WO2022186184A1 - Film stratifié et procédé de fabrication de film stratifié - Google Patents
Film stratifié et procédé de fabrication de film stratifié Download PDFInfo
- Publication number
- WO2022186184A1 WO2022186184A1 PCT/JP2022/008541 JP2022008541W WO2022186184A1 WO 2022186184 A1 WO2022186184 A1 WO 2022186184A1 JP 2022008541 W JP2022008541 W JP 2022008541W WO 2022186184 A1 WO2022186184 A1 WO 2022186184A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- resin sheet
- less
- film
- release layer
- resin
- Prior art date
Abstract
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2023503853A JPWO2022186184A1 (fr) | 2021-03-02 | 2022-03-01 | |
CN202280017754.0A CN116897109A (zh) | 2021-03-02 | 2022-03-01 | 层叠薄膜和层叠薄膜的制造方法 |
KR1020237032990A KR20230152102A (ko) | 2021-03-02 | 2022-03-01 | 적층 필름 및 적층 필름의 제조 방법 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2021032835 | 2021-03-02 | ||
JP2021-032835 | 2021-03-02 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022186184A1 true WO2022186184A1 (fr) | 2022-09-09 |
Family
ID=83154749
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2022/008541 WO2022186184A1 (fr) | 2021-03-02 | 2022-03-01 | Film stratifié et procédé de fabrication de film stratifié |
Country Status (4)
Country | Link |
---|---|
JP (1) | JPWO2022186184A1 (fr) |
KR (1) | KR20230152102A (fr) |
CN (1) | CN116897109A (fr) |
WO (1) | WO2022186184A1 (fr) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2024019038A1 (fr) * | 2022-07-20 | 2024-01-25 | 東洋紡株式会社 | Film stratifié et procédé pour produire un film stratifié |
WO2024019039A1 (fr) * | 2022-07-20 | 2024-01-25 | 東洋紡株式会社 | Film stratifié et procédé de production de film stratifié |
WO2024019037A1 (fr) * | 2022-07-20 | 2024-01-25 | 東洋紡株式会社 | Rouleau de film stratifié et procédé de fabrication de rouleau de film stratifié |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2009227735A (ja) * | 2008-03-19 | 2009-10-08 | Fujifilm Corp | 防眩性フィルム及びその製造方法 |
JP2011002820A (ja) * | 2009-05-21 | 2011-01-06 | Daicel Chemical Industries Ltd | ニュートンリング防止フィルム及びタッチパネル |
WO2019082664A1 (fr) * | 2017-10-25 | 2019-05-02 | 株式会社ダイセル | Film tactile, son procédé de production, article moulé, et procédé destiné à améliorer l'aptitude au glissement des doigts |
WO2021005823A1 (fr) * | 2019-07-10 | 2021-01-14 | 株式会社村田製作所 | Condensateur à film et film pour condensateur à film |
Family Cites Families (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP5774857B2 (ja) | 2011-01-14 | 2015-09-09 | ユニチカ株式会社 | 易滑性ポリエステルフィルムおよびその製造方法 |
JP6085185B2 (ja) | 2013-02-06 | 2017-02-22 | 株式会社ダイセル | 燃料電池製造用離型フィルム及び積層体並びに燃料電池の製造方法 |
JP6340855B2 (ja) | 2014-03-22 | 2018-06-13 | 三菱ケミカル株式会社 | フィルム積層体 |
JP6981205B2 (ja) | 2017-11-24 | 2021-12-15 | コニカミノルタ株式会社 | 光学フィルムおよび偏光板 |
KR102190888B1 (ko) | 2020-04-07 | 2020-12-15 | 삼성전자 주식회사 | 디스플레이장치 및 그 제어방법 |
-
2022
- 2022-03-01 JP JP2023503853A patent/JPWO2022186184A1/ja active Pending
- 2022-03-01 KR KR1020237032990A patent/KR20230152102A/ko unknown
- 2022-03-01 CN CN202280017754.0A patent/CN116897109A/zh active Pending
- 2022-03-01 WO PCT/JP2022/008541 patent/WO2022186184A1/fr active Application Filing
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2009227735A (ja) * | 2008-03-19 | 2009-10-08 | Fujifilm Corp | 防眩性フィルム及びその製造方法 |
JP2011002820A (ja) * | 2009-05-21 | 2011-01-06 | Daicel Chemical Industries Ltd | ニュートンリング防止フィルム及びタッチパネル |
WO2019082664A1 (fr) * | 2017-10-25 | 2019-05-02 | 株式会社ダイセル | Film tactile, son procédé de production, article moulé, et procédé destiné à améliorer l'aptitude au glissement des doigts |
WO2021005823A1 (fr) * | 2019-07-10 | 2021-01-14 | 株式会社村田製作所 | Condensateur à film et film pour condensateur à film |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2024019038A1 (fr) * | 2022-07-20 | 2024-01-25 | 東洋紡株式会社 | Film stratifié et procédé pour produire un film stratifié |
WO2024019039A1 (fr) * | 2022-07-20 | 2024-01-25 | 東洋紡株式会社 | Film stratifié et procédé de production de film stratifié |
WO2024019037A1 (fr) * | 2022-07-20 | 2024-01-25 | 東洋紡株式会社 | Rouleau de film stratifié et procédé de fabrication de rouleau de film stratifié |
Also Published As
Publication number | Publication date |
---|---|
CN116897109A (zh) | 2023-10-17 |
JPWO2022186184A1 (fr) | 2022-09-09 |
KR20230152102A (ko) | 2023-11-02 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2022163569A1 (fr) | Film stratifié et procédé de fabrication de film stratifié | |
WO2022186184A1 (fr) | Film stratifié et procédé de fabrication de film stratifié | |
CN111527136B (zh) | 陶瓷生片制造用脱模膜 | |
JP6962217B2 (ja) | セラミックグリーンシート製造用離型フィルム | |
JP2022025703A (ja) | 積層フィルム | |
WO2000021752A1 (fr) | Film a couche detachable | |
JP2022167896A (ja) | セラミックグリーンシート製造用離型フィルム | |
KR101600104B1 (ko) | 이형 필름 | |
KR102453649B1 (ko) | 세라믹 그린 시트 제조용 이형 필름 | |
WO2009088094A1 (fr) | Film lubrifiant de moule | |
JP5346640B2 (ja) | 離型フィルム | |
JP5378703B2 (ja) | 離型フィルム | |
WO2024019038A1 (fr) | Film stratifié et procédé pour produire un film stratifié | |
WO2024019039A1 (fr) | Film stratifié et procédé de production de film stratifié | |
WO2024019037A1 (fr) | Rouleau de film stratifié et procédé de fabrication de rouleau de film stratifié | |
JP7106912B2 (ja) | セラミックグリーンシート製造用離型フィルム | |
JP6973054B2 (ja) | セラミックグリーンシート製造用離型フィルム | |
JP7188536B2 (ja) | セラミックグリーンシート製造用離型フィルム | |
JP7188537B2 (ja) | セラミックグリーンシート製造用離型フィルム | |
JP7188535B2 (ja) | セラミックグリーンシート製造用離型フィルム | |
JP7306515B2 (ja) | セラミックグリーンシート製造用離型フィルム | |
JP7306514B2 (ja) | セラミックグリーンシート製造用離型フィルム | |
JP7306516B2 (ja) | セラミックグリーンシート製造用離型フィルム | |
JP7327554B2 (ja) | セラミックグリーンシート製造用離型フィルム | |
KR102333059B1 (ko) | 세라믹 그린시트 제조용 이형 필름 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 22763239 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2023503853 Country of ref document: JP Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 202280017754.0 Country of ref document: CN |
|
ENP | Entry into the national phase |
Ref document number: 20237032990 Country of ref document: KR Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 22763239 Country of ref document: EP Kind code of ref document: A1 |