WO2023171759A1 - Module de batterie à électrolyte solide - Google Patents

Module de batterie à électrolyte solide Download PDF

Info

Publication number
WO2023171759A1
WO2023171759A1 PCT/JP2023/009101 JP2023009101W WO2023171759A1 WO 2023171759 A1 WO2023171759 A1 WO 2023171759A1 JP 2023009101 W JP2023009101 W JP 2023009101W WO 2023171759 A1 WO2023171759 A1 WO 2023171759A1
Authority
WO
WIPO (PCT)
Prior art keywords
solid
state battery
solid state
battery module
substrate
Prior art date
Application number
PCT/JP2023/009101
Other languages
English (en)
Japanese (ja)
Inventor
友裕 加藤
圭輔 清水
公博 水上
Original Assignee
株式会社村田製作所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社村田製作所 filed Critical 株式会社村田製作所
Publication of WO2023171759A1 publication Critical patent/WO2023171759A1/fr

Abstract

Un mode de réalisation de la présente invention concerne un module de batterie à électrolyte solide comprenant: une batterie à électrolyte solide qui présente une couche d'électrode positive, une couche d'électrode négative et une couche d'électrolyte à l'état solide disposée entre la couche d'électrode positive et la couche d'électrode négative; une unité conductrice; une unité de chauffage; et un substrat. La batterie à électrolyte solide est disposée sur le substrat, et l'unité de chauffage et la batterie à électrolyte solide peuvent être couplées thermiquement l'une à l'autre à travers l'unité conductrice.
PCT/JP2023/009101 2022-03-11 2023-03-09 Module de batterie à électrolyte solide WO2023171759A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2022-038379 2022-03-11
JP2022038379 2022-03-11

Publications (1)

Publication Number Publication Date
WO2023171759A1 true WO2023171759A1 (fr) 2023-09-14

Family

ID=87935302

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2023/009101 WO2023171759A1 (fr) 2022-03-11 2023-03-09 Module de batterie à électrolyte solide

Country Status (1)

Country Link
WO (1) WO2023171759A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019220981A1 (fr) * 2018-05-15 2019-11-21 株式会社村田製作所 Batterie solide, module de batterie et procédé de charge de batterie solide
WO2020203879A1 (fr) * 2019-03-29 2020-10-08 株式会社村田製作所 Batterie à l'état solide
JP2021114359A (ja) * 2020-01-16 2021-08-05 セイコーエプソン株式会社 電子デバイスおよび液体吐出装置

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019220981A1 (fr) * 2018-05-15 2019-11-21 株式会社村田製作所 Batterie solide, module de batterie et procédé de charge de batterie solide
WO2020203879A1 (fr) * 2019-03-29 2020-10-08 株式会社村田製作所 Batterie à l'état solide
JP2021114359A (ja) * 2020-01-16 2021-08-05 セイコーエプソン株式会社 電子デバイスおよび液体吐出装置

Similar Documents

Publication Publication Date Title
JP7192866B2 (ja) 固体電池
JP7396352B2 (ja) 固体電池
WO2020195381A1 (fr) Batterie à semi-conducteur
US20220302506A1 (en) Solid-state battery
CN113016092A (zh) 固体电池
JP7259980B2 (ja) 固体電池
US20220302507A1 (en) Solid-state battery
WO2023171759A1 (fr) Module de batterie à électrolyte solide
US20220013816A1 (en) Solid-state battery
WO2021235451A1 (fr) Batterie à électrolyte solide et corps extérieur pour batterie à électrolyte solide
JP7180685B2 (ja) 固体電池
JP7115559B2 (ja) 固体電池
CN114503339A (zh) 固体电池
WO2024014345A1 (fr) Module de batterie solide
WO2023243489A1 (fr) Boîtier de batterie solide
WO2024014260A1 (fr) Batterie à semi-conducteurs et dispositif électronique
WO2024014261A1 (fr) Batterie à semi-conducteurs encapsulée
JP7327496B2 (ja) 固体電池
US20220302498A1 (en) Solid-state battery
WO2024042927A1 (fr) Module de batterie à semi-conducteurs
WO2024009963A1 (fr) Batterie à électrolyte solide
WO2022230901A1 (fr) Boîtier de batterie solide
US20230163434A1 (en) Solid state battery
WO2023167100A1 (fr) Compartiment de batterie à semi-conducteurs
WO2023127247A1 (fr) Batterie à semi-conducteurs

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23766935

Country of ref document: EP

Kind code of ref document: A1