WO2022210554A1 - 樹脂被覆アルミニウム合金板 - Google Patents

樹脂被覆アルミニウム合金板 Download PDF

Info

Publication number
WO2022210554A1
WO2022210554A1 PCT/JP2022/015045 JP2022015045W WO2022210554A1 WO 2022210554 A1 WO2022210554 A1 WO 2022210554A1 JP 2022015045 W JP2022015045 W JP 2022015045W WO 2022210554 A1 WO2022210554 A1 WO 2022210554A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin
aluminum alloy
alloy plate
coated aluminum
polyesteramide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2022/015045
Other languages
English (en)
French (fr)
Inventor
治 加藤
博紀 渡邉
修一 俣川
昇行 武田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
UACJ Corp
Original Assignee
UACJ Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by UACJ Corp filed Critical UACJ Corp
Publication of WO2022210554A1 publication Critical patent/WO2022210554A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

ポリエステルアミド樹脂（ａ）、架橋剤（ｂ）及び触媒（ｃ）を含有する被覆樹脂層形成用樹脂組成物の硬化物からなる被覆樹脂層を有し、該ポリエステルアミド樹脂（ａ）は、二塩基酸の重合残基と、ジオール化合物の重合残基及びジアミン化合物の重合残基と、を有し、該架橋剤（ｂ）が、アミノ樹脂であり、該被覆樹脂層の厚みが、１．０～２０．０μｍであること、を特徴とする樹脂被覆アルミニウム合金板。本発明によれば、絞り及びしごき成形に供される樹脂被覆アルミニウム合金板であって、成形性が良好であり且つ耐高温水性が良好である樹脂被覆アルミニウム合金板を提供することができる。

Description

樹脂被覆アルミニウム合金板
　本発明は、円筒又は角筒に絞り成形される樹脂被覆アルミニウム合金板に関し、特に製品の使用環境により耐高温水性が必要とされる用途に使用される樹脂被覆アルミニウム合金板に関する。
　従来、例えば、アルミニウム電解コンデンサの多くは、アルミニウム合金板を絞り及びしごき成形した有底円筒形のケース内に、電解液を含浸させたコンデンサ素子を収納し、開口部をゴム等で封口し、さらに外周面に電気絶縁や内容物表示を目的とした塩化ビニル樹脂やオレフィン樹脂等の熱収縮性チューブで被覆された構成になっている。
　そして、絞り及びしごき成形による有底円筒形のケースの製造に用いられるアルミニウム合金板としては、樹脂被覆アルミニウム板が用いられる。
　樹脂被覆アルミニウム板としては、例えば、特許文献１には、「ポリアミドを含有する樹脂と複合化するインサート成形用の表面処理アルミニウム材であって、アルミニウムを主成分とする基材と、この基材に直接又は下地膜を介して積層される樹脂膜とを備え、上記樹脂膜が、主成分として末端にヒドロキシル基又はアミノ基を有するポリエステルアミドを含有することを特徴とする表面処理アルミニウム材。」が開示されている。
　しかしながら、近年の電子部品の小型化により、アルミニウム電解コンデンサの小型化も求められているが、このような小型のアルミニウム電解コンデンサ用の有底円筒ケースの絞り及びしごき成形では、成形条件が過酷なため、引用文献１の表面処理アルミニウム材では、成形に耐えられず、樹脂層の剥離等が起こってしまう。
　そこで、絞り成形性に優れる樹脂被覆アルミニウム合金板として、特許文献２には、「化成皮膜が形成されているアルミニウム合金板、及び該化成皮膜の表面に形成されている樹脂塗膜からなる絞り及びしごき加工用樹脂被覆アルミニウム合金板であって、該樹脂塗膜が、（ａ）数平均分子量が７０００～３００００であり且つガラス転移温度が－２０℃以上であるポリエステル樹脂、（ｂ）エポキシ樹脂、及び（ｃ）アミノ樹脂を含有する樹脂混合物の硬化物であり、硬化前の該樹脂混合物中の該（ａ）ポリエステル樹脂、該（ｂ）エポキシ樹脂及び該（ｃ）アミノ樹脂の合計含有量を１００質量部としたときの該（ａ）ポリエステル樹脂の含有量が５０～９０質量部、該（ｂ）エポキシ樹脂の含有量が３～４０質量部、該（ｃ）アミノ樹脂の含有量が５～３０質量部であることを特徴とする絞り及びしごき加工用樹脂被覆アルミニウム合金板。」が開示されている。
特開２０１６－２１５６３０号公報 特開２００７－２３７５４２号公報
　特許文献２の樹脂被覆アルミニウム合金板は、過酷な絞り及びしごき成形に対しても、成形性が良好であり、樹脂の剥離の問題は生じない。
　ところが、最近の自動車用、屋外で使用される機器用等の用途に用いられる電子部品では、使用環境が過酷であり、耐高温水性が求められるようになってきた。
　そして、特許文献２の樹脂被覆アルミニウム合金板では、被覆樹脂として、加水分解し易いポリエステル樹脂を用いているため、耐高温水性に劣るという問題があった。
　従って、本発明は、絞り及びしごき成形に供される樹脂被覆アルミニウム合金板であって、絞り及びしごき成形性が良好であり且つ耐高温水性が良好である樹脂被覆アルミニウム合金板を提供することを目的とする。
　上記課題は、以下の本発明によって解決される。
　すなわち、本発明（１）は、ポリエステルアミド樹脂（ａ）、架橋剤（ｂ）及び触媒（ｃ）を含有する被覆樹脂層形成用樹脂組成物の硬化物からなる被覆樹脂層を有し、
　該ポリエステルアミド樹脂（ａ）は、二塩基酸の重合残基と、ジオール化合物の重合残基及びジアミン化合物の重合残基と、を有し、
　該架橋剤（ｂ）が、アミノ樹脂であり、
　該被覆樹脂層の厚みが、１．０～２０．０μｍであること、
を特徴とする樹脂被覆アルミニウム合金板を提供するものである。
　また、本発明（２）は、前記架橋剤（ｂ）が、ベンゾグアナミン骨格を有するアミノ樹脂であることを特徴とする（１）の樹脂被覆アルミニウム合金板を提供するものである。
　また、本発明（３）は、前記架橋剤（ｂ）が、メチル化ベンゾグアナミンであることを特徴とする（２）の樹脂被覆アルミニウム合金板を提供するものである。
　また、本発明（４）は、前記ポリエステルアミド樹脂（ａ）を構成する二塩基酸の重合残基が、重合脂肪酸の重合残基であることを特徴とする（１）～（３）いずれかの樹脂被覆アルミニウム合金板を提供するものである。
　また、本発明（５）は、前記ポリエステルアミド樹脂（ａ）におけるエステル成分とアミド成分の共重合比（モル比）が、１０：９０～９０：１０であることを特徴とする（１）～（４）いずれかの樹脂被覆アルミニウム合金板を提供するものである。
　また、本発明（６）は、前記ポリエステルアミド樹脂（ａ）の赤外分光分析（ＩＲ）において、２９２５ｃｍ－１付近の吸収ピークの高さをＸ、１７３５ｃｍ－１付近の吸収ピークの高さをＸ１、１６４５ｃｍ－１付近の吸収ピークの高さをＸ２としたとき、以下の式（１）及び（２）：
　　　０．５≦（Ｘ１／Ｘ）≦２．０　　　　（１）
　　　０．５≦（Ｘ２／Ｘ）≦３．０　　　　（２）
を満たすことを特徴とする（１）～（５）いずれかの樹脂被覆アルミニウム合金板を提供するものである。
　また、本発明（７）は、前記ポリエステルアミド樹脂（ａ）の赤外分光分析（ＩＲ）において、１７３５ｃｍ－１付近の吸収ピークの高さＸ１に対する１６４５ｃｍ－１付近の吸収ピークの高さＸ２の比が、０．２５～６．０であることを特徴とする（１）～（５）いずれかの樹脂被覆アルミニウム合金板を提供するものである。
　また、本発明（８）は、前記架橋剤（ｂ）の含有量が、前記ポリエステルアミド樹脂（ａ）１００質量部に対し、５．０～３０．０質量部であることを特徴とする（１）～（７）いずれかの樹脂被覆アルミニウム合金板を提供するものである。
　また、本発明（９）は、前記触媒（ｃ）の含有量が、前記ポリエステルアミド樹脂（ａ）及び前記架橋剤（ｂ）の合計１００質量部に対し、０．０５０～０．９０質量部であることを特徴とする（１）～（８）いずれかの樹脂被覆アルミニウム合金板を提供するものである。
　本発明（１０）は、前記触媒（ｃ）が、ドデシルベンゼンスルホン酸であることを特徴とする（１）～（９）いずれかの樹脂被覆アルミニウム合金板を提供するものである。
　また、本発明（１１）は、前記被覆樹脂層形成用樹脂組成物の硬化物のゲル分率が、４．０～１４．０％であることを特徴とする（１）～（１０）いずれかの樹脂被覆アルミニウム合金板を提供するものである。
　また、本発明（１２）は、前記樹脂被覆アルミニウム合金板が、アルミニウム合金板と、該アルミニウム合金板の表面に形成されている化成皮膜と、該化成皮膜の表面に形成されている前記被覆樹脂層と、からなることを特徴とする（１）～（１１）いずれかの樹脂被覆アルミニウム合金板を提供するものである。
　本発明によれば、絞り及びしごき成形に供される樹脂被覆アルミニウム合金板であって、絞り及びしごき成形性が良好であり且つ耐高温水性が良好である樹脂被覆アルミニウム合金板を提供することができる。
本発明の樹脂被覆アルミニウム合金板の形態例の模式的な断面図である。
　本発明の樹脂被覆アルミニウム合金板は、ポリエステルアミド樹脂（ａ）、架橋剤（ｂ）及び触媒（ｃ）を含有する被覆樹脂層形成用樹脂組成物の硬化物からなる被覆樹脂層を有し、
　該ポリエステルアミド樹脂（ａ）は、二塩基酸の重合残基と、ジオール化合物の重合残基及びジアミン化合物の重合残基と、を有し、
　該架橋剤（ｂ）が、アミノ樹脂であり、
　該被覆樹脂層の厚みが、１．０～２０．０μｍであること、
を特徴とする樹脂被覆アルミニウム合金板である。
　本発明の樹脂被覆アルミニウム合金板について、図１を参照して説明する。図１は、本発明の樹脂被覆アルミニウム合金板の形態例の模式的な断面図である。図１中、樹脂被覆アルミニウム合金板１は、アルミニウム合金板（アルミニウム板）２の表面に形成されている化成皮膜３及び該化成皮膜３の表面に形成されている被覆樹脂層４からなる。なお、図１に示す形態例の樹脂被覆アルミニウム合金板は、被覆樹脂層の下地として、化成皮膜を有しているが、本発明において、化成皮膜は任意であり、被覆樹脂層は、アルミニウム合金板（アルミニウム板）の表面に直接形成されていてもよい。例えば、被覆樹脂層は、有機溶剤、アルカリ又は酸で洗浄されたアルミニウム合金板（アルミニウム板）の表面に直接形成されていてもよい。本発明の樹脂被覆アルミニウム合金板としては、（ｉ）アルミニウム合金板（アルミニウム板を含む。）と、該アルミニウム合金板の表面に形成されている化成皮膜と、該化成皮膜の表面に形成されている被覆樹脂層と、からなる樹脂被覆アルミニウム合金板、（ｉｉ）アルミニウム合金板（例えば、有機溶剤、アルカリ又は酸で洗浄されたアルミニウム合金板）（アルミニウム板を含む。）と、該アルミニウム合金板の表面に形成されている被覆樹脂層と、からなる樹脂被覆アルミニウム合金板が挙げられる。アルミニウム合金板の洗浄に用いられる有機溶剤としては、アセトン、塩化メチレン、メチルエチルケトン等が挙げられ、また、アルカリとしては、水酸化ナトリウム水溶液、市販のアルミニウム用脱脂液（アルカリビルダー、キレート剤、界面活性剤等を含む。）等が挙げられ、また、酸としては、硝酸、硫酸等が挙げられる。
　本発明の樹脂被覆アルミニウム合金板において、アルミニウム合金板とは、アルミニウム又はアルミニウム合金のいずれかからなる板である。アルミニウム合金板としては、通常、１０５０、１１００、３００３、３００４、５０５２、５１８２等の深絞り成形やしごき成形に用いられるアルミニウム合金であれば、特に制限されず、用途に応じて、適宜選択される。　
　アルミニウム合金板の厚みは、用途により適宜選択される。例えば、コンデンサケース用の場合０．２～０．４μｍ程度である。
　本発明の樹脂被覆アルミニウム合金板が化成皮膜を有する場合、アルミニウム合金板に、樹脂を被覆するための下地、すなわち、被覆樹脂層を形成させるための下地として、通常用いられている化成皮膜であれば、特に制限されない。化成皮膜としては、例えば、アルカリ－クロム酸塩系、クロム酸塩系、リン酸－クロム酸塩系、リン酸亜鉛系、非クロム酸塩系、酸化被膜系等が挙げられ、更に具体的には、アルミニウムの酸化物及びクロムの酸化物の混合被膜、リン酸クロム及びリン酸アルミニウムの混合被膜、リン酸亜鉛被膜、酸化アルミニウム及びリン酸エステルの混合被膜、クロムの酸化物及びポリアクリル酸樹脂の混合被膜、アルミニウムの水和酸化物被膜が挙げられる。
　化成皮膜を形成させる方法としては、通常、アルミニウム合金板に被覆樹脂層を形成させるための下地としての化成皮膜の形成に用いられる方法であれば、特に制限されない。例えば、圧延等により得られたアルミニウム合金板の表面を、中性洗剤、弱酸性洗剤、弱アルカリ性洗剤又は脱脂剤等で洗浄するか、あるいは、エッチング処理して、圧延等により得られたアルミニウム合金板の表面に付着している潤滑油等の油脂分を除去し、次いで、得られた脱脂アルミニウム合金板の表面を、被膜処理することにより、アルミニウム合金板の表面に化成皮膜を形成させる方法が挙げられる。被膜処理としては、リン酸、無水クロム酸、フッ化水素を含有する処理液に、脱脂アルミニウム合金板を浸漬するリン酸クロメート処理；無水クロム酸等を含有する処理液に、脱脂アルミニウム合金板を浸漬するクロム酸クロメート処理；ジルコニウム化合物又はチタン化合物を主とする化合物を含有する処理液に、脱脂アルミニウム合金板を浸漬する処理；有機樹脂及び金属塩を含有する処理液を、脱脂アルミニウム合金板に塗布及び乾燥する塗布型処理等が挙げられる。
　被覆樹脂層は、ポリエステルアミド樹脂（ａ）、架橋剤（ｂ）及び触媒（ｃ）を含有する被覆樹脂層形成用樹脂組成物の硬化物からなる。つまり、被覆樹脂層は、該被覆樹脂層形成用樹脂組成物を熱硬化させて得られる。
　被覆樹脂層形成用樹脂組成物は、ポリエステルアミド樹脂（ａ）、架橋剤（ｂ）及び触媒（ｃ）を含有する。
　ポリエステルアミド樹脂（ａ）は、二塩基酸の重合残基と、ジオール化合物の重合残基及びジアミン化合物の重合残基と、を有する樹脂である。つまり、ポリエステルアミド樹脂（ａ）は、エステル成分と、アミド成分と、を有する。言い換えると、ポリエステルアミド樹脂（ａ）は、二塩基酸と、ジオール化合物及びジアミン化合物とを、反応させて得られる樹脂であり、二塩基酸とジオール化合物のエステル化反応によるエステル結合及び二塩基酸とジアミン化合物のアミド化反応によるアミド結合により、二塩基酸の重合残基とジオール化合物の重合残基が結合しており且つ二塩基酸の重合残基とジアミン化合物の重合残基が結合している樹脂である。なお、本発明において、ジオール化合物の重合残基及びエステル成分とは、重合原料のジオール化合物がＨＯ－Ｒ１－ＯＨであるとすると、ポリエステルアミド樹脂（ａ）中の「－Ｏ－Ｒ１－Ｏ－」の部分を指す。また、本発明において、ジアミン化合物の重合残基及びアミド成分とは、重合原料のジアミン化合物がＮＨ２－Ｒ２－ＮＨ２であるとすると、ポリエステルアミド樹脂（ａ）中の「－ＮＨ－Ｒ２－ＮＨ－」の部分を指す。
　ポリエステルアミド樹脂（ａ）中の二塩基酸の重合残基は、二塩基酸が、ジオール化合物又はジアミン化合物と反応することにより生成する。二塩基酸の重合残基とは、重合原料の二塩基酸がＨＯＯＣ－Ｒ３－ＣＯＯＨであるとすると、ポリエステルアミド樹脂（ａ）中の「－ＣＯ－Ｒ３－ＣＯ－」の部分を指す。
　ポリエステルアミド樹脂（ａ）中の二塩基酸の重合残基は、二塩基酸に由来する。ポリエステルアミド樹脂（ａ）の重合原料となる二塩基酸としては、重合脂肪酸、アジピン酸、ピメリン酸、スベリン酸、アゼライン酸、セバシン酸、ドデカン二酸、ヘキサデカンジオン酸、エイコサンジオン酸、ジグリコール酸、２，２，４－トリメチルアジピン酸、キシリレンジカルボン酸、１，４－シクロヘキサンジカルボン酸、テレフタル酸、イソフタル酸が挙げられる。
　ポリエステルアミド樹脂（ａ）の重合原料となる二塩基酸としては、重合脂肪酸が、耐高温水性が高くなる点で好ましい。重合脂肪酸としては、炭素数１０～２４の二重結合又は三重結合を１個以上有する一塩基性不飽和脂肪酸をディールス－アルダー反応させて得られた重合脂肪酸が用いられる。例えば、重合脂肪酸としては、大豆油脂肪酸、トール油脂肪酸、菜種油脂肪酸等の天然の脂肪酸及びこれらを精製したオレイン酸、リノール酸、エルカ酸等を原料に用いてディールス－アルダー反応させて得られた重合脂肪酸が用いられる。重合脂肪酸は、通常、ダイマー酸（二量体化脂肪酸）を主成分とし、他に、原料の脂肪酸や三量体化以上の脂肪酸の混合物として得られるものである。中でも、重合脂肪酸としては、ダイマー酸（二量体化脂肪酸）含有量が７０重量％以上、好ましくは９５重量％以上であり、且つ、水素添加（水添反応）して不飽和度を下げたものが、耐酸化性に優れる点、特に高温域における着色が少ない点で、好適に用いられる。
　ポリエステルアミド樹脂（ａ）中のジオール化合物の重合残基は、ジオール化合物に由来する。ポリエステルアミド樹脂（ａ）の重合原料となるジオール化合物としては、エチレングリコール、１，２－プロパンジオール、１，３－プロパンジオール、１，３－ブタンジオール、１，４－ブタンジオール、ネオペンチルグリコール、１，５－ペンタンジオール、１，６－ヘキサンジオール、１，７－ヘプタンジオール、１，８－オクタンジオール、１，９－ノナンジオール、１，１０－デカンジオール、１，１２－ドデカンジオール、３－メチル－１，５－ペンタンジオール、２－メチル－２，４－ペンタンジオール、２，２，４－トリメチル－１，３－ペンタンジオール、２，４－ヘプタンジオール、２，２－ジエチル－１，３－プロパンジオール、２－エチル－１，３－ヘキサンジオール、２－ブチル－２－エチル－１，３－プロパンジオール等の脂肪族ジオール化合物、シクロペンタジエン－１，２－ジオール、シクロヘキサン－１，３－ジオール、シクロヘキサン－１，４－ジオール、シクロヘキサン－１，４－ジメタノール等の脂環族ジオール、ダイマー酸（二量体化脂肪酸）を還元反応したダイマージオールなどが挙げられる。これらのうち、ジオール化合物としては、エチレングリコール、１，４－ブタンジオール、ネオペンチルグリコール、１，６－ヘキサンジオール、シクロヘキサン－１，４－ジオール、ダイマージオールが、被覆樹脂層形成用樹脂組成物の硬化物の耐高温水性が高くなる点で好ましい。
　ポリエステルアミド樹脂（ａ）中のジアミン化合物の重合残基は、ジアミン化合物に由来する。ポリエステルアミド樹脂（ａ）の重合原料となるジアミン化合物としては、ヘキサメチレンジアミン、テトラメチレンジアミン、ノナメチレンジアミン、ウンデカメチレンジアミン、ドデカメチレンジアミン、メチルペンタメチレンジアミン、２，２，４－または２，４，４－トリメチルヘキサメチレンジアミン、炭素数２０～４８の重合脂肪酸から誘導されるダイマージアミン等の脂肪族ジアミン化合物、ビス－（４，４－アミノシクロヘキシル）メタン、メタキシリレンジアミン、イソホロンジアミン、ノルボルナンジアミン、ピペラジンなどが挙げられる。これらのうち、ジアミン化合物としては、ヘキサメチレンジアミン、ドデカメチレンジアミン、ビス－（４，４－アミノシクロヘキシル）メタン、メタキシリレンジアミンが、ポリエステルアミド樹脂の溶剤溶解性に優れる点で、好ましい。
　ポリエステルアミド樹脂（ａ）におけるエステル成分とアミド成分の共重合比（モル比）は、好ましくは１０：９０～９０：１０、特に好ましくは１５：８５～６０：４０である。ポリエステルアミド樹脂（ａ）におけるエステル成分とアミド成分の共重合比が上記範囲にあることにより、絞り及びしごき成形性が良好となり、且つ、耐高温水性が良好となる。
　ポリエステルアミド樹脂（ａ）中のエステル成分とアミド成分の共重合比（モル比）は、重合原料中のジオール化合物とジアミン化合物のモル比に由来する。つまり、ポリエステルアミド樹脂（ａ）は、重合原料中のジオール化合物とジアミン化合物のモル比を、好ましくは１０：９０～９０：１０、特に好ましくは１５：８５～６０：４０として、二塩基酸と、ジオール化合物及びジアミン化合物と、を共重合させて得られるものが好ましい。ポリエステルアミド樹脂（ａ）が、重合原料中のジオール化合物とジアミン化合物のモル比を、上記範囲として共重合させて得られるものであることより、絞り成形性が良好となり、且つ、耐高温水性が良好となる。
　ポリエステルアミド樹脂（ａ）は、本発明の効果を損なわない範囲で、二塩基酸の重合残基、ジオール化合物の重合残基及びジアミン化合物の重合残基以外に、一塩基酸や、３価以上の多塩基酸等の酸の重合残基、モノアルコールや、３価以上の多価アルコール等のアルコール化合物の重合残基、モノアミノ化合物や、３価以上の多価アミノ化合物等のアミン化合物の重合残基等を有していてもよい。
　ポリエステルアミド樹脂（ａ）の重量平均分子量は、好ましくは１，０００～１００，０００、特に好ましくは５，０００～５０，０００である。ポリエステルアミド樹脂（ａ）の分子量が上記範囲にあることにより、塗料としたときのハンドリング性が良好となる。なお、本発明において、ポリエステルアミド樹脂（ａ）の重量平均分子量は、ゲル浸透型クロマトグラフィー（ＧＰＣ）分析におけるスチレン換算の分子量である。
　ポリエステルアミド樹脂（ａ）としては、ポリエステルアミド樹脂（ａ）を赤外分光分析（ＩＲ）したときに、得られる赤外吸収スペクトル中、２９２５ｃｍ－１付近の吸収ピークの高さをＸ、１７３５ｃｍ－１付近の吸収ピークの高さをＸ１、１６４５ｃｍ－１付近の吸収ピークの高さをＸ２としたとき、以下の式（１）及び（２）：
　　　０．５≦（Ｘ１／Ｘ）≦２．０　　　　（１）
　　　０．５≦（Ｘ２／Ｘ）≦３．０　　　　（２）
を満たすものが好ましく、下記（１’）及び（２’）：
　　　０．７≦（Ｘ１／Ｘ）≦１．５　　　　（１’）
　　　０．７≦（Ｘ２／Ｘ）≦１．５　　　　（２’）
を満たすものが特に好ましい。ポリエステルアミド樹脂（ａ）が上記式を満たすものであることにより、絞り成形性が良好となり、且つ、耐高温水性が良好となる。
　ポリエステルアミド樹脂（ａ）としては、ポリエステルアミド樹脂（ａ）を赤外分光分析（ＩＲ）したときに、得られる赤外吸収スペクトル中、１７３５ｃｍ－１付近の吸収ピークの高さをＸ１、１６４５ｃｍ－１付近の吸収ピークの高さをＸ２としたとき、１７３５ｃｍ－１付近の吸収ピークの高さＸ１に対する１６４５ｃｍ－１付近の吸収ピークの高さＸ２の比（Ｘ２／Ｘ１）は、好ましくは０．２５～６．０、より好ましくは０．５０～３．０、特に好ましくは０．５０～１．５である。ポリエステルアミド樹脂（ａ）の１７３５ｃｍ－１付近の吸収ピークの高さＸ１に対する１６４５ｃｍ－１付近の吸収ピークの高さＸ２の比（Ｘ２／Ｘ１）が上記範囲にあることにより、絞り成形性が良好となり、且つ、耐高温水性が良好となる。
　架橋剤（ｂ）は、ポリエステルアミド樹脂（ａ）を架橋し、架橋構造を形成することにより、樹脂層の機械的強度を高め、耐高温水性や耐溶剤性を向上させる成分である。
　架橋剤（ｂ）は、アミノ樹脂である。架橋剤（ｂ）に係るアミノ樹脂としては、ベンゾグアナミン骨格を有するアミノ樹脂、メラミン骨格を有するアミノ樹脂等が挙げられる。
　ベンゾグアナミン骨格を有するアミノ樹脂としては、メチル化ベンゾグアナミン、ブチル化ベンゾグアナミン、メチルブチル化ベンゾグアナミン、エチル化ベンゾグアナミン等が挙げられ、これらのうち、メチル化ベンゾグアナミンが好ましい。
　メラミン骨格を有するアミノ樹脂としては、メチル化メラミン、ブチル化メラミン、ブチルメチル化メラミン等が挙げられ、これらのうち、メチル化メラミンが好ましい。
　触媒（ｃ）は、架橋反応を促進させる架橋反応用触媒である。触媒（ｃ）としては、ジノニルナフタレンスルホン酸、ジノニルナフタレンジスルホン酸、ドデシルベンゼンスルホン酸、パラトルエンスルホン酸、リン酸等が挙げられ、これらのうち、ドデシルベンゼンスルホン酸が好ましい。
　被覆樹脂層形成用樹脂組成物中、架橋剤（ｂ）の含有量は、ポリエステルアミド樹脂（ａ）１００質量部に対し、好ましくは５．０～３０．０質量部、特に好ましくは５．０～２０．０質量部である。被覆樹脂層形成用樹脂組成物中の架橋剤（ｂ）の含有量が上記範囲にあることにより、成形性、耐高温水性、耐溶剤性が良好となる。
　被覆樹脂層形成用樹脂組成物中、触媒（ｃ）の含有量は、ポリエステルアミド樹脂（ａ）及び架橋剤（ｂ）の合計１００質量部に対し、好ましくは０．０５０～０．９０質量部である。被覆樹脂層形成用樹脂組成物中の触媒（ｃ）の含有量が上記範囲にあることにより、成形性、耐高温水性、耐溶剤性が良好となる。
　被覆樹脂層形成用樹脂組成物は、ポリエステルアミド樹脂（ａ）、架橋剤（ｂ）及び触媒（ｃ）以外に、必要に応じて、ワックス、表面調整剤、消泡剤等を含有することができる。
　本発明の樹脂被覆アルミニウム合金板に用いられる被覆樹脂層形成用樹脂組成物、すなわち、ポリエステルアミド樹脂（ａ）、架橋剤（ｂ）、触媒（ｃ）及び必要に応じて含有される成分は、通常、有機溶媒に、溶解又は分散され、溶液状又はペースト状とされて、アルミニウム合金板又は化成皮膜が形成されたアルミニウム合金板の表面に塗布される。
　有機溶媒としては、特に制限されないが、芳香族炭化水素、アルコール等が挙げられる。また、被覆樹脂層形成用樹脂組成物に対する有機溶媒の使用量は、被覆樹脂層形成用樹脂組成物の粘度等により、適宜選択される。
　本発明の樹脂被覆アルミニウム合金板において、被覆樹脂層は、被覆樹脂層形成用樹脂組成物を加熱することにより硬化させたものである。被覆樹脂層形成用樹脂組成物を硬化させる際の硬化温度は、好ましくは２００～２５０℃、特に好ましくは２２０～２４０℃である。
　本発明の樹脂被覆アルミニウム合金板において、被覆樹脂層は、例えば、被覆樹脂層形成用樹脂組成物が、有機溶媒に溶解又は分散された溶液又はペースト状物を、アルミニウム合金板又は化成皮膜が形成されたアルミニウム合金板の表面に塗布し、次いで、乾燥して有機溶媒を除去して塗膜を形成し、次いで、硬化温度で所定の時間加熱することにより、被覆樹脂層形成用樹脂組成物を硬化させることにより形成される。
　本発明の樹脂被覆アルミニウム合金板において、被覆樹脂層形成用樹脂組成物の硬化物のゲル分率は、好ましくは４．０～１４．０％、より好ましくは５．０～１２．０％、特に好ましくは６．０～８．０％である。被覆樹脂層形成用樹脂組成物の硬化物のゲル分率が上記範囲にあることは、主樹脂と架橋剤の架橋反応が適正に進んでいることを示しており、樹脂層が十分な耐高温水性、耐溶剤性を有する状態となる。なお、本発明において、被覆樹脂層形成用樹脂組成物の硬化物のゲル分率は、被覆樹脂層形成用樹脂組成物をアルミニウム合金板上に塗装焼付して硬化させ、その樹脂被覆アルミニウム合金板を８０℃に加熱したメチルエチルケトンに１時間浸漬し、浸漬前後の単位面積当たりの重量減少率を測定することにより求められ、得られる重量減少率がゲル分率であり、以下の操作により測定された値である。
（１）樹脂被覆アルミニウム板の単位面積当たりの樹脂層重量ｘ１（ｇ／ｍ２）を測定する。なお、樹脂層重量については、樹脂被覆アルミニウム板の重量から樹脂被覆に用いたものと同じ材質、厚さ及び寸法のアルミニウム板の重量を差し引いて算出する。
（２）樹脂被覆アルミニウム合金板を８０℃に加熱したメチルエチルケトンに１時間浸漬する。
（３）樹脂被覆アルミニウム合金板を１００℃にて１５分以上乾燥する。
（４）樹脂被覆アルミニウム板の単位面積当たりの樹脂層重量ｘ２（ｇ／ｍ２）を測定する。
（５）以下の式にて、ゲル分率を算出する。
　　　ゲル分率（％）＝（（ｘ１－ｘ２）／ｘ１）×１００
　本発明の樹脂被覆アルミニウム合金板において、被覆樹脂層の厚み（被覆樹脂層形成用樹脂組成物の硬化物の厚み）は、１．０～２０．０μｍ、好ましくは４．０～８．０μｍである。被覆樹脂層形成用樹脂組成物の硬化物の厚みが上記範囲にあることにより、絞り及びしごき成形性が良好となる。一方、被覆樹脂層形成用樹脂組成物の硬化物の厚みが、上記範囲未満だと、環境によっては耐食性が不足し、長期の使用によりアルミニウム合金板が腐食する場合があり、また、上記範囲を超えると、絞り及びしごき成形性が悪くなる。なお、被覆樹脂層の厚みとは、図１中、符号ｔで示す厚みである。
　本発明の樹脂被覆アルミニウム合金板は、被覆樹脂層の形成原料の樹脂として、ポリエステルアミド樹脂（ａ）を用い、架橋剤としてアミノ樹脂を用い、且つ、硬化後の被覆樹脂層を所定の厚みとすることにより、絞り加工時に、被覆樹脂層の割れ又は剥離が発生し難く、成形性が良好となり、且つ、高温多湿環境に曝されても、被覆樹脂層の剥離が発生し難く、耐高温水性が良好となる。
　本発明の樹脂被覆アルミニウム合金板の用途としては、アルミニウム電解コンデンサケース、キャパシタケース等が挙げられる。
　次に、実施例を挙げて本発明を更に具体的に説明するが、これは単に例示であって、本発明を制限するものではない。
（実施例１～５及び比較例１）
（１）アルミニウム合金板
ＪＩＳ　Ａ　３００３、厚さ０．３０ｍｍ、幅２００ｍｍ、長さ３００ｍｍ
（２）化成皮膜の形成
　上記アルミニウム合金板を、市販の弱アルカリ性脱脂剤ファインクリーナー４３７７（日本パーカライジング製、１０ｇ／Ｌ、６５℃）に、１分間浸漬した後、上水で水洗して、脱脂した。次いで、アルサーフ４０１（日本ペイント社製）３０ｇとアルサーフ４１（日本ペイント社製）３ｇの混合液に、上水を加え、全量を１リットルとした、４２℃の溶液に、脱脂したアルミニウム合金板を、２０秒間浸漬することにより、リン酸クロメート処理を行い、化成皮膜が形成されたアルミニウム合金板を得た。この時、リン酸クロメート処理の目付け量を、クロム量で２０ｍｇ／ｍ２とした。
（３）被覆樹脂層形成用樹脂組成物塗料の調製
　表１に示す主樹脂、架橋剤及び触媒を、表１に示す配合量で有機溶媒に混合し、被覆樹脂層形成用樹脂組成物塗料を調製した。
・ポリエステルアミド樹脂（主樹脂）
　二塩基酸として、重合脂肪酸（炭素数１８、カルボキシル基数１、不飽和結合数１～３の不飽和肪酸の二量化物）を、ジオール化合物として、ダイマージオール（炭素数１８、カルボキシル基数１、不飽和結合数１～３の不飽和肪酸を二量化したダイマー酸を水添し、更に還元して得られるジオール）を、ジアミン化合物として、ヘキサメチレンジアミンを用いて重合させたもの、エステル成分とアミド成分の共重合比（モル比）が４０：６０、重量平均分子量が２０，０００、赤外分光分析（ＩＲ）におけるＸ１／Ｘ値が１．２、Ｘ２／Ｘ値が０．９、Ｘ２／Ｘ１値が０．７６
・ポリエステル樹脂（主樹脂）
　市販のポリエステル樹脂（バイロン社製、ＲＶ６００）を用いた。
・ベンゾグアナミン系アミノ樹脂（架橋剤）：メチル化ベンゾグアナミン
・メラミン系アミノ樹脂（架橋剤）：メチル化メラミン
・触媒：ドデシルベンゼンスルホン酸（ＤＤＢＳＡ）
・有機溶媒：トルエン／イソプロピルアルコール＝７／３
＜赤外分光分析（ＩＲ）＞
　ポリエステルアミド樹脂（ａ）を赤外分光分析（ＩＲ）し、２９２５ｃｍ－１付近の吸収ピークの高さをＸ、１７３５ｃｍ－１付近の吸収ピークの高さをＸ１、１６４５ｃｍ－１付近の吸収ピークの高さをＸ２として求めた。
＜樹脂組成物の硬化物のゲル分率＞
　先ず、樹脂被覆アルミニウム板の単位面積当たりの樹脂層重量ｘ１（ｇ／ｍ２）を測定した。なお、樹脂層重量については、樹脂被覆アルミニウム板の重量から樹脂被覆に用いたものと同じ材質、厚さ及び寸法のアルミニウム板の重量を差し引いて算出した。
　次いで、樹脂被覆アルミニウム合金板を８０℃に加熱したメチルエチルケトンに１時間浸漬した後、樹脂被覆アルミニウム合金板を１００℃にて１５分以上乾燥した。
　次いで、樹脂被覆アルミニウム板の単位面積当たりの樹脂層重量ｘ２（ｇ／ｍ２）を測定し、以下の式にて、ゲル分率を算出した。
　　　ゲル分率（％）＝（（ｘ１－ｘ２）／ｘ１）×１００
（４）被覆樹脂層の形成
　表１に示す配合量の被覆樹脂層形成用樹脂組成物塗料を、化成皮膜を形成させたアルミニウム合金板に、バーコーターにて塗布し、次いで、焼付け硬化させて塗膜を形成させた。このとき、被覆樹脂層形成用樹脂組成物塗料の塗布量は、硬化後の被覆樹脂層の厚みが表１に示す厚みとなるように調節した。
　次いで、被覆樹脂層形成用樹脂組成物の塗膜を形成させたアルミニウム合金板を、空気炉にてアルミニウム合金の温度が２４０℃になるまで加熱して、被覆樹脂層形成用樹脂組成物を硬化させて、被覆樹脂層を形成させ、樹脂被覆アルミニウム合金板を製造した。
　次いで、得られた樹脂被覆アルミニウム合金板の成形性及び耐高温水性を評価した。その結果を表１に示す。
＜成形性＞
　樹脂被覆アルミニウム合金板を、アルミニウム板用成形油を用いて、φ１０ｍｍ、高さ２０ｍｍに、それぞれ５個の円筒深絞り成形をした。成形後の側面の樹脂層を目視観察して、５個全部に樹脂層の剥離がなかった場合を「〇」、１個～４個の樹脂層に剥離があった場合を「△」、５個全部に樹脂層の剥離があった場合を「×」とした。
＜耐溶剤性＞
　半田フラックス洗浄液を４０℃に加熱して、秒間超音波洗浄し、浸漬前後の樹脂層外観を比較した。変色がなかった場合を「○」、部分的に変色が発生した場合「△」、全面に変色が発生した場合「×」とした。
＜耐高温水性＞
　樹脂被覆アルミニウム合金板を、プレッシャークッカーを用いて、１２０℃にて加圧水蒸気中４８時間暴露した。試験後の側面の樹脂層を目視観察して、変化がなかった場合を「〇」、変色が発生した場合を「△」、変色しさらに樹脂層に凹凸が発生した場合を「×」とした。
Figure JPOXMLDOC01-appb-T000001
　なお、表１中、触媒量の上段は主樹脂１００質量部に対する質量部であり、下段は主樹脂及びアミノ樹脂の合計を１００質量部としたときの質量部である。また、硬化物のゲル分率とは、被覆樹脂形成用樹脂組成物の硬化物のゲル分率である。
１　　　　　樹脂被覆アルミニウム合金板
２　　　　　アルミニウム合金板（アルミニウム板）
３　　　　　化成皮膜
４　　　　　被覆樹脂層

Claims (12)

  1. 　ポリエステルアミド樹脂（ａ）、架橋剤（ｂ）及び触媒（ｃ）を含有する被覆樹脂層形成用樹脂組成物の硬化物からなる被覆樹脂層を有し、
    　該ポリエステルアミド樹脂（ａ）は、二塩基酸の重合残基と、ジオール化合物の重合残基及びジアミン化合物の重合残基と、を有し、
    　該架橋剤（ｂ）が、アミノ樹脂であり、
    　該被覆樹脂層の厚みが、１．０～２０．０μｍであること、
    を特徴とする樹脂被覆アルミニウム合金板。
  2. 　前記架橋剤（ｂ）が、ベンゾグアナミン骨格を有するアミノ樹脂であることを特徴とする請求項１記載の樹脂被覆アルミニウム合金板。
  3. 　前記架橋剤（ｂ）が、メチル化ベンゾグアナミンであることを特徴とする請求項２記載の樹脂被覆アルミニウム合金板。
  4. 　前記ポリエステルアミド樹脂（ａ）を構成する二塩基酸の重合残基が、重合脂肪酸の重合残基であることを特徴とする請求項１～３いずれか１項記載の樹脂被覆アルミニウム合金板。
  5. 　前記ポリエステルアミド樹脂（ａ）におけるエステル成分とアミド成分の共重合比（モル比）が、１０：９０～９０：１０であることを特徴とする請求項１～４いずれか１項記載の樹脂被覆アルミニウム合金板。
  6. 　前記ポリエステルアミド樹脂（ａ）の赤外分光分析（ＩＲ）において、２９２５ｃｍ－１付近の吸収ピークの高さをＸ、１７３５ｃｍ－１付近の吸収ピークの高さをＸ１、１６４５ｃｍ－１付近の吸収ピークの高さをＸ２としたとき、以下の式（１）及び（２）：
    　　　０．５≦（Ｘ１／Ｘ）≦２．０　　　　（１）
    　　　０．５≦（Ｘ２／Ｘ）≦３．０　　　　（２）
    を満たすことを特徴とする請求項１～５いずれか１項記載の樹脂被覆アルミニウム合金板。
  7. 　前記ポリエステルアミド樹脂（ａ）の赤外分光分析（ＩＲ）において、１７３５ｃｍ－１付近の吸収ピークの高さＸ１に対する１６４５ｃｍ－１付近の吸収ピークの高さＸ２の比（Ｘ２／Ｘ１）が、０．２５～６．０であることを特徴とする請求項１～５いずれか１項記載の樹脂被覆アルミニウム合金板。
  8. 　前記架橋剤（ｂ）の含有量が、前記ポリエステルアミド樹脂（ａ）１００質量部に対し、５．０～３０．０質量部であることを特徴とする請求項１～７いずれか１項記載の樹脂被覆アルミニウム合金板。
  9. 　前記触媒（ｃ）の含有量が、前記ポリエステルアミド樹脂（ａ）及び前記架橋剤（ｂ）の合計１００質量部に対し、０．０５０～０．９０質量部であることを特徴とする請求項１～８いずれか１項記載の樹脂被覆アルミニウム合金板。
  10. 　前記触媒（ｃ）が、ドデシルベンゼンスルホン酸であることを特徴とする請求項１～９いずれか１項記載の樹脂被覆アルミニウム合金板。
  11. 　前記被覆樹脂層形成用樹脂組成物の硬化物のゲル分率が、４．０～１４．０％であることを特徴とする請求項１～１０いずれか１項記載の樹脂被覆アルミニウム合金板。
  12. 　前記樹脂被覆アルミニウム合金板が、アルミニウム合金板と、該アルミニウム合金板の表面に形成されている化成皮膜と、該化成皮膜の表面に形成されている前記被覆樹脂層と、からなることを特徴とする請求項１～１１いずれか１項記載の樹脂被覆アルミニウム合金板。
PCT/JP2022/015045 2021-03-31 2022-03-28 樹脂被覆アルミニウム合金板 Ceased WO2022210554A1 (ja)