WO2024018944A1 - 電極触媒層、膜電極接合体、および、固体高分子形燃料電池 - Google Patents

電極触媒層、膜電極接合体、および、固体高分子形燃料電池 Download PDF

Info

Publication number
WO2024018944A1
WO2024018944A1 PCT/JP2023/025471 JP2023025471W WO2024018944A1 WO 2024018944 A1 WO2024018944 A1 WO 2024018944A1 JP 2023025471 W JP2023025471 W JP 2023025471W WO 2024018944 A1 WO2024018944 A1 WO 2024018944A1
Authority
WO
WIPO (PCT)
Prior art keywords
catalyst layer
ionic liquid
mass
electrode catalyst
particles
Prior art date
Application number
PCT/JP2023/025471
Other languages
English (en)
French (fr)
Inventor
雅弘 上野
均 栗原
克行 岸
まどか 小澤
Original Assignee
Ｔｏｐｐａｎホールディングス株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2022117534A external-priority patent/JP2024014589A/ja
Priority claimed from JP2022164944A external-priority patent/JP2024057940A/ja
Priority claimed from JP2022191848A external-priority patent/JP2024079112A/ja
Application filed by Ｔｏｐｐａｎホールディングス株式会社 filed Critical Ｔｏｐｐａｎホールディングス株式会社
Publication of WO2024018944A1 publication Critical patent/WO2024018944A1/ja

Abstract

電極触媒層は、触媒粒子、高分子電解質、および、繊維状物質を含む。触媒粒子は、金属粒子と導電性担体とイオン液体とを含む。電極触媒層は、１０００ｍｇ／ｃｍ３以上１６００ｍｇ／ｃｍ３以下の密度を有する。触媒粒子はさらに、金属粒子および導電性担体の一部を被覆する無機被膜を含む。

Description

電極触媒層、膜電極接合体、および、固体高分子形燃料電池
　本開示は、電極触媒層、膜電極接合体、および、固体高分子形燃料電池に関する。
　固体高分子形燃料電池は、プロトン伝導性を有する高分子電解質膜と、厚さ方向に高分子電解質膜を挟む一対の電極触媒層とを有した膜電極接合体を備えている。電極触媒層の一方は、アノードである燃料極を構成し、電極触媒層の他方は、カソードである空気極を構成する。電極触媒層は、白金等の金属粒子を担持した担体を含む触媒粒子と、高分子電解質とを含有している（例えば、特許文献１，２参照）。
　燃料極には、水素を含む燃料ガスが供給され、空気極には、酸素を含む酸化剤ガスが供給される。燃料極の電極触媒層では、燃料ガスからプロトンと電子とが生じる。プロトンは、電極触媒層と高分子電解質膜とが含む高分子電解質によって伝導され、高分子電解質膜を通って空気極に移動する。電子は、燃料極から外部回路に取り出され、外部回路を通って空気極に移動する。空気極の電極触媒層では、酸化剤ガスと、燃料極から移動してきたプロトンおよび電子とが反応して水が生成される。こうした電極反応の進行により、電流の流れが生じる。
特許第７０２６６６９号公報 特開２００８－４５４１号公報
　上記電極反応における主要な反応は電極触媒層にて生じることから、電極触媒層の構成は、燃料電池の発電性能を高めるための重要な因子である。それゆえ、電極触媒層の材料や各材料の比率について多くの研究が為されている。特に、触媒粒子の構成や、触媒粒子の構成に関連した電極触媒層の特性については、なお改良の余地が残されている。
　上記課題を解決するための電極触媒層の一態様は、触媒粒子、高分子電解質、および、繊維状物質を含む電極触媒層であって、前記触媒粒子は、金属粒子と導電性担体とイオン液体とを含み、前記電極触媒層は、１０００ｍｇ／ｃｍ３以上１６００ｍｇ／ｃｍ３以下の密度を有する。
図１は、各実施形態における基本構成の膜電極接合体の構成を示す図である。 図２は、各実施形態における基本構成の電極触媒層の構成を示す図である。 図３は、各実施形態における基本構成の触媒粒子の構成を示す図である。 図４Ａは、各実施形態における基本構成の触媒粒子の構成を示す図であり、図４Ｂ，図４Ｃは、触媒粒子の要部断面図である。 図５は、各実施形態における基本構成の固体高分子形燃料電池の構成を示す図。 図６は、第２実施形態の触媒粒子の構成を示す図である。 図７は、第２実施形態の触媒粒子の構成を拡大して示す図である。 図８Ａは、第３実施形態の実施例の触媒粒子における元素分布を示す図である。 図８Ｂは、第３実施形態の実施例の触媒粒子における元素分布を示す図である。 図８Ｃは、第３実施形態の実施例の触媒粒子における元素分布を示す図である。
　（第１実施形態）
　図面を参照して、電極触媒層、膜電極接合体、および、固体高分子形燃料電池の第１実施形態を説明する。なお、各図においては、理解を容易にするために、各部の形状や比率を適宜誇張して表現している。また、本明細書における記述「ＡおよびＢの少なくとも一つ」は、「Ａのみ、または、Ｂのみ、または、ＡとＢの両方」を意味するものとして理解されたい。
　＜基本構成＞
　［膜電極接合体および電極触媒層］
　図１に示すように、膜電極接合体２０は、高分子電解質膜２１、および、一対の電極触媒層を備えている。一対の電極触媒層は、燃料極触媒層２２Ａおよび空気極触媒層２２Ｃである。
　燃料極触媒層２２Ａは、固体高分子形燃料電池のアノードである燃料極を構成する。空気極触媒層２２Ｃは、固体高分子形燃料電池のカソードである空気極を構成する。燃料極触媒層２２Ａは、燃料ガスをプロトンと電子に分離するための層であり、空気極触媒層２２Ｃは、外部回路から電子を受け取るとともに、高分子電解質膜２１を介して輸送されたプロトンを、酸素を含む酸化剤により酸化するための層である。
　高分子電解質膜２１は、厚さ方向において、燃料極触媒層２２Ａと空気極触媒層２２Ｃとの間に挟まれている。燃料極触媒層２２Ａは、高分子電解質膜２１が有する２つの面の一方に接触し、空気極触媒層２２Ｃは、高分子電解質膜２１が有する２つの面の他方に接触している。燃料極触媒層２２Ａと空気極触媒層２２Ｃとの厚さは互いに一致していてもよいし、異なっていてもよい。
　高分子電解質膜２１が有する一方の面と対向する位置から見たとき、燃料極触媒層２２Ａと空気極触媒層２２Ｃとの外形はほぼ同形であり、これらの外形は高分子電解質膜２１の外形よりも小さい。触媒層２２Ａ，２２Ｃおよび高分子電解質膜２１の外形の形状は特に限定されず、例えば、矩形であればよい。
　高分子電解質膜２１は高分子電解質を含む。高分子電解質膜２１に用いられる高分子電解質は、プロトン伝導性を有する高分子電解質であればよく、例えば、フッ素系高分子電解質や炭化水素系高分子電解質である。フッ素系高分子電解質の例は、Ｎａｆｉｏｎ（登録商標：ケマーズ社製）、Ｆｌｅｍｉｏｎ（登録商標：旭硝子社製）、Ｇｏｒｅ－Ｓｅｌｅｃｔ（登録商標：日本ゴア合同会社製）である。炭化水素系高分子電解質の例は、エンジニアリングプラスチックや、スルホン酸基が導入されたエンジニアリングプラスチックである。
　高分子電解質膜２１の厚さは、例えば、０．０５ｍｍ以上０．２５ｍｍ以下である。
　図２に、空気極触媒層２２Ｃの構成を模式的に示す。空気極触媒層２２Ｃは、触媒粒子１０および高分子電解質１６を含む。さらに、空気極触媒層２２Ｃは、繊維状物質１７を含んでいることが好ましい。
　燃料極触媒層２２Ａは、触媒粒子および高分子電解質を含む。さらに、燃料極触媒層２２Ａは、繊維状物質を含んでいることが好ましい。なお、空気極触媒層２２Ｃと燃料極触媒層２２Ａとで、含有する触媒粒子や高分子電解質や繊維状物質の材料や割合は異なっていてもよい。
　触媒粒子１０は、導電性担体と、導電性担体に担持された金属粒子とを含んでいる。触媒粒子１０の詳細な構成は後述する。
　高分子電解質１６は、アイオノマーである高分子電解質が凝集力によって凝集した塊状を有する。凝集力は、アイオノマー間に働くクーロン力やファンデルワールス力を含む。
　高分子電解質１６は、プロトン伝導性を有する高分子電解質であればよく、例えば、フッ素系高分子電解質や炭化水素系高分子電解質であればよい。フッ素系高分子電解質の例は、Ｎａｆｉｏｎ（登録商標：ケマーズ社製）等のテトラフルオロエチレン骨格を有する電解質である。炭化水素系高分子電解質の例は、スルホン化ポリエーテルケトン、スルホン化ポリエーテルスルホン、スルホン化ポリエーテルエーテルスルホン、スルホン化ポリスルフィド、スルホン化ポリフェニレン等である。電極触媒層が含む高分子電解質は、１種類であってもよいし、２種類以上であってもよい。
　高分子電解質膜２１と電極触媒層とに用いられる高分子電解質が同種の電解質であると、高分子電解質膜２１に対する電極触媒層の密着性が高められる。また、高分子電解質膜２１と電極触媒層との界面における界面抵抗を小さくする観点、および、湿度が変化した場合における高分子電解質膜２１と電極触媒層との寸法変化率の差を小さくする観点では、高分子電解質膜２１と電極触媒層とに用いられる高分子電解質は、互いに同じ高分子電解質であるか、熱膨張係数が近い高分子電解質であることが好ましい。
　電極触媒層における高分子電解質１６の含有量は、電極触媒層における導電性担体の含有量を１００質量部としたとき、１０質量部以上２００質量部以下であることが好ましく、４０質量部以上１４０質量部以下であることがより好ましい。高分子電解質１６の含有量が１０質量部以上、好ましくは４０質量部以上であれば、プロトンの伝導経路が欠損することによるプロトン伝導性の低下を抑制することができる。その結果、電極触媒層におけるプロトン伝導性と電子伝導性とのバランスが好適に得られやすくなる。また、高分子電解質１６の含有量が２００質量部以下、好ましくは１４０質量部以下であれば、電極触媒層にて三相界面が形成されやすくなることから、触媒活性が高められる。
　繊維状物質１７は、触媒粒子１０および高分子電解質１６に侵されない材料から構成されていることが好ましい。電極触媒層の抵抗を下げる観点では、繊維状物質１７は、電子伝導性、または、プロトン伝導性を有することが好ましい。
　電子伝導性を示す繊維状物質１７の例は、カーボンファイバー、カーボンナノファイバー、カーボンナノチューブ等のカーボン繊維である。なかでも、カーボンナノファイバー、カーボンナノチューブが好適に用いられる。
　プロトン伝導性を示す繊維状物質１７の例は、高分子電解質を繊維状に加工した繊維である。高分子電解質としては、フッ素系高分子電解質や炭化水素系高分子電解質が使用可能である。フッ素系高分子電解質の例は、Ｎａｆｉｏｎ（登録商標：ケマーズ社製）である。炭化水素系高分子電解質の例は、エンジニアリングプラスチックや、スルホン酸基が導入されたエンジニアリングプラスチックである。また、酸をドープすることでプロトン伝導性を発現する酸ドープ型ポリベンゾアゾール類も好適に用いることができる。
　また、繊維状物質１７は、親水性炭素繊維、あるいは、高分子ポリマー繊維であってもよい。親水性炭素繊維の例は、親水性を付与されたＶＧＣＦ（Vapor Grown Carbon Fiber）、ＣＮＴ（Carbon Nano Tube）である。高分子ポリマー繊維の例は、イミド構造やアゾール構造を有するアミン類の高分子ポリマーからなるナノファイバーである。
　繊維状物質１７が含有されていることによって、電極触媒層にクラックが生じ難くなり、電極触媒層の耐久性が高められる。また、繊維状物質１７が含有されていることによって、電極触媒層内に空隙が適度に確保されるため、電極触媒層の排水性が高められる。それゆえ、生成水が増大する高電流密度での運転中でも、生成水の滞留によってガスの拡散経路が塞がれて発電性能が低下する現象であるフラッディングの発生を抑えることができる。
　繊維状物質１７の形状は特に限定されず、例えば、繊維状物質１７は、中空構造を有していてもよいし、中実構造を有していてもよい。また、電極触媒層が含む繊維状物質１７は、１種類であってもよいし、２種類以上であってもよい。
　繊維状物質１７は、分子構造中に酸性もしくは塩基性の官能基を含んでいてよい。酸性の官能基を有する繊維状物質１７としては親水性炭素繊維、塩基性の官能基を有する繊維状物質１７としてはイミド構造やアゾール構造を有する高分子ポリマー繊維が挙げられる。酸性の官能基の例はカルボニル基等であり、塩基性の官能基の例はピリジンやイミド等を含むアミン基等である。これにより、高分子電解質１６が繊維状物質１７の周辺に存在しやすくなる。
　繊維状物質１７が酸性の官能基を含む場合、当該酸性の官能基に対して、高分子電解質１６中に含まれるスルホニル基等のプロトン伝導部位が水素結合することで、繊維状物質１７の周辺に高分子電解質１６が存在し易くなる。一方、繊維状物質１７が塩基性の官能基を含む場合、当該塩基性の官能基に対して、高分子電解質１６中に含まれるスルホニル基等の酸性のプロトン伝導部位が酸と塩基として結合することで、繊維状物質１７の周辺に高分子電解質１６が存在しやすくなる。水素結合に比べ、酸塩基の結合の方が結合力は強いため、繊維状物質１７は塩基性の官能基を含んでいることが好ましい。言い換えれば、繊維状物質１７が、その分子構造中に窒素原子を含む塩基性官能基を有していることで、高分子電解質１６が繊維状物質１７の周辺に存在しやすくなる。
　また、繊維状物質１７における塩基性の官能基に、高分子電解質１６における酸性のプロトン伝導部位が結合すると、繊維状物質１７の表面が高分子電解質１６に被覆されて、繊維状物質１７がプロトン伝導性を示すことも可能となる。塩基性の官能基の具体例は、イミノ基、アミノ基、アミン誘導体、ピリジン誘導体、イミダゾール誘導体、イミダゾリウム基等である。塩基性の官能基を含む繊維状物質１７の材料の具体例は、ポリベンズイミダゾール（ＰＢＩ）、ポリベンズオキサゾール、ポリベンズチオアゾール、ポリビニルイミダゾール、ポリアリルアミン等である。なかでも、プロトン伝導性および加工性の観点から、アゾール構造を有するポリベンズイミダゾール（ＰＢＩ）が用いられることが好ましい。
　繊維状物質１７の平均繊維径は、０．５ｎｍ以上５００ｎｍ以下であることが好ましく、１０ｎｍ以上３００ｎｍ以下であることがより好ましい。平均繊維径が上記範囲内であれば、電極触媒層内の空隙が適切に確保される。
　また、繊維状物質１７の平均繊維径あるいは繊維径分布のピークは、１００ｎｍ以上４００ｎｍ以下であることが好ましく、１５０ｎｍ以上２５０ｎｍ以下であることがより好ましく、１８０ｎｍ以上２２０ｎｍ以下であることがさらに好ましい。繊維径が上記範囲内であれば、電極触媒層内の空隙を増加させるとともにプロトン伝導性の低下を抑制することが可能であるため、燃料電池の出力が高められる。繊維径が小さすぎると、空隙が狭くなり十分な排水性およびガス拡散性が確保できない場合がある。この場合、電極触媒層中に水が滞留して、出力の低下および電極触媒層の劣化を促進することがある。繊維径が大きすぎると、高分子電解質１６によるプロトン伝導の経路や導電性担体１１による電子伝導の経路が遮断され、抵抗が増大する場合がある。
　繊維状物質１７の繊維径は、例えば、電極触媒層の断面を、走査型電子顕微鏡（ＳＥＭ）を用いて観察し、繊維状物質１７の断面の直径を測長することで得ることができる。繊維状物質１７が斜めに切断された場合には、観察可能な断面の形状は楕円形となることがある。その場合には、短軸に沿ってフィッティングした真円の直径を測定することで繊維状物質１７の繊維径を得ることができる。複数箇所、例えば５０箇所の繊維状物質１７の繊維径を測長し、算術平均または度数分布を作成することで、平均繊維径や繊維径分布のピークを得ることができる。
　繊維状物質１７の平均繊維長は１μｍ以上２００μｍ以下であることが好ましく、１μｍ以上５０μｍ以下であることがより好ましい。平均繊維長が上記範囲内であれば、電極触媒層におけるクラックの発生が好適に抑えられることから、電極触媒層および膜電極接合体の耐久性が高められる。また、電極触媒層内の空隙が適切に確保されることから、燃料電池の出力の向上が可能である。
　また、繊維状物質１７の繊維長分布のピークは、１μｍ以上１００μｍ以下であることが好ましく、５μｍ以上５０μｍ以下であることがより好ましく、５μｍ以上３０μｍ以下であることがさらに好ましい。繊維長分布のピークが上記範囲内であれば、電極触媒層におけるクラックの発生が好適に抑えられることから、電極触媒層および膜電極接合体の耐久性が高められる。また、電極触媒層内の空隙が適切に確保されることから、燃料電池の出力の向上が可能である。
　電極触媒層における繊維状物質１７の含有量は、電極触媒層における導電性担体の含有量を１００質量部としたとき、１質量部以上３００質量部以下であることが好ましく、５質量部以上１００質量部以下であることがより好ましく、５質量部以上２０質量部以下であることがさらに好ましい。繊維状物質１７の含有量が１質量部以上、好ましくは５質量部以上であれば、繊維状物質１７同士のネットワークが好適に形成される。これにより、電極触媒層におけるプロトンの伝導経路の構築、電子の伝導経路の構築、ガス拡散性の向上、および、電極触媒層の強度の向上が好適に可能である。その結果、燃料電池の発電性能が高められる。また、繊維状物質１７の含有量が３００質量部以下、好ましくは１００質量部以下、さらに好ましくは２０質量部以下であれば、電極触媒層の厚さの増大に起因した抵抗増加や触媒反応の阻害を抑制できる。
　［触媒粒子の構成］
　図３および図４Ａ～図４Ｃに示すように、触媒粒子１０は、導電性担体１１と、導電性担体１１に担持された複数の金属粒子１２とからなる触媒担持担体１５を有している。さらに、触媒粒子１０は、触媒担持担体１５の一部を被覆する無機被膜１３と、触媒担持担体１５に含浸されたイオン液体１４とを有している。
　無機被膜１３は、主として金属粒子１２を被覆している。金属粒子１２の表面の一部は、無機被膜１３から露出し、この露出部分の少なくとも一部において金属粒子１２はイオン液体１４と接している。また、無機被膜１３は、導電性担体１１の表面の一部も被覆していてもよい。無機被膜１３の厚さは均一であってもよいし、不均一であってもよい。
　なお、複数の金属粒子１２には、表面全体が無機被膜１３に覆われている金属粒子１２、表面全体が無機被膜１３から露出している金属粒子１２、および、イオン液体１４に接していない金属粒子１２の少なくとも１つが含まれてもよい。
　イオン液体１４はさらに、導電性担体１１の表面の一部と接し、また、導電性担体１１の内部の少なくとも一部に浸透している。また、無機被膜１３がその内部に細孔等の隙間を有するとき、イオン液体１４は、無機被膜１３の内部の少なくとも一部にも浸透していてよい。イオン液体１４は、触媒担持担体１５および無機被膜１３が有するいずれの隙間にも浸透可能である。
　なお、上記構成において、無機被膜１３は、イオン液体１４を介して、金属粒子１２を被覆していてもよい。すなわち、無機被膜１３と金属粒子１２との間にイオン液体１４が介在していてもよい。また、無機被膜１３は、イオン液体１４を介して、導電性担体１１の表面を被覆していてもよい。すなわち、無機被膜１３と導電性担体１１の表面との間にイオン液体１４が介在していてもよい。
　［触媒粒子の材料］
　（導電性担体）
　導電性担体１１は、導電性を有する微粒子であり、金属粒子１２に侵されない材料からなる。導電性担体１１は、メソ孔を含む細孔を有している。導電性担体１１は、炭素材料からなることが好ましい。導電性担体１１として用いられる炭素材料は、例えば、カーボンブラック、グラファイト、黒鉛、活性炭、フラーレン等である。なお、電極触媒層が含む導電性担体１１の構成材料は、１種類であってもよいし、２種類以上であってもよい。
　導電性担体１１の平均粒径は、１０ｎｍ以上１０００ｎｍ以下であることが好ましく、１０ｎｍ以上１００ｎｍ以下であることがより好ましい。導電性担体１１の平均粒径が１０ｎｍ以上であれば、電極触媒層内に電子の伝導経路が形成されやすくなる。また、導電性担体１１が電極触媒層において密に詰まり過ぎないため、電極触媒層のガス拡散性の低下を抑えることができる。また、導電性担体１１の平均粒径が１０００ｎｍ以下であれば、電極触媒層の厚さが増大することによる抵抗の増加を抑制できる。また、電極触媒層におけるクラックの発生を抑えることができる。なお、導電性担体の平均粒径は、レーザー回折／散乱法による体積平均径である。
　高表面積の導電性担体１１に金属粒子１２を担持させることで、金属粒子１２を高密度に担持することが可能であることから、触媒活性の向上が可能である。
　（金属粒子）
　金属粒子１２としては、例えば、白金、パラジウム、ルテニウム、イリジウム、ロジウム、オスミウムの白金族元素や、金、鉄、鉛、銅、クロム、コバルト、ニッケル、マンガン、バナジウム、モリブデン、ガリウム、アルミニウム等の金属や、これらの合金、酸化物、複酸化物、炭化物等が用いられる。なかでも、白金、金、パラジウム、ロジウム、ルテニウム、および、これらの合金は、触媒としての活性が高いため好適に用いられる。特に、金属粒子１２は、白金または白金合金であることが好ましい。なお、電極触媒層が含む金属粒子１２の構成材料は、１種類であってもよいし、２種類以上であってもよい。
　金属粒子１２の平均粒径は、０．５ｎｍ以上２０ｎｍ以下であることが好ましく、１ｎｍ以上５ｎｍ以下であることがより好ましい。金属粒子１２の平均粒径が０．５ｎｍ以上であれば、触媒としての安定性が高められる。金属粒子１２の平均粒径が２０ｎｍ以下であれば、触媒としての活性が高められる。
　なお、本明細書において、粒子の平均粒径は、ＴＥＭ画像の解析による平均径（例えばＪＩＳ　Ｈ７８０４：２００５）である。
　電極触媒層が含む金属粒子１２の総質量は、触媒担持担体１５の総質量に対して、５質量％以上７５質量％以下であることが好ましく、１０質量％以上７０質量％以下であることがより好ましい。
　（無機被膜）
　無機被膜１３の材料は、シリカ（ＳｉＯ２）、ジルコニア（ＺｒＯ２）、および、チタニア（ＴｉＯ２）のうちの１種以上を含むことが好ましい。なかでも、無機被膜１３の材料は、シリカであることが好ましく、特に、テトラエトキシシランもしくはトリエトキシメチルシランのいずれかを加水分解および脱水縮合することにより得られたシリカであることが好ましい。こうしたシリカが用いられることにより、無機被膜１３が、シリカ膜からなる多層構造に形成されるため、無機被膜１３の内部にイオン液体１４が保持されやすくなる。なお、テトラエトキシシランから生成されたシリカの組成は、（ＳｉＯ）ｎである。また、トリエトキシメチルシランから生成されたシリカの組成は、（ＳｉＯ－Ｍｅ－ＳｉＯ）ｎであって、当該シリカはポーラスシリカ（低結晶性シリカ）である。
　無機被膜１３の膜厚は、１ｎｍ以上１００ｎｍ以下であることが好ましく、１０ｎｍ以上５０ｎｍ以下であることがより好ましく、２０ｎｍ以上４０ｎｍ以下であることがさらに好ましい。無機被膜１３の膜厚が１ｎｍ以上であれば、無機被膜１３の形成が容易である。また、無機被膜１３の膜厚が１００ｎｍ以下であれば、多層構造における層間の隙間が十分に確保されやすい。また、無機被膜１３が剥がれにくくなる。
　（イオン液体）
　イオン液体１４は、イミダゾリウム塩であることが好ましい。イミダゾリウム塩とは、イミダゾール環構造を有するカチオンとカウンターアニオンとの塩である。カチオンは、例えば、下記構造式に示す化合物である。下記構造式において、ＲおよびＲ’は、各々独立に、－ＣＨ３、－Ｃ２Ｈ５、－Ｃ３Ｈ７、－Ｃ４Ｈ９、－Ｃ６Ｈ１３、および、－ＣＨ２－ＣＨ＝ＣＨ２からなる群から選択される基である。

　カウンターアニオンの例は、Ｃｌ－、Ｂｒ－、Ｉ－、ＢＦ４ －、ＰＦ６ －、ＦＳＩ（（ＦＳＯ２）２Ｎ－）、ＴＦＳＩ（（ＣＦ３ＳＯ２）２Ｎ－）である。
　具体的には、イオン液体１４は、１－アルキル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを含んでいることが好ましい。当該化合物が含むアルキル基は、例えば、メチル基、エチル基、ブチル基、ペンチル基、ヘプチル基、オクチル基、ノニル基、デシル基等である。なかでも、アルキル基は、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基であることが好ましく、エチル基であることがより好ましい。すなわち、イオン液体１４は、１－エチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミド、１－プロピル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミド、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミド、１－ペンチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミド、および、１－ヘキシル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドから選択される少なくとも１つを含むことが好ましく、１－エチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを含むことがより好ましい。アルキル基が長くなると、金属粒子１２表面の活性サイトが減少し、ＥＣＳＡが低下する。
　例えば、イオン液体１４は、１－エチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドのみから構成されていることが好ましいが、当該化合物以外に、他の１－アルキル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを含んでいてもよい。イオン液体１４が、複数の種類の１－アルキル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを含む場合には、１－エチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドの含有率がイオン液体１４全体の質量の５０％以上であることが好ましい。
　電極触媒層が含むイオン液体１４の総質量は、触媒担持担体１５の総質量に対して、２質量％以上３０質量％以下であることが好ましい。
　［固体高分子形燃料電池］
　図５を参照して、上述の膜電極接合体２０を備える固体高分子形燃料電池の構成を説明する。
　図５に示すように、固体高分子形燃料電池３０は、膜電極接合体２０と、一対のガス拡散層３１Ａ，３１Ｃと、一対のセパレータ３２Ａ，３２Ｃとを備えている。膜電極接合体２０は、ガス拡散層３１Ａとガス拡散層３１Ｃとの間に挟まれており、ガス拡散層３１Ａは燃料極触媒層２２Ａに接し、ガス拡散層３１Ｃは空気極触媒層２２Ｃに接している。
　ガス拡散層３１Ａ，３１Ｃは、供給されるガスを均一に拡散するための層であり、ガスの拡散性および導電性を有する。ガス拡散層３１Ａ，３１Ｃは、例えば、カーボンクロス、カーボンペーパー、不織布等のポーラス材を含む。ガス拡散層３１Ａは、燃料極触媒層２２Ａと共に燃料極を構成し、ガス拡散層３１Ｃは、空気極触媒層２２Ｃと共に空気極を構成する。
　膜電極接合体２０とガス拡散層３１Ａ，３１Ｃとの積層体は、セパレータ３２Ａとセパレータ３２Ｃとの間に挟持されている。セパレータ３２Ａ，３２Ｃは、ガス不透過性であって、導電性を有する。セパレータ３２Ａ，３２Ｃの材料は、例えば、炭素系あるいは金属系の材料である。セパレータ３２Ａ，３２Ｃの材料は、強度および成形性の良好な材料であることが好ましい。
　セパレータ３２Ａは、ガス拡散層３１Ａと向かい合い、セパレータ３２Ｃは、ガス拡散層３１Ｃと向かい合う。セパレータ３２Ａにて、ガス拡散層３１Ａと向かい合う面には、ガス流路３３Ａが形成され、ガス拡散層３１Ａとは反対側の面には、冷却水流路３４Ａが形成されている。同様に、セパレータ３２Ｃにて、ガス拡散層３１Ｃと向かい合う面には、ガス流路３３Ｃが形成され、ガス拡散層３１Ｃとは反対側の面には、冷却水流路３４Ｃが形成されている。
　固体高分子形燃料電池３０の使用時には、セパレータ３２Ａのガス流路３３Ａに水素等の燃料ガスが流され、セパレータ３２Ｃのガス流路３３Ｃに酸素等の酸化剤ガスが流される。また、各セパレータ３２Ａ，３２Ｃの冷却水流路３４Ａ，３４Ｃには、冷却水が流される。そして、ガス流路３３Ａから燃料極に燃料ガスが供給され、ガス流路３３Ｃから空気極に酸化剤ガスが供給されることによって、下記の（式１）および（式２）で示す電極反応が進行し、燃料極と空気極との間に起電力が生じる。なお、燃料極には、メタノール等の有機物燃料が供給されてもよい。
　燃料極：Ｈ２ → ２Ｈ＋ ＋ ２ｅ－　　　　　　　　　　　　　　　・・・（式１）
　空気極：１/２Ｏ２＋２Ｈ＋＋ ２ｅ－→Ｈ２Ｏ　　　・・・（式２）
　固体高分子形燃料電池３０は、図５に示した単セルの状態で用いられてもよいし、複数の固体高分子形燃料電池３０が積層されて直列接続されることにより１つの燃料電池として用いられてもよい。固体高分子形燃料電池３０を、ガス供給装置、冷却装置、その他の付随装置に組み付けることで、固体高分子形燃料電池３０の使用が可能となる。
　なお、固体高分子形燃料電池３０は、上記の部材に加えて、ガスの漏れを抑制するためのガスケット等の部材を備えていてもよい。また、ガス拡散層３１Ａとセパレータ３２Ａとは、一体の構造物であってもよいし、ガス拡散層３１Ｃとセパレータ３２Ｃとは、一体の構造物であってもよい。あるいは、ガス拡散層３１Ａ，３１Ｃは、膜電極接合体２０を構成する部材であってもよい。
　［触媒粒子の製造方法］
　触媒粒子１０は、導電性担体１１に金属粒子１２を担持させて触媒担持担体１５を生成し、触媒担持担体１５にイオン液体１４を含浸させた後に、無機被膜１３を形成することにより製造される。イオン液体１４の含浸に際しては、触媒担持担体１５にイオン液体１４の溶液を含浸させ、その後、溶媒を除去すればよい。溶媒の例はアセトニトリルである。無機被膜１３の形成には、ＴＥＯＳ等の原料を用いたゾル－ゲル法等の公知の被膜形成方法が用いられる。
　イオン液体１４の含浸よりも前に無機被膜１３を形成する場合には、金属粒子１２表面の帯電状態の調整のために触媒担持担体１５に界面活性剤を付与した後に無機被膜１３を形成し、その後に界面活性剤を除去することが必要となる。そして、界面活性剤の除去工程では高温での熱処理を要するため、触媒担持担体１５が高温に曝される結果、導電性担体１１が炭素材料である場合、導電性担体１１の劣化、すなわち結晶化の悪化が起こる。その結果、触媒粒子１０を用いた電極触媒層の耐久性が低下してしまう。
　これに対し、触媒担持担体１５にイオン液体１４を含浸させた後に無機被膜１３を形成する製法を用いることで、界面活性剤を要さずに無機被膜１３の形成が可能である。それゆえ、熱処理を回避して導電性担体１１の劣化を抑えることが可能であり、電極触媒層の耐久性の低下を抑えることができる。
　触媒粒子１０において、炭素材料である導電性担体１１のラマン分光法によるＧバンドとＤバンドのピーク強度比（Ｇ／Ｄ比）は、好ましくは１．６以上２．２以下であり、より好ましくは１．８以上２．０以下である。Ｇ／Ｄ比が上記範囲内であれば、導電性担体１１の結晶性が好適であることから、電極触媒層の耐久性の低下を抑えることができる。そして、触媒担持担体１５にイオン液体１４を含浸させた後に無機被膜１３を形成する製法を用いることで、無機被膜１３を有する触媒粒子１０であっても、導電性担体１１のＧ／Ｄ比を上記範囲内に留めることが容易である。
　なお、本明細書において、ラマン分光法で用いるレーザー光の波長は５３２ｎｍである。また、Ｇバンドとは、１５８０ｃｍ－１付近に位置するラマンピークを意味し、Ｄバンドとは、１３６０ｃｍ－１付近に位置するラマンピークを意味する。
　［電極触媒層および膜電極接合体の製造方法］
　燃料極触媒層２２Ａおよび空気極触媒層２２Ｃの各々は、各電極触媒層の材料を含む触媒層用スラリーを基材に塗布して塗膜を形成し、塗膜を乾燥することによって製造できる。
　触媒層用スラリーの溶媒は、触媒層用スラリーの分散媒として機能する。溶媒は、電極触媒層の材料を浸食せず、かつ、流動性の高い状態で高分子電解質を溶解する、あるいは、微細ゲルとして分散することが可能であれば特に限定されない。溶媒は、揮発性の有機溶媒を含むことが好ましい。
　溶媒は、例えば、水、アルコール類、ケトン類、エーテル類、アミン類、エステル類である。アルコール類の例は、メタノール、エタノール、１‐プロパノール、２‐プロパノール、１‐ブタノール、２‐ブタノール、イソブチルアルコール、ｔｅｒｔ‐ブチルアルコールである。ケトン類の例は、アセトン、メチルエチルケトン、メチルプロピルケトン、メチルブチルケトン、メチルイゾブチルケトン、メチルアミルケトン、ペンタノン、へプタノン、シクロヘキサノン、メチルシクロヘキサノン、アセトニルアセトン、ジエチルケトン、ジプロピルケトン、ジイソブチルケトンである。エーテル類の例は、テトラヒドロフラン、テトラヒドロピラン、ジオキサン、ジエチレングリコールジメチルエーテル、アニソール、メトキシトルエン、ジエチルエーテル、ジプロピルエーテル、ジブチルエーテルである。アミン類の例は、イソプロピルアミン、ブチルアミン、イソブチルアミン、シクロヘキシルアミン、ジエチルアミン、アニリンである。エステル類の例は、蟻酸プロピル、蟻酸イソブチル、蟻酸アミル、酢酸メチル、酢酸エチル、酢酸プロピル、酢酸ブチル、酢酸イソブチル、酢酸ペンチル、酢酸イソペンチル、プロピオン酸メチル、プロピオン酸エチル、プロピオン酸ブチルである。その他、溶媒として、酢酸、プロピオン酸、ジメチルホルムアミド、ジメチルアセトアミド、Ｎ‐メチルピロリドン、エチレングリコール、ジエチレングリコール、プロピレングリコール、エチレングリコールモノメチルエーテル、エチレングリコールジメチルエーテル、エチレングリコールジエチルエーテル、ジアセトンアルコール、１‐メトキシ‐２‐プロパノール、１‐エトキシ‐２‐プロパノール等を用いてもよい。
　なお、溶媒が低級アルコールを含む場合、発火の恐れを低減するために、溶媒を水との混合溶媒とすることが好ましい。水の添加量は、高分子電解質の分離による白濁や高分子電解質のゲル化が生じない程度であれば特に制限はない。
　触媒層用スラリーに対しては、分散処理が行われてもよい。分散処理には、例えば、遊星型ボールミル、ビーズミル、超音波ホモジナイザー等が用いられる。
　触媒層用スラリーの塗布方法は特に限定されず、例えば、ドクターブレード法、ダイコーティング法、カーテンコーティング法、ディッピング法、スクリーン印刷法、ラミネータロールコーティング法、スプレー法、スキージーを用いる方法等を用いることができる。
　塗膜の乾燥方法には、温風乾燥、ＩＲ（Infrared Rays）乾燥、ホットプレートを用いた乾燥、減圧乾燥等を用いることができる。乾燥温度は、４０℃以上２００℃以下であることが好ましく、４０℃以上１２０℃以下であることがより好ましい。乾燥時間は、０．５分以上１時間以下であることが好ましく、１分以上３０分以下であることがより好ましい。乾燥時には、電極触媒層を厚さ方向にプレスすることが好ましい。
　電極触媒層の形成のための基材は、触媒層２２Ａ，２２Ｃを高分子電解質膜２１に転写した後に剥離される転写基材であってもよいし、ガス拡散層３１Ａ，３１Ｃであってもよいし、高分子電解質膜２１であってもよい。
　基材が転写基材である場合、熱圧着によって触媒層２２Ａ，２２Ｃが高分子電解質膜２１に接合された後、転写基材が触媒層２２Ａ，２２Ｃから剥離される。これにより、膜電極接合体２０が形成される。
　転写基材の材料は、例えば、フッ素系樹脂や、フッ素系樹脂以外の有機高分子化合物である。フッ素系樹脂を含む転写基材は、転写性に優れている。フッ素系樹脂の例は、エチレンテトラフルオロエチレン共重合体（ＥＴＦＥ）、テトラフルオロエチレン－ヘキサフルオロプロピレン共重合体（ＦＥＰ）、テトラフルオロパーフルオロアルキルビニルエーテル共重合体（ＰＦＡ）、ポリテトラフルオロエチレン（ＰＴＦＥ）である。有機高分子化合物の例は、ポリイミド、ポリエチレンテレフタラート、ポリアミド（ナイロン：登録商標）、ポリサルホン、ポリエーテルサルホン、ポリフェニレンサルファイド、ポリエーテルエーテルケトン、ポリエーテルイミド、ポリアリレート、ポリエチレンナフタレートである。
　基材がガス拡散層３１Ａ，３１Ｃである場合、ガス拡散層３１Ａ，３１Ｃに支持された触媒層２２Ａ，２２Ｃが熱圧着によって高分子電解質膜２１に接合されることにより、膜電極接合体２０が形成される。
　基材が高分子電解質膜２１である場合、触媒層２２Ａ，２２Ｃが高分子電解質膜２１の面上に直接に形成される。これにより、膜電極接合体２０が形成される。高分子電解質膜２１に直接に触媒層２２Ａ，２２Ｃを形成すると、高分子電解質膜２１と触媒層２２Ａ，２２Ｃとの密着性が高くなり、また、圧着によって触媒層２２Ａ，２２Ｃが潰れる恐れもないため、好ましい。
　電極触媒層の形成のための基材が転写基材またはガス拡散層３１Ａ，３１Ｃである場合、電極触媒層の転写時に電極触媒層に加わる圧力や温度が膜電極接合体２０の発電性能に影響する。発電性能が高い膜電極接合体２０を得るためには、電極触媒層に加わる圧力は、０．１ＭＰａ以上２０ＭＰａ以下であることが好ましい。圧力が２０ＭＰａ以下であることによって、電極触媒層が過剰に圧縮されることが抑えられる。圧力が０．１ＭＰa以上であることによって、電極触媒層と高分子電解質膜２１との接合性の低下により発電性能が低下することが抑えられる。接合時の温度は、高分子電解質膜２１と電極触媒層との接合性の向上や、界面抵抗の抑制の観点から、高分子電解質膜２１または電極触媒層が含む高分子電解質のガラス転移点付近であることが好ましい。
　電極触媒層の厚さは、２μｍ以上２０μｍ以下であることが好ましい。電極触媒層の厚さが２０μｍ以下であれば、クラックの発生が抑えられるとともに、ガスや水の拡散性および導電性が好適に得られやすい。電極触媒層の厚さが２μｍ以上であれば、電極触媒層の厚さにばらつきが生じ難くなり、電極触媒層内の触媒担持担体１５や高分子電解質１６の分布が均一となりやすい。
　電極触媒層の厚さは、例えば、膜電極接合体２０の断面を、走査型電子顕微鏡（ＳＥＭ）を用いて観察することによって計測することができる。例えば、観察倍率１０００倍から１００００倍程度の電極触媒層全体が収まる視野内で、電極触媒層の厚みを測長すればよい。電極触媒層内での偏りなく厚さを把握するため、少なくとも２０カ所以上の観察点において同様に計測することが好ましい。膜電極接合体２０の断面を露出させる方法としては、例えば、イオンミリング、ウルトラミクロトーム等の公知の方法を用いることができる。
　＜第１実施形態の課題＞
　現在、燃料電池の利用に要するコストの削減のために、高出力かつ高耐久の燃料電池が望まれている。しかし、低加湿条件では、電極触媒層内の高分子電解質によるプロトン輸送の効率が低下するため、出力が低下するという課題がある。また、電極触媒層内の触媒である金属粒子は、長時間使用すると粗大化するため、これによっても出力が低下する。
　特許文献１（特許第７０２６６６９号公報）には、電極触媒層がイオン液体を含有することにより、低加湿条件での出力の向上が期待できると記載されている。しかし、イオン液体は電極触媒層内の空隙率を低下させるため、排水性が低下する。このことにより、高加湿条件においては、生成水によるフラッディングが発生し、発電性能が低下する。また、特許文献１には、触媒およびイオン液体の種類や重量比率についての記載はあるが、電極触媒層の構造についての記載はない。
　第１実施形態は、イオン液体を含有しながらも、排水性やガス拡散性が向上可能であり、高加湿条件および低加湿条件において高出力かつ高耐久な電極触媒層を提供することを目的とする。
　＜第１実施形態の電極触媒層の特徴＞
　第１実施形態では、電極触媒層が、触媒担持担体１５、高分子電解質１６、および、繊維状物質１７に加えて、イオン液体１４を含む。これにより、低加湿条件においても、プロトン輸送の効率の低下を抑制することが可能となる。また、無機被膜１３によって、金属粒子１２の粗大化およびイオン液体１４の流出を抑制でき、耐久性を向上させることが可能である。ただし、第１実施形態の課題解決のためには、無機被膜１３は必須ではない。
　第１実施形態の電極触媒層の密度は、１０００ｍｇ／ｃｍ３以上１６００ｍｇ／ｃｍ３以下である。電極触媒層の密度は、１０５０ｍｇ／ｃｍ３以上でもよく、１１００ｍｇ／ｃｍ３以上でもよい。
　電極触媒層の密度を１０００ｍｇ／ｃｍ３以上１６００ｍｇ／ｃｍ３以下とするためには、電極触媒層における繊維状物質１７の添加量や繊維長、電極触媒層の形成時の乾燥温度や温度勾配、乾燥中または乾燥後における厚さ方向のプレス圧力等の条件を調整すればよい。電極触媒層の密度を高めるためには、乾燥温度は４０℃以上１５０℃以下であることが好ましく、プレス圧力は０．０５ＭＰａ以上８ＭＰａ以下であることが好ましい。
　電極触媒層の密度を高める観点では、電極触媒層が含む金属粒子１２の総質量は、触媒担持担体１５の総質量に対して、５質量％以上７５質量％以下であることが好ましい。また、電極触媒層の密度を高める観点では、電極触媒層が含む高分子電解質１６の総質量は、導電性担体１１の質量に対する質量比で０．１以上２．０以下であることが好ましい。また、電極触媒層の密度を高める観点では、電極触媒層が含むイオン液体１４の総質量は、触媒担持担体１５の総質量に対して、２質量％以上３０質量％以下であることが好ましい。
　電極触媒層の密度を高める観点では、電極触媒層における繊維状物質１７の含有量は、導電性担体１１の総質量に対して１質量％以上３００質量％以下であることが好ましい。繊維状物質１７の含有量が多すぎると、密度が小さくなって排水性が向上するが、電極触媒層が厚くなり、性能が低下しやすくなる傾向がある。繊維状物質１７の含有量が少なすぎると、密度が大きくなってフラッディングが発生しやすくなる傾向がある。
　電極触媒層が、触媒担持担体１５、高分子電解質１６、繊維状物質１７、および、イオン液体１４を含み、電極触媒層の密度が１０００ｍｇ／ｃｍ３以上１６００ｍｇ／ｃｍ３以下であることにより、排水性やガス拡散性が向上可能であり、高加湿条件および低加湿条件において高い出力および高い耐久性が得られる。
　イオン液体１４を含有する電極触媒層において、電極触媒層の密度が従来のように低いと、電極触媒層の厚さの増加により、電気抵抗や拡散抵抗が増加すると考えられる。イオン液体１４を含有する電極触媒層において、電極触媒層の密度がある程度高くなると、ガス拡散性や排水性を十分に確保したまま、電気抵抗や拡散抵抗が低減すると考えられる。
　なお、燃料極触媒層２２Ａおよび空気極触媒層２２Ｃの少なくとも一方が、上述した第１実施形態の特徴を有していればよい。
　また、金属粒子１２は、導電性担体１１に代えて繊維状物質１７に担持されていてもよいし、導電性担体１１と繊維状物質１７とのいずれもが金属粒子１２を担持していてもよい。電極触媒層内において、繊維状物質１７の絡み合いにより形成された空隙は、発電による生成水の排出経路となり得る。ここで、繊維状物質１７が金属粒子１２を担持する場合には、生成水の排出経路内で電極反応も起こる。一方で、導電性担体１１が金属粒子１２を担持していると、導電性担体１１と金属粒子１２とガスとに起因する三相界面による反応点と、繊維状物質１７により形成された空間による生成水の排出経路とを区別できることから、電極触媒層の排水性の向上が可能であるため好ましい。
　＜第１実施形態の実施例＞
　［実施例１－１］
　イオン液体を含む触媒粒子である白金担持カーボン（ＴＥＣ１０Ｅ５０Ｅ、田中貴金属社製）を２０ｇ容器にとり、水と混合した。２０ｇの内訳は、導電性担体が９．３８ｇ、白金が８．３２ｇ、イオン液体が２．３０ｇである。この混合液に、１－プロパノール、高分子電解質（Ｎａｆｉｏｎ（登録商標）分散液、電解質質量７．５０ｇ、和光純薬工業社製）、１０ｇの繊維状物質であるカーボンナノファイバー（商品名「ＶＧＣＦ」、昭和電工社製、繊維径約１５０ｎｍ、繊維長約１０μｍ）を加えて撹拌して、触媒層用スラリーを得た。触媒層用スラリーを高分子電解質膜（Ｎａｆｉｏｎ２１２、ケマーズ社製）にダイコーティング法で塗工し、炉内で乾燥することで、実施例１－１の電極触媒層を有した膜電極接合体を得た。
　［実施例１－２］
　繊維状物質としてアゾール構造を有する樹脂繊維（繊維径約２００ｎｍ、繊維長約２０μｍ）を用いたこと以外は、実施例１－１と同様の手順で実施例１－２の電極触媒層を有した膜電極接合体を得た。
　［実施例１－３］
　イオン液体を含む白金担持カーボンをシリカで被覆したこと以外は、実施例１－１と同様の手順で実施例１－３の電極触媒層を有した膜電極接合体を得た。
　［実施例１－４］
　繊維状物質としてアゾール構造を有する樹脂繊維（繊維径約２００ｎｍ、繊維長約２０μｍ）を用いたこと以外は、実施例１－３と同様の手順で実施例１－４の電極触媒層を有した膜電極接合体を得た。
　［比較例１－１］
　イオン液体を含まない白金担持カーボンを用いたこと以外は、実施例１－１と同様の手順で比較例１－１の電極触媒層を有した膜電極接合体を得た。
　［比較例１－２］
　電極触媒層の密度が１０００ｍｇ／ｃｍ２未満になるように繊維状物質の量を１．５倍に増やしたこと以外は、実施例１－１と同様の手順で比較例１－２の電極触媒層を有した膜電極接合体を得た。
　［比較例１－３］
　電極触媒層の密度が１６００ｍｇ／ｃｍ２を超えるように繊維状物質の量を０．５倍に減らしたこと以外は、実施例１－１と同様の手順で比較例１－３の電極触媒層を有した膜電極接合体を得た。
　［比較例１－４］
　繊維状物質を加えないこと以外は、実施例１－１と同様の手順で比較例１－４の電極触媒層を有した膜電極接合体を得た。
　［クラックの観察］
　各実施例および各比較例の電極触媒層について、顕微鏡（倍率：２００倍）で１０μｍ以上クラックの有無を確認した。結果を表１に示す。
Figure JPOXMLDOC01-appb-T000002
　表１に示す通り、電極触媒層が繊維状物質を含有していない比較例１－４では、クラックが発生した。これに対して、各実施例および比較例１－１～１－３のように電極触媒層が繊維状物質を含有している場合には、クラックの発生が確認されなかった。
　［密度の算出］
　電極触媒層の密度は、電極触媒層の質量と厚さから求めた。質量は、触媒層用スラリー塗工量から求めた質量または乾燥質量を用いた。厚さは、走査型電子顕微鏡（倍率：２０００倍）で電極触媒層の断面を観察することにより求めた。
　［発電特性の評価］
　電極触媒層の外側にガス拡散層（ＳＩＧＲＡＣＥＴ（Ｒ）　２２ＢＢ、ＳＧＬ社製）を配置し、市販のＪＡＲＩ標準セルを用いて発電特性の評価を行った。セル温度は、８０℃とした。高加湿条件では、アノードに水素（１００％ＲＨ）、カソードに空気（１００％ＲＨ）を、低加湿条件では、アノードに水素（３０％ＲＨ）、カソードに空気（３０％ＲＨ）を、供給した。
　［耐久性能の評価］
　耐久試験として、新エネルギー・産業技術総合開発機構（ＮＥＤＯ）が刊行する「セル評価解析プロトコル」に記載されている電位サイクル試験を実施した。耐久試験の前後における発電特性を測定し、電流密度が１．５Ａ／ｃｍ２のときの電圧降下量を算出して耐久性を評価した。
　表２に、各実施例および各比較例について、電極触媒層の密度、低加湿条件および高加湿条件での発電特性の評価結果、および、耐久性の評価結果を示す。発電性能および耐久性は、比較例１を基準として比較例１に対する比率で示している。ここで、電極触媒層における触媒含有量は全ての膜電極接合体で同様である。
Figure JPOXMLDOC01-appb-T000003
　表１および表２から、電極触媒層が、触媒担持担体とイオン液体と高分子電解質と繊維状物質とを含み、電極触媒層の密度が１０００ｍｇ／ｃｍ３以上１６００ｍｇ／ｃｍ３以下であることで、電極触媒層においてクラックが発生せず、イオン液体を含有する電極触媒層であっても、高加湿条件および低加湿条件の双方で高出力かつ高耐久性が得られることが確認された。
　（第２実施形態）
　電極触媒層、膜電極接合体、および、固体高分子形燃料電池の第２実施形態を説明する。第２実施形態は、第１実施形態と同様の基本構成を有する。以下では、第２実施形態と第１実施形態との相違点を中心に説明し、第１実施形態と同様の構成については同じ符号を付してその説明を省略する。なお、第２実施形態の特徴は他の実施形態の特徴と組み合わせ可能である。
　＜第２実施形態の課題＞
　現在、燃料電池の利用に要するコストの削減のために、高出力かつ高耐久の燃料電池が望まれている。しかし、低加湿条件では、電極触媒層内の高分子電解質によるプロトン輸送の効率が低下するため、出力が低下するという課題がある。また、電極触媒層内の触媒である金属粒子は、長時間使用すると粗大化するため、これによっても出力が低下する。
　特許文献１（特許第７０２６６６９号公報）には、電極触媒層がイオン液体を含有することにより、プロトン輸送が促進され、低加湿条件での出力の向上が期待できると記載されている。
　しかし、燃料電池の運転が長時間続くと、イオン液体が流出するために徐々に出力が低下する。すなわち、イオン液体を用いた電極触媒層には耐久性に問題がある。また、電極触媒層がイオン液体を含有していても、長時間の運転による金属粒子の粗大化を抑制することはできない。結局のところ、イオン液体の含有だけでは、出力の向上が短期間に限定されてしまい、耐久性の課題を解決することはできない。
　第２実施形態は、発電性能および耐久性に優れた電極触媒層、膜電極接合体、および、固体高分子形燃料電池を提供することを目的とする。
　＜第２実施形態の特徴＞
　図６および図７に示すように、無機被膜１３は、導電性担体１１および金属粒子１２の表面と接触するイオン液体１４を介して、導電性担体１１の表面および金属粒子１２の表面を被覆している。導電性担体１１の表面の一部が無機被膜１３で被覆されていればよく、金属粒子１２の表面の一部が無機被膜１３で被覆されていればよい。無機被膜１３は、主としてイオン液体１４を介して金属粒子１２を被覆している。
　触媒担持担体１５にイオン液体１４を含浸させた後に、無機被膜１３を形成することにより、イオン液体１４を介して導電性担体１１および金属粒子１２の表面を無機被膜１３で被覆することができる。無機被膜１３はシリカを含む。特に、無機被膜１３は、テトラエトキシシランを加水分解および脱水縮合することにより得られたシリカから構成されていることが好ましい。
　第２実施形態において、電極触媒層のエネルギー分散型Ｘ線分光分析により得られる、炭素、窒素、酸素、フッ素、ケイ素、硫黄、および、白金元素の合計原子数に占めるケイ素の原子数の割合は０．５ａｔ％以上１０ａｔ％以下である。
　上記ケイ素の原子数の割合は、例えば、エネルギー分散型Ｘ線分光分析装置が搭載された透過型電子顕微鏡（ＴＥＭ－ＥＤＸ）を用いて元素マッピングを行うことで計測することができる。ＴＥＭ－ＥＤＸにおけるＸ線の加速電圧は２００ｋＶとすることが好適である。このような加速電圧により、特定領域において１００ｎｍ程度の厚みまで電子線を透過させることができ、電極触媒層の元素の情報が得られる。元素マッピングを行う領域である観察エリアの形状は、例えば矩形である。観察エリアは、例えば、縦が１５０ｎｍ、横が１５０ｎｍの正方形や、縦が３０ｎｍ、横が５０ｎｍの長方形である。観察エリアは、触媒粒子１０が面積の２０％以上を占める領域とすることが好ましい。
　元素マッピングに供する電極触媒層は、１００ｎｍ程度の薄片に加工される。薄片への加工には、例えば、収束イオンビーム、ウルトラミクロトーム等の公知の方法を用いることができる。薄片への加工を行う際には、電極触媒層を構成する高分子電解質１６へのダメージを軽減するため、電極触媒層を冷却しながら加工を行うことが特に好ましい。
　発明者は、固体高分子形燃料電池の発電性能と耐久性について鋭意検討を行った結果、発電性能には電極触媒層におけるプロトン伝導性が大きく影響しており、触媒である金属粒子１２と触媒を担持する導電性担体１１とをイオン液体１４で被覆すると、プロトン伝導性が向上することを見出した。さらに、発明者は、金属粒子１２および導電性担体１１を、Ｓｉを含む無機被膜１３で被覆すると、イオン液体１４の流出および金属粒子１２の粗大化が抑制され、長期的に高い発電性能を発揮可能であることを突き止めた。
　詳細には、図７に示すように、無機被膜１３が金属粒子１２を覆っているため、電極触媒層にて触媒粒子１０を囲む高分子電解質１６中に金属粒子１２が溶出することが抑えられる。一方で、無機被膜１３が金属粒子１２を直接に覆っていると、プロトンを伝導する高分子電解質１６と電極反応の触媒として作用する金属粒子１２との接触が妨げられる。これに対し、本実施形態では、プロトンを通すことが可能なイオン液体１４が無機被膜１３と金属粒子１２との間に介在しているため、イオン液体１４を介してプロトンが伝導される。また、無機被膜１３内の隙間にイオン液体１４が浸透していれば、こうした無機被膜１３中のイオン液体１４もプロトン伝導に寄与する。また、金属粒子１２が、イオン液体１４および無機被膜１３に覆われていない露出部を有すると、電子伝導の観点から有利となる。
　さらに、図６に示すように、導電性担体１１の表面がイオン液体１４と接触していると、電極触媒層におけるプロトン伝導性が高められ、無機被膜１３がイオン液体を介して導電性担体１１を被覆していると、金属粒子１２の移動が妨げられて金属粒子１２の粗大化が抑制される。また、導電性担体１１が、イオン液体１４および無機被膜１３に被覆されていない露出部を有すると、電子伝導の観点から有利となる。
　さらに、電極触媒層のエネルギー分散型Ｘ線分光分析により得られる、炭素、窒素、酸素、フッ素、ケイ素、硫黄、および、白金元素の合計原子数に占めるケイ素の原子数の割合が、０．５ａｔ％以上１０ａｔ％以下であることにより、高い発電性能を発揮するとともに耐久性に優れた固体高分子形燃料電池が得られる。
　上記ケイ素の原子数の割合が０．５ａｔ％以上であることは、イオン液体１４の流出や金属粒子１２の粗大化を抑制する無機被膜１３の量が、的確に確保されていることを意味する。上記ケイ素の原子数の割合が１０ａｔ％以下であることは、無機被膜１３の量が過剰でなく、無機被膜１３によってプロトンや電子の伝導の阻害が生じることを抑えられることを意味する。
　以上のように、本実施形態の構成を採用することで、十分な排水性、ガス拡散性およびプロトン伝導性を有し、長期的に高い発電性能を発揮することが可能な電極触媒層、膜電極接合体、および、固体高分子形燃料電池を得ることができる。
　なお、燃料極触媒層２２Ａおよび空気極触媒層２２Ｃの少なくとも一方が、上述した第２実施形態の特徴を有していればよい。
　＜第２実施形態の実施例＞
　［実施例２－１］
　・触媒粒子の生成
　高結晶化カーボン担体に白金粒子が担持された白金担持カーボン（Ｐｔ質量割合５０質量％）をアセトニトリルに加えて、さらに、白金担持カーボンのメソ孔体積の６０％に相当する量のイオン液体を添加した。なお、触媒担持担体である白金担持カーボンのメソ孔体積の大きさは実質的に導電性担体のメソ孔体積の大きさと同じである。この混合物に対して、３０分間、超音波分散を実施した後、一晩、スターラーで撹拌後、エバポレーターでアセトニトリルを除去することにより、イオン液体が含浸した白金担持カーボンを得た。イオン液体としては、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドのみからなる液体を用いた。白金担持カーボンのメソ孔体積は、低温窒素吸着法を用いて、２ｎｍから１００ｎｍまでの空孔を対象として求めた。
　次に、上記イオン液体が含浸した白金担持カーボンを水に加え、超音波撹拌後、テトラエトキシシラン（ＴＥＯＳ）とエタノールとを含む混合溶液を加えた。その後、水酸化ナトリウムを加えて２時間撹拌後、遠心分離機を用いて分離物を得た。そして、分離物を８０℃で６時間乾燥させることにより、実施例１の触媒粒子を得た。この触媒粒子は、シリカからなる無機被膜を有している。
　上記にて、触媒粒子における無機被膜の被覆量はＴＥＯＳの量で調整し、無機被膜の重量比（シリカの重量／シリカおよび白金担持カーボンの総重量）が０．１となるようにした。
　・膜電極接合体の作製
　実施例１の触媒粒子と、高分子電解質と、繊維状物質と、分散媒とを混合した混合液に対して分散処理を実施することにより、触媒層用スラリーを調製した。触媒粒子以外の各材料は下記を用いた。
　高分子電解質：フッ素系高分子電解質（ナフィオン（登録商標）分散液、和光純薬工業社製）
　繊維状物質：アゾール構造を有する樹脂繊維（平均繊維長２０μｍ、平均繊維径２２０ｎｍ）
　分散媒：水と１－プロパノールとの質量比１：１の混合液
　高分子電解質および繊維状物質の配合量は、触媒層用スラリーにおける触媒粒子中の導電性担体の配合量を１００質量部として、高分子電解質が７０質量部であり、繊維状物質が２０質量部である。分散媒の配合量は、触媒インクにおける固形分濃度が１０質量％となる量とした。分散処理は、遊星型ボールミルを用いて、６００ｒｐｍの回転速度で６０分間、実施した。その際、直径２ｍｍのジルコニアボールをジルコニア容器の３分の１程度加えた。
　次に、ダイコーターを用いて、高分子電解質膜（ナフィオン（登録商標）２１１、デュポン社製）の片面に対して、触媒層用スラリーを１００μｍの厚さとなるように塗布することにより塗膜を形成した。塗膜の形状は正方形であり、１辺の長さは５０ｍｍとした。そして、８０℃のオーブンを用いた乾燥処理を実施し、塗膜に含まれる分散媒を揮発させることにより、空気極触媒層を形成した。
　次に、高分子電解質膜における空気極触媒層が形成された面の反対の面に対して、触媒層用スラリーを３０μｍの厚さとなるように塗布することにより塗膜を形成した。塗膜の形状は正方形であり、１辺の長さは５０ｍｍである。塗膜は、空気極触媒層に相対する位置に形成した。そして、８０℃のオーブンを用いた乾燥処理を実施し、塗膜に含まれる分散媒を揮発させることにより、燃料極触媒層を形成した。
　これにより、実施例２－１の電極触媒層を備える膜電極接合体を得た。
　［実施例２－１］
　触媒粒子の生成工程において、無機被膜の重量比が０．２となるようにＴＥＯＳの添加量を変更したこと以外は、実施例２－１と同様の材料および工程によって、実施例２－２の膜電極接合体を得た。
　［実施例２－３］
　触媒粒子の生成工程において、無機被膜の重量比が０．０１となるようにＴＥＯＳの添加量を変更したこと以外は、実施例２－１と同様の材料および工程によって、実施例２－３の膜電極接合体を得た。
　［実施例２－４］
　触媒層用スラリーを調製する工程において、繊維状物質としてカーボンナノファイバー（ＶＧＣＦ－Ｈ（登録商標）、昭和電工パッケージング社製、平均繊維長７μｍ、平均繊維径１５０ｎｍ）を添加したこと以外は、実施例２－１と同様の方法によって、実施例２－４の膜電極接合体を得た。
　［比較例２－１］
　触媒粒子の生成工程において、無機被膜の重量比が０．３となるようにＴＥＯＳの添加量を変更したこと以外は、実施例２－１と同様の材料および工程によって、比較例２－１の膜電極接合体を得た。
　［比較例２－２］
　白金担持カーボンに対する無機被膜の形成を実施しなかったこと以外は、実施例２－１と同様の材料および工程によって、比較例２－２の膜電極接合体を得た。すなわち、比較例２－２の触媒粒子は無機被膜を有していない。
　［比較例２－３］
　白金担持カーボンに対するイオン液体の含浸と無機被膜の形成を実施しなかったこと以外は、実施例２－１と同様の材料および工程によって、比較例２－３の膜電極接合体を得た。すなわち、比較例２－３の触媒粒子は、白金担持カーボンのみからなり、イオン液体および無機被膜を有していない。
　［ケイ素の原子数の比の測定］
　電極触媒層のエネルギー分散型Ｘ線分光分析により得られる、カーボン、窒素、酸素、フッ素、ケイ素、硫黄、および、白金元素の合計原子数に占めるケイ素の原子数の割合を測定した。具体的には、まず、電極触媒層を冷却しながら加工を行うクライオウルトラミクロトームを用いて、電極触媒層の薄片を得た。続いて、エネルギー分散型Ｘ線分光分析装置が搭載された透過型電子顕微鏡（ＴＥＭ－ＥＤＸ）を用いて元素マッピングを行い、各元素の元素比を得て、ケイ素の原子数の比を計算した。加速電圧は２００ｋＶとした。観察エリアは１５０ｎｍ×１５０ｎｍの大きさであり、白金担持カーボンが視野の面積の２０％以上を占めるようにした。
　［発電性能の評価］
　発電性能の測定では、新エネルギー・産業技術総合開発機構（ＮＥＤＯ）の刊行物である「セル評価解析プロトコル」に準拠して、膜電極接合体の両面にガス拡散層（ＳＩＧＲＡＣＥＴ（Ｒ）　２２ＢＢ、ＳＧＬ社製）、ガスケット、および、セパレータを配置し、所定の面圧となるように締め付けたＪＡＲＩ標準セルを評価用単セルとして用いた。そして、「セル評価解析プロトコル」に記載のＩＶ測定を実施した。なお、測定時のセル温度は、８０℃に設定した。加湿条件は、燃料極の相対湿度を８８％ＲＨ、空気極の相対湿度を４２％ＲＨとした。また、燃料ガスとして水素を用い、酸化剤ガスとして空気を用いた。この際に、水素を水素利用率が７０％となる流量で流すとともに、空気を酸素利用率が４０％となる流量で流した。
　［耐久性の評価］
　各実施例および各比較例について、上述の発電性能の評価で用いた評価用単セルを用い、新エネルギー・産業技術総合開発機構（ＮＥＤＯ）が刊行する「セル評価解析プロトコル」に記載されている負荷応答模擬電位サイクル試験を実施した。試験前と試験後のそれぞれについて、上述した発電性能の評価と同様の条件でＩＶ測定を実施した。
　表３に、各実施例および各比較例について、空気極触媒層におけるケイ素原子数の割合と、発電性能および耐久性の評価結果とを示す。なお、発電性能の評価では、電流が３５Ａのときの電圧が０．６５Ｖ以上である場合を「◎」とし、電流が３５Ａのときの電圧は０．６５Ｖ未満であるが電流が２５Ａのときの電圧が０．６５Ｖ以上である場合を「〇」とし、電流が２５Ａのときの電圧が０、６５Ｖ未満である場合を「×」とした。また、耐久性の評価では、電流密度が１．５Ａ／ｃｍ２のときの試験前に対する試験後の電圧降下率が２０％未満である場合を「◎」とし、上記電圧降下率が２０％以上３０％未満である場合を「〇」とし、上記電圧降下率が３０％以上である場合を「×」とした。
Figure JPOXMLDOC01-appb-T000004
　表３に示すように、実施例２－１～２－４のいずれにおいても、電極触媒層中のケイ素原子数の割合が０．５ａｔ％以上１０ａｔ％以下であった。そして、発電性能および耐久性の評価については、いずれも「◎」または「○」であった。すなわち、実施例２－１～２－４においては、発電性能および耐久性に優れた燃料電池を構成可能な膜電極接合体が得られた。
　一方、比較例２－１～２－３においては、いずれも、電極触媒層中のケイ素原子数の割合が０．５ａｔ％以上１０ａｔ％以下の範囲外となった。そして、発電性能および耐久性の評価については、少なくとも一方が「×」であった。すなわち、電極触媒層におけるケイ素原子数の割合が上記範囲外となった場合に、発電性能および耐久性の少なくとも一方が低下した。
　したがって、電極触媒層中のケイ素原子数の割合が０．５ａｔ％以上１０ａｔ％以下である場合に、発電性能および耐久性に優れた燃料電池を構成可能な膜電極接合体が得られることが確認された。
　（第３実施形態）
　電極触媒層、膜電極接合体、および、固体高分子形燃料電池の第３実施形態を説明する。第３実施形態は、第１実施形態と同様の基本構成を有する。以下では、第３実施形態と第１実施形態との相違点を中心に説明し、第１実施形態と同様の構成については同じ符号を付してその説明を省略する。なお、第３実施形態の特徴は他の実施形態の特徴と組み合わせ可能である。
　＜第３実施形態の課題＞
　電極反応の触媒として作用する金属粒子が高分子電解質中に溶出すると、燃料電池の出力の低下が起こる。そこで、特許文献２（特開２００８－４５４１号公報）では、金属粒子の溶出を抑えるために、金属粒子をシリカ等の多孔性無機材料で被覆することが提案されている。
　しかしながら、特許文献２のように金属粒子が多孔性無機材料で被覆されていると、金属粒子の溶出が抑えられる一方で、金属粒子と高分子電解質との接触が妨げられる。その結果、プロトンの伝導が阻害されて抵抗が増加することから、燃料電池の出力電圧が低下するという問題が生じる。
　従来から、金属粒子としては白金が広く用いられているが、白金は高価であるため、電極触媒層に使用する白金の量を低減したいという要請がある。白金の量を低減した電極触媒層においては特に、上記出力電圧の低下が顕著に起こる。
　＜第３実施形態の特徴＞
　無機被膜１３は、主として金属粒子１２を被覆している。金属粒子１２の表面の一部は、無機被膜１３から露出し、この露出部分の少なくとも一部において金属粒子１２はイオン液体１４と接している。
　上記構成によれば、無機被膜１３が金属粒子１２を覆っているため、電極触媒層にて触媒粒子１０を囲む高分子電解質１６中に金属粒子１２が溶出することが抑えられる。一方で、無機被膜１３が各金属粒子１２を完全に覆っていると、プロトンを伝導する高分子電解質１６と電極反応の触媒として作用する金属粒子１２との接触が妨げられる。これに対し、本実施形態では、プロトンを通すことが可能なイオン液体１４が金属粒子１２に接しているため、イオン液体１４を介してプロトンが伝導される。また、無機被膜１３内の隙間にイオン液体１４が浸透していれば、こうした無機被膜１３中のイオン液体１４もプロトン伝導に寄与する。さらに、導電性担体１１の表面の一部は無機被膜１３から露出しているため、電子伝導の経路も確保される。
　また、イオン液体１４が存在しない構成では、無機被膜１３がシリカ等の親水性材料から形成されている場合、特に電極反応によって水が生じる空気極にて、生成された水が無機被膜１３の付近に留められることから、電極触媒層の排水性の低下が生じる。これに対し、本実施形態では、親水性の低いイオン液体１４を用いることで、イオン液体１４の付近、すなわち触媒粒子１０付近での水の滞留を抑えることができる。これにより、電極触媒層の排水性の低下が抑えられる。
　触媒粒子１０において、無機被膜１３と触媒担持担体１５との合計重量に対する無機被膜１３の重量比は、０．０１以上０．２以下である。触媒担持担体１５の重量は、すなわち導電性担体１１と当該導電性担体１１に担持されている金属粒子１２との総重量である。
　上記無機被膜１３の重量比が０．０１以上であれば、金属粒子１２の溶出が十分に抑えられる程度に、触媒担持担体１５の表面に無機被膜１３が形成される。また、無機被膜１３内にイオン液体１４が保持されやすい。上記無機被膜１３の重量比が０．２以下であれば、無機被膜１３の膜厚や形成範囲が大きくなりすぎないため、好適なプロトン伝導が得られる程度に金属粒子１２とイオン液体１４との接触を確保できる。
　なお、無機被膜１３の重量比は、例えば、ＸＰＳ（Ｘ線光電子分光法）を用いて求めることができる。
　触媒粒子１０において、イオン液体１４の体積は、触媒担持担体１５のメソ孔体積の１０％以上５０％以下であることが好ましく、１０％以上３０％以下であることがより好ましい。上記メソ孔体積、すなわちメソポア領域の細孔容積は、２ｎｍから１００ｎｍまでの空孔総体積である。メソ孔体積は、例えば、低温窒素吸着法により求めることができる。
　イオン液体１４の上記体積割合が１０％以上であれば、イオン液体１４を介した高分子電解質と金属粒子１２との間のプロトン伝導が好適に可能になる。特に、空気極の電極触媒層では、十分な酸素還元活性が得られる。また、イオン液体１４の上記体積割合が５０％以下であれば、イオン液体１４の量が多くなりすぎない。イオン液体１４はプロトンを通す機能を有してはいるが、その程度は高分子電解質１６と比較すると補助的なものであり、イオン液体１４の量が多くなりすぎると、触媒粒子１０と高分子電解質１６との離間が大きくなって抵抗が増加してしまう。これに対し、イオン液体１４の上記体積割合が５０％以下であれば、イオン液体１４の過多に起因した抵抗の増加が抑えられる。
　以上のことから、本実施形態の触媒粒子１０を用いた燃料電池では、良好な発電性能が得られる。特に、金属粒子１２として白金系金属を用いたときに、金属粒子１２の担持量を低減した場合でも、高い出力を得ることができる。
　なお、燃料極触媒層２２Ａおよび空気極触媒層２２Ｃの少なくとも一方が、上述した第３実施形態の特徴を有していればよい。燃料極触媒層２２Ａと空気極触媒層２２Ｃとの一方のみが第３実施形態の特徴を有する場合、空気極触媒層２２Ｃが第３実施形態の特徴を有することが好ましい。
　＜第３実施形態の実施例＞
　［実施例３－１］
　・触媒粒子の生成
　触媒担持担体として白金担持カーボン（担持密度３０質量％）を用い、白金担持カーボンをアセトニトリルに加えて、さらに、白金担持カーボンのメソ孔体積の５０％に相当する量のイオン液体を添加した。この混合物に対して、３０分間、超音波分散を実施した後、一晩、スターラーで撹拌後、エバポレーターでアセトニトリルを除去することにより、イオン液体が含浸した触媒担持担体を得た。イオン液体としては、１－エチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドのみからなる液体を用いた。白金担持カーボンのメソ孔体積は、低温窒素吸着法を用いて、２ｎｍから１００ｎｍまでの空孔を対象として求めた。
　次に、上記イオン液体が含浸した触媒担持担体を水に加え、超音波撹拌後、テトラエトキシシラン（ＴＥＯＳ）とエタノールとを含む混合溶液を加えた。その後、水酸化ナトリウムを加えて２時間撹拌後、遠心分離機を用いて分離物を得た。そして、分離物を８０℃で６時間乾燥させることにより、実施例３－１の触媒粒子を得た。この触媒粒子は、シリカからなる無機被膜を有している。
　上記にて、触媒粒子における無機被膜の被覆量はＴＥＯＳの量で調整し、無機被膜の重量比（シリカの重量／シリカおよび触媒担持担体の総重量）が０．１となるようにした。
　・膜電極接合体の作製
　実施例１の触媒粒子と、高分子電解質と、繊維状物質と、分散媒とを混合した混合液に対して分散処理を実施することにより、触媒層用スラリーを調製した。触媒粒子以外の各材料は下記を用いた。
　高分子電解質：フッ素系高分子電解質（ナフィオン（登録商標）分散液、和光純薬工業社製）
　繊維状物質：炭素繊維（ＶＧＣＦ－Ｈ（登録商標）、昭和電工社製、平均繊維長６μｍ、平均繊維径１５０ｎｍ）　
　分散媒：水と１－プロパノールとの質量比１：１の混合液
　高分子電解質および繊維状物質の配合量は、触媒層用スラリーにおける触媒粒子中の導電性担体の配合量を１００質量部として、高分子電解質が７０質量部であり、繊維状物質が２０質量部である。分散媒の配合量は、触媒層用スラリーにおける固形分濃度が１０質量％となる量とした。分散処理は、直径３ｍｍのジルコニアボールおよび遊星型ボールミルを用いて、６００ｒｐｍの回転速度で６０分間、実施した。
　次に、ダイコーターを用いて、高分子電解質膜（ナフィオン（登録商標）２１１、デュポン社製）の片面に対して、触媒層用スラリーを塗布することにより塗膜を形成した。塗膜の形状は正方形であり、１辺の長さは５０ｍｍである。触媒層用スラリーの塗布量は、塗膜における白金担持量が０．１ｍｇ／ｃｍ２となる量とした。そして、８０℃のオーブンを用いた乾燥処理を実施し、塗膜に含まれる分散媒を揮発させることにより、空気極触媒層を形成した。
　次に、高分子電解質膜における空気極触媒層が形成された面の反対の面に対して、触媒層用スラリーを塗布することにより塗膜を形成した。塗膜の形状は正方形であり、１辺の長さは５０ｍｍである。触媒層用スラリーの塗布量は、塗膜における白金担持量が０．０５ｍｇ／ｃｍ２となる量とした。そして、８０℃のオーブンを用いた乾燥処理を実施し、塗膜に含まれる分散媒を揮発させることにより、燃料極触媒層を形成した。
　これにより、実施例３－１の電極触媒層を備える膜電極接合体を得た。
　［実施例３－２］
　触媒粒子の生成工程において、イオン液体の添加量を白金担持カーボンのメソ孔体積の３０％に相当する量に変更したこと以外は、実施例３－１と同様の材料および工程によって、実施例３－２の膜電極接合体を得た。
　［実施例３－３］
　触媒粒子の生成工程において、イオン液体の添加量を白金担持カーボンのメソ孔体積の１０％に相当する量に変更したこと以外は、実施例３－１と同様の材料および工程によって、実施例３－３の膜電極接合体を得た。
　［実施例３－４］
　触媒粒子の生成工程において、無機被膜の重量比が０．２となるようにＴＥＯＳの添加量を変更したこと以外は、実施例３－１と同様の材料および工程によって、実施例３－４の膜電極接合体を得た。
　［実施例３－５］
　触媒粒子の生成工程において、無機被膜の重量比が０．２となるようにＴＥＯＳの添加量を変更したこと、および、イオン液体の添加量を白金担持カーボンのメソ孔体積の３０％に相当する量に変更したこと以外は、実施例３－１と同様の材料および工程によって、実施例３－５の膜電極接合体を得た。
　［実施例３－６］
　触媒粒子の生成工程において、無機被膜の重量比が０．２となるようにＴＥＯＳの添加量を変更したこと、および、イオン液体の添加量を白金担持カーボンのメソ孔体積の１０％に相当する量に変更したこと以外は、実施例３－１と同様の材料および工程によって、実施例３－６の膜電極接合体を得た。
　［比較例３－１］
　触媒粒子の生成工程において、イオン液体の添加量を白金担持カーボンのメソ孔体積の６０％に相当する量に変更したこと以外は、実施例３－１と同様の材料および工程によって、比較例３－１の膜電極接合体を得た。
　［比較例３－２］
　触媒粒子の生成工程において、イオン液体の添加量を白金担持カーボンのメソ孔体積の５％に相当する量に変更したこと以外は、実施例３－１と同様の材料および工程によって、比較例３－２の膜電極接合体を得た。
　［比較例３－３］
　触媒粒子の生成工程において、無機被膜の重量比が０．２となるようにＴＥＯＳの添加量を変更したこと、および、イオン液体の添加量を白金担持カーボンのメソ孔体積の６０％に相当する量に変更したこと以外は、実施例３－１と同様の材料および工程によって、比較例３－３の膜電極接合体を得た。
　［比較例３－４］
　触媒粒子の生成工程において、無機被膜の重量比が０．２となるようにＴＥＯＳの添加量を変更したこと、および、イオン液体の添加量を白金担持カーボンのメソ孔体積の５％に相当する量に変更したこと以外は、実施例３－１と同様の材料および工程によって、比較例３－４の膜電極接合体を得た。
　［比較例３－５］
　触媒粒子の生成工程において、無機被膜の重量比が０．３となるようにＴＥＯＳの添加量を変更したこと、および、イオン液体の添加量を白金担持カーボンのメソ孔体積の３０％に相当する量に変更したこと以外は、実施例３－１と同様の材料および工程によって、比較例３－５の膜電極接合体を得た。
　［比較例３－６］
　触媒粒子の生成工程において、無機被膜の重量比が０．００５となるようにＴＥＯＳの添加量を変更したこと、および、イオン液体の添加量を白金担持カーボンのメソ孔体積の３０％に相当する量に変更したこと以外は、実施例３－１と同様の材料および工程によって、比較例３－６の膜電極接合体を得た。
　［比較例３－７］
　白金担持カーボンに対するイオン液体の含浸と無機被膜の形成を実施しなかったこと以外は、実施例３－１と同様の材料および工程によって、比較例３－７の膜電極接合体を得た。すなわち、比較例３－７の触媒粒子は、触媒担持担体のみからなり、イオン液体および無機被膜を有していない。
　［無機被膜の被覆状態の解析］
　実施例１の触媒粒子に対し、ＴＥＭ－ＥＤＳ（エネルギー分散型Ｘ線分光法）を利用した元素マッピングによって、元素の分布を解析した。図８ＡはＣの分布を示し、図８ＢはＳｉの分布を示し、図８ＣはＰｔの分布を示す。図８Ａ～図８Ｃに示されるように、Ｓｉの分布はＰｔの分布と重なりを有しており、シリカからなる無機被膜が、主として、白金である金属粒子を覆うように形成されていることが確認された。
　［発電性能の評価］
　各実施例および各比較例について、膜電極接合体の両面にガス拡散層であるカーボンペーパーを貼り合わせてサンプルを作製した。各サンプルを、発電評価セル内に設置し、燃料電池測定装置を用いて電流電圧測定を行った。測定時のセル温度は、８０℃に設定した。加湿条件は、燃料極の相対湿度を９０％ＲＨ、空気極の相対湿度を３０％ＲＨとした。また、燃料ガスとして水素を用い、酸化剤ガスとして空気を用いた。この際に、水素を水素利用率が８０％となる流量で流すとともに、空気を酸素利用率が４０％となる流量で流した。なお、背圧は５０ｋＰａとした。
　発電性能の評価では、電流密度が１．５Ａ／ｃｍ２のときの電圧が０．６５Ｖ以上である場合を「〇」とし、電流密度が１．５Ａ／ｃｍ２のときの電圧が０、６５Ｖ未満である場合を「×」とした。上記電圧が０．６５Ｖ以上であると、実用上において好ましい発電性能が得られていると言える。
　［耐久性の評価］
　各実施例および各比較例について、上述の発電性能の評価で用いたサンプルと同一のサンプルを用い、新エネルギー・産業技術総合開発機構（ＮＥＤＯ）が刊行する「セル評価解析プロトコル」に記載されている電位サイクル試験を実施した。試験前と試験後のそれぞれについて、上述した発電性能の評価と同様の条件で電流電圧測定を実施し、電流密度が１．５Ａ／ｃｍ２のときの試験前に対する試験後の電圧降下量を算出した。
　耐久性の評価では、電圧低下量が１００ｍＶ以内である場合を「〇」とし、電圧降下量が１００ｍＶを超えた場合を「×」とした。電圧降下量が１００ｍＶ以内であると、実用上において好ましい耐久性が得られ、すなわち膜電極接合体が長期使用に耐え得ると言える。
　表４に、各実施例および各比較例について、無機被膜の重量比およびイオン液体の体積割合と、発電性能および耐久性の評価結果を示す。
Figure JPOXMLDOC01-appb-T000005
　表４に示すように、無機被膜の重量比が０．０１以上０．２以下であり、かつ、イオン液体の体積割合が１０％以上５０％以下である実施例３－１～３－６では、発電性能および耐久性の双方が良好であった。
　一方、イオン液体の体積割合が１０％未満あるいは５０％を超える比較例３－１～３－４では、発電性能が低く、プロトン伝導の阻害による抵抗増加が起こっていると考えられる。また、無機被膜の重量比が０．２を超える比較例３－５でも発電性能が低く、無機被膜が多すぎることによるプロトン伝導の阻害が生じていると考えられる。また、無機被膜の重量比が０．０１未満である比較例３－６，３－７では、発電性能に加えて耐久性も低くなっており、金属粒子の溶出が生じていると考えられる。
　以上、実施例を用いて説明したように、第３実施形態の触媒粒子、電極触媒層、膜電極接合体、および、固体高分子形燃料電池によれば、以下の効果が得られる。
　（１）触媒粒子が無機被膜とイオン液体を含むことにより、高分子電解質への金属粒子の溶出が抑えられるとともに、プロトン伝導の阻害が抑えられる。したがって、触媒粒子を電極触媒層に用いた燃料電池において、良好な耐久性および発電性能が得られる。
　（２）無機被膜が、テトラエトキシシランおよびトリエトキシメチルシランのいずれかから形成されたシリカからなることにより、無機被膜が多層構造に形成されるため、無機被膜の内部にイオン液体が保持されやすくなる。
　（３）イオン液体が、１－アルキル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを含み、特に、１－エチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを含む。こうした構成によれば、イオン液体を介したプロトンの伝導が好適に可能である。
　（第４実施形態）
　電極触媒層、膜電極接合体、および、固体高分子形燃料電池の第４実施形態を説明する。第４実施形態は、第１実施形態と同様の基本構成を有する。以下では、第４実施形態と第１実施形態との相違点を中心に説明し、第１実施形態と同様の構成については同じ符号を付してその説明を省略する。なお、第４実施形態の特徴は他の実施形態の特徴と組み合わせ可能である。
　＜第４実施形態の課題＞
　白金担持カーボン触媒は耐久性に課題がある。具体的には、炭素材料に担持された白金粒子が、高分子電解質中に溶出することにより、燃料電池の性能低下を招いてしまうという課題がある。
　特許文献２（特開２００８－４５４１号公報）では、導電性担体と、導電性担体上に配接された金属粒子とを、多孔性無機材料で被覆することにより、金属粒子の溶出を防ぎ、燃料電池の性能低下を抑制することが可能な電極材料が報告されている。
　しかしながら、特許文献２に記載の電極材料では、金属粒子の溶出抑制の効果が得られるものの、多孔性無機材料が金属粒子の表面を覆うため、金属粒子とアイオノマーとの接触が削減される。その結果、抵抗が増大し、ＩＶ曲線における電圧が低下する問題があった。
　また、非特許文献１（ＩＮＴＥＲＮＡＴＩＯＮＡＬ　ＪＯＵＲＮＡＬ　ＯＦ　ＨＹＤＲＯＧＥＮ　ＥＮＥＲＧＹ，２０２０，４５，１８６７－１８７７）では、シリカで被覆された触媒を用いた膜電極接合体は、低湿（２０％ＲＨ）下で、未処理の触媒を用いた膜電極接合体に比べて優れた発電性能を示すことが報告されている。このことは、シリカによって水分が保持されるためと思われる。
　非特許文献２（ＡＣＳ　Ｃａｔａｌｙｓｉｓ，２０１８，８，８２４４－８２５４．）では、Ｐｔ粒子と水との反応を抑制するために、触媒粒子を、水との親和性が低い液体であるイオン液体で被覆することで、酸素還元活性が向上することが報告されている。
　しかしながら、高い黒鉛化度のカーボン担体を用いた触媒を、イオン液体で被覆した場合、イオン液体は安定に保持されず、耐久試験下でイオン液体が流出し、耐久試験後の発電性能は大きく低下する。
　第４実施形態は、触媒の質量活性の耐久性に優れるイオン液体含浸シリカ被覆触媒粒子、および、高温低湿でのＩＶ特性の耐久性に優れる燃料電池用膜電極接合体と燃料電池を提供することを目的とする。
　＜第４実施形態の特徴＞
　発明者は、低湿下での発電特性に優れるシリカで被覆された触媒粒子に、８０℃～１２０℃でも化学的に安定なイオン液体を含浸させることで、未処理の触媒に比べ、高温低湿下での発電特性が向上するとともに、耐久試験後も高い発電性能が得られることを見出した。
　炭素材料である導電性担体１１のラマン分光法によるＧバンドとＤバンドのピーク強度比（Ｇ／Ｄ比）は、１．６以上である。また、導電性担体１１の上記ピーク強度比（Ｇ／Ｄ比）は、１．８以上であることが好ましい。なお、ラマン分光法で用いるレーザー光の波長は５３２ｎｍである。また、Ｇバンドとは、１５８０ｃｍ－１付近に位置するラマンピークを意味し、Ｄバンドとは、１３６０ｃｍ－１付近に位置するラマンピークを意味する。
　上記ピーク強度比（Ｇ／Ｄ比）が１．６以上の炭素材料は、従来用いられてきた炭素材料に比べて高い結晶性を有しているため、触媒粒子１０の耐久性試験における導電性担体１１の酸化消失を低減することができる。その結果、触媒粒子１０の耐久性を向上させることができる。
　なお、上記ピーク強度比（Ｇ／Ｄ比）が１．６未満であると、導電性担体の比表面積が大きくなるため、導電性担体に担持可能な金属粒子の量は、ピーク強度比（Ｇ／Ｄ比）が１．６以上の場合に比べて増加するが、導電性担体の結晶性は、ピーク強度比（Ｇ／Ｄ比）が１．６以上の場合に比べて低下する。つまり、導電性担体がアモルファスカーボンとなる。その結果、触媒粒子の耐久性は、上記ピーク強度比（Ｇ／Ｄ比）が１．６以上の場合に比べて低下する。
　なお、本実施形態において、上記ピーク強度比（Ｇ／Ｄ比）は、２．２以下であり、２．０以下であることが好ましい。上記ピーク強度比（Ｇ／Ｄ比）が２．０以下であれば、導電性担体１１に十分に金属粒子１２が担持可能である。
　金属粒子１２は、Ｐｔ、Ｒｈ、Ｐｄ、Ａｕ、および、Ｉｒのうち１つ以上の元素を含んでいることが好ましい。金属粒子１２は、例えば、Ｐｔ単体、ＰｔとＣｏの合金粒子、ＰｄコアにＰｔ粒子が被覆されたコアシェル粒子等であってもよい。
　また、金属粒子１２は、ＸＲＤ法による結晶子サイズ（１，１，１）が１０ｎｍ以下のＰｔ粒子であることが好ましく、８ｎｍ以下のＰｔ粒子であることがより好ましい。ここで、上記（１，１，１）は、ミラー指数を示す。結晶子サイズ（１，１，１）が１０ｎｍ以下のＰｔ粒子であれば、触媒活性が高く、高い電圧を得ることができる。また、結晶子サイズ（１，１，１）が３ｎｍ以上７ｎｍ以下のＰｔ粒子であれば、高い触媒活性が確実に得られる。
　金属粒子１２の上記結晶子サイズ（１，１，１）の下限値は特に制限されないが、３ｎｍ以上が好ましい。結晶子サイズ（１，１，１）が３ｎｍ以上であれば、触媒活性が確実に得られる。
　なお、結晶子サイズ（１，１，１）が８ｎｍ超のＰｔ粒子であると、Ｐｔ粒子の表面積とＰｔ粒子の質量との比（Ｐｔ粒子の表面積／Ｐｔ粒子の質量）が、結晶子サイズ（１，１，１）が８ｎｍ以下のＰｔ粒子と比べて小さくなる。その結果、Ｐｔ粒子の触媒能とＰｔ粒子の質量との比（Ｐｔ粒子の触媒能／Ｐｔ粒子の質量）が、結晶子サイズ（１，１，１）が８ｎｍ以下のＰｔ粒子と比べて小さくなる。そのため、結晶子サイズ（１，１，１）が８ｎｍ超のＰｔ粒子は、結晶子サイズ（１，１，１）が８ｎｍ以下のＰｔ粒子と比べて、高いＩＶ特性を得にくくなる。
　触媒粒子１０における金属粒子１２の質量割合は、触媒担持担体１５の質量を１００質量部としたとき、６０質量部以上７０質量部以下である。金属粒子１２の質量割合が６０質量部以上であれば、単位面積当たりの金属重量に対し、電極触媒層が厚くなりすぎないため、酸素等のガスが拡散しやすくなる。金属粒子１２の質量割合が７０質量部以下であれば、結晶子サイズ（１，１，１）が８ｎｍ以下のＰｔ粒子等の微小な金属粒子を担持することが容易である。
　触媒粒子１０において、ＢＪＨ法によるメソポア領域の細孔容積は、０．１８ｃｍ３／ｇ以上であり、かつ、ＢＪＨ法による細孔分布曲線のピークトップ細孔径は、２．６ｎｍ以上２．８ｎｍ以下であることが好ましい。メソポア領域の細孔容積が０．１８ｃｍ３／ｇ以上であれば、イオン液体１４を含浸させやすくなる。また、細孔分布曲線のピークトップ細孔径が２．６ｎｍ以上であれば、イオン液体１４が導電性担体１１に含浸しやすくなる。そのため、酸素還元活性が得られやすく、十分な電圧が得られやすくなる。また、細孔分布曲線のピークトップ細孔径が２．８ｎｍ以下であれば、イオン液体１４が導電性担体１１内から流出することを抑えられる。そのため、酸素還元活性が得られやすく、十分な電圧が得られやすくなる。
　なお、メソポア領域の細孔容積とは、窒素吸着ＢＥＴ多点法による測定結果をＢＪＨ解析して、２ｎｍから１００ｎｍまでの細孔分布から得られる空孔総体積を意味する。また、ピークトップ細孔径とは、ＢＪＨ解析で得られる細孔分布曲線の２ｎｍから１００ｎｍのピークにおける細孔径を意味する。
　触媒粒子１０に含まれる無機被膜１３の量は、ＸＲＦによるＳｉ強度から検量線を用いて算出することができる。無機被膜１３の量は、導電性担体１１、金属粒子１２、イオン液体１４、および、無機被膜１３の総質量を１００質量部としたとき、６質量部以上１３質量部以下である。無機被膜１３の量が６質量部以上であれば、イオン液体１４の安定した保持が可能であり、耐久性が高められる。無機被膜１３の量が１３質量部以下であれば、金属粒子１２への酸素拡散とプロトン伝導が好適となり、触媒活性が高められる。
　イオン液体１４は、触媒粒子１０の全体に吸着されている。触媒粒子１０が含むイオン液体１４の量は、触媒担持担体１５のメソ孔体積の５０％以上１００％以下であってよい。より詳しくは、触媒粒子１０が含むイオン液体１４の体積は、触媒担持担体１５のメソ孔体積の５０％以上１００％以下であることが好ましく、７０％以上９５％以下であることがより好ましく、８５％以上９０％以下であることがさらに好ましい。
　触媒担持担体１５のメソ孔体積は、例えば、低温窒素吸着法により求めることができる。本実施形態ではメソ孔体積、すなわちメソポア領域の細孔容積として、２ｎｍから１００ｎｍまでの空孔総体積を用いた。イオン液体１４の量が触媒担持担体１５のメソ孔体積の５０％以上であれば、十分な酸素還元活性が得られやすい。また、イオン液体１４の量が触媒担持担体１５のメソ孔体積の１００％以下、好ましくは９０％以下であれば、触媒粒子１０の製造工程や調液工程、燃料電池の運転中において、イオン液体１４の安定した保持が可能である。また、イオン液体１４が多すぎないため、イオン液体１４中から金属粒子１３表面へ酸素が透過しやすくなり、抵抗の増加に起因したＩＶ性能の低下を抑えることができる。
　触媒粒子１０が含むイオン液体１４の量は、導電性担体１１、金属粒子１２、無機被膜１３、および、イオン液体１４の総質量を１００質量部としたとき、１０質量部以上２０質量部以下である。イオン液体１４の量が１０質量部以上であれば、無機被膜１３で金属粒子１２を被覆したことによるイオン抵抗の増大をイオン液体１４によって抑制する効果が的確に得られる。イオン液体１４の量が２０質量部以上であれば、触媒粒子１０の製造工程や調液工程、燃料電池の運転中において、イオン液体１４の安定した保持が可能である。また、イオン液体１４が多すぎないため、イオン液体１４中から金属粒子１３表面へ酸素が透過しやすくなり、抵抗の増加に起因したＩＶ性能の低下を抑えることができる。
　電極触媒層における繊維状物質１７の含有量は、電極触媒層の総質量を１００質量部としたとき、０．１質量部以上４５質量部以下であることが好ましく、０．１質量部以上１０質量部以下であることがより好ましく、０．１質量部以上５質量部以下であることがさらに好ましい。繊維状物質１７の含有量が上記範囲内であれば、電極触媒層における電子伝導性やプロトン伝導性が高められ、電極触媒層の構造も保持されやすい。
　電極触媒層における高分子電解質１６の総質量は、電極触媒層が含む触媒粒子１０の総質量に対して、０．１７以上０．２以下である。触媒粒子１０に対する高分子電解質１６の質量比が０．１７以上であれば、プロトン伝導性が高められるため、抵抗の増加によるＩＶ性能の低下を抑えることができる。触媒粒子１０に対する高分子電解質１６の質量比が０．２以下であれば、電極触媒層内の空隙が十分に得られることから水の排出や酸素拡散が好適に可能となり、ＩＶ性能が高められる。
　本実施形態において、触媒粒子１０に対する高分子電解質１６の質量比と、触媒粒子１０における無機被膜１３に対するイオン液体１４の質量比との積は、０．２以上０．４以下であることが好適である。これにより、高分子電解質１６と無機被膜１３とイオン液体１４とのバランスが好適となり、耐久試験後でも、電極触媒層内や金属粒子１２表面に対するプロトン伝導と酸素拡散とが円滑に行われやすい。
　なお、燃料極触媒層２２Ａおよび空気極触媒層２２Ｃの少なくとも一方が、上述した第４実施形態の特徴を有していればよい。燃料極触媒層２２Ａと空気極触媒層２２Ｃとの一方のみが第４実施形態の特徴を有する場合、空気極触媒層２２Ｃが第４実施形態の特徴を有することが好ましい。
　＜第４実施形態の実施例＞
　［Ｐｔ担持カーボンの合成］
　Ｐｔ担持カーボンは、既知の方法に従って合成される。Ｐｔ担持カーボンは、質量比でＰｔ／Ｃ＝７０／３０のＰｔ担持量を有する。カーボン担体において、ラマン分光よるＧバンド／Ｄバンド比は１．６以上である。
　［イオン液体含浸Ｐｔ担持カーボンの合成］
　合成したＰｔ担持カーボンをアセトニトリルに加え、Ｐｔ担持カーボンのメソ孔体積に対する所定量のイオン液体を添加した。この液体に対し、３０分間、超音波分散を実施した後、一晩、スターラーで撹拌後、エバポレーターでアセトニトリルを除去して、イオン液体含浸Ｐｔ担持カーボンを得た。
　［イオン液体含浸シリカ被覆Ｐｔ担持カーボンの合成］
　合成したイオン液体含浸Ｐｔ担持カーボンを水に加え、超音波撹拌後、水酸化ナトリウムを加えた。続いて、テトラエトキシシラン（ＴＥＯＳ）とエタノールとを含む混合溶液を加えた。２時間撹拌後、遠心分離機を用いて分離物を得て、分離物を８０℃で６時間乾燥させることにより、イオン液体含浸シリカ被覆Ｐｔ担持カーボンを得た。
　また、合成したイオン液体含浸シリカ被覆Ｐｔ担持カーボンに含まれるＰｔ粒子について、ＸＲＤ法で求めた結晶子サイズ（１，１，１）は、６．４ｎｍであった。
　また、合成したイオン液体含浸シリカ被覆Ｐｔ担持カーボンに含まれるシリカ量は、ＸＲＦで求めたＳｉ元素量から算出した。
　イオン液体の量は、仕込み量から計算した。
　［触媒評価］
　３電極セルを用いて、回転ディスク電極法による質量活性の測定を実施した。回転数は、２００ｒｐｍ、４００ｒｐｍ、９００ｒｐｍ、１６００ｒｐｍ、２５００ｒｐｍとした。Ｋｏｕｔｅｃｋｙ－Ｌｅｖｉｃｈプロットにて、０．８５Ｖ　vs. RHEの質量活性を求めた。
　作用極は、合成したイオン液体含浸Ｐｔ担持カーボンを水に加え、アイオノマーを添加後、３０分間超音波撹拌し、得られた触媒インクを、グラッシーカーボン電極上に滴下・乾燥させることで作製した。対極は、Ｐｔメッシュを用いた。参照極は、飽和カロメル電極を用いた。電解溶液は、０．１Ｍ　過塩素酸水溶液を用いた。
　質量活性を測定後、耐久性試験として、ＣＶを０．６Ｖ～１，２１Ｖ　vs. RHEの範囲で繰り返し１２００回実施した。耐久性試験後、再度、質量活性を測定した。
　［実施例４Ａ－１］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、６質量部となるように調整した。
　上述の評価方法に沿って、イオン液体含浸シリカ被覆Ｐｔ担持カーボンの質量活性を評価した。
　［実施例４Ａ－２］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、９質量部となるように調整した。
　上述の評価方法に沿って、イオン液体含浸シリカ被覆Ｐｔ担持カーボンの質量活性を評価した。
　［実施例４Ａ－３］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１１質量部となるように調整した。
　上述の評価方法に沿って、イオン液体含浸シリカ被覆Ｐｔ担持カーボンの質量活性を評価した。
　［実施例４Ａ－４］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１３質量部となるように調整した。
　上述の評価方法に沿って、イオン液体含浸シリカ被覆Ｐｔ担持カーボンの質量活性を評価した。
　［比較例４Ａ－１］
　上述の評価方法に沿って、白金担持カーボンの質量活性を評価した。この触媒粒子は、イオン液体を含浸しておらず、シリカによる被覆もされていない。
　［比較例４Ａ－２］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、３質量部となるように調整した。
　上述の評価方法に沿って、イオン液体含浸シリカ被覆Ｐｔ担持カーボンの質量活性を評価した。
　［比較例４Ａ－３］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。
　上述の評価方法に沿って、イオン液体含浸シリカ被覆Ｐｔ担持カーボンの質量活性を評価した。
　［実施例４Ａ－５］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１０質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１０質量部となるように調整した。
　上述の評価方法に沿って、イオン液体含浸シリカ被覆Ｐｔ担持カーボンの質量活性を評価した。
　［実施例４Ａ－６］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、２０質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１０質量部となるように調整した。
　上述の評価方法に沿って、イオン液体含浸シリカ被覆Ｐｔ担持カーボンの質量活性を評価した。
　［比較例４Ａ－４］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１０質量部となるように調整した。
　上述の評価方法に沿って、イオン液体含浸シリカ被覆Ｐｔ担持カーボンの質量活性を評価した。
　［比較例４Ａ－５］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、２５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１０質量部となるように調整した。
　上述の評価方法に沿って、イオン液体含浸シリカ被覆Ｐｔ担持カーボンの質量活性を評価した。
Figure JPOXMLDOC01-appb-T000006
　表５は、シリカ量と耐久性試験前後の質量活性との関連を示す。表６は、イオン液体量と耐久性試験前後の質量活性との関連を示す。
　表５において、シリカ量が６ｗｔ％～１３ｗｔ％である実施例４Ａ－１～４Ａ－４では、初期の質量活性がいずれも１７Ａ／ｇ－Ｐｔ以上であった。シリカ量が３ｗｔ％である比較例４Ａ－２では、初期の質量活性が１５．２Ａ／ｇ－Ｐｔであった。また、シリカ量が１５ｗｔ％である比較例４Ａ－３では、初期の質量活性が１６．８Ａ／ｇ－Ｐｔであった。シリカ量が６ｗｔ％より少ないと、アイオノマーによるＰｔ被毒抑制が不十分なため、質量活性が低下したと思われる。一方、シリカ量が１３ｗｔ％より多いと、シリカ膜による抵抗で、質量活性が低下したと思われる。耐久試験後の質量活性については、シリカ量が６ｗｔ％以上である実施例４Ａ－１～４Ａ－４と比較例４Ａ－３は、いずれも１４．５Ａ／ｇ－Ｐｔ以上を示したが、シリカ量が３ｗｔ％である比較例４Ａ－２は、１０．５Ａ／ｇ－Ｐｔと低かった。
Figure JPOXMLDOC01-appb-T000007
　表６において、実施例４Ａ－５，４Ａ－６および比較例４Ａ－４のように、イオン液体量が２０ｗｔ％以下である場合、初期の質量活性は１６Ａ／ｇ－Ｐｔ以上であったが、イオン液体量が２５ｗｔ％の比較例４Ａ－５では、初期の質量活性が１４Ａ／ｇ－Ｐｔであった。これは、イオン液体層が厚くなり、酸素拡散が不足したためと思われる。耐久試験後については、実施例４Ａ－５，４Ａ－６では、質量活性がいずれも１４Ａ／ｇ－Ｐｔ以上であったが、比較例４Ａ－４では、質量活性が大きく低下した。これは、イオン液体量が少ないと、金属粒子の酸化溶出抑制効果が不十分であるためと思われる。
　［実施例４Ｂ－７］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１０質量部となるように調整した。
　水、ＩＰＡ、および、エタノールを含む混合溶液に、イオン液体含浸シリカ被覆Ｐｔ担持カーボン、アイオノマー、および、イオン伝導性繊維状物質を加えて、触媒層用スラリーを調製した。高分子電解質膜に、白金量が０．４ｍｇ／ｃｍ２になるように、触媒層用スラリーを塗布し、塗膜を乾燥させて、空気極触媒層を得た。アイオノマーとイオン液体含浸シリカ被覆Ｐｔ担持カーボンとの質量比は０．１７とした。
　また、水、および、ＩＰＡを含む混合溶液に、Ｐｔ担持カーボン、アイオノマー、および、繊維を加えて、触媒層用スラリーを調製した。当該触媒層用スラリーを、高分子電解質膜における空気極触媒層の反対側の面に、白金量が０．１ｍｇ／ｃｍ２になるように塗布し、塗膜を乾燥させて、燃料極触媒層を作製した。これにより、膜電極接合体を得た。
　［実施例４Ｂ－８］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１０質量部となるように調整した。
　水、ＩＰＡ、および、エタノールを含む混合溶液に、イオン液体含浸シリカ被覆Ｐｔ担持カーボン、アイオノマー、および、イオン伝導性繊維状物質を加えて、触媒層用スラリーを調製した。高分子電解質膜に、白金量が０．４ｍｇ／ｃｍ２になるように、触媒層用スラリーを塗布し、塗膜を乾燥させて、空気極触媒層を得た。アイオノマーとイオン液体含浸シリカ被覆Ｐｔ担持カーボンとの質量比は０．１８とした。
　また、水、および、ＩＰＡを含む混合溶液に、Ｐｔ担持カーボン、アイオノマー、および、繊維を加えて、触媒層用スラリーを調製した。当該触媒層用スラリーを、高分子電解質膜における空気極触媒層の反対側の面に、白金量が０．１ｍｇ／ｃｍ２になるように塗布し、塗膜を乾燥させて、燃料極触媒層を作製した。これにより、膜電極接合体を得た。
　［実施例４Ｂ－９］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１０質量部となるように調整した。
　水、ＩＰＡ、および、エタノールを含む混合溶液に、イオン液体含浸シリカ被覆Ｐｔ担持カーボン、アイオノマー、および、イオン伝導性繊維状物質を加えて、触媒層用スラリーを調製した。高分子電解質膜に、白金量が０．４ｍｇ／ｃｍ２になるように、触媒層用スラリーを塗布し、塗膜を乾燥させて、空気極触媒層を得た。アイオノマーとイオン液体含浸シリカ被覆Ｐｔ担持カーボンとの質量比は０．２とした。
　また、水、および、ＩＰＡを含む混合溶液に、Ｐｔ担持カーボン、アイオノマー、および、繊維を加えて、触媒層用スラリーを調製した。当該触媒層用スラリーを、高分子電解質膜における空気極触媒層の反対側の面に、白金量が０．１ｍｇ／ｃｍ２になるように塗布し、塗膜を乾燥させて、燃料極触媒層を作製した。これにより、膜電極接合体を得た。
　［実施例４Ｂ－１０］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１３質量部となるように調整した。
　水、ＩＰＡ、および、エタノールを含む混合溶液に、イオン液体含浸シリカ被覆Ｐｔ担持カーボン、アイオノマー、および、イオン伝導性繊維状物質を加えて、触媒層用スラリーを調製した。高分子電解質膜に、白金量が０．４ｍｇ／ｃｍ２になるように、触媒層用スラリーを塗布し、塗膜を乾燥させて、空気極触媒層を得た。アイオノマーとイオン液体含浸シリカ被覆Ｐｔ担持カーボンとの質量比は０．２とした。
　また、水、および、ＩＰＡを含む混合溶液に、Ｐｔ担持カーボン、アイオノマー、および、繊維を加えて、触媒層用スラリーを調製した。当該触媒層用スラリーを、高分子電解質膜における空気極触媒層の反対側の面に、白金量が０．１ｍｇ／ｃｍ２になるように塗布し、塗膜を乾燥させて、燃料極触媒層を作製した。これにより、膜電極接合体を得た。
　［実施例４Ｂ－１１］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１０質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、７質量部となるように調整した。
　水、ＩＰＡ、および、エタノールを含む混合溶液に、イオン液体含浸シリカ被覆Ｐｔ担持カーボン、アイオノマー、および、イオン伝導性繊維状物質を加えて、触媒層用スラリーを調製した。高分子電解質膜に、白金量が０．４ｍｇ／ｃｍ２になるように、触媒層用スラリーを塗布し、塗膜を乾燥させて、空気極触媒層を得た。アイオノマーとイオン液体含浸シリカ被覆Ｐｔ担持カーボンとの質量比は０．２とした。
　また、水、および、ＩＰＡを含む混合溶液に、Ｐｔ担持カーボン、アイオノマー、および、繊維を加えて、触媒層用スラリーを調製した。当該触媒層用スラリーを、高分子電解質膜における空気極触媒層の反対側の面に、白金量が０．１ｍｇ／ｃｍ２になるように塗布し、塗膜を乾燥させて、燃料極触媒層を作製した。これにより、膜電極接合体を得た。
　［比較例４Ｂ－６］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１０質量部となるように調整した。
　水、ＩＰＡ、および、エタノールを含む混合溶液に、イオン液体含浸シリカ被覆Ｐｔ担持カーボン、アイオノマー、および、イオン伝導性繊維状物質を加えて、触媒層用スラリーを調製した。高分子電解質膜に、白金量が０．４ｍｇ／ｃｍ２になるように、触媒層用スラリーを塗布し、塗膜を乾燥させて、空気極触媒層を得た。アイオノマーとイオン液体含浸シリカ被覆Ｐｔ担持カーボンとの質量比は０．１５とした。
　また、水、および、ＩＰＡを含む混合溶液に、Ｐｔ担持カーボン、アイオノマー、および、繊維を加えて、触媒層用スラリーを調製した。当該触媒層用スラリーを、高分子電解質膜における空気極触媒層の反対側の面に、白金量が０．１ｍｇ／ｃｍ２になるように塗布し、塗膜を乾燥させて、燃料極触媒層を作製した。これにより、膜電極接合体を得た。
　［比較例４Ｂ－７］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１０質量部となるように調整した。
　水、ＩＰＡ、および、エタノールを含む混合溶液に、イオン液体含浸シリカ被覆Ｐｔ担持カーボン、アイオノマー、および、イオン伝導性繊維状物質を加えて、触媒層用スラリーを調製した。高分子電解質膜に、白金量が０．４ｍｇ／ｃｍ２になるように、触媒層用スラリーを塗布し、塗膜を乾燥させて、空気極触媒層を得た。アイオノマーとイオン液体含浸シリカ被覆Ｐｔ担持カーボンとの質量比は０．３とした。
　また、水、および、ＩＰＡを含む混合溶液に、Ｐｔ担持カーボン、アイオノマー、および、繊維を加えて、触媒層用スラリーを調製した。当該触媒層用スラリーを、高分子電解質膜における空気極触媒層の反対側の面に、白金量が０．１ｍｇ／ｃｍ２になるように塗布し、塗膜を乾燥させて、燃料極触媒層を作製した。これにより、膜電極接合体を得た。
　［実施例４Ｂ－１２］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１０質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１３質量部となるように調整した。
　水、ＩＰＡ、および、エタノールを含む混合溶液に、イオン液体含浸シリカ被覆Ｐｔ担持カーボン、アイオノマー、および、イオン伝導性繊維状物質を加えて、触媒層用スラリーを調製した。高分子電解質膜に、白金量が０．４ｍｇ／ｃｍ２になるように、触媒層用スラリーを塗布し、塗膜を乾燥させて、空気極触媒層を得た。アイオノマーとイオン液体含浸シリカ被覆Ｐｔ担持カーボンとの質量比は０．１７とした。
　また、水、および、ＩＰＡを含む混合溶液に、Ｐｔ担持カーボン、アイオノマー、および、繊維を加えて、触媒層用スラリーを調製した。当該触媒層用スラリーを、高分子電解質膜における空気極触媒層の反対側の面に、白金量が０．１ｍｇ／ｃｍ２になるように塗布し、塗膜を乾燥させて、燃料極触媒層を作製した。これにより、膜電極接合体を得た。
　［実施例４Ｂ－１３］
　上述の合成方法に沿って、イオン液体として、１－ブチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを用いたイオン液体含浸シリカ被覆Ｐｔ担持カーボンを合成した。イオン液体の含浸量は、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、１５質量部となるように調整した。シリカ量は、ＴＥＯＳ量を調整し、導電性担体、金属粒子、イオン液体、および、シリカの合計質量を１００質量部として、７質量部となるように調整した。
　水、ＩＰＡ、および、エタノールを含む混合溶液に、イオン液体含浸シリカ被覆Ｐｔ担持カーボン、アイオノマー、および、イオン伝導性繊維状物質を加えて、触媒層用スラリーを調製した。高分子電解質膜に、白金量が０．４ｍｇ／ｃｍ２になるように、触媒層用スラリーを塗布し、塗膜を乾燥させて、空気極触媒層を得た。アイオノマーとイオン液体含浸シリカ被覆Ｐｔ担持カーボンとの質量比は０．２とした。
　また、水、および、ＩＰＡを含む混合溶液に、Ｐｔ担持カーボン、アイオノマー、および、繊維を加えて、触媒層用スラリーを調製した。当該触媒層用スラリーを、高分子電解質膜における空気極触媒層の反対側の面に、白金量が０．１ｍｇ／ｃｍ２になるように塗布し、塗膜を乾燥させて、燃料極触媒層を作製した。これにより、膜電極接合体を得た。
　［発電性能の評価］
　ＪＡＲＩ標準セルに、作製した膜電極接合体とガスケット、ＧＤＬ（Ｇａｓ　Ｄｉｆｆｕｓｉｏｎ　Ｌａｙｅｒ）をそれぞれ組み込み、ＮＥＤＯの固体高分子形燃料電池実用化推進技術開発基盤技術開発「セル評価解析の共通基盤技術」に記載の発電条件にて、ＩＶ特性を評価した。高温・低湿条件とするため、セル温度は９０℃、空気極の湿度は２０％ＲＨとした。
　耐久性試験として、国立研究開発法人新エネルギー・産業技術総合開発機構（ＮＥＤＯ）の固体高分子形燃料電池実用化推進技術開発基盤技術開発「セル評価解析の共通基盤技術」に記載の起動停止１００００サイクル、負荷応答３００００サイクルを実施した。
　耐久性試験後に、再度ＩＶ特性を評価した。
Figure JPOXMLDOC01-appb-T000008
　表７に、耐久性試験前後のＩ－Ｖ測定の結果における１．５Ａ／ｃｍ２時の電圧を示す。実施例４Ｂ－７～４Ｂ－９および比較例４Ｂ－６，４Ｂ－７は、空気極触媒層におけるアイオノマー量の検討のためのデータである。これらの実施例および比較例では、アイオノマーとイオン液体含浸シリカ被覆触媒粒子との質量比が０．１７以上０．２０以下の範囲であるときに、初期の電圧が０．６４０Ｖ以上、耐久後の電圧が０．５００Ｖ以上を示した。アイオノマーが少ないと、抵抗過電圧が高くなり、アイオノマーが多いと濃度過電圧が高くなってしまうためと思われる。
Figure JPOXMLDOC01-appb-T000009
　表８に、耐久性試験前後のＩ－Ｖ測定の結果における１．５Ａ／ｃｍ２時の電圧を示す。実施例４Ｂ－１０～４Ｂ－１３は、イオン液体含浸シリカ被覆触媒粒子を含んだ電極触媒層におけるアイオノマー量と、イオン液体量、シリカ量の組み合わせについて検討したデータである。
　触媒粒子の総質量に対するアイオノマーの総質量の比と、シリカの総質量に対するイオン液体の総質量の比との積が、０．２以上０．４以下である場合、初期の電圧が０．６６０Ｖ以上、耐久後の電圧が０．５６０Ｖ以上を示した。これにより、抵抗過電圧および濃度過電圧が、アイオノマー量、イオン液体量、シリカ量の組み合わせの影響を受けることが確認された。
　以上のように、第４実施形態の触媒粒子および電極触媒層は、以下の効果を奏する。
　（１）導電性担体は、ラマン分光法によるＧバンドとＤバンドのピーク強度比（Ｇ／Ｄ比）が、１．６以上２．２以下の炭素材料を含む。触媒粒子が含む触媒担持担体の質量を１００質量部としたとき、触媒粒子が含む金属粒子の総質量は、６０質量部以上７０質量部以下である。触媒粒子の質量を１００質量部としたとき、触媒粒子が含む無機被膜の総質量は６質量部以上１３質量部以下である。触媒粒子の質量を１００質量部としたとき、触媒粒子が含むイオン液体の総質量は、１０質量部以上２０質量部以下である。
　このような構成であれば、金属粒子に対する無機被膜の被覆が適切であるため、耐久性試験における金属粒子の溶出を抑制できることから、耐久性が上がるとともに、イオン液体の含浸によって、金属粒子表面へのプロトン伝導性を確保することができる。さらに、シリカからなる無機被膜によって、イオン液体の金属粒子表面への吸着を抑制することができる。
　より詳しくは、金属粒子の少なくとも一部を無機被膜で被覆し、無機被膜で被覆した金属粒子へのプロトン移動を、イオン液体を介して行うことができるので、低湿・高温下での高い発電性能が得られるとともに、無機被膜によってイオン液体が安定に保持されて、耐久性に優れた電極触媒層、膜電極接合体、および、燃料電池が得られる。
　（２）電極触媒層が含む触媒粒子の総質量に対する高分子電解質の総質量の比が、０．１７以上０．２以下である。このような構成であれば、触媒粒子における金属粒子へのプロトン伝導と酸素拡散が十分に確保されやすい。
　（３）電極触媒層が含む触媒粒子の総質量に対する高分子電解質の総質量の比と、触媒粒子が含む無機被膜の総質量に対するイオン液体の総質量の比との積が、０．２以上０．４以下である。
　このような構成であれば、プロトン伝導と酸素拡散、イオン液体の安定保持の観点から、触媒粒子の金属粒子上に位置するイオン液体層と無機被膜、アイオノマー量のバランスが最適となり、耐久後のＩＶ性能の低下を抑制できる。

Claims (13)

  1. 　触媒粒子、高分子電解質、および、繊維状物質を含む電極触媒層であって、
    　前記触媒粒子は、金属粒子と導電性担体とイオン液体とを含み、
    　前記電極触媒層は、１０００ｍｇ／ｃｍ３以上１６００ｍｇ／ｃｍ３以下の密度を有する
    　電極触媒層。
  2. 　前記金属粒子は、前記導電性担体に担持されており、
    　前記イオン液体は、前記金属粒子の表面および前記導電性担体の表面に接し、
    　前記触媒粒子はさらに、前記イオン液体を介して前記金属粒子および前記導電性担体を被覆する無機被膜を含み、
    　前記無機被膜はケイ素を含み、
    　エネルギー分散型Ｘ線分光法により得られる、前記電極触媒層の炭素、窒素、酸素、フッ素、ケイ素、硫黄、および、白金元素の合計原子数に占めるケイ素の原子数の割合が、０．５ａｔ％以上１０ａｔ％以下である
    　請求項１に記載の電極触媒層。
  3. 　前記金属粒子は前記導電性担体に担持されており、複数の前記金属粒子とこれらの金属粒子を担持した前記導電性担体とから触媒担持担体が構成され、
    　前記イオン液体は、前記触媒担持担体の表面を含む部分に位置し、
    　前記触媒粒子はさらに、前記触媒担持担体の一部を被覆する無機被膜を含み、
    　前記複数の金属粒子には、表面の一部が前記無機被膜から露出して前記イオン液体と接している前記金属粒子が含まれ、
    　前記触媒担持担体および前記無機被膜の合計重量に対する前記無機被膜の重量比が、０．０１以上０．２以下であり、
    　前記触媒担持担体のメソ孔体積に対する前記イオン液体の体積割合が、１０％以上５０％以下である
    　請求項１に記載の電極触媒層。
  4. 　前記金属粒子は前記導電性担体に担持されており、複数の前記金属粒子とこれらの金属粒子を担持した前記導電性担体とから触媒担持担体が構成され、
    　前記イオン液体は、前記金属粒子の表面の少なくとも一部に接し、
    　前記触媒粒子はさらに、前記金属粒子の表面の一部を被覆する無機被膜を含み、
    　前記導電性担体は、ラマン分光法によるＧバンドとＤバンドのピーク強度比（Ｇ／Ｄ比）が、１．６以上２．２以下の炭素材料を含み、
    　前記触媒粒子が含む前記触媒担持担体の質量を１００質量部としたとき、前記触媒粒子が含む前記金属粒子の総質量は、６０質量部以上７０質量部以下であり、
    　前記触媒粒子の質量を１００質量部としたとき、前記触媒粒子が含む前記無機被膜の総質量は６質量部以上１３質量部以下であり、
    　前記触媒粒子の質量を１００質量部としたとき、前記触媒粒子が含む前記イオン液体の総質量は、１０質量部以上２０質量部以下である
    　請求項１に記載の電極触媒層。
  5. 　前記電極触媒層が含む前記触媒粒子の総質量に対する前記高分子電解質の総質量の比は、０．１７以上０．２以下である
    　請求項４に記載の電極触媒層。
  6. 　前記電極触媒層が含む前記触媒粒子の総質量に対する前記高分子電解質の総質量の比と、前記触媒粒子が含む前記無機被膜の総質量に対する前記イオン液体の総質量の比との積は、０．２以上０．４以下である
    　請求項５に記載の電極触媒層。
  7. 　前記無機被膜は、テトラエトキシシランおよびトリエトキシメチルシランのいずれかから形成されたシリカからなる
    　請求項２～６のいずれか一項に記載の電極触媒層。
  8. 　前記イオン液体は、１－アルキル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを含む
    　請求項１～７のいずれか一項に記載の電極触媒層。
  9. 　前記イオン液体は、１－エチル－３－メチルイミダゾリウム　ビス（トリフロオロメタンスルホニル）イミドを含む
    　請求項８に記載の電極触媒層。
  10. 　前記繊維状物質は、電子伝導性およびプロトン伝導性の少なくとも一方を有する
    　請求項１～９のいずれか一項に記載の電極触媒層。
  11. 　前記繊維状物質は、アゾール構造を有する材料を含む
    　請求項１～１０のいずれか一項に記載の電極触媒層。
  12. 　高分子電解質膜と、
    　前記高分子電解質膜を挟む一対の電極触媒層と、を備え、
    　前記一対の電極触媒層の少なくとも一方が、請求項１～１１のいずれか一項に記載の電極触媒層である
    　膜電極接合体。
  13. 　請求項１２に記載の膜電極接合体と、
    　前記膜電極接合体を挟む一対のセパレータと、
    　を備える固体高分子形燃料電池。
PCT/JP2023/025471 2022-07-22 2023-07-10 電極触媒層、膜電極接合体、および、固体高分子形燃料電池 WO2024018944A1 (ja)