WO2022249890A1 - 二次電池 - Google Patents

二次電池 Download PDF

Info

Publication number
WO2022249890A1
WO2022249890A1 PCT/JP2022/020015 JP2022020015W WO2022249890A1 WO 2022249890 A1 WO2022249890 A1 WO 2022249890A1 JP 2022020015 W JP2022020015 W JP 2022020015W WO 2022249890 A1 WO2022249890 A1 WO 2022249890A1
Authority
WO
WIPO (PCT)
Prior art keywords
heat storage
storage sheet
secondary battery
storage material
resin
Prior art date
Application number
PCT/JP2022/020015
Other languages
English (en)
French (fr)
Inventor
健一 藤崎
Original Assignee
Dic株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dic株式会社 filed Critical Dic株式会社
Priority to JP2023511954A priority Critical patent/JP7388596B2/ja
Publication of WO2022249890A1 publication Critical patent/WO2022249890A1/ja

Abstract

本発明が解決しようとする課題は、停止時における保温効果に優れる二次電池を提供することである。本発明は、二次電池１００はが正極タブを有する正極２と、負極タブを有する負極３と、正極２と負極３との間に介挿されたセパレータ４と、セパレータ４に保持された電解質とを備える電池積層体９を含む少なくとも１つの単電池１と、単電池１を収納するケース１０と、ケース１０の内面に固定され、第１蓄熱材を含有する第１蓄熱シート２０とを有するものである。

Description

二次電池
　本発明は、二次電池に関する。
　電動車両用の二次電池は、限られた温度領域（１５～３５℃）を外れると、性能が低下する。例えば、０℃以下の低温になると、起電力が極端に低下して、起動や充電に支障を来たすこととなる。このため、停止から次の起動までの一定時間、電池を保温可能な保温機構を備えることが望まれている。
　また、高速充電時や高出力放電時の発熱によって、電池の温度が上昇すると、電解質の不安定化や、電池の短寿命化を招き、大きな性能劣化に繋がる。そして、８０℃を超えると、電池の破損の危険性も生じる。このため、冷却機構が必須となるが、大規模な装置等が必要になることから、電池の大型化を招く。さらに、今後、超高速充電化が進むにつれて、より発熱量が高まることが予測され、電力だけに頼らない昇温抑制方法の開発が求められている。
　これらの要望に対応すべく、例えば、特許文献１には、単電池同士の間に蓄熱シートを挟持した構成の車載用組電池（二次電池）が開示されている。
特開２００９－１４０７８６号公報
　しかしながら、本発明者らの検討によれば、従来の二次電池では、保温効果および昇温抑制効果が未だ十分ではないことが判明した。
　そこで、本発明の目的は、特に、停止時における保温効果に優れる二次電池を提供することにある。
　本発明は、下記（１）～（１２）に関する。
　（１）　本発明の二次電池は、正極端子を有する正極と、負極端子を有する負極と、前記正極と前記負極との間に介挿されたセパレータと、該セパレータに保持された電解質とを備える電池積層体を含む少なくとも１つの単電池と、
　前記単電池を収納するケースと、
　該ケースの内面に固定され、第１蓄熱材を含有する第１蓄熱シートとを有することを特徴とする。
　（２）　本発明の二次電池では、前記第１蓄熱材の融点は、－３０℃以上１５℃以下であることが好ましい。
　（３）　本発明の二次電池では、前記第１蓄熱シート中の前記第１蓄熱材の含有量は、１０～９０質量％であることが好ましい。
　（４）　本発明の二次電池では、前記第１蓄熱シートの厚さは、１００～６０００μｍであることが好ましい。
　（５）　本発明の二次電池では、前記第１蓄熱シートは、前記第１蓄熱材を含有する発泡体で構成されていることが好ましい。
　（６）　本発明の二次電池は、さらに、前記第１蓄熱シートより内側に配置され、前記第１蓄熱材より融点が高い第２蓄熱材を含有する第２蓄熱シートを有することが好ましい。
　（７）　本発明の二次電池では、前記単電池を複数備え、
　前記第２蓄熱シートは、隣り合う前記単電池同士を隔離するように配置されていることが好ましい。
　（８）　本発明の二次電池では、各前記単電池は、前記正極端子および前記負極端子が露出した状態で、前記第２蓄熱シートで被覆されていることが好ましい。
　（９）　本発明の二次電池では、前記第２蓄熱材の融点は、１５℃超６０℃以下であることが好ましい。
　（１０）　本発明の二次電池では、前記第２蓄熱シート中の前記第２蓄熱材の含有量は、１０～９０質量％であることが好ましい。
　（１１）　本発明の二次電池では、前記第２蓄熱シートの厚さは、１００～６０００μｍであることが好ましい。
　（１２）　本発明の二次電池では、巻回された状態の前記電池積層体を含む前記単電池を複数備え、
　各前記単電池は、その長手方向を前記ケースの厚さ方向として、前記ケースに収納されていることが好ましい。
　（１３）　本発明の二次電池では、前記単電池は、さらに、前記正極端子および前記負極端子が露出した状態で、前記電池積層体を封止する封止体を含むことが好ましい。
　本発明によれば、特に、停止時における保温効果に優れる二次電池を提供することができる。
本発明の二次電池の第１実施形態を示す斜視図である。 図１中のＡ－Ａ線に沿って切断した単電池の部分断面図である。 単電池の他の構成を示す部分断面図である。 本発明の二次電池の第２実施形態を示す横断面図である。 第２実施形態の電池積層体の分解斜視図である。 本発明の二次電池の第３実施形態を部分的に切り欠いて示す斜視図である。 降温抑制の模擬実験の結果を示すグラフである。 昇温抑制の模擬実験の結果を示すグラフである。
　以下、本発明の二次電池について、添付図面に示す好適実施形態に基づいて詳細に説明する。
　＜第１実施形態＞
　まず、本発明の二次電池の第１実施形態について説明する。
　図１は、本発明の二次電池の第１実施形態を示す斜視図であり、図２は、図１中のＡ－Ａ線に沿って切断した単電池の部分断面図であり、図３は、単電池の他の構成を示す部分断面図である。
　図１に示す二次電池１００は、例えば、車両等に搭載される二次電池であり、複数の単電池１と、単電池１を収納するケース１０とを有している。
　各単電池１は、図２に示すように、正極タブ（正極端子）２９を有する正極２と、負極タブ（負極端子）３９を有する負極３と、正極２と負極３との間に介挿されたセパレータ４と、このセパレータ４に保持された電解質とを備える電池積層体９を有している。
　そして、この電池積層体９は、図１に示すように、正極タブ２９および負極タブ３９が露出した状態で、封止体５により封止されている。
　本実施形態の正極２は、正極集電体（アルミニウム箔等）２１と、正極集電体２１の両面に設けられた正極活物質層２２とを有している。
　そして、正極活物質層２２から露出する正極集電体２１の部分に、正極タブ２９が接合されている。正極タブ２９は、金属片（銅片、アルミニウム片、ニッケル片等）で構成されている。なお、正極集電体２１を加工して、正極タブ２９を形成してもよい。
　正極活物質層２２は、例えば、正極活物質と導電助剤とを含有する。
　正極活物質としては、特に限定されないが、例えば、コバルト酸リチウム、ニッケル酸リチウム、マンガン酸リチウムのような金属酸リチウム化合物、ナトリウム層状化合物等が挙げられる。これらの金属酸リチウム化合物またはナトリウム層状化合物は、１種を単独で使用しても、２種以上を併用してもよい。
　導電助剤としては、特に限定されないが、例えば、グラフェン、カーボンブラック等が挙げられる。
　また、正極活物質層２２は、必要に応じて、ポリフッ化ビニリデンのような結着剤（結着ポリマー）を含有してもよい。
　本実施形態の負極３は、負極集電体（銅箔等）３１と、負極集電体３１の両面に設けられた負極活物質層３２とを有している。
　そして、負極活物質層３２から露出する負極集電体３１の部分に、負極タブ３９が接合されている。負極タブ３９は、金属片（銅片、アルミニウム片、ニッケル片等）で構成されている。なお、負極集電体３１を加工して、負極タブ３９を形成してもよい。
　負極活物質層３２は、例えば、負極活物質と導電助剤とを含有する。
　負極活物質としては、特に限定されないが、例えば、グラファイト（黒鉛）、ハードカーボン、ソフトカーボンのような炭素系材料が挙げられる。これらの炭素系材料は、１種を単独で使用しても、２種以上を併用してもよい。
　導電助剤としては、特に限定されないが、例えば、カーボンナノチューブ等が挙げられる。
　また、負極活物質層３２は、必要に応じて、ポリフッ化ビニリデンのような結着剤（結着ポリマー）を含有してもよい。
　正極２と負極３との間には、セパレータ４が介挿されている。セパレータ４は、正極２と負極３との短絡を防止する機能および電解質を保持する機能を有する。なお、電解質を保持したセパレータ４を、電解質層とも呼ぶことができる。
　セパレータ４は、絶縁性を有し、かつ電解質を保持可能であればよく、例えば、複数の細孔を有するシート材、不織布のような多孔膜で構成することができる。
　多孔膜の構成材料としては、例えば、ポリプロピレン、ポリエチレンのようなポリオレフィン等が挙げられる。
　電解質は、好ましくは、非水系溶媒に溶解した電解液として使用される。電解質（電解液）は、単電池１の充放電時における、金属イオンの移動媒体として機能する。
　非水系溶媒としては、例えば、プロピレンカーボネート、エチレンカーボネート等が挙げられる。これらの非水系溶媒は、１種を単独で使用しても、２種以上を併用してもよい。
　電解質としては、例えば、四フッ化ホウ酸リチウム、六フッ化リン酸リチウムのようなリチウムとフッ化物との塩、ヘキサフルオロリン酸ナトリウムのようなナトリウムとフッ化物との塩等が挙げられる。
　なお、電解質には、電解質ポリマーを使用することもできる。
　封止体５は、金属箔と樹脂シートとの積層体（ラミネートフィルム）、金属製の缶体等で構成することができる。
　本実施形態の二次電池１００は、かかる単電池１の複数個をケース１０に収納して構成されている。
　ケース１０は、例えば、アルミニウム、鉄、またはこれらを含む合金のような金属材料、ポリフェニレンサルファイドのような樹脂材料等により形成することができる。
　ケース１０は、底部と周壁部とを有する箱状の部材で構成され、開口部を塞ぐように蓋体（図示せず。）が装着される。蓋体には、ケース１０に装着した状態で、複数の正極タブ２９に一括して接続される外部接続用正極端子と、複数の負極タブ３９に一括して接続される外部接続用負極端子とが設けられている。
　このケース１０の内面に、第１蓄熱材を含有する第１蓄熱シート２０が固定されている。ケース１０を樹脂材料で構成することにより、二次電池１００の軽量化に寄与するとともに、ケース１０と第１蓄熱シート２０との密着性を高めることもできる。
　蓄熱材は、固体から液体へ相変化する際に熱を吸収し、一方で液体から固体へ相変化する際に熱を放出する物質である。
　したがって、相変化を生じる温度が比較的低い蓄熱材を選択すれば、周辺温度が低下することに伴って単電池１の温度が低下した場合、蓄熱材が蓄えた熱を放出することで、単電池１の温度の低下等を防止することができる。
　一方、相変化を生じる温度（すなわち、融点）が比較的高い蓄熱材を選択すれば、二次電池１００（単電池１）の充電時等における発熱を蓄熱材が吸収することで、単電池１の温度の上昇等を防止することができる。
　本実施形態では、第１蓄熱材として、融点が比較的低い蓄熱材を使用する。この場合、第１蓄熱材がケース１０の内面付近に散らばって存在することになるので、周辺温度の低温領域での変化に応じて、第１蓄熱材が熱を円滑に吸収および放出することができる。
　したがって、第１蓄熱シート２０をケース１０の内面に固定することにより、停止後、次の起動までの一定時間、単電池１の保温が可能となる。その結果、二次電池１００（車両）の電圧が極端に低下するのを防止することができる。
　第１蓄熱材の融点の具体的な値は、－３０℃以上６０℃以下であることが好ましく、－１０℃以上１５℃以下であることがより好ましく、－１０℃以上１０℃以下であることがさらに好ましく、０℃以上８℃以下であることが特に好ましい。かかる範囲の融点を有する第１蓄熱材を使用することにより、停止後の単電池１の保温効果をより向上させることができる。
　一方、単電池からの発熱や、周辺温度の上昇によるケース内の温度上昇を抑制する場合には、第１蓄熱材の融点は、１５℃超６０℃以下であるものを使用してもよく、２０℃以上５０℃以下であるものを使用してもよく、３０℃以上４５℃以下であるものを使用してもよく、３５℃以上４５℃以下であるものを使用してもよい。かかる範囲の融点を有する第１蓄熱材を使用することにより、二次電池１００（単電池１）の充電時等における発熱をより良好に吸収することができる。
　第１蓄熱材としては、特に限定されないが、例えば、脂肪酸エステル、アルカン（パラフィン）等が挙げられる。これらの化合物は、１種を単独で使用しても、２種以上を併用してもよい。
　脂肪酸エステルとしては、例えば、デカン酸メチル、デカン酸エチル、ラウリン酸メチル、ラウリン酸エチル、ミリスチン酸エチル、パルミトレイン酸メチルエステル、オレイン酸メチル等が挙げられる。中でも、脂肪酸エステルは、ラウリン酸メチル、ラウリン酸エチル、ミリスチン酸エチル、パルミトレイン酸メチルエステルが好ましく、ラウリン酸メチルがより好ましい。
　アルカンとしては、例えば、デカン、ウンデカン、ドデカン、トリデカン、テトラデカン、ペンタデカン等が挙げられる。中でも、アルカンは、トリデカン、テトラデカン、ペンタデカンが好ましく、テトラデカンがより好ましい。
　かかる第１蓄熱材は、メラミン樹脂、アクリル樹脂、ウレタン樹脂のような有機材料からなる外殻で被覆された被覆粒子の形態であることが好ましい。
　この場合、被覆粒子の平均粒子径は、特に限定されないが、１０～３０００μｍであることが好ましい。かかる範囲の平均粒子径を有する被覆粒子を使用することにより、第１蓄熱シート２０において、被覆粒子同士の間に空隙部を形成し易く、かつ良好な成形性を実現し易くなる。
　平均粒子径は、３０μｍ以上がより好ましく、５０μｍ以上がさらに好ましく、１００μｍ以上が特に好ましい。また、好適な空隙部の形成や良好な成形性とともに、強固に被覆粒子を第１蓄熱シート２０に保持し易いことから、平均粒子径は、２０００μｍ以下がより好ましく、１０００μｍ以下がさらに好ましい。なお、一次粒子の平均粒子径が上記範囲であることが好ましい。
　被覆粒子の平均粒子径は、レーザー回折式粒度分布測定装置（株式会社堀場製作所製、「ＬＡ－９５０Ｖ２」）により測定して、得られたメジアン径（体積累積分布の５０％に相当する粒径：５０％粒径）とすることができる。
　第１蓄熱シート２０は、第１蓄熱材（被覆粒子）を保持するとともに、第１蓄熱材同士の間を結合する樹脂を含有することが好ましい。かかる樹脂が第１蓄熱材同士の間を、三次元網目状に結合することにより、空隙部を有する第１蓄熱シート２０を作製し易い。
　また、樹脂には、その水性分散液を第１蓄熱材と混合して混合液を調製する際に、第１蓄熱材１００質量部に対する水性分散液の吸収量が７０質量部以下である樹脂を使用することが好ましい。この場合、第１蓄熱シート２０中に好適なサイズの空隙部を確保し易く、また第１蓄熱材同士の間を樹脂で強固に結合して、高い機械的強度を有する第１蓄熱シート２０を作製することができる。また、その作製時にも、混合液の良好な塗工性を確保して、第１蓄熱シート２０を作製し易くなる。
　上記吸収量は、６０質量部以下がより好ましく、５５質量部以下がさらに好ましく、５０質量部以下が特に好ましい。吸収量の下限値は、通常、１０質量部程度である。第１蓄熱材に対する水性分散液の吸収量は、例えば、ＪＩＳ　Ｋ５１０１－１３－１に準じて測定することができる。なお、樹脂の水性分散液には、水４５質量部中に樹脂５５質量部を分散させた水性分散液を使用することが好ましい。
　樹脂の態様は、空隙部を有する第１蓄熱シート２０（マトリクス）を作製可能であれば、特に制限はない。ただし、第１蓄熱シート２０の全体構造を形成し易く、また良好な空隙部の形成や、空隙部の含有量（空隙率）の確保が容易であることから、機械発泡により空隙部を形成し得るエマルジョン樹脂が好適である。
　したがって、第１蓄熱シート２０は、第１蓄熱材を含有する発泡体で構成されていることが好ましい。これにより、第１蓄熱シート２０の保温性をより高めることができる。
　エマルジョン樹脂としては、例えば、アクリル系エマルジョン樹脂、ウレタン系エマルジョン樹脂、エチレン酢酸ビニル系エマルジョン樹脂、塩化ビニル系エマルジョン樹脂、エポキシ系エマルジョン樹脂等が挙げられる。中でも、アクリル系エマルジョン樹脂は、耐熱性や断熱性に優ることから好ましく、ウレタン系エマルジョン樹脂は、柔軟性に優れることから好ましい。
　エマルジョン樹脂の平均粒子径は、第１蓄熱材の被覆や、樹脂で被覆された第１蓄熱材同士の間を結合し易いことから、３０～１５００ｎｍであることが好ましく、５０～１０００ｎｍであることがより好ましい。
　エマルジョン樹脂の平均粒子径は、動的光散乱法により測定される５０％メジアン径、例えば、日機装株式会社製のマイクロトラックＵＰＡ型粒度分布測定装置により測定される体積基準での５０％メジアン径とすることができる。
　第１蓄熱シート２０は、第１蓄熱材が樹脂で被覆されるとともに、この第１蓄熱材同士が樹脂により互いに結合してなる構造を有することが好ましい。第１蓄熱シート２０は、かかる構成により、成形されたフォーム材に第１蓄熱材を保持させた構成や、樹脂のマトリクス中に独立気泡や第１蓄熱材が分散した構成に比べ、第１蓄熱材および空隙部の双方を高密度で含有することができる。
　また、空隙部の含有率（空隙率）および第１蓄熱材の含有率の双方の調整も容易であることから、第１蓄熱シート２０の蓄熱性や保温性、断熱性を適切に調整することもできる。さらに、軽量でシート形状への成形や加工も容易であり、第１蓄熱材の脱落も生じ難く、柔軟性の付与も容易である。
　第１蓄熱シート２０は、樹脂で被覆された第１蓄熱材同士を上記樹脂が結合することにより、第１蓄熱材同士の間に空隙部を有する構造である。このため、第１蓄熱シート２０の比重は、０．１５～０．９であることが好ましく、０．３～０．９であることがより好ましい。この場合、第１蓄熱シート２０の高い保温性を得易い。また、この場合、第１蓄熱シート２０の軽量化が容易であり、良好な加工性も得られる。
　第１蓄熱シート２０中の第１蓄熱材の含有量は、好適な蓄熱性や保温性を実現し易いことから、１０～９０質量％であることが好ましく、２０～８０質量％であることがより好ましく、３０～７０質量％であることがさらに好ましい。
　また、第１蓄熱シート２０中の樹脂の含有量は、空隙部および第１蓄熱材の含有量の調整や、双方の含有量を向上させ易いことから、１０～９０質量％であることが好ましく、２０～８０質量％であることがより好ましく、３０～７０質量％であることがさらに好ましい。
　また、好適な保温性や断熱性を得易いことから、第１蓄熱材と樹脂との量比は、第１蓄熱材／樹脂で表される固形分質量比で、８０／２０～１５／８５であることが好ましく、７０／３０～３０／７０であることがより好ましい。
　第１蓄熱シート２０は、切断等の加工が容易であることから、取り扱い性に優れる。
　第１蓄熱シート２０の厚さは、特に限定されないが、１００～６０００μｍであることが好ましく、３００～４０００μｍであることがより好ましく、５００～３０００μｍであることがさらに好ましい。この場合、第１蓄熱シート２０の蓄熱性および保温性をより向上させることができる。
　第１蓄熱シート２０は、ＪＩＳ　Ｋ５６００－５－１（１９９９）に準拠した耐屈曲性試験において割れの生じるマンドレル直径が、２５ｍｍ以下であることが好ましく、２０ｍｍ以下であることがより好ましく、１６ｍｍ以下であることがさらに好ましい。かかる要件を満たす第１蓄熱シート２０は、好適な柔軟性や各種部材の表面への優れた追従性を確保することができる。
　また、第１蓄熱シート２０のＪＩＳ　Ｌ１９１３（２０１０）に規定されるガーレ法に準拠して測定した剛軟度は、０．１～３０ｍＮであることが好ましく、０．５～２０ｍＮであることがより好ましく、１～１０ｍＮであることがさらに好ましい。かかる剛軟度を有する第１蓄熱シート２０も、好適な柔軟性や各種部材の表面への優れた追従性を確保することができる。
　第１蓄熱シート２０の引張強さは、０．１ＭＰａ以上であることが好ましく、０．２ＭＰａ以上であることがより好ましい。この場合、柔軟性を有しながらも強靭な第１蓄熱シート２０とすることができる。また、かかる第１蓄熱シート２０は、加工時や搬送時等にも割れが生じ難く、好適な加工性や取扱い性、搬送適正、曲げ適性等を発揮し得るため好ましい。
　なお、第１蓄熱シート２０の引張強さの上限は、特に限定されないが、１５ＭＰａ以下であることが好ましく、１０ＭＰａ以下であることがより好ましく、５ＭＰａ以下であることがさらに好ましい。
　また、第１蓄熱シート２０の引張破断時の伸び率は、１０％以上であることが好ましく、３０％以上であることがより好ましく、５０％以上であることがさらに好ましい。この場合、第１蓄熱シート２０の脆化を抑制することができる。また、かかる第１蓄熱シート２０は、仮に、加工時や搬送時等に曲げや歪みが生じた場合にも、割れや欠けが生じ難い。
　なお、第１蓄熱シート２０の引張破断時の伸び率の上限は、１０００％以下であることが好ましく、５００％以下であることがより好ましく、３００％以下であることがさらに好ましい。この場合、第１蓄熱シート２０は、強靭でありながら優れた柔軟性を実現することができる。よって、第１蓄熱シート２０は、良好な加工性や取扱い性、搬送適正、各種部材の表面への追従性等を得易い。
　第１蓄熱シート２０の引張強さおよび引張破断時の伸び率は、それぞれＪＩＳ　Ｋ６２５１に規定の方法に準じて測定することができる。
　具体的には、第１蓄熱シート２０をダンベル状２号形に切り出し、初期の標線間距離を２０ｍｍとして２本の標線をつけた試験片を作製する。この試験片を引張り試験機に取り付け、速度２００ｍｍ／分で引っ張って破断させる。このとき、破断までの最大の力（Ｎ）および破断時の標線間距離（ｍｍ）を測定し、以下の式により引張り強さおよび引張り破断時の伸び率を算出することができる。
　引張強さＴＳ（ＭＰａ）は、以下の式により算出される。
　　ＴＳ＝Ｆｍ／Ｗｔ
　　ただし、Ｆｍは最大の力（Ｎ）、Ｗは平行部分の幅（ｍｍ）、ｔは平行部分の厚さ（ｍｍ）である。
　また、引張り破断時の伸び率Ｅｂ（％）は、以下の式により算出される。
　　Ｅｂ＝（Ｌｂ－Ｌ０）／Ｌ０×１００
　　ただし、Ｌｂは破断時の標線間距離（ｍｍ）、Ｌ０は初期の標線間距離（ｍｍ）である。
　なお、第１蓄熱シート２０は、必要に応じて、各種添加剤を含有してもよい。この添加剤としては、例えば、難燃剤、ホルムアルデヒド等の有害物質吸着剤、着色顔料、消臭剤等が挙げられる。
　以上のような第１蓄熱シート２０は、好ましくは、樹脂、第１蓄熱材および水性媒体を含有する樹脂組成物を機械発泡させた後、塗布や注型し、乾燥して作製することができる。第１蓄熱シート２０の作製に際しては、樹脂組成物は、乾燥した後に、必要に応じて、熱や紫外線等により硬化させてもよい。
　樹脂組成物の調製に使用可能な水性媒体としては、水を好ましく使用することができる。
　また、水性媒体は、水と水溶性溶剤との混合物であってもよい。この水溶性溶剤としては、例えば、メチルアルコール、エチルアルコール、イソプロピルアルコール、エチルカルビトール、エチルセロソルブ、ブチルセロソルブのようなアルコール類、Ｎ－メチルピロリドンのような極性溶剤等が挙げられる。これらの水溶性溶剤は、１種を単独で使用しても、２種以上を併用してもよい。
　樹脂組成物には、必要に応じて、界面活性剤、増粘剤、難燃剤、架橋剤、その他の添加物を混合してもよい。
　例えば、起泡した泡の微細化や安定化のために、樹脂組成物には、任意の界面活性剤を混合することができる。界面活性剤には、アニオン性界面活性剤、カチオン性界面活性剤、ノニオン性界面活性剤、両イオン性界面活性剤等のいずれを使用してもよい。
　特に、起泡した泡の安定性を高める観点から、界面活性剤としては、アニオン性界面活性剤が好ましく、ステアリン酸アンモニウムのような脂肪酸アンモニウム性界面活性剤がより好ましい。界面活性剤は、１種を単独で使用しても、２種以上を併用してもよい。
　樹脂組成物には、起泡した泡の安定性や成膜性を向上させるために、増粘剤を必要量混合してもよい。増粘剤としては、例えば、アクリル酸系増粘剤、ウレタン系増粘剤、ポリビニルアルコール系増粘剤等が挙げられる。中でも、増粘剤には、アクリル酸系増粘剤、ウレタン系増粘剤を使用することが好ましい。
　樹脂組成物中には、第１蓄熱シート２０の難燃性を向上させるために、難燃剤を必要量混合してもよい。難燃剤としては、特に限定されないが、有機系難燃剤、無機系難燃剤を適宜使用することができる。
　有機系難燃剤としては、例えば、リン系化合物、ハロゲン化合物、グアニジン化合物等であることが好ましい。有機系難燃剤の具体例としては、リン酸第一アンモニウム、リン酸第二アンモニウム、リン酸トリエステル、亜リン酸エステル、フォスフォニウム塩、リン酸トリアミド、塩素化パラフィン、臭化アンモニウム、デカブロモビスフェノール、テトラブロモビスフェノールＡ、テトラブロモエタン、デカブロモジフェニルオキサイド、ヘキサブロモフェニルオキサイド、ペンタブロモオキサイド、ヘキサブロモベンゼン、塩酸グアニジン、炭酸グアニジン、リン酸グアニル尿素等が挙げられる。
　無機系難燃剤としては、例えば、アンチモンやアルミニウムの化合物、ホウ素化合物、アンモニウム化合物であることが好ましい、無機系難燃剤の具体例としては、五酸化アンチモン、三酸化アンチモン、四ホウ酸ナトリウム十水和物（ホウ砂）、硫酸アンモニウム、スルファミン酸アンモニウム等が挙げられる。
　難燃剤には、上記化合物のうちの１種を単独で使用しても、２種以上を併用してもよい。
　樹脂組成物には、第１蓄熱シート２０の機械的強度を向上させるために、硬化剤を必要量混合してもよい。硬化剤は、使用する樹脂の種類に応じて適宜選択すればよく、例えば、エポキシ系硬化剤、メラミン系硬化剤、イソシアネート系硬化剤、カルボジイミド系硬化剤、オキサゾリン系硬化剤等が挙げられる。
　樹脂組成物中の樹脂の含有量は、例えば、アクリル系エマルジョン樹脂を使用する場合には、水性媒体１００質量部に対して、３０～２００質量部であることが好ましく、５０～１５０質量部であることがより好ましい。この場合、樹脂組成物の粘度を好適な範囲に調整し易く、また、安定的に発泡させ易くなる。
　樹脂組成物中の第１蓄熱材の含有量は、第１蓄熱シート２０中の第１蓄熱材／樹脂の量比が上記範囲となるように配合すればよい。
　樹脂組成物に界面活性剤を混合する場合、その含有量は、好適な発泡性を得易いことから、樹脂１００質量部（固形分）に対して、３０質量部以下であることが好ましく、０．５～２０質量部であることがより好ましく、３～１５質量部であることがさらに好ましい。
　樹脂組成物に増粘剤を混合する場合、その含有量は、樹脂１００質量部（固形分）に対して、０．１～１０質量部であることが好ましく、０．５～８質量部であることがより好ましい。
　第１蓄熱シート２０のケース１０の内面への固定は、例えば、接着剤、融着（超音波融着、高周波融着、熱融着）、粘着剤等により行うことができる。
　また、二次電池１００は、ケース１０内に収容された隣り合う単電池１同士を隔離する第２蓄熱シート３０を有している。この第２蓄熱シート３０としては、下記に示す範囲の融点を有する第２蓄熱材を含有するものであれば、いずれも使用することができる。特に、前記第２蓄熱シート３０としては、第１蓄熱材より融点が高い第２蓄熱材を含有するものを使用することが好ましい。かかる構成により、二次電池１００（単電池１）の充電時等における発熱を第２蓄熱材が吸収することで、単電池１の温度の上昇等を防止することができる。よって、単電池１の劣化、発火等を未然に防止することができる。
　本実施形態では、各単電池１は、正極タブ２９および負極タブ３９が露出した状態で、その周囲が第２蓄熱シート３０で被覆されている。これにより、二次電池１００（単電池１）の充電時等において、単電池１の温度の上昇等をより確実に抑制することができる。
　第２蓄熱材の融点の具体的な値は、－３０℃以上６０℃以下であることが好ましく、１５℃超６０℃以下であることが好ましく、２０℃以上５０℃以下であることがより好ましく、３０℃以上４５℃以下であることがさらに好ましく、３５℃以上４５℃以下であることが特に好ましい。かかる範囲の融点を有する第２蓄熱材を使用することにより、二次電池１００（単電池１）の充電時等における発熱をより良好に吸収することができる。
　第２蓄熱材としては、特に限定されないが、例えば、脂肪酸エステル、アルカン（パラフィン）等が挙げられる。これらの化合物は、１種を単独で使用しても、２種以上を併用してもよい。
一方、周辺温度の低下に対して、単電池の温度低下を抑制する場合には、第２蓄熱材の融点は、－１０℃以上１５℃以下であることがより好ましく、－１０℃以上１０℃以下であることがより好ましく、０℃以上８℃以下であることがさらに好ましい。かかる範囲の融点を有する第２蓄熱材を使用することにより、停止後の単電池１の保温効果をより向上させることができる。
　脂肪酸エステルとしては、例えば、ミリスチン酸メチル、パルミチン酸メチル、パルミチン酸エチル、ステアリン酸メチル、ステアリン酸エチル等が挙げられる。中でも、脂肪酸エステルは、パルミチン酸メチル、パルミチン酸エチル、ステアリン酸メチル、ステアリン酸エチルが好ましく、ステアリン酸メチルがより好ましい。
　アルカンとしては、例えば、ヘキサデカン、ヘプタデカン、オクタデカン、ノナデカン、イコサン、ヘンイコサン、ドコサン等が挙げられる。中でも、アルカンは、ヘプタデカン、オクタデカン、ノナデカン、イコサン、ヘンイコサン、ドコサンが好ましく、ノナデカン、イコサン、ヘンイコサン、ドコサンがより好ましく、イコサン、ヘンイコサン、ドコサンがさらに好ましい。
　かかる第２蓄熱材は、メラミン樹脂、アクリル樹脂、ウレタン樹脂のような有機材料からなる外殻で被覆された被覆粒子の形態であることが好ましい。これにより、相変化による溶融時の第２蓄熱材の染み出し等を防止することができる。
　この場合、被覆粒子の平均粒子径は、特に限定されないが、１０～１０００μｍであることが好ましく、５０～５００μｍであることがより好ましい。
　なお、一次粒子の平均粒子径が上記範囲であることが好ましいが、平均粒子径が１～５０μｍ（好ましくは２～１０μｍ）の一次粒子が凝集して二次粒子を形成し、この二次粒子の平均粒子径が上記範囲であってもよい。
　被覆粒子の平均粒子径は、第１蓄熱材で記載したのと同様に定義される。
　第２蓄熱材は、その含水率が３質量％以下であることが好ましく、２質量％以下であることがより好ましく、１．５質量％以下であることがさらに好ましく、１．２質量％以下であることが特に好ましい。第２蓄熱材の含水率を上記範囲とすることにより、得られる第２蓄熱シート３０の微細な膨れや凹み等の発生を抑制し易くなり、好適な外観を有する第２蓄熱シート３０を得易くなる。
　第２蓄熱シート３０は、マトリクスを形成する樹脂を含有することが好ましい。
　かかる樹脂としては、熱可塑性樹脂、熱硬化性樹脂、紫外線硬化性樹脂等が挙げられる。中でも、第２蓄熱シート３０の成形性に優れることから、樹脂としては、熱可塑性樹脂であることが好ましい。
　熱可塑性樹脂としては、塩化ビニル系樹脂、アクリル系樹脂、ウレタン系樹脂、オレフィン系樹脂、エチレン酢酸ビニル共重合、スチレン・ブタジエン系樹脂、ポリスチレン系樹脂、ポリブタジエン系樹脂、ポリエステル系樹脂、ポリアミド系樹脂、ポリイミド系樹脂、ポリカーボネート系樹脂、１，２－ポリブタジエン系樹脂、ポリカーボネート系樹脂、ポリイミド系樹脂等が挙げられる。中でも、低温下での成形性や第２蓄熱材の分散性を高め易いことから、塩化ビニル系樹脂が好ましい。
　塩化ビニル系樹脂を使用すれば、その粒子を使用した樹脂組成物を調製して、ゾルキャスト膜を形成することで、低温下で第２蓄熱シート３０の作製が可能となるため好ましい。樹脂組成物は、塩化ビニル系樹脂粒子と可塑剤との混合物中に、第２蓄熱材が分散されたペースト状の組成物である。
　塩化ビニル系樹脂粒子の平均粒子径は、０．０１～１０μｍであることが好ましく、０．１～５μｍであることがより好ましい。樹脂組成物中では、塩化ビニル系樹脂粒子は、一次粒子の状態で直接分散していても、一次粒子が球状の二次粒子として凝集した状態で分散していてもよい。
　また、平均粒子径の異なる塩化ビニル樹脂粒子が混合されて、ピークが２以上存在する粒度分布を有してもよい。粒子径は、レーザー法等により測定することができる。
　塩化ビニル系樹脂粒子の形状は、好適な流動性を発現し易く、熟成粘度変化が小さいことから、略球形形状であることが好ましい。
　塩化ビニル系樹脂粒子は、乳化重合、懸濁重合により製造することで、球形形状にし易く、また、粒度分布を制御し易いため好ましい。
　塩化ビニル系樹脂の重合度は、５００～４０００であることが好ましく、６００～２０００であることがより好ましい。また、上記範囲とすることにより、樹脂組成物の回転粘度計の粘度や定常せん断粘度を好適な範囲に調整し易くなる。
　塩化ビニル系樹脂粒子は、市販品を適宜に使用することができる。市販品の具体例としては、例えば、ＺＥＳＴ　ＰＱ８３、ＰＷＬＴ、ＰＱ９２、Ｐ２４Ｚ等（いずれも、新第一塩ビ株式会社製）や、ＰＳＬ－６７５、６８５等（いずれも、株式会社カネカ製）が挙げられる。
　熱可塑性樹脂を使用する場合、第２蓄熱シート３０中の熱可塑性樹脂の含有量は、１０～８０質量％であることが好ましく、２０～７０質量％であることがより好ましく、３０～６０質量％であることがさらに好ましい。かかる範囲とすることにより、第２蓄熱シート３０中において樹脂のマトリクスを好適に形成することでき、柔軟性と強靭性とを有する第２蓄熱シート３０を形成し易くなる。また、上記範囲とすることにより、第２蓄熱シート３０の貯蔵弾性率を好適な範囲に調整し易くなる。
　また、熱可塑性樹脂を使用する場合、樹脂組成物の良好な塗工性や成形性を確保し易いことから、樹脂組成物には、可塑剤を混合することが好ましい。
　可塑剤としては、エポキシ系可塑剤、メタクリレート系可塑剤、ポリエステル系可塑剤、ポリエーテルエステル系可塑剤、脂肪族ジエステル系可塑剤、トリメリット酸系可塑剤、アジピン酸系可塑剤、安息香酸系可塑剤、フタル酸系可塑剤等が挙げられる。これらの可塑剤は、１種を単独で使用しても、２種以上を併用してもよい。
　可塑剤には、市販品を適宜使用することができる。
　エポキシ系可塑剤の市販品としては、ＤＩＣ社製　モノサイザーＷ－１５０；新日本理化社製　サンソサイザー　Ｅ－ＰＳ、Ｅ－ＰＯ、Ｅ－４０３０、Ｅ－６０００、Ｅ－２０００Ｈ、Ｅ－９０００Ｈ；ＡＤＥＫＡ社製　アデカサイザー　Ｏ－１３０Ｐ、Ｏ－１８０Ａ、Ｄ－３２、Ｄ－５５、花王社製　カポックス　Ｓ－６等が挙げられる。
　ポリエステル系可塑剤の市販品としては、ＤＩＣ社製　ポリサイザーＷ－２０５０、Ｗ－２３１０、Ｗ－２３０Ｈ；ＡＤＥＫＡ社製　アデカサイザー　ＰＮ－７１６０、ＰＮ－１６０、ＰＮ－９３０２、ＰＮ－１５０、ＰＮ－１７０、ＰＮ－２３０、ＰＮ－７２３０、ＰＮ－１０１０、三菱化学社製　Ｄ６２０、Ｄ６２１、Ｄ６２３、Ｄ６４３、Ｄ６４５、Ｄ６２０Ｎ；花王社製　ＨＡ－５等が挙げられる。
　トリメリット酸系可塑剤の市販品としては、ＤＩＣ社製　モノサイザーＷ－７０５、ＡＤＥＫＡ社製　アデカサイザーＣ－９Ｎ、三菱化学社製　ＴＯＴＭ、ＴＯＴＭ－ＮＢ等が挙げられる。
　安息香酸系可塑剤の市販品としては、ＤＩＣ社製　モノサイザーＰＢ－３Ａ、三菱化学社製　ＪＰ１２０等が挙げられる。
　第２蓄熱材や可塑剤の染み出しを抑制し易いことから、上記の中でも、特に低温でゲル化し得る可塑剤を使用することが好ましい。
　かかる可塑剤のゲル化終了温度は、１５０℃以下であることが好ましく、１４０℃以下であることがより好ましく、１３０℃以下であることがさらに好ましく、１２０℃以下であることが特に好ましく、１１０℃以下であることが最も好ましい。ゲル化終了温度は、ゲル化膜の光透過性が一定となる温度とすることができる。
　低温成形性の良好な可塑剤としては、エポキシ系可塑剤、ポリエステル系可塑剤、安息香酸系可塑剤等が挙げられる。これらの低温成形性の良好な可塑剤は、好適な蓄熱性とともに、樹脂のマトリクスに対して強靭性を付与し易いため好ましい。
　また、耐熱性と低温成形性との観点からは、エポキシ系可塑剤およびポリエステル系可塑剤を特に好ましく使用することができる。
　ゲル化終了温度は、具体的には、ペースト用塩化ビニル系樹脂（重合度：１７００）と上記可塑剤と熱安定剤（Ｃａ－Ｚｎ系）とを質量比１００／８０／１．５で混合した組成物を調製し、この組成物をガラスプレートとプレパラートとの間に挟み込み、その後、５℃／分の昇温速度で昇温し、光透過性の変化を顕微観察用ホットステージ（Ｍｅｔｔｅｒ
　８００）を用いて観察して、光透過性が一定となる温度とすることができる。
　可塑剤の２５℃における粘度は、１５００ｍＰａ・ｓ以下であることが好ましく、１０００ｍＰａ・ｓ以下であることがより好ましく、５００ｍＰａ・ｓ以下であることがさらに好ましく、３００ｍＰａ・ｓ以下であることが特に好ましい。
　かかる範囲の粘度を有する可塑剤を使用すれば、第２蓄熱シート３０を作製するための樹脂組成物の粘度を低く抑えることができるため、第２蓄熱シート３０における第２蓄熱材の充填率を高めることができる。
　また、この場合、樹脂組成物の回転粘度計の粘度や定常せん断粘度を好適な範囲に調整し易くなる。
　また、可塑剤の重量平均分子量は、２００～３０００であることが好ましく、３００～１０００であることがより好ましい。この場合、可塑剤自身が染み出し難く、かつ樹脂組成物の粘度を低く抑えることができる。このため、第２蓄熱シート３０における第２蓄熱材の充填率を高めることができる。
　また、この場合、樹脂組成物の回転粘度計の粘度や定常せん断粘度を好適な範囲に調整し易くなる。
　重量平均分子量（Ｍｗ）は、ゲル浸透クロマトグラフィー（以下、「ＧＰＣ」と略記する。）測定に基づきポリスチレン換算した値である。なお、ＧＰＣ測定は、以下の条件にて測定することができる。
　＜重量平均分子量の測定条件＞
　測定装置　：東ソー株式会社製ガードカラム「ＨＬＣ－８３３０」
　カラム　　：東ソー株式会社製「ＴＳＫ　ＳｕｐｅｒＨ－Ｈ」
　　　　　　　＋東ソー株式会社製「ＴＳＫ　ｇｅｌ　ＳｕｐｅｒＨＺＭ－Ｍ」
　　　　　　　＋東ソー株式会社製「ＴＳＫ　ｇｅｌ　ＳｕｐｅｒＨＺＭ－Ｍ」
　　　　　　　＋東ソー株式会社製「ＴＳＫ　ｇｅｌ　ＳｕｐｅｒＨＺ－２０００」
　　　　　　　＋東ソー株式会社製「ＴＳＫ　ｇｅｌ　ＳｕｐｅｒＨＺ－２０００」
　検出器　　：ＲＩ（示差屈折計）
　データ処理：東ソー株式会社製「ＧＰＣ－８０２０モデルＩＩバージョン４．１０」
　カラム温度：４０℃
　展開溶媒　：テトラヒドロフラン（ＴＨＦ）
　流速　　　：０．３５ｍＬ／分
　試料　　　：樹脂固形分換算で１．０質量％のテトラヒドロフラン溶液をマイクロフィルターにより濾過して得られた濾過物（１００μＬ）
　標準試料　：上記「ＧＰＣ－８０２０モデルＩＩバージョン４．１０」の測定マニュアルに準拠して、分子量が既知の下記の単分散ポリスチレンを用いる。
　＜標準試料：単分散ポリスチレン＞
　東ソー株式会社製「Ａ－３００」
　東ソー株式会社製「Ａ－５００」
　東ソー株式会社製「Ａ－１０００」
　東ソー株式会社製「Ａ－２５００」
　東ソー株式会社製「Ａ－５０００」
　東ソー株式会社製「Ｆ－１」
　東ソー株式会社製「Ｆ－２」
　東ソー株式会社製「Ｆ－４」
　東ソー株式会社製「Ｆ－１０」
　東ソー株式会社製「Ｆ－２０」
　東ソー株式会社製「Ｆ－４０」
　東ソー株式会社製「Ｆ－８０」
　東ソー株式会社製「Ｆ－１２８」
　東ソー株式会社製「Ｆ－２８８」
　また、第２蓄熱材が被覆粒子である場合、上記可塑剤の中でも、第２蓄熱材とのＨＳＰ距離が６以上の可塑剤を使用することが好ましい。かかる可塑剤を使用することにより、高温下での第２蓄熱シート３０からの脱離成分の発生を抑制することできる。また、第２蓄熱シート３０は、高温下でも体積収縮が生じ難い好適な耐熱性を実現し易くなる。
　ここで、蓄熱材を含有する蓄熱シートにおいては、高温下で大きく体積収縮を生じる場合がある。第２蓄熱材と可塑剤とのＨＳＰ距離を上記範囲とすることにより、高温下で多量の脱離成分を生じる要因となる可塑剤の第２蓄熱材への取り込みを抑制することができる。その結果、第２蓄熱シート３０の高温下での体積収縮を抑制し易くなり、好適な耐熱性を実現し易くなる。
　このＨＳＰ距離は、好適な耐熱性を得やすいことから、７以上であることが好ましく、８以上であることがより好ましい。また、ＨＳＰ距離の上限は、特に限定されないが、好適な相溶性や成形性を得易いことから、４０以下であることが好ましく、３０以下であることがより好ましく、２５以下であることがさらに好ましい。
　ＨＳＰ距離とは、ハンセン溶解度パラメータ（ＨＳＰ）を用いた物質同士の間の溶解性を表す指標である。ハンセン溶解度パラメータは、溶解性を多次元（典型的には、三次元）のベクトルで表すものであり、このベクトルは、分散項、極性項、水素結合項で表すことができる。そして、ベクトルの類似度を、ハンセン溶解度パラメータの距離（ＨＳＰ距離）として表す。
　ハンセン溶解度パラメータは、各種文献において参考となる数値が提示されており、例えば、Ｈａｎｓｅｎ　Ｓｏｌｕｂｉｌｉｔｙ　Ｐａｒａｍｅｔｅｒｓ：Ａ　Ｕｓｅｒ’ｓ
　Ｈａｎｄｂｏｏｋ（Ｃｈａｒｌｅｓ　Ｈａｎｓｅｎ等、２００７、第２版）等が挙げられる。また、市販のソフトウェア、例えば、Ｈａｎｓｅｎ　Ｓｏｌｕｂｉｌｉｔｙ　Ｐａｒａｍｅｔｅｒ　ｉｎ　Ｐｒａｃｔｉｃｅ（ＨＳＰｉＰ）を用いて、物質の化学構造に基づいてハンセン溶解度パラメータを算出することもできる。なお、算出は、溶媒温度を２５℃として行う。
　可塑剤と第２蓄熱材との好ましい組み合わせとしては、例えば、以下の組み合わせが挙げられる。
　アクリル系樹脂の外殻を有する第２蓄熱材（被覆粒子）を使用する場合、エポキシ系可塑剤、ポリエステル系可塑剤、トリメリット酸系可塑剤等を好ましく使用することができる。
　また、メラミン系樹脂の外殻を有する第２蓄熱材（被覆粒子）を使用する場合、エポキシ系可塑剤、ポリエステル系可塑剤、トリメリット酸系可塑剤、安息香酸系可塑剤等を好ましく使用することができる。
　特に、エポキシ系可塑剤は、第２蓄熱シート３０に対して、耐熱性等の各種特性を好適に付与し得るため好ましい。
　また、第２蓄熱シート３０において、樹脂のマトリクスを好適に形成し易いことから、使用する熱可塑性樹脂と可塑剤とのＨＳＰ距離は、１５以下であることが好ましく、１２以下であることがより好ましい。また、ＨＳＰ距離の下限は、特に限定されないが、１以上であることが好ましく、２以上であることがより好ましく、３以上であることがさらに好ましい。
　第２蓄熱材として被覆粒子を使用する場合、第２蓄熱材に対して可塑剤を混合した際のＪＩＳ　Ｋ５１０１－１３－１に準じて測定される第２蓄熱材１００質量部に対する可塑剤の吸収量が１５０質量部以下の可塑剤を好適に使用することができる。
　かかる可塑剤を使用することにより、高温下での第２蓄熱シート３０からの脱離成分の発生を抑制でき、高温下でも体積収縮が生じ難い好適な耐熱性を実現できる。
　可塑剤の吸収量は、好適な耐熱性を得易いことから、１４０質量部以下であることが好ましく、１３５質量部以下であることがより好ましく、１３０質量部以下であることがさらに好ましい。また、吸収量の下限は、特に限定されないが、好適な相溶性や成形性を得易いことから、５質量部以上であることが好ましく、１０質量部以上であることがより好ましい。可塑剤の吸収量が上記範囲であることにより、樹脂組成物の貯蔵弾性率を好適な範囲に調整し易くなる。
　可塑剤の吸収量は、ＪＩＳ　Ｋ５１０１－１３－１の吸油量の測定方法に準じて測定される。具体的には、予想される吸収量に応じて、１～２０ｇを秤量した第２蓄熱材を試料としてガラス板上に設置し、可塑剤をビュレットから一回に４～５滴ずつ徐々に加える。その都度、鋼製のパレットナイフで試料に練り込む。この操作を繰り返し、可塑剤と試料との塊ができるまで滴下を続ける。以後、１滴ずつ滴下し完全に混練する操作を繰り返し、ペーストが滑らかな硬さになったところを終点とし、このときの吸収量を可塑剤の吸収量とする。
　なお、終点は、ペーストが割れたりぼろぼろになったりせず広げることができ、かつ、測定板に軽く付着する程度とする。
　第２蓄熱シート３０は、樹脂と第２蓄熱材とを含有する樹脂組成物を調製し、この樹脂組成物を支持体上に塗布して塗工膜を形成した後、塗工膜の温度が１５０℃以下の温度で加熱することにより作製することができる。
　支持体は、第２蓄熱シート３０を剥離可能で、加熱工程の温度での耐熱性を示すフィルム状基材を好適に使用することができる。
　フィルム状基材としては、例えば、各種の工程フィルムとして使用される樹脂フィルムを好適に使用することができる。かかる樹脂フィルムとしては、例えば、ポリエチレンテレフタレート樹脂フィルム、ポリブチレンテレフタレート樹脂フィルムのようなポリエステル樹脂フィルム等が挙げられる。
　樹脂フィルムの厚さは、特に限定されないが、取扱い性や入手の容易性の観点から、２５～１００μｍであることが好ましい。
　樹脂フィルムは、表面が剥離処理されているのが好ましい。剥離処理に用いられる剥離処理剤としては、例えば、アルキッド系樹脂、ウレタン系樹脂、オレフィン系樹脂、シリコーン系樹脂等が挙げられる。
　樹脂組成物を支持体上に塗布するキャスト成膜は、ロールナイフコーター、リバースロールコーター、コンマコーターのような塗工機を使用して行うことができる。中でも、支持体上に樹脂組成物を送り出し、ドクターナイフ等により、一定の厚みの塗工膜を形成する方法を好ましく使用することができる。
　また、形成された塗工膜は、加熱や乾燥によるゲル化や硬化により、第２蓄熱シート３０とすることができる。
　加熱時の塗工膜の温度（加熱温度）は、１５０℃以下であることが好ましく、１４０℃以下であることがより好ましく、１３０℃以下であることがさらに好ましく、１２０℃以下であることが特に好ましい。塗工膜の温度を上記範囲に設定することにより、第２蓄熱材の熱による破壊（分解、劣化）を好適に抑制することができる。
　加熱時間は、ゲル化速度等に応じて適宜調整すればよいが、１０秒～１０分程度であることが好ましい。
　また、塗工膜に対しては、加熱とともに、適宜、風乾等の乾燥を行ってもよい。
　樹脂組成物が溶媒を含有する場合、上記加熱工程において、溶媒の除去を同時に行ってもよいが、上記加熱の前に、予備乾燥を行うことも好ましい。
　第２蓄熱シート３０は、支持体から剥離されて使用される。この剥離は、適宜、好適な手法で行えばよい。
　第２蓄熱シート３０を形成する樹脂組成物（塗工液）は、樹脂および第２蓄熱材に応じて適宜混合して調製すればよい。例えば、樹脂として塩化ビニル系樹脂を使用する場合、塩化ビニル系樹脂粒子を含むビニルゾル塗工液を用いて、ゾルキャストにより塗工膜を形成する方法が好ましい。この場合、ミキサー等による混練や押出成形等を用いることなく、低温下での塗工膜の成形が可能となる。このため、第２蓄熱材の破壊が生じ難く、得られる第２蓄熱シート３０からの第２蓄熱材の染み出し等が生じ難い。
　ビニルゾル塗工液は、適宜、溶媒を含有することもできる。溶媒としては、塩化ビニル系樹脂のゾルキャスト法にて使用される溶媒を適宜使用することができる。中でも、溶媒としては、ジイソブチルケトン、メチルイソブチルケトンのようなケトン類、酢酸ブチルのようなエステル類、グリコールエーテル類等が挙げられる。これらの溶媒は、１種を単独で使用しても、２種以上を併用してもよい。
　上記溶媒は、常温で樹脂をわずかに膨潤して分散を助長し易く、また、加熱工程で溶融ゲル化を促進し易いため好ましい。
　また、上記溶媒とともに希釈溶媒を使用してもよい。希釈溶媒としては、樹脂を溶解せず、分散溶媒の膨潤性を抑制する溶媒が好適に使用される。このような希釈溶媒としては、例えば、パラフィン系炭化水素、ナフテン系炭化水素、芳香族炭化水素、テルペン系炭化水素等が挙げられる。
　ビニルゾル塗工液には、塩化ビニル系樹脂の脱塩化水素反応を主とする分解劣化、着色を抑制するために、熱安定剤を混合することできる。熱安定剤としては、例えば、カルシウム／亜鉛系安定剤、オクチル錫系安定剤、バリウム／亜鉛系安定剤等が挙げられる。ビニルゾル塗工液中の熱安定剤の含有量は、塩化ビニル系樹脂１００質量部に対して、０.５～１０質量部が好ましい。
　ビニルゾル塗工液には、上記以外の成分として、減粘剤、分散剤、消泡剤のような添加剤を、必要に応じて混合してもよい。これら添加剤の含有量は、それぞれ塩化ビニル樹脂１００質量部に対して、０．５～１０質量部が好ましい。
　ビニルゾル塗工液の塗工時の粘度は、目的とする第２蓄熱シート３０の厚さや、塗工条件等により適宜調整すればよいが、良好な塗工性を得易いことから、１０００ｍＰａ・ｓ以上であることが好ましく、３０００ｍＰａ・ｓ以上であることがより好ましく、５０００ｍＰａ・ｓ以上であることがさらに好ましい。また、この粘度の上限は、７００００ｍＰａ・ｓ以下であることが好ましく、５００００ｍＰａ・ｓ以下であることがより好ましく、３００００ｍＰａ・ｓ以下であることがさらに好ましく、２５０００ｍＰａ・ｓ以下であることが特に好ましい。なお、塗工液の粘度は、Ｂ型粘度計にて測定することができる。
　上記塩化ビニル系樹脂粒子および第２蓄熱材を含有するビニルゾル塗工液のゾルキャスト膜からなる第２蓄熱シート３０は、製造時に第２蓄熱材にシェアや圧力がかからないため第２蓄熱材の破壊が生じ難い。したがって、樹脂系の材料を使用しながらも第２蓄熱材の染み出しが生じ難い。また、第２蓄熱材による蓄熱性を有するとともに、良好な柔軟性を有する第２蓄熱シート３０が得られる。さらに、容易に他の層との積層や加工も可能であることから、二次電池１００へ好適に適用される。
　第２蓄熱シート３０中の第２蓄熱材の含有量は、好適な蓄熱性を実現し易いことから、１０～９０質量％であることが好ましく、２０～７０質量％であることがより好ましく、３０～５０質量％であることがさらに好ましい。
　第２蓄熱シート３０中の可塑剤の含有量は、５～７５質量％であることが好ましく、１０～７０質量％であることがより好ましく、２０～６０質量％であることがさらに好ましく、２０～４０質量％であることが特に好ましい。この場合、樹脂組成物の良好な塗工適性や成形性を得易くなる。
　また、熱可塑性樹脂に対する可塑剤の量比は、樹脂組成物の粘度を好適な範囲に調整し易いことから、熱可塑性樹脂１００質量部に対して可塑剤が３０～１５０質量部であることが好ましく、４０～１３０質量部であることがより好ましく、５０～１２０質量部であることがさらに好ましい。
　第２蓄熱シート３０の厚さは、特に限定されないが、１００～６０００μｍであることが好ましく、３００～４０００μｍであることがより好ましく、５００～３０００μｍであることがさらに好ましい。この場合、隣り合う単電池１同士での熱の移動を良好に防止しつつ、第２蓄熱シート３０の蓄熱性より向上させることができる。
　第２蓄熱シート３０の引張強さは、０．１ＭＰａ以上であることが好ましく、０．３ＭＰａ以上であることがより好ましく、０．６ＭＰａ以上であることがさらに好ましく、１ＭＰａ以上であることが特に好ましい。この場合、柔軟性を有しながらも強靭な第２蓄熱シート３０を得ることができる。また、第２蓄熱シート３０は、加工時や搬送時等にも割れが生じ難く、好適な加工性や取扱い性、搬送適正、曲げ適性等を発現し易くなるため好ましい。
　なお、第２蓄熱シート３０の引張強さの上限は、特に限定されないが、１５ＭＰａ以下であることが好ましく、１０ＭＰａ以下であることがより好ましく、５ＭＰａ以下であることがさらに好ましい。
　また、第２蓄熱シート３０の引張破断時の伸び率は、１０％以上であることが好ましく、１５％以上であることがより好ましく、２０％以上であることがさらに好ましく、２５％以上であることが特に好ましい。この場合、第２蓄熱シート３０の脆化を抑制することができる。また、第２蓄熱シート３０は、加工時や搬送時等に曲げや歪みが生じた場合にも、割れや欠けが生じ難い。
　なお、第２蓄熱シート３０の引張破断時の伸び率の上限は、１０００％以下であることが好ましく、５００％以下であることがより好ましく、３００％以下であることがさらに好ましい。この場合、第２蓄熱シート３０は、強靭でありながら好適な柔軟性を有することができる。よって、第２蓄熱シート３０は、良好な加工性や取扱い性、搬送適正、曲げ適性等をより発現し易くなる。
　第２蓄熱シート３０の引張強さおよび引張破断時の伸び率は、それぞれ第１蓄熱シート２０の引張強さおよび引張破断時の伸び率と同様にして測定される。
　本実施形態では、各単電池１が、正極タブ２９および負極タブ３９が露出した状態で、その周囲が第２蓄熱シート３０で被覆されているが、単電池１同士の間に第２蓄熱シート３０を挟持するように配置してもよい。
　また、図３に示すように、封止体５の内面に第２蓄熱シート３０を配置するようにしてもよい。この場合、単電池１の周囲を被覆する第２蓄熱シート３０は、省略しても、省略しなくてもよい。
　＜第２実施形態＞
　図４は、本発明の二次電池の第２実施形態を示す横断面図、図５は、第２実施形態の電池積層体の分解斜視図である。
　以下、第２実施形態の二次電池１００について説明するが、上記第１実施形態の二次電池１００との相違点を中心に説明し、同様の事項については、その説明を省略する。
　図４に示す二次電池１００では、ケース１０が円筒状の胴部１１を備えている。そして、胴部１１の内周面に、第１蓄熱シート２０が固定されている。
　また、１つの電池積層体９（封止体５が省略された単電池１）と、第２蓄熱シート３０とが重ねられ（図５参照）、かつ巻回された状態で胴部１１（第１蓄熱シート２０）の内側に収納されている（図４参照）。
　かかる第２実施形態の二次電池１００においても、上記第１実施形態の二次電池１００と同様の作用・効果が得られる。特に、第２実施形態によれば、電池積層体９と第２蓄熱シート３０との接触面積を増大することができ、第２蓄熱シート３０は、電池積層体９からの熱をより効率よく吸収および排出することができる。
　なお、第２実施形態では、第２蓄熱シート３０に代えて、セパレータ４が電池積層体９と重ねられ、かつ巻回された状態で胴部１１の内側に収納されていてもよい。
　また、電池積層体９は、封止体（外装材）５で封止された単電池１として、胴部１１の内側に収納されていてもよい。
　＜第３実施形態＞
　図６は、本発明の二次電池の第３実施形態を部分的に切り欠いて示す斜視図である。
　以下、第３実施形態の二次電池１００について説明するが、上記第１および第２実施形態の二次電池１００との相違点を中心に説明し、同様の事項については、その説明を省略する。
　図６に示す二次電池１００では、矩形状のケース１０内に複数の円筒状の単電池１が配置されている。そして、ケース１０の内面に、第１蓄熱シート２０が固定されている。
　複数の単電池１は、長手方向（軸方向）をケース１０の厚さ方向（高さ方向）として行列状（マトリクス状）にケース１０に収納（配置）されている。また、ケース１０の側面には、複数の正極タブ２９に一括して接続される外部接続用正極端子１２と、複数の負極タブ３９に一括して接続される外部接続用負極端子１３とが設けられている。
　各単電池１には、図４に示す構成を採用することができる。ただし、この場合、単電池１内の第１蓄熱シート２０は省略される。
　さらに、単電池１内の第２蓄熱シート２０に代えて、セパレータ４を配置して巻回するようにしてもよい。すなわち、各単電池１には、通常の円筒状の単電池を使用することもできる。
　この場合、各単電池１の外周を第２蓄熱シート３０で被覆するようにしてもよく、一列に並ぶ複数の単電池１を一括して、第２蓄熱シート３０で被覆するようにしてもよい。
　以上、本発明の二次電池について説明したが、本発明は、上述した実施形態の構成に限定されない。
　例えば、本発明の二次電池は、上述した実施形態に構成において、他の任意の目的の構成を追加してもよいし、同様の機能を発揮する任意の構成と置換されていてよい。
　また、第１蓄熱シート２０および第２蓄熱シート３０は、それぞれ複数が積層された積層体であってもよい。
　また、ケース１０の内面に第１蓄熱シート２０が固定され、その内側に第２蓄熱シート３０が積層されてもよい。
　また、本発明の二次電池は、充放電の際に移動させるイオン種に応じて、正極活物質、負極活物質および電解質の種類が適宜選択される。
　次に、実施例を挙げて本発明をより詳しく説明するが、本発明はこれらに限定されるものではない。
　１．第１蓄熱シートの作製
　水分散アクリル系エマルジョン樹脂（ＤＩＣ社製　ＤＩＣＮＡＬ　ＭＦ－３４２　カイ１５：不揮発分５５％）１００質量部、アニオン界面活性剤６質量部、増粘剤３質量部、ラウリン酸メチルを含有する第１蓄熱材をウレタン樹脂からなる外殻を用いてマイクロカプセル化した被覆粒子（平均一次粒子径１５０μｍ、融点５℃）１００質量部を配合し、ディスパーにて攪拌混合し（２０００ｒｐｍ、３分）、機械発泡用バインダーを調製した。
　なお、被覆粒子１００質量部に対する水分散アクリル系エマルジョン樹脂の吸収量は、２８質量部であった。
　機械発泡用バインダーをＰＥＴフィルム上にアプリケーターにて塗布した後、予備乾燥として１００℃のドライヤー温度で５分間加熱した後、１４０℃のドライヤー温度で１０分間熱処理して硬化させた。これにより、厚さ３ｍｍの第１蓄熱シートを作製した。
　この第１蓄熱シートの比重は０．４２、第１蓄熱シートの質量は１２６０ｇ／ｍ２、第１蓄熱シート中に含まれる被覆粒子の含有量は６５質量％であった。
　２．第２蓄熱シートの作製
　重合度９００のポリ塩化ビニル系樹脂粒子（新第一塩ビ社製　ＺＥＳＴ　ＰＱ９２）１００質量部、ポリエステル系可塑剤（ＤＩＣ社製　ポリサイザーＷ－２３０Ｈ）７０質量部、その他添加剤として分散剤（ＤＩＣ社製　エポサイザーＥ－１００ＥＬ）２質量部、および分散剤（ＢＹＫ社製　Ｄｉｓｐｅｒｐｌａｓｔ－１１４２）２質量部と、ステアリン酸メチルを含有する第２蓄熱材をウレタン樹脂からなる外殻を用いてマイクロカプセル化した被覆粒子（平均粒子径：１５０μｍ、融点：３８℃）１００質量部を配合し、プラスチゾル塗工液を調製した。
　このプラスチゾル塗工液をＰＥＴフィルム上にアプリケーター塗工機にて塗布した後、１５０℃のドライヤー温度で８分間加熱してゲル化させ、ＰＥＴフィルムを剥離して、厚さ１ｍｍの第２蓄熱シートを作製した。
　第２蓄熱シート中に含まれる被覆粒子の含有量は３５．５質量％であった。
　３．降温抑制の模擬実験
　３－１．試験体の準備
　（実施例Ａ）
　まず、高さ２００ｍｍ×横５００ｍｍ×縦５００ｍｍの鉄製のケースを用意した。
　次に、ケースの内面全体に、上記で作製した第１蓄熱シートを張り付けた。
　その後、模擬単電池として、ケース内の底面に、厚さ８ｍｍ×横２１６ｍｍ×縦２６１ｍｍのアルミニウム（Ａ５０５２）板を配置した。
　なお、ａ）ケース内の空間の温度、ｂ）第１蓄熱シートの表面の温度およびｃ）アルミニウム板の表面の温度を測定するために３つの温度センサを取り付けた。
　（比較例Ａ１）
　第１蓄熱シートに代えて、厚さ３ｍｍの断熱材（東レ社製、「トーレペフ」；熱伝導率：０．０３５Ｗ／ｍＫ）を使用した以外は、実施例Ａと同様にして、試験体を準備した。
　（比較例Ａ２）
　第１蓄熱シートを省略した以外は、実施例Ａと同様にして、試験体を準備した。
　３－２．実験方法
　各試験体の外気を３５℃で４．５時間保持した後、０．５℃／ｍｉｎの降温速度で－５℃まで冷却し、－５℃で４．５時間保持した。
　このとき、各測定点の温度変化を記録した。その結果を図７に示す。
　図７に示すように、第１蓄熱シートを固定することにより、単電池の降温を抑制することができる。
　４．昇温抑制の模擬実験
　４－１．試験体の準備
　（実施例Ｂ）
　まず、６枚の厚さ１ｍｍ×横２００ｍｍ×縦３００ｍｍのアルミニウム（Ａ１０５０）板と、３つの横５０ｍｍ×縦１００ｍｍ×容量３０Ｗのシリコンラバーヒータ（八光電機社製、「ＳＢＨ２１２３」）とを準備した。
　次に、２枚のアルミニウム板同士の間に、１つのシリコンラバーヒータを介挿することにより、３つの模擬単電池を作製した。
　次に、模擬単電池同士の間に第２蓄熱シートを配置した。
　なお、ａ）周辺空間の温度およびｂ）上から２つ目の模擬単電池と第２蓄熱シートとの間の温度を測定するために２つの温度センサを取り付けた。
　（比較例Ｂ１）
　第２蓄熱シートに代えて、厚さ１ｍｍ×横１５０ｍｍ×縦１５０ｍｍの塩化ビニルシート（第２蓄熱材を含有せず。）を使用した以外は、実施例Ｂと同様にして、試験体を準備した。
　（比較例Ｂ２）
　第２蓄熱シートを省略した以外は、実施例Ｂと同様にして、試験体を準備した。なお、模擬単電池同士の間には、１ｍｍの隙間を保持した。
　４－２．実験方法
　各試験体を２５℃の環境下に配置した状態で、シリコンラバーヒータによる３０Ｗの発熱を１０分間継続した後、シリコンラバーヒータをオフして３０分間放置した。
　このとき、各測定点の温度変化を記録した。その結果を図８に示す。
　図８に示すように、第２蓄熱シートを固定することにより、単電池の昇温を抑制することができる。
　１００　　　二次電池
　１　　　　　単電池
　２　　　　　正極
　２１　　　　正極集電体
　２２　　　　正極活物質層
　２９　　　　正極タブ
　３１　　　　負極集電体
　３２　　　　負極活物質層
　３９　　　　負極タブ
　４　　　　　セパレータ
　５　　　　　封止体
　９　　　　　電池積層体
　１０　　　　ケース
　１１　　　　胴部
　１２　　　　外部接続用正極端子
　１３　　　　外部接続用負極端子
　２０　　　　第１蓄熱シート
　３０　　　　第２蓄熱シート

Claims (13)

  1. 　正極端子を有する正極と、負極端子を有する負極と、前記正極と前記負極との間に介挿されたセパレータと、該セパレータに保持された電解質とを備える電池積層体を含む少なくとも１つの単電池と、
    　前記単電池を収納するケースと、
    　該ケースの内面に固定され、第１蓄熱材を含有する第１蓄熱シートとを有することを特徴とする二次電池。
  2. 　前記第１蓄熱材の融点は、－３０℃以上１５℃以下である請求項１に記載の二次電池。
  3. 　前記第１蓄熱シート中の前記第１蓄熱材の含有量は、１０～９０質量％である請求項１または２に記載の二次電池。
  4. 　前記第１蓄熱シートの厚さは、１００～６０００μｍである請求項１～３のいずれか１項に記載の二次電池。
  5. 　前記第１蓄熱シートは、前記第１蓄熱材を含有する発泡体で構成されている請求項１～４のいずれか１項に記載の二次電池。
  6. 　さらに、前記第１蓄熱シートより内側に配置され、前記第１蓄熱材より融点が高い第２蓄熱材を含有する第２蓄熱シートを有する請求項１～５のいずれか１項に記載の二次電池。
  7. 　前記単電池を複数備え、
    　前記第２蓄熱シートは、隣り合う前記単電池同士を隔離するように配置されている請求項６に記載の二次電池。
  8. 　各前記単電池は、前記正極端子および前記負極端子が露出した状態で、前記第２蓄熱シートで被覆されている請求項７に記載の二次電池。
  9. 　前記第２蓄熱材の融点は、１５℃超６０℃以下である請求項６～８のいずれか１項に記載の二次電池。
  10. 　前記第２蓄熱シート中の前記第２蓄熱材の含有量は、１０～９０質量％である請求項６～９のいずれか１項に記載の二次電池。
  11. 　前記第２蓄熱シートの厚さは、１００～６０００μｍである請求項６～１０のいずれか１項に記載の二次電池。
  12. 　巻回された状態の前記電池積層体を含む前記単電池を複数備え、
    　各前記単電池は、その長手方向を前記ケースの厚さ方向として、前記ケースに収納されている請求項１～１１のいずれか１項に記載の二次電池。
  13. 　前記単電池は、さらに、前記正極端子および前記負極端子が露出した状態で、前記電池積層体を封止する封止体を含む請求項１～１２のいずれか１項に記載の二次電池。
PCT/JP2022/020015 2021-05-25 2022-05-12 二次電池 WO2022249890A1 (ja)