WO2022158568A1 - 塗布液及びその製造方法、膜付基材の製造方法 - Google Patents

塗布液及びその製造方法、膜付基材の製造方法 Download PDF

Info

Publication number
WO2022158568A1
WO2022158568A1 PCT/JP2022/002186 JP2022002186W WO2022158568A1 WO 2022158568 A1 WO2022158568 A1 WO 2022158568A1 JP 2022002186 W JP2022002186 W JP 2022002186W WO 2022158568 A1 WO2022158568 A1 WO 2022158568A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating liquid
film
weight
titanium oxide
dispersion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2022/002186
Other languages
English (en)
French (fr)
Japanese (ja)
Inventor
夕子 箱嶋
宏忠 荒金
良 村口
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JGC Catalysts and Chemicals Ltd
Original Assignee
JGC Catalysts and Chemicals Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JGC Catalysts and Chemicals Ltd filed Critical JGC Catalysts and Chemicals Ltd
Priority to JP2022548251A priority Critical patent/JP7169493B1/ja
Publication of WO2022158568A1 publication Critical patent/WO2022158568A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Links

Classifications

    • BPERFORMING OPERATIONS; TRANSPORTING
    • B05SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05DPROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D3/00Pretreatment of surfaces to which liquids or other fluent materials are to be applied; After-treatment of applied coatings, e.g. intermediate treating of an applied coating preparatory to subsequent applications of liquids or other fluent materials
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B05SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05DPROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
    • B05D7/00Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials
    • B05D7/24Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials for applying particular liquids or other fluent materials
    • CCHEMISTRY; METALLURGY
    • C09DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09DCOATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D201/00Coating compositions based on unspecified macromolecular compounds
    • CCHEMISTRY; METALLURGY
    • C09DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09DCOATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D201/00Coating compositions based on unspecified macromolecular compounds
    • C09D201/02Coating compositions based on unspecified macromolecular compounds characterised by the presence of specified groups, e.g. terminal or pendant functional groups
    • C09D201/10Coating compositions based on unspecified macromolecular compounds characterised by the presence of specified groups, e.g. terminal or pendant functional groups containing hydrolysable silane groups
    • CCHEMISTRY; METALLURGY
    • C09DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09DCOATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D7/00Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
    • C09D7/40Additives
    • C09D7/60Additives non-macromolecular
    • C09D7/61Additives non-macromolecular inorganic
    • CCHEMISTRY; METALLURGY
    • C09DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09DCOATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D7/00Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
    • C09D7/40Additives
    • C09D7/60Additives non-macromolecular
    • C09D7/63Additives non-macromolecular organic

Definitions

  • the present invention relates to a coating liquid for forming a thick film with a high refractive index on a substrate.
  • Patent Document 2 It is also known to prepare a coating liquid for forming a high refractive index film using a resin having an adamantane skeleton with a high refractive index (see Patent Document 2, for example).
  • JP 2016-194008 A Japanese Patent Publication No. 2019-510119
  • a high refractive index film can be formed on a substrate using the coating liquid of Patent Document 1.
  • the coating film tends to shrink during film formation, a thick film of 150 nm or more cannot be formed.
  • the coating liquid of Patent Document 2 contains a resin with a high refractive index, the density of the formed film is low, so only a refractive index of about 1.7 can be obtained.
  • An object of the present invention is to provide a coating liquid with a high refractive index and capable of forming a thick film.
  • the ratio of these components in the solid content is preferably 50 to 75% by weight for the titanium-containing oxide, 10 to 35% by weight for the adamantane derivative, and 10 to 25% by weight for the organic binder.
  • the organic binder preferably has an alkoxy group.
  • the method for producing the coating liquid includes a step of preparing a dispersion of the titanium-containing oxide (preparing step), and a step of mixing the dispersion of the titanium-containing oxide and an organic binder to prepare a mixture (mixing step). , and a step of adding an adamantane derivative (adding step).
  • the coating liquid of the present invention contains a titanium-containing oxide (hereinafter referred to as titanium oxide), an organic binder and an adamantane derivative.
  • titanium oxide titanium-containing oxide
  • organic binder organic binder
  • adamantane derivative a film in which the adamantane derivative and the organic binder are densely packed around the titanium oxide is formed. That is, since the film becomes dense, the density of the film increases. Therefore, the refractive index and transparency of the film are increased.
  • the refractive index of titanium oxide Since the refractive index of titanium oxide is high, the refractive index of the film increases when the titanium oxide is 50% by weight or more of the solid content contained in the coating liquid. If the titanium oxide is 75% by weight or less of the solids contained in the coating liquid, the titanium oxide is easily dispersed in the coating liquid and the film.
  • the organic binder is 25% by weight or less of the solid content in the coating liquid, the content of titanium oxide and adamantane derivative is relatively high. Titanium oxide and adamantane derivatives have a higher refractive index than the organic binder, so a high content of these will increase the refractive index of the film.
  • the organic binder accounts for 10% by weight or more of the solid content in the coating liquid, the compatibility between the titanium oxide and the adamantane derivative is enhanced. Therefore, the titanium oxide is easily dispersed in the coating liquid. Therefore, the film is easily formed in a state in which the titanium oxide is dispersed, and the titanium oxide can be uniformly present in the film. As a result, the film becomes more transparent. Also, when a film is formed in a state where titanium oxide is dispersed, voids in the film are reduced as compared with the case where titanium oxide is agglomerated, so the film becomes denser.
  • the solid content of the coating liquid is 50 to 75% by weight
  • the adamantane derivative is 10 to 35% by weight
  • the organic binder is 10 to 25% by weight
  • a component with a high refractive index titanium oxide and adamantane derivative
  • titanium oxide easily disperses in the coating solution or film.
  • the content of titanium oxide is 2.5 to 4.0, and the content of adamantane derivative is 0.5 to 1.5. If it is in the range of , the film will be dense. In particular, it is preferable that the content of titanium oxide is in the range of 3.0 to 3.5 and the content of adamantane derivative is in the range of 0.8 to 1.3.
  • the solid content in the coating liquid When the solid content in the coating liquid is 5% by weight or more, it becomes easier to form a thick film of 150 nm or more with a uniform thickness. 10% by weight or more is more preferable. Further, when the solid content in the coating liquid is 50% by weight or less, the titanium oxide tends to disperse in the film. 45% by weight or less is more preferable.
  • the organic binder has an alkoxy group
  • compatibility with titanium oxide increases. Further, the alkoxy group is hydrolyzed in the coating liquid to undergo a dehydration condensation reaction with the OH group of the titanium oxide (hereinafter, hydrolysis and dehydration condensation are collectively referred to as coupling reaction). That is, titanium oxide chemically bonds with the organic binder. Therefore, the film becomes dense. Also, the hardness of the film increases. Since the titanium oxide chemically bonded to the organic binder has high compatibility with the adamantane derivative and the organic solvent, it is easily dispersed in the coating liquid and the film.
  • the organic binder is easily hydrolyzed. That is, it easily undergoes a coupling reaction with titanium oxide. Further, when a catalyst that promotes hydrolysis of the alkoxy group is added to the coating liquid, the coupling reaction is facilitated.
  • the organic binder When the organic binder has two or more alkoxy groups, the organic binder that has not undergone coupling reaction (unreacted organic binder) in the coating liquid is polymerized. As a result, oligomers of the organic binder are formed. The oligomers are believed to have a polarity intermediate between titanium oxides and adamantane derivatives. When such an oligomer is contained in the coating liquid, the solid content is easily dispersed in the coating liquid, resulting in a dense film. At this time, if an organic binder having 2 to 3 alkoxy groups is used, the compatibility between the titanium oxide and the adamantane derivative is enhanced. Therefore, the solid content is easily dispersed in the film during film formation. In particular, when an organic binder having three alkoxy groups is used, the oligomer becomes moderately polar. Therefore, the compatibility between the titanium oxide and the adamantane derivative is enhanced.
  • the compatibility between the titanium oxide and the adamantane derivative increases.
  • the amount of the monomer is 10% or less of the total amount of the unreacted organic binder, the organic binder is difficult to volatilize during film formation, and a dense film can be formed.
  • the molecular weight of the oligomer is 5000 or less, the strength of the film and the adhesion of the film to the substrate are increased.
  • the molecular weight is in the range of 500 to 5000, the compatibility between the titanium oxide and the adamantane derivative is high. More preferably, the molecular weight ranges from 1,500 to 4,000.
  • the organic binder having an alkoxy group further has a (meth)acrylate group
  • the (meth)acrylate groups will bond together when irradiated with ultraviolet rays, so the film can be cured at a low temperature.
  • the (meth)acrylate groups of the organic binder are bonded to the (meth)acrylate groups of other solids during curing, resulting in a dense film.
  • Oligomers formed from organic binders with alkoxy groups have multiple (meth)acrylate groups. Upon curing, such oligomers combine with multiple solids, resulting in a denser film.
  • the organosilicon compound can be represented by the general formula (RO) m Si(Y) 4-m .
  • R is Me or Et.
  • m represents an integer of 1 to 4;
  • Y is an organic compound having a (meth)acrylate group.
  • the adamantane derivative of the monomer When the adamantane derivative of the monomer is used, the adamantane derivative can be polymerized with the solid content in the coating liquid, so a denser film can be obtained. Also, monomers are more likely to shrink than oligomers or polymers during curing. Therefore, the film becomes dense.
  • the adamantane derivative has two or more (meth)acrylate groups in the molecule, it can be polymerized with other solids having two or more (meth)acrylate groups.
  • an adamantane derivative having two (meth)acrylate groups has less steric hindrance than three or more (meth)acrylate groups. Therefore, when such an adamantane derivative is used, the film becomes dense.
  • (meth)acrylate groups are bonded to the 1- and 3-positions of the adamantane skeleton, the steric hindrance of the adamantane derivative is further reduced.
  • adamantane derivative does not have a substituent other than a (meth)acrylate group, steric hindrance is reduced. Moreover, when the molecular weight of the adamantane derivative is 350 or less, steric hindrance is reduced.
  • a precursor of titanium oxide may be contained in the coating liquid instead of titanium oxide.
  • precursors include monomers and oligomers.
  • the precursor is titanium alkoxide, it will be hydrolyzed and condensed when the coating film is heated and dried to form titanium oxide. Since the organic binder having an alkoxy group hydrolyzes and condenses with titanium alkoxide, the film becomes dense.
  • the coating liquid contains an organic solvent
  • the solid content tends to disperse in the coating liquid.
  • Such a coating liquid can be easily applied to the substrate.
  • the content of the organic solvent is 50% by weight or more
  • the titanium oxide is easily dispersed in the coating liquid or the film. More preferably, the content is 60% by weight or more.
  • the content of the organic solvent is 95% by weight or less, it becomes easy to form a film having a thickness of 150 nm or more with a uniform thickness. 90% by weight or less is more preferable.
  • the coating liquid can be dried slowly. Therefore, the titanium oxide is easily dispersed uniformly in the film.
  • the coating liquid can be dried at a low temperature of substantially 120° C. or less in a few minutes, thereby increasing productivity.
  • the organic solvent has an ester bond, an ether bond, or a ketone group
  • the adamantane derivative can be dispersed in the coating liquid, and the surface of the film becomes smooth. If the organic solvent has two or more of these bonds or functional groups, the solid content will be more easily dispersed in the coating liquid. Two or more of the same type may be used, or one or more of each of two different types may be used. Organic solvents having three are more preferred.
  • organic solvents examples include propylene glycol monomethyl ether (PGME) and propylene glycol monomethyl ether acetate (PGMEA). Among them, PGMEA is preferable.
  • Curing agents and surface conditioners are added to the coating liquid as necessary.
  • the curing agent is a photopolymerization initiator
  • the film can be formed at a low temperature.
  • an acylphosphine oxide-based photopolymerization initiator is used, curing of the film proceeds efficiently and the film becomes dense.
  • the content of the photopolymerization initiator is 2 parts by mass or more with respect to 100 parts by mass of the adamantane derivative, the curing reaction proceeds easily and the hardness of the film increases.
  • the content is 10 parts by mass or less, the ratio of excess polymerization initiator decreases, so polymerization proceeds efficiently.
  • the coating liquid does not contain solids other than titanium oxide, organic binders, adamantane derivatives, and curing agents, the film tends to be dense. At this time, these may include those that have changed over time.
  • the titanium oxide will be described in detail below.
  • the crystal structure of titanium oxide may be anatase, rutile, brookite, or amorphous. A plurality of crystals may be mixed. A portion of the titanium oxide may be amorphous.
  • the titanium oxide contains 80% by weight or more of titanium oxide in terms of TiO 2 concentration, the refractive index of the film increases. 90% by weight or more is more preferable, and 95% by weight or more is even more preferable.
  • particulate titanium oxide When the titanium oxide is particulate (hereinafter, particulate titanium oxide is simply referred to as particles), the film tends to be dense. Moreover, it is easy to form a thick film.
  • the crystallite diameter is preferably 1 nm or more, more preferably 5 nm or more.
  • the haze of the film becomes low. 50 nm or less is more preferable.
  • the particle diameter of the particles is 100 nm or less, the haze of the film becomes low.
  • the particles contain an inorganic component other than titanium oxide, they will be easily dispersed in the coating liquid.
  • inorganic components such as alumina, silica, zirconia, and tin oxide are contained in the particles in an amount of 0.5 to 10.0% by weight in terms of Al 2 O 3 , SiO 2 , ZrO 2 , and SnO 2 , respectively
  • the particles are added to the coating liquid. easily dispersed.
  • a range of 0.5 to 6.0% by weight is more preferred.
  • titanium oxide containing 1 to 3% by weight of tin oxide in terms of SnO 2 tends to form particles.
  • particles containing 0.5 to 1.5% by weight of alumina in terms of Al 2 O 3 easily disperse in the solvent.
  • the particles when the particles are treated with 1 to 30 parts by mass of a surface treatment agent with respect to 100 parts by mass of the particles, the particles become easier to disperse in the organic solvent. More preferably, the particles are treated with 5 to 22 parts by mass of the surface treatment agent.
  • the surface treatment agent having an alkoxy group easily undergoes a coupling reaction with the particle surface, the particles are easily dispersed in the organic solvent. The more alkoxy groups, the more likely the coupling reaction will occur on the particle surface. Surface treatment agents having 3 to 4 alkoxy groups are preferred, and surface treatment agents having 4 alkoxy groups are more preferred.
  • the alkoxy group is a methoxy group or an ethoxy group, it is easily hydrolyzed. That is, the smaller the molecular weight of the alkyl group in the alkoxy group, the easier the hydrolysis of the alkoxy group.
  • Examples of surface treatment agents include silicon compounds, titanium compounds, zirconium compounds, and aluminum compounds.
  • the surface treatment agent can be represented by the general formula (RO) n M(X) 4-n .
  • n is an integer of 1-4.
  • M represents either Si, Ti, Zr or Al.
  • R is Me or Et.
  • the surface treatment agent is a silicon compound, it is industrially easy to handle.
  • a dispersion of titanium oxide is prepared (preparation step).
  • a dispersion of titanium oxide and an organic binder are mixed to prepare a mixture (mixing step).
  • An organic binder may be mixed in the preparation step.
  • a coating liquid is obtained by adding an adamantane derivative to the mixture (adding step).
  • a dispersion of titanium oxide is prepared.
  • a dispersion of titanium-containing oxide particles (hereinafter referred to as titanium oxide particles) was prepared.
  • a compound containing titanium is neutralized in an aqueous solution to prepare a slurry.
  • the prepared slurry can be washed with water to remove excess salt.
  • a hydrogen peroxide solution is added to the slurry to prepare an aqueous peroxotitanic acid solution. After that, it is preferable to carry out a dealkalization treatment.
  • a dispersion of titanium oxide particles having a crystallite size of several nanometers to several tens of nanometers can be obtained.
  • Grain growth can be controlled by adding an inorganic component other than titanium oxide before heating.
  • the particles are easily dispersed in the coating liquid.
  • the amount of the inorganic component to be added is preferably an amount corresponding to the concentration of the inorganic component in the particles described above. By reducing the amount added, the proportion of titanium oxide in the particles can be increased.
  • the prepared dispersion of titanium oxide may further contain an oxide other than titanium oxide.
  • the surface of the particles can be treated by adding the surface treating agent to the dispersion of the particles.
  • the surface-treated particles are easier to disperse in organic solvents.
  • the treatment amount of the surface treatment agent is 20 to 85 parts by mass with respect to 100 parts by mass of the particles (3 to 30 parts by mass in terms of oxide ⁇ in terms of SiO2 if the surface treatment agent is a silicon compound ⁇ ). is easily dispersed in organic solvents.
  • a surface treatment agent When a surface treatment agent is added to an aqueous dispersion of particles, aggregation of the surface treatment agent is suppressed by adding an organic solvent. Therefore, the surfaces of the particles are easily uniformly treated with the surface treatment agent. At this time, if the organic solvent to be added is alcohol, aggregation of the surface treatment agent is further suppressed. Also, alcohol is easily mixed with water.
  • the solvent of the dispersion is an organic solvent
  • the aggregation of the organic binder that is mixed later is suppressed.
  • the solvent of the titanium oxide dispersion is water
  • the organic solvent is alcohol
  • a replacement method a method of removing water (dehydrating) after adding an organic solvent can be mentioned. Methods of dehydration include methods such as ultrafiltration and distillation.
  • the titanium oxide is particles, the solvent is easily replaced if the particles are treated with a surface treatment agent.
  • a dispersion liquid of the precursor of titanium oxide may be prepared and used for preparing the coating liquid.
  • ⁇ Mixing process> In this step, a dispersion of titanium oxide and an organic binder are mixed to prepare a mixture. At this time, by using an organic binder having an alkoxy group, the organic binder can undergo a coupling reaction with titanium oxide. The compatibility between the titanium oxide that has undergone the coupling reaction and the organic solvent is high. Unreacted organic binders are hydrolyzed and condensed to form oligomers. When the oligomer is contained in the coating liquid, the compatibility between the titanium oxide and the organic solvent is further enhanced.
  • the hydrolysis reaction proceeds by maintaining the temperature of the mixture at 40°C or higher.
  • the holding temperature is preferably 45°C or higher.
  • holding for 1 hour or more facilitates the progress of the reaction.
  • the retention time is preferably 10 hours or longer, more preferably 15 hours or longer.
  • stirring the mixture facilitates uniform condensation reaction of the organic binder with the surface of the titanium oxide.
  • the solvent is alcohol, if the mixture is kept at 60° C. or less, the solvent is difficult to evaporate.
  • the organic binder has an alkoxy group
  • adding a catalyst, water, etc. to the mixture accelerates the hydrolysis reaction of the organic binder. If the catalyst does not easily remain in the film after film formation, the density of the film increases.
  • the hydrolysis reaction is preferably carried out on the alkali side rather than the acid side. Ammonia is suitable as a catalyst that hardly remains and can promote the hydrolysis reaction on the alkaline side.
  • the amount of the organic binder mixed with 100 parts by mass of titanium oxide is 10 parts by mass or more, the titanium oxide is easily dispersed in the organic solvent. 20 parts by mass or more is more preferable, and 30 parts by mass or more is even more preferable.
  • the amount of organic binder mixed with 100 parts by mass of titanium oxide is 50 parts by mass or less, the proportion of titanium oxide in the film increases. 40 parts by mass or less is more preferable.
  • 100 parts by mass is the amount including the surface treatment agent.
  • the adamantane derivative can be dispersed in the organic solvent.
  • the stability of the film formation is enhanced, so that a uniform, dense and smooth surface film can be easily obtained.
  • PGMEA is suitable as such an organic solvent.
  • a coating liquid is obtained by adding an adamantane derivative to the mixture. After the addition, it is preferable to sufficiently stir using an ultrasonic device or the like. Moreover, it is preferable to add a photopolymerization initiator after the addition. Moreover, in this step, a resin other than the adamantane derivative may be further added. At this time, the order of addition does not matter.
  • a substrate with a film can be produced by applying the coating liquid described above onto the substrate.
  • the coating liquid is dried and cured to obtain the base material with the film.
  • coating methods include spin coating, bar coating, gravure coating, and slit coating.
  • drying means volatilizing and removing the solvent. If the drying temperature is 60°C or higher, the drying time will be shortened. Also, the solvent hardly remains in the film. Therefore, a dense film can be obtained. On the other hand, if the drying temperature is 120° C. or less, the base material is difficult to deform. Moreover, it is industrially easy to handle. The drying temperature is more preferably 100° C. or lower, more preferably 80° C. or lower. If the coating film is dried and then cured, production efficiency increases.
  • a dispersion of titanium oxide particles was prepared as follows. 900 g of an aqueous titanium tetrachloride solution containing 2% by weight of titanium tetrachloride in terms of TiO 2 and 352 g of 15% by weight ammonia water were mixed to prepare a white slurry having a pH of 8.6. After filtering this slurry, it was washed with pure water to obtain 360 g of a cake having a solid concentration of 5% by weight. To 360 g of this cake, 411.2 g of 35% by weight hydrogen peroxide solution and 128.8 g of pure water were added to obtain slurry again. By heating this slurry at 80° C.
  • silica sol manufactured by Nikki Shokubai Kasei Co., Ltd.: Cataloid (registered trademark) SN-350
  • aqueous solution was held at 165° C. for 18 hours using an autoclave.
  • the aqueous solution was cooled to room temperature, it was concentrated using an ultrafiltration membrane apparatus to obtain 209.1 g of an aqueous dispersion of titanium oxide having a solid content of 10% by weight.
  • Table 1 shows the composition of the prepared titanium oxide (ratio of inorganic components added).
  • Alkaline components were removed by adding a cation exchange resin (Mitsubishi Chemical Co., Ltd.) to water glass containing 2% by weight of sodium silicate in terms of SiO 2 concentration. After that, the ion exchange resin was separated to obtain a silicic acid aqueous solution of 2% by weight as SiO 2 .
  • a cation exchange resin Mitsubishi Chemical Co., Ltd.
  • aqueous dispersion After adding 640 g of pure water to 160 g of an aqueous dispersion of titanium oxide, the aqueous dispersion was heated to 90°C. This aqueous dispersion, 53.4 g of an aqueous zirconic acid peroxide solution, and 42.4 g of an aqueous silicic acid solution were mixed to obtain a mixture. This mixed solution was stirred at 90° C. for 1 hour and then kept at 165° C. for 18 hours using an autoclave. After the mixed solution was cooled to room temperature, it was concentrated using an ultrafiltration membrane apparatus to obtain 195.2 g of an aqueous dispersion of titanium oxide having a solid content of 10% by weight.
  • a cation exchange resin was added (dealkalized) to 195.2 g of this aqueous dispersion.
  • the ion exchange resin was then separated.
  • 210.1 g of a methanol solution containing 14.9 g of tetraethoxysilane (manufactured by Tama Kagaku Co., Ltd.) having an SiO 2 equivalent concentration of 28.8% by weight dissolved therein the mixture was stirred at 50° C. for 1 hour. After cooling this dispersion to room temperature, the solvent was replaced with methanol using an ultrafiltration membrane. Thereafter, by concentrating the dispersion, 119.2 g of a methanol dispersion of titanium oxide having a solid content concentration of 20% by weight and having a silica layer was obtained. This methanol dispersion was used as a titanium oxide dispersion.
  • the titanium oxide dispersion and the organic binder were mixed. Specifically, a mixture is prepared by mixing 100 g of a methanol dispersion of titanium oxide and 3.68 g of 3-methacryloxypropyltrimethoxysilane (manufactured by Shin-Etsu Chemical Co., Ltd.: KBM-503) as an organic binder. did. The mixture was stirred at 50° C. for 19 hours. After cooling the mixture to room temperature, the solvent in the mixture was replaced with PGMEA using a rotary evaporator to obtain 103.7 g of a mixture having a solid concentration of 20% by weight.
  • PGMEA 3-methacryloxypropyltrimethoxysilane
  • an adamantane derivative was added to prepare a coating liquid.
  • a coating liquid was prepared by adding and stirring 0.36 g of 2,4,6-trimethylbenzoyl)-phenylphosphine oxide (manufactured by IGM Resins B.V.: OMNIRAD (registered trademark) TPO-H).
  • Table 1 A summary of the conditions for preparing the coating liquid is shown in Table 1.
  • a substrate with a transparent film glass substrate
  • a transparent film-coated substrate silicon wafer
  • Table 2 shows the measurement results and evaluation results.
  • transparent film-attached substrates were produced in the same manner, and measured and evaluated.
  • the coating liquid was applied to a glass substrate (made by Hamashin Co., Ltd.: FL glass, thickness: 3 mm, refractive index: 1.51) by a spin coating method. After drying this coating solution at 80° C. for 2 minutes, a high-pressure mercury lamp (manufactured by GS Yuasa: EYEUVMETER) was used to irradiate this coating solution with ultraviolet light under the conditions of 3000 mJ/cm 2 to form a transparent film. A substrate (glass substrate) was prepared.
  • the uncoated glass substrate had a total light transmittance of 99.0% and a haze of 0.1%.
  • the coating liquid was applied to a silicon wafer (manufactured by Matsuzaki Manufacturing Co., Ltd.: 6-inch dummy wafer (P type), thickness: 625 ⁇ m) by spin coating. After drying this coating liquid at 80° C. for 2 minutes, this coating liquid was irradiated with ultraviolet light under the condition of 3000 mJ/cm 2 using an EYEUVMETER to prepare a base material (silicon wafer) with a transparent film. Using spectroscopic ellipsometry (manufactured by Japan Semilab Co., Ltd.: SE-2000), the refractive index and film thickness of the transparent film-attached substrate (silicon wafer) were evaluated.
  • Example 2 A white slurry having a pH of 9.2 was prepared by mixing 2000 g of an aqueous titanium tetrachloride solution containing 7.5% by weight of titanium tetrachloride in terms of TiO 2 and 2000 g of 7.5% by weight of aqueous ammonia. This slurry was filtered and washed with pure water to obtain 1500 g of a cake having a solid content of 10% by weight. 1500 g of this cake was diluted with pure water to 1.5% by weight. After adding 1714 g of 35% by weight hydrogen peroxide water to this cake, it was held at 80° C.
  • a coating liquid was prepared in the same manner as in Example 1, except that in the addition step, the mixture prepared in this example was used and Diapurest ADTM manufactured by Mitsubishi Gas Chemical Company, Inc. was used as the adamantane derivative.
  • Example 3 A coating solution was prepared in the same manner as in Example 2, except that DIAPUREST HADDM manufactured by Mitsubishi Gas Chemical Company, Inc. was used as the adamantane derivative in the addition step.
  • a white slurry having a pH of 8.6 was prepared by mixing 4500 g of an aqueous titanium tetrachloride solution containing 2% by weight of titanium tetrachloride in terms of TiO 2 and 450 g of 15% by weight of ammonia water. This slurry was filtered and washed with pure water to obtain 900 g of a cake having a solid content of 10% by weight. After 900 g of this cake was diluted with pure water to 1.5% by weight and slurried, 1029 g of 35% by weight hydrogen peroxide solution was added to the slurry. By holding this slurry at 80° C.
  • a cation exchange resin was added (dealkalization) to 9000 g of this aqueous solution. After separating the ion exchange resin, 91 g of 1% by weight sodium aluminate aqueous solution was added to the aqueous solution and the aqueous solution was stirred. This aqueous solution was held at 155° C. for 18 hours using an autoclave. After cooling this aqueous solution to room temperature, it was concentrated using an ultrafiltration membrane apparatus to obtain 2275 g of an aqueous dispersion of titanium oxide having a solid concentration of 4% by weight.
  • this aqueous dispersion was stirred at 50° C. for 18 hours to obtain a water/methanol dispersion of titanium oxide.
  • This dispersion was cooled to room temperature, and the solvent of this dispersion was replaced with methanol using an ultrafiltration membrane. By concentrating this dispersion, 555.8 g of a methanol dispersion of titanium oxide having a solid concentration of 20% by weight was obtained.
  • Example 5 A coating solution was prepared in the same manner as in Example 4, except that in the adding step, the amount of the adamantane derivative added was changed to 14.0 g and the amount of the photopolymerization initiator added was changed to 0.84 g.
  • Example 6 To 500 g of the methanol dispersion of titanium oxide of Example 2, 10.0 g of 5% aqueous ammonia was added. After adding 29.9 g of 3-phenyltrimethoxysilane (manufactured by Shin-Etsu Chemical Co., Ltd.: KBM-103), the dispersion was stirred at 50° C. for 18 hours. After cooling this dispersion to room temperature, the solvent of this dispersion was replaced with PGMEA using a rotary evaporator to obtain 529.9 g of a mixture having a solid concentration of 20% by weight.
  • 3-phenyltrimethoxysilane manufactured by Shin-Etsu Chemical Co., Ltd.: KBM-103
  • a coating liquid was prepared in the same manner as in Example 1, except that the mixture prepared in this example was used in the addition step.
  • Example 7 An aqueous dispersion of titanium oxide was obtained in the same manner as in Example 2, except that the potassium stannate aqueous solution was not added and the addition amount of the 1% by weight sodium aluminate aqueous solution was changed to 152 g. However, the amount of the aqueous dispersion of titanium oxide after ultrafiltration was 3788 g.
  • the solid content concentration was 20% by weight in the same manner as in Example 2, except that 17 g of 5% aqueous ammonia was added to 824 g of the methanol dispersion of titanium oxide of this example, and then 49 g of KBM-503 was mixed. 873 g of a mixture of
  • Example 8 Example except that the mixture of Example 4 with a solid content concentration of 20% by weight was used in the addition step, and that the polymerization initiator was changed to 1-hydroxycyclohexylphenyl ketone (manufactured by IGM Resins B.V.: OMNIRAD184). A coating liquid was prepared in the same manner as in 1.
  • Example 9 A coating solution was prepared in the same manner as in Example 4, except that in the addition step, the amount of the adamantane derivative mixed was changed to 8.0 g, and the amount of the photopolymerization initiator added was changed to 0.48 g.
  • Example 10 A coating solution was prepared in the same manner as in Example 1, except that the mixture of Example 2 with a solid content concentration of 20% by weight was used in the addition step.
  • [Comparative Example 1] 403.71 g of methyltriethoxysilane (manufactured by Shin-Etsu Chemical Co., Ltd.: KBM-13) having an SiO 2 equivalent concentration of 44.1% by weight and a solvent (manufactured by Nippon Alcohol Sales Co., Ltd.: Solmix (registered trademark) AP-11) 1061. 55 g were mixed to prepare a mixed liquid. The mixture was stirred for 30 minutes. 322.92 g of 0.1% by weight nitric acid was added to this mixed solution over 30 minutes while stirring. It was then stirred for an additional 30 minutes. The pH of the mixed solution at this time was 2.0.
  • a substrate with a transparent film (glass substrate) was formed as follows, and the total light transmittance and haze were measured. Also, a base material (silicon wafer) with a transparent film was formed in the same manner, and the refractive index and film thickness were evaluated. Table 2 shows the measurement results and evaluation results.
  • This coating liquid was applied onto a glass substrate by a flexographic printing method. After that, this coating liquid was dried at 90° C. for 5 minutes. After irradiating this coating liquid with ultraviolet rays (wavelength: 365 nm) at 3000 mJ/cm 2 , this coating liquid was heated at 230° C. for 30 minutes to prepare a substrate with a transparent film (glass substrate). Using NDH-5000, the total light transmittance and haze of the transparent film-coated substrate (glass substrate) were measured. The uncoated glass substrate had a total light transmittance of 99.0% and a haze of 0.1%.
  • the coating liquid was applied onto a silicon wafer by a flexographic printing method. After that, this coating liquid was dried at 90° C. for 5 minutes. After irradiating this coating liquid with ultraviolet rays (wavelength: 365 nm) at 3000 mJ/cm 2 , this coating liquid was heated at 230° C. for 30 minutes to prepare a base material (silicon wafer) with a transparent film. SE-2000 was used to evaluate the refractive index and film thickness of the base material (silicon wafer) with a transparent film.
  • Example 2 A coating liquid was prepared in the same manner as in Example 1, except that the adamantane derivative was not mixed in the addition step.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Wood Science & Technology (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Inorganic Chemistry (AREA)
  • Paints Or Removers (AREA)
  • Laminated Bodies (AREA)
PCT/JP2022/002186 2021-01-22 2022-01-21 塗布液及びその製造方法、膜付基材の製造方法 Ceased WO2022158568A1 (ja)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2022548251A JP7169493B1 (ja) 2021-01-22 2022-01-21 塗布液及びその製造方法、膜付基材の製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2021-009006 2021-01-22
JP2021009006 2021-01-22

Publications (1)

Publication Number Publication Date
WO2022158568A1 true WO2022158568A1 (ja) 2022-07-28

Family

ID=82548796

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2022/002186 Ceased WO2022158568A1 (ja) 2021-01-22 2022-01-21 塗布液及びその製造方法、膜付基材の製造方法

Country Status (3)

Country Link
JP (1) JP7169493B1 (https=)
TW (1) TW202239880A (https=)
WO (1) WO2022158568A1 (https=)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2026004730A1 (ja) * 2024-06-26 2026-01-02 セントラル硝子株式会社 高屈折率膜の製造方法、高屈折率膜を有する光学部材の製造方法、高屈折率膜及び高屈折率膜を有する光学部材

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009096253A1 (ja) * 2008-01-29 2009-08-06 Konica Minolta Opto, Inc. 光学用複合材料及びそれを用いた光学素子
WO2010071134A1 (ja) * 2008-12-15 2010-06-24 旭硝子株式会社 光硬化性材料の製造方法、光硬化性材料および物品
JP2011053518A (ja) * 2009-09-03 2011-03-17 Olympus Corp 材料組成物およびそれを用いた光学素子
JP2015193757A (ja) * 2014-03-31 2015-11-05 日揮触媒化成株式会社 塗料組成物、ハードコート層およびハードコート層付き光学基材ならびにこれらの製造方法
JP2016194008A (ja) * 2015-03-31 2016-11-17 日揮触媒化成株式会社 透明被膜形成用塗布液、透明被膜形成用塗布液の製造方法、透明被膜付基材、および透明被膜付基材の製造方法
JP2020132857A (ja) * 2019-02-15 2020-08-31 Agc株式会社 硬化性組成物、硬化物及び積層体

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009096253A1 (ja) * 2008-01-29 2009-08-06 Konica Minolta Opto, Inc. 光学用複合材料及びそれを用いた光学素子
WO2010071134A1 (ja) * 2008-12-15 2010-06-24 旭硝子株式会社 光硬化性材料の製造方法、光硬化性材料および物品
JP2011053518A (ja) * 2009-09-03 2011-03-17 Olympus Corp 材料組成物およびそれを用いた光学素子
JP2015193757A (ja) * 2014-03-31 2015-11-05 日揮触媒化成株式会社 塗料組成物、ハードコート層およびハードコート層付き光学基材ならびにこれらの製造方法
JP2016194008A (ja) * 2015-03-31 2016-11-17 日揮触媒化成株式会社 透明被膜形成用塗布液、透明被膜形成用塗布液の製造方法、透明被膜付基材、および透明被膜付基材の製造方法
JP2020132857A (ja) * 2019-02-15 2020-08-31 Agc株式会社 硬化性組成物、硬化物及び積層体

Also Published As

Publication number Publication date
JPWO2022158568A1 (https=) 2022-07-28
JP7169493B1 (ja) 2022-11-10
TW202239880A (zh) 2022-10-16

Similar Documents

Publication Publication Date Title
JP3635692B2 (ja) 低屈折率反射防止膜
KR100635550B1 (ko) 경질 코팅물질 및 이를 포함하는 막
TWI805546B (zh) 被膜形成用組成物及其製造方法
JPWO2000034396A1 (ja) ハードコート剤及びこれを用いたフィルム
JP2008266043A (ja) 透明酸化チタンゾルおよびその製造法
WO1998039253A1 (en) Process for producing composite sols, coating composition, and optical member
WO2014098167A1 (ja) 金属酸化物ナノ粒子とシルセスキオキサンポリマーとの複合体およびその製造方法、ならびにその複合体を用いて製造した複合材料
WO2018181241A1 (ja) 鉄含有ルチル型酸化チタン微粒子分散液の製造方法、鉄含有ルチル型酸化チタン微粒子およびその用途
CN115315412B (zh) 被覆氧化锆的氧化钛微粒的制造方法、被覆氧化锆的氧化钛微粒及其用途
JP3881051B2 (ja) 透明被膜形成用塗布液および被膜付基材
TWI411580B (zh) 氧化鋯一氧化錫之複合物溶膠、塗佈組成物及光學構件
KR102371414B1 (ko) 표면 처리 금속 산화물 졸
JP5337393B2 (ja) 透明酸化チタンオルガノゾルおよびそれを配合したコーティング組成物,光学基材
WO2004050560A1 (ja) 変性された酸化第二スズゾル、酸化第二スズ−酸化ジルコニウム複合体ゾル、コーティング組成物及び光学部材
JP7169493B1 (ja) 塗布液及びその製造方法、膜付基材の製造方法
JPWO2008007708A1 (ja) 変性された酸化ジルコニウム−酸化第二スズ複合体ゾルの製造方法
JP6592897B2 (ja) シリカエアロゲル膜の製造方法
JP5827107B2 (ja) 被膜形成用組成物の調製方法、および太陽電池モジュールの製造方法
KR20170107441A (ko) 저굴절률막 형성용 액 조성물
WO2022210973A1 (ja) ルチル型の結晶構造を有する粒子およびその製造方法、並びに粒子の分散液、塗布液、膜付基材の製造方法
JP7463164B2 (ja) コーティング液
JP2684364B2 (ja) 高屈折率コーティング膜
JPH06212125A (ja) 塗布液、その製造方法および被膜付基材
JP2024146607A (ja) 酸化チタン含有膜形成用の塗布液
JP2025503471A (ja) 高屈折率ナノ結晶およびナノコンポジットの合成、キャッピングおよび分散

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2022548251

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22742687

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 22742687

Country of ref document: EP

Kind code of ref document: A1