WO2023199544A1 - 複合活物質粒子、電池、および複合活物質粒子の製造方法 - Google Patents

複合活物質粒子、電池、および複合活物質粒子の製造方法 Download PDF

Info

Publication number
WO2023199544A1
WO2023199544A1 PCT/JP2022/041393 JP2022041393W WO2023199544A1 WO 2023199544 A1 WO2023199544 A1 WO 2023199544A1 JP 2022041393 W JP2022041393 W JP 2022041393W WO 2023199544 A1 WO2023199544 A1 WO 2023199544A1
Authority
WO
WIPO (PCT)
Prior art keywords
active material
solid electrolyte
composite active
negative electrode
particles
Prior art date
Application number
PCT/JP2022/041393
Other languages
English (en)
French (fr)
Inventor
邦彦 峯谷
忠朗 松村
Original Assignee
パナソニックＩｐマネジメント株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by パナソニックＩｐマネジメント株式会社 filed Critical パナソニックＩｐマネジメント株式会社
Publication of WO2023199544A1 publication Critical patent/WO2023199544A1/ja

Abstract

本開示の複合活物質粒子は、酸化物を含む酸化物相と、活物質を含み、前記酸化物相に分散して存在する複数の活物質ドメインと、前記酸化物と異なる組成を有する第１固体電解質と、を備え、前記第１固体電解質は、前記酸化物相および前記複数の活物質ドメインによって構成された母体粒子の表面の少なくとも一部を被覆している。

Description

複合活物質粒子、電池、および複合活物質粒子の製造方法
　本開示は、複合活物質粒子、電池、および複合活物質粒子の製造方法に関する。
　パソコン、ビデオカメラ、携帯電話などの電気製品の急速な普及に伴い、電源としての電池の開発が重要視されている。また、自動車産業界では、電気自動車又はハイブリッド自動車用に高出力かつ高容量のリチウム電池の開発が進められている。高容量のリチウム電池の負極活物質として、リチウムと合金化する合金系材料が期待されている。合金系材料の代表例はシリコンである。
　特許文献１には、リチウムシリケート相とリチウムシリケート相中に分散したシリコン粒子とを備えた負極活物質が記載されている。
特許第６７８６４７４号公報
　従来技術においては、複合活物質粒子を用いた電池の充電効率の低下を抑制するための技術が望まれる。
　本開示は、
　酸化物を含む酸化物相と、
　活物質を含み、前記酸化物相に分散して存在する複数の活物質ドメインと、
　前記酸化物と異なる組成を有する第１固体電解質と、
　を備え、
　前記第１固体電解質は、前記酸化物相および前記複数の活物質ドメインによって構成された母体粒子の表面の少なくとも一部を被覆している、
　複合活物質粒子を提供する。
　本開示によれば、複合活物質粒子を用いた電池の充電効率の低下を抑制するための技術を提供できる。
図１は、実施の形態１における複合活物質粒子の概略構成を示す断面図である。 図２は、実施の形態１における複合活物質粒子の製造方法で用いられる母体粒子の概略構成を示す断面図である。 図３は、実施の形態１における複合活物質粒子の製造方法の一例を示すフローチャートである。 図４は、実施の形態２における電池の概略構成を示す断面図である。 図５は、負極および負極活物質層の詳細な構成を示す断面図である。
　（本開示の基礎となった知見）
　特許文献１は、充放電に伴うシリコン粒子の膨張および収縮をリチウムシリケート相が吸収することによって、電池のサイクル特性が向上することを開示している。
　特許文献１に記載されるような、リチウムシリケート相中にシリコン粒子を分散させた負極活物質では、多くのシリコン粒子が負極活物質の外表面に露出した状態で存在している。多くのシリコン粒子が負極活物質の外表面に露出していると、負極活物質と固体電解質との間の界面接触が悪化しやすい。すなわち、電池の充放電に伴い負極活物質の外表面に露出したシリコン粒子が膨張および収縮し、負極活物質と固体電解質との乖離が生じることがある。負極活物質と固体電解質との乖離は、特に、シリコン粒子の膨張速度の大きいハイレート充電時に生じやすい。負極活物質と固体電解質とが乖離すると、電池の充電効率が低下する。
　本開示は、上記実情に鑑みてなされたものであり、複合活物質粒子を用いた電池の充電効率の低下を抑制するための技術を提供する。
　（本開示に係る一態様の概要）
　本開示の第１態様に係る複合活物質粒子は、
　酸化物を含む酸化物相と、
　活物質を含み、前記酸化物相に分散して存在する複数の活物質ドメインと、
　前記酸化物と異なる組成を有する第１固体電解質と、
　を備え、
　前記第１固体電解質は、前記酸化物相および前記複数の活物質ドメインによって構成された母体粒子の表面の少なくとも一部を被覆している。
　本開示の複合活物質粒子によれば、電池の充電効率の低下を抑制できる。
　本開示の第２態様において、例えば、第１態様に係る複合活物質粒子では、前記第１固体電解質は、ガーネット型の結晶構造を有していてもよい。ガーネット型の結晶構造を有する固体電解質は、高いリチウムイオン伝導度を有するとともに、負極における還元雰囲気下でも電気的に安定している。
　本開示の第３態様において、例えば、第１または第２態様に係る複合活物質粒子では、前記第１固体電解質は、Ｌｉ7Ｌａ3Ｚｒ2Ｏ12、Ｌｉ7-3xＬａ3Ｚｒ2ＡｌxＯ12（０≦ｘ＜０．３）、Ｌｉ7-yＬａ3Ｚｒ2-yＮｂyＯ12（０≦ｙ＜０．３）、およびＬｉ7-zＬａ3Ｚｒ2-zＴａzＯ12（０≦ｚ＜０．５）からなる群より選ばれる少なくとも１つを含んでいてもよい。このような第１固体電解質は、高いリチウムイオン伝導度を有するとともに、負極における還元雰囲気下でも電気的に安定している。
　本開示の第４態様において、例えば、第１から第３態様のいずれか１つに係る複合活物質粒子では、前記活物質は、リチウムと合金を形成する材料を含んでいてもよい。本開示の複合活物質粒子は、活物質がリチウムと合金を形成する材料を含む場合に特に有用である。
　本開示の第５態様において、例えば、第１から第４態様のいずれか１つに係る複合活物質粒子では、前記活物質は、単体のシリコンおよびＳｉＯa（０＜ａ＜２）からなる群より選ばれる少なくとも１つを含んでいてもよい。本開示の複合活物質粒子は、活物質粒子が単体のシリコンおよびＳｉＯa（０＜ａ＜２）からなる群より選ばれる少なくとも１つを含む場合に特に有用である。
　本開示の第６態様において、例えば、第１から第５態様のいずれか１つに係る複合活物質粒子では、前記酸化物相は、非晶質であってもよい。本開示の複合活物質粒子は、酸化物相が非晶質である場合に特に有用である。
　本開示の第７態様において、例えば、第１から第６態様のいずれか１つに係る複合活物質粒子では、前記酸化物相は、リチウムシリケートを含んでいてもよい。本開示の複合活物質粒子は、酸化物相がリチウムシリケートを含む場合に特に有用である。
　本開示の第８態様において、例えば、第７態様に係る複合活物質粒子では、前記リチウムシリケートは、Ｌｉ2bＳｉＯ(2+b)（０＜ｂ≦２）で表される組成を有していてもよい。以上の構成によれば、活物質の膨張および収縮が有意に吸収されうる。
　本開示の第９態様に係る電池は、
　正極と、
　負極と、
　前記正極と前記負極との間に位置する電解質層と、
　を備え、
　前記負極は、第１から第８態様のいずれか１つの複合活物質粒子を含む。
　本開示の電池によれば、電池の充電効率の低下を抑制できる。
　本開示の第１０態様において、例えば、第９態様に係る電池では、前記負極は、前記酸化物および前記第１固体電解質と異なる組成を有する第２固体電解質をさらに含んでいてもよい。本開示の複合活物質粒子は、負極が固体電解質を含む場合に特に有用である。
　本開示の第１１態様において、例えば、第１０態様に係る電池では、前記第２固体電解質は、硫化物固体電解質を含んでいてもよい。以上の構成によれば、電池の充電効率を向上させることができる。
　本開示の第１２態様において、例えば、第８から第１１態様のいずれか１つに係る電池では、前記電解質層は、第３固体電解質を含んでいてもよい。以上の構成によれば、電池の充電効率を向上させることができる。
　本開示の第１３態様に係る複合活物質粒子の製造方法は、
　活物質を含む複数の活物質ドメインが酸化物相に分散された構造を有する母体粒子の表面の少なくとも一部を第１固体電解質で被覆することを含む。
　本開示の複合活物質粒子の製造方法によれば、電池の充電効率の低下の抑制に適した構造を有する複合活物質粒子を製造できる。
　本開示の第１４態様において、例えば、第１３態様に係る複合活物質粒子の製造方法では、固相法によって、前記母体粒子の前記表面の少なくとも一部を前記第１固体電解質で被覆してもよい。以上の構成によれば、より簡易に電池の充電効率の低下の抑制に適した構造を有する複合活物質粒子を製造できる。
　以下、本開示の実施の形態が、図面を参照しながら説明される。
　（実施の形態１）
　図１は、実施の形態１における複合活物質粒子３０の概略構成を示す断面図である。複合活物質粒子３０は、酸化物相３１、複数の活物質ドメイン３２、および第１固体電解質３３を備える。酸化物相３１は、酸化物を含む。活物質ドメイン３２は、活物質を含む。第１固体電解質３３は、酸化物相３１に含まれる酸化物とは異なる組成を有する。複数の活物質ドメイン３２は、酸化物相３１に分散して存在している。第１固体電解質３３は、酸化物相３１および複数の活物質ドメイン３２によって構成された母体粒子２０の表面２０Ｓの少なくとも一部を被覆している。
　本実施の形態の複合活物質粒子３０では、複数の活物質ドメイン３２が酸化物相３１に分散して存在しており、かつ、第１固体電解質３３が酸化物相３１および複数の活物質ドメイン３２によって構成された母体粒子２０の表面２０Ｓの少なくとも一部を被覆している。したがって、複合活物質粒子３０では、第１固体電解質３３によって、複合活物質粒子３０の外表面３０Ｓに露出した状態で存在する活物質の量が抑制されている。そのため、電池の充放電に伴って活物質が膨張および収縮しても、負極活物質層において複合活物質粒子３０と後述する第２固体電解質との乖離が抑制され、界面接触が良好に維持される。その結果、電池の充電効率の低下が抑制される。
　第１固体電解質３３は、酸化物固体電解質を含んでいてもよい。酸化物固体電解質は、２５℃環境下において約１０-4Ｓｃｍ-1という高いリチウムイオン伝導度を有するとともに、負極における還元雰囲気下でも電気的に安定している。第１固体電解質３３は、酸化物固体電解質であってもよい。
　酸化物固体電解質としては、例えば、ＬｉＴｉ2（ＰＯ4）3およびその元素置換体を代表とするＮＡＳＩＣＯＮ型固体電解質、（ＬａＬｉ）ＴｉＯ3系のペロブスカイト型固体電解質、Ｌｉ14ＺｎＧｅ4Ｏ16、Ｌｉ4ＳｉＯ4、ＬｉＧｅＯ4およびその元素置換体を代表とするＬＩＳＩＣＯＮ型固体電解質、Ｌｉ7Ｌａ3Ｚｒ2Ｏ12およびその元素置換体を代表とするガーネット型固体電解質、Ｌｉ3ＮおよびそのＨ置換体、Ｌｉ3ＰＯ4およびそのＮ置換体、ＬｉＢＯ2、Ｌｉ3ＢＯ3などのＬｉ－Ｂ－Ｏ化合物を含むベース材料にＬｉ2ＳＯ4、Ｌｉ2ＣＯ3などの材料が添加されたガラスまたはガラスセラミックスなどが用いられうる。
　第１固体電解質３３は、ガーネット型の結晶構造を有していてもよい。すなわち、第１固体電解質３３は、ガーネット型固体電解質であってもよい。第１固体電解質３３は、立方晶系に属するガーネット型固体電解質であってもよい。ガーネット型の結晶構造を有する固体電解質は、高いリチウムイオン伝導度を有するとともに、負極における還元雰囲気下でも電気的に安定している。なかでも立方晶系に属するガーネット型固体電解質は、高いリチウムイオン伝導度を有する。
　ガーネット型の結晶構造を有する固体電解質として、例えば、Ｌｉ7Ｌａ3Ｚｒ2Ｏ12、Ｌｉ7-3xＬａ3Ｚｒ2ＡｌxＯ12（０≦ｘ＜０．３）、Ｌｉ7-yＬａ3Ｚｒ2-yＮｂyＯ12（０≦ｙ＜０．３）、およびＬｉ7-zＬａ3Ｚｒ2-zＴａzＯ12（０≦ｚ＜０．５）が挙げられる。第１固体電解質３３は、これらから選ばれる少なくとも１つを含んでいてもよい。第１固体電解質３３は、Ｌｉ7-3xＬａ3Ｚｒ2ＡｌxＯ12（０≦ｘ＜０．３）であってもよい。このような第１固体電解質３３は、２５℃環境下において１０-4Ｓｃｍ-1という高いリチウムイオン伝導度を有するとともに、負極における還元雰囲気下でも電気的に安定している。
　第１固体電解質３３は、硫化物固体電解質を含んでいてもよい。硫化物固体電解質は、２５℃環境下において１０-4Ｓｃｍ-1という高いリチウムイオン伝導度を有するとともに、負極における還元雰囲気下でも電気的に安定している。第１固体電解質３３は、硫化物固体電解質であってもよい。
　硫化物固体電解質としては、Ｌｉ2Ｓ－Ｐ2Ｓ5、Ｌｉ2Ｓ－ＳｉＳ2、Ｌｉ2Ｓ－Ｂ2Ｓ3、Ｌｉ2Ｓ－ＧｅＳ2、Ｌｉ3.25Ｇｅ0.25Ｐ0.75Ｓ4、Ｌｉ10ＧｅＰ2Ｓ12などが用いられうる。これらに、ＬｉＸ、Ｌｉ2Ｏ、ＭＯq、ＬｉpＭＯqなどが添加されてもよい。ここで、「ＬｉＸ」における元素Ｘは、Ｆ、Ｃｌ、Ｂｒ、およびＩからなる群より選ばれる少なくとも１つである。「ＭＯq」および「ＬｉpＭＯq」における元素Ｍは、Ｐ、Ｓｉ、Ｇｅ、Ｂ、Ａｌ、Ｇａ、Ｉｎ、Ｆｅ、およびＺｎからなる群より選ばれる少なくとも１つである。「ＭＯq」および「ＬｉpＭＯq」におけるｐおよびｑは、それぞれ独立な自然数である。
　母体粒子２０は、一次粒子であってもよく、二次粒子であってもよい。酸化物相３１は、明確な粒界を持たない連続した相であってもよい。
　第１固体電解質３３は、母体粒子２０の表面２０Ｓを一様に被覆していてもよい。すなわち、第１固体電解質３３によって複合活物質粒子３０の外表面３０Ｓが形成されていてもよい。以上の構成によれば、第１固体電解質３３によって、複合活物質粒子３０の外表面３０Ｓに露出した状態で存在する活物質の量が更に減らされる。そのため、電池の充放電に伴って活物質が膨張および収縮しても、負極活物質層において複合活物質粒子３０と後述する第２固体電解質との乖離がより抑制され、界面接触がより良好に維持される。
　第１固体電解質３３は、母体粒子２０の表面２０Ｓの一部のみを被覆していてもよい。すなわち、第１固体電解質３３によって複合活物質粒子３０の外表面３０Ｓの一部が形成されていてもよい。
　母体粒子２０の表面２０Ｓの少なくとも一部を被覆する第１固体電解質３３の厚さは均一であってもよく、均一でなくてもよい。
　第１固体電解質３３の平均厚さは、１０ｎｍ以上５００ｎｍ以下であってもよい。以上の構成によれば、負極全体に対する固体電解質の総量を適度に保つことができる。これにより、負極の重量エネルギー密度の低下を抑制しうる。
　第１固体電解質３３の平均厚さは、例えば、以下の方法によって求められうる。具体的には、まず、複合活物質粒子３０を加工し、断面を露出させる。複合活物質粒子３０の加工は、例えば、クロスセクションポリッシャ（登録商標）を用いて行うことができる。クロスセクションポリッシャによれば、複合活物質粒子３０について、平滑な断面を形成することができる。次に、複合活物質粒子３０の断面を走査型電子顕微鏡（ＳＥＭ）または透過型電子顕微鏡（ＴＥＭ）で観察する。これにより、複合活物質粒子３０の断面のＳＥＭ像またはＴＥＭ像が得られる。次に、得られたＳＥＭ像またはＴＥＭ像から、母体粒子２０および第１固体電解質３３を特定する。これらの特定は、画像のコントラストに基づいて行ってもよく、エネルギー分散型Ｘ線分析（ＥＤＳ）などの元素分析の結果に基づいて行ってもよい。次に、ＳＥＭ像またはＴＥＭ像から、任意に選択した１０点における第１固体電解質３３の厚さを計測する。これらの計測値を平均することにより第１固体電解質３３の平均厚さを求めることができる。
　母体粒子２０において、複数の活物質ドメイン３２に含まれる活物質の質量Ｍ１に対する酸化物相３１の質量Ｍ２の比率（Ｍ２／Ｍ１＝シリケート/シリコン）は、０．５≦Ｍ２／Ｍ１≦１を満たしてもよい。比率（Ｍ２／Ｍ１）を適切に調整することによって、活物質の膨張および収縮を酸化物相３１で有意に吸収することができる。
　複合活物質粒子３０の質量Ｍ３に対する第１固体電解質３３の質量Ｍ４の比率（Ｍ４／Ｍ３）は、０．１≦Ｍ４／Ｍ３≦０．３を満たしてもよい。比率（Ｍ４／Ｍ３）を適切に調整することによって、第１固体電解質３３により活物質の膨張および収縮を有意に抑制することができる。
　複合活物質粒子３０の断面を観察したとき、母体粒子２０の占める面積は第１固体電解質３３の占める面積よりも大きくてもよい。例えば、酸化物相３１がリチウムシリケート相である場合、リチウムシリケート相に含まれるリチウムシリケートは電子伝導性を有していない。しかし、母体粒子２０の占める面積が第１固体電解質３３の占める面積よりも大きければ、母体粒子２０に含まれる活物質により、十分な電子伝導性を確保できる。
　活物質ドメイン３２は、金属イオンを吸蔵かつ放出する特性を有する活物質を含む。活物質ドメイン３２に含まれる活物質は、リチウムと合金を形成する材料を含んでいてもよい。このような材料としては、リチウムと合金を形成する単体金属、リチウムと合金を形成する金属を含む化合物などが挙げられる。単体金属としては、シリコン、スズ、ゲルマニウム、ビスマスなどが挙げられる。リチウムと合金を形成する金属を含む化合物としては、酸化物、炭化物、窒化物、珪化物、硫化物、燐化物等が挙げられる。
　活物質ドメイン３２は、活物質として、単体のシリコンおよびＳｉＯa（０＜ａ＜２）からなる群より選ばれる少なくとも１つを含んでいてもよい。本実施の形態の複合活物質粒子３０は、活物質が単体のシリコンおよびＳｉＯa（０＜ａ＜２）からなる群より選ばれる少なくとも１つを含む場合に特に有用である。活物質は、単体のシリコンであってもよい。
　活物質ドメイン３２は、単体のシリコンでできた粒子であってもよい。この場合、シリコン粒子におけるシリコンの純度は特に限定されず、例えば、９９％（２Ｎ）以上である。シリコン粒子は、単結晶シリコン粒子であってもよく、多結晶シリコン粒子であってもよい。
　活物質ドメイン３２の大きさは特に限定されない。活物質ドメイン３２は、ナノオーダーの大きさを有していてもよい。活物質ドメイン３２の平均粒径は、例えば、０．０１μｍ以上３μｍ以下である。活物質ドメイン３２の平均粒径は、例えば、次の方法によって算出することができる。例えば、複合活物質粒子３０の断面を電子顕微鏡（ＳＥＭまたはＴＥＭ）で観察し、ＳＥＭ像またはＴＥＭ像における特定の活物質ドメイン３２の面積を画像処理にて算出する。算出された面積に等しい面積を有する円の直径をその特定の活物質の直径とみなす。任意の個数（例えば１０個）の活物質ドメイン３２の直径を算出し、それらの平均値を活物質ドメイン３２の平均粒径とみなす。
　活物質ドメイン３２には、粒子とは言い難い形状を有する活物質がドメインとして存在していてもよい。図１では、活物質ドメイン３２が概ね一定の大きさを有する。しかし、例えば、いくつかの活物質粒子が合体して比較的大きい活物質ドメイン３２が形成されていてもよい。場合によって、活物質ドメイン３２と酸化物相３１とがまだら模様を呈していてもよい。活物質ドメイン３２の形状も特に限定されない。活物質ドメイン３２は、例えば、球状、楕円球、鱗片状などの形状を有する。
　酸化物相３１は、単体のシリコンおよびＳｉＯa（０＜ａ＜２）を含んでいなくてもよい。本実施の形態の複合活物質粒子３０は、酸化物相３１が単体のシリコンおよびＳｉＯa（０＜ａ＜２）を含まない場合に特に有用である。
　酸化物相３１は、非晶質であってもよい。本開示において、「非晶質」とは、結晶化度が実質的に０％（具体的には、０．１％未満）であることを指し、Ｘ線回析スペクトラムにおいて、非晶質ハローのみが認められ、結晶質ピークが認められないことをいう。
　酸化物相３１は、リチウムシリケートを含んでいてもよい。本実施の形態の複合活物質粒子３０は、酸化物相３１がリチウムシリケートを含む場合に特に有用である。リチウムシリケートはリチウムイオン伝導性を有し、かつ、電池の充電時に膨張しないためである。酸化物相３１は、リチウムシリケート相であってもよい。
　リチウムシリケートは、Ｌｉ2bＳｉＯ(2+b)（０＜ｂ≦２）で表される組成を有しうる。酸化物相３１がリチウムシリケート相である場合、リチウムシリケート相である酸化物相３１に複数の活物質ドメイン３２が内包されている。このような組成を有するリチウムシリケートによって、活物質ドメイン３２の膨張および収縮が有意に吸収されうる。結晶性のリチウムシリケートの具体的な組成としては、Ｌｉ4ＳｉＯ4（ｂ＝２）、Ｌｉ2ＳｉＯ3（ｂ＝１）、およびＬｉ2Ｓｉ2Ｏ5（ｂ＝１／２）が挙げられる。リチウムシリケート相は、単一の組成のリチウムシリケートを含んでいてもよく、複数の組成のリチウムシリケートを含んでいてもよい。リチウムシリケートは、非晶質であってもよい。非晶質のリチウムシリケートにおいては、複数の組成のリチウムシリケートが複合化することによって、上記した「ｂ」が１／２、１および２以外の値をとりうる。
　リチウムシリケートとして、例えば、Ｌｉ4ＳｉＯ4、Ｌｉ2ＳｉＯ3、およびＬｉ2Ｓｉ2Ｏ5が挙げられる。リチウムシリケートは、Ｌｉ4ＳｉＯ4、Ｌｉ2ＳｉＯ3、およびＬｉ2Ｓｉ2Ｏ5からなる群より選ばれる少なくとも１つを含んでいてもよい。リチウムシリケートは、Ｌｉ2ＳｉＯ3を含んでいてもよい。リチウムシリケートは、Ｌｉ2ＳｉＯ3であってもよい。
　複合活物質粒子３０は、例えば、０．１μｍ以上３０μｍ以下の範囲に平均粒径を有する。複合活物質粒子３０の平均粒径も、活物質ドメイン３２の平均粒径の測定方法と同じ方法によって測定されうる。複合活物質粒子３０の平均粒径が適切に調整されていると、負極において、複合活物質粒子３０と後述する第２固体電解質とが良好な分散状態を形成できる。これにより、電池の充放電特性が向上する。また、複合活物質粒子３０内のリチウム拡散が速くなる。このため、電池が高出力で動作しうる。
　複合活物質粒子３０の質量に対する活物質ドメイン３２の質量の比率は、例えば、３０％以上７０％以下である。
　複合活物質粒子３０の製造方法について、説明する。
　複合活物質粒子３０の製造方法は、活物質を含む複数の活物質ドメイン３２が酸化物相３１に分散された構造を有する母体粒子２０の表面２０Ｓの少なくとも一部を第１固体電解質３３で被覆することを含む。
　図３は、複合活物質粒子３０の製造方法の一例を示すフローチャートである。複合活物質粒子３０は、フローチャートに示す各工程により製造されてもよい。
　最初に、活物質を含む複数の活物質ドメイン３２が酸化物相３１に分散された構造を有する母体粒子２０を準備する（工程Ｓ１）。図２は、母体粒子２０の概略構成を示す断面図である。例えば、活物質ドメイン３２の材料としてシリコン粒子を用い、酸化物相３１の材料としてリチウムシリケートを用いる。この場合、工程Ｓ１は以下のように行われる。まず、シリコン粉末およびリチウムシリケート粉末を準備する。これらを所定の比率で混合して原料粉末を得る。メカニルアロイングのような方法によって原料粉末を処理する。これにより、母体粒子２０が得られる。所定の目開きのメッシュ又は篩を使用して母体粒子２０を処理することで、所望の平均粒径を持つ母体粒子２０の粉末が得られる。
　次に、母体粒子２０の表面２０Ｓの少なくとも一部を第１固体電解質３３で被覆する（工程Ｓ２）。工程Ｓ２では、まず、第１固体電解質３３の粉末を準備する。母体粒子２０の表面２０Ｓの少なくとも一部を第１固体電解質３３で被覆する方法は、特に限定されない。液相法、気相法、または固相法のいずれの方法で被覆してもよい。取り扱いが容易であることから、固相法が好適に用いられる。固相法としては、例えば、固相反応法が挙げられる。液相法としては、共沈法、ゾルゲル法、水熱反応法などが挙げられる。気相法としては、スパッタリング法、ＣＶＤ法などが挙げられる。
　（実施の形態２）
　図４は、実施の形態２における電池１００の概略構成を示す断面図である。電池１００は、正極２２０、負極２１０、および電解質層１３を備える。電解質層１３は、正極２２０と負極２１０との間に位置する。
　正極２２０は、正極活物質層１７および正極集電体１８を有する。正極活物質層１７は、電解質層１３と正極集電体１８との間に配置されている。正極活物質層１７は、正極集電体１８に電気的に接触している。
　正極集電体１８は、正極活物質層１７から電力を集める機能を有する部材である。正極集電体１８の材料としては、アルミニウム、アルミニウム合金、ステンレス、銅、ニッケルなどが挙げられる。正極集電体１８は、アルミニウムまたはアルミニウム合金で作られていてもよい。正極集電体１８の寸法、形状などは、電池１００の用途に応じて適宜選択されうる。
　正極活物質層１７は、正極活物質と固体電解質とを含む。正極活物質としては、リチウムイオンなどの金属イオンを吸蔵かつ放出する特性を有する材料が用いられうる。正極活物質としては、リチウム含有遷移金属酸化物、遷移金属フッ化物、ポリアニオン材料、フッ素化ポリアニオン材料、遷移金属硫化物、遷移金属オキシ硫化物、遷移金属オキシ窒化物などが用いられうる。リチウム含有遷移金属酸化物の例は、Ｌｉ（Ｎｉ，Ｃｏ，Ａｌ）Ｏ2、Ｌｉ（Ｎｉ，Ｃｏ，Ｍｎ）Ｏ2、およびＬｉＣｏＯ2である。特に、正極活物質として、リチウム含有遷移金属酸化物を用いた場合には、製造コストを安くでき、平均放電電圧を高めることができる。
　本開示において、化学式中の表記「（Ａ，Ｂ，Ｃ）」は、「Ａ、Ｂ、およびＣからなる群より選ばれる少なくとも１つ」を意味する。例えば、「（Ｎｉ，Ｃｏ，Ａｌ）」は、「Ｎｉ、ＣｏおよびＡｌからなる群より選ばれる少なくとも１つ」と同義である。他の元素の場合でも同様である。
　正極活物質は、例えば、粒子の形状を有する。正極活物質の粒子の形状は特に限定されない。正極活物質の粒子の形状は、針状、球状、楕円球状または鱗片状でありうる。
　正極活物質の粒子のメジアン径は、０．１μｍ以上かつ１００μｍ以下であってもよい。正極活物質の粒子のメジアン径が０．１μｍ以上の場合、正極２２０において、正極活物質と固体電解質とが、良好な分散状態を形成しうる。この結果、電池１００の充放電特性が向上する。正極活物質の粒子のメジアン径が１００μｍ以下の場合、正極活物質の粒子内のリチウム拡散が速くなる。このため、電池１００が高出力で動作しうる。
　正極２２０の固体電解質としては、硫化物固体電解質、酸化物固体電解質、ハロゲン化物固体電解質、高分子固体電解質および錯体水素化物固体電解質からなる群より選ばれる少なくとも１つを用いてもよい。酸化物固体電解質は、優れた高電位安定性を有する。酸化物固体電解質を用いることで、電池１００の充電効率をより向上させることができる。
　正極２２０において、正極活物質と固体電解質との体積比率「ｖ１：１００－ｖ１」について、３０≦ｖ１≦９５が満たされてもよい。３０≦ｖ１が満たされる場合、電池１００のエネルギー密度が十分に確保される。また、ｖ１≦９５が満たされる場合、電池１００の高出力での動作が可能となる。
　正極２２０の厚みは、１０μｍ以上かつ５００μｍ以下であってもよい。正極２２０の厚みが１０μｍ以上である場合、電池１００のエネルギー密度が十分に確保される。正極２２０の厚みが５００μｍ以下である場合、電池１００の高出力での動作が可能となる。
　正極２２０に含まれた固体電解質の形状は、特に限定されない。固体電解質の形状は、例えば、針状、球状、楕円球状などであってもよい。例えば、固体電解質の形状は、粒子状であってもよい。
　正極２２０に含まれた固体電解質の形状が粒子状（例えば、球状）の場合、固体電解質の粒子のメジアン径は、１００μｍ以下であってもよい。メジアン径が１００μｍ以下の場合、正極活物質と固体電解質とが、正極２２０において良好な分散状態を形成しうる。このため、電池１００の充放電特性が向上する。
　本明細書において、「メジアン径」は、体積基準の粒度分布における累積体積が５０％に等しい場合の粒径を意味する。体積基準の粒度分布は、例えば、レーザー回折式測定装置または画像解析装置により測定される。
　正極活物質層１７は、電子伝導性を高める目的で、導電助剤を含んでいてもよい。導電助剤としては、例えば、天然黒鉛または人造黒鉛のグラファイト類、アセチレンブラック、ケッチェンブラックなどのカーボンブラック類、炭素繊維または金属繊維などの導電性繊維類、フッ化カーボン、アルミニウムなどの金属粉末類、酸化亜鉛またはチタン酸カリウムなどの導電性ウィスカー類、酸化チタンなどの導電性金属酸化物、ポリアニリン、ポリピロール、ポリチオフェンなどの導電性高分子化合物などが用いられうる。炭素導電助剤を用いた場合、低コスト化を図ることができる。
　電解質層１３は、正極２２０と負極２１０との間に位置している。電解質層１３は、電解質を含む層である。電解質は、例えば、リチウムイオン伝導性を有する固体電解質である。電解質層１３は、固体電解質層でありうる。以下、電解質層１３に含まれる固体電解質を第３固体電解質と称する。
　電解質層１３は、第３固体電解質として、ハロゲン化物固体電解質、硫化物固体電解質、酸化物固体電解質、高分子固体電解質および錯体水素化物固体電解質からなる群より選ばれる少なくとも１つを含んでいてもよい。
　電解質層１３は、多層構造を有していてもよい。この場合、負極２１０に接する層の材料の組成は、正極２２０に接する層の材料の組成と異なっていてもよい。負極２１０に接する層は、還元耐性に優れた硫化物固体電解質で作られていてもよい。正極２２０に接する層は、酸化耐性に優れるハロゲン化物固体電解質で作られていてもよい。
　電解質層１３に含まれた第３固体電解質の形状は、特に限定されない。第３固体電解質の形状は、例えば、針状、球状、楕円球状などであってもよい。例えば、第３固体電解質の形状は、粒子状であってもよい。
　電解質層１３に含まれた第３固体電解質の形状が粒子状（例えば、球状）の場合、第３固体電解質の粒子のメジアン径は、１００μｍ以下であってもよい。メジアン径が１００μｍ以下の場合、第３固体電解質が、電解質層１３において良好な分散状態を形成しうる。このため、電池１００の充放電特性が向上する。
　電解質層１３の厚みは、１μｍ以上かつ３００μｍ以下であってもよい。電解質層１３の厚みが１μｍ以上の場合には、正極２２０と負極２１０との間の短絡を確実に防止できる。電解質層１３の厚みが３００μｍ以下の場合には、電池１００が高出力での動作を実現しうる。
　負極２１０は、負極活物質層１１および負極集電体１２を備える。負極活物質層１１は、電解質層１３と負極集電体１２との間に配置されている。負極活物質層１１は、負極集電体１２に電気的に接触している。
　負極集電体１２は、負極活物質層１１から電力を集める機能を有する部材である。負極集電体１２の材料としては、アルミニウム、アルミニウム合金、ステンレス、銅、ニッケルなどが挙げられる。負極集電体１２は、ニッケルで作られていてもよい。負極集電体１２の寸法、形状などは、電池１００の用途に応じて適宜選択されうる。
　図５は、負極２１０および負極活物質層１１の詳細な構成を示す断面図である。負極活物質層１１は、負極活物質としての実施の形態１の複合活物質粒子３０を含む。
　負極活物質層１１は、第２固体電解質４０をさらに含んでいてもよい。第２固体電解質４０は、実施の形態１の複合活物質粒子３０における酸化物相３１に含まれる酸化物および第１固体電解質３３と異なる組成を有していてもよい。第２固体電解質４０は、硫化物固体電解質、酸化物固体電解質、ハロゲン化物固体電解質、高分子固体電解質および錯体水素化物固体電解質からなる群より選ばれる少なくとも１つが使用されうる。第２固体電解質４０は、硫化物固体電解質であってもよい。
　負極活物質層１１が第２固体電解質４０を含む場合、言い換えると、電池１００が固体電池である場合、複合活物質粒子３０の活物質ドメイン３２に含まれる活物質がシリコン粒子であると、シリコン粒子の膨張および収縮のスペースが限られる。そのため、充電効率の観点から、シリコン粒子を負極活物質層１１に直接分散させて使用することは容易ではない。したがって、実施の形態１の複合活物質粒子３０は、負極活物質層１１が第２固体電解質４０を含む場合に特に有用である。
　硫化物固体電解質として、実施の形態１の第１固体電解質３３で挙げた硫化物固体電解質を用いることができる。
　酸化物固体電解質として、実施の形態１の第１固体電解質３３で挙げた酸化物固体電解質を用いることができる。
　高分子固体電解質としては、例えば、高分子化合物と、リチウム塩との化合物が用いられうる。高分子化合物はエチレンオキシド構造を有していてもよい。エチレンオキシド構造を有することで、高分子化合物はリチウム塩を多く含有することができるので、イオン導電率をより高めることができる。リチウム塩としては、ＬｉＰＦ6、ＬｉＢＦ4、ＬｉＳｂＦ6、ＬｉＡｓＦ6、ＬｉＳＯ3ＣＦ3、ＬｉＮ（ＳＯ2ＣＦ3）2、ＬｉＮ（ＳＯ2Ｃ2Ｆ5）2、ＬｉＮ（ＳＯ2ＣＦ3）（ＳＯ2Ｃ4Ｆ9）、ＬｉＣ（ＳＯ2ＣＦ3）3などが使用されうる。リチウム塩として、これらから選ばれる１つのリチウム塩が単独で使用されてもよいし、これらから選ばれる２つ以上のリチウム塩の混合物が使用されてもよい。
　錯体水素化物固体電解質としては、例えば、ＬｉＢＨ4－ＬｉＩ、ＬｉＢＨ4－Ｐ2Ｓ5などが用いられうる。
　ハロゲン化物固体電解質は、例えば、下記の組成式（１）により表される。組成式（１）において、α、β、およびγは、それぞれ独立して、０より大きい値である。Ｍは、Ｌｉ以外の金属元素および半金属元素からなる群より選ばれる少なくとも１つを含む。Ｘは、Ｆ、Ｃｌ、Ｂｒ、およびＩからなる群より選ばれる少なくとも１つを含む。
　ＬｉαＭβＸγ・・・式（１）
　半金属元素は、Ｂ、Ｓｉ、Ｇｅ、Ａｓ、Ｓｂ、およびＴｅを含む。金属元素は、水素を除く周期表１族から１２族に含まれる全ての元素、ならびに、Ｂ、Ｓｉ、Ｇｅ、Ａｓ、Ｓｂ、Ｔｅ、Ｃ、Ｎ、Ｐ、Ｏ、Ｓ、およびＳｅを除く１３族から１６族に含まれる全ての元素を含む。金属元素は、ハロゲン化合物と無機化合物を形成した際にカチオンとなりうる元素群である。
　ハロゲン化物固体電解質として、Ｌｉ3ＹＸ6、Ｌｉ2ＭｇＸ4、Ｌｉ2ＦｅＸ4、Ｌｉ（Ａｌ，Ｇａ，Ｉｎ）Ｘ4、Ｌｉ3（Ａｌ，Ｇａ，Ｉｎ）Ｘ6などが用いられうる。ハロゲン化物固体電解質は、優れたイオン伝導性を示す。
　上記した各固体電解質は、負極２１０だけでなく、上述の正極２２０の固体電解質および電解質層１３の第３固体電解質にも使用可能である。
　負極２１０における複合活物質粒子３０と第２固体電解質４０との体積比率が「ｖ２：１００－ｖ２」で表されるとき、複合活物質粒子３０の体積比率ｖ２は、３０≦ｖ２≦９５を満たしてもよい。３０≦ｖ２が満たされる場合、電池１００のエネルギー密度が十分に確保される。また、ｖ２≦９５が満たされる場合、電池１００の高出力での動作が可能となる。
　負極２１０に含まれた第２固体電解質４０の形状は、特に限定されない。第２固体電解質４０の形状は、例えば、針状、球状、楕円球状などであってもよい。例えば、第２固体電解質４０の形状は、粒子状であってもよい。
　負極２１０に含まれた第２固体電解質４０の形状が粒子状（例えば、球状）の場合、第２固体電解質４０の粒子のメジアン径は、１００μｍ以下であってもよい。メジアン径が１００μｍ以下の場合、複合活物質粒子３０と第２固体電解質４０が、負極２１０において良好な分散状態を形成しうる。このため、電池１００の充放電特性が向上する。
　第２固体電解質４０の粒子のメジアン径は、複合活物質粒子３０のメジアン径よりも小さくてもよい。これにより、複合活物質粒子３０と第２固体電解質４０とが良好な分散状態を形成できる。
　負極２１０の厚みは、１０μｍ以上かつ５００μｍ以下であってもよい。負極２１０の厚みが１０μｍ以上である場合、電池１００のエネルギー密度が十分に確保される。負極２１０の厚みが５００μｍ以下である場合、電池１００の高出力での動作が可能となる。
　負極活物質層１１は、電子伝導性を高める目的で、導電助剤５０を含んでもよい。導電助剤５０としては、正極活物質層１７に含まれていてもよい導電助剤５０として列挙した材料を使用することができる。
　正極活物質層１７、電解質層１３、および負極活物質層１１からなる群より選ばれる少なくとも１つには、リチウムイオンの授受を容易にし、かつ、電池１００の出力特性を向上する目的で、硫化物固体電解質、酸化物固体電解質、高分子固体電解質、および錯体水素化物固体電解質からなる群より選ばれる少なくとも１つが含まれてもよい。硫化物固体電解質、酸化物固体電解質、ハロゲン化物固体電解質、高分子固体電解質、および錯体水素化物固体電解質としては、負極２１０の第２固体電解質４０として挙げた硫化物固体電解質、酸化物固体電解質、ハロゲン化物固体電解質、高分子固体電解質、および錯体水素化物固体電解質を用いることができる。
　正極活物質層１７、電解質層１３、および負極活物質層１１からなる群より選ばれる少なくとも１つには、リチウムイオンの授受を容易にし、電池の出力特性を向上する目的で、非水電解液、ゲル電解質、またはイオン液体が含まれていてもよい。
　非水電解液は、非水溶媒と非水溶媒に溶けたリチウム塩とを含む。非水溶媒としては、環状炭酸エステル溶媒、鎖状炭酸エステル溶媒、環状エーテル溶媒、鎖状エーテル溶媒、環状エステル溶媒、鎖状エステル溶媒、フッ素溶媒などが挙げられる。環状炭酸エステル溶媒としては、エチレンカーボネート、プロピレンカーボネート、ブチレンカーボネートなどが挙げられる。鎖状炭酸エステル溶媒としては、ジメチルカーボネート、エチルメチルカーボネート、ジエチルカーボネートなどが挙げられる。環状エーテル溶媒としては、テトラヒドロフラン、１，４－ジオキサン、１，３－ジオキソランなどが挙げられる。鎖状エーテル溶媒としては、１，２－ジメトキシエタン、１，２－ジエトキシエタンなどが挙げられる。環状エステル溶媒としては、γ－ブチロラクトンなどが挙げられる。鎖状エステル溶媒としては、酢酸メチルなどが挙げられる。フッ素溶媒としては、フルオロエチレンカーボネート、フルオロプロピオン酸メチル、フルオロベンゼン、フルオロエチルメチルカーボネート、フルオロジメチレンカーボネートなどが挙げられる。非水溶媒として、これらから選ばれる１つの非水溶媒が単独で使用されてもよいし、これらから選ばれる２つ以上の非水溶媒の混合物が使用されてもよい。非水電解液には、フルオロエチレンカーボネート、フルオロプロピオン酸メチル、フルオロベンゼン、フルオロエチルメチルカーボネート、およびフルオロジメチレンカーボネートからなる群より選ばれる少なくとも１つのフッ素溶媒が含まれていてもよい。
　リチウム塩としては、ＬｉＰＦ6、ＬｉＢＦ4、ＬｉＳｂＦ6、ＬｉＡｓＦ6、ＬｉＳＯ3ＣＦ3、ＬｉＮ（ＳＯ2ＣＦ3）2、ＬｉＮ（ＳＯ2Ｃ2Ｆ5）2、ＬｉＮ（ＳＯ2ＣＦ3）（ＳＯ2Ｃ4Ｆ9）、ＬｉＣ（ＳＯ2ＣＦ3）3などが挙げられる。リチウム塩として、これらから選ばれる１つのリチウム塩が単独で使用されてもよく、これらから選ばれる２つ以上のリチウム塩の混合物が使用されてもよい。リチウム塩の濃度は、例えば、０．５から２ｍｏｌ／リットルの範囲にある。
　ゲル電解質は、ポリマー材料に非水電解液を含ませたものを用いることができる。ポリマー材料として、ポリエチレンオキシド、ポリアクリルニトリル、ポリフッ化ビニリデン、ポリメチルメタクリレート、およびエチレンオキシド結合を有するポリマーからなる群より選ばれる少なくとも１つが使用されてもよい。
　イオン液体を構成するカチオンは、テトラアルキルアンモニウム、テトラアルキルホスホニウムなどの脂肪族鎖状４級塩類、ピロリジニウム類、モルホリニウム類、イミダゾリニウム類、テトラヒドロピリミジニウム類、ピペラジニウム類、ピペリジニウム類などの脂肪族環状アンモニウム、ピリジニウム類、イミダゾリウム類などの含窒ヘテロ環芳香族カチオンなどであってもよい。イオン液体を構成するアニオンは、ＰＦ6 -、ＢＦ4 -、ＳｂＦ6 -、ＡｓＦ6 -、ＳＯ3ＣＦ3 -、Ｎ（ＳＯ2ＣＦ3）2 -、Ｎ（ＳＯ2Ｃ2Ｆ5）2 -、Ｎ（ＳＯ2ＣＦ3）（ＳＯ2Ｃ4Ｆ9）-、Ｃ（ＳＯ2ＣＦ3）3 -などであってもよい。イオン液体はリチウム塩を含有してもよい。
　正極活物質層１７、電解質層１３、および負極活物質層１１からなる群より選ばれる少なくとも１つには、粒子同士の密着性を向上させる目的で、結着剤が含まれてもよい。結着剤は、電極を構成する材料の結着性を向上させるために、用いられる。結着剤としては、ポリフッ化ビニリデン、ポリテトラフルオロエチレン、ポリエチレン、ポリプロピレン、アラミド樹脂、ポリアミド、ポリイミド、ポリアミドイミド、ポリアクリルニトリル、ポリアクリル酸、ポリアクリル酸メチルエステル、ポリアクリル酸エチルエステル、ポリアクリル酸ヘキシルエステル、ポリメタクリル酸、ポリメタクリル酸メチルエステル、ポリメタクリル酸エチルエステル、ポリメタクリル酸ヘキシルエステル、ポリ酢酸ビニル、ポリビニルピロリドン、ポリエーテル、ポリエーテルサルフォン、ヘキサフルオロポリプロピレン、スチレンブタジエンゴム、カルボキシメチルセルロースなどが挙げられる。また、結着剤としては、テトラフルオロエチレン、ヘキサフルオロエチレン、ヘキサフルオロプロピレン、パーフルオロアルキルビニルエーテル、フッ化ビニリデン、クロロトリフルオロエチレン、エチレン、プロピレン、ペンタフルオロプロピレン、フルオロメチルビニルエーテル、アクリル酸、ヘキサジエンより選ばれる２つ以上の材料の共重合体が用いられうる。また、これらから選ばれた２つ以上が混合されて、結着剤として用いられてもよい。
　複合活物質粒子３０を用いた電池１００は、例えば、下記の方法によって製造されうる。
　セラミックス製の型に固体電解質の粉末を投入する。固体電解質の粉末を加圧して電解質層１３を形成する。電解質層１３の一方の側に、負極材料の粉末を投入する。負極材料の粉末を加圧して電解質層１３の上に負極活物質層１１を形成する。負極材料は、複数の複合活物質粒子３０および第２固体電解質４０を含んでいる。負極材料は、導電助剤５０を含んでいてもよい。電解質層１３のもう一方の側に、正極材料の粉末を投入する。正極材料の粉末を加圧して正極活物質層１７を形成する。これにより、負極活物質層１１、電解質層１３、および正極活物質層１７を備える発電要素が得られる。
　発電要素の上下に負極集電体１２および正極集電体１８をそれぞれ配置し、負極集電体１２および正極集電体１８にそれぞれ集電リードを付設する。これにより、電池１００が得られる。
　複合活物質粒子３０を用いた電池１００は、湿式法によっても製造されうる。湿式法では、例えば、複数の複合活物質粒子３０および第２固体電解質４０を含む負極スラリーを集電体に塗布して塗膜を形成する。次に、１２０℃以上の温度に加熱したロールまたは平板プレスに塗膜を通して加圧する。これにより、負極２１０が得られる。同様の方法により電解質層１３および正極２２０を作製する。次に、負極２１０、電解質層１３、および正極２２０をこの順に積層する。これにより、電池１００が得られる。
　本実施の形態における電池１００は、コイン型、円筒型、角型、シート型、ボタン型、扁平型、積層型などの種々の形状の電池として構成されうる。
　なお、本発明は上記実施の形態に限定されるものではない。上記実施形態は、例示であり、本発明の特許請求の範囲に記載された技術的思想と同一な構成を有し、同様な作用効果を奏するものは、いかなるものであっても本発明の技術的範囲に包含される。
　以下、実施例および比較例を用いて、本開示の詳細が説明される。
　［硫化物固体電解質の作製］
　露点－６０℃以下のＡｒ雰囲気のグローブボックス内で、Ｌｉ2ＳとＰ2Ｓ5とをモル比でＬｉ2Ｓ：Ｐ2Ｓ5＝７５：２５となるように秤量した。これらを乳鉢で粉砕して混合して混合物を得た。その後、遊星型ボールミル（フリッチェ社製、Ｐ－７型）を用い、１０時間、５１０ｒｐｍの条件で混合物をミリング処理することで、ガラス状の固体電解質を得た。ガラス状の固体電解質を、不活性雰囲気中、２７０度、２時間の条件で熱処理した。これにより、ガラスセラミックス状の硫化物固体電解質であるＬｉ2Ｓ－Ｐ2Ｓ5粉末を得た。以下、Ｌｉ2Ｓ－Ｐ2Ｓ5粉末を単に「ＬＰＳ」と称することがある。
　《実施例１》
　［複合活物質粒子の作製］
　活物質として、Ｓｉ粉末（３Ｎ、２．５μｍ粉砕品）を準備した。酸化物として、Ｌｉ2ＳｉＯ3粉末（２Ｎ、１０μｍ粉砕品）を準備した。Ｓｉ粉末とＬｉ2ＳｉＯ3粉末とを質量比でＳｉ粉末：Ｌｉ2ＳｉＯ3粉末＝１：１となるように秤量した。これらを露点－６０℃以下のＡｒ雰囲気のグローブボックス内で混合して第１混合粉末を得た。遊星ボールミル（フリッチェ社製、Ｐ－７型）のポッド（ＳＵＳ製、容積４５ｍＬ）に第１混合粉末を充填した。ポッドにＳＵＳ製ボール（直径５ｍｍ）を６０ｇ入れて蓋を閉め、６００ｒｐｍ、４８時間の条件で第１混合粉末を粉砕処理した。その後、処理粉末を目開き４５μｍのメッシュに通して粗大粒子を除去した。さらに、目開きの小さい篩を用いて細かい粒子を除去し、粉末の平均粒径を概ね２０μｍに調整した。これにより、母体粒子を得た。
　第１固体電解質として、ガーネット型固体電解質であるＬｉ6.25Ｌａ3Ｚｒ2Ａｌ0.25Ｏ12粉末（豊島製作所製、３Ｎ）を準備した。以下、Ｌｉ6.25Ｌａ3Ｚｒ2Ａｌ0.25Ｏ12粉末を単に「ＬＬＺＡｌ」と称することがある。最終的な複合活物質粒子の質量に対するＬＬＺＡｌ粉末の質量の比率が１０％となるように母体粒子に対してＬＬＺＡｌ粉末を追加して第２混合粉末を得た。遊星ボールミル（フリッチェ社製、Ｐ－７型）のポッド（ＳＵＳ製、容積４５ｍＬ）に第２混合粉末を充填した。ポッドにジルコニア製ボール（直径５ｍｍ）を４０ｇ入れて蓋を閉め、４００ｒｐｍ、８時間の条件で処理し、母体粒子を被覆した。これにより、実施例１の複合活物質粒子を得た。
　実施例１の複合活物質粒子は、図１を参照して説明した構造を有していた。
　（第１固体電解質の平均厚さの測定）
　上述した方法により測定した実施例１の複合活物質粒子における第１固体電解質の平均厚さは、１０ｎｍであった。
　［負極材料の作製］
　第２固体電解質としてＬＰＳを用いた。露点－６０℃以下のＡｒ雰囲気のグローブボックス内で、実施例１の複合活物質粒子とＬＰＳとを１００：２８．６の質量比で混合して混合物を得た。混合物において、母体粒子、第１固体電解質（ＬＬＺＡｌ）、および第２固体電解質（ＬＰＳ）の質量の合計と、第１固体電解質および第２固体電解質の質量の合計との比率は、７：３であった。第１固体電解質および第２固体電解質に対して１０質量％のＶＧＣＦ－Ｈ（昭和電工社製）を加えて混合した。これにより、実施例１の負極材料を得た。「ＶＧＣＦ」は、昭和電工社の登録商標である。
　［正極材料の作製］
　露点－６０℃以下のＡｒ雰囲気のグローブボックス内で、Ｌｉ（Ｎｉ0.33Ｃｏ0.33Ｍｎ0.33）Ｏ2とＬＰＳとを７：３の質量比で混合した。これにより、正極材料を得た。正極材料は、実施例および比較例に共通である。
　［二次電池の作製］
　まず、絶縁性外筒の中に４ｍｇのＬＰＳおよび１０ｍｇの負極材料を入れ、これらを３６０ＭＰａの圧力で加圧成型することで、負極活物質層と電解質層との積層体を得た。
　次に、負極活物質層の上に銅箔（厚み１２μｍ）を積層させた。これらを３６０ＭＰａの圧力で加圧成型することで、実施例１の負極を得た。
　実施例１の負極は、図５を参照して説明した構造を有していた。
　次に、電解質層の上に１００ｍｇの正極材料を積層させ、これらを３６０ＭＰａの圧力で加圧成型することで、負極、電解質層、および正極活物質層を含む積層体を得た。
　次に、正極活物質層の上にアルミ箔を積層した。これらを３６０ＭＰａの圧力で加圧成型することで、正極、電解質層、および負極からなる積層体を得た。
　次に、積層体の上下にステンレス鋼集電体を配置し、集電体に集電リードを取り付けた。
　最後に、絶縁性フェルールを用いて絶縁性外筒を密閉し、絶縁性外筒の内部を外気雰囲気から遮断することで、実施例１の電池を作製した。
　《実施例２》
　［複合活物質粒子の作製］
　母体粒子として実施例１の母体粒子を用いた。第１固体電解質としてＬＰＳを用いた。母粒子の質量に対するＬＳＰ粉末の質量の比率が１０％となるように母体粒子に対してＬＰＳ粉末を追加して混合粉末を得た。遊星ボールミル（フリッチェ社製、Ｐ－７型）のポッド（ＳＵＳ製、容積４５ｍＬ）に混合粉末を充填した。ポッドにジルコニア製ボール（直径５ｍｍ）を４０ｇ入れて蓋を閉め、４００ｒｐｍ、８時間の条件で処理し、母体粒子を被覆した。これにより、実施例２の複合活物質粒子を得た。
　実施例２の複合活物質粒子は、図１を参照して説明した構造を有していた。
　（第１固体電解質の平均厚さの測定）
　上述した方法により測定した実施例２の複合活物質粒子における第１固体電解質の平均厚さは、１０ｎｍであった。
　［負極材料の作製］
　実施例１の複合活物質粒子に代えて実施例２の複合活物質粒子を使用したことを除き、実施例１と同じ方法で実施例２の負極材料を作製した。
　［二次電池の作製］
　実施例１の負極材料に代えて実施例２の負極材料を使用したことを除き、実施例１と同じ方法で実施例２の電池を作製した。
　《比較例１》
　［複合活物質粒子の作製］
　活物質および酸化物として、実施例１と同じものを用いた。Ｓｉ粉末とＬｉ2ＳｉＯ3粉末とを質量比でＳｉ粉末：Ｌｉ2ＳｉＯ3粉末＝１：１となるように秤量した。これらを露点－６０℃以下のＡｒ雰囲気のグローブボックス内で混合して混合粉末を得た。遊星ボールミル（フリッチェ社製、Ｐ－７型）のポッド（ＳＵＳ製、容積４５ｍＬ）に混合粉末を充填した。ポッドにＳＵＳ製ボール（直径５ｍｍ）を６０ｇ入れて蓋を閉め、６００ｒｐｍ、４８時間の条件で混合粉末を粉砕処理した。その後、処理粉末を目開き４５μｍのメッシュに通して粗大粒子を除去した。さらに、目開きの小さい篩を用いて細かい粒子を除去し、粉末の平均粒径を概ね２０μｍに調整した。これにより、比較例１の複合活物質粒子を得た。すなわち、比較例１の複合活物質粒子は、第１固体電解質（ＬＬＺＡｌ）により被覆されていなかった。
　［負極材料の作製］
　露点－６０℃以下のＡｒ雰囲気のグローブボックス内で、比較例１の複合活物質粒子とＬＰＳとを７：３の質量比で混合して混合物を得た。混合物に対して１０質量％のＶＧＣＦ－Ｈ（昭和電工社製）を加えて混合した。これにより、比較例１の負極材料を得た。
　［二次電池の作製］
　実施例１の負極材料に代えて比較例１の負極材料を使用したことを除き、実施例１と同じ方法で比較例１の電池を作製した。
　（充放電試験）
　実施例および比較例の電池を用いて、以下の条件で、充放電試験が実施された。なお、実施例および比較例の電池の理論容量は、互いに同一であった。
　電池を２５℃の恒温槽に配置した。
　電池の理論容量に対して０．０５Ｃレート（２０時間率）となる電流値７７０μＡで定電流充電し、電圧４．２Ｖで充電を終了した。
　次に、０．０５Ｃレート（２０時間率）となる電流値７７０μＡで定電流放電し、電圧２Ｖで放電を終了した。
　ここまでの工程により、初回の不可逆容量を解消した。
　再び、電池の理論容量に対して０．０５Ｃレート（２０時間率）となる電流値７７０μＡで定電流充電し、電圧４．２Ｖで充電を終了した。
　次に、０．０５Ｃレート（２０時間率）となる電流値７７０μＡで定電流放電し、電圧２Ｖで放電を終了した。
　さらに、電池の理論容量に対して０．５Ｃレート（２時間率）となる電流値７７０μＡで定電流充電し、電圧４．２Ｖで充電を終了した。
　次に、０．０５Ｃレート（２０時間率）となる電流値７７０μＡで定電流放電し、電圧２Ｖで放電を終了した。
　以上の充放電試験の結果から、１００×（０．５Ｃでの充電容量／０．０５Ｃでの充電容量）で求められる充電効率Ｅを算出した。電池のハイレート充電効率は、充電効率Ｅの値が高ければ高いほど優れる。結果を表１に示す。
Figure JPOXMLDOC01-appb-T000001
　《考察》
　実施例１および２の電池は、比較例１の電池に比べて、高い充電効率Ｅを示した。実施例１および２の電池では、充電で膨張したシリコン粒子が複合活物質粒子の内部に偏在し、第２固体電解質との界面には膨張しない第１固体電解質が存在することにより、複合活物質粒子と第２固体電解質との乖離が抑制されたと考えられる。これにより、充電時において界面接触が良好に維持され、複合活物質粒子へのリチウムイオンの挿入が抑制されなかったため、充電効率Ｅが向上したと考えられる。
　特に、第１固体電解質としてガーネット型固体電解質を用いた実施例１の電池は、実施例２に比べて充電効率Ｅが高かった。
　一方、比較例１の電池の充電効率Ｅは３５％よりも低かった。比較例１の電池では、複合活物質粒子の外表面に多くのシリコン粒子が露出していたため、充放電に伴うシリコン粒子の膨張および収縮によって複合活物質粒子と第２固体電解質との乖離が促進されたと考えられる。これにより、複合活物質粒子へのリチウムイオンの挿入が抑制され、充電効率Ｅが低下したと考えられる。
　本開示の技術は、例えば、全固体リチウム二次電池、非水電解質リチウムイオン電池などのリチウム電池に有用である。
３０　複合活物質粒子
３０Ｓ　複合活物質粒子の外表面
３１　酸化物相
３２　活物質ドメイン
３３　第１固体電解質
２０　母体粒子
２０Ｓ　母体粒子の表面
１００　電池
２１０　負極
２２０　正極
１１　負極活物質層
１２　負極集電体
１３　電解質層
１７　正極活物質層
１８　正極集電体
４０　第２固体電解質
５０　導電助剤

Claims (14)

  1. 　酸化物を含む酸化物相と、
    　活物質を含み、前記酸化物相に分散して存在する複数の活物質ドメインと、
    　前記酸化物と異なる組成を有する第１固体電解質と、
    　を備え、
    　前記第１固体電解質は、前記酸化物相および前記複数の活物質ドメインによって構成された母体粒子の表面の少なくとも一部を被覆している、
    　複合活物質粒子。
  2. 　前記第１固体電解質は、ガーネット型の結晶構造を有する、
    　請求項１に記載の複合活物質粒子。
  3. 　前記第１固体電解質は、Ｌｉ7Ｌａ3Ｚｒ2Ｏ12、Ｌｉ7-3xＬａ3Ｚｒ2ＡｌxＯ12（０≦ｘ＜０．３）、Ｌｉ7-yＬａ3Ｚｒ2-yＮｂyＯ12（０≦ｙ＜０．３）、およびＬｉ7-zＬａ3Ｚｒ2-zＴａzＯ12（０≦ｚ＜０．５）からなる群より選ばれる少なくとも１つを含む、
    　請求項２に記載の複合活物質粒子。
  4. 　前記活物質は、リチウムと合金を形成する材料を含む、
    　請求項１に記載の複合活物質粒子。
  5. 　前記活物質は、単体のシリコンおよびＳｉＯa（０＜ａ＜２）からなる群より選ばれる少なくとも１つを含む、
    　請求項１に記載の複合活物質粒子。
  6. 　前記酸化物相は、非晶質である、
    　請求項１に記載の複合活物質粒子。
  7. 　前記酸化物相は、リチウムシリケートを含む、
    　請求項１に記載の複合活物質粒子。
  8. 　前記リチウムシリケートは、Ｌｉ2bＳｉＯ(2+b)（０＜ｂ≦２）で表される組成を有する、
    　請求項７に記載の複合活物質粒子。
  9. 　正極と、
    　負極と、
    　前記正極と前記負極との間に位置する電解質層と、
    　を備え、
    　前記負極は、請求項１から８のいずれか１項に記載の複合活物質粒子を含む、
    　電池。
  10. 　前記負極は、前記酸化物および前記第１固体電解質と異なる組成を有する第２固体電解質をさらに含む、
    　請求項９に記載の電池。
  11. 　前記第２固体電解質は、硫化物固体電解質を含む、
    　請求項１０に記載の電池。
  12. 　前記電解質層は、第３固体電解質を含む、
    　請求項９に記載の電池。
  13. 　活物質を含む複数の活物質ドメインが酸化物相に分散された構造を有する母体粒子の表面の少なくとも一部を第１固体電解質で被覆することを含む、
    　複合活物質粒子の製造方法。
  14. 　固相法によって、前記母体粒子の前記表面の少なくとも一部を前記第１固体電解質で被覆する、
    　請求項１３に記載の複合活物質粒子の製造方法。
PCT/JP2022/041393 2022-04-13 2022-11-07 複合活物質粒子、電池、および複合活物質粒子の製造方法 WO2023199544A1 (ja)