WO2021230319A1 - Film barrière aux gaz - Google Patents

Film barrière aux gaz Download PDF

Info

Publication number
WO2021230319A1
WO2021230319A1 PCT/JP2021/018226 JP2021018226W WO2021230319A1 WO 2021230319 A1 WO2021230319 A1 WO 2021230319A1 JP 2021018226 W JP2021018226 W JP 2021018226W WO 2021230319 A1 WO2021230319 A1 WO 2021230319A1
Authority
WO
WIPO (PCT)
Prior art keywords
gas barrier
barrier film
layer
base material
film according
Prior art date
Application number
PCT/JP2021/018226
Other languages
English (en)
Japanese (ja)
Inventor
健太 大沢
Original Assignee
凸版印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 凸版印刷株式会社 filed Critical 凸版印刷株式会社
Priority to JP2022522197A priority Critical patent/JPWO2021230319A1/ja
Publication of WO2021230319A1 publication Critical patent/WO2021230319A1/fr

Abstract

Ce film barrière aux gaz comprend : un substrat dont le composant principal est le propylène et dont une première surface a une dureté de surface inférieure ou égale à 150 Mpa; une couche barrière aux gaz formée sur la première surface ; et une couche de revêtement formée sur la couche barrière aux gaz.
PCT/JP2021/018226 2020-05-14 2021-05-13 Film barrière aux gaz WO2021230319A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2022522197A JPWO2021230319A1 (fr) 2020-05-14 2021-05-13

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-085435 2020-05-14
JP2020085435 2020-05-14

Publications (1)

Publication Number Publication Date
WO2021230319A1 true WO2021230319A1 (fr) 2021-11-18

Family

ID=78524494

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/018226 WO2021230319A1 (fr) 2020-05-14 2021-05-13 Film barrière aux gaz

Country Status (2)

Country Link
JP (1) JPWO2021230319A1 (fr)
WO (1) WO2021230319A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023095915A1 (fr) * 2021-11-29 2023-06-01 凸版印刷株式会社 Film barrière, stratifié et sac d'emballage
WO2023219141A1 (fr) * 2022-05-12 2023-11-16 凸版印刷株式会社 Film barrière contre les gaz, film d'emballage et sac d'emballage
WO2024150748A1 (fr) * 2023-01-11 2024-07-18 Ｔｏｐｐａｎホールディングス株式会社 Stratifié barrière aux gaz, récipient de mise en boîtier et produit de mise en boîtier

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07329258A (ja) * 1994-06-06 1995-12-19 Toray Ind Inc 二軸配向ポリプロピレン複合フイルム及び金属酸化物蒸着二軸配向ポリプロピレン複合フイルム
JPH09290477A (ja) * 1996-03-01 1997-11-11 Toppan Printing Co Ltd バリア性フィルムおよびそれを用いた包装材料
JPH11300911A (ja) * 1998-04-23 1999-11-02 Daicel Chem Ind Ltd バリア性フィルム及びその製造法
US6033786A (en) * 1995-09-27 2000-03-07 Applied Extrusion Technologies, Inc. Metallized films
JP2000202959A (ja) * 1999-01-19 2000-07-25 Dainippon Printing Co Ltd バリア性フィルムおよびそれを使用した積層材
JP2000233476A (ja) * 1999-02-16 2000-08-29 Dainippon Printing Co Ltd 透明バリア性フィルム
JP2001047552A (ja) * 1999-06-03 2001-02-20 Toray Ind Inc 金属化二軸配向ポリプロピレンフィルムおよびそれを用いた積層体
JP2016010889A (ja) * 2014-06-27 2016-01-21 富士フイルム株式会社 ガスバリアフィルムおよび機能性フィルムの製造方法
WO2019087960A1 (fr) * 2017-10-30 2019-05-09 大日本印刷株式会社 Film stratifié, film stratifié barrière et matériau d'emballage barrière aux gaz et corps emballé barrière aux gaz utilisant chacun ledit film stratifié barrière

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07329258A (ja) * 1994-06-06 1995-12-19 Toray Ind Inc 二軸配向ポリプロピレン複合フイルム及び金属酸化物蒸着二軸配向ポリプロピレン複合フイルム
US6033786A (en) * 1995-09-27 2000-03-07 Applied Extrusion Technologies, Inc. Metallized films
JPH09290477A (ja) * 1996-03-01 1997-11-11 Toppan Printing Co Ltd バリア性フィルムおよびそれを用いた包装材料
JPH11300911A (ja) * 1998-04-23 1999-11-02 Daicel Chem Ind Ltd バリア性フィルム及びその製造法
JP2000202959A (ja) * 1999-01-19 2000-07-25 Dainippon Printing Co Ltd バリア性フィルムおよびそれを使用した積層材
JP2000233476A (ja) * 1999-02-16 2000-08-29 Dainippon Printing Co Ltd 透明バリア性フィルム
JP2001047552A (ja) * 1999-06-03 2001-02-20 Toray Ind Inc 金属化二軸配向ポリプロピレンフィルムおよびそれを用いた積層体
JP2016010889A (ja) * 2014-06-27 2016-01-21 富士フイルム株式会社 ガスバリアフィルムおよび機能性フィルムの製造方法
WO2019087960A1 (fr) * 2017-10-30 2019-05-09 大日本印刷株式会社 Film stratifié, film stratifié barrière et matériau d'emballage barrière aux gaz et corps emballé barrière aux gaz utilisant chacun ledit film stratifié barrière

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023095915A1 (fr) * 2021-11-29 2023-06-01 凸版印刷株式会社 Film barrière, stratifié et sac d'emballage
JPWO2023095915A1 (fr) * 2021-11-29 2023-06-01
JP7377425B2 (ja) 2021-11-29 2023-11-10 Ｔｏｐｐａｎホールディングス株式会社 バリアフィルム、積層体及び包装袋
WO2023219141A1 (fr) * 2022-05-12 2023-11-16 凸版印刷株式会社 Film barrière contre les gaz, film d'emballage et sac d'emballage
JP7473088B2 (ja) 2022-05-12 2024-04-23 Ｔｏｐｐａｎホールディングス株式会社 ガスバリアフィルム、包装フィルム及び包装袋
WO2024150748A1 (fr) * 2023-01-11 2024-07-18 Ｔｏｐｐａｎホールディングス株式会社 Stratifié barrière aux gaz, récipient de mise en boîtier et produit de mise en boîtier

Also Published As

Publication number Publication date
JPWO2021230319A1 (fr) 2021-11-18

Similar Documents

Publication Publication Date Title
WO2021230319A1 (fr) Film barrière aux gaz
JP4200972B2 (ja) ガスバリア積層フィルム
JP6251970B2 (ja) ガスバリア性フィルム及びその製造方法、並びにガスバリア性積層体
JP2000233478A (ja) 積層フィルム
WO2021020401A1 (fr) Stratifié formant barrière contre les gaz et matériau d'emballage utilisant celui-ci
WO2022168976A1 (fr) Film barrière aux gaz
JP4924806B2 (ja) ガスバリア性積層体
WO2021112243A1 (fr) Film barrière contre les gaz
JP4978066B2 (ja) ガスバリアフィルム積層体の製造条件の評価方法
JP2020131676A (ja) 高層間密着性ガスバリア蒸着フィルム
JP2001138457A (ja) 積層体
JP2011051277A (ja) ガスバリア性積層フィルム
JP2021109381A (ja) ガスバリアフィルム、これを用いた積層体およびガスバリアフィルムの製造方法
JP2001138446A (ja) 積層体
JP2020040221A (ja) 積層体
WO2024014451A1 (fr) Film barrière aux gaz et stratifié barrière
JP7486894B2 (ja) バリア性積層フィルムおよびバリア性包装体
JP2021091202A (ja) ガスバリアフィルム
WO2024024780A1 (fr) Stratifié, matériau d'emballage et emballage
JP7494015B2 (ja) バリア性積層フィルムおよびバリア性包装体
WO2021024873A1 (fr) Film barrière aux gaz et procédé de fabrication d'un film barrière aux gaz
JP2023085732A (ja) ガスバリアフィルムおよび積層体
JP2023132672A (ja) ガスバリアフィルム
WO2024166966A1 (fr) Stratifié, et sac d'emballage
JP2024017603A (ja) 積層体、包装材料、および包装体

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21803892

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2022522197

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase