WO2021221100A1 - Composition, couche de composition, corps multicouche optique et dispositif d'affichage d'image - Google Patents

Composition, couche de composition, corps multicouche optique et dispositif d'affichage d'image Download PDF

Info

Publication number
WO2021221100A1
WO2021221100A1 PCT/JP2021/016952 JP2021016952W WO2021221100A1 WO 2021221100 A1 WO2021221100 A1 WO 2021221100A1 JP 2021016952 W JP2021016952 W JP 2021016952W WO 2021221100 A1 WO2021221100 A1 WO 2021221100A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
composition
photo
polymer
surfactant
Prior art date
Application number
PCT/JP2021/016952
Other languages
English (en)
Japanese (ja)
Inventor
一茂 中川
大樹 脇阪
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Priority to JP2022518114A priority Critical patent/JP7355928B2/ja
Publication of WO2021221100A1 publication Critical patent/WO2021221100A1/fr

Abstract

La présente invention aborde le problème consistant à fournir : une composition pour la formation d'une sous-couche, ladite composition supprimant l'apparition de rétraction pendant la formation d'une sous-couche, tout en permettant à une couche optiquement anisotrope formée sur la sous-couche de présenter de bonnes propriétés d'alignement de cristaux liquides ; une couche de composition qui est formée à l'aide de cette composition ; et un corps multicouche optique et un dispositif d'affichage d'image, chacun de ceux-ci comprenant cette couche de composition. Une composition selon la présente invention contient un polymère photo-alignable et un tensioactif ; le polymère photo-alignable comprend un groupe photo-alignable, et un atome de fluor ou un atome de silicium ; le tensioactif comprend un atome de fluor ou un atome de silicium, tout en ayant une masse moléculaire moyenne en poids inférieure ou égale à 10 000 ; et la tension superficielle de liquide A1 du tensioactif et la tension de surface de liquide A2 du polymère photo-alignable satisfont à la formule (IA).　(IA) : A2 – A1 ≥ 0,5 mN/m
PCT/JP2021/016952 2020-04-30 2021-04-28 Composition, couche de composition, corps multicouche optique et dispositif d'affichage d'image WO2021221100A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2022518114A JP7355928B2 (ja) 2020-04-30 2021-04-28 組成物、組成物層、光学積層体および画像表示装置

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-080600 2020-04-30
JP2020080600 2020-04-30

Publications (1)

Publication Number Publication Date
WO2021221100A1 true WO2021221100A1 (fr) 2021-11-04

Family

ID=78331988

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/016952 WO2021221100A1 (fr) 2020-04-30 2021-04-28 Composition, couche de composition, corps multicouche optique et dispositif d'affichage d'image

Country Status (2)

Country Link
JP (1) JP7355928B2 (fr)
WO (1) WO2021221100A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014185410A1 (fr) * 2013-05-13 2014-11-20 日産化学工業株式会社 Procédé de production d'un substrat ayant une membrane d'orientation de cristaux liquides, pour utilisation dans un élément d'affichage à cristaux liquides à commutation dans le plan
WO2015030000A1 (fr) * 2013-08-27 2015-03-05 日産化学工業株式会社 Composition permettant de former un film durci, matériau d'alignement, et matériau à différence de phase
WO2017010560A1 (fr) * 2015-07-16 2017-01-19 富士フイルム株式会社 Composition de cristaux liquides, film, miroir semi-réfléchissant pour dispositif d'affichage d'image projetée, et procédé de production de film
WO2017183682A1 (fr) * 2016-04-22 2017-10-26 Dic株式会社 Composition polymérisable et film l'utilisant
WO2018216812A1 (fr) * 2017-05-26 2018-11-29 富士フイルム株式会社 Polymère de photo-alignement, composition de liant, couche de liant, stratifié optique, procédé de production de stratifié optique, et dispositif d'affichage d'image
WO2019069911A1 (fr) * 2017-10-02 2019-04-11 富士フイルム株式会社 Composition de cristaux liquides, couche réfléchissante, procédé de fabrication de couche réfléchissante et copolymère

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014185410A1 (fr) * 2013-05-13 2014-11-20 日産化学工業株式会社 Procédé de production d'un substrat ayant une membrane d'orientation de cristaux liquides, pour utilisation dans un élément d'affichage à cristaux liquides à commutation dans le plan
WO2015030000A1 (fr) * 2013-08-27 2015-03-05 日産化学工業株式会社 Composition permettant de former un film durci, matériau d'alignement, et matériau à différence de phase
WO2017010560A1 (fr) * 2015-07-16 2017-01-19 富士フイルム株式会社 Composition de cristaux liquides, film, miroir semi-réfléchissant pour dispositif d'affichage d'image projetée, et procédé de production de film
WO2017183682A1 (fr) * 2016-04-22 2017-10-26 Dic株式会社 Composition polymérisable et film l'utilisant
WO2018216812A1 (fr) * 2017-05-26 2018-11-29 富士フイルム株式会社 Polymère de photo-alignement, composition de liant, couche de liant, stratifié optique, procédé de production de stratifié optique, et dispositif d'affichage d'image
WO2019069911A1 (fr) * 2017-10-02 2019-04-11 富士フイルム株式会社 Composition de cristaux liquides, couche réfléchissante, procédé de fabrication de couche réfléchissante et copolymère

Also Published As

Publication number Publication date
JP7355928B2 (ja) 2023-10-03
JPWO2021221100A1 (fr) 2021-11-04

Similar Documents

Publication Publication Date Title
JP7232754B2 (ja) 光配向性ポリマー、バインダー組成物、バインダー層、光学積層体、光学積層体の製造方法および画像表示装置
KR102467728B1 (ko) 광배향성 공중합체, 광배향막 및 광학 적층체
KR20200090870A (ko) 광학 적층체의 제조 방법, 광학 적층체 및 화상 표시 장치
WO2015182704A1 (fr) Corps stratifié et son procédé de production, plaque de polarisation, dispositif d'affichage à cristaux liquides, dispositif d'affichage el organique
JP2019120949A (ja) 光学積層体および画像表示装置
JP7228049B2 (ja) 光配向性ポリマー、バインダー組成物、バインダー層、光学積層体、光学積層体の製造方法、画像表示装置
KR102701371B1 (ko) 광학 적층체, 편광판, 화상 표시 장치
JP4297436B2 (ja) 液晶性ジ（メタ）アクリレート化合物及びこれを用いた位相差フィルム、光学フィルム、偏光板、液晶パネル並びに液晶表示装置
JP7212136B2 (ja) 光配向膜用組成物、光配向膜、積層体
WO2019035468A1 (fr) Composition de cristaux liquides, film anisotrope absorbant la lumière, corps stratifié et dispositif d'affichage d'image
JP7181376B2 (ja) 共重合体、光配向膜用組成物、光配向膜、光学異方性素子および偏光素子
JP7189232B2 (ja) 光配向性共重合体、バインダー組成物、バインダー層、光学積層体および画像表示装置
JP6945052B2 (ja) バインダー組成物、バインダー層、光学積層体および画像表示装置
JP7355928B2 (ja) 組成物、組成物層、光学積層体および画像表示装置
JP7496416B2 (ja) 光配向性ポリマー、バインダー組成物、バインダー層、光学積層体、光学積層体の製造方法、画像表示装置
US11827727B2 (en) Photo-alignment polymer, binder composition, binder layer, optical laminate, optical laminate manufacturing method, and image display device
JP7303334B2 (ja) 光配向性ポリマー、バインダー組成物、バインダー層、光学積層体、光学積層体の製造方法、画像表示装置
JP7385729B2 (ja) 光学積層体、偏光板および画像表示装置
JP7502446B2 (ja) バインダー組成物、化合物、バインダー層、光学積層体、光学積層体の製造方法、および、画像表示装置
JP7335986B2 (ja) 化合物、液晶組成物、液晶フィルム
JP2023080006A (ja) 光配向性ポリマー、バインダー組成物、バインダー層、光学積層体、光学積層体の製造方法、画像表示装置
JP2023104473A (ja) 光配向性ポリマー、バインダー組成物、バインダー層、光学積層体、光学積層体の製造方法、画像表示装置
WO2020110817A1 (fr) Procédé de fabrication de stratifié optique

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21797906

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2022518114

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21797906

Country of ref document: EP

Kind code of ref document: A1