電解液がベンゾチアゾリン型化合物を含んでいると、高い容量維持率が得られた。よって、サイクル特性が改善されたため、二次電池において優れた電池特性が得られた。
　以上、一実施形態および実施例を挙げながら本技術に関して説明したが、その本技術の構成は、一実施形態および実施例において説明された構成に限定されないため、種々に変形可能である。
　具体的には、電池素子の素子構造が巻回型である場合に関して説明した。しかしながら、電池素子の素子構造は、特に限定されないため、積層型および九十九折り型などの他の素子構造でもよい。積層型では、正極および負極がセパレータを介して交互に積層されていると共に、九十九折り型では、正極および負極がセパレータを介して互いに対向しながらジグザグに折り畳まれている。
　また、電極反応物質がリチウムである場合に関して説明したが、その電極反応物質は、特に限定されない。具体的には、電極反応物質は、上記したように、ナトリウムおよびカリウムなどの他のアルカリ金属でもよいし、ベリリウム、マグネシウムおよびカルシウムなどのアルカリ土類金属でもよい。この他、電極反応物質は、アルミニウムなどの他の軽金属でもよい。
　本明細書中に記載された効果は、あくまで例示であるため、本技術の効果は、本明細書中に記載された効果に限定されない。よって、本技術に関して、他の効果が得られてもよい。
　なお、本技術は、以下のような構成を取ることもできる。

＜１＞
　正極と、
　負極と、
　式（１）により表されるベンゾチアゾリン型化合物を含む電解液と
　を備えた、二次電池。
Figure JPOXMLDOC01-appb-C000011
 （Ｒ１～Ｒ１２のそれぞれは、水素、フッ素、アミノ基、アルキル基、シクロアルキル基、アリール基、アルコキシ基、フッ素化アルキル基、フッ素化シクロアルキル基、フッ素化アリール基、フッ素化アルコキシ基およびそれらの２種類以上が互いに結合された１価の結合基のうちのいずれかである。）
＜２＞
　前記負極は、負極活物質を含み、
　前記負極活物質は、ケイ素含有材料を含む、
　＜１＞に記載の二次電池。
＜３＞
　前記電解液における前記ベンゾチアゾリン型化合物の含有量は、０．００１重量％以上５重量％以下である、
　＜１＞または＜２＞に記載の二次電池。
＜４＞
　前記電解液は、さらに、不飽和環状炭酸エステル、フッ素化環状炭酸エステルおよびシアノ化環状炭酸エステルのうちの少なくとも１種を含む、
　＜１＞ないし＜３＞のいずれか１つに記載の二次電池。
＜５＞
　前記電解液は、さらに、スルホン酸エステル、硫酸エステル、亜硫酸エステル、ジカルボン酸無水物、ジスルホン酸無水物、スルホン酸カルボン酸無水物およびスルホ安息香酸イミドのうちの少なくとも１種を含む、
　＜１＞ないし＜４＞のいずれか１つに記載の二次電池。
＜６＞
　リチウムイオン二次電池である、
　＜１＞ないし＜５＞のいずれか１つに記載の二次電池。
＜７＞
　式（１）により表されるベンゾチアゾリン型化合物を含む、
　二次電池用電解液。
Figure JPOXMLDOC01-appb-C000012
 （Ｒ１～Ｒ１２のそれぞれは、水素、フッ素、アミノ基、アルキル基、シクロアルキル基、アリール基、アルコキシ基、フッ素化アルキル基、フッ素化シクロアルキル基、フッ素化アリール基、フッ素化アルコキシ基およびそれらの２種類以上が互いに結合された１価の結合基のうちのいずれかである。）

Claims (7)

  1. 　正極と、
    　負極と、
    　式（１）により表されるベンゾチアゾリン型化合物を含む電解液と
    　を備えた、二次電池。
    Figure JPOXMLDOC01-appb-C000001
     （Ｒ１～Ｒ１２のそれぞれは、水素、フッ素、アミノ基、アルキル基、シクロアルキル基、アリール基、アルコキシ基、フッ素化アルキル基、フッ素化シクロアルキル基、フッ素化アリール基、フッ素化アルコキシ基およびそれらの２種類以上が互いに結合された１価の結合基のうちのいずれかである。）
  2. 　前記負極は、負極活物質を含み、
    　前記負極活物質は、ケイ素含有材料を含む、
    　請求項１に記載の二次電池。
  3. 　前記電解液における前記ベンゾチアゾリン型化合物の含有量は、０．００１重量％以上５重量％以下である、
    　請求項１または請求項２に記載の二次電池。
  4. 　前記電解液は、さらに、不飽和環状炭酸エステル、フッ素化環状炭酸エステルおよびシアノ化環状炭酸エステルのうちの少なくとも１種を含む、
    　請求項１ないし請求項３のいずれか１項に記載の二次電池。
  5. 　前記電解液は、さらに、スルホン酸エステル、硫酸エステル、亜硫酸エステル、ジカルボン酸無水物、ジスルホン酸無水物、スルホン酸カルボン酸無水物およびスルホ安息香酸イミドのうちの少なくとも１種を含む、
    　請求項１ないし請求項４のいずれか１項に記載の二次電池。
  6. 　リチウムイオン二次電池である、
    　請求項１ないし請求項５のいずれか１項に記載の二次電池。
  7. 　式（１）により表されるベンゾチアゾリン型化合物を含む、
    　二次電池用電解液。
    Figure JPOXMLDOC01-appb-C000002
     （Ｒ１～Ｒ１２のそれぞれは、水素、フッ素、アミノ基、アルキル基、シクロアルキル基、アリール基、アルコキシ基、フッ素化アルキル基、フッ素化シクロアルキル基、フッ素化アリール基、フッ素化アルコキシ基およびそれらの２種類以上が互いに結合された１価の結合基のうちのいずれかである。）
PCT/JP2023/032776 2022-10-19 2023-09-08 二次電池用電解液および二次電池 WO2024084858A1 (ja)