WO2023054192A1 - 配線基板 - Google Patents

配線基板 Download PDF

Info

Publication number
WO2023054192A1
WO2023054192A1 PCT/JP2022/035483 JP2022035483W WO2023054192A1 WO 2023054192 A1 WO2023054192 A1 WO 2023054192A1 JP 2022035483 W JP2022035483 W JP 2022035483W WO 2023054192 A1 WO2023054192 A1 WO 2023054192A1
Authority
WO
WIPO (PCT)
Prior art keywords
insulating
layer
insulating layer
filler
wiring board
Prior art date
Application number
PCT/JP2022/035483
Other languages
English (en)
French (fr)
Inventor
英敏 湯川
Original Assignee
京セラ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 京セラ株式会社 filed Critical 京セラ株式会社
Priority to JP2023551426A priority Critical patent/JPWO2023054192A1/ja
Priority to CN202280063358.1A priority patent/CN118020392A/zh
Priority to KR1020247008918A priority patent/KR20240043804A/ko
Publication of WO2023054192A1 publication Critical patent/WO2023054192A1/ja

Abstract

本開示に係る配線基板は、第１絶縁フィラーが分散している第１絶縁層と、第１絶縁層の上面に位置する第２絶縁層とを含む。第１絶縁層は、第１絶縁フィラーのうち、第１絶縁層の上面から突出するように位置した突出フィラーと、突出フィラーの突出している表面の一部または全てを被覆する被膜とを含む。被膜が、スズ層およびシランカップリング剤層の順で積層された構造を有している。第２絶縁層は、被膜を含む第１絶縁層の上面を被覆している。

Description

配線基板
　本開示は、配線基板に関する。
　従来、配線基板に含まれる絶縁樹脂層（コア層およびビルドアップ絶縁層）には、低熱膨張率化および高密度化を目的に、例えば特許文献１に記載のように、シリカフィラーのような絶縁フィラーが充填されている。近年、この絶縁フィラーの充填率が高くなってきており、絶縁フィラーの充填率が高くなると、絶縁樹脂層の表面から露出する絶縁フィラーが多くなる。その結果、絶縁樹脂層間の境界面において、絶縁フィラーと絶縁樹脂との密着性が乏しくなり、絶縁信頼性に影響を及ぼすことになる。
特開２０１１－１６４３０５号公報
　本開示に係る配線基板は、第１絶縁フィラーが分散している第１絶縁層と、第１絶縁層の上面に位置する第２絶縁層とを含む。第１絶縁層は、第１絶縁フィラーのうち、第１絶縁層の上面から突出するように位置した突出フィラーと、突出フィラーの突出している表面の一部または全てを被覆する被膜とを含む。被膜が、スズ層およびシランカップリング剤層の順で積層された構造を有している。第２絶縁層は、被膜を含む第１絶縁層の上面を被覆している。
本開示の一実施形態に係る配線基板の要部を示す拡大説明図である。 図１において、第１絶縁層と第２絶縁層とが分離した状態を示す説明図である。 本開示の一実施形態に係る配線基板の要部を示す電子顕微鏡写真である。
　上記のように、絶縁フィラーの充填率が高くなると、絶縁樹脂層の表面から露出する絶縁フィラーが多くなる。その結果、絶縁樹脂層間の境界面において、絶縁フィラーと絶縁樹脂との密着性が乏しくなり、絶縁信頼性に影響を及ぼすことになる。したがって、絶縁フィラーが分散している絶縁樹脂層の表面に積層される絶縁樹脂層の密着性に優れ、絶縁信頼性に優れる配線基板が求められている。
　本開示に係る配線基板によれば、上記のように、第１絶縁層の上面から突出するように位置した突出フィラーの突出している表面の一部を被覆する特定の被膜が存在する。このような特定の被膜が存在することによって、本開示に係る配線基板は、絶縁フィラーが分散している絶縁樹脂層の表面に積層される絶縁樹脂層の密着性に優れ、絶縁信頼性に優れる。
　本開示の一実施形態に係る配線基板を、図１～３に基づいて説明する。図１は、本開示の一実施形態に係る配線基板の要部を示す拡大説明図である。図１に示すように、一実施形態に係る配線基板は、第１絶縁層１および第２絶縁層２を含む。図示していないが、第１絶縁層１および第２絶縁層２との間の一部には、銅などの金属で形成された配線導体層などの導体層が存在している。
　第１絶縁層１は、図１に示すように、第１絶縁樹脂１１に第１絶縁フィラー１２が分散した構造を有している。第１絶縁樹脂１１は、絶縁性を有する素材で形成されていれば限定されない。絶縁性を有する素材としては、例えば、エポキシ樹脂、ビスマレイミド－トリアジン樹脂、ポリイミド樹脂、ポリフェニレンエーテル樹脂、液晶ポリマーなどの樹脂が挙げられる。第１絶縁樹脂１１は、単独で用いてもよく、２種以上を併用してもよい。第１絶縁層１は配線基板の絶縁性を有するコア基板であってもよい。コア基板はガラス繊維を有していても、有していなくてもよい。第１絶縁層１の厚みは特に限定されず、例えばコア基板の場合は１０μｍ以上２０ｍｍ以下であり、積層用の絶縁層の場合は２μｍ以上１００μｍ以下である。
　第１絶縁樹脂１１に分散している第１絶縁フィラー１２は、第１絶縁層１の熱膨張係数を小さくする機能を有している。第１絶縁フィラー１２は限定されず、例えば、シリカ、アルミナ、硫酸バリウム、タルク、クレー、ガラス、炭酸カルシウム、酸化チタンなどの無機絶縁性フィラーが挙げられる。第１絶縁樹脂１１は単独で用いてもよく、２種以上を併用してもよい。
　第１絶縁フィラー１２の平均粒子径は限定されない。第１絶縁フィラー１２の充填率を高めるために、平均粒子径は複数種類あるのがよい。第１絶縁フィラー１２は、例えば、０．１μｍ以上１μｍ以下の平均粒子径を有していてもよい。第１絶縁層１における第１絶縁フィラー１２の充填率は、限定されない。第１絶縁層１の熱膨張係数を十分に小さくするために、第１絶縁層１における第１絶縁フィラー１２の充填率は、５０質量％以上９０質量％以下であってもよい。平均粒子径は、例えばＸ線ＣＴ分析で測定してもよい。充填率は、エネルギー分散型Ｘ線分析により検出してもよい。
　第１絶縁フィラー１２には、第１絶縁層１１の上面から突出するように位置した突出フィラー１２１が含まれる。この突出フィラー１２１の突出している表面の一部は、図２および３に示すように、被膜１３で被覆されている。図２は、図１において、第１絶縁層１と第２絶縁層２とが分離した状態を示す説明図である。図３は、一実施形態に係る配線基板の要部を示す電子顕微鏡写真である。被膜１３は、突出フィラー１２１の突出している表面の全てを被覆していてもよい。
　被膜１３は、突出フィラー１２１の表面からスズ層およびシランカップリング剤層の順で積層された構造を有する。このような被膜１３が存在することによって、第１絶縁層１の表面に積層される第２絶縁層２の密着性を向上させることができ、得られる一実施形態に係る配線基板の絶縁信頼性を向上させることができる。
　スズ層は、シランカップリング剤層を、突出フィラー１２１の表面に安定して被着させる機能を有しており、スズおよび酸化スズを含有している。スズが酸化していると、絶縁抵抗が高くなることから、スズが酸化していない場合に比べて、例えば互いに隣接している配線導体間の絶縁信頼性を向上させることができる。スズ層の厚みは限定されない。スズ層は、例えば２ｎｍ以上５ｎｍ以下の厚みを有する。スズ層が存在する場合には、後述する飛行時間型二次イオン質量分析（ＴＯＦ－ＳＩＭＳ）により、例えばスズおよび酸化スズが検出される。スズ層の厚みは、透過電子顕微鏡観察により測定することができる。
　シランカップリング剤層は、スズ層を被覆するように位置している。シランカップリング剤は、分子内に無機材料と反応する官能基と有機材料に反応する官能基とを有する化合物である。そのため、例えば、無機材料である突出フィラー１２１および導体層と反応して接続している官能基と、有機材料である第２絶縁層２と反応して接続している官能基とを備えた分子構造を有するシランカップリング剤層が存在することによって、第１絶縁フィラー１２と第２絶縁層２に含まれる第２絶縁樹脂２１との接着性（密着性）を向上させることができる。シランカップリング剤層の厚みは限定されない。シランカップリング剤層は、例えば１５ｎｍ以下の厚みを有しており、スズ層よりも厚くてもよい。
　シランカップリング剤層が存在するか否かは、例えば、飛行時間型二次イオン質量分析（ＴＯＦ－ＳＩＭＳ）で質量分析したり、フーリエ変換赤外分光法（ＦＴＩＲ）を用いて上記の官能基構造を分析したりすることによって確認することができる。ＴＯＦ－ＳＩＭＳは、ごく表面に存在する元素や分子を定性分析する表面分析方法である。具体的には、超高真空中で固体試料へ収束化したイオンビームを照射すると、スパッタリング現象に伴って、中性粒子と二次イオンとが真空中に放出される。この二次イオンが検出器に到達するまでの飛行時間を精密に測定することによって、試料表面の構成元素を分析する。シランカップリング剤層が存在する場合には、ＴＯＦ－ＳＩＭＳにより、例えばポリジメチルシロキサンが検出される。
　被膜１３は、突出フィラー１２１の突出している表面の一部を被覆するだけでなく、図２に示すように、第１絶縁層１の上面において、突出フィラー１２１以外の一部にも位置していてよい。このように、突出フィラー１２１以外の一部にも被膜１３が位置していることによって、第１絶縁層１の表面に積層される第２絶縁層２の密着性を、より向上させることができる。
　第１絶縁層１の上面における被膜１３の占める割合は、限定されない。平面透視した場合、第１絶縁層１の上面における被膜１３の占める割合は、例えば、４０％以上８０％以下であってもよい。被膜１３の占める割合が４０％以上８０％以下であれば、優れた密着性を発揮しつつ、優れた絶縁信頼性も維持することができる。
　第２絶縁層２は、第１絶縁層１の上面に位置している。第２絶縁層２は、図１に示すように、第２絶縁樹脂２１に第２絶縁フィラー２２が分散した構造を有している。第２絶縁樹脂２１は、第１絶縁樹脂１１と同様、絶縁性を有する素材で形成されていれば特に限定されない。絶縁性を有する素材としては、例えば、エポキシ樹脂、ビスマレイミド－トリアジン樹脂、ポリイミド樹脂、ポリフェニレンエーテル樹脂、液晶ポリマーなどの樹脂が挙げられる。第２絶縁樹脂２１は、第１絶縁樹脂１１と同じ樹脂であってもよく、異なる樹脂であってもよい。第２絶縁樹脂２１は、単独で用いてもよく、２種以上を併用してもよい。第２絶縁層２の厚みは特に限定されず、例えば２μｍ以上１００μｍ以下である。
　第２絶縁樹脂２１に分散している第２絶縁フィラー２２は、第２絶縁層２の熱膨張係数を小さくする機能を有している。第２絶縁フィラー２２は限定されず、第１絶縁フィラー１２と同様、例えば、シリカ、アルミナ、硫酸バリウム、タルク、クレー、ガラス、炭酸カルシウム、酸化チタンなどの無機絶縁性フィラーが挙げられる。第２絶縁フィラー２２は、第１絶縁フィラー１２と同じ絶縁フィラーであってもよく、異なる絶縁フィラーであってもよい。第２絶縁フィラー２２は単独で用いてもよく、２種以上を併用してもよい。
　第２絶縁フィラー２２の平均粒子径は限定されない。第２絶縁フィラー２２の充填率を高めるために、平均粒子径は複数種類あるのがよい。第２絶縁フィラー２２は、例えば、０．１μｍ以上１μｍ以下の平均粒子径を有していてもよい。第２絶縁層２における第２絶縁フィラー２２の充填率は、限定されない。第２絶縁層２の熱膨張係数を十分に小さくするために、第２絶縁層２における第２絶縁フィラー２２の充填率は、５０質量％以上９０質量％以下であってもよい。平均粒子径および充填率の算出方法は、上述の通りである。
　一実施形態に係る配線基板において、第１絶縁層１の表面に被膜１３を形成する方法は限定されず、例えば、下記の手順によって形成される。まず、第１絶縁フィラー１２が分散している第１絶縁樹脂１１で形成された樹脂フィルムを準備する。この樹脂フィルム（樹脂板）が第１絶縁層１の前駆体となる。以下、第１絶縁層１がコア層である場合について説明する。
　次いで、樹脂フィルムに、必要に応じてスルーホールを形成する。スルーホールは、例えば、ドリル、ブラストまたはレーザー加工によって形成される。第１絶縁層１がビルドアップ絶縁層である場合は、スルーホールの代わりにビアホールである。次いで、デスミア処理を行い、樹脂フィルムの表面およびスルーホールの内壁面に、無電解めっきによって銅などの金属でシード層を形成する。次いで、樹脂フィルムの表面にレジストを形成して、露光および現像を行う。次いで、電解めっきによって、銅などの金属を、スルーホールの樹脂フィルムの表面およびスルーホールの内壁面に形成させる。その後、レジストを剥離して、シード層も除去する。
　次いで、酸洗浄によって、銅の酸化膜など金属酸化膜を除去する。その後、スズめっきによって、樹脂フィルムの上面から突出している突出フィラー１２１の突出している表面、および突出フィラー１２１以外の部分に、１００ｎｍ程度の厚みを有するようにスズを析出させる。
　次いで、過剰に析出させたスズを、例えば硝酸を用いたエッチングによって除去する。このようにエッチングを行い、スズの厚みを２ｎｍ以上５ｎｍ以下程度に調整する。銅上は突出フィラー１２１に比べてスズの析出量が多いため、硝酸によるエッチングにより１０ｎｍ以上２０ｎｍ以下程度の厚みに調整される。１００ｎｍのスズを、２ｎｍ以上５ｎｍ以下程度に調整するためには、硝酸に２秒以上９０秒以下程度浸漬させればよい。硝酸に浸漬させる時間によって、スズ層の厚みを調整することができる。
　次いで、形成されたスズ層を被覆するように、シランカップリング剤を塗布する。シランカップリング剤としては、ＦＣ－９１００Ｚ（メック株式会社製）、ＫＢＭ－３０３（信越化学工業株式会社製）、ＤＯＷＳＩＬＴＭＺ－６０４０　Ｓｉｌａｎｅ（ダウ・東レ株式会社製）など市販されているものを使用することができる。シランカップリング剤を塗布した後、７０℃以上１００℃以下の温度で１分以上１０分以下処理することによって、スズ層の表面にシランカップリング剤層を形成する。シランカップリング剤層は、上記のように、１５ｎｍ以下の厚みを有しており、スズ層よりも厚くてもよい。加熱温度または加熱時間によって、シランカップリング剤層の厚みを調整することができる。
　このようにして、絶縁層間の密着性に優れた配線基板を製造することができる。絶縁層間であれば、コア層とビルドアップ絶縁層との接合であってもよく、ビルドアップ絶縁層間の接合であってもよい。本明細書において「第１絶縁層」および「第２絶縁層」の用語は、便宜的に記載しており、「第１絶縁層」がコア層というように限定されない。例えば、「第１絶縁層」および「第２絶縁層」のいずれも、ビルドアップ絶縁層の場合もあり得る。
　さらに、図１は、一実施形態に係る配線基板１の要部を示す拡大説明図であるため、２層の絶縁層しか示していない。しかし、本開示の配線基板は、３層以上の絶縁層が積層された構造を有していてもよい。３層以上の絶縁層が積層された構造を有する場合、隣接する２層の絶縁層において、下部に位置している絶縁層を「第１絶縁層」、上部に位置している絶縁層を「第２絶縁層」とみなせばよい。
　上述の一実施形態に係る配線基板１において、第２絶縁層２には第２絶縁フィラー２２が分散している。しかし、本開示に係る配線基板において、第２絶縁層には絶縁フィラーが存在していなくてもよい。
　さらに、上述の一実施形態に係る配線基板１において、被膜１３は、突出フィラー１２１以外の第１絶縁層１の上面の一部にも位置している。しかし、本開示に係る配線基板において、被膜は、突出フィラー１２１の突出している表面の一部を被覆しているだけでもよい。
　１　　第１絶縁層
　１１　第１絶縁樹脂
　１２　第１絶縁フィラー
　１２１　突出フィラー
　１３　被膜
　２　　第２絶縁層
　２１　第２絶縁樹脂
　２２　第２絶縁フィラー

Claims (9)

  1. 　第１絶縁フィラーが分散している第１絶縁層と、
    　該第１絶縁層の上面に位置する第２絶縁層と、
    を含み、
    　前記第１絶縁層は、前記第１絶縁フィラーのうち、前記第１絶縁層の上面から突出するように位置した突出フィラーと、該突出フィラーの突出している表面の一部または全てを被覆する被膜とを含み、
    　該被膜が、スズ層およびシランカップリング剤層の順で積層された構造を有しており、
    　前記第２絶縁層は、前記被膜を含む前記第１絶縁層の上面を被覆している、
    配線基板。
  2. 　前記被膜が、前記第１絶縁層の上面において、前記突出フィラー以外の一部にも位置している、請求項１に記載の配線基板。
  3. 　前記第２絶縁層に、第２絶縁フィラーが分散している、請求項１または２に記載の配線基板。
  4. 　平面透視した場合、前記第１絶縁層の上面における前記被膜の占める割合が、４０％以上８０％以下である、請求項１～３のいずれかに記載の配線基板。
  5. 　前記第１絶縁フィラーが、０．１μｍ以上１μｍ以下の平均粒子径を有する、請求項１～４のいずれかに記載の配線基板。
  6. 　前記第１絶縁層における前記第１絶縁フィラーの充填率が、５０質量％以上９０質量％以下である、請求項１～５のいずれかに記載の配線基板。
  7. 　前記スズ層が、２ｎｍ以上５ｎｍ以下の厚みを有する、請求項１～６のいずれかに記載の配線基板。
  8. 　前記スズ層は、酸化している、請求項１～７のいずれかに記載の配線基板。
  9. 　前記シランカップリング剤層は、１５ｎｍ以下の厚みを有し、かつ前記スズ層よりも厚い、請求項１～８のいずれかに記載の配線基板。
PCT/JP2022/035483 2021-09-29 2022-09-22 配線基板 WO2023054192A1 (ja)