WO2023120703A1 - Élément d'instillation oculaire - Google Patents

Élément d'instillation oculaire Download PDF

Info

Publication number
WO2023120703A1
WO2023120703A1 PCT/JP2022/047635 JP2022047635W WO2023120703A1 WO 2023120703 A1 WO2023120703 A1 WO 2023120703A1 JP 2022047635 W JP2022047635 W JP 2022047635W WO 2023120703 A1 WO2023120703 A1 WO 2023120703A1
Authority
WO
WIPO (PCT)
Prior art keywords
propylene
eyedropper
nozzle
based polymer
mass
Prior art date
Application number
PCT/JP2022/047635
Other languages
English (en)
Japanese (ja)
Inventor
幸博 矢野
真 黒木
孝史 塚谷
彩子 佐々木
秀和 三橋
武志 狩野
Original Assignee
大成化工株式会社
株式会社プライムポリマー
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 大成化工株式会社, 株式会社プライムポリマー filed Critical 大成化工株式会社
Priority to CN202280079120.8A priority Critical patent/CN118317757A/zh
Priority to JP2023569571A priority patent/JPWO2023120703A1/ja
Publication of WO2023120703A1 publication Critical patent/WO2023120703A1/fr

Abstract

L'invention concerne un élément d'instillation oculaire comprenant au moins un composant choisi parmi un corps principal de récipient d'instillation oculaire et une buse d'instillation oculaire, dans lequel le corps principal de récipient d'instillation oculaire comprend une partie inférieure, une partie de corps cylindrique creuse qui est continue à un bord circonférentiel de la partie inférieure, une partie d'épaulement qui est continue à la partie de corps, et une partie cylindrique d'ouverture qui est continue à la partie d'épaulement, chacun parmi le corps principal de récipient d'instillation oculaire et la buse d'instillation oculaire contenant un polymère à base de propylène, et la formule (1) est satisfaite. x1-x2 ≦ 60.0 mg · · · (1) [dans la formule, x1 représente la masse (mg) d'un produit séché produit par découpe d'un échantillon d'essai ayant un poids de 5,0 g de la partie de corps du corps principal de récipient d'instillation oculaire ou de la buse d'instillation oculaire, puis par découpe de l'échantillon d'essai en une pièce ayant une taille de 3 cm x 0,3 cm, puis par le placement de la pièce découpée dans un ballon à fond rond contenant 50 ml de n-hexane, puis par chauffage de la solution résultante à reflux pendant 4 heures, puis refroidissement de la solution à température ambiante pour produire une solution, puis filtrage de la solution pour produire un filtrat, puis placement du filtrat dans un bac d'évaporation, puis séchage du filtrat dans un bain d'eau, puis séchage du produit résultant à 105 °C pendant 2 heures ; et x2 représente la masse (mg) d'un produit séché produit par réalisation d'un essai à blanc de la même manière que mentionné ci-dessus à l'exception du fait que l'échantillon d'essai n'est pas utilisé.]
PCT/JP2022/047635 2021-12-24 2022-12-23 Élément d'instillation oculaire WO2023120703A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN202280079120.8A CN118317757A (zh) 2021-12-24 2022-12-23 滴眼构件
JP2023569571A JPWO2023120703A1 (fr) 2021-12-24 2022-12-23

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2021211110 2021-12-24
JP2021-211110 2021-12-24

Publications (1)

Publication Number Publication Date
WO2023120703A1 true WO2023120703A1 (fr) 2023-06-29

Family

ID=86902807

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2022/047635 WO2023120703A1 (fr) 2021-12-24 2022-12-23 Élément d'instillation oculaire

Country Status (3)

Country Link
JP (1) JPWO2023120703A1 (fr)
CN (1) CN118317757A (fr)
WO (1) WO2023120703A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009108310A (ja) * 2007-10-12 2009-05-21 Japan Polypropylene Corp 医療用ポリプロピレン系樹脂組成物及び成形品
CN107417836A (zh) * 2017-04-13 2017-12-01 中国石油化工股份有限公司 一种低正己烷溶出的透明聚丙烯材料
CN109971070A (zh) * 2019-03-29 2019-07-05 贵州千叶药品包装股份有限公司 一种能用于高温灭菌的聚丙烯药瓶配方及其制备方法
WO2021193422A1 (fr) * 2020-03-27 2021-09-30 株式会社プライムポリマー Article moulé par injection à usage médical

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009108310A (ja) * 2007-10-12 2009-05-21 Japan Polypropylene Corp 医療用ポリプロピレン系樹脂組成物及び成形品
CN107417836A (zh) * 2017-04-13 2017-12-01 中国石油化工股份有限公司 一种低正己烷溶出的透明聚丙烯材料
CN109971070A (zh) * 2019-03-29 2019-07-05 贵州千叶药品包装股份有限公司 一种能用于高温灭菌的聚丙烯药瓶配方及其制备方法
WO2021193422A1 (fr) * 2020-03-27 2021-09-30 株式会社プライムポリマー Article moulé par injection à usage médical

Also Published As

Publication number Publication date
JPWO2023120703A1 (fr) 2023-06-29
CN118317757A (zh) 2024-07-09

Similar Documents

Publication Publication Date Title
ES2387885T5 (es) Procedimiento para producir un componente catalizador sólido para la polimerización de olefinas
ES2317273T3 (es) Composiciones de copolimero de propileno con elevada transparencia.
CA2308076C (fr) Procede de preparation de polypropylene
ES2683300T3 (es) Componente donante para catalizador de polimerización de propileno
CN105164201B (zh) 聚烯烃组合物
EP1511783B1 (fr) Compositions de copolymere de propylene flexibles a transparence elevee
ES2948965T3 (es) Composición de polipropileno con una capacidad de procesamiento y resistencia al impacto mejoradas
SK34896A3 (en) Ethylene copolymers and process for the preparation thereof
SA515360440B1 (ar) بوليمر مشترك من البروبيلين العشوائي لزجاجات ذات خصائص بصرية جيدة
JPS62256802A (ja) α−オレフイン重合体の製造法
ES2926234T3 (es) Composición de polipropileno heterofásico de alta flexibilidad y suavidad
ES2866673T3 (es) Diamidas de ácido oxálico como modificadores para los catalizadores de poliolefina
CN103687905A (zh) 聚烯烃组合物
WO2023120703A1 (fr) Élément d'instillation oculaire
US10155829B2 (en) Sterilizable article made of propylene copolymer
JP2005533920A (ja) プロピレンポリマー組成物の製造の少なくとも２段階方法
JP2021024641A (ja) 延伸容器
WO2021025142A1 (fr) Composition de polymère à base de propylène, film non étiré et stratifié
CN102459453B (zh) 聚烯烃组合物
CN105121485A (zh) 成核丙烯类聚烯烃组合物
JP2013249094A (ja) 容器
JPH0565523B2 (fr)
JP5345509B2 (ja) 加熱殺菌処理食品の包装フィルム用ポリプロピレン系樹脂組成物、及びそれを用いて得られる加熱殺菌処理食品の包装用フィルム
JPS6026129B2 (ja) エチレン共重合体の製造方法
EP2222731A1 (fr) Articles moulés transparents

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22911404

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2023569571

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 202280079120.8

Country of ref document: CN

NENP Non-entry into the national phase