WO2022071419A1 - Matériau d'acier - Google Patents

Matériau d'acier Download PDF

Info

Publication number
WO2022071419A1
WO2022071419A1 PCT/JP2021/035934 JP2021035934W WO2022071419A1 WO 2022071419 A1 WO2022071419 A1 WO 2022071419A1 JP 2021035934 W JP2021035934 W JP 2021035934W WO 2022071419 A1 WO2022071419 A1 WO 2022071419A1
Authority
WO
WIPO (PCT)
Prior art keywords
steel material
ferrite
less
cross
section
Prior art date
Application number
PCT/JP2021/035934
Other languages
English (en)
Japanese (ja)
Inventor
聡 志賀
豊 根石
誠 江頭
雄介 河原木
Original Assignee
日本製鉄株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本製鉄株式会社 filed Critical 日本製鉄株式会社
Priority to JP2022554053A priority Critical patent/JP7417171B2/ja
Priority to DE112021005117.2T priority patent/DE112021005117T5/de
Priority to CN202180066500.3A priority patent/CN116209782A/zh
Priority to KR1020237013781A priority patent/KR20230072500A/ko
Publication of WO2022071419A1 publication Critical patent/WO2022071419A1/fr

Abstract

L'invention concerne un matériau d'acier qui présente une excellente usinabilité, une excellente résistance à la fatigue par flexion et une excellente résistance à la fatigue de surface y compris après avoir subi un procédé de carburation sous vide ou analogue, et qui peut supprimer une déformation de traitement thermique. Le matériau d'acier selon un mode de réalisation de la présente invention présente une composition chimique qui contient, en % en masse, de 0,18 à 0,25 % de C, de 0,70 à 2,00 % de Si, de 0,70 à 1,50 % de Mn, de 0,005 à 0,050 % de S, de 0,0050 à 0,0200 % de N, de 0,001 à 0,100 % d'Al, une proportion inférieure ou égale à 0,0050 % d'O, et une proportion inférieure ou égale à 0,030 % de P, la partie restante étant constituée de Fe et d'impuretés, et qui satisfait à la formule (1) et à la formule (2) décrite dans la description. Dans le matériau d'acier, des microstructures dans une section transversale latérale et une section transversale longitudinale contiennent de la ferrite et les parties restantes sont constituées de perlite et/ou de bainite. La valeur moyenne arithmétique du pourcentage de surface de la ferrite est de 50 à 70 %, l'écart-type du pourcentage de surface de la ferrite n'est pas supérieur à 4,0 %, et le rapport de diamètre de particule moyen de la ferrite n'est pas supérieur à 2,00.
PCT/JP2021/035934 2020-09-30 2021-09-29 Matériau d'acier WO2022071419A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
JP2022554053A JP7417171B2 (ja) 2020-09-30 2021-09-29 鋼材
DE112021005117.2T DE112021005117T5 (de) 2020-09-30 2021-09-29 Stahlmaterial
CN202180066500.3A CN116209782A (zh) 2020-09-30 2021-09-29 钢材
KR1020237013781A KR20230072500A (ko) 2020-09-30 2021-09-29 강재

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020164591 2020-09-30
JP2020-164591 2020-09-30

Publications (1)

Publication Number Publication Date
WO2022071419A1 true WO2022071419A1 (fr) 2022-04-07

Family

ID=80950651

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/035934 WO2022071419A1 (fr) 2020-09-30 2021-09-29 Matériau d'acier

Country Status (5)

Country Link
JP (1) JP7417171B2 (fr)
KR (1) KR20230072500A (fr)
CN (1) CN116209782A (fr)
DE (1) DE112021005117T5 (fr)
WO (1) WO2022071419A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011055651A1 (fr) * 2009-11-05 2011-05-12 住友金属工業株式会社 Barre d'acier ou tige en fil métallique laminée à chaud
WO2013031587A1 (fr) * 2011-08-31 2013-03-07 新日鐵住金株式会社 Barre ou fil en acier laminé pour un forgeage à chaud
WO2013111407A1 (fr) * 2012-01-26 2013-08-01 新日鐵住金株式会社 Matériau à base d'acier de cémentation ayant une faible déformation de traitement thermique
JP2013151719A (ja) * 2012-01-25 2013-08-08 Nippon Steel & Sumitomo Metal Corp 熱間鍛造用圧延棒鋼または線材
WO2019182054A1 (fr) * 2018-03-23 2019-09-26 日本製鉄株式会社 Matériau d'acier

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4254816B2 (ja) 2005-08-24 2009-04-15 大同特殊鋼株式会社 浸炭部品
JP5182067B2 (ja) 2008-12-24 2013-04-10 新日鐵住金株式会社 真空浸炭または真空浸炭窒化用の鋼材
WO2010082481A1 (fr) * 2009-01-16 2010-07-22 新日本製鐵株式会社 Acier de cementation, composant cemente, et procede de production d'acier de cementation
JP5776623B2 (ja) * 2012-05-08 2015-09-09 新日鐵住金株式会社 冷間加工性に優れた鋼線材・棒鋼とその製造方法
JP6720643B2 (ja) 2015-03-30 2020-07-08 日本製鉄株式会社 浸炭部品
JP6690464B2 (ja) 2016-08-18 2020-04-28 日本製鉄株式会社 浸炭部品

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011055651A1 (fr) * 2009-11-05 2011-05-12 住友金属工業株式会社 Barre d'acier ou tige en fil métallique laminée à chaud
WO2013031587A1 (fr) * 2011-08-31 2013-03-07 新日鐵住金株式会社 Barre ou fil en acier laminé pour un forgeage à chaud
JP2013151719A (ja) * 2012-01-25 2013-08-08 Nippon Steel & Sumitomo Metal Corp 熱間鍛造用圧延棒鋼または線材
WO2013111407A1 (fr) * 2012-01-26 2013-08-01 新日鐵住金株式会社 Matériau à base d'acier de cémentation ayant une faible déformation de traitement thermique
WO2019182054A1 (fr) * 2018-03-23 2019-09-26 日本製鉄株式会社 Matériau d'acier

Also Published As

Publication number Publication date
JPWO2022071419A1 (fr) 2022-04-07
CN116209782A (zh) 2023-06-02
DE112021005117T5 (de) 2023-07-20
KR20230072500A (ko) 2023-05-24
JP7417171B2 (ja) 2024-01-18

Similar Documents

Publication Publication Date Title
US9200354B2 (en) Rolled steel bar or wire for hot forging
WO2018016505A1 (fr) Acier pour trempe par induction
JP6384627B2 (ja) 高周波焼入れ用鋼
JP5660259B2 (ja) 浸炭部品
WO2019244503A1 (fr) Composant mécanique
WO2020145325A1 (fr) Matériau en acier
WO2018016506A1 (fr) Acier pour durcissement par induction
JP5561436B2 (ja) 熱間鍛造用圧延棒鋼又は線材
WO2018016504A1 (fr) Acier pour trempe par induction
JP5617798B2 (ja) 熱間鍛造用圧延棒鋼又は線材
JP6414385B2 (ja) 浸炭部品
CN107429359B (zh) 热轧棒线材、部件及热轧棒线材的制造方法
WO2022071419A1 (fr) Matériau d'acier
JP2016074951A (ja) 肌焼鋼の製造方法
WO2022071420A1 (fr) Matériau d'acier
JP2013108144A (ja) 熱間鍛造用圧延棒鋼又は線材
WO2020138432A1 (fr) Acier
JP6838508B2 (ja) 真空浸炭用鋼及び浸炭部品
WO2021171494A1 (fr) Matériau en acier
JP2013112826A (ja) 耐摩耗性と面疲労特性に優れた高周波焼入歯車およびその製造方法
WO2021260954A1 (fr) Matériau d'acier et pièce en acier cémenté
JP2022080398A (ja) 鋼材、及び、浸炭鋼部品
JP2022080369A (ja) 鋼材、及び、浸炭鋼部品
JP2024095320A (ja) 窒化部品用素形材及び窒化部品
JP2023056778A (ja) 鋼材、及び、浸炭鋼部品

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21875717

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2022554053

Country of ref document: JP

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 20237013781

Country of ref document: KR

Kind code of ref document: A

122 Ep: pct application non-entry in european phase