WO2022210558A1 - Pastilles et procédés de production de pastilles - Google Patents
Pastilles et procédés de production de pastilles Download PDFInfo
- Publication number
- WO2022210558A1 WO2022210558A1 PCT/JP2022/015053 JP2022015053W WO2022210558A1 WO 2022210558 A1 WO2022210558 A1 WO 2022210558A1 JP 2022015053 W JP2022015053 W JP 2022015053W WO 2022210558 A1 WO2022210558 A1 WO 2022210558A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- pellets
- lignocellulosic biomass
- pellet
- less
- biomass
- Prior art date
Abstract
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2023511274A JPWO2022210558A1 (fr) | 2021-03-29 | 2022-03-28 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2021056162 | 2021-03-29 | ||
JP2021-056162 | 2021-03-29 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022210558A1 true WO2022210558A1 (fr) | 2022-10-06 |
Family
ID=83456358
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2022/015053 WO2022210558A1 (fr) | 2021-03-29 | 2022-03-28 | Pastilles et procédés de production de pastilles |
Country Status (2)
Country | Link |
---|---|
JP (1) | JPWO2022210558A1 (fr) |
WO (1) | WO2022210558A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR102517510B1 (ko) * | 2022-10-27 | 2023-04-04 | 한국세라믹기술원 | 보일러의 내부 부식, 응집현상 및 슬래깅을 방지할 수 있는 바이오매스에서 추출한 실리카 성분을 포함한 연료 제조방법 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS52101202A (en) * | 1976-01-05 | 1977-08-25 | Gunnerman Rudolf W | Fuel pellets and method of producing same |
JPS59102989A (ja) * | 1982-12-03 | 1984-06-14 | Japan Steel Works Ltd:The | 燃料ペレツトの製造方法 |
JPS60170696A (ja) * | 1984-02-15 | 1985-09-04 | アイアン フレイザ− ジヨンストン | 燃料ペレツト及びその製造方法 |
JP2014132052A (ja) * | 2013-01-07 | 2014-07-17 | Oji Holdings Corp | 燃料組成物 |
JP2021178886A (ja) * | 2020-05-11 | 2021-11-18 | 出光興産株式会社 | バイオマス固形燃料の製造方法及びバイオマス固形燃料 |
-
2022
- 2022-03-28 JP JP2023511274A patent/JPWO2022210558A1/ja active Pending
- 2022-03-28 WO PCT/JP2022/015053 patent/WO2022210558A1/fr active Application Filing
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS52101202A (en) * | 1976-01-05 | 1977-08-25 | Gunnerman Rudolf W | Fuel pellets and method of producing same |
JPS59102989A (ja) * | 1982-12-03 | 1984-06-14 | Japan Steel Works Ltd:The | 燃料ペレツトの製造方法 |
JPS60170696A (ja) * | 1984-02-15 | 1985-09-04 | アイアン フレイザ− ジヨンストン | 燃料ペレツト及びその製造方法 |
JP2014132052A (ja) * | 2013-01-07 | 2014-07-17 | Oji Holdings Corp | 燃料組成物 |
JP2021178886A (ja) * | 2020-05-11 | 2021-11-18 | 出光興産株式会社 | バイオマス固形燃料の製造方法及びバイオマス固形燃料 |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR102517510B1 (ko) * | 2022-10-27 | 2023-04-04 | 한국세라믹기술원 | 보일러의 내부 부식, 응집현상 및 슬래깅을 방지할 수 있는 바이오매스에서 추출한 실리카 성분을 포함한 연료 제조방법 |
Also Published As
Publication number | Publication date |
---|---|
JPWO2022210558A1 (fr) | 2022-10-06 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
AU2005289333B2 (en) | Continuous flowing pre-treatment system with steam recovery | |
Rabelo et al. | A comparison between lime and alkaline hydrogen peroxide pretreatments of sugarcane bagasse for ethanol production | |
CA2848935C (fr) | Procede de chauffage d'une charge d'alimentation | |
JP5149785B2 (ja) | エタノールを得るためのバイオマスの処理 | |
Kurakake et al. | Pretreatment with ammonia water for enzymatic hydrolysis of corn husk, bagasse, and switchgrass | |
US8728770B2 (en) | Method for enzymatic saccharification treatment of lignocellulose-containing biomass, and method for producing ethanol from lignocellulose-containing biomass | |
US9574212B2 (en) | Process comprising sulfur dioxide and/or sulfurous acid pretreatment and enzymatic hydrolysis | |
US20140004571A1 (en) | Compositions and methods for biomass liquefaction | |
JP4619917B2 (ja) | リグノセルロースの前処理方法 | |
JP2010524473A (ja) | リグノセルロースバイオマスの熱化学的前処理と精砕の組合せ | |
JP2013544099A (ja) | 充填床反応器のための連続供給バイオマス前処理方法 | |
CN102089435A (zh) | 产生发酵产物的方法 | |
JP2010041923A (ja) | 酵素糖化方法ならびにエタノール製造方法 | |
JP2011045277A (ja) | セルロース系エタノール生産システムおよび生産方法 | |
WO2022210558A1 (fr) | Pastilles et procédés de production de pastilles | |
US20150037848A1 (en) | Method for producing saccharide | |
JP5824074B2 (ja) | バイオエタノールの製造方法及び製造システム | |
WO2010016536A1 (fr) | Procédé de traitement d'une matière lignocellulosique | |
JP6331490B2 (ja) | リグノセルロース含有バイオマスからのエタノール製造方法 | |
JP2014090707A (ja) | リグノセルロース含有バイオマスの酵素糖化処理方法及びリグノセルロース含有バイオマスからのエタノール製造方法 | |
JP5910427B2 (ja) | リグノセルロース含有バイオマスからのエタノール製造方法 | |
JP2014039492A (ja) | リグノセルロース含有バイオマスからのエタノール製造方法 | |
JP2013141415A (ja) | 単糖の製造方法及び製造装置並びにエタノールの製造方法及び製造装置 | |
JP2015159755A (ja) | リグノセルロース含有バイオマスからのエタノール製造方法 | |
JP5910367B2 (ja) | リグノセルロース含有バイオマスからのエタノール製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 22780769 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2023511274 Country of ref document: JP Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2301006389 Country of ref document: TH |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 22780769 Country of ref document: EP Kind code of ref document: A1 |